By L. R. Budrow, R. T. Mishler

The Lucky-Tiger mine is a silver-gold property, situated at El Tigre, in the northeastern part of Sonora, Mexico, at an elevation of 6000 ft. in the Sierra Madre Mountains. It is 30 miles by wagon road from the Esqueda station on the Nacozari railroad. Since its discovery in 1903, the mine has produced forty million ounces of silver. The ore has averaged 40 oz. silver and 0.25 oz. gold per ton. Copper, lead and zinc have been of minor importance, having averaged 0.4 per cent., 1.1 per cent., and 1.5 per cent., respectively. The richness of the ore, combined with its occurrence in narrow veins, required the use of the more expensive methods. of mining. Geology Wall Rock The wall rock is rhyolite and rhyolite tuff, both of Tertiary age. In rare instances, post-mineral andesite dikes have been intruded along the veins. In the upper part of the mine, the walls were fairly solid. On the lower levels, the walls are usually cither kaolinized and soft or silicified and fractured, both conditions requiring closely filled stopes or much timber. Veins The veins have been deposited along fracture planes in the volcanics. There are three principal veins, about 600 ft. apart, all striking nearly north-south and dipping steeply to the west. Table 1 records the approximate dimensions and assay of the veins. Although the average

Jan 1, 1925

By Van Der Muelen P. A.

SOME time ago, the writer received from W. 0. Borcherdt, Manager of the, works of the Bertha Mineral Co. at Austinville, Va., several specimens of a dense yellowish slag-like material, containing cavities showing clear needle-like crystals, and representing a product formed by the fumes of zinc oxide and basic lead sulphate from the oxide furnace, attacking the firebrick lining of the flues. The matrix, which is of a greenish-yellow color, is made up chiefly of an amorphous glass, carrying numerous crystals, the latter being well-defined, clear, and transparent, but colored a very light yellow by small amounts of ferric oxide. A number of the crystals were carefully separated from the matrix and tested with the blowpipe. They have a fusibility of about 2, yield a globule of lead and a coating of lead oxide before the blowpipe on charcoal, and contain some zinc. Their hardness is 5 to 6. 1 Fig. 1. Under the microscope the crystals appear to be made up of a prism, with narrow faces, and a fairly large pinacoid, but unfortunately show no terminal faces (Fig. 1). Between crossed nicols they gave parallel extinction in. the three planes containing the crystallographic axes, and are therefore orthorhombic. The index of refraction is high. A number of the best crystals were measured on the reflection goniometer, the angles given below representing the average of measurements made on different individuals. mm = 46° 52' mb = 66° 34' a:b:c = 0.4334:1 :?

Jan 5, 1917

By Frederick K. Allgaier

As part of an ongoing research program, the Bureau of Mines, U.S. Department of the Interior, is monitoring surface subsidence over six longwall panels at three Utah coal mines. These sites are characterized by mining depths of 244 to 610 meters (800 to 2,000 ft .), thick and massive sandstone layers in the overburden strata, multiple seam mining, extraction heights of approximately 1.8 to 3 meters (6 to 10 ft.), and rugged surface topography. Maximum subsidence, angle of draw, timing relative to mining, horizontal strain, and rate of subsidence development are being determined and correlated with mining and geologic variables. Results to date indicate the maximum vertical subsidence over the monitored panels ranges from 0.6 to 0.9 meters (2 to 3 ft.). The major factors controlling the amount of subsidence are the panel dimensions and the status of adjacent panel mining. Only minor surface cracking at the panel ends was evident at any of the sites. In all cases, there was a time lag of several months between the start of mining and subsidence at the surface. As subsequent panels are monitored and additional data become available, better estimates of the effect of various site characteristics on the subsidence will be possible. Ultimately, improved prediction capabilities will allow mine operators in the West to evaluate the potential for subsidence-related damage which could affect the current or future land use above the mine.

Jan 1, 1982

By J. H. Keeler

QUESTIONS raised during earlier investigations of the preferred orientation in titanium1 and zirco-nium sheet led to the examination of the rolling and annealing textures of beryllium and hafnium sheet. Since the c/a ratios are 1.568 and 1.584, less than that of ideal close packing, 1.633, it would be expected that the preferred orientations would be similar to those exhibited by zirconium and titanium. This was found to be true. However, in several regards the orientations observed for beryllium differed from those reported by Smigels-kas and Barrett4 and so are given here. The okientations for hafnium are presented since only the cold-rolling texture has been reported in the unclassified literature. The pole figures were determined by transmission using an X-ray spectrogoniometer with copper Ka radiation and the automatic pole-figure recorder designed by Geisler described previously.6 The intensity units in the pole figures in this case are only arbitrary since calibration against a random sample of the same material was not considered necessary for the original purpose of the examination. The beryllium sheet, cold-rolled from 0.036 in. to 0.006 in., a reduction of about 84 pct, exhibited a split texture with the [1010] direction in the rolling direction as shown in Fig. 1. The same specimen annealed in vacuo for 1 hr at 1000°C showed no change in orientation. These textures

Jan 1, 1959

By Alan T. Gorton, T. L. Joseph, Gust Bitsianes

High-temperature X-ray diffraction techniques were used to determine thermal expansion coefficients of iron and its oxides. Lattice parameters of a and iron, wiistite, magnetite, hematite, and goethite were determined and plotted as a function of temperature. From these results, the true and mean linear thermal expansion coefficients were calculated. In the case of noncubic crystals, the expansion coefficients were determined along each of the crystallographic axes. The effect of the magnetic transformation on lattice parameter was measured for a iron and magnetite at their respective curie temperatures. COEFFICIENTS of expansion for iron and its oxides were determined from the temperature dependence of their lattice parameters. From these data, the true linear coefficients were derived by means of the formula: at =[(l/ao )(dao/dt)] [1] where at is the true linear coefficient of expansion, a, is the lattice parameter in angstrom units, and all variables are referred to the temperature, t, in OC. Thus the true expansion coefficient represents the instantaneous change in lattice parameter on a unit basis and at a particular temperature. A second expansion coefficient is also often used. It is termed the mean linear coefficient and is defined in the following way: am = [ao(t) - ao(O)]/ao(0) l [21 This coefficient represents the average change in lattice parameter on a unit basis but at a specified parameter length, ao at O°C, and over a specified temperature range,1 to 0°C. Generally the true co-

Jan 1, 1965

By W. L. Chen

The Batac jig was first introduced in the US for fine coal cleaning in 1973 (Tackett, 1977; Hake, 1976). Since then, a total of six such jigs of various sizes have been installed in five US plants for a total capacity of 2346 t/h. The raw coal size ranges from 19 mm x 0 to 9.5 mm x 0-fraction sizes previously fed to heavy medium cyclones, Deister tables, or water only cyclones. Growing interest in the Batac jig as a replacement for the above equipment is due to the following reasons: • Unlike heavy medium cyclones, no magnetite is required. As a result, the operating cost of the plant is reduced. • The compactness of equipment is unique on a unit ton per hour basis as compared to other equipment. • Solid state electronic control of jig stroke length, frequency, and jig bed depth makes the equipment highly efficient. Installations of Batac jigs in the US as of June 1980 are shown in [Table 1]. Use of the Batac jig is even greater outside the US (Anonymous, 1980; Chen, 1980). Its use is not limited to fine coal but is applied to coarse coal as well, with 102 mm size in the feed (Zimmerman, 1975). In countries where consumption of magnetite associated with the heavy medium system of coal cleaning is considered a waste of iron ore resource, the Batac jig is regarded as the primary choice in the selection of cleaning equipment (Chen, 1980).

Jan 1, 1981

By G. W. Elger, H. E. Bell, J. E. Tress, J. B. Wright

This paper describes laboratory techniques and subsequent results of US Bureau of Mines (USBM) research to produce chlorination-grade feed- stock from an abundant, low-grade, domestic, rock ilmenite ore. The research is part of the Bureau effort to devise technology that may help decrease US dependence on imported raw materials. A rock ilmenite containing about 46 wt % TiO2 was smelted in an electric arc furnace with coke, wood-chips, and Na2CO3 to separate most of the iron as pig iron and to form a low-iron, titanium-enriched slug. The slug was ground, pelletized, oxidized, and then sulfated with mixtures of SO2 and air in a continuous 4.5- to 9.1-kg/h (10- to 20-lb per hour) apparatus at 1023° to 122J0 K (1380° to 1740° F). The sulfated slug, containing 60% to 65% TiOb, was reground and leached in water at ambient temperature to decrease the combined levels of the troublesome calcium, magnesium, and manganese impurities from 7.0 to 1.7 wt 70. The final product was upgraded to about 8.4 wt % TiO2. This material is potentially suitable for chlorination in a fluidized bed reactor. The most favorable results were achieved with leached slug sulfated at a feed rate of 4.5 kg/h (10 lb per hour) and at temperatures of 1073° to 1123° K (1470° to 1560' F).

Jan 1, 1986

By P. Ramachandrarao, T. R. Anantharaman

CONSIDERABLE interest has lately been evinced as regards the nature of chill zones in solidified metals and alloys. Biloni and Chalmersl were the first to show through their study of segregation substructures in some nonferrous alloys that the formation of the dendritic region may be preceded by a diffusionless solidification process, viz., predendritic solidification. Subsequently Bower and Flemings2 tried a special solidification technique wherein the liquid was drawn into a narrow copper mold with polished surfaces and concluded that convection might trigger some multiplication mechanism leading to grain refinement. Using uncoated and partially coated surfaces for molds in the Bower-Flemings technique as well as in conventional molds, Biloni and Morando3 have very recently brought out the importance of the rate of heat extraction on the mechanism of solidification. We report here on the surface structures and substructures observed in a Sn-1 wt pct Pb alloy solidified at even higher cooling rates (riz., l05 to l07 ºc per sec) than those employed by earlier workers. The alloy was made by melting tin (99.99+ pct) and lead (99.9+ pct) in a silica tube under vacuum. Small quantities of the homogenized alloy (0.5 to 1.0 g) were then quenched (or splat-cooled) from the melt by the "gun technique" developed by Duwez et al.4 The thickness of the resultant foils varied from specimen to

Jan 1, 1970

By W. W. Tyler, A. C. Wilson, L. B. Nesbitt

INVESTIGATIONS of thermal conductivity and impact strength of the titanium alloy RC-130-B and 316 stainless steel were undertaken because of interest in strong, nonmagnetic, commercially available alloys of low thermal conductivity for use in low temperature experiments. Measurements of electrical resistivity and thermoelectric power were also made for some of the samples studied. The titanium alloy designated as RC-130-B is manufactured by Rem Cru Titanium Inc. It contains 0.14 pct C, 3.99 pct Al, and 4.7 pct Mn. A general discussion of properties of the two phase Ti-4Mn- 4A1 alloys is given by Finlay and Vordahl.' The alloy is machinable and has a yield strength greater than 130,000 lb per sq in. at 0.2 pct offset. The 316 stainless steel sample used for both conductivity and impact strength measurements was obtained from the Allegheny-Ludlum Steel Corp. and is designated as Allegheny metal 18-8M, Type 316, Grade 316. The sample had received 25 pct minimum final cold reduction and had a Brine11 hardness rating of 255. Several impact tests were made on a sample of 316 stainless which had not received the 25 pct cold reduction. Also several data points are reported giving thermal conductivity and electrical resistivity for a sample of 304 stainless steel taken from stock. Figs. 1 and 2 give thermal conductivity and electrical resistivity data for the titanium alloy and for

Jan 1, 1954

The total crude production from the Dutch East Indies, and the British Protectorates of Sarawak and Brunei for 1932 is given in the following table: Production, which had shown a rapid increase from 1921 to 1929, has since been reduced. Exploitation drilling in the majority of the larger fields was suspended and existing production kept within predetermined limits by beaning. Most of the smaller fields were shut down entirely. The depth of producing levels varies widely in the different fields. Shallow fields with drilling depths to 500 meters (1650 ft.) are still numerous as well as those with depths between 500 and 1000 m. (3300 ft.). A few of the newer fields reach greater drilling depths up to 1600 m. (5250 ft.). The deepest exploration well drilled to date (Djambi field, South Sumatra) reached a, depth of 2332 m. (7650 ft.) before abandonment in March, 1930. The specific gravities of the various crude oils produced range between 0.65 (86.2° A.P.I.) and 0.95 (17.5° A.P.I.). The lighter crudes have a high gasoline content and fuel oils are derived from the heavier crudes, which usually are rich in paraffin. Producing companies are: De Bataafsche Petroleum Maatschappij (Royal Dutch-Shell combine in Dutch territory); The Anglo-Saxon Petroleum Co. Ltd. (Royal Dutch-Shell combine in British territory); De Nederlandsch-Indische Aardolie Maatschappij (De Bataafsche Petroleum Maatschappij-Dutch East Indian Government combine); De Nederlandsche Koloniale Petroleum Maatschappij (Standard Oil Co. of

Jan 1, 1933

By W. F. Tanner

A river delivers a given load of sand, and hence heavy materials, into the sea. The load is fixed by drainage basin characteristics and processes. Wave energy available for redistributing that load is fixed in an entirely different way. An equilibrium diagram of these two parameters (load vs energy) pennits a tentative prediction of what will happen to the heavy minerals. Alluvial rivers transport a mechanical load which consists essentially of wash load (finer than about 0.05 mm in particle diam), bed load (coarser than about 0.10 mm) and the transition sizes in between. A few rivers carry no appreciable mechanical load, and are excluded from this discussion. An example of the latter is the Suwannee River of Florida, which empties across an oyster bar into the Gulf of Mexico and does not build a delta despite the absence of significant waves or currents in that part of the Gulf. An alluvial river may deliver its load into a protected sediment trap (such as an estuary, sound or lagoon), onto a low-energy coast (where it builds a delta) or onto a high-energy coast (from which spot the river load is swept away). The nature and disposition of the load depends, obviously, on three sets of factors: 1) drainage basin characteristics and processes, which determine quantity and make-up of the load; 2) coastal structure and geomorphology, which determine the kind of river-sea coupling which

Jan 1, 1962

By David Sinclair, Philip B. Bucky

THE dimensions and shapes of mine structures may at present be determined by (1) field experience, (2) structural calculations, and (3) barodynamic tests.§ None of these, however, provide information as to the stresses, their direction and distribution in a mine structure. For the design of pillars, the placing of openings relative to working places such as gangways, haulage levels, etc., this information is desirable. Photoelastic methods provide this and, while relatively new, their application in all engineering fields is assuming increasing importance. This paper, therefore, will present the method with a few applications to mining, and with sufficient reference for further study by the reader. PART I THE PHOTOELASTIC METHOD The photoelastic method of stress measurement determines the stress distribution in a two-dimensional model by optical means. It makes use of the fact that when a piece of isotropic transparent material, such as glass, celluloid, or Bakelite, is stressed and viewed in polarized** light a picture is seen which indicates by its color bands of light, or fringes, the magnitude of the stresses, their direction and their distribution. GENERAL EXPLANATION The stress at any point 0 in a structure (Fig. 1), may be resolved into two components, P and Q, each a pure tension or compression, at right angles to each other, called principal stresses.1 To fully identify the stress, the values of P and Q and their directions or angle [0] must be known.

Jan 1, 1940

By J. C. Branner

DuriKg the past two or three years I have seen statements regarding the first discovery of fullers' earth in this country that seem to require correction or modification. One appears again in the Mineral Resources of the United States for 1909, part II., p. 738, where it is said that 'fullers' earth was firat discovered in the United States at Quincy, Fla., in 1893." In this connection the following bit of unpublished history concerning fullers' earth in the State of Arkansas is worthy of attention. In April, 1891, when I was State Geologist of Arkansas, a Swede named John Olsen, formerly a copper-miner in Michigan, but then living south of Little Rock, brought me a sample of what he thought mas fullers' earth. He reported that it was from near the town of Alexander, the locality being 1 S. 13 W., section 8, SW. quarter of the SE. quarter. My chemist, Dr. R. N. Brackett, analyzed the material, and reported: Per Cent. Silica,.....SiO2 .... 63.19 Alumina,.... A12O3 .... 18.76 Iron,.....Fe2O3 .... 7.05 Lime,.,...CaO .... 0.78 Magnesia,.... MgO .... 1.68 Potash,.... K2O ,... 0.21 Soda,.....Na2O .... 1.50 Loss on ignition,........7.57 100.74 Water at 110° to 115° C. = 7.84. Another sample from about the same locality, also brought by John Olsen, on analysis by Dr. Brackett gave :

Jan 1, 1913

NORMAN B. PILLING (author's reply to discussion *).-The discussion by Mr, Bassett raised one or two points that deserve further discussion. The printed figure for the lead content of the copper used was 0.015 per cent. and not 0.15 per cent., upon which his comment was based. A copper having the latter figure would, of course, be quite unusual. Mr. Bassett takes exception to the writer's statement regarding the distribution of cuprous oxide in wrought copper and states that "the FIG. 1.--ROLLED AND ANNEALED SHEET. ETCHED WITH AMMONIA AND HYDROGEN PEROXIDE. X 75. eutectic of copper with cuprous oxide is usually found between the crystals of pure copper, whether in the cast or the wrought form." While it is very well known that during the solidification of cast copper the cuprous oxide is segregated completely as an envelope of cuprous oxide-copper eutectic around the crystals of copper free from oxide, it is the writer's opinion that, as a result of repeated rolling, this eutectic structure is quite destroyed and the small particles of cuprous oxide become widely scattered, and in the recrystallization following, during annealing, the rearrangement of the grain boundaries takes place with much indifference to the actual distribution of these particles. In the accompanying micrograph, taken from a rolled and annealed sheet, the random distribution of the small cuprous-oxide particles with reference to the location of the grain boundaries may be seen.

Jan 3, 1919

By A. G. Metcalfe, R. P. Elliott, F. A. Crossley

THE texture method (utilizing monochromatic copper radiation) was applied to determine the orientation of the columnar grains of two vacuum cast beryllium ingots of 3 in. diam. Samples were mounted in a fixture as illustrated in Fig. 1, which permitted rotation and translation in order to approximate the method used for wires. The specimens were aligned so that the major axes of the columnar grains were parallel. Rotation was around the growth direction. After each translation the specimen holder was rotated 2 deg (1 deg for the samples from the second ingot) until a range of 30 deg on either side of the vertical was covered. The speed of translation was 1 mm per sec. A representative Debye pattern is shown in Fig. 2. The pattern was compared with theoretical patterns for various orientations. Also shown in Fig. 2 is the disposition of reflections on the (10i0), (0002), and (1011) Debye rings for the two possibilities that growth is either in the <10i0> or <ll30> direction. It is apparent that no significant preference for the direction of columnar growth is indicated. It is considered that the lack of a preferred orientation is due to the occurrence of the phase transformation (reported by Martin and oore&apos; to occur above 1250 "C) which masked the original solidification orientation. This research was supported by the United States Air Force under Contract No. AF 33(616)-5911, monitored by the Materials Central, WADD, Wright-Patterson Air Force Base.

Jan 1, 1962

By A. J. Opinsky

THE purpose of this note is to indicate the locations and sizes of various interstitial holes in the orthorhombic uranium lattice based on a hard-sphere model. First, plane configurations of three and four atoms will be examined, and then the true interstices surrounded by four atoms in space and by five atoms in space will be obtained. The data and notation contained in a report by Tucker&apos; will be used. Plane Configurations Fig. 1 presents the orthorhombic uranium lattice made of spheres touching at the closest interatomic distance. The three light-colored spheres in the ab plane are illustrative of the first type of configuration to be examined. If one edge of the unit cell is taken as the origin, the three atoms can be represented by the vectors [Oi + Oj + Ok], [ai + Oj + Ok] and [(a/2)i + (b/2)j + Ok] where i, j, and k are respectively parallel to a, b, and c. In the future, this notation will be shortened to [000], [a00] and [a/2 b/2 0], respectively. A vector R = [r s t] de-scribes the position of the hole surrounded by the atoms. Since the center of the hole must be equidistant from the three atoms R2 = r2 + s2 + t2 = (r-a)2 + s2 + t2 = (r-a/2)2 + (s-b/2)2 + t2. R = [a/2 (b/4) - (a2/4b) 0] is the solution of these

Jan 1, 1955

By Hsun Hu, B. B. Ruth

The rates of migration of high-angle boundaries in zone-refined aluminum crystals rolled 20 to 70 pct in the (110)[i12/ orientation were studied. Following a recovery anneal at an appropriate temperature to stabilize the polygonized structure, boundary migration rates of artificially nucleated grains were measwed isothermally at several temperatures. Results indicate that the rate of boundary migration depends strongly on the amount of deformation and on the cell size of the polygonized matrix, and is related to the driving free energy by a power function. The degree of anisotropy in growth 0.f the re crystallized grains nn&apos;th preferred mientation is independent of deformation; the migration rates of the fast-moving and the slow-moping boundary segments of a gowing grain differ by as much as one order of magnitude. The actir\ation energy fm a grain boundary migration, although nearly the same for both the fast-moving and the slow-moving boundaries for a given deformalion, decreases from 45 to 30 kcal per mole with an increase in deformation from 20 to 70 pct reduction. Re crstallization by the growth of the artificially nucleated grains results in preferred orientation. The Percentuge of&apos; grains favorably oriented for growth increases with increasing deformation. None of these grains corresponds to the ideal Kronberg-Wilson orientation relationship. The observed growth aniso-tropy is discussed in terms of boundary structure. The boundary velocity as a function of the cell inter -facial area, or the driving free energy, is discussed in the light of current theories of boundary migration. It is well established that recrystallization with re-orientation occurs by the migration of high-angle boundaries of strain-free grains. The driving force for this process is provided by the free energy stored in the metal during deformation. A quantitative study of the effect of varying driving force on grain boundary migration in deformed metals has not been possible heretofore, primarily because of: 1) concurrent recovery steadily decreasing the available driving free energy for boundary migration, &apos;-3 and 2) in-homogeneity of strain in the deformed metal.4 Aust and Rutter3 studied grain boundary migration in striated single crystals of zone-refined lead. Although the driving free energy in such crystals remains unaltered during annealing, this method does not provide a range of driving free energies over which measurements of grain boundary migration can be made. In the present investigation, the rates of migration of high-angle boundaries in deformed aluminum zone- refined single crystals were studied at various temperatures, after deformation ranging from 20 to 70 pct reduction by rolling at -78°C in the (ll0)[i12] orientation. The boundary migration rates along different crystallographic directions were determined under steady-state conditions, i.e., in the absence of competing recovery processes or impingement of recrystallized grains growing into the deformed single crystal matrix. Simultaneous recovery was eliminated by suitable anneals prior to the boundary migration measurements. The recrystallized grains, which grew a ni so tropically into the homogeneously polygonized matrix, developed flat boundary segments during early stages of growth. These boundary segments subsequently migrated along a direction approximately normal to the boundary plane into the matrix rystal. Increasing deformation over the range employed was estimated to increase the driving free energy for boundary migration by about five times. The kinetics of the boundary migration process, examined under these conditions, indicate that the boundary velocity is greatly affected by a small change of the driving free energy in the matrix crystals. These results were examined in the light of the current theories of grain boundary migration. EXPERIMENTAL PROCEDURES Single crystal strips (9 by 1 by 0.125 in.) of zone-refined aluminum, were seed-grown by the Bridgman method in a high-purity graphite mold (<lo ppm ash) at 1 in. per hr. Precautions were taken to minimize contamination of the metal during crystal preparation and subsequent handling. Spectrographic analysis of the metallic impurities in the grown crystals is Qven in Table I. The crystals were rolled in the (110)[112] orientation at -78°C to various reductions in thickness, ranging from 20 to 70 pct, in 10 pct increments. The desired reduction was achieved by many rolling passes, each being no more than 0.002 in. To minimize surface friction, the crystal was rolled between two thin layers of teflon. For those crystals rolled more than 40 pct, it was necessary to remove the disturbed surface layers by electropolishing at -5" to -10°C at an intermediate stage of rolling. The edges of deformed crystals were removed by a jeweler&apos;s saw while submerged in alcohol at -78° C to obtain samples of about ? by i in. The distorted metal at the cut edges and the surface layers were then removed by electropolishing, with removal of a minimum of 0.004 in. from each surface. The thickness of the crystals prior to rolling was chosen so that the final thickness was 0.025 in. for all samples. These deformed single crystals were each prean-nealed for 1 hr at an appropriate temperature in the range of 130" to 280°C, depending upon the amount of deformation. The purpose of this preannealing was to

Jan 1, 1970

By R. W. Carpenter, J. C. Ogle

It is possible, by using pack-rolling instead of conventional rolling, to reduce a number of metals to thicknesses of 2µm or less. Such thinfoils are generally made at room temperature without intermediate annealing. In addition, pack-rolled foils fail by developing pinholes at thicknesses near 2µm instead of developing the shear cracks usually observed in cold-rolled ductile metals. This paper presents the results of a general investigation of the deformation substructure and texture developed in copper and iron pack -rolled from 130 to about 2µm thickness. Electron microscopy showed that in both metals a fine (0.2 to 0.5?µ m) deformation subgrain structure formed during pack-rolling; in neither case was this substructure grossly different from substructures formed during conventional rolling. The deformation texture formed in pack-rolled iron was quite similar to usual bcc textures; however, in the case of copper, the cube texture was stable during pack-rolling and the normal copper deformation texture was unstable. It is shown analytically that the constraining pack induced a large hydrostatic pressure in the foils during pack-rolling. The pinhole failure mechanism is attributed to the presence of the large hydrostatic pressure during pack-rolling; this strongly suppressed the growth of shear cracks. The stability of the cube texture in copper is also probably due to the unusuul stress distribution developed during pack-rolling. EXPERIMENTS at several laboratories have shown that very thin foils of the common structural metals and many of the rare earths can be made by "pack-rolling". 1-3 The technique was originally developed to make specimens for nuclear scattering experiments and foils for X-ray filters. It is also useful for making experimental laminar metallic composite bodies and foils thin enough for direct examination by ultra-high voltage electron microscopy without the need for special thinning techniques. Pack-rolling in the present context means a three-layer pack, with the material to be rolled into foil comprising the center layer. The outer two layers, which constrain the foil during reduction, are ordinarily austenitic stainless steel. Typically, a 130 µm (0.005 in.) metal strip can be reduced to a final thickness of 2 µm or less by this process. This is accomplished at room temperature, without intermediate annealing. It has been observed that foils produced by this process do not exhibit at any stage of their reduction the severe work-hardening found in strip rolled by conventional cold-rolling methods. Neither is the failure characteristic the same."&apos; Conventionally cold-rolled ductile metal strip fails by developing shear cracks on planes whose normals nearly bisect the angle between the rolling direction and normal to the rolling plane; these are planes of maximum shear stress. In pack-rolling this mechanism has not been observed; failure occurs by the formation of pinholes on the foil surface (penetrating the foil). If pack-rolling is continued the hole density increases. These differences in behavior imply the existence of appreciably different substructure in pack-rolled foils compared to substructure in conventionally rolled material, or perhaps that the geometry of pack-rolling has an effect on the foil behavior. This paper describes an investigation of deformation substructure and texture in some specimens of pack-rolled copper and iron, and some considerations of the stress distribution in the foils during rolling that result from the geometry of pack-rolling. EXPERIMENTAL DETAILS Three different materials were used for pack-rolling in the present work: soft copper sheet (99.8 pct Cu, 0.03 pct 0, electrolytic tough pitch) and two types of iron, Ferrovac E* and Armco iron. Each was "Crucible Stccl Co. initially in the form of 130 µm annealed strip with grain size ranges of approximately 10 to 40 µm. The initial texture of the copper (determined as noted below) was the normally observed cube type (001)[100]; there was evidence of a small amount of material in the cube-twin orientation reported by Beck and Hu.4 The initial texture of the Ferrovac E was similar to that reported for recrystallized iron by Kurdjumov and sachs,5 who list the principal orientations as {111}<112>, {001}<110> 15degfrom RD and a weak component {112}(110) 15 deg from RD. The starting texture of the Armco iron was not determined. Pack-Rolling Procedure. A four-high mill was used for all specimens. The work roll and backing roll diameters were 1.625 and 5.25 in., respectively. The peripheral roll speed of the work rolls was about 2.5 in. per sec. All foils were initially reduced from 130 to 100 µm by conventional straight rolling and then inserted into a pack, without any intermediate annealing, for further reduction. The pack consisted of an 0.033 in. (838 µm) thick 3 by 6 in. polished sheet of austenitic stainless steel, folded to make a 3 by 3 in. jacket. After folding, the jacket was given a small reduction to close the fold tightly before insertion of the foil. During pack-rolling a constant change in roll spacing was made every third pass. The roll-spacing change corresponded to a 5 pct reduction in thickness for a new pack. This approached a 10 pct reduction when the pack had decreased to about half its original thickness. At this point the deformed pack was discarded and a new one

Jan 1, 1970

By Rees D. Rawlings, C. W. A. Newey

The aging characteristics of an Fe-11 at. pct Mo alloy have been studied by means of light metallography together with density, Young&apos;s modulus, and hardness measurements. The results were consistent with the precipitation of a single intermetallic compound during aging; overaging was slow relative to that in other iron-based binary alloys. The solution treatment temperature had a small effect on the rate of hardening whereas deformation prior to aging had a marked effect on both the rate of hardening and the peak hardness. The density data indicate that the compound precipitated is Fe3MO2 and not the Laves phase Fe2Mo. Analysis of the modulus and density results gave values for the time exponent for precipitate growth of approximately 1.0 and 1.5 for the alloy aged with and without prior deformation, respectively. DETAILED studies of precipitation hardening in bcc matrices have been confined largely to the effects of carbides and nitrides. In view of this and the growing technological interest in intermetallic compound strengthening, e.g., in maraging steels, a study of precipitation in iron-based alloys with a low interstitial content has been undertaken. This paper is concerned with the aging behavior of an Fe-11 at. pct Mo alloy; the mechanical behavior of the alloy will be reported later. The early work of sykes on Fe-Mo alloys showed that precipitation of the intermetallic compound was accompanied by an increase in hardness and a decrease in volume of the material. More recent surveys of the strengthening associated with precipitation have been made3-5 and, in particular, Elsen and wassermann4 showed that deformation prior to aging increased the rate of hardening. These latter workers also followed the precipitation process by means of dilatometry, electrical resistivity, and lattice parameter measurements. Their results confirmed that there is a decrease in volume on aging. Except for the work of Hornbogen on an Fe-20 at. pct Mo alloy, neither clustering nor the precipitation of a nonequilibrium phase has been observed in Fe-Mo alloys. Studies of alloys of lower molybdenum content475 indicate that the equilibrium intermetallic compound is precipitated during aging. However, there is some doubt concerning the nature of the equilibrium precipitate phase. According to the phase diagram constructed by Hansen,8 the phase should be precipitated. This phase has a rhombohedra1 crystal structure which is characterized by the formula Fe706,&apos; although the composition of the molybdenum-rich boundary corresponds approximately to Fe3Mo2. The version of the diagram proposed by Sinha, Buckley, and Hume-Rother indicates that the A phase, a Laves phase Fe2Mo, should be precipitated. Their observation of a Laves phase supports the earlier findings of Bechtoldt and Vacher,13 although, in a recent study of the system by means of diffusion couples, Rawlings and Newey did not detect the phase. The work presented here describes the effect of solution-treatment temperature, aging temperature, and prior deformation on the aging characteristics of the alloy as revealed by light metallography together with hardness, density, and Young&apos;s modulus measurements. In addition the density data are used in an attempt to determine the compound precipitated during aging. EXPERIMENTAL PROCEDURE A 29-kg ingot of the alloy was cast at R.A.R.D.E., Fort Halstead, from deoxidized, Japanese electrolytic iron and sintered molybdenum. The ingot was homogenized for 6 hr at 1473°K and then worked, with intermediate anneals, into 6- and 16-mm-diam rods and 6-mm plate. Chemical analysis of the alloy gave, wt pct: Mo, 17.5 (11 at. pct); C, 0.003; Si, 0.002; S, 0.005; P, <0.002; and02, 0.0098. Solution treatments were carried out under a dynamic argon atmosphere in a vertical, "crusilite" element, furnace which had a facility for rapid quenching into iced water. Except for the study of the effect of solution treatment temperature, all specimens were solution-treated at 1573" * 2°K for 1 hr. Salt baths were used for the aging treatments. Specimens for hardness, density, and Young&apos;s modulus measurements were produced, after heat treatment, from the stock rod or bar using a precision silicon carbide slitting wheel. As described later, the quenching treatment produced local plastic strain in the stock material; consequently, care was taken to ensure that the specimens were not prepared from these regions. Those specimens used in the studies of the effects of prior deformation on the aging behavior were strained in compression in a Denison universal testing machine. Specimens for light metallographic observations were mechanically polished on successively finer grades of diamond paste down to and then etched in either alcoholic ferric chloride or in a 2 pct nital solution. Vickers diamond pyramid hardness data were obtained using a 30-kg load. At least five impressions were averaged for each determination. Density measurements were made using a displacement technique in which each specimen was weighed in air and in dibromoethane at 296°K. The specimens were cylindrical and weighed 3 to 4 g; all weighings were made on a balance reading to 1 x 10"5 g. For each specimen the mean value of five weighings was used to calculate the density. The density of the dibromoethane was determined using the displacement procedure and a standard nickel specimen. The error in an absolute density value was estimated to be HI.01 pct. To obtain the density as a function of aging time a single specimen was used and the density meas-

Jan 1, 1969

By J. H. Swisher

The rate of internal sulfidation of austenitic Fe-Ti alloys in H2S-H2 gas mixtures is controlled primarily by sulfur diffusion, with counterdiffusion of titanium playing a minor role. At temperatures below 1100°C, enhanced diffusion along grain boundaries becomes important. The rate of internal sulfidation at 1300°C is approximately equal to the rate computed from the sulfur diffusion coefficient. The diffusion coefficient of titanium in y iron has been determined from electron microprobe traces in the base alloy near the subscale interface. The solubility of sulfur in Fe-Ti alloys has been measured in the temperature range from 1150° to 1300°C. The equilibrium sulfur content is found to increase with titanium content, due to the large effect of titanium on the activity coefficient of sulfur. The Ti-S interaction becomes stronger as the temperature decreases. TITANIUM as an alloying element in stainless steels is an effective scavenger for interstitial impurities, carbon in particular. Titanium is known to form stable sulfides; however extensive thermodynamic data on the Ti-S system are not available. Schindlerova and Buzek1 have shown that the Ti-S interaction in liquid iron is moderately strong. There have been no previous studies of the Ti-S interaction in solid iron. Internal sulfidation of Fe-Mn alloys was the subject of a recent investigation by Herrnstein.2 He found the rate of internal sulfidation to be an order of magnitude greater than predicted from available solubility and diffusivity data. A satisfactory explanation for the discrepancy could not be given. In the present study, the solubility of sulfur in austenitic Fe-Ti alloys was measured using a standard gas equilibration technique. Fe-Ti alloy specimens were also internally sulfidized. The rate of internal sulfidation was measured as a function of temperature and alloy composition. Supplementary electron micro-probe measurements were made to provide additional information on the nature of the internal sulfidation process. EXPERIMENTAL The starting materials were alloys containing 0.12, 0.24, 0.38, and 0.54 wt pct Ti. The alloys were made in an induction furnace by adding titanium to electrolytic iron that previously had been vacuum-carbon-deoxidized. The major impurity in the alloys as determined by chemical analysis was carbon. The carbon content of the alloys averaged about 100 ppm; metallic impurities were presented in concentrations of 50 ppm or less. Specimens were made in the form of flat plates, 0.03 by 2 by 4 cm for the equilibrium measurements and 0.5 by 1.5 by 3 cm for the rate measurements. The experiments were performed in a vertical resistance furnace wound with molybdenum wire and containing a recrystallized alumina reaction tube. In the gas train, flow rates of the reacting gases were measured using capillary flow meters. The source of H2S was a mixture of approximately 2 pct H2S in H2, which was obtained in cylinders from the Matheson Co. A chemical analysis was provided with each cylinder. The H2-H2S mixture was diluted with additional hydrogen to obtain the desired ratio of H2S to H2, and the resulting mixture was diluted with 30 pct Ar to minimize thermal segregation of H2S in the furnace. Argon was purified by passage over copper chips at 350°C and subsequently over anhydrone. Hydrogen was purified by passage over platinized asbestos at 450°C and then over anhydrone. The H2-H2S mixture was purified by passage over platinized asbestos and then over Pas. The samples used in the solubility measurements were analyzed for sulfur by combustion and iodometric titration. The subscale thickness in the internally sulfidized samples was measured on a polished cross section, using a microscope with a micrometer stage. Electron microprobe traces for titanium in solution were made on several samples that had been internally sulfidized. A Cambridge microanalyzer was used, and the known titanium content at the center of the specimen was used as a calibration standard. The procedure for the microprobe measurements will be described further when the results are presented. RESULTS AND DISCUSSION Equilibrium Data. Fig. 1 shows the sulfur concentration as a function of gas composition for three alloys equilibrated at 1300°C. The dashed line is based on data published by Turkdogan, Ignatowicz, and pearson3 for pure iron. The breaks in the curves are the saturation points for the alloys. The fact that the initial slope decreases with increasing titanium content indicates that titanium interacts strongly with sulfur in solution. To obtain information on the composition of the precipitating sulfide phase, the measurements described in Fig. 1 were extended to higher sulfur partial pressures. These results are shown in Fig. 2. (The initial portions of the curves are reproduced from Fig. 1.) The highest PH2s /pH2 ratio used is believed to be below the ratio required for the formation of a liquid sulfide phase. Time series experiments were used to study the approach to equilibrium in the samples. It was found that equilibrium with the gas phase was reached in less than 4 hr at 1300°C.

Jan 1, 1969