By W. V. Kotlensky, H. E. Martens

In an earlier communication, Ref. 1, the authors presented the tensile properties and the changes in crystal structure and microstructure for pyrolytic graphite tested at 2750°C. It was suggested that changes in the structure may have an effect on the tensile properties of this material. Accordingly, tensile tests were run on a series of specimens, from one block of pyrolytic graphite, some of which were hot-worked by being strained at 2750°C, others of which were tested in the as-deposited condition. According to the manufacturer, General Electric Co., the polycrystalline material was deposited at 2100°C on a substrate of synthetic graphite by decomposition of a dilute natural gas mixture. The as-deposited material had a density of approximately 2.19 g per cc, and as shown in Fig. 1 had a structure of medium size growth cones which were regenera-tively nucleated. All specimens had a gage section 0.75 in. long by 0.06 in. wide by 0.1 in. thick with the thickness direction perpendicular to the basal planes. The testing method and equipment used have been previously described, Ref. 2 and 3. For both the hot-working and the testing the load was applied parallel to the basal planes; a cross-head speed of 1.5 x l04 in, per sec was used. All heating was done in an atmosphere of bottled helium.

Jan 1, 1962

By E. F. Steeb, P. C. Rosenthal

BlANKS 8 in. long were cut from the as-received bar stock and austenitized at 1560° F for 1 hr, oil quenched, tempered at 1140°F for 1 hr, and water quenched. The heat-treated blanks were machined into tensile specimens which were subsequently used for the straining operation. Some of the tensile specimens were temper embrittled at 900°F for 24 hr and air cooled prior to or following the straining operation. The specimens were strained in tension up to 5 pct total strain (elastic plus plastic) either at room temperature or at 900°F. The reduced sec- tion of the tensile specimen employed was 5 in. long and 0.600 in. in diam. This size specimen was sufficiently large to permit two standard Charpy impact bars to be machined from it. One group of specimens was temper embrittled at 900°F for 24 hr under stress of about 20,000 psi applied with a hydraulic tensile testing machine. Approximately 0.34 pct plastic strain occurred during this treatment. A comparison of series "A" and "B" data in Table I at 0 pct strain, reveals that the steel was rather highly susceptible to temper embrittlement, the embrittling treatment causing the transition temperature to rise 165°F. The 28 ft-lb level, which was near the center of the sharp-rising portion of the transition curve, was selected as the

Jan 1, 1959

FRANK N. SPELLER,? Pittsburgh,. Pa.-Mr. -Hayward's paper again draws attention to the fact that copper in steel is not the enemy that a good many of us it one time thought it was. He shows clearly that steel with over 0.75 per cent. of copper is as dependable, under the :conditions which he describes, as the same steel without copper. I might add that you-can weld copper-steel- satisfactorily up to that point; in fact, we have succeeded in welding pipe by the lap weld process up to 1 per cent. copper. Notwithstanding the date that have been presented on the effects of copper on the physical properties and corrosion of steel, a maximum copper limitation is still found in many specifications. In some cases the limit is extremely low, such as below 0.05 .or 0.03: per cent., or thereabout. That is a relic of days gone by, and I think the practice should be discouraged. E. F. CONE, New York; N. Y.-Not so many years ago steel-casting makers were very particular as to the amount of copper that existed in the pig iron that they used. They would not use copper-bearing pig iron unless mixed with non-copper iron. I do not know what the practice now is in the particular foundry where I was metallurgist at one time,

Jan 4, 1918

By W. J. Slatosky

W. 0. Philbrook (Cairiegie Institute of Technologyogv—Mr. Slatosky has presented an interesting and constructive paper that represents another step along the way of converting steelmaking from an art to a science. I am confident that his computer will be practical and successful and that with a very few months of experience it will provide a significantly better degree of control than his record of 65 pct of heats within range obtained with the slide-rule calculator . A paper such as this, with a lot of symbols and condensed mathematics, is difficult to comprehend quickly. Since I have had an opportunity to study it carefully, perhaps my evaluation of its validity and accomplishments will save time for others. Mr. Slatosky has correctly used standard principles of stoichiometry and heat balances, which are available to anybody, but he has also brought to them two original contributions: 1) He has developed from operating data some empirical relations for predicting the final FeO content of the slag (at 0.5 pct C end-point) as a function of slag basicity, lance height, and scrap, ore, and scale in the charge. This improves the accuracy of prediction of temperature or scrap requirement compared with assuming an arbitrary, constant FeO content at the end of each heat. There is no assurance yet that exactly the same relations will hold for other furnaces or practices, but similar correlations can be expected. 2) He has combined calculations that are ordinarily carried out laboriously as a number of individual steps into a single, simple linear equation that can readily be fed into a machine. This involved a tremendous amount of painstaking detail work as well as the imagination to see the possibility and work out the steps. While his particular Eqs. [3] and [6] are valid only for the furnace design, charge weight, and blowing time used at Aliquippa Works, only a few numerical values have to be changed to adapt it for other conditions. In order to arrive at a useable solution, Mr. Slatosky had to make some basic assumptions about the process that are similar to those used by others. He neglected variation in some process variables and assumed an arbitrary average value for waste gas analysis and temperature for want of more exact information at the present time. All of these judgments are clearly stated. In addition, some thermody-namic data presently available are not adequate for the job, notably in relation to heats of formation and sensible heat in slag, and some expedient has to be adopted to get around the difficulty. Other people might prefer slightly different judgments about these details and hence obtain somewhat different numerical solutions. This is not of serious importance, however, because the errors accumulate in the "heat loss" term and are largely self-compensating for a constant heat time. Although the extended Eq. l(a) in Appendix I was set up as a rate equation originally, for convenience in using an analogue computer as stated in the paper, the time dependence was removed by later mathematical manipulations and assumptions about the process. The final result is an integration of element and energy balances from initial to final states; this procedure is as legitimate here as in any other form of heat-balance calculation. The formal handling of stoichiometry and thermochemistry appears to be correct, and it is assumed that any arithmetical errors would have come to light in applying the calculations to furnace practice. Mr. Slatosky's approach is not necessarily unique, in that other people might start with apparently different equations or prefer another form of final equation for another type of computer. However, he has presented an accomplished result that appears to be a theoretically sound and practically useful way of applying scientific principles and rapid computation for better control of steelmaking. His success will undoubtedly encourage himself and others to improve on the mathematical model and its use as better informatioq becomes available. John F. Elliott (Massachusetts Institute of Teck-t2ology)-The last comment by Mr. Richards that a calculator is quite unnecessary for an L-D operation ?-equi??es a rebuttal. The L-D furnace is a very high capacity process which places a premium on close control. When one is making steel at rates between 100 and 200 tons per hr, one cannot afford the luxury of an extra 5 or 10 min at the end of a heat correcting for an error that should never have been made in the first place. Mr. Slatosky's paper is a very sound application of the simple principles of stoichiometry and the energy balance. It is a satisfactory and valuable start, but only the start of the development of methods of control for this process. An analysis of the process shows that it should be very suitable to control by a computer. This is especially the case when various grades of steel are to be made. In fact, it would seem that the organizations who are planning new and bigger installations of L-D vessels should consider carefully the advantages that would stem from computer control of a vessel with the operator present to do little more

Jan 1, 1962

By W. E. Quist, R. Taggart, D. H. Polonis, C. J. van der Wekken

An intermediate compound that has been identified as Niab is observed to form as a decomposition product from supersaturaled Ni-Nb solid solutions during aging at temperatures between approximately 300" and 500°C. On the basis of data from electron microscopy and selected-area diffraction, the structure of this compound has been determined as fct with a = b - 3a0 and c = a, wlzere a,, is the lattice parameter of the parent solid solution. The compound consists of close-packed layers with triangular ordering, where the niobiutrl atoms are separated by two nickel atoms ([long- close?-packed directions. A nine layer stacking sequence is required to describe the proposed structure. STUDIES of the Ni-Nb binary system have been limited primarily to phase diagram determinations,'-4 investigations of high-temperature equilibrium phases,5"1 and the determination of the influence of deformation on the structure of the equilibrium compound.8 The nickel-rich portion of the binary system is reported to be of the simple eutectic type in which the maximum solubility of 12.7 at. pct Nb occurs at 1282"c.' The two-phase field below the eutectic temperature is bounded by the a fcc solid solution and an orthorhombic Ni3Nb compound. No metastable phases have been reported in previous investigations. In transformation studies of certain nickel-base commercial alloys that contain niobium, two ordered metastable compounds containing niobium have been shown to precipitate from the solid solution, both of which have been identified as y' and have the composition NisNb or Ni,Nb. One compound has been reported to have the bct DOz2 type Al3Ti structure" and the other the cubic LI2 type Cu3Au structure.9,11 In the present work on Ni-Nb binary alloys a metastable y' compound has not been detected after conventional quenching and aging treatments. An anomalous behavior was noted in electrical resistivity measurements. in alloys containing between 7 to 12 at. pct Nb when aging treatments were performed below 500°C after fast quenching from 1250°C. Transmission electron microscopy has shown that this behavior is caused by the formation of a low-temperature precipitate of unreported structure type and composition. EXPERIMENTAL METHODS Several Ni-Nb alloys, containing up to 11.5 at. pct Nb. were prepared by either levitation melting and casting in copper molds or by induction melting in alumina crucibles; both techniques employed purified helium gas as a protective atmosphere. The purity of the nickel and niobium used to make the alloys was 99.98 wt pct Ni and 99.9 wt pct Nb. The composition and homogeneity of the alloys were checked by weight measurements and by electron microprobe analysis. The induction-melted alloys were homogenized for 100 hr at 1100°C. The resistivity specimens were prepared from rods swaged to 2.5 mm and the electron microscopy specimens were cut from sheet that was rolled to 0.4 mm and thinned using a modified Bollmann technique." The elevated-temperature solution treatments were carried out in a purified helium atmosphere followed by direct quenching into a 10 pct NaCl solution at 23°C. Additional protection against oxidation of the samples during solution treatment was accomplished by using tantalum foil as a "getter" in the furnace. The specimens were aged at various temperatures in salt baths controlled to +2oC. A Leeds and Northrup K5 potentiometer was used to make electrical resistivity measurements on specimens immersed in liquid nitrogen. Electron microscopy and diffraction studies were carried out with JEM-7 and Philips EM-200 microscopes operating at 100 kv. RESULTS AND DISCUSSION Ni-Nb alloys containing between 7 and 11.5 at. pct Nb that have been solution-treated in the range 1220" to 1280°C and quenched to 23°C undergo a precipitation reaction when aged in the temperature range 300" to 500°C. Precipitation was detected by selected-area electron diffraction after aging a specimen for as little as 30 sec at 350°C) whereas the reaction was well-advanced after aging for 150 hr at 475°C. Electrical resistivity measurements were used to monitor the progress of the precipitation reaction. In the present experiments the nucleation process for precipitation required a high solution temperature and a rapid quench into brine. The presence of aluminum, iron? and carbon in amounts totaling less than 1 wt pct was found by electron diffraction to completely suppress the formation of the low-temperature precipitate that has been detected in the binary alloy. Electron diffraction techniques were used to determine the structure of the precipitates that formed during the decomposition of the Ni-Nb supersaturated solid solutions. Figs. l(a) through l(d) show electron diffraction patterns oriented to the [loo], [110], [lll], and [I031 zone axes of the matrix. Areas of reciprocal space between these sections were investigated by slowly varying the orientations of the crystal under study; this procedure revealed no reflections other than those depicted in Fig. 1. The presence of super-lattice reflections at points coincident with the matrix reflections was confirmed by the examination of an almost completely transformed structure. On the basis of the accumulated diffraction data, the reciprocal lat-

Jan 1, 1970

By W. C. Ellis

IN an ingot of germanium solidified progressively from the bottom by a method' devised by J. H. Scaff and H. C. Theuerer, examination discloses ex- IH. C. Torrey and C. A. Whitmer, Crystal Rectifiers. p. 364. 1948. New York. McGraw-Hill Pub. Co. tensive twin relationships. A slice taken about midway in a cylindrical ingot approximately 3/4 in. in diameter and 1 1/2 in. in length, after etching and polishing to delineate different orientations, is shown in fig. la. The orientations of the regions designated with letters were determined by Laue X-ray back-reflection methods and plotted on stereograms. The orientation relationships of the designated components were determined by comparing the values for the nine angles between the three respective cube poles of each orientation with the values calculated in a formal treatment of octahedral multiple twinning in cubic crystals. Germanium, diamond cubic in structure, has the octahedral twinning habit. I am indebted to K. H. Storks for the calculation of the angular relationships of cube poles in octahedral twinning to four orders. The set of values for the nine angles is distinctive of the order of twinning. Confirmation for a multiple twin relationship is obtained from the determined indices of the mirror planes. These exist for all orders of twinning through the third and for some of the fourth." If the orientations are not those for twinning, then the nine angles for the cube poles do not correspond in value and distribution to those formally calculated. Since all nine angles must correspond in values and distribution of values to the calculated ones, the Laue method with a precision of one or two degrees is adequate to establish or deny with confidence the existence of multiple twins. Regions of the same orientation can also frequently be identified by the optical reflections. For example, the narrow twin bands in A at 2: 00 o'clock have orientation B1. The interesting twin relationships shown schematically in fig. lb were found for the section in fig. la. Most of this slice was made up of orientation, A, appearing in widely separated regions. Of the four possible first order twins of A, three were present in this slice and are designated by B with subscripts. Four second order twins of A are designated by C with subscripts. It is worth emphasizing that two of these, C, and C,, are second orders of A through the first order missing in this section. Two regions, designated by D with subscripts are third order twins of A. D2 is a sixth order twin of D,. All orientations found were ascribable to multiple twinning, as if the orientations in this section originated earlier in solidification from a single nucleus. The presence of extensive multiple twinning to- gether with the absence of other orientations appears to be a characteristic result in many instances of solidification of germanium. Fertile conditions for twinning probably exist in the array of atoms in the diamond cubic structure. The high order twins in the section shown, it is reasonable to presume, are the result of progressive octahedral twinning through several generations in the material freezing earlier. Some of these generations do not appear in this section, it is suggested, because their orientations with respect to the growth direction were unfavorable for survival. The extensive twinning is probably promoted during solidification by constraint imposed by volume increase, and to an irregular growth front. Twinning may also be due, in part, to the attempt of the solidifying region to attain the orientation most favorable to the growth direction (maximum thermal gradient). The nucleus for a twinned orientation could have its origin in a "stacking fault" on the close-packed octahedral plane. Further work is being done in which the course of twinning throughout an ingot is being studied. The results appear to be important in the general theory of solidification.

Jan 1, 1951

By G. P. Airey, R. F. Mehl, T. A. Hughes

The coarsening of cementite particles in a ferrite matrix has been studied in a series of steels with 0.15 pct C only and 0.15 pct C plus 1 pct Ni, Mn, and Cr, respectively. Two initial states were employed: quenched nartensite, and quenched and cold-rolled martensite. A series of tempering temperatures between 500' and 700" and tempering times of up to 190 hr were used. The structures were studied by replica and transmission electron microscopy. Particle size distribution curves were determined. From the average size value coarsening curves were obtained. These were plotted in accordance with the Wagner analysis assuming diffusion control. A discussion of the significance of the results is given. L HE reactions occuring upon the tempering of martensite have long engaged the attention of metallurgists. The latter stages, when cementite particles coarsen in a ferrite matrix, have been studied both qualitatively and quantitatively. Studies of such coarsening processes have recently been spurred by the publication of the Lifshitz-Wagner theory1, and the extension of this to the a Fe-Fe3C system by Oriani3 and by Li, Blakely, and einold. Following Wagner the coarsening process is often designated as "Ostwald Ripening". The only quantitative data on the rate of coarsening, except for the work of Hyam and uttin,' in the a Fe-Fe3C system are those of Bannyh, Modin, and odin' for a commercial eutectoid steel and those of Heckel and ereorio" using a pure eutectoid steel. The data of Bannyh, Modin, and Modin have been employed by 0riani3 to derive the a Fe-FeE interface energy. The reaction is one of the most important ones in steel and is worthy of detailed study. This is the purpose of the present study. Laboratory heats were prepared; these were steels with approximately 0.15 pct C, selected so that the num ber of carbide particles would be relatively small and thus so that the overlapping diffusion fluxes would be minimized, presumably a desirable circumstance.'-3 In addition to Fe-C alloys, comparable heats containing 1 pct of Ni, Mn, and Cr, respectively, were included with a view of appraising the effect of alloying elements. This report includes an account of the micro-structures observed, primarily with the electron microscope, and of kinetic data and their interpretation. MATERIALS AND TREATMENT The alloys were prepared from electrolytic iron ("Plastiron") and high-purity graphite; these were melted in a zirconia crucible using a vacuum furnace. The alloy steels were made by adding electrolytic nickel, electrolytic manganese, and "vacuum grade" chromium, respectively, under a partial pressure of argon. Each melt was poured into a mold within the vacuum furnace and cooled in the mold. The ingots were 2 in. in diam. and 8 to 10 in. long. The analysis of the alloys is given in Table I. These ingots were hot-rolled to strip 0.1 in. thick, then cold-rolled to 0.05 in. and each alloy split into two batches. One batch was austenitized at 1200 for 1 min, quenched in cold brine, then cold-rolled to 0.02 in.; samples given this treatment are hereinafter designated as "worked". The other batch was cold-rolled to 0.025 in., austenitized at 1200" for 1 min, and quenched in cold brine; such samples are hereinafter designated as "quenched". These two batches were then tempered, as below. The purpose of the treatment given the first batch was to provide an initial structure of cold-worked martensite, with the expectation that the additional defect structure created by cold work would encourage a higher rate of nucleation of cementite on tempering and hence a more uniform distribution of cementite particles. Individual specimens were sealed in evacuated quartz or Pyrex tubes, then tempered in a muffle furnace. The temperature control was better than 3'C at 700. Tempering treatments wer: performed at 400°, 500°, 550°, 600°, 65o°, and 700C for time periods between 15 min and 190 hr. PREPARATION OF SPECIMENS Specimens for optical and replicalelectron microscopy were mounted, polished conventionally, and etched with 2 pct nital. For electron microscopy, single-stage "formvar" replicas were made, dry-stripped and rotary-shadowed with chromium at an angle of 30 deg. Carbide extraction replicas were prepared from electropolished specimens usirig the method described by Smith and uttin.' Thin foils for electron transmission microscopy were prepared by chemical thinning in an H202-HF bath prior to electropolishing in a chromium trioxide-acetic acid solution. The most

Jan 1, 1969

By W. R. Hansen, F. W. Boulger

Twenty-nine laboratory steels were studied to determine the effects of composition and ferrite grain size on drop-weight and Charpy V-notch transition temperatures. The experimental steels covered the following ranges in composition.. 0.10 to 0.32 pct C, 0.30 to 1.31 pct Mn, 0.02 to 0.43 pct Si, md nil to 0.136 pct acid-soluble Al. Although most of the data were obtained on hot-rolled samples, some plates were heat-treated in order to cover a wider range in ferrite grain size. The experimental data were used for a multiple-correlation analysis conducted with the aid of an electronic computer. The study showed that carbon raises and that manganese, silicon, aluminum, and finer ferrite grains lower both drop-weight and Charpy transition temperatures. Quantitatively, variations in composition and grain size have a more marked effect on V15 Charpy transition temperatures than on the drop-weight transition temperature. Useful correlations were found between transition temperatures in drop-weight tests and those defined by seven different criteria for Charpy tests. Evidence was accumulated that the conditions ordinarily used for drop-weight tests are more severe for 1-1/4-in. -thick plate than for 5/8- to 1-in. -thickplate. PROJECT SR-151, to study quantitatively the effects of metallurgical variables on performance in the drop-weight test, was established by the Ship Structure Committee late in 1958 on recommendation of the National Academy of Sciences, National Research Council. This project was initiated as a result of the increasing use of the drop-weight (nil-ductility) test in predicting the ductile-to-brittle behavior of steel. Qualitative data indicated the drop-weight was not as sensitive to metallurgical variables as the Charpy V-notch test. Furthermore, the available information indicated that the drop-weight test did not show the superiority of killed steels over semikilled steels reflected by Charpy tests. This difference in sensitivity to brittle fracture is considered important because the drop-weight transition temperature has been reported1 to correlate better with service-temperature failures than the V-notch test does at a constant energy level. Therefore, this project was concerned with establishing quantitatively the effects of metallurgical variables in the drop-weight test. For comparison, Charpy V-notch data were obtained for the steels investigated. This paper summarizes the results of the investigation. Most of the steels used for the study were made and processed in the laboratory. However, some tests were also made on commercial killed steels available from Project SR-139 (SSC-141). During the course of the investigation, data were obtained on the effects of carbon, silicon, manganese, and aluminum on transition temperatures of drop-weight and Charpy specimens. In addition, the effects of heat treatment which changed the ferrite grain size and the transition temperatures were also investigated. Finally a few exploratory studies were made on commercial killed steels to evaluate the effects of plate thickness, grain size, and heat treatment on the performance of drop-weight specimens. EXPERIMENTAL PROCEDURES Preparation of Materials. A total of twenty-nine 500-lb induction-furnace heats were made and processed in the laboratory for the investigation. Carbon, manganese, silicon, and aluminum contents were systematically varied. Melting and rolling techniques proven satisfactory in a previous project2 were used as a guide for the current investigation. Composition. The composition of the twenty-nine laboratory heats made for this project are given in Table I. The steels are divided into three groups. The first group consists of ten aluminum-killed steels similar in composition to Class C ship-plate steel. The second group consists of ten semikilled or Class B type steels. In both of these groups the carbon and manganese contents were intentionally varied over a wide range. This wide range in composition was helpful in obtaining quantitative data from a limited number of steels. The primary purposes of these two groups of steels was to determine the effects of carbon, manganese, and deoxidation practice. In addition, one steel in each group (Steels 2-2 and 9-2) were made about 1 year after the start of the program in order to check consistency of melting practice. The third group of nine steels listed in Table I was intended for studies on the effects of silicon and aluminum. In eight of these steels carbon and manganese were held relatively constant at levels of about 0.2 and 0.8 pct, respectively, while silicon and

Jan 1, 1963

By H. S. Hanna, C. Rampacek

The problems and limitations encountered in the Physical beneficiation of the Appalachian Red Iron Ores are discussed. Two major problems are identified - the high phosphorus content and the fine dissemination or encapsulation of mineral impurities in the iron-bearing minerals. A process that combined extreme fine grinding techniques with magnetizing roasting or flotation-separation methods is suggested. By these methods, concentrates assaying 60-61 % Fe, exceeding the widely accepted upper limit of 56% Fe set for these ores, were produced with 75-90% iron recovery. Moreover, it was shown that the phosphorus content of these concentrates could be reduced from 0.25% to 0.03% phosphorus by acid leaching. A brief discussion on production costs based on current and future developments in iron ore processing is given.

Jan 1, 1983

By Per-Martin Sandgren, Alrik Anttila

LKAB's ores have specific mineralogical properties that make them especially suitable for the production of supergrade concentrates. Conditions are particularly good for this purpose at Malmberget, where a concentrate for high-purity sponge iron production has been produced for many years. This product assays approximately 71.5% Fe and 0.20% SiO2. Potential exists for still further improvement. In recent years, the production of fractioned concentrates has been started. The material lies within the size range 74-125 µm and the approximate chemical analysis is 71.4% Fe and 0.30% SiO2. Other special products are under discussion. Malmberget ores are also suitable for the production of high- purity direct reduction pellets with a SiO2 content below 1%.

Jan 1, 1983

By I. Sheinhartz, H. M. McCullough

DURING the course of a lubrication study in relation to the compacting of metal powders, it became desirable to measure the thickness of sprayed graphite coatings on steel dies for hot pressing. The thickness of these lubricant coatings ranged between 0.0001 and 0.002 in. In their particular case, the authors were interested in a method for measuring the lubricant thickness on tapered die inserts having curved surfaces. The lubricant was sprayed on the inserts at an elevated temperature and it was desirable to measure the thickness as soon as possible after application. Various standard types of commercial equipment were tried. Most of the available devices operated on either a mechanical or magnetic principle. The mechanical devices, such as micrometers, dial indi-

Jan 1, 1956

By Edwin T. Wood

THE term blending as used herein refers to the mixing of ores assaying more than 0.20 pct U3O8 with low grade material assaying less than 0.20 pct U3O8. Such blending when properly understood and controlled will produce more total dollars of profit from many mining ventures. The question whether or not to blend is particularly vexing when an orebody is surrounded by an envelope of low grade material or separate tonnages of low grade exist which could be extracted coincident with the higher grade ores. Should any, all or part of this low grade be mined? If so, in what proportion and what is the limiting assay of the low grade material?

Jan 7, 1958

By C. S. Smith, L. H. Beck

KNOWLEDGE of the Cu-Zn constitution diagram was critically examined in 1944 by G. V. Ray-nor,1 who suggested the diagram reproduced in Fig. 1 as the best evaluation of available data. No pertinent work on the constitution has been published since that time, although a number of authors have discussed transformation kinetics and theory. Despite the large amount of work that has been done on the constitution of these industrially important and scientifically interesting alloys, minor uncertainties still exist. For example, it is still not possible to say definitely whether a two-phase region exists between the ordered and disordered forms of the 8 phase. A careful re-examination of the phase boundaries in this part of the diagram was therefore undertaken. Two methods were selected for the new investigation—quantitative metallography for the higher temperatures and precision lattice parameter measurement for lower temperatures. Because of the relatively narrow two-phase regions flanking the ß phase in these alloys, quantitative metallography is particularly suited for their examination, since the relative amounts of the two phases are very sensitive to their compositions. The method, however, is useless below about 350°C because of the inadequate resolution of the two constituents. Below 400°, however, the X-ray diffraction method is applicable, although it is of somewhat lower sensitivity in this system. The changes of composition that occur during quenching from above about 500°C entirely vitiate X-ray measurements at room temperature though they do not affect metallographic area measurements. The two methods overlap and supplement each other admirably. Both methods depend on the attainment of equilibrium composition of the two phases in a more or less intimate mixture and thus avoid the difficult problems of nucleation and long range diffusion involved in the conventional metallographic bracketing method. The alloys were melted from a master alloy made from re-electrolyzed cathode copper and Horsehead 99.99 pct Zn. Melting was done under a cover of either borax or charcoal and the alloys cast into a 7/8 in. sq graphite mold for the a-ß alloys or a 3/8 in. diam cylindrical graphite mold for the ß-? alloys. The a-ß alloys were rolled at 750°C to 5/8 in. sq; annealed for 24 hr at 800°C and quenched; then rolled and swaged at 200°C to 3/8 in. diam rods, annealed 24 hr at 200°C, quenched and cold rolled 2 pct reduction. This treatment was intended to obtain a small grain size and to produce many nuclei of the minor phase for growth on subsequent heat treatment. The unworkable ß-? alloys were given preliminary treatment by sealing in Vycor tubes in vacuum and annealing for 4 hr at 800°C followed by cooling in air. Samples of homogenized alloys were checked spectrographically for impurities, but the principal components were determined on samples subsequent to heat treatment. The impurities analyzed averaged approximately as follows: Ag, 0.0002 pct; Fe, 0.004; Si, 0.0008; Cd, 0.005; Mg, 0.0002; and Pb, 0.002. For metallography, samples of appropriate composition were cut into rods 5/8 in. long, sealed in pyrex tubes in vacuum and annealed for eight weeks at temperatures of 470°C and below, two weeks at 480°, 500°, and 600°C, and 4 hr at 700°C, followed by quenching in cold water. Temperatures were accurate to ±2°C. The cylinders were then machined to 8.7 mm diam and a slice weighing 1.5 g cut with a thin saw transversely from the center of each. This

Jan 1, 1953

By D. G. Wilder

D.G. Wilder I found the suggestion that the amount of displacement of a fault can be numerically related to the thickness of gouge or breccia to be both intuitively satisfying and intriguing. I have long agreed that there is some type of relationship between the amount of gouge and the amount of displacement of faults. I congratulate the author for developing a numerical relationship between them. However, I am concerned that the limits for applying this relationship be fully understood. An underlying assumption in this approach is that there is either a uniform thickness of gouge or breccia along a given fault or the thickness does not vary widely. Since it is not always possible to confirm this, the displacements derived by this method should be viewed with caution unless significant fault extent can be observed. At the Nevada Test Site, in drifts constructed in granite for test emplacement of spent nuclear reactor fuel, we found a fault with 0.3 to 0.4 m (12 to 16 in.) of clay gouge. Within a few meters of this location, the fault had no clay gouge, but rather consisted of a highly fractured zone with significantly altered rock and some slickensides. Based on Fig. 1, the 0.3 to 0.4 m (12 to 16 in.) thickness of gouge would indicate a displacement in excess of 30 m (98 ft). However, no gouge thickness would indicate essentially no displacement. Based on a quartz vein that terminated on the fault, and is not identified nearby, an estimated displacement of more than a few meters was made. This estimate is consistent with that obtained using the regression line proposed in the paper if the 0.3 to 0.4 m (12 to 16 in.) thickness for the gouge is used. However, using the regression curves with zero thickness would not yield results consistent with what was observed in the field. Therefore, it is important to recognize that the suggested procedure would properly yield a range of probable displacements. ? *Work performed under the auspices of the US Department of Energy by the Lawrence Livermore National Laboratory under Contract W-7405-Eng-48. Reply by E.C. Robertson It is certainly true that the t (thickness) of gg-bx (gouge and breccia) on a fault does vary along the fault. My observations have been that near the termination of a fault, the displacement d is small and the t is also small, whereas the maximum d and t will usually be found in the central part of the fault. The information on gg-bx and t of the fault found in granite in the NTS tunnel by Mr. Wilder could be interpreted somewhat differently than he does. He speaks of the fault changing within a few meters from 0.3 to 0.4 m (12 to 16 in.) of clay gg to "a highly fractured zone with significantly altered rock and some slickensides," but no gg. The highly fractured rock may be taken to be bx, rock not so finely ground as gg but still crushed by the fault movement, equivalent to the gg in my usage, and probably occupying about the same t. Mr. Wilder's estimates for the fault in the NTS tunnel for t of 0.3 to 0.4 m (12 to 16 in.) and for d of a quartz vein, in excess of "a few meters," would place the point on the low side of the central trend line in my Fig. 1, at the lower limit. There is, of course, a problem with determining d using displacement of only one planar surface. It would be greater or lesser depending on the rake of the movement. Finally, estimating the d of a fault from its t should be made with awareness of our present uncertainties, as pointed out by Mr. Wilder. Although the central trend line in my Fig. 1 has a ratio of d/t of 100, I have put the limiting ratios at 10 and 1000. Understanding of the values of the ratio will be improved only with collection of more data, for which the discussion of Mr. Wilder is much appreciated. ? G.C. Waterman E.C. Robertson's paper provides significant information to a geologist attempting to deduce fault offset by noting the products of structural dislocation. However, considerable mapping in underground and open-pit mines, and examination of structures produced in different geological settings, have convinced me that gouge and breccia thickness are controlled by geological conditions and fault movement. The following paragraphs suggest geological variables that control them. 1. Depth of Loading A near-surface fault resulting from tensional stress has more breccia/gouge than is produced by a similar stress at considerable depth. A deep-loaded compressional stress may produce a linear zone of schist, or structural dislocation may occur along an earlier formed belt of schist. Such "shear zones" are common in Canadian mines in precambrian rocks. In neither case can offset be directly deduced by an analysis of the minimal gouge/breccia in the shistose rocks. At greater depth, stress may be partially to wholly relieved by flowage. I vividly recall first noting the regional "Midas Thrust" in the Lark mine, Bingham Mining District, UT (where we called the structure the North Fault). My recorded notes, as I remember them, showed a narrow gouge streak separated the "Jordan" and "Commercial" limestone units from impure, muddy limestone beds of uncertain stratigraphic position. The visible structure did not indicate the great importance of this premineral fault

Jan 1, 1985

By C. Altstetter

THE work herein reported is restricted to the carbides which occur in quenched and tempered AISI 43XX steels with carbon contents up to 0.40 pct and silicon additions of up to 3 pct. In view of the instability and extremely small size of the carbides formed at low tempering temperatures, the technique for successfully preparing specimens for X-ray diffraction will be outlined. The alloys listed in Table I were obtained through the courtesy of the United States Steel Corp. in the form of 1/2-in. rounds forged from 100 lb. induction furnace heats (except for 4337 which was a commercial heat). The stock was normalized and then swaged and drawn to 15 mil wire with anneals at 1200F between passes. The wire was austenitized for 45 min in evacuated vycor capsules and quenched into iced brine with simultaneous smashing of the capsule. Tempering was done in air with a water quench after tempering. The carbides were extracted in a simple cell using a solution of 1M KC1 and 0.5 pct citric acid with an initial current density of 0.1 amp per sq cm. One end of a short length of wire was immersed in the solution, and the current at constant voltage was noted as a function of time. After about an hour the current dropped sharply because of the decrease in specimen cross-section. At this point it was found that the dissolution could be stopped and that the very fine wire which then resulted was just large enough to permit handling of the extracted precipitate still clinging to it, yet so small that it diffracted and absorbed only a negligible amount of the X-radiation. This rod of residue with a convenient handle of undissolved wire was rinsed in distilled water. alcohol, and acetone. Then it was dipped in a thin solution of cellulose-acetate cement and dried in vacuum. The resulting specimen was straight, uniform in density, easily handled, but most important, was completely sealed and never exposed to air. Furthermore, the residue had never been subjected to strong acids or rough handling such as in the extraction-replica technique or in the complete extraction to a powdered residue. It was found that improperly coated specimens were pyrophoric, turning to oxide with a dull red glow as they were exposed to air and yielding patterns of Fe2O3 and Fe3O4. The steels containing 3 pct Si were especially difficult to prepare for this reason. The specimens were put in a 57 mm Straumanis camera with double pinholes or slits and irradiated with filtered-chromium radiation. Readable patterns were obtained in less than an hour. A preliminary finding of some note was that for both tempered and as-quenched specimens of steels 4337 and 4337 (1.5 Si). M23C6 patterns were found along with the patterns of other constituents of the residues. This result was somewhat surprising in that previous investigators had reported that this carbide did not appear in a 0.38 pct C, 0.48 pct Mo steel1 or in chromium steels of less than about 10 pct Cr.2 Although the total amount of carbide-forming alloying elements is less than 2 pct, due to their mutual interaction and the action of the plastic deformation in promoting equilibrium, this carbide was able to form even in the steel containing 1.5 pct Si. M23C6 was not detected in the 4337 (3.0 Si) steel and the lower-carbon steels were not investigated in this condition. It is very likely then that the steels studied herein underwent a fourth stage of tempering during the anneals at 1200°F. This result has significance in that even a small amount of undissolved M23C6 in a low-carbon, low-alloy steel would exert a large effect on its hardenability. Its presence would also influence the mechanical properties by decreasing the carbon content of the matrix. Annealing in vacuum for 1 to 4 hr in the austenite field removed all traces of MZ3C+ The results on carbide precipitation during tempering, summarized in Table I, are in agreement with those of Klingler et al.3 for the higher carbon steels. For the AISI 4337 steels it is noteworthy that in the steels with added silicon the E carbide persists to longer times and higher temperatures and that silicon delays the formation of cementite. The results for the lowzr-carbon steels parallel those of the higher-carbon grade. The appearance of E carbide in the AISI 4315 is significant. There is considerable disagreem-nt in the literature as to whether this carbide forms in the tempering of steels containing less than about 0.2 pct C. Following the detection of E carbide in a 0.18 pct C plain-carbon steel,4 its occurrence in a steel containing chromium and molybdenum should be expected. The fact that the low-carbon steels have the same carbide-precipitation sequence as the high-carbon steels has bearing on the larger problem of the exact tempering reactions in all steels. Following the suggestion of Roberts et al.,' the first stage has been generally assumed to result in a metastable equilibrium of c carbide and martensite of about 0.25 pct C. From this it was concluded that a steel having less than 0.25 pct C should then be under-saturated with respect to c carbide and should not precipitate this carbide upon tempering. In view of the experimental findings of c carbide in steels hav-

Jan 1, 1962

By A. T. Aldred, K. M. Myles

The vapor pressure of chromium over solid V-Cr alloys has been measured by the torsion-effusion method in the temperature range 1450" to 1650°K. The chemical activities as well as the free energies, entropies, and enthalpies of formation of the alloys have hem computed from the vapor-pressure data. The activities of both chromium and vanadium exhibit fairly small negative deviations from Raoult's law over the entire composition range. The values of the excess entropies and the enthalpies of formation found at 1550°K are considered in terms of the changes in the clzaracteristic properties of vanadium and chromium that occur upon alloying. RECENT interest in the theory and properties of transition-metal alloys has shown the need for relevant thermodynamic data. The present investigation of the V-Cr system was undertaken as part of a more general study of thermodynamic properties of transition-metal alloys. The system was chosen because of the reported complete solid solubility of the components at all temperatures1 and because the difference in magnitude of the vapor pressures of vanadium and chromium allowed a simple effusion technique to be used. The torsion-effusion method was employed to minimize compositional changes in the alloys during the experiments. EXPERIMENTAL Equipment. The torsion-effusion apparatus, shown diagrammatic ally in Fig. 1, consists of a torsion system suspended inside a vertical vacuum chamber whose lower end is surrounded by a high-temperature vacuum furnace. An auxiliary optical lever and screen are used to determine the angle of rotation of the effusion cell. The torsion fiber is an annealed, high-purity, tungsten wire usually between 0.003 and 0.007 cm in diameter and about 43 cm long. The wire supports a concave mirror and a rigid tantalum connector tube. The effusion cell is fastened to the lower end of the connector tube by a dovetailed yoke and har- ness arrangement. The cells, which are 1.27 cm in diameter and 4.4 cm long, were made by electron-beam welding tantalum endcaps onto a 0.025-cm-wall tantalum tube. The two orifices, formed by drilling, have similar areas ranging from 0.011 to 0.031 sq cm. The noninductive sheath-type furnace consists of a single-phase tantalum heating element 6.35 cm in diameter, 15 cm high, and 0.013 cm thick; the element is completely surrounded by radiation shields in an evacuated chamber. The power system includes a 17-kva self-saturating saturable core reactor with an integral magnetic amplifier and a water-cooled, 15-kva, step-down power transformer with a multitap secondary. Temperatures are controlled to within ±1/2o at 1600°K by means of a unit that includes a reference voltage source, a dc electronic null detector, a current-adjusting proportional band relay, and the self - saturating reactor. At 1650°K the temperature variation within the cell, vertically and horizontally, is 3/4oK. Unwanted motions of the torsion system are damped by the movement of an aluminum vane, which is mounted on the connector tube, between the poles of an electromagnet. When not in use the magnet is withdrawn and rotated 90 deg to prevent its interaction with the rotation of the system. Measurements. The vapor pressure, p, is re-

Jan 1, 1964

By F. I. Grace, L. E. Murr

The mechanical responses and residual defect structures in 70/30 brass and type 304 stainless steel following explosive shock loading and cold reduction by rolling have been studied. A distinct relationship was observed to exist between the residual mechanical properties and micro structures observed by transmission electron microscopy. Shock-loaded brass deformed primarily by the formation of coplanar arrays of dislocations and stacking faults at lower pressures, and twin-faults (deformation twins and €-martensite bundles) at higher pressures (> 200 kbar). The micro -structures of cold-rolled brass were characterized by dense dislocation fields elongated in the rolling direction. Stainless steel was observed to deform by the formation of dense arrays of stacking faults at lower shock pressures and twin-faults at high shock pressures (>200 kbar). Lightly cold-rolled stainless steel deformed similar to low Pressure shock-loaded stainless steel, but transformed to a' martensite in heavily cold-rolled stainless steel. Discontinuous yielding was observed for the heavily cold-rolled stainless steel, and stress reluxution in the weyield region for cold-rolled and shock -loaded stainless steel was interpreted as an indication of the ability of twin-faults and stacking faults to act as effective barriers to dislocation motion. A simple model for the formation of the planar defects and a' martetnsite is presented based on the propagating of Shochley partial and half-partial dislocations. A considerable effort has been expended over the past decade in an attempt to elucidate the response of metallic-crystalline solids to the passage of a high velocity shock wave (e.g., smith,' Dieter,2 and zukas3). While it has been possible to obtain relevant information pertaining to the residual defect structures and mechanical properties, there have been few rigorous attempts to draw a direct comparison between these structures and properties. In addition, numerous investigators have recently observed the occurrence of deformation twinning in shock deformed fcc metals (e.g., Nolder and Thomas,4 and Johari and Thomas5), but little attempt has been made to elucidate the mechanisms of formation of these defects. Comparative data for metals deformed by shock-loading and the same metals deformed by more conventional modes of deformation such as cold-reduction by rolling is also generally lacking. The present investigation therefore has the following objectives: 1) to examine the mechanical properties of some explosively shock loaded and cold-rolled fcc metals of low stacking-fault energy as a function of their residual substructures; 2) to present a simple model for the formation twin-faults and related defect structures in the low stack-ing-fault energy materials of interest (70/30 brass, ySFg= 14 ergs per sq cm; and 304 stainless steel, ySF = 21 ergs per sq cm); 3) to make some deductions with regard to the residual characteristics of dislocation and planar defect substructures in cold rolled and shock loaded 70/30 brass and type 304 stainless steel. In particular, it was desirable to characterize the residual hardening effects of particular deformation substructures. I) EXPERIMENTAL PROCEDURE Sheet samples of 70/30 brass (0.005 and 0.15 in. thick; annealed at 659°C for 2 hr) and type 304 stainless steel (0.007 in. thick; annealed 0.25 hr at 1060°C) of nominal compositions shown in Table I were cold-rolled in one direction only to produce reductions in thickness of 15, 30, 45, 60, and 75 pct in the brass; and 5, 15, 25, 35, and 45 pct in the stainless steel. Identical sheet samples in the annealed (unrolled) state were subjected to plane compressive shock waves to various peak pressures ranging from 0 to 400 kbar in the brass and 0 to 425 kbar in the stainless steel; and with a constant peak pressure duration of approximately 2 microseconds. A detailed description of the shock loading technique has been given previously.6 Tensile specimens 1.0 in. in length and 0.125 in. in width were cut from the cold-rolled sheets (tensile axis parallel to the rolling direction), and the shock-loaded sheet specimens. Stress (load)-strain (elongation) measurements on the tensile specimens were made on a Tinius-Olsen load-compensating tensile tester using a strain rate of 2.7 x 10-3 sec-1. Tensile tests were repeated at least twice, giving essentially the same results. Stress relaxation measurements in the preyield region were also made using an initial strain rate of 5.4 x 10-4 sec-1. In addition to tensile and stress relaxation measurements, Vickers microhardness measurements were made on all samples. A total of 100 microhard-ness readings were obtained for each specimen following a light electropolish to ensure uniform surface conditions for all tests. The hardness averages ob-

Jan 1, 1970

By L. D. Jaffe, F. W. Cotter, E. Cordon

The hardenability of titanium-base alloys was studied by metallographic examination and hardness survey of Jominy specimens end-quenched from the B range. Analyses of the data led to the equation log J = -0.57 + 0.25 @ct Fe + pct Mn + pct Mo) + 0.19 @ct Cr) +0.16 @ct V) + 0.03 @ct Zr). Here J is the distance, in sixteenths of an inch, from the quenched end of a Jominy hardenability specimen in the position of peak hardness, for material quenched from the B range. This equation fitted the experimental data with a standard deviation of approximately 0.29. The effects of the elements Al, Sn, W, Cu, Ni, B, C, N, 0, and H, and of pain size, were not statistically significant or not practically significant. A check against hardenability measurements in the literature showed agreement within the stated standard deviation. The equation should be useful in estimating hardenability of new or modified titanium alloys. HARDENABILITY in a titanium-base alloy is the ability of the alloy to retain the B structure on quenching. An alloy with high hardenability will retain the /3 structure even when cooled relatively slowly from a temperature at which B or P plus a is stable. A low hardenability material will retain P only if quenched extremely rapidly from the range of p or 0-plus-a stability, or will not retain it at all, at room temperature. High hardenability is desirable in titanium alloys to be heat-treated to high-strength levels. Its value is by no means limited to large section sizes. With high hardenability, a material can be solution-treated and cooled at a variety of rates, either to give high strength directly or, more generally, to give a soft ductile condition from which high strength can be obtained by subsequent aging. With low hardenability, high strength can be obtained, if at all, only by very rapid quenching, and there will generally be little increase in hardness on subsequent aging; an alloy of this type is limited in its applicability. On the other hand, alloys of very low hardenability have some advantages in weldability; essentially, they are always in the annealed condition, after welding as well as before. For commercial alloys, hardenability data are usually available, in the form either of property data after cooling from the solution temperature at various rates, with or without subsequent aging, or of results of a standard hardenability test, such as that originally developed for steels by Jominy and Boegehold.' When modifications of an available alloy are considered, or preparation of new alloy compositions, it would be Very convenient to be able to estimate the hardenability of the new material without having to make and test it. A method of estimating hardenability of titanium alloys from their composition was suggested by one of the authors some time ago, on a preliminary basis, utilizing scattered data found in the literature.' It seemed worthwhile to carry out a systematic experimental study of the effect of composition upon hardenability. EXPERIMENTAL PROCEDURE Approximately fifty heats of various compositions, weighing 8 to 10 Ib apiece, were melted in a small inert-gas tungsten-arc furnace with water-cooled copper walls. The starting material was 110 Brine11 titanium sponge, with high-purity metals added for alloying. Each heat was bottom-poured under vacuum through a molybdenum burnout strip into a cold graphite mold, to form an ingot approximately 4-1/2 by 3-1/2 by 3 in.* From each ingot were cut *The material was melted and cast by Pitman-Dunn Laboratory, Frankford Arsenal, to whom the authors must express their thanks. two pieces 4-1/2 by 1-1/2 by 1-1/2 in. These were forged, at temperatures adjusted to the composition, into 1-1/4-in. rounds, from which standard 1-in.-diam hardenability specimens3 were machined. A number of small samples were also prepared from forged materials of each heat, annealed, quenched from various temperatures, and examined metallographically. The P-transus temperature was determined by observation of the degree of resolution of primary a in these pieces. samples for chemical analyses were also taken from the forgings. One hardenability specimen of each heat was solution-treated for 1 hr approximately 50°F above the measured transus temperature, and the other for 1 hr approximately 250°F above the transus. (An additional hour was allowed for the specimens to reach furnace temperature.) These are not necessarily the temperatures that would be selected for

Jan 1, 1964

By David W. James, Howard Jones, George M. Leak

Conditions are described for producing, by primary recrystallization, a matrix suitable for the growth of large grains near (110)[001] orientation in silicon iron strip by secondary recrystallizaliun in a steep temperature gradient. The orientation distribution of these large grains is expressed in terms of rotational deviations about the cross-rolling direction, the rolling direction, and the normal to the sheet, the deviational spread increasing in that order. With the aid of cowplenientary published data on the orientation dependence of growth rate, it is shown that this observation is consistent with the oriented-growth theory of recrystallization lextures. It is conclutled that growth-rate and orientation-distribution data obtained in a steep thermal gradient should be used with caution to account for isothermally Produced recrystallization textures. SEVERAL authors have reported methods of growing large grains by re crystallization of a small-grained matrix in silicon iron 1- B and pure a cr The present study was a preliminary in the growth of single crystals and bicrystals for surface relaxation," grain boundary mobility, and grain boundary diffusion studies. The method was to control the growth of a seed crystal into a suitable primary re crystallized matrix by feeding through a steep temperature gradient. The driving energy for growth derived from the grain boundary energy released as the seed crystals grew into the matrix. Thus, stability of the matrix against normal grain growth was considered to be essential for success. It was known that the manganese sulfide dispersion present in commercial silicon iron performs this function during secondary recrystallization to the (110)[001.] texture.12 Hence commercial, rather than high-purity, material was used throughout. The paper describes the growth conditions for grains large enough to be used as seed crystals for further growth into single crystals. The orientation distribution of the seed crystals is analyzed and its significance for the theory of recrystallization textures is discussed. EXPERIMENTAL PROCEDURE Strip material was supplied by the Steel Co. of Wales, Ltd. The chemical analysis in weight percent was Si, 2.90; C, 0.015; Mn, 0.059; P, 0.011; S, 0.027; Ni, 0.032; 0, 0.009; Fe, balance. A gradient furnace of similar design to one described previously4 was loaned from B.I.S.R.A. It consisted essentially of a vertical water-cooled copper slot projecting downwards into the hot zone of a molybdenum furnace. Hydrogen was passed through the furnace to protect both heating element and specimen from oxidation. Strip specimens up to 8 cm wide and 0.2 cm thick were sealed into the furnace at the mouth of the copper slot. A coating of light oil on the strip surface maintained the seal during translation of a specimen. The maximum temperature gradient in the region just below the copper slot was 500°C per cm over 1 cm, with the hottest point controlled at 1175°C. Several large grains would usually grow by secondary recrystallization from the primary matrix when a specimen was immersed in the hot zone for about 30 min. A back-reflection X-ray camera was constructed to facilitate rapid and accurate orientation determinations of the large grains produced. It was possible to reproduce a standard geometry, with regard to strip and camera, without the tedium of careful alignment on each occasion. Specimens, typically 4 cm wide and 75 cm long, were cut with the longitudinal axis parallel to the rolling direction of the original strip. The surfaces were cleaned by immersion alternately in a hot aqueous solution containing 2 pct hydrofluoric acid plus 10 pct sulfuric acid and in cold 10 pct nitric acid. The nitric acid etch was just sufficient to reveal the grain structure. Rolling and annealing treatments to prepare the matrix (discussed below) were followed by growth of seed crystals in the gradient furnace. The matrix was transformed to a single crystal by growth of a selected seed crystal connected to the matrix by a thin neck. 4,5 Growth was promoted by controlled feeding into the gradient furnace. Several single crystals of controlled orientation were grown successfully from seed crystals by twisting the interconnecting neck in a reorien-tation jig.4 EXPERIMENTAL RESULTS AND DISCUSSION Growth Conditions. A suitable matrix for growth of large grains was prepared starting from primary re-crystallized strip 1.9 mm thick. This was cold-rolled in two stages each being followed by a recrystallization anneal at 800°C for a few minutes. Such treatment gave the required growth matrix only if the two cold-reduction stages were each performed in several passes and in the following ranges: the first, 30 to 70 pct; the second, 10 to 50 pct. Immersion in the temperature gradient otherwise resulted in an equiaxed

Jan 1, 1967

By R. K. Dann, L. W. Roberts, R. B. Benson

The mechanical properties of 300-series stainless steels were investigated in both high-pressure hydrogen and helium environments at ambient temperatures. An auslenitic steel which is unstable with respect to formation of strain-induced a (bee) and € (hcp) mar-tensile is embrittled when plastically strained in a hydrogen environment. A stable austenitic steel is not embriltled when tested under the same conditions. The presence of hydrogen causes embrittlement at the mar-lensitic structure and a definite change in the general fracture mode from a ductile to a quasicleavage type. The embrittled martensitic facets are surrounded by a more ductile type fracture which suggests that the presence of hydrogen initiates microcracks at the martensitic structure. If a steel is unstable with respecl to fortnation of strain induced martensile, plastic deformation in a hydrogen environment will produce rapid embrittlement of a notched specimen in comparison to an unnotched one. FERRITIC and martensitic steels can be embrittled by hydrogen that has been introduced into the alloys, either by thermal or cathodic charging prior to testing.1-5 However, conflicting reports exist as to whether austenitic steels that are stable or unstable with respect to formation of strain-induced martensite can be embrittled by hydrogen.8-12 A recent investigation has shown that cathodically-charged thin foils of a stable austenitic steel can be embrittled.13 An earlier investigation of a thermally charged 18-10 stainless steel revealed a significant decrease in the ductility only at the lowest test temperature of -78°C, although strain-induced bee martensite was shown to be present in one specimen tested at ambient temperatures.' When martensitic steels are tested in a hydrogen atmosphere, they are embrittled.'4-'7 It has been observed in this Laboratory that 304L steel, which is unstable with respect to formation of strain induced martensite, forms surface cracks when plastically strained in a high-pressure hydrogen environment. Work in progress elsewhere concurrent with this investigation has also established that 304L is embrittled when tested in a high-pressure hydrogen atmosphere." The objective of this investigation was to study the effect of a high-pressure hydrogen environment on the tensile properties of a stainless steel that contained strain-induced martensite (304L) and one that did not (310). EXPERIMENTAL TECHNIQUES Notched and unnotched cylindrical specimens were machined from 304L* and 310 rods that were heat- treated at 1000°C in argon for 1 hr followed by a water quench. The chemical analyses of these steels are given in Table I. The unnotched specimens had a reduced section diameter of 0.184 & 0.001 in., a gage length of 0.7 in., and were threaded with a 0.5-in.-diam. thread on each end. The notched specimens had a reduced section diameter of 0.260 * 0.001 in. and a 0.75-in. gage length, with a 30 pct 60 deg v-notch at the center. The notch had a maximum root radius of 0.002 in. The tensile bars were fractured in a hydrogen or helium atmosphere of 104 psi at ambient temperatures. The system used for mechanically testing the specimens is to be described in detail elsewhere.19 Several specimens of each type were tested in air using an Instron testing machine. The same yield strength and ultimate tensile strength were obtained in 104 psi helium with the above system as with the conventional testing machine. Magnetic analysis was employed to determine that there was a (bee) martensite in plastically deformed 304L and that it was not present in plastically deformed 310. The magnetic technique depended on allowing the material being studied to serve as the core between a primary and secondary coil. Thus, any change in the amount of magnetic material present between the annealed and plastically deformed steels will be indicated by corresponding changes in the induced voltage in the secondary circuit." The ratio of the output signal of a nonmagnetic stainless steel to a completely magnetic maraging steel was 2000 to I. Several unnotched 304L bars tested in hydrogen were analyzed for hydrogen by vacuum fusion analysis. There was an increase in the hydrogen content to approximately 2 ppm for the specimens tested in hydrogen, as compared to less than 1 ppm for the as-received material. Several thin sections cut from notched areas of 304L specimens tested in hydrogen and containing the fracture surface contained approximately 1.5 ppm H. The accuracy of these determinations was estimated to be ± 50 pct.

Jan 1, 1969