By T. T. Read

TWO papers on health and safety were given Thursday afternoon when a joint session of the Health and Safety Committee and the Mining Methods Committee was held. T. T. Read presided and the first paper, on ventilation at Climax, was presented by the author, L. H. Glanville. In the subsequent discussion by Cloyd M. Smith, P. B. Bucky, B. F. Tillson, D. F. Haley, J. L. G. Weysser, and others a number of interesting points not covered by the paper, which appears in full in the January Mining Technology, were brought out. Ventilation troubles in mines so often hinge on the air being too hot and damp that it was interesting to hear of one where it is frequently too cold and too dry.

Jan 1, 1943

By Eugene McAuliffe

NO physical impairment can be more serious than the partial or complete loss of sight. With reasonably good eyesight, a person is equipped to care for life and I limb, provided a rational measure of t caution is manifested. When the sight of one eye is lost or badly impaired, one-half of this God-given asset is gone, and extreme care must be taken to prevent the tragedy of total darkness that closes out the beauty of sky, field and mountain, the faces of relatives and friends, and either removes entirely or in part one's capacity to produce and earn. During 1933, The Union Pacific Coal Co., operating ten coal mines in Wyoming, decided to undertake a visual survey of all of its mine operating officials and employees. Although the cost of workmen's compensation paid because of eye injuries was material, the management was more deeply concerned with the social loss and the suffering resulting from the many eye injuries. As every element of coal production cost must be scrutinized, accurate data on all accidents, with the workmen's compensation paid therefor, are carried forward monthly. The number of accidents to eyesight and the resultant compensation paid are shown in Table 1 for nine calendar years:

Jan 1, 1934

By L. D. Ricketts

AN older man looks back, perhaps wistfully, on a long and rather active experience, and possibly a popular and brief glimpse of some contrast between past and present may hold your attention for a few brief moments and prove useful. In the late nineties an engineer was .called on to de- sign and build two copper ore concentrating mills of 400 tons average daily capacity. There were larger mills than this at Washoe and elsewhere, but a 400 ton' mill was a large one as mills went over thirty years ago, and one might say a large mill of those days could crush a ton of copper ore in 216 seconds. In the mills I refer to steel construction and the conveying belts were introduced into the copper industry and rein- forced concrete came shortly after. Since then we in the West have ever been faced with a constantly de- creasing tenor in the grade of our copper ores and a constantly increasing demand for our product, and we have therefore been obliged to call for far larger castings and finished machines than were formerly used. The mechanical engineer has also enabled us to accomplish notable economies in power generation and distribution. Ore handling and crushing have been simplified and through the introduction of reagents to induce physical or chemical reactions, or both, our older methods have been vastly improved or even supplanted by new and better ones and our recoveries greatly improved.

Jan 1, 1929

By AIME AIME

ALMOST as many attended the annual dinner this year as last, when the presence of Mr. Hoover was such an attraction that almost two-thirds more than had ever attended before were present. Only by putting the late comers at tables in the balcony could everybody be accommodated. Past President De-Golyer was the toastmaster and in opening the post-prandial exercises referred to the regrettable fact that this was the last of the long series of dinners which have been held at the Waldorf, as the hotel will be torn down to give way to an office building before another year. To the delight of the gathering "Oscar" appeared and, in a delightfully brief but characteristic speech, referred to the long association that had existed and hinted that a new Waldorf-Astoria may arise, where the Institute could continue to gather annually in an enlarged replica of the room they had met in so long. Before taking up the presentation of the medals, Mr. DeGolyer referred to the Institute's "Legion of Honor," the 34 men who have been members continuously for over fifty years. For various reasons only five of them, W. S. Ayres, F. G. Corning, Henry D. Hibbard, A. F. Schneider and Arthur Thacher, could be present. They were all seated at the speaker's table, and W. S. Ayres, 56 years a member, as the dean of the group, was called on to respond for them all. He said: "The introduction I have just received would indicate that this particular group of men to which I belong is considered by the chairman to be a group of real antiques. Possibly you are questioning the accuracy of his judgment. I hope you are, although there may be some first-sight evidences tending to substantiate the view held by the chairman.

Jan 1, 1929

By AIME AIME

THE petroleum economics session," held on Wednesday morning, Feb. 20, 1929, presided over by Campbell Osborn, chairman, proved to be of un- usual interest and resulted in serious and constructive discussion of the papers presented. The first paper on the program, "Gasoline Economics and Refinery Operation," was by H. J. Struth, petroleum economist of the Gulf Publishing Co., Houston, Tex. While this paper was intended to cover the re- finery situation, it also presented the author's reasons for believing that the oil producer should give cognizance to gasoline demand as a most reliable barometer by which to parallel the production of crude petroleum. The discussion which followed brought out some interesting points in connection with the immediate outlook for the industry as a whole during the present year. Some advanced the opinion that, regardless of the out- come of proration efforts, the refiner is in a position to conduct his operations on a reasonably profitable basis, provided that he exercises control over them. This would mean running less crude and resorting to wider utilization of cracking to produce the gasoline demand. Thus, if the refiner uses diligent care in scheduling his still runs, the producer will be obliged to carry over a large stock of crude this year, unless he is able to keep production below the limits prescribed by the demand for gasoline.

Jan 1, 1929

By Ernest A. Hersam

IN every commercial establishment,' it is customary and necessary to take inventory, periodically, and to account for profits and detect losses, to achieve productiveness and enhance efficiency. So, too, in the ordered life of every individual, there is the need of periodic introspection. The exercise of the Sabbath for rational thought, the utilization of pause, or rest, from the technique of daily occupation, orient the efforts. These are the constructive opportunities by which we grow always better than we were. Thus, also, there' is need of a periodic analysis of the organizations to which we belong and toward which we con- tribute. So we find' reason for the fitness of our loyalty. There seems to be no half-ground for the engineer. Whatever presumes to bear his name demands either the crushing pressure of his heel or the supporting pressure of his hand.

Jan 1, 1929

By Charles Will Wright

THE economy as well as the living standards of a country depends largely upon adequate supplies of raw materials at reasonable prices. Geological and climatic conditions responsible for the occurrence of commercial minerals and the growth of raw agricultural and forest products are so varied in different parts of the world that no country can be self-sufficient. The world is rapidly shrinking because of improvement in transportation facilities, but populations are steadily increasing and so are the needs for a greater production of raw materials and for their more equitable distribution. Too many barriers between nations prevent free access to the main sources of supply of the raw materials vital to neighboring nations and it is just such barriers that are often the cause of friction and even war. The International Trade Organization is doing a commendable job in helping to. break down barriers and to reduce friction, and we should now find ways to facilitate access to these sources of supply and encourage more efficient and greater production of the raw materials so urgently needed throughout the world. This cannot be done by individual selfish governmental agencies, influenced as they are by politics, nor by socialistic governments attempting to nationalize industries. It can be done efficiently only by the free individual through private enterprise properly protected against adverse governmental action. This protection can be supplied by the World Bank.

Jan 1, 1948

By Albert Sauveur

Jan 1, 1924

By Albert Sauveur

Jan 1, 1924

By E. W. Davis

DURING late years, the proportion of beileficiated iron ore shipped from the Lake Superior District has increased very rapidly. By benefication is meant washing, screening, drying, sintering or any process by which the grade or structure of the crude ore is improved before shipment. In 1915, only 3,000,- 000 tons, or 9 per cent, of t6e total Minnesota shipment was beneficiated ore, compared with 13,500,000 tons, or 35 per cent, of the total Minnesota shipment in 1925. This increase is, of course, due to the fact that iron and steel can be made more cheaply after beneficiating these ores than they could have been had these ores not been so treated. Fundamentally, however, several causes contribute to the necessity for beneficiating iron ores, such as depletion of the reserves of high-grade ores, the iron ore leasing systems and taxation methods and, at the smelting plants, a better understanding of blast-furnace operations, increased operating costs and increased sulfur content of blast-furnace coke. As economic conditions change, it is by no means certain that the proportion of beneficiated ore shipped each year is going to continue to increase. Undoubtedly some of the beneficiation operations are not economically sound at the present time and what the future has in store for the iron ore industry is problematical. Generally speaking, the cost of fuel for blast-furnace operations will increase as time goes on and in order to continue to produce cheap iron and steel, some of the other costs must be lowered. Freight and labor rates probably can- not be reduced. The cost of producing iron ore cannot be reduced much below the present price. It therefore appears that the best opportunity for maintaining iron and steel prices at their present level in spite of in- creased costs of labor and raw materials is to use. less or cheaper raw materials. This, of course, contemplates an improvement in metallurgical processes all along the line and, as a matter of fact, we can confidently expect these improvements because scientific investigations will undoubtedly be even more productive in the future than they have been in the past.

Jan 1, 1926

By Hans Lundberg

IN last year's report on the progress of geophysics, the airborne magnetometer was the featured new development. At that time only a relatively small number of surveys had been made. During 1947, the airborne magnetometer was used in making many surveys and is again one of the high lights of the year in geophysics. This report is mainly concerned with geophysics as applied to the search for minerals exclusive of petroleum. In 194,5 and 1946, the use of the magnetic method reached a peak, partly because of an active period of prospecting brought on by an active mining market, particularly in Canada.

Jan 1, 1948

By F. J. Norton

THE object of this investigation was to make a comprehensive study of the degassing of molybdenum in order to determine how rigorous a treatment was necessary to completely remove sorbed gases from molybdenum electrodes in vacuum tubes. Some work has also been done with tungsten, nickel and carbon. As a logical development of this work it has been shown that the gas is present throughout the body of the metal and a study has been made of the solubility of nitrogen in molybdenum and tungsten and the rate of diffusion of nitrogen through molybdenum has been calculated. Tests were made on molybdenum from all the commercial sources and no difference was discovered in the nature of the gases present, the amounts or the ease of removal. The reason for this was apparent when a study was made of the manner in which gases are absorbed by gas-free molybdenum. It is necessary to heat molybdenum to 1760° C. in a vacuum of the order of 0.001 micron for a time which varies lineally with the thickness, in order to obtain a condition in which no further gas is evolved by the sample. A sample so degassed can be handled and subsequently assembled in a tube and then degassed readily. The gases obtained from molybdenum are carbon monoxide and nitrogen, the nitrogen being the more difficult to remove.

Jan 1, 1932

By L. F. Tedsen, A. E. Flanigan, J. E. Dorn

SINCE aluminum-alloy sheet may be used occasionally at moderately elevated temperatures, the effects of temperature en the mechanical properties are of interest. Recently the short-time tensile properties of several high-strength materials have been studied at temperatures up to 375°F. This paper deals with stress-rupture and [ ] creep properties at the same temperatures. The work was done at the University of California as a portion of the project NRC-548. It was financed by the War Production Board and was supervised by the Office of Production Research and Development. This paper has been released for publication by the latter agency. The following materials were studied, all in the form of 0.040-in. sheet: Alclad 24S-T Alclad 24S-T8I Alclad 24S-T86 Alclad 75S-T R301-T (clad) [ ] Specimens were loaded in tension in the cross-grain direction. Testing temperatures included 94°F., 211°F., 300°F., and 375°F. Stress levels were selected to cause rupture in times ranging from several minutes to boo hr. In each test the following data were obtained: (I) fracture time, (2) elongation at fracture, (3) the complete strain-versus-time curve (creep curve), (4) creep rate (defined in a later section). MATERIALS Materials for specimens were obtained from the manufacturers' commercial

Jan 1, 1946

By W. H. Bassett

Beads of metal frequently appear at the ends of cast-copper wire bars and on the sides of wedge cakes near the top. These are richer in cuprous-oxide than the rest of the casting. A micrographical study of these exudations has been made. It is suggested that the material is forced through the surface while the copper is solidifying. If not eliminated in process of manufacture, it shows on the finished polished sheet copper in patches differing in color from the main body of the sheet. FIGURES 1 to 4 show the copper exudations, at different magnifications, as they appear on the ends of cast wire bars, and on the sides, usually near the top, of wedge cakes. Sometimes the exudations are in fine "drops;" at other times, large masses of the material are found. Microscopic examination of the copper exudation indicates that it is high in oxide and of eutectic proportions. Because of the difficulty of securing a suitable sample, the protuberances have not been analyzed chemically; but the spectroscope shows no indication that there are any more metallic impurities present than in the balance of the copper. The lowest copper plus silver content of the coppers studied for this? paper was 99.914 per cent.; the highest, 99.966 per cent.; so the oxygen content of the whole casting would be well under 0.07 per cent.

Jan 2, 1926

By J. B. Cohen, S. L. Sass

The nucleation process for y', Ni3Ti, is shou'n to change from heterogeneous to uniform as the undercooling within the phase boundary increases. As unifornz nucleation beconres copious, (100) alignment is observed in the early stages of aging; howecer. whether or not the alignment is due to spinodal decomposition could not be determined. The presence oi a large-scale reversible segregation of titanium and not the intermediate precipitate y' may be the cause of the initial strengthening in this alloy system and the discrete regions detected magnetically by Ben-Israel and Fine. Evidence is presented for the role of dislocations in the formation at long aging tines oJ the equilibrium precipitate . ThE nickel-rich portion of the Ni-Ti phase diagram consists of a terminal fcc solid solution of titanium in nickel called y.' For temperatures below 1290°C if the solubility limit is exceeded and the temperature is high enough, the excess titanium will combine with nickel to form q, Ni3Ti, a four-layer hcp ordered structure with stacking sequence ABAC."~ Since a change in structure is involved, formation of q is slow and a metastable precipitate referred to as y' forms. This metastable precipitate is an ordered cubic phase in the unconstrained state having a structure similar to Cu3Au (LIZ) with the composition Ni,Ti."'5 From X-ray studies,8, 7 the following sequence is indicated for the precipitation reaction at low temperatures: 1) The appearance of satellites around low-index diffraction spots and splitting of high-index spots, indicating the formation of a slightly tetragonal phase in an imperfectly periodic arrangement. The tetragonal phase is y' or the depleted matrix, depending on the volume fractions of matrix and precipitate (and hence, the alloy composition); tetragonality apparently arises from coherency strains. 2) The appearance of diffraction spots from the equilibrium second phase, q. Ben-Israel and Fine'" used magnetic methods to measure the changes in matrix composition during aging, and to estimate the precipitate composition in a Ni-10.1 at. pct Ti alloy. They observed that the alloy, solution-treated at 1270°C and quenched, contained heterogeneities with discrete compositions which gradually vanished upon aging. It was suggested that y' may initially form as a defect structure with several possible compositions deficient in titanium as compared to Ni3Ti; the composition Ni3Ti develops with prolonged aging. The initial composition was Ni6Ti which would require a very large deviation in stoichiometry for y'. It was noted that at 700°C the precipitation reaction was 80 pct complete after 2 hr and that the volume fraction of second phase was 0.2 after 1 hr. Mihalisin and Decker' suggested that the equilibrium precipitate, besides being nucleated at grain boundaries, could also form at stacking faults. ~errick" examined the formation of in Ni-Cr-Ti, and suggested that a collapsed vacancy cluster within y' acted as a nucleus for intragranular q at high temperatures, 820" and 900°C. After long aging times at lower temperatures, 650" and 750°C, diffraction patterns taken from regions containing ribbons of stacking faults showed spots associated with q. Aging greatly enhances the mechanical properties of these alloys, even at high temperatures, and the metastable precipitate y' is thought to be responsible.' At 600°C the hardness of a Ni-10.1 at. pct Ti alloy increases rapidly during the first 20 hr of aging and continues to increase slowly thereafter.'" At 700°C the hardness reaches a maximum at 1 to 2 hr and then decreases.l1 In this paper the kinetics of formation of y' and the mechanism of transformation to in a Ni-Ti alloy are described. Evidence is presented that suggests that large-scale regions of titanium segregation are present initially and these may have an important influence on the initial strengthening of the alloy: these regions may be the heterogeneities detected by Ben-Israel and Fine. I) EXPERIMENTAL TECHNIQUES The Ni-10.3 at. pct Ti-0.6 at. pct A1 alloy was prepared by vacuum melting. Its chemical analysis is given in Table I. A 0.007-in.-thick strip was sandwiched between foils of the alloy and placed in an open Vycor tube with titanium chips (to get oxygen) and solution-treated for ; hr at 1150°C in a Globar Furnace under a flowing argon atmosphere. Following a quench into an ice-brine mixture at -5" to -2"C, a sample to be aged at temperatures up to and including 700°C was sealed in an evacuated Vycor capsule before being put into a fused salt bath. Aging above 700°C was carried out on bare samples in a salt bath. When removed from this bath and quenched into an ice-water mixture, the sample was normally coated with a thin layer of oxide easily removed with emery

Jan 1, 1970

By G. W. P. Rengstorff

In an effort to find an oxidation-resistant alloy of molybdenum, binary and ternary alloys containing aluminum, chromium, cobalt, iron, nickel, silicon, titanium, tungsten, vanadium, and zirconium were screened. Fourteen other alloying additions were also tested. Many of the alloys were more oxidation-resistant than molybdenum, but none were entirely satisfactory. MOLYBDENUM oxidizes extremely rapidly above 1450°F in air. At 1800°F, a loss of metal at the rate of 0.1 in. in 4 hr is typical. The high speed of this oxidation may be judged by comparison with the oxidation rate of 0.1 in. per year (0.00005 in. in 4 hr), sometimes taken as the maximum permissible oxidation rate at 1800°F for a satisfactory Fe-Cr-Ni alloy. Great strides have been made in the development of coatings and cladding to protect molybdenum from oxidizing atmospheres. These developments in surface protection will undoubtedly make it possible to take advantage of the excellent hot strength of molybdellum and its alloys in many new applications. Still, even the best coating can protect molybdenum only as long as the surface layer is unbroken. Research was undertaken to determine whether an alloy of molybdenum could be found which would resist oxidation. Such an alloy would not deteriorate suddenly when the protective surface layer was destroyed in a small area. In seeking an alloy of molybdenum to resist oxidation, the physical properties of molybdenum could not be sacrificed entirely. The development of an alloy with the desired resistance to oxidation was not achieved. The information obtained on the effect of a large number of elements on the oxidation of molybdenum is, however, of value in the development of coatings. Indeed, many of the alloys tested for oxidation resistance were already known to have poor mechanical properties but were tested to aid in the development of coatings. Oxidation of Molybdenum The rapid oxidation of molybdenum is usually attributed to the volatility of Moo,,. Gulbransen and Wysong have shown that molybdenum oxidizes very slowly up to 850°F, the temperature at which the oxide film begins to evaporate. Melting as well as evaporation of molybdenum oxides promotes the oxidation of molybdenum. MoO melts at 1465°F. MOO, the oxide which is believed to form at the metal-oxide interface, combines with MoO, to form a eutectic having a melting point of 1432°F.' The liquid oxide, even if nonvolatile, could cause poor resistance to oxidation by allowing easy transport of molybdenum and oxygen ions through the oxide. Actually, a sudden increase in the rate of oxidation of molybdenum at 1460°F has been observed to coincide with the appearance of a liquid phase. The formation of a volatile oxide is not unique with molybdenum. The problem is also encountered with vanadium, tungsten, and some of the Pt-Pd group of metals. Vanadium not only forms the volatile V2O3 but, like molybdenum, forms a liquid oxide coating. Few attempts have been made, however, to prevent the rapid oxidation of these metals by alloying. Oxidation of Molybdenum Alloys At the beginning of this work, very little was known of the oxidation resistance of molybdenum alloys. It was known that molybdenum disilicide (with 37 pct Si) has extremely good oxidation resistance,' but this compound is so brittle that it has few uses. It is an effective protective coating for molybdenum when allowance can be made for its brittleness. Chromium was known to retard the oxidation of molybdenum,' but at least 50 pct Cr was necessary to have an appreciable effect. Other, unpublished, reports show that a few other alloys have been given preliminary tests, but the results have not been promising." Choice of Alloys to be Investigated An alloying element might be expected to protect molybdenum in either of two ways: Its oxide might combine with molybdenum oxide to form a stable, nonvolatile complex oxide (a molybdate); or the oxide of the alloying element might form in preference to molybdenum oxide, developing an impervious layer which would prevent the formation of a volatile molybdenum oxide. The knowledge available about the formation of molybdates was meager. Therefore, the initial study was made on alloys of molybdenum with elements having especially stable oxides. On this basis, binary and ternary alloys containing the following six elements were investigated: aluminum, chromium, titanium, zirconium, silicon, and vanadium. Nickel was also added as an alloying element. Although it does not form a more stable oxide than molybdenum, it does impart some oxidation resistance to copper and iron. Its inclusion in the study was fortunate because its alloys proved to be the most promising of those first tested. Apparently nickel formed a stable molybdate. Because nickel was effective in reducing the oxidation rate of molybdenum, the elements iron, cobalt, and tungsten were added to the list. The ten alloying elements mentioned form ten binary and 45 ternary alloying systems with molybdenum. A series of alloys was tested in each of these systems. In addition, at least one test was made on the effect of each of the following alloying elements:

Jan 1, 1957

By Joachim J. Hauser

Experiments on latent hardening were peyformed by compressing single crystals along a direction perpendicular to the tension axis. The slope and length of easy glide in the tension test were found to depend only on prior deformation in the same slip plane. Prior deformation on a different slip plane changes the stress level of the resulting stress-strain curve. The yield points appearing upon reloading after prior extension and unloading were related to the end of easy glide. SEVERAL researchers have studied the latent hardening due to deformation of a crystal by slip on a slip System after prior deformation. These experiments can be divided into those in which the prior deformation was on the same plane as the subsequent and those in which the two deformation processes were in different planes. In the former category are the experiments of Buckley and Entwistle,1 Parker and washburn,2 and Haasen and Kelly.3 The latter case has not been studied systematically; it was the main purpose of this investigation to produce this type of latent hardening and explain the results in terms of the existing theories of work hardening. In general, tension producing slip on a certain slip system can be preceded by tension, transverse compression or longitudinal compression, each with predictable dislocation movement and intersection. The intersection of dislocations can lead to glissile or sessile jogs, Cottrell-Lomer locks and other sessile dislocations. The effect on the stress-strain curve could depend on which combination of the former mechanisms is operating. Haasen and Kelly3 have studied the yield points which occur in aluminum and nickel single crystals upon reloading after prior unloading in a tension experiment. They attributed this effect to the anchoring of dislocations occurring during unloading. As Cottrell and stokes4 have shown that dislocations cutting through the "forest" could only lead to reversible changes, they attributed the anchoring to the formation of sessile dislocations during unloading. However, different kinds of sessile dislocations could be formed during unloading, and it was the purpose of this experiment to determine whether Cottrell-Lomer locks are responsible for the yield effect and for the end of easy glide. The case where a longitudinal compression is followed by tension along the same axis is commonly referred to as a Bauschinger test. This type of effect was studied by Buckley and Entwistle1 on aluminum single crystals and by Parker and washburn2 on zinc single crystals. In such a test, the tension and the compression activate the same slip plane with opposite slip directions. The use of sideways compression in the present experiments permits the activation of different types of slip systems and the study of their effect on the easy glide region and on the transition between the elastic and easy glide region. The theory of seeger5 for the flow stress in fee materials is applied to explain the latent hardening. EXPERTMENTAL PROCEDURE All the single crystals used in this investigation had an axial orientation close to <210>, called the "0.5" orientation. This is the orientation for which the tensile axis is 45 deg from both the slip plane and the slip direction. The single crystals were grown from the melt under a helium atmosphere using milled graphite boats,=at a rate of 8.6 mm per min. The silver used in the experiment was 99.98 pct pure. The single crystals had a square cross section about 0.9 by 0.9 cm and a length of 14 cm. The orientation of the specimen was determined within ±2 deg by the Laue back-reflection method. The specimens were annealed at 940&apos; ± 2°C in a helium atmosphere for 24 hr and then furnace cooled over a period of 7 hr. The specimens were electropolished in a solution of 9 pct KCN in water. The specimens were tested in a soft-type tensile machine (the load is prescribed) up to 3 pct strain. The stress was increased continuously at approximately 30 g per mm2 per min. The strain was measured over a 5 cm gage length with a mechanical extensometer employing an optical lever. The strain and stress were measured with accuracies of i 2 X 10-5 and ± 2 g per mm2, respectively. The remainder of the stress-strain curve up to 20 pct strain was obtained in a hard-type tensile machine (the strain rate is prescribed). The strain and the stress were measured in that machine with an accuracy of ±2 pct. The compression tests were performed in the hard-type machine using accurately machined steel blocks without lubrication. The blocks were used so as to apply a uniform compression over a length of 13 cm. The strains were measured on the hard-type machine and with a micrometer.

Jan 1, 1962

By P. Chiotti, J. T. Mason

Ther?nal, X-ray, metallographic, and vapor pressure data were obtained to establish the phase diagram and standard free energy, enthalpy, and entropy of formation for the compounds in the Sw-Zn system. Four compounds, SmZn, SmZn2 , SmZn4.s, and SmZn8.5, melt congruently at 960°, 94Z°, 908°, and 940°C, respectively. The cornpounds SlnZns, Sm3Znll, and SnzZn7.3 undergo peritectic decomposition at 855", 870°, and 890C, respectively. Another compound of uncertain stoichiometry, SmZn11, undergoes peritectic decomposition at 760°C. Four entectics were observed with the following compositions in weight percent zinc and eutectic tenzperatures in degrees Centigrade: 12 pct, 680°C; 36 pct, 890°C; 58 pct, 850°C; and 72 pct, 900°C. An allotropic transformation and a composition range were observed for the SmZnz compound. The transfor)nation varies from 905" to 865°C as the zinc content increases from 16.0 to 48.5 wt pct, respectively. The free energy of formation of the compounds at 50PC varies between -15.9 kcal per mole for SmZn to -51.1 kcal per mole for SmZn,.,. Corresponding enthalpies vary between -19.2 to -78.3 kcal per mole. The ther-modynamic properties for the liquid alloys are described by the relations: A search of the literature revealed very little information on the Sm-Zn system. Chao et al.&apos; as well as Iandelli and palenzonai have reported the structure of SmZn to be cubic B2 type and Kuz&apos;ma et al3. have reported the structure of -sm2zn17 to be of the Th2Ni17 type. The purpose of this work was to establish the phase diagram of this system, to determine the zinc vapor pressure over the solid two-phase regions of the SYstem, and to calculate the thermodynamic properties of the compounds. MATERIALS AND EXPERIMENTAL PROCEDURES The metals used in this investigation were Bunker Hill slab zinc 99.99 wt pct pure and Ames Laboratory samarium. Analysis of the samarium by chemical, spectrographic, and vacuum-fusion methods gave the following average impurities in ppm: Nd, <200; Eu, <100; Gd, <100; Y, <50;Ca, 225; Ta, 400; Mg, 10; Cu, ~50; 0, 175; H, 20; and N, 15. The elements Fe, Si, Cr, Ni, Al, and W were not detected. The samarium was received as sponge metal and was kept under argon except when being cut with shears and when being weighed. Tantalum was found to be a suitable container for alloys with zinc contents up to the Sm2Znl, stoichio-metry. At higher zinc contents the grain boundaries of the tantalum containers were penetrated by the alloy and the containers failed during prolonged annealing. About 25 g of massive zinc and samarium sponge were sealed in tantalum crucibles equipped with thermocouple wells. These crucibles were in turn sealed in stainless-steel jackets. All closures were made by arc welding under an argon atmosphere. The samples were equilibrated in an oscillating furnace and in some cases were given various heat treatments in a soaking furnace. After appropriate heat treatment the steel jackets were removed and the alloy subjected to differential thermal analysis. The apparatus was calibrated against pure zinc and pure copper and found to reproduce the accepted melting points within 1°C. Alloys were subsequently subjected to metallographic examination and those of appropriate compositions were used for X-ray diffraction analysis and for zinc vapor pressure determinations. The vapor pressures were determined by the dewpoint method. Both the differential analysis and dewpoint measuring apparatuses have been described in earlier papers.4, 5 All alloy samples were etched with Nital (0.5 to 3 pct nitric acid in alcohol) except the samarium-rich alloys. These more reactive alloys were electro-polished in a 1 to 6 pct HClO4 in methanol solution at -700c at a potential of 50 v. EXPERIMENTAL RESULTS Phase Diagram. The results of thermal analysis are indicated by the points on the phase diagram, Fig. 1. Eight compounds and four eutectics were observed. The composition of the compounds and their melting or peritectic temperatures are given on the phase diagram. The four eutectic compositions in wt pct zinc and eutectic temperatures in % are: 12 pct,- 680°C; 36 pct, 890°C; 58 pct, 850°C; and 72 pct, 900°C. The stoichiometry of the most zinc-rich compound is still uncertain, but is very likely either SmZnll or SmZnlz. However, to simplify the presentation which follows it will be referred to as SmZnll. As shown on the phase diagram the phase regions for some of the samarium-rich alloys have not been unambiguously established. A sample of pure samarium was observed to transform at 924°C and to melt at 1074"C, in good agreement with corresponding val-

Jan 1, 1968

By P. G. Shewmon, H. E. Collins

We have studied the effect of adsorbed sulfur on the surface self-diffusion of copper using eight diflerent surface orientations and the grain boundary grooving method. The eight orientations studied were the four lying near the low-index surfaces—(loo), (Ill), and two directions in the (110)-plus four higher-index surfaces. Surface-diffusion measurements were made over a range of HZS concentrations (in Hz) from 3 to 1500 ppm between 830°and 1050°C. The results can be divided into two groups—Group 1 contains the two (110) surfaces while Group 2 contains the remaining six surfaces. In Group 1, increasing the temperature increases the effect of Hz S on DS for the Hz S range 5700 ppvn. Qs and Do increase with increasing H2S concentration in this Hz S range. Beyond this range, increasing the temperature decreases this effect on D,; also Q, and Do decrease. In Group 2, increasing the telnperature decreases the effect of H2 S on D, for the H2S range studied, and Qs and Do decrease with increasing Hz S concentration. In any study of surface phenomena, there invariably arises the question of the possible presence of and effect of adsorbed impurities. Such questions are well-founded since the presence of adsorbed atoms can sometimes produce marked changes in the kinetics of surface-energy-driven processes. In the last few years, values of the surface self-diffusion coefficient, D,, have been determined on a variety of metals by studying the decay of scratches or the growth of grain boundary grooves.L~3-L0~L3 Yet there has been relatively little work done in which the concentration of an adsorbed impurity was systematically varied and the effects observed. Work of this sort would provide some basis in fact for the assertions often made about the ro1.e of adsorbed impurities in the differences between the results of different workers in different atmospheres and on different metals. It also is relevant to those cases in which surface monolayers produce profound effects in commercially important processes. The most marked example of such effects is the ability of nickel or palladium to increase the sintering rate of tungsten by many orders of magnitude.&apos; The aim of this work was to study the effect of sulfur partial pressures on the surface self-diffusion of copper. It was felt that this in conjunction with a study of the degree of adsorption and type of active sites involvedL8 would provide a wide range of data for one system and hopefully lead to some insight into the mechanism by which sulfur adsorption influences copper diffusion. The main reasons for choosing the Cu-S system were, first, faceting was reported not to accompany the adsorption of sulfur. This is required if our experimental technique is to work. Second, Oudar has determined a high temperature adsorption isotherm for this system, an event which puts the Cu-S system almost in a class by itself.I4 EXPERIMENTAL PROCEDURE Initially, we considered studying the effect of an adsorbed impurity on surface self-diffusion of copper using isolated (or single) scratch smoothing as the technique and oxygen as the impurity. Copper was chosen as the material because the effects of orientation and anisotropy of the surface self-diffusion coefficient, D,, of copper in a dry hydrogen atmosphere had been studied extensively by Gjostein&apos; and by Shewmon and ~hoi.~,~ The isolated scratch technique was chosen because both the effects of surface orientation and anisotropy of D, in a given surface could be easily studied with this method.~ Oxygen was tried as the impurity because Robertson and Shewmon""~ had studied its adsorption on copper at 1000°C over the range of oxygen partial pressures of 10"22 to 10-l3 atm. After several preliminary runs, it became evident that neither the scratch technique nor the impurity oxygen would be satisfactory for this work. Scratching deforms an annealed surface so that the region near the scratches recrystallizes, thereby disrupting the scratch profiles. One can avoid this by deforming the specimen sufficiently before scratching to give complete recrystallization on subsequent heating.4 However, as a result of Gjostein&apos;s success in scratching and annealing undeformed gold single crystals without local recrystallization,13 we attempted something similar with copper single crystals using a 0.7-mil diamond phonograph needle mounted in a Tukon hardness tester. All specimens recrystallized upon being annealed. Also, some copper specimens were sent to Gjostein to be scratched using his technique. The results were the same. As a result, the scratch technique was dropped in favor of the grooving of symmetric grain boundaries. Preliminary work using oxygen showed that faceting began to occur before oxygen adsorption had any measurable effect on D, at 938°C (at Pbo/P, = 0.12). Since heavy faceting would interfere with the measurement, we decided to use a sulfur-containing atmosphere (H2S/H2). Work by Oudar and Benard&apos; and Robertson" showed that sulfur absorbed on copper and that faceting was not observed.

Jan 1, 1967

By Nicholas J. Grant, Ulf Kalling, John Chipman

THE operation of a blast furnace is dependent to an important extent upon the sulphur content of materials charged and the desired limit of sulphur in the product. It has long been known that the blast furnace is the most efficient tool for desulphurization in common use and that this efficiency is associated with the strongly reducing conditions of the hearth and is enhanced by increased basicity and fluidity of the slag. The chemical reactions of desulphurization may be studied from the viewpoint of the ratio of the process or of the final equilibrium conditions. Both kinds of studies contribute to an understanding of the process and both are included here. A simple measure of the desulphurization power of a slag is given by the ratio: Pct sulphur in slag (Pet S) Pct sulphur in metal [Pct S] This ratio was used by Holbrook and Joseph&apos;,&apos; to measure relative desulphurizing powers under controlled laboratory conditions. It was also used by Hatch and Chipman3 as a measure of the equilibrium distribution. For the latter purpose it would be preferable to employ thermodynamic activities rather than percentages, but until very recently this has been impossible for lack of data. Now, thanks to the work of Morris and Williams and Morris and Buehl," the effects of carbon and silicon upon the activity of sulphur in the metal are known. The confirmation of this work and its extension to include the effects of other elements by Sherman and Chipman and by Rosenqvist and Cox&apos; make it possible to calculate the activity of sulphur in pig iron of any composition. Hence it is now possible to use data on the equilibrium distribution of sulphur to find its activity in the liquid slag and to approach an ultimate solution of the thermodynamic aspects of the problem. The rate of transfer of sulphur from metal to slag is the problem of major industrial importance and indeed the principal need for equilibrium data has been as a necessary adjunct to the kinetic studies. The rate of approach to equilibrium under laboratory conditions seems slow compared to the requirements of industrial practice, and it is clear that further laboratory studies of rates are needed. In the research reported below, the items which were investigated were the following: I—The role of mechanical stirring on the approach to equilibrium. 2—The role of MgO in desulphurization as compared to CaO. 3—The role of MnO in desulphurization. 4— The limiting reactions which constitute the slow steps in desulphurization. Experimental Procedure The experimental set-up and procedure previously described by Hatch and Chipman" were essentially followed with several small modifications. The graphite crucible containing the slag and metal charge was altered to provide considerably more active stirring and mixing of the slag and metal in the carbon monoxide atmosphere. For this purpose the crucible was machined to provide two deep cylindrical wells which were interconnected at top and bottom as shown in Fig. 1. A graphite screw with a flat thread and of shallow pitch (4 threads per in.) spinning at 600 to 800 rpm was used to lift the slag and metal over the partition between the two wells and throw them over into the second well, where the metal settled through the slag into the reservoir at the bottom. It was possible to see actual particles of slag and metal being thrown over the partition. In this respect, the stirring was more vigorous than used in the work of Hatch and Chipman. A charge of 400 g of wash metal was first melted, and 20 g of FeS was then added to yield a bath containing 1.65 pct S. Immediately 400 g of slag (as pure mixed oxides) was added and fused. The slag was generally fused in 1 hr * 10 min. Within 30 to 45 min after melting, the temperature was adjusted to 1525"C, and the first slag and metal samples were taken. The slag was picked up on the end of a cold Armco iron rod, whereas the metal was sucked into a silica tube. The wash metal composition was (in percent): 4.29 C; 0.022 S; 0.021 P; 0.38 Si. The slags used were of four fixed starting compositions covering a wide range of acid-base ratios shown in Table I. Deliberate variations in MgO were made in these slags to check the role of MgO in blast-furnace desulphurization. Changes due to additions and reactions were followed by analysis of samples. Additions of Mn and MnO were made to most of the heats to note the role of Mn and MnO on desulphurization. Three heats (62 through 64) were made in an open pot induction crucible (graphite) using a

Jan 1, 1952