University of Michigan Press, Ann Arbor, Mich. The publications of the various divisions of the University are issued by the Press A large number of scientific treatises and books are listed in the catalogue of the Press but only a few of them are of a nature to be given here. In the Scientific Series, vol 3 should be cited, The geology of the Netherland East Indies, by H A Brouwer; price, $3 plus 15 cents postage. Some of the volumes of the Michigan Academy of Science, Arts and Letters, also issued by the Press, contain papers on geology. Specifically:

Jan 1, 1933

By D. J. McAdam

Results of investigation of corrosion-fatigue of metals at the U. S. Naval Engineering Experiment Station have been presented by the author in four papers.1, 2, 3, 4 In those papers references were given to the work of Haigh in 1917.5 The investigation at Annapolis included a variety of ferrous and non-ferrous alloys. The experiments showed that even slight corrosion simultaneous with fatigue may cause failure at stresses far below the ordinary endurance limit. The experiments also showed that, for most metals, severe stressless corrosion prior to fatigue is much less damaging than even slight corrosion simultaneous with fatigue. The term "corrosion-fatigue" was restricted to mean the simultaneous action of corrosion and fatigue. The combined effect of corrosion followed by fatigue was called "prior-corrosion fatigue." A stress-cycle graph representing corrosion-fatigue is a curve approaching a horizontal asymptote, the ordinate of which may be called a "corrosion-fatigue limit." To avoid confusion in later discussion, the term "endurance limit" will be restricted to mean the fatigue limit obtained by tests in air with specimens as free as possible from stress concentration and from corrosion. The cndursnce limit as thus obtained presumably represents an inherent property of the metal.

Jan 1, 1929

By D. J. McAdam

Results of investigation of corrosion-fatigue of metals at the U. S. Naval Engineering Experiment Station have been presented by the author in four papers.1, 2, 3, 4 In those papers references were given to the work of Haigh in 1917.5 The investigation at Annapolis included a variety of ferrous and non-ferrous alloys. The experiments showed that even slight corrosion simultaneous with fatigue may cause failure at stresses far below the ordinary endurance limit. The experiments also showed that, for most metals, severe stressless corrosion prior to fatigue is much less damaging than even slight corrosion simultaneous with fatigue. The term "corrosion-fatigue" was restricted to mean the simultaneous action of corrosion and fatigue. The combined effect of corrosion followed by fatigue was called "prior-corrosion fatigue." A stress-cycle graph representing corrosion-fatigue is a curve approaching a horizontal asymptote, the ordinate of which may be called a "corrosion-fatigue limit." To avoid confusion in later discussion, the term "endurance limit" will be restricted to mean the fatigue limit obtained by tests in air with specimens as free as possible from stress concentration and from corrosion. The cndursnce limit as thus obtained presumably represents an inherent property of the metal.

Jan 1, 1929

By C. K. Leith

QUOTING from Dr. Richard T. Ely:1 "Conservation, narrowly and strictly considered, means the preservation in unimpaired efficiency of the resources of the earth; or in a condition so nearly unimpaired as the nature of the case, or Wise exhaustion, admits. And broadly considered, it means more than the word itself implies, for it naturally includes an examination of methods Whereby the natural inheritance of the human race may be improved; and still more broadly considered, and as used in popular discussion, it includes a treatment of the effects of productive conservation methods upon distribution. "Conservation means a sacrifice of the present generation to the future generations Whenever it is carried too far. There is a sharp limit to the economic sacrifice that we may reasonably ask the private person to make for even the present Welfare, and the limit is still sharper when we come to consider the interests of future generations." In a paper on the iron ores of America, presented to the Pan-American Scientific Congress at Washington, I have emphasized the fact that the reserves of iron ores in the two Americas are enormously in excess of the requirements of the present generation, in fact, so large that no shortage is to be anticipated for many generations in the future; that a large part of the value of iron ores is put into them by man's efforts to make them available. This fact is fundamental for the intelligent consideration of- policies of conservation as applied to iron ore. As I interpret it, this fact makes it practically unnecessary that the present generation should make any especial sacrifice for future generations in the way of conservation of its iron-ore resources. Even if we were disposed to look forward to a period of 100 or 200 years, with a view to insuring the welfare of the people living at that time, it is doubtful whether any procedure we could now formulate would materially help them in the matter of iron ores, so large are the reserves available. In order that an appeal for conservation may be effective it must obviously favor the welfare of the present or immediately following generations; it must promise benefits to general and individual welfare during a period within the range of comprehension of the average man.

Jan 2, 1916

By F. E. Wood

Since the earliest discoveries of oil in the Rocky Mountain area the spirit of cooperation in drilling and production programs has prevailed. There has scarcely been a field which has not been developed in an orderly manner through mutual agreement between competitive operators. An appreciable saving has resulted, as many unnecessary wells have been eliminated. We have unit operation plans and agreements which were developed at an early date. Rock River, found in 1918, has been a unit operation. One of the first prorate agreements ever attempted was made in Salt Creek in 1921. Teapot, first developed in 1922, has been a unit operation; the lessee, the Government, and the lessor, one operator. South Casper Creek, found in 1918, has been developed as a unit. Rex Lake, found in 1923, is a unit operation. The list might be extended materially but it serves to indicate that the Rocky Mountain region enjoyed the fruits of unit operation at an early date. It is concluded from this unitization study in the Rocky Mountain region that there is an appreciable saving in both development and production costs as well as the elimination of waste of a natural resource. Certainly, when unit operation conserves an irreplaceable natural resource as well as capital, any legal or political impediment to its successful development will be overcome. If one company supervises the operations in one field, it appears to be a unit operation. This may not be true if the lands involved have been leased from a great number of lessors. Royalty holders create a most intense competitive operation. The Rocky Mountain region has its full quota of such diversified interests. The original study calls for consideration of two types of fields, unit and near-unit operation. This Committee has felt that if an agreement of any character has brought about a saving it is an approach to unit operation. The fields have been classified into four types: 1. Unit Operation.—Any field whereby the competitive drilling-drainage feature is or will be absent in the development and operation of the pool.

Jan 1, 1930

By L. C. McCabe

THIS paper is a progress report on a study, of the distribution of the banded ingredients (Figs. 1 and 2) in- Illinois screenings and the method of determining their distribution. Proximate analyses and screen tests1 have been reported and a further report on the washability characteristics of the screenings is in preparation. The microscopic study of the screen-ings is not yet far enough advanced to permit a conclusive report on the effect of mining, screening and washing on the distribution of the banded ingredients in the coals of Illinois. However, considerable fundamental data-have been collected as a background for the screenings investigation and for a proposed study of fuels composed of known quantities of vitrain, clarain and fusain, the three common banded ingredients of Illinois coals. These fundamental data and the preliminary information now available from the microscopic study of screenings are broadly indicative of the reaction of the coals to the physical processes affecting them in mining and preparation. Proximate analyses of samples of vitrain, clarain, and fusain from several Illinois mines have been published 2, but those given in Table 1 serve to show the differences that are apparent in proximate analyses. The vitrain samples are consistently low in ash, and the unit-coal value is uniformly lower than in clarain. The average .fuel ratio (F.C./V.M.) of the vitrain samples in the table is 1.57-whereas the clarain average is 1.42. The fusain analyses vary considerably in ash and moisture. In the two samples from this mine the moisture values range from 8.99 to 22.80 and the ash from 4.86 to 16.91 per cent. Fusain has higher fixed carbon than either vitrain or clarain but the percentage is erratic from sample to sample.

Jan 1, 1936

Discussion of the paper of PHILIP W. HENRY, presented at the New York meeting, February, 1915, and printed in Bulletin No. 97, January, 1915, pp. 23 to 30. C. ,E. GRUNSKY, JR., San Francisco, Cal. (communication to the Secret ary*).-The difference of opinion of engineers on the subject of depreciation is justified, to some, extent, by the many viewpoints from which such a subject can be considered when applied to properties of widely differing physical characteristics. Mr. Henry takes up the subject of depreciation as applied alone to oil properties, and in doing so makes a clear distinction between amortization and the repair or renewal requirement. After carefully reading the paper the purpose of its author in suggesting a "depreciation" reserve or fund to keep the property at a constant value does not seem clear. As shown by Mr. Henry, the depreciation element as compared with the operating expense per gallon of oil is very large because of the comparatively short life of the oil properties, and it is also evident that such a "depreciation" fund would in a short time contain a very large amount of money. It seems desirable and permissible in income-tax matters to take into account the depreciation of property and to separate from the income such money as is necessary to amortize the invested capital to an extent warranted by the depreciation. However, it does not seem either necessary or desirable to create a large fund which will in time approximate the entire invested capital and which may he invested by the directors, as Mr. Henry suggests, "in the property itself or in outside securities." This method seems cumberome and liable to offer in the reinvestment of such a fund temptations to a directorate that might show more devotion to its own interests than that of the stockholders. A reserve fund is very frequently desirable in mining and oil operations, but to keep up a fund of this magnitude or to reinvest it in outside securities does not seem desirable from a stockholders' standpoint. The. money withdrawn from the receipts to be placed in the depreciation fund (not including replacements and the drilling of new wells necessary to keep up the productiveness) should he returned to the stockholders of the company, not as dividends, but as an amortization of the invested capital.

Jan 5, 1915

By George Rice

WHEN miners in the interior coal fields of the United States began the practice of blasting the coal without undercutting, or what is known as "shooting off the solid," many explosions resulted, some of them of great extent and 'violence, and attended with large loss of life. One of the means adopted for preventing this large loss of life, though not preventive of explosions, was to employ shot firers to discharge the shots when all the other employees had gone out of the mine at the end of the day's shift. This system still prevails in most of the Central and Southwestern mines. Following the disaster at Winter Quarters mine, Utah, May 1, 1900, in which 200 lives were lost, a system of firing shots electrically from outside and when the men were out of the mine was adopted at the mines of the Utah Fuel Co.1 This system has also been used in France in certain mines that are subject to instantaneous outbursts of carbonic acid gas. These outbursts generally occurred at shot-firing time, on account of the blasts releasing the gas held in crevices under high pressure. The system was also adopted at a number of other mines in Utah, at the Cokedale mine, Colorado, at the Dawson mines, New Mexico, and in some mines of the Tennessee Coal, Iron & Railroad Co. in the Birmingham Ala. district; and more recently in certain mines in Iowa and Kansas. At first there was considerable trouble from misfires, and in a few instances from premature firing, while men were in the mine, through the shot-firing lines becoming crossed with power lines. Fortunately, however, no loss of life resulted from such premature firing within the knowledge of the writers, and latterly this danger has been reduced to a minimum by certain measures of precaution. The proportion of misfires, or failures of individual shots to fire, has also been reduced to a very small

Jan 10, 1914

By E. S. Fisher

GRAIN coarsening implies a discontinuous type of grain growth during which a few grains in a fine grained recrystallized matrix grow to large grain sizes at the expense of the matrix. Studies of this phenomenon in various metals1,2 indicate that grain coarsening may result when continuous grain growth in a fine grained matrix is inhibited by either a dispersion of very fine inclusions or by a strong texture. In the former case a period of annealing time exists prior to grain coarsening during which grain growth inhibition is gradually de- creased by dissolution or coalescence of the dispersed inclusions. This mechanism can be made to occur in uranium during anneals at high a phase temperatures. ' A study of some of the factors influencing the kinetics of grain coarsening and the coarse grain sizes in a uranium has led to a method for preparing a uranium single crystals. Previously such single crystals containing considerable substructure were prepared at this laboratory by a phase change method, similar to that described by Cahn.3 Attempts to prepare more perfect single crystals by strain-anneal techniques were unsuccessful. Cahn3- as reported his attempts to apply such techniques to uranium. He proposed that the failure of strain-anneal techniques is basically due to the many twins which

Jan 1, 1958

By Arthur L. Flagg

The Elk City mining district of Idaho occupies a position near the geographical center of Idaho county, a region of moderate elevation in the western foot-hills of the Bitter Root mountains. The district comprises an area of approximately 350 Sq. miles, bounded on the west by the Newsome district and on the south by the Dixie and Oro Grande districts. There are no mining districts to the north or east. Elk City, the principal town and the seat of the mining office for the district, is situated in a hydrographical basin surrounded by low hills. The elevation is 4,200 ft. above sea-level. Through this basin flow Elk Creek, Red river, and American river, which unite west of town to form the south fork of the Clearwater. The one township is set out from the Bitter Root Forest Reserve. Though a railroad starting from the Stites terminus of the Clearwater Short Line of the Northern Pacific railroad has been under consideration for some years, the camp is yet without railroad facilities. The projected road would follow the south fork of the Clearwater on easy grades, but would be very expensive to build and maintain. While such a road would greatly benefit those who are now operating in the camp, and in a sligh degree stimulate interest in its possibilities, there is hardly business enough to warrant its construction. At present all supplies and equipment are hauled in by wagon from Stites, a distance of 58 miles, over a wagon road constructed by the State in 1904, following in the main the old Nez Perce trail. While this is not a bad road, it is not all that might be desired. Starting at Stites at an elevation of 1,327 feet above sea-level, the road runs through low hills to Clearwater, a distance of 10 miles. In the next 16 miles the climb is steady until the Mountain House is reached, which is near the summit of Mount Pisgah. This is the highest point passed on the road, having an elevation of 6,500 ft. From the

Jan 1, 1914

By D. B. Kibler

THE Florida hard-rock field extends from Suwanee and Columbia Counties in northwest Florida to south of Croom, Florida, in Hernando County. This area is approximately 100 miles long and varies from 2 to 30 miles in width. Florida hard-rock phosphate was discovered at Hale Springs, about one mile northwest of the town of Dunnellon, Marion County, in the year 1888, by Albertus Voight, who lived within a few hundred yards of the spring. Soon after this discovery there was a great influx of land speculators and wildcat operators into the vicinity of Dunnellon. A few years later phosphate was found in Alachua, Levy, Citrus and Hernando Counties, and a great number of small crude plants were built from Newberry, Alachua County, all the way to Croom, Hernando County. Phosphate was found in many places as "outcrops." Looking for outcrops was the first method used by the early prospectors in searching for deposits. Several years passed before any systematic method of prospecting was used. EARLY MINING The early method of mining hard-rock phosphate was with picks and shovels, wheelbarrows, mules and wagons. The pick-and-shovel method was used altogether until about 1900, when some of the larger operators began to use railroad-type steam shovels of from ½ to 1-yd. capacity. Picks and shovels, with negro labor loading the phosphate ore (called "matrix") into wooden side-dump skip-cars, was continued until about 1907. From the discovery of hard-rock phosphate until approximately 1905, overburden was removed with mules and scrapers. At some places, the overburden was loaded into side-dump skip-cars by negro laborers and the cars were then pulled up an incline with a steam hoisting engine. The maximum depth of overburden that could be economically removed by hand labor, mules and scrapers was approximately 15 feet. About 1905 one of the companies erected a producer-gas powerhouse near Dunnellon and generated its own electricity and about the same time the larger companies began using hydraulic methods for the removal of overburden. From the year 1888 through the year 1939, approximately 75 companies were operating at one time or another in the hard-rock territory, on approximately 500 locations. The hard-rock deposits are more irregular and have higher mining costs than the pebble-rock deposits, therefore they have not been competitive in the domestic market, but because of the higher grade of the hard rock it is in demand for the export trade. Discovery of phosphate outside of the United States has made it increasingly difficult in recent years for the hard-rock companies to survive, so today only three companies are operating. These

Jan 1, 1941

By E. H. Jr. Dix

THE success of the Charpy impact test in the steel industry has led those interested in aluminum alloys to investigate the possible applica¬tion of this test to aluminum and its alloys. In this paper are set forth the results of a few preliminary tests made at the Lynite Laboratories of the Aluminum Manufactures, Inc. In order to study more thor-oughly the significance of the Charpy test, slow-bending tests have been made duplicating the arrangement of the impact machine. Tests have been made on both notched and unnotched specimens of a series of copper-aluminum alloys. APPARATUS The standard American-made Charpy impact machine delivering a blow of over 200 ft.-lb. was- much too large to test aluminum-alloy specimens of the same type used for steel, so that it was necessary either to adopt a larger specimen or to have a special light-weight hammer made. Since there is no known relation between specimens of different sizes, even though geometrically similar, it was decided to adhere to the 10 by 10 mm. specimen. Accordingly, Sauveur and Boylston, the American makers of the machine, were asked to construct a special light-weight pendulum adapted to their standard machine, this pendulum to have one-tenth the capacity of the standard. The writer wishes here to acknowledge his indebtedness to Mr. H. M. Boylston for the personal interest and care exercised in constructing this pendulum. The machine with, the light-weight hammer in place is shown in Fig. 1. It is mounted on a concrete foundation with the concrete covering the flange on the base of the machine. Vibration is further prevented by four 5/8 -in. (15.8 mm.) foundation bolts. The large standard hammer shown against the wall was also used for some of the unnotched bars that requited more than 20 ft.-lb. to rupture.

Jan 4, 1920

By J. H. Richards, G. Derge, W. Peifer

A WIDE Variety of metallurgical defects in steel have commonly been attributed to the presence of excessive amounts of hydrogen. These defects include flakes in rails and forgings, cracks in welds, and blisters in enameled ware, They have been related to hydrogen largely by circumstantiat evidence because the proper sampling and analysis of steel for hydrogen has been known to be difficult and because no general agreement has existed with regard to the relative suitability and accuracy of available methods. The need for a direct approach to these problems has been widely recognized. This general situation has been well described in the publications of the British committee on the Heterogeneity of Steel Ingots,' and current approaches to the problem were reviewed in a recent symposium of the AIME.I2 The plans described by the present authors at that meeting have now matured satisfactorily and will form the basis of this paper. The principal object of this paper will be to describe the methods of sampling and analysis which have been developed and to illustrate the usefulness and limitations of these methods by citing their application to a specific problem, The first problem selected for investigation was the behavior of hydrogen in rail steel. This was chosen because the occurrence of shatter cracks in rails has received a great deal of study over a long period of time. The defect can be controlled by the expensive procedure of slow in However, it may be hoped that a better understanding of the factors influencing the hydrogen content of rails will lead to a more efficient control of this problem. Rails provide a good starting point for a more general study of hydrogen in steel because they provide a cross-section large enough to develop cracks, Yet small enough for convenient handling and sampling. Rails were also selected because they arc made from plain carbon steel and it was felt that the initial work should not be complicated by the effects introduced by alloying elements. The considerations which determined the original planning of this study should be reviewed. The inherently complex nature of most hydrogen problems requires that a large amount of data must be collected for any particular case. This in turn means that any analytical procedure should be as rapid and simple as possible. The same objective of speed is indicated by the fact that it may finally become desirable to use hydrogen analysis in process control. It is also known that hydrogen is highly fugitive and that any procedure which facilitat~s early analysis of the sample without prolonged or irregular storage has distinct advantages. The most important previously reported methods of analysis may be classified into three general groups: (I) Vacuum fusion, (2) Vacuum extraction (without melting), (3) Total combustion.

Jan 1, 1949

By C. M. Loeb, T. E. Norman

THE use of ball, rod and tube mills for grinding ore, cement and other materials has grown so rapidly during the past forty years that the world's annual consumption of ferrous grinding media for these mills is now estimated to be between one half million and one million tons per year. Ferrous grinding balls constitute the major portion of this tonnage. Obviously they represent sufficient value to justify thorough studies of the factor sgoverning their performance. The selection of grinding balls is governed principally by: I. Quality (wear resistance, impact resistance, soundness, and the like). 2. Sources of supply and delivered cost. 3. Grinding characteristics or efficiency in the ball mill. This paper deals principally with the quality of ferrous grinding balls. In the study of these factors certain data relative to the fundamental nature of ball wear in ball mills have been obtained. These data are also presented and discussed briefly. THE DEVELOPMENT OF A SUITABLE WEAR TEST A study of the fundamental factors governing the quality of grinding balls has been hampered seriously by the fact that a competent test has, in the past, involved the purchase of several hundred tons of balls of a specific type which were then run in one or more ball mills for a period ranging from several months to several years' duration. Often, during the period of test, it became necessary to change operating conditions or the character of the ore fed to the test mill with the result that the rate of ball consumption changed and the test figures became of little value. Under such circumstances, progress in the development of better grinding balls, has been necessarily slow. Economic factors and variations in the quality of balls produced by different sources of supply generally make it necessary for each mill operator to determine for himself the most suitable type of balls for his mills. In our own ball mill grinding operations at Climax, Colo., we were faced with this problem. After we had run a few large scale wear tests at considerable expense we decided to investigate the possibilities of a small scale wear test which would be capable of testing numerous types of balls within a relatively short time. The most important requirement of any test is, of course, that it give results which can be used to predict accurately the wear in full scale operations. It was. known that Ellis and his associates1.2 had developed a method of testing grinding balls by small scale tests run at the Ontario Research Foundation. Ellis' method of testing was used as a starting point in our investigations. In the course of our tests a number of modifications of the original method were found to be desirable so that, by an evolutionary procedure, a method of small scale

Jan 1, 1948

By G. Derge, W. Peifer, J. H. Richards

A WIDE Variety of metallurgical defects in steel have commonly been attributed to the presence of excessive amounts of hydrogen. These defects include flakes in rails and forgings, cracks in welds, and blisters in enameled ware, They have been related to hydrogen largely by circumstantiat evidence because the proper sampling and analysis of steel for hydrogen has been known to be difficult and because no general agreement has existed with regard to the relative suitability and accuracy of available methods. The need for a direct approach to these problems has been widely recognized. This general situation has been well described in the publications of the British committee on the Heterogeneity of Steel Ingots,' and current approaches to the problem were reviewed in a recent symposium of the AIME.I2 The plans described by the present authors at that meeting have now matured satisfactorily and will form the basis of this paper. The principal object of this paper will be to describe the methods of sampling and analysis which have been developed and to illustrate the usefulness and limitations of these methods by citing their application to a specific problem, The first problem selected for investigation was the behavior of hydrogen in rail steel. This was chosen because the occurrence of shatter cracks in rails has received a great deal of study over a long period of time. The defect can be controlled by the expensive procedure of slow in However, it may be hoped that a better understanding of the factors influencing the hydrogen content of rails will lead to a more efficient control of this problem. Rails provide a good starting point for a more general study of hydrogen in steel because they provide a cross-section large enough to develop cracks, Yet small enough for convenient handling and sampling. Rails were also selected because they arc made from plain carbon steel and it was felt that the initial work should not be complicated by the effects introduced by alloying elements. The considerations which determined the original planning of this study should be reviewed. The inherently complex nature of most hydrogen problems requires that a large amount of data must be collected for any particular case. This in turn means that any analytical procedure should be as rapid and simple as possible. The same objective of speed is indicated by the fact that it may finally become desirable to use hydrogen analysis in process control. It is also known that hydrogen is highly fugitive and that any procedure which facilitat~s early analysis of the sample without prolonged or irregular storage has distinct advantages. The most important previously reported methods of analysis may be classified into three general groups: (I) Vacuum fusion, (2) Vacuum extraction (without melting), (3) Total combustion.

Jan 1, 1949

By R. W. Raymond

Jan 1, 1905

By Danforth R. Hale, R. E. Blair

Minerals for electronic and optical uses divide easily into two sections: (1) quartz and (2) minerals other than quartz. Quartz Quartz, having a great usefulness discovered by the radio communication enthusiasts about 1918, has become a subject of amazingly expanded interest in the US over the past decade as a man-made mineral and a multimillion dollar crystal-growing business. An economic summary of the commercial growing of quartz crystals has a place in a handbook directed to the mineral engineering industry when it is remembered that quartz crystals have long been an important commercial mineral, and that the raw material for "cultured quartz"-that is to say, quartz crystals grown through the ingenuity of man-is still natural quartz. Nearly all the natural crystals come from Brazil. The larger pieces which meet rigorous standards of quality are used for electronic and, to a lesser extent, optical components. Smaller pieces and fragments are used for vitreous silica. The need for high quality material in quantity led to US government-sponsored research programs in the 1940s that have resulted in the factory growing of beautiful crystals of prescribed shape, size, and quality. The development of the cultured quartz crystal is typical of man's success in adapting the product of the mine to increasingly sophisticated uses. A remarkable achievement perhaps, but foreshadowed by experiments in 1908 by Giorgio Spezia (1908), an Italian geologist studying the relative effects of temperature and alkaline environment on the solubility of quartz. Modern radio equipment is most often controlled as to frequency by the presence in the circuit of a separately added "crystal"-the 1918 discovery responsible for the existence and growth of the quartz industry. The "crystal" is quartz, but this component is a carefully oriented and prepared slice from a crystal, but not a crystal as recognized by a rock hound or seen in a museum. How quartz operates to control frequencies is not a proper subject for a handbook on industrial minerals, and references should be consulted (Cady, 1964; Mason, 1964). Quartz belongs to that class of materials called dielectrics: those that do not conduct an electric current but permit electric fields to exist and act across them. Quartz shows the "piezoelectric effect," which means that when a quartz plate is mechanically deformed against its natural stiffness, one of its surfaces becomes negatively charged, the other, positively charged. When the plate is released from the stress quickly, the charges disappear as the plate regains its original shape, but because of mechanical momentum the plate deforms in the opposite direction (to a lesser amount) and the surfaces correspondingly become charged in the opposite direction. By coating the two surfaces thinly with metal and attaching flexible wires, these charges may be brought into an electronic circuit. If the surfaces are suddenly electrically charged by movement of current through the wires, the "converse piezoelectric effect" occurs -the plate deforms. Carry the thought further and it is realized that an alternating current flowing through the wires responds to the mechanical oscillation of the plate and is keyed to this oscillation. By controlling the thickness of the plate its mechanical vibration frequency can be varied through a wide range. One type of quartz plate, called the AT-cut, having a precisely defined orientation with respect to the crystallographic axes of the crystal, vibrates on a microscopic scale much as a book would deform when placed flat on a table and the top cover moved parallel back and forth with the hand. There are at least 17 other orientations which have been studied, some of

Jan 1, 1983

By Alphonse C. Van Besien, Arcy A., L. T. Larson, D&apos Shock, J. W. Peters, Ted H. Eyde, Dermot Ross-Brown, David L. Campbell, W. W. Dudley, John P. Bunch

Over the last several years, unfavorable economic and political pressures on open-pit mining have placed the industry in a generally defensive position. As a consequence, there have been changes in the traditional organizational and production methods to increase operating efficiency. For example, staff groups that were once used almost exclusively for production support are now being organized as mining/environmental specialists. These specialized groups are responsible for obtaining mining permits and insuring compliance with existing permit requirements. Permit issurance and renewal continues to grow as a major budget item in open-pit operations.

Jan 2, 1977

By Robert E. Hoffman, John B. Hudson

The self-diffusion coefficient of pure lead has been measured at five pressures between atmospheric and 40 kb. over a temperature range of about 150°C near the melting point at each pressure. Measurements were made using a radiotracer technique, samples being sectioned electrochemically after the diffusion anneal to determine the diffusion penetration curve. Pressure was applied in a "belt" type pressure device similar to that used by Hall et al., in the diamond synthesis. The self-diffusion coefficient, D, can be represented by an equation of the form at constant pressure, and an equation of the format constant temperature. An apparent correlation between the effects of pressure on self-diffusion and on the melting point of the material observed by Nachtrieb et al., at pressures below 10 kb. was found to be only approximate as measurements are carried to higher pressures. OVER the course of the past 30 years a large number of studies1-' of the rate of atom movements in solid metals have been carried out. These studies have in general been aimed at increasing the understanding of the detailed atomic process by which atom movements in metals can take place. The largest portion of these studies consisted of measurements of the self-diffusion coefficient, D, as a function of temperature. From such studies con- siderable information regarding the energetics of the motive process has been deduced. Recently such measurements have been extended to the pressure dimension. However, the existing work in this area is scanty and has in the past been limited to the pressures attainable in oil or gas bombs—i.e., up to about 10 kilobars (kb). In the present work, the self-diffusion behavior of pure lead has been investigated using the "belt" type high-pressure apparatus designed by Hall7 over a pressure range from atmospheric to 40 kb at temperatures extending over about a 150°C range close to the melting point at each pressure.

Jan 1, 1962

By H. Le Chatelier

SILICA brick are indispensable in the manufacture of steel because they alone are able to withstand the high temperature of regenerative furnaces. All attempts to replace silica brick by other refractory materials for this purpose have failed, but the reason for this failure has remained obscure; we shall give an explanation later in this paper. Before the war, silica brick employed in France came principally from abroad, for which reason, since the beginning of hostilities, certain French steel works have been seriously handicapped. Our attention was first directed to the question by M. Bred, Engineer of the Teil Works. With him, we began certain investigations, at first using our laboratory and the furnaces of neighboring steel works. The larger part of our experiments, however, have been made in the laboratory of the Faculty of Sciences at the Sorbonne. For the heating of our samples, we are deeply obliged to MM. Charpy, Yeatmann and Guérineau. In undertaking these studies, our first aim has been to render assistance to French industry, by indicating, as precisely as possible, the necessary conditions for the manufacture of high-grade brick; but at the same time we have intended to give an example of the manner in which scientific methods may be put to practical application in the solution of industrial problems. Although our work has been confined to samples of only a few grams, we are nevertheless convinced that our information can be directly utilized by brick-works of which the output is measured in thousands of tons

Jan 9, 1918