The mining fraternity of North America was grieved and shocked to learn of the death of Dr. Willet G. Miller on Feb. 10, 1925. Doctor Miller was for many years the Provincial Geologist of Ontario and the one who more than any other had contributed by his personal work and the reports of his subordinates to the recent extraordinary mineral development of the Province. Doctor Miller was fifty-eight at the time of his decease. A man of unusually stalwart physique, he seemed destined to many years of useful service. His friends in both the American and Canadian Mining Institutes can with difficulty reconcile themselves to his loss. Doctor Miller was born in 1867 in Port Rowan, Ont., on the shores of Lake Erie. After preparation in the high school of his native town, he entered the University of Toronto and took his bachelor's degree in 1890. He pursued graduate studies in geology at Chicago, Harvard, and Heidelberg Universities. In 1893, he was first appointed lecturer and soon thereafter Professor of Geology in Queens University, Kingston, Ont., a chair which he held until 1902. He was then appointed Provincial Geologist of Ontario and was placed at the head of the Survey which was attached to the Department of Mines. Within the next year, 1903, he performed the service that made him famous. In the summer of 1903, in connection with the building of the Ontario Government Railway toward an objective on James Bay, veins had been noticed by construction parties just north of what is Cobalt Lake today, and in the rocky pass that is now traversed by the main line of the Canadian National Railway en route to Vancouver. The pink stain of cobalt bloom on the vein, known later as La Rose, caught the eye of a workman; in November, Doctor Miller recognized the silver in it, and brought the possibilities of the district to general attention. In December, he published an article in the Engineering and Mining Journal, stating that the veins could be worked at a handsome profit. During the winter and spring, the mining interest awoke, which resulted in the astonishingly productive silver district of Cobalt; but in which, Doctor Miller, because a government official, scrupulously refrained from having any financial interest whatever. Seldom has so high a sense of honor been manifested; and as the result, Doctor Miller commanded confidence and respect to an extraordinary degree. Hard on the discoveries at Cobalt came, in the next few years, those at the other famous camps in Northern Ontario; and step by step with them, reports issued from

Jan 1, 1925

By D. M. Dunbar

LONG before Columbus discovered America the original inhabitants toiled in the copper workings of the Andean Cordillera. Their best diggings appear to have been at Chuquicamata, site of the huge present-day open pit owned by the Chile Exploration Co., subsidiary of Anaconda Copper Mining Co. Located in Antofagasta Province of northern Chile, Chuquicamata is in the Atacama desert, high on the western slope of the Andes at 9500-ft elevation. In the Chuquicamata area the Atacama desert merges into the Cordillera. The climate is extremely arid and precipitation, either in the form of rain or snow, is very infrequent. The temperature varies from 50° to 85°F during the day, and drops to 20° to 40° at night. The Antofagasta and Bolivia Railroad, which connects the Chilean Port of Antofagasta with La Paz, Bolivia, passes within approximately 6 miles of the plant. A branch from the main line to Chuquicamata serves the property for outgoing copper and incoming freight. The distance to Antofagasta by rail is 163 miles. Previous to the Inca conquest, this region was inhabited by the Chuco Indians, a small tribe, descendants of the Aymaras and Quechuas. The Incas, whose capital was located in Cuzco, Peru, gradually extended their empire to the south, reaching at one time to what is now central Chile. It is believed that they built crude primitive furnaces on the banks of the Rio Salado where on a small scale they smelted copper ore from Chuquicamata. At the time of the subsequent Spanish conquest, legend has it that Diego de Almagro, on his return to Cuzco in 1536 after his invasion of Chile, obtained from these furnaces metallic copper for horseshoes. During the period from 1560 to 1879 the high grade veins of the Chuquicamata deposit were worked superficially by the Spaniards and Bolivians. The treaty signed after the war of 1879 recognized the sovereignty of Chile over this territory and Chile, realizing the importance of the district, started to develop it in an orderly manner, although only high grade veins were worked. New Process Is Key Reports on the deposit were brought to the attention of Albert C. Burrage, a Boston lawyer and financier, in 1910. Chuquicamata was described as a huge deposit of ore that was not amenable to the usual treatment by concentrating and smelting since much of the copper occurred as oxides. He had been working on a process for the recovery of copper from sulphide ore which involved a sulphating roast, leaching of the roasted product, and pre-

Jan 1, 1952

By H. Conrad, V. V. Damiano, G. J. London

A method is described for producing single crystals of high-purity beryllium, Be-4.37pct Cu, and Be-5.24 pct Ni. These crystals were prepared for testing in compression parallel to the [0001] by orienting and lapping to within ±3' of arc of the (0001). Microstrain testing apparatus is described along with c axis compression results for ingot purity beryllium, twelve-zone-pass material, and the above-mentioned alloys. Results show no measurable plasticity for the ingot purity material from -196" to 400°C, although some surface traces of (1122) slip was observed at 200°C and above. The twelve-zone-pass material shows substantial microstrain plasticity at 220°C with slip on (1122). Both alloys show significant plasticity at room temperature and above with slip also on (1122) planes. THE two slip systems which normally operate during the plastic deformation of beryllium in the vicinity of room temperature are:' basal slip (0001)(1120) and prism slip . Pyramidal slip with a vector inclined to the basal plane has been reported for elevated temperatures,'-a but occurs near room temperature only at very high stresses.~ A summary of the available data on the effect of temperature on the critical resolved shear stress for slip on these systems has been compiled by Conrad and Perlmutter.~ It has been postulated6'7 that one of the principal factors contributing to the brittleness of poly crystalline beryllium at temperatures below about 200°C is the difficulty of operating pyramidal slip with a vector inclined to the basal plane. Hence, detailed information on the operation of such a slip system is important to understanding the brittleness of beryllium. The operation of pyramidal slip with a vector inclined to the basal plane is best accomplished in beryllium by compressing single crystals in a direction parallel to the c axis. In such a test the resolved macroscopic shear strzss on the basal and prism planes is zero and (1012) twinning which is favored by tension along the c axis does not occur. Hence, in c axis compression of beryllium the normal deformation modes are inhibited and the operation of pyramidal slip with a vector inclined to the basal plane is favored. In the present investigation, c axis compression tests were performed on beryllium single crystal as a function of temperature (77" to 700°K), purity (commercial and twelve zone pass), and alloy content (4.37 wt pct Cu and 5.24 wt pct Ni). Presented here is a description of the test techniques employed and the gross mechanical behavior observed. A detailed analysis of the slip traces developed on the surfaces of the deformed specimens during these tests and the results of electron transmission studies of the deformed crystals are given in a separate paper.B PROCEDURE 1) Materials and Preparation. Single crystals about 1 in. diam were prepared of the following materials: commercial-purity beryllium, high-purity beryllium, and two beryllium alloys, one with 4.37 wt pct Cu and the other with 5.24 wt pct Ni. The commercial-purity single crystals were obtained by cutting specimens from large-grained ingot of Pechiney SR material, which is approximately 99.98 pct pure. The high-purity crystals were prepared by floating-zone refining (twelve passes) a rod (7 in. by 1 in, diam) of Pechiney SR grade cast and extruded beryllium. Although an absolute chemical analysis of the zone-refined material was not established, mass spectro-graphic analysis, emission spectrographic analysis, and y activation analysis indicated that it contained in atomic fractions about 5 to 10 ppm each of carbon and oxygen, 1 to 5 ppm each of nickel and iron, and about 1 to 2 ppm of copper, with the remaining residual impurities being less than 1 ppm. Further indication of the purity of this material is provided by the critical resolved shear stress for basal slip, which was approximately 300 psi. The starting material for the alloy single crystals was 1-in.-diam floating-zone-refined (six passes) rod of Pechiney SR grade beryllium. Two such rods were wrapped respectively with sufficient weight of wire of high-purity copper (99.999 pct) or nickel (99.999 pct) to yield a 5 wt pct alloy. A seventh floating-zone pass was then applied to each of the rods to accomplish the initial alloying and an eighth pass for homogenization. Analytical samples were taken from regions of the rod immediately adjacent to where the mechanical test specimens were cut; these indicated 4.37 wt pct Cu and 5.24 wt pct Ni. 2) Crystal Orientation. To avoid the occurrence of basal slip during c axis compression testing, it is necessary to load the crystals as nearly parallel to the c axis as possible. Preliminary c axis compression tests indicated that plastic flow and/or fracture occurred at stresses of the order of 300,000 psi; hence on the basis of a critical resolved shear stress for basal slip of 300 to 400 psi, the maximum crystal misorientation permitted is about 4 to 5' of arc. Since this accuracy cannot be obtained using the usual back-

Jan 1, 1969

By Bruno V. Nordberg

The high cost of coal in Butte and the development of large amounts of cheap electric power from the Missouri river caused the Anaconda Copper Mining Co. in 1908 to make an investigation as to the possibility of adapt- ing this cheap electric power for the operation of their many large hoisting plants. At this time electric power had already been adopted for practically all other power purposes around the mines, such as pumping, compressing air, etc. The map (Fig. 1) shows the location of the mines of the Butte mining district. These mines are located within a circle of approximately a 1-mile

Jan 1, 1914

By J. Chipman, T. Fuwa

The effects of various elements on the activity coefficient of carbon in liquid iron have been studied by two experimental methods: 1) equilibration with controlled mixtures of CO and CO2; 2) the solubility of graphite in the melt. Activity coefficient of C is increased by Al, Co, Cu, Ni, P, Si, S, and Srz. It is decreased by Cr, Cb, Mn, Mo, W, and V. THE thermodynamic properties of the iron-carbon binary system have now been fairly well established, although some uncertainty remains with respect to the exact location of some of the phase boundaries. The activity of carbon in ferrite and in austenite has been measured in the classic researches of R. P. smith' while similar measurements by Richardson and ~ennis, and by Rist and chipman3 have established the values of the activity of carbon in liquid iron up to 1760°C. On the other hand, our knowledge of the effects of alloying elements on the activity of carbon in dilute solutions is restricted to Smith's experiments on systems Fe-C-Mn and Fe-C-Si in the austenitic range and to some more recent experiments of schwarzman4 in the a range. In addition there have been a number of determinations of the effects of various elements on the solubility of graphite in liquid iron, and from these the corresponding effect in saturated solution may be obtained. The purpose of the present study was to extend the investigation of the liquid system to include the effects of alloying elements upon the activity coefficient of carbon, principally in dilute solutions. Equilibrium measurements were made on the reaction C + co, = 2 CO (g) The prepared mixture of CO and CO,, diluted with argon, flowed over the surface of the liquid metal which, after several hours' exposure to the gas, was quenched and anqlyzed. As in the earlier experiments, the principal experimental difficulty was in the deposition of carbon on the parts of the furnace at temperatures slightly below that of the metal bath. In order to minimize this difficulty, the ratio (Pco)2 /PCo2 was restricted to values not much higher than 100 atm, and correspondingly the carbon concentration in the metal seldom exceeded 0.30 pct. EXPERIMENTAL METHODS The method and apparatus were essentially the same as used by Rist and Chipman.3 The gaseous mixture consisting of highly purified CO, CO,, and argon, each controlled by a flowmeter, was led into the furnace and passed over the surface of the liquid-iron melt which was heated and stirred by high-frequency induction. One slight modification was made in that a molybdenum susceptor was placed outside the crucible for the sake of uniformity of temperature and to combat the tendency of carbon to precipitate on the crucible wall. Pure alumina crucibles approximately 25 mm ID were used. The charge consisting of about 30 g was made up of electrolytic iron, the alloying element to be added, and enough graphite to supply slightly more or less than the anticipated equilibrium carbon concentration. All metals used were of high purity. Metallic chromium, columbium, and vanadium were from special lots supplied by the Electro Metallurgical Co. Tin, copper, molybdenum, tungsten, cobalt, and nickel were of purest commercial grades. The electrolytic iron, after being cut to the proper size for charging, was prereduced by hydrogen at 850° to 1000°C to remove surface oxidation. The oxygen content of the reduced material was 0.002 pct. This treatment made it easy to control the carbon content of the initial melt. The charge was melted under the gas mixture to be used for the entire run. In some earlier melts the charge was melted under a stream of argon, but in this case some alumina was reduced from the crucible, and the aluminum thus absorbed in the melt was subsequently oxidized with the formation of a solid film of alumina on the surface of the melt. AS another safeguard against film formation, overheating of the bath was carefully avoided. All runs were made at a temperature of 1560°C. Under experimental conditions a charge of pure iron picked up 0.17 pct C in 3 hr and 0.23 pct C in 6 hr under an atmosphere for which the equilibrium concentration of carbon is 0.27. It is clear that the time required to reach equilibrium from an initially carbon-free melt would be very great. For this reason each experiment was started with a melt of known carbon concentration not far above or below the expected equilibrium value, and each melt was held at temperature for a period of at least 5 hr. Under such circumstances it was possible to chart the approach to equilibrium from both high-carbon and low-carbon materials. Temperature was controlled by frequent optical observation and adjustment and the metls were timed in such a way that the final 2 hr occurred during a time when electric power was steady; for example, 2 to 4 pm or after 11 pm. In melts containine volatile metals such as copper, tin, and mangane\e the time of holding was decreased somewhat in

Jan 1, 1960

By C. E. Lundin

The Ce-H system was investigated in the temperature range, 573° to 1023°K, and the pressure range, 10-3 to 630 Torr, as a function of 'composition up to 72 at. pct H. Families of isothermal arid isopleth curves were plotted from the pressure-terr~perature-composition relationships. From these curves the solubility relationships were determined for the system. The isopleths are analytically represented by equilibrium dissociation pressure equations. The relative partial molal enthalpzes and entropies of solution of hydvogen in the systerrz were calculated fronz the dissociation pressure equulions and are tabulated. The integral free energies, enthalpies, and entropies of mixing in the Ce-H system were determined from the relative partial quantities and are also tabulated. The standard free energy, enthelpy, and entvopy of reaction of the dihydride phase at kcal per kcal per mole H2, and ?S° = -34. 1 cal per deg mole H2, respectively. The equilibrium dissociation pressure equation in the two-phase region is: UNTIL recently very little was known of the detailed solubility and thermodynamic relationships of the Ce-H system. Two previous investigations1,2 are noteworthy. However, significant discrepancies and omissions exist on analyzing them. The work of Mulford and Holley1 on cerium did not clearly delineate the boundaries of the two-phase region, Cess - CeH2-x. The plateau partial pressures were not thoroughly defined and were considerably displaced in pressure compared to those from the work of Warf and Korst.2 These latter authors concentrated their studies primarily from 823° to 1023°K in the pressure range of 1 to 760 Torr. No data were determined to outline the regions of primary solid solubility and the hydride phase. Also the establishment of the plateau partial pressures was rather limited in scope. In neither work was a treatment conducted of the relative partial molal enthalpies and entropies of solution of hydrogen in the single-phase regions and the integral thermodynamic quantities of mixing throughout the system. Therefore, it was the objective of this research to determine the complete equilibrium solubility relationships and thermodynamic data for the system by pressure-temperature-composition studies. EXPERIMENTAL PROCEDURE The cerium metal for this study was donated by the Reno Metallurgy Research Center of the Bureau of Mines. Total impurity content was 0.13 pct with only 60 ppm O. The metal was checked metallographically and contained only minor amounts of second phase compared to cerium from other sources. Specimen preparation was done in a dry box flushed with argon gas. The surface of a small rectangular piece of cerium (about 0.2 g) was filed with a clean, mill file. Final weighing was done in a tared enclosed vial containing argon gas. The specimen was then loaded quickly into the reaction chamber which was purged several times with high-purity hydrogen gas and then allowed to pump to about 10-6 Torr. The furnace was heated to the reaction temperature and the run started. The equipment used to conduct the hydriding was a Sievert's-type apparatus. Basically it consisted of a source for pure hydrogen, a precision gas-measuring burette, a heated reaction chamber, a McLeod gage, and a mercury manometer. Pure hydrogen was supplied by the thermal decomposition of uranium hydride. The 100-ml precision gas burette was graduated to 0.1-ml divisions and was used to measure the quantity of gas and admit it to the chamber. The reaction chamber was a quartz tube. Prior to each run, the cerium specimen was wrapped in a tungsten foil capsule to prevent reaction of the cerium with the quartz. Control of the temperature was achieved within ±1°K. Pressures in the manometer range were measured to ±0.5 Torr and in the McLeod range (10-3 to 5 Torr) to ±3 pct. The compositions of hydrogen in cerium were calculated in terms of hydrogen to cerium atomic ratio. These compositions were estimated to be ±0.01 H/Ce ratio. The technique used to study the equilibrium pressure-temperature-composition relationships of the Ce-H system was to develop experimentally a family of isothermal curves of composition vs pressure. The range of pressure through which each isotherm was developed was from 10-9 to about 630 Torr in the temperature interval, 573° to 1023°K. RESULTS AND DISCUSSION The hydriding characteristics of cerium are iso-morphous with those of the elements of the light-rare-earth group (lanthanum, cerium, praseodymium, and neodymium) wherein the region from the dihydride to trihydride is continuously single phase.' The structure of this phase is fcc.3 The heavy rare earths form a trihydride,2 which is hcp, separated by a two-phase region from the fcc dihydride phase. The Ce-H system is represented by the family of experimental isotherms in Fig. 1. Due to the small scale required to draw the curves, the experimental points are omitted; however, a total of 240 experimental data points were taken to prepare these curves. The solubility relationships can be deduced therefrom. Three distinct regions of partial pressure and composition can be seen. The region of cerium solid solution is represented by the rapidly rising isotherms in the dilute composition range. In accordance with Gibbs Phase Rule only one solid phase, the cerium solid so-

Jan 1, 1967

By William D. Klopp, Joseph R. Stephens

A substantial reduction in the 300°F ductile-to-brittle transition temperature for unalloyed chromium was achieved in alloys from systems which resemble the Cr-Re system. These alloy systems include Cr-Ru, Cr-Co, and Cr-Fe. Transition temperatures ranged from -300° F for Cr-35 at. pct Re to -75°F for 0-50 at. pct Fe. The ductile alloys have high grain gvowth rates at elevated temperatures. Also, Cr-24 at. pct Ru exhibited enhanced tensile ductility at elevated temperatures, characteristic of superplas-ticity. It is concluded that phase relations play an importarlt role in the rhenium ductilizing effect. The ductile alloys have compositions near the solubility limit in systems with a high terminal solubility and which contain an intermediate o phase. The importance of enhanced high-temperature ductility to the rhenium ductilizing effect is not well understood although both may have common basic features. CHROMIUM alloys are currently being investigated for advanced air-breathing engine applications, primarily as turbine buckets and/or stator vanes. The inherent advantages of chromium as a high-temperature structural material are well-known1 and include its high melting point relative to superalloys, moderately high modulus of elasticity, low density, good thermal shock resistance, and superior oxidation resistance as compared to the other refractory metals. Additionally, it is capable of being strengthened by conventional alloying techniques. The major disadvantage of chromium is its poor ductility at ambient temperatures, a problem which it shares with the other two Group VI-A metals, molybdenum and tungsten. For chromium, the problem is further amplified by its susceptibility to nitrogen em-brittlement during high-temperature air exposure. In cases of severe nitrogen embrittlement, the ductile-to-brittle transition temperature might exceed the steady-state operating temperature of the component. The low ductility of chromium would make stator vanes and turbine buckets prone to foreign object damage. The present work was directed towards improvement of the ductility of chromium through alloying, with the anticipation that any improvements so obtained might be additive to strengthening improvements achieved through different types of alloying. The alloying additions for ductility were selected on the basis of the similarity of their phase relations with chromium to that of Cr-Re. The reduction in the ductile-to-brittle transition temperatures of the Group VI-A metals as a result of alloying with 25 to 35 pct Re is well established.a4 the temperature range -300" to 750° F. This phenomenon is commonly referred to as the &apos;<rhenium ductilizing effect"; this term is also used to describe systems in which the ductilizing element is not rhenium. Other alloy systems which have recently been shown to exhibit the rhenium ductilizing effect include Cr-Co and c-Ru.= In order to explore the generality of this effect, alloys were selected from systems having phase relations similar to that of Cr-Re, primarily a high solubility in chromium and an intermediate o phase. The following compositions were prepared: Cr-35 and -40Re; Cr-10, -15, -18, -21, -24, and -27 pct Ru; Cr-25 and -30 pct Co; Cr-30, -40, and -50 pct Fe; Cr-45, -55, and -65 pct Mn. Seven other systems were also studied which partially resemble Cr-Re. These systems have extensive chromium solid solutions or a complex intermediate phase, not necessarily o. The compositions evaluated include the following: Cr-20 pct Ti; Cr-15, -30, and -45 pct V; Cr-2.5 pct Cb; Cr-2.5 pct Ta; Cr-20 pct Ni; Cr-6, -9, -12, and -15 pct 0s; Cr-10 pct Ir. The compositions of alloys in these systems were chosen near the solubility limit for the chromium-base solid solutions, since in the Group VI-A Re systems, the saturated alloys are the most ductile. These alloys were evaluated on the basis of hardness, fabricability, and ductile-to-brittle transition temperatures. In addition to the studies of alloying effects on ductility, an exploratory investigation was conducted on mechanical properties at high temperatures in Cr-Ru alloys EXPERIMENTAL PROCEDURE High-purity chromium prepared by the iodide deposition process was employed for all studies. An analysis of this chromium is given in Table I. Alloying elements were obtained in the following forms: Commercially pure powder — iridium, osmium, rhenium, and ruthenium. Arc-melted ingot — titanium and vanadium. Electrolytic flake — iron, manganese, and nickel. Sheet rolled from electron-bearn-melted ingot — columbium and tantalum. Electron-beam-melted ingot — cobalt. Sheet rolled from arc-melted ingot — rhenium. All alloys were initially consolidated by triple arc melting into 60-g button ingots on a water-cooled hearth using a nonconsumable tungsten electrode. The melting atmosphere was Ti-gettered Ar at a pressure of 20 torr. The ingots were drop cast into rectangular slabs and fabricated by heating at 1470" to 2800° F in argon followed by rolling in air. Bend specimens measuring 0.3 by 0.9 in. were cut from the 0.035-in. sheet parallel to the rolling direction. The specimens were annealed for 1 hr in argon, furnace cooled or water quenched, and electropolished prior to testing. Three-point loading bend tests were conducted at a crosshead speed of l-in. per min over

Jan 1, 1969

By G. R. Love, M. L. Picklesimer

Aboue 950°C the Nb-Zr system consists of a completely miscible bcc solid solution, commonly called the phase. Between 950 and 600°C, and between 20 and 85 pct Nb, the phase deconlposes, after sunciently long times, into two bcc solid solutions. The pct Zr alloys are conveniently descibecl with T-T-T (time-temperature-transformation) curves having a nose at about 2 hr at 700°C. The reaction rate varies only slowly with zirconium content and negligibly with oxygen contanzination; it is speeded up by a factor of 10 to 15 by 90 pct cold ulork and slowed dou by n factor oj 10 to 30 by a two-hundrecljold increase in grain size. Nb-r alloys with compositions between 40 and 85 pct Nb have been the basis for the majority of commercially important superconducting materials. In part because of their commercial promise, more is known about these alloys than about most other high-field superconducting materials. At the same time, there is considerable disputed or incomplete metallurgical information. For example, although Rogers and tkins&apos; indicate a monotectoid reaction at approximately 600°C and a two-phase 01 + 0, field extending between 20 and 85 pct Nb and to a maximum of 95OGC, erhout&apos; has reported that this entire region would be a single homogeneous B were it not for oxygen contamination. Again, although it has been shown that relatively short-time heat treatments in the vicinity of 700CZ significantly improve the ability of short wire samples to carry high currents in high magnetic fields at 4.2K, these observations have never been fully correlated with the structural change or changes occurring during the anneal. We intend to investigate in detail the effect of metallurgical variables, including heat treatment, on the superconducting properties of hard superconductors. To verify that our experimental techniques are valid and to establish a relative standard against which other materials may be measured, we feel it advisable to know the behavior of the Nb-Zr alloys under a variety of processing conditions. As an initial step toward this goal, we have determined in detail the kinetics of the transformations in Nb-Zr alloys. EXPERIMENT A number of problems had to be solved before beginning any fruitful work on the reaction kinetics in this system. While solving some of these problems, either by chance or by design, small amounts of information were obtained about alloys containing 40, 50, 60, 65, 67, 70, and 75 pct Nb, bal. Zr. In addition, a large range of grain sizes and a range of temperatures considerably greater than the range indicated by Rogers and Atkins phase diagram were examined. We will, however, report in detail only the results obtained for the Nb + 33 pct Zr and Nb + 25 pct Zr alloys at three grain sizes, two levels of oxygen contamination, and the temperature range 550 to 950°C. These data are most complete, but the other data are sufficiently complete to indicate the kind and magnitude of the variation of the transformation kinetics outside this range. The first and most difficult problem encountered in this inquiry was one of sample homogeneity. When Nb-Zr alloys are arc- or electron-beam-melted on a cooled copper hearth, solidification is sufficiently slow that there is appreciable coring in the cast structure and a large variation of grain size across the button thickness. Both these factors significantly affect the apparent reaction rate in the system. A two-step solution to the problem was attempted; an arc-melting and drop-casting technique has been developed by conald that greatly reduces the as-cast grain size and virtually eliminates coring segregation. Ingots made in this way exhibited no detectable (3 pct maximum) zirconium segregation. Before it was evident just how good this technique was, we attempted to supplement it with rather long-time, high-temperature annealing of the cast ingots. This annealing was carried out in evacuated and sealed (seal-off pressures < 1.0 x 106 torr) quartz capsules lined with tantalum foil at 1400 to 1450 C for 8 to 72 hr. There were two principal effects of this treatment: the grain size increased to a fairly uniform 150 p, and the surface and all grain boundaries near the surface acquired a film of a second phase, tentatively identified as an oxide (possibly additionally contaminated with silicon). There was no evidence that this 1400 C treatment had affected the zirconium segregation. High-temperature annealing was subsequently used only for grain-size control, but anneals of longer than 4 hr at temperatures greater than 1000°C were performed in dynamic vacuums (pressure no greater than 1.0 x lo torr). Any contamination resulting from these treatments was well below the limits of detection of our techniques. All samples, as cast, were cold-swaged to at least 85 pct reduction in area. The samples called cold-worked were tested as swaged. The minimum re-crystallization anneal for these alloys was about 12 hr at 1050 C; this produced an equiaxed grain diameter of about 4 to 8 P. Annealing for 4 hr at 1450°C produced a grain size of about 80 to 150 p; and annealing for 4 hr at 1650aC, close to the melting point of many of these alloys, produced a grain size of 0.5 to 1.0 mm. At all temperatures, the larger grain size was

Jan 1, 1967

By D. P. Pope, T. Vreeland

Observations of dislocations in zinc using Berg-Barrett X-ray micrography confirm the validity of a dislocation etch for (1010) surfaces. A technique for measurement of the depth in which dislocations can be imaged in X-ray micrographs is given. This depth on (0001) surfaces of zinc was found to be 2.5 µ using a (1013) reflection and CoKa radiation. BUCHANAN and Reed-Hill (B & RH) have recently questioned the ability of a dislocation etch to reveal all of the basal dislocations which intersect (1010) surfaces in annealed zinc crystals.&apos; This etch was developed by Brandt, Adams, and Vreeland who conducted a number of different experiments to check its ability to reveal dislocations.2,3 B & RH prepared (0001) foil specimens for transmission electron microscopy from annealed crystals and observed dislocation densities of about l08 cm per cu cm in the foils, while the etch indicated densities of the order of l04 cm per cu cm in their annealed crystals. As this etch has been used in a number of studies of dislocations in zinc, it is of considerable importance to reassess its validity in the light of the B & RH results. The X-ray work reported here was undertaken to check the ability of the etch to reveal dislocation intersections on (1070) surfaces of zinc. The X-ray technique was chosen for this check because it could be applied to the as-grown crystals with a relatively small amount of specimen preparation. We believe that the possibility of accidental deformation in preparation of the bulk specimens is considerably less than that for thin foil specimens suitable for transmission electron microscopy. Unfortunately, basal dislocations are not visible on Berg-Barrett topo-graphs of (1010) surfaces, which are the surfaces on which the etch is most effective. Therefore, a one-to-one correspondence between the etch and X-ray observations could not be made. Basal dislocations near (0001) surfaces have been observed by Schultz and Armstrong4 using the Berg-Barrett technique, but they did not report the as-grown dislocation density observed in their crystals. We have applied the X-ray technique in this study to surfaces oriented from 1 to 2 deg of the (0001) to determine the basal dislocation density, and have compared this density with that observed using the etch on a (1070) plane of the same crystal. The X-ray observations permit determination of the depth in which basal dislocations can be observed under the diffracting conditions used. SPECIMEN PREPARATION High purity zinc crystals are very soft, so a good deal of care must be exercised in the preparation of observation surfaces. As-grown crystals approximately 2.5 cm in diam and 20 cm long were acid cut into 1.25 cm cubes. A thin slab was cleaved from an (0001) surface to produce an accurately oriented reference surface on the specimen. Some of the cubes were examined in the as-machined condition while some were annealed in argon at 410°C for 2 hr. Heating and cooling rates were less than 2°C per min. Some of the specimens were scratched on a (0001) surface with a razor blade to produce fresh dislocations. Approximately 2 mm of material was acid lapped from one face of a cube to produce a surface oriented between 1 and 2 deg from the basal plane and parallel to the [1210] direction. A (1070) surface was also acid lapped. The lap used a 1 to 3 pct solution of HN03 in water to saturate a soft cloth which was backed by a stainless steel plate. The cloth was moved over the crystal surface at a rate of 20 cm per sec while a normal force of about 4 g was maintained between the cloth and the specimen. As-lapped surfaces were examined as were surfaces which were chemically and electrolytically polished after lapping. The small angle between a lapped surface and the (0001) plane was measured to 0.1 deg using a Unitron microgoniometer microscope (the cleaved surface was used as a reference in this measurement). The microscope was modified so that the intensity of reflected light could be continuously monitored on a meter. This modification produced nearly a ten-fold increase in the reproduceability of orientation readings. OBSERVATIONS The Unitron Microgoniometer observations indicated that the lapped surfaces had a terraced structure with the terraces quite rounded and spaced about 0.1 mm in the [1010] direction. The maximum change in slope between terraces was 0.25 deg, indicating a terrace height of about 0.1 µ. A Unitron measurement of the average angle between (0001) and a lapped surface was checked by micrometer measurement of the specimen and found to agree within 0.1 deg. The Berg-Barrett micrographs using (1013) reflections and CoKa radiation5 revealed subboundaries, short dislocation segments, spirals, and loops near the surfaces which were oriented from 1 to 2 deg of the (0001). Micrographs of surfaces prepared by lapping appeared very similar to those of the chemically and electrolytically polished surfaces. The loops and spirals were not extinct in (1013) or (0002) reflections, indicating that they have a nonbasal Burgers vector. Extinctions of the short, straight dislocations indicated that they belonged to an (0001)(1210) system. Fig. 1 is an example of a micrograph which shows a subboundary, and dislocation segments which are pre-

Jan 1, 1970

By R. R. Jones, R. W. Kraft

Zn-Mg2Znn eutectic alloys nzay freeze willr either rodlike or lanzellar rnorphology. Alloys with slighlly more than /he eutectic arrzount of rnagnesillrn usually contain three-cnned dendrjles of MgzZnll in a eutec-lic ttlulris. All three morphologies haue the same cryslallographic orientution relationship: (0UOl) zn - 11 (111) Mg2Znll and (2310)Zn 11(101) Mg2Znll, but u3ith different prej-erred groulth direclions. The lurnellae lo rods transifion in con/rolled ingols qf euleclic cotnposition occurs because lhe large kinelic undercooling due to MgzZnll minirrzizes /he ejj-ecl of the solid-solid inlerface energy. The eutectic morphology is influenced by the presence of lhree-nned dendrites 0-f MgzZn11 which may conlrol /he rricroslrccture by acting as nuclealion sites. In recent years there has been much interest in eutectic solidification and several theories have been proposed. One of the confusing factors is the existence of various morphologies in which the solidified phases may form. The lamellar microstructure seems to be most common in metal eutectics, and it has been claimed&apos; that all regular eutectics should be lamellar if sufficiently pure. However, there still remain eutectic alloys which are not lamellar or which change their morphology as a function of growth conditions. The eutectic between zinc and the intermetallic phase Mg2Znll was chosen for this investigation because it has been found to solidify in more than one morphology. The diagram in anssen&apos; locates the eutectic point at 3.0 wt pct Mg and 367°C. lliott gives 364°C as the eutectic temperature, leaving the phase compositions unaltered. Since the growth conditions determine the micro-structure of the solidified alloy, the factors controlling the transition from one morphology to another could be studied. The lamellae to rods transition is of particular interest. PROCEDURE Alloys were prepared from carefully weighed portions of 99.999 pct Zn and 99.97 pct Mg by melting in Pyrex containers under argon and casting into graphite boats. The resulting ingots were remelted under argon and solidified unidirectionally in a horizontal tube furnace at growth rates ranging from 2.0 to more than 50 cm per hr under a temperature gradient, measured over a 5-cm length, of 9" to 14°C per cm. The solid-liquid interface appeared to be planar at all growth rates although no attempt was made to confirm this by decantation or quenching. A few ingots were allowed to freeze uncontrolled. Most alloys were of the nominal eutectic composition, 3.0 wt pct Mg according to Hansen2 and lliott, but some contained as much as 3.35 wt pct Mg. Chemical analyses were not run since metallographic examination confirmed that the desired composition was achieved. Specimens were cut from the middle portion of the ingot normal to the growth axis, polished mechanically, and etched with 2 pct Nital. Suitable areas were selected for the determination of crystallographic orientation relationships by a tiontechniqueof described previously by one of the authors.4 The (2310) planes of zinc and the (8701, {944}? (1032) planes of Mg2Znll were found suitable for orientation determination; experimental error was on the order of 2 or 3 deg. RESULTS Three different morphologies were found in the unidirectionally solidified alloys: lamellar eutectic, rod-like eutectic, and a structure whose most predominant characteristic was the presence of three-vaned (cellular) dendrites of Mg2Znll. These dendrites were only found in alloys with more than the eutectic amount of magnesium. In some ingots fine hexagonal needles of Mg2Znll surrounding a core of MgZn2 were observed. They were probably due to incomplete alloying and seemed to have no effect on the eutectic morphology. In addition hexagonal spirals like those discussed by Fullman and wood5 and Hunt and acksonh ere observed in some ingots frozen without directional control. Both MgZZn,, and MgZnz were detected by X-ray diffraction in these alloys. Since the morphology could not be grown unidirectionally and no characteristic orientation relationship between the phases was found, further study was limited to the lamellar: rodlike, and three-vaned dendrite morphologies. Alloys of Eutectic Composition, No Dendrites. The mcrostructures of allovs with no three-vaned dendrites were either lamellar or rodlike depending on the growth rate. At rates below 10 cm per hr the morphology was lamellar, consisting of two sets of parallel plates intersecting at about 54 deg like the Mg-MgzSn eutectic described by raft.7 At growth rates faster than 14 cm per hr the microstructure showed rods of zinc in a matrix of MgnZnll, while intermediate rates yielded mixtures of rods and lamellae in small groups. The lamellar "grains" were often several millimeters in cross section, but contained small irregular areas which divided each grain into perfect islands 100 or 200 p in diam. Lamellae were parallel to each other throughout the grain in spite of these defects in the structure, Fig. 1. Rods, on the other hand, could only be produced in small groups arranged like fish scales and separated by irregular areas of appreciable thickness, Fig. 2. Alloys Not of Eutectic Composition, With Dendrites. In alloys with 3.1 to 3.35 wt pct ME,-. three-vaned dendrites bf MgzZnll were usually found surrounded by eutectic. At growth rates slower than about 10 cm per hr the dendrites were separated from each other by small areas of both lamellar and rod eutectic, Fig. 3.

Jan 1, 1969

By R. J. Fruehan, F. D. Richardson

Electrochemical measurements have been made of the activity of oxygen in copper and its alloys with silver and tin at 1100" and 1200°C. The galvanic cell used was Pt, Ni + NiO/solid ellectrolyte/[O] in metal, cermet, Pt The results do not support any of the equations so far designed for predicting the activities of dilute solutes in ternary solutions from activities in the corresponding binaries. If, however, a quasichemical equation is used with the coordination number set to unity, agreement between observed and calculated activities shows that this empirical relationship can be useful over a fair range of conditions. SEVERAL solution models have been proposed for predicting the activity coefficients of dilute solutes in ternary alloys from a knowledge of the three binary systems involved. Alcock and Richardson1 have shown that a regular model, and a quasichemical model,&apos; in which the dissolved oxygen is coordinated with eight or so metal atoms, can reasonably predict the behavior of both metal and nonmetal solutes when the heats of solution of the solute in the separate solvent metals are similar. But when this is not so, neither model gives useful predictions unless coordination numbers of one or two are assumed. Wada and Saito3 subsequently adopted a similar model to derive the interaction energies for two dilute solutes in a solvent metal. Belton and Tankins4 Rave proposed both regular and quasichemical type models in which the oxygen is bound into molecular species, such as NiO and CuO in mixtures of Cu + Ni + 0. However, their models have only been tested on systems in which the excess free energies of solution of the solute in the two separate metals differ by a few kilocalories. Ope of the reasons why more advanced models have not been proposed is because few complete sets of data exist for ternary systems in which the solute behaves very differently in the two separate metals. For this reason measurements have been made of the activities of oxygen dissolved in Cu + Ag and Cu + Sn. Measurements on both systems were made by means of the electrochemical cell, Pt, Ni + NiO/solid electrolyte/O(in alloy), cermet,Pt [1] The activity of oxygen was calculated from the electromotive force and the standard free energy of formation of NiO, which is accurately known.5 Before investigating the alloys, studies were made of oxygen in copper to test the reliability of the cell and to check the thermodynamics of the system. Of the previous studies those by Sano and Sakao,6 Tom-linson and Young,7 and Tankins et al.8,7 have been made with gas-metal equilibrium techniques; those by Diaz and Richardson,9 Osterwald,10 wilder," Plusch-kell and Engell,12 Rickert and wagner,13 and Fischer and Ackermann14 have been made by electrochemical methods. EXPERIMENTAL The apparatus employed was the same as described previously,9 apart from slight modification. The molten sample of approximately 40 g was held in a high grade alumina crucible 1.2 in. OD and 1.6 in. long. The solid electrolytes were ZrO2 + 7½ wt pct CaO and ZrO2 + 15 wt pct CaO; the tubes 4 in. OD and 6 in. long were supplied by the Zirconia Corp. of America. They were closed (flat) at one end. In one experiment with Cu + O, both electrolytes were used in the cell at the same time. The reference electrodes inside the electrolyte tubes consisted of a mixture of Ni + NiO. They were made by mixing the powdered materials and pressing them manually into the ends of the tubes, with a platinum lead embedded in them. The tubes were then sintered overnight in the electromotive force apparatus at 1100°C. By sintering the powders inside the tubes (instead of using a presintered pellet9) better contacts were obtained between the electrolyte, the powder, and the platinum lead. Troubles arising from polarization9 were thus much reduced. The electromotive force was measured by a Vibron Electrometer with an input impedence of 1017 ohm; the temperature was measured with a Pt:13 pct Rh + Pt thermocouple protected by an alumina sheath. The couple was calibrated against the melting point of copper. The cermet conducting lead of Cr + 28 pct Al2O3, previously found to be satisfactory9 for use with Cu + 0 was also found satisfactory with Cu + Ag + 0 and Cu + Sn + 0. Superficial oxidation was observed, but it did not interfere with the working of the cell. The reaction tube containing the cell was closed at each end with cooled brass heads and suspended in a platinum resistance furnace. The tube was electrically shielded by a Kanthal A-1 ribbon which was wound round it, and the ribbon was protected by a N2 atmosphere between the furnace and the reaction tube. The cell was protected by a stream of high purity argon which was dried and passed through copper gauze at 450°C and titanium chips at 900°C. All the metals used were of spectrographic standard. Procedure. In studies of the system Cu + 0, be-

Jan 1, 1970

By R. E. Cech, J. H. Hollomon

KURDJUMOV and Maksimova reported experiments with manganese steels and high carbon steels&apos; and with an Fe-Ni-Mn alloy&apos; in which mar-tensite was formed isothermally over a range of temperatures. They found in some cases that mar-tensite formation could be suppressed by rapid quenching to liquid nitrogen temperature. From their microstructural observations of martensite formed isothermally, they concluded that the rate controlling step is nucleation rather than growth. Kulin and Cohen,3 in an attempt to reproduce these experiments, found that with a steel having the same composition as that reported by Kurd-jumov and Maksimova, the transformation to martensite was essentially complete above the temperature range of Kurdjumov and Maksimova&apos;s isotherms. The possible reasons for this disagreement were not considered. Recent papers by Das Gupta and Lement4 and Kulin and Speich5 report the formation of isothermal martensite in a high chromium steel and in an Fe-Cr-Ni alloy, but neither paper can be considered a verification of the original Kurdjumov and Maksimova results. Further, in neither case were the authors able to suppress the formation of martensite entirely. Because of the important bearing the Kurdjumov and Maksimova results have to an understanding of the mechanism of martensite reactions it was felt that an experimental investigation directly concerned with checking the validity of their results was in order. This paper describes the results obtained on the isothermal transformation over the temperature range from —79" to —196°C of an alloy of iron, nickel, and manganese. Experimental Apparatus A 15 lb heat of an alloy containing 73.3 pct Fe, 23.0 pct Ni, and 3.7 pct Mn was melted by induction and cast under argon. The ingot was forged to 1-in. bar and a portion rolled to 1/16x1 1/2-in. strip. This strip was pack-homogenized 300 hr at 1100" in a helium-filled sealed iron tube. The composition after homogenization was 73.2 pct Fe, 22.94 pct Ni, 3.73 pct Mn, 0.05 pct C, and 0.015 pct N. The strips were cut to 1/2-in. width for dilatometer and metal-lographic specimens. Only the center portion of the 11/2-in. strip was used in the present investigation. The dilatometer employed was similar in design to one described by Flinn, Cook, and Fellows." A concentric fused auartz rod and tube assembly with hooks for holding the specimen was mounted so as to transmit the specimen dilation to a 1/10,000 in., 1/10 in. travel dial gage. The dilatometer proper was mounted by means of extension arms to a counterweighted sliding member on a vertical standard. This method of mounting permitted rapid transfer of the dilatometer from the austenitizing furnace to the quenching bath and low temperature chamber. A small electrical vibrator on the dilatometer kept frictional effects of the quartz members at a minimum. The austenitizing unit was a vertical, molybdenum-wound, hydrogen atmosphere furnace maintained at a constant temperature ±3°C by means of constant power input. A 12-in. stainless steel jacketed copper liner having 1/2-in wall thickness acted to equalize the temperature in the hot zone of the furnace. This liner, closed at the bottom end and open at the top to permit entrance of the dilatometer and specimen, was kept filled with dry nitrogen gas. A chromel-alumel thermocouple was placed inside the tube to determine the temperature. The 4-in. dilatometer specimens in the chamber varied less than 1/2° across the specimen length except for a 1 1/20 drop at the end nearest the open end of the furnace. The low temperature isothermal holding bath was a double Dewar arrangement similar to one described by Turnbull7. The outer bath was filled with a refrigerant at a temperature lower than the desired holding temperature. The inner bath was filled with Freon "11" or "12" or a mixture of both, depending upon the holding temperature. This inner bath which tended to be cooled by the outer bath was kept at a constant temperature by introducing a small amount of heat with a manually controlled electric heater. Stirring was accomplished by bubbling dry air through the bath. A Leeds and North-rup type K potentiometer was used to measure the inner bath temperature as indicated by a five element copper-constantan thermopile. The bath temperature was maintained within ±0.2°C of the desired temperature by occasionally adjusting the heater current so as to keep the Leeds and Northrup galvanometer at zero deflection with a constant setting of the potentiometer. Isothermal tests were usually continued for 300 to 400 min and another reading made at approximately 1000 min if the bath, unattended overnight, had not deviated in temperature more than 5°C. Transformation curves are drawn dashed (Fig. 1) through the time region where temperature was not controlled precisely. Experimental Procedure Dilatometer specimens of 1/2x1/16-in. strip were cut to 41/2-in. length and holes were drilled for the quartz hooks with proper spacing to give a 4-in. measured length. A thermocouple consisting of 0.012-in. diameter chrome1 and alumel wires was spot welded to the specimen and threaded between the dilatometer rods to binding posts near the dial

Jan 1, 1954

By P. D. Merica

ALUMINUM and its alloys have been the subject of much investigation, during recent years, in the course of which the principal features of the constitution of most of the binary alloy systems with aluminum have been determined. Except in the case of a few metals-silicon, bismuth, cadmium, lead, zinc, and tin-an aluminum-rich compound is formed in each binary system, which forms a eutectic with the aluminum or its solid solution with this compound. Thus such compounds as FeAl3, CuAl2, Mg4Al3, and NiAl3 are formed, which are found in aluminum-rich alloys of their respective series as eutectics with the aluminum solid solution. These compounds are, in all cases, hard and brittle and their presence affects profoundly the physical properties of the alloys in which they occur. Within the zinc-aluminum system a compound, Al2Zn3, is formed that decomposes at lower temperatures. Silicon and tin each form a simple eutectiferous series with aluminum; bismuth, lead, and cadmium are only partly miscible in the liquid state with it. The extent of the solubility in aluminum, in solid solution, of these compounds or of the elements themselves, in the case of those series

Jan 7, 1919

By A. S. Richardson

AIR conditioning, or air cooling, for the improvement of ventilation in the Butte mines has come into increasing use during the past 10 years. In part, the methods practiced have been described in previous publications of the Institute, but some improvements on earlier methods have been made and a number of new features have been developed. This paper is presented as a record of progress made, and for the sake of completeness describes all general features of the work. The need for air conditioning in the ventilation of mines in the district arises from the fact that the temperature of the ground and mine water has shown a very great increase with increase in mining depth, and has now reached a maximum of slightly over 130ºF. The most difficult part of the ventilation problem is the maintenance of temperature and humidity of a satisfactory standard in the working places, especially on the lower levels. Although ordinary ventilation is adequate to maintain good conditions in most of the working places it is subject to a number of limitations at great depth. Most important among these limitations is that with increase in depth the air becomes heated before it reaches the working places, both by compression from increase in atmospheric pressure and by heat transferred to it from rock at high temperature, so that its capacity for lowering temperatures is greatly reduced before it reaches the operating zone. Increasing depth of mining also increases the distance traveled by the air in its passage through the mine, and this causes a corresponding increase in resistance to air flow, so that there is greater difficulty in maintaining even the same volume in circulation. Thus, in the face of a demand that the ventilating system have a very much greater capacity to remove heat from the mine, the tendency is for that capacity to diminish. The only evident alternatives were (I) the opening of additional air shafts to increase the volume of air in circulation, (2) an extension of the existing system that would be subject to the same limitations, or (3) the adoption of an entirely different method such as air cooling. Fortunately for an economic solution of the problem, the mean annual temperature of the surface atmosphere at Butte is about 40°F., with very low relative humidity in summer, so that there is unlimited natural cooling power at a temperature range adaptable to air-conditioning methods. METHODS Two similar methods of air conditioning are used, as necessitated by service requirements and dependent upon the equipment available. In one, which is the more important and has the greater cooling capacity, water is circulated in a closed circuit, and, alternately, first absorbs heat from warm mine air and then dissipates it in the surface atmosphere by cooling at a cooling tower. The second

Jan 1, 1941

By Edmund Davenport

THE specific aim of this work has been to study certain forms of internal deterioration which occur in tungsten filaments when subjected to high temperatures under various conditions, and to determine the cause of such deterioration. This would naturally lead to a consideration of methods of control or means of prevention of the phenomena. The deterioration was first noticed as a peculiar condition in the grain boundaries of certain tungsten filaments which had been burned? for long periods in lamps. In these cases it was noted that the grain boundaries contained a number of minute black dots which were at first thought to be non-metallic inclusions. It was demonstrated later that these dots or pits, as they were designated, could be readily produced by burning filaments in an atmosphere of flowing hydrogen. This method was convenient and adequate for the purpose, and was adopted for most of the work discussed in this paper. The evidence accumulated to date indicates that these pits are actually small voids between the grains. The purpose of this paper is to present- the information on this interesting subject gathered during a period of about 3 years. As applied to tungsten, the subject appears to be of considerable importance, experience having shown that this pitting ?is frequently associated with poor performance of filaments in lamps. The question has arisen as to whether these intergranular pits are peculiar to tungsten, or if they occur in all metals. If they are found iii all metals, the facts will be of considerable theoretical interest, as the material at the grain boundary plays an important part in most of the current theories of the properties of metals and alloys.

Jan 1, 1927

By H. W. Immolz

The Palo Pinto limestone pools of Jones and Shackelford Counties were defined and almost fully developed during the year. A new Palo Pinto limestone pool was apparently discovered when the K. B. Nowels NO. 1 Pardue, S.F.I. and W. survey, south central Haskell County, was completed for a small well in Palo Pinto limestonc at 3395 to 3421 feet. In Haskell County, Amerada Petroleum Corporation&apos;s C. J. Kleiner, J. M. Cass survey, drilled to the Ellenburger with a total depth of 5607 ft., where it was abandoned. A Bluff Creek sand field of undetermined size was discovered by the Fain-McGaha No. 1 Dawson-Conway, P. G. Holcomb survey, which was chompleted for 37 bbl. at 1496 feet. The Cook field was extended by the Roeser-Pendleton B-113 Cook in sec. 113, E.T.R.R. Co. survey, the well being completed for 510 bbl. from Cook sand encountered at 1545 to 1568 feet. Several shallow pools of minor importancc mere also discovered in Shackelford County during the year. In Jones County the Lewis and the Steffens fields, in block 15, T. and P.R.R. Co. survey, were further developed during the year but the limits of the Steffens field were not definitely defined. The most, important discovery in Jones County was the Guitar field, where most of the wells that had been producing from the Cook sand were deepened to the Hope limestone, a new producing horizon. In Taylor County, the Bowles field, see. 28, B.A.L. survey, was defined arid proved to he of minor importance. The Goldsboro and Novice area, ill northwest Coleman County, continued to hold considerable interest because of the developments near the town of Novice, where new Ieases continued to be opened for production. Nolan County was placed in the ranks of the producing counties when the S. B. Owens No. 1 Tipton, sec. 43, block 19, T. and P.R.R. Co. survey,

Jan 1, 1940

By S. G. Bankoff

INCE1 proposed that electrostatic attraction between oppositely charged particles was responsible for slime-coating. Del Giudice2 postulated the metathetic formation of a cementing compound. Wark3 suggested that prevention of slime-coating was related to peptization of the slime. [ ] In the experiments of Table I the technique employed was essentially that of del Giudice, with the difference that the particle was examined under a film of water rather than dry.4 In general, the polished particle was agitated for 2 min. in a pulp consisting of 12.5 grams of the slime (-200 mesh) and 50 c.c. of distilled water, washed in three baths of distilled water, and examined at 220 diameters with the Leitz Ultropak. Observations of Brownian movement were made at 850 diameters with dark-field illumination. Several of these experiments do not jibe with the metathesis theory. According to published solubilities,5,6 the lead salts of the anions in experiments [c] through g are more insoluble than lead carbonate, therefore should prevent the formation of lead carbonate on the galena surface. In experiment [i] the calcium oxalate, which presumably was on the calcite surfaces, should have permitted the formation of a lead carbonate cement by virtue of its greater solubility. Experiments [j] through m show that the addition of lime accelerates the deposition of quartz onto a galena surface. The writer is unable to postulate a satisfactory cementing compound, according to the metathesis theory, to explain this effect. These experiments led to the conclusion that the metathetic formation of a cement-

Jan 1, 1941

By Charles R. Keyes

During the past decade the genesis of the lead- and zincdeposits of the Mississippi valley has received special attention from many distinguished observers. But their united egorts, instead of settling all disputed questions, have, in many respects, involl-ed the general problem in greater uncertainty than would be thought possible under the circumstances. In place of the harmony of opinion that might be expected, there is unexpected disagreement, largely due to the fact that, instead of giving attention to a possible multiplicity of ore-producing conditions among the different deposits, the attempt has been made to bring all deposits under a single genetic head. To a new observer of the lead- and zinc-deposits of the Mississippi valley, it appears at the outset that all the deposits cannot possibly have had the same genesis. In fact, different modes of origin have been often asserted for the ore-bodies, but the difficulty has been that each writer has referred them either all to one category or all to another, and no intermediate ground has been considered possible. Such a position now appears to be clearly untenable. The opinion that, in the deposits of the region under consideration, the ore-materials represent original depositions, made at the time the rocks themselves were formed, is no longer held by any authority, and therefore need not be considered here. Of late years, a number of writers have attempted to account for the presence of the lead- and zinc-ores on the hypothesis that the metallic materials arose in heated solutions from the

Jan 1, 1902

By H. W. Immolz

The Palo Pinto limestone pools of Jones and Shackelford Counties were defined and almost fully developed during the year. A new Palo Pinto limestone pool was apparently discovered when the K. B. Nowels NO. 1 Pardue, S.F.I. and W. survey, south central Haskell County, was completed for a small well in Palo Pinto limestonc at 3395 to 3421 feet. In Haskell County, Amerada Petroleum Corporation&apos;s C. J. Kleiner, J. M. Cass survey, drilled to the Ellenburger with a total depth of 5607 ft., where it was abandoned. A Bluff Creek sand field of undetermined size was discovered by the Fain-McGaha No. 1 Dawson-Conway, P. G. Holcomb survey, which was chompleted for 37 bbl. at 1496 feet. The Cook field was extended by the Roeser-Pendleton B-113 Cook in sec. 113, E.T.R.R. Co. survey, the well being completed for 510 bbl. from Cook sand encountered at 1545 to 1568 feet. Several shallow pools of minor importancc mere also discovered in Shackelford County during the year. In Jones County the Lewis and the Steffens fields, in block 15, T. and P.R.R. Co. survey, were further developed during the year but the limits of the Steffens field were not definitely defined. The most, important discovery in Jones County was the Guitar field, where most of the wells that had been producing from the Cook sand were deepened to the Hope limestone, a new producing horizon. In Taylor County, the Bowles field, see. 28, B.A.L. survey, was defined arid proved to he of minor importance. The Goldsboro and Novice area, ill northwest Coleman County, continued to hold considerable interest because of the developments near the town of Novice, where new Ieases continued to be opened for production. Nolan County was placed in the ranks of the producing counties when the S. B. Owens No. 1 Tipton, sec. 43, block 19, T. and P.R.R. Co. survey,

Jan 1, 1940

By H. T. Van Ells

The following is a brief description of the cost accounts in effect at the mines of the Anaconda Copper Mining Co. The accompanying chart, Table I., shows the distribution of labor, materials, and redistributable accounts to the various operating and repair accounts. OperatiNG. Development. Owing to the fact that every mine has its peculiarities in formation and methods, the question of arriving at what charges should be included under the head of " Development" is one that has occasioned considerable thought and comment, and in the cost sheet of the Anaconda Copper Mining Co. this account has been sub-divided to show the expenses of breaking ground, tramming, timbering, shaft sinking, up-raising, and cutting stations and skip chutes. It has always been the policy of the company to charge the entire cost of this work to operations monthly, whether the mines are producing or not, also the cost of the opening up of new mines; and only surface construction and additions are charged to capital, excepting original machinery installed for operating pumping plants. Explanations of the charges to the various sub-accounts follow : Breaking Ground.—Work performed in driving cross-cuts from the station, or cross-cuts from the drifts, and diamond-drill work, for the purpose of discovering or developing ore bodies. Tramming.—Cost of tramming waste produced by cross-cuts mentioned above. When waste is hoisted to another level to be used for filling, the charge to this account stops at the station, and when hoisted to surface the charge includes tramming from the collar of the shaft to the dump. Timbering.—Cost of timbering the cross-cuts mentioned above includes the cost of handling and framing such timbers, but does not include the wages of station tenders and top carmen.

Jan 1, 1914