By G. L. F. Powell, L. M. Hogan

Samples of silver and Ag-O alloy, 0.12 wl pet, have been undercooled to a maximum of 250°C by melting in a slag of commercial soda-lime glass. Grain refinement occurred in undercooled silver samples whet the degree of undercooling exceeded a critical value which varied from 153° to 175°C, depending on the melting conditions. In under cooled Ag-0 samples, the grain structure was fine and equiaxed at degrees of undercooling larger than 50oC. The grain refinement in both silver and Ag-0 alloy samples was the result of recrystallization during or immediately following freezing. When the oxygen content was increased, the degree of undercooling at which recrys-tallization occurred decreased. INVESTIGATIONS of the grain structure of strongly undercooled melts of nickel and cobalt1-4 have revealed a change in room-temperature grain size as a function of undercooling. At large degrees of undercooling the grain size was fine, but samples undercooled by smaller amounts exhibited a much coarser grain structure. The reported undercooling at which this grain size transition occurred in nickel varied between 140° and 175'C undercooling. Walker1 attributed this grain size change to an enhanced nuclea-tion rate. Cavitation at a melt-solid interface was con sidered to generate a high-pressure wave. This, in turn, produced nucleation in the liquid as a result of an elevated freezing point increasing the undercooling in the melt. A similar grain size transition was observed in undercooled silver between 133° and 153°C undercooling.5 The grain size transition in undercooled silver was found to be dependent on oxygen con tent. More recently, the authors5 showed that a simila transition occurred in an undercooled Cu-O alloy, =0.08 pet, but not in oxygen-free copper undercooled more than 200°C. The transition was attributed to recrystallization of the solidified grains after freezing; the greater the degree of undercooling, the more complete the recrystallization. In view of this effect of oxygen content on grain size transition, additional undercooling experiments were carried out with silver. This paper reports the results of these studies on silver and Ag-O alloys undercooled more than 50°C EXPERIMENTAL 1) Materials. The silver was supplied by Matthey Garrett Pty., Ltd., as fine granulate, silver mini' mum 99.9 pet, and contained the trace impurities shown in Table I. The silver originated from two different refineries resulting in the difference in impurity content shown in Table I. However, the variation in composition had no discernible effect on the undercooling behavior. Samples of the silver were melted in an open-ended, vertical, cylindrical resistance furnace, wound with Kantha] wire, the temperature of which was adjusted by means of a variable transformer, 2) Melting and Undercooling. Bulk samples of silver were undercooled by preoxidation and removal of oxidized impurities in a glass slag, as previously described,5 but special precautions were necessary to allow comparison between oxygen-free silver and a Ag-O alloy. Samples free of oxygen were prepared by first melting weights of granulate varying from 200 to 400 g in clean vitreous silica crucibles in air for approximately 15 min. A sample was frozen and a complete glass cover formed over the top surface by adding granulated glass rod. The sample was then melted and frozen several times until no oxygen bubbles appeared in the glass slag. Subsequent thermal analysis indicated that the oxygen content was negligible. The glass acted as an efficient barrier to absorption of oxygen from the air. Ag-O alloys were prepared by melting silver in silica crucibles with only a partial cover of glass, so that the top surface of the melt was in contact with air. The silver was held molten in air for several hours at 1000° to 1050°C, in the expectation that the oxygen in solution would reach equilibrium with atmospheric oxygen. At T - 1000°C the equilibrium oxygen content was calculated as 0.12 wt pet O, using Sieverts law and Eq, [l], derived by Mizikar et a!.7 from the data of Sieverts and Hagenacker8 for 1 atm of oxygen:

Jan 1, 1970

By S. R. Goodman, Hsun Hu

The rolling texture transition in copper as a function of deformation temperature is found to be quite similar to that in high-purity silver. The ordinary copper type texture changes gradually to the brass type, accompanied by an increase in the stacking fault frequency, as the temperature of deformation decreases. The rolling textures obtained at low temperatures and the corresponding annealing textures compare remarkably well with the ordinary rolling and annealing textures of low-zinc brasses. Furthermore, it is also found that the observed stacking fault energies of copper specimens deformed at low temperatures correspond closely with those of low-zinc brasses, as deduced from measurements of the dislocation nodes. These results are consistent with the idea that texture transition may be significantly dependent on the stacking fault energy. It was shown in a series of previous publications1"3 that the rolling texture of high-purity silver changes gradually from the common silver type (or the brass type) to the copper type* with increasing temperature *The silver or brass type rolling textures are commonly described as (110)[112],4,5 whereas the copper type rolling textures are mainly (123) [a121 and (146)[211].5 Other ideal orientations have been used by various investigators for the copper type rolling textures, but the actual difference among these ideal orientations is rather small. of deformation, and that such texture transition can be correlated with the change in stacking fault frequency as a function of rolling temperature. Furthermore, it was shown that the formation of annealing textures in high-purity silver from the various rolling textures obtained during the course of texture transition depends entirely upon the deformation texture. From a common silver type or brass type rolling texture (such as produced by rolling at 0" or at 50° C) the recrystallization texture is mainly (120)[211], which is quite different from the recrystallization texture of brass.* However, for both ma- terials the orientation relationship between the rolling texture and the recrystallization texture can be expressed in terms of similar rotations around [Ill.] axes of approximately 30 or 35 deg. They differ in that the [Ill] rotational axes are different. In the case of high-purity silver, the axes of rotation are the two (111) poles near the plane normal of the deformed specimen with a (11l)[112] type rolling texture, whereas in brass, they are the (111) poles near the direction of rolling. For high-purity silver with a predominantly copper type rolling texture (such as produced by rolling at 150° or 200°C) the recrystallization texture is mainly (100)[001], or the cube texture, plus its twin orientations. It was shown previously6 that such reorientation observed in copper or aluminum can be described as [Ill] rotations of 30 to 40 deg. For intermediate cases, i.e., when the rolling textures are composed of a

Jan 1, 1963

By F. H. Daniels

IN this, paper it is my intention to, call your attention to* a few of the many producers using blast, now, in common use in Sweden, and also those constructed by the Washburn & Moen Manufacturing Company at their Quinsigamond Works. During a prolonged stay in Sweden the writer had an opportunity

Jan 1, 1881

W. H. BASSETT, * Waterbury, Conn.-Manganese should not be expected to remedy all the defects that are due to poor melting practice. It is undoubtedly valuable in helping to eliminate porosity in many of the alloys. In the copper-nickel alloys, its use is becoming almost universal, for, beside helping to make sound castings, it tends to hold the carbon in solution in the solidified alloy. GWILLIAM H. CLAMER,? Philadelphia, Pa.-I have found that manganese copper is satisfactory for eliminating sulfur and that it works very well in the crucible and when you have reducing conditions; but in a large reverberatory charge, where the conditions are oxidizing, we were not able to eliminate the sulfur.

Jan 1, 1919

By W. Joseph Schlitt

The types of copper leaching and recovery operations in the United States are reviewed, along with characteristics and trends in the industry. The contribution of the various leach operations to total mine output is discussed in order to provide a perspective on the relative importance of copper leaching as a method of production.

Jan 1, 1980

By Mark Malamphy

DURING colonial times, Brazil was famous for the richness of her alluvial gold deposits. Paul Ferrand has estimated that the gold produced during the period from 1700 to 1820 was the equivalent of some 64 million pounds sterling. Since that time, most of the more prolific alluvial deposits have been exhausted. A few gold mines are still func-tioning, notably the Morro Velho mine, which is one of the deepest mines in the world. Today, the gold production of Brazil is insignificant when compared with world figures, but there are still many gold-bearing regions and it is probable that in at least some of them profitable returns would result from an exploitation program taking advantage of all the most modern innovations in gold mining and ore treatment on a large scale. In order to demonstrate the value of some of these abandoned pros-pects and stir up interest in increasing the national gold production, the government has stimulated research. Experimental plants have been and are being established in various places, and tests on large quantities of ores are being carried out on a semicommercial basis. The Geological Survey of the State of Minas Geraes is very active in this line and the Federal Institution is also showing an increased interest in the matter. One of the lesser known gold-bearing regions of Brazil is in the vicinity of Lavras, in the State of Rio Grande do Sul. Gold was first reported from this region in the early part of the nineteenth century. In 1811, D. João VI sent an experienced prospector from Minas Geraes to investi-gate the validity of the reports. According to the reports of Baron

Jan 1, 1934

By Giovanni B. Barla, Stefan H. Boshkov

The block caving method is examined in this paper on the basis of experimental results and observations in the field, and through the use of numerical modeling by the Finite Element Method. The Grace Mine, developed by a panel caving method, served as a reference case. However, the results obtained and the simulation techniques which have been developed may find useful application in more general conditions as encountered in other mining operations by block caving. Following a brief description of the Grace Mine and of the mining method, the problems associated with the behavior of underground drifts at the production levels, during undercutting and caving, are addressed. The most important results obtained through monitoring of strains and loads in the supports of a runway are discussed, while giving relevance to the sequence of mining operations in the immediate vicinity. The most important geomechanical data, as provided for subsequent modeling, are described with reference to: (a) rock mass characterization and (b) in situ state of stress. Then, the numerical modeling procedures, developed by the Finite Element Method in order to predict the caving phenomena and the behavior of underground openings during undercutting, are discussed. Finally, an attempt is made to compare the pre- dictions of the numerical analyses with, the measurements carried out at the instrumented site. Suggestions as to how to improve the results both qualitatively and quantitatively are also given.

Jan 1, 1984

The discovery of nickel at the Wallace Mine in 1846, recorded in the Report of Progress of the Geological Survey of Canada, 1.848-49, was not the first find in the Sudbury mining district. As long ago as 1770 a company had been formed to work the rich deposits of, copper whose existence was then known. .But it was during the first mentioned year that, incited thereto by fresh finds and a favorable report by Mr. W. E. Logan, then Provincial Geologist, two [ ] groups of Canadians organized "The Montreal Mining Company and "The Upper Canada Mining Company." By the former company the Bruce Mines Location' was purchased and work was immediately commenced upon it. The Wallace Mine acquired by the Upper Canada Mining Company, was abandoned after a shaft had been sunk and a few test pits opened.

Jan 1, 1907

By B. Silliman

THE remarkable outflow of natural gas recently developed in Western Pennsylvania, and along the valley of the Ohio and its tributaries, has called attention to an important series of patents for improvements in glass-fnrnaces and the manufacture of glass, which the brothers Siemens have made since 1872. The basement-patent of this series, is No. 127,806 of the U. S. Patent office, and is of date June 11th, 1872. This has been followed by eleven other patents (including one re-issue), all for improvements in glass-furnaces, or methods of manufacture, of which the latest is of date July 11th, 1882. Nine of these patents were issued in 1880-82. The following is the list of these patents, in order of dates, viz.: 1872. June 11th. No. 127,806 (U. S. office), Improvement in glass-furnaces; 17 sheets drawings, 5 pages text. This is the basement-patent. 1877. April 17th. No. 139,800. Improvement in the manufacture of glass; 3 sheets drawings, 2 pages text. Boats and floating vessels swimming in the liquid glass of the tank-furnace. Re-issued in 1880. q. v. 1880. April 27th. No. 226,931. Furnace for annealing and tem pering glass. " July 13th. No. 220,846. Glass-melting-furnace. " August 3d. No. 230,668. Glass-melting-furnace; 4 sheets drawings, 2 pages text.

Jan 1, 1885

By Joseph W. Roe

MaNY questions arising in the work of the mining engineer may be solved quickly and with suffcient accuracy by the methods of descriptive geometry; but, unfortunately, this subject is more often considered from a mathematical view-point than as an effective tool for solving practical problems. Some of the principles involved are merged into the ordinary operations of mechanical drawing, and are used unconsciously by the engineer in his every-day work. The rest are stowed away on the book-shelf with his forgotten or rarely-used college text-books. One reason for this condition of " innocuous desuctude " may lie in the uifortunate and often cumbersome notation which it has been found necessary to introduce. If some of these principles can be recalled to the engineer's attenti011 in terms of' every-day use they may prove of practical hearing. Recently, in talking with several mining engineers, I used some of the drawing-room methods of a machine-designer, to the evident surprise of those around me. These men were perfectly familiar with the methods, but their application to mining-work had not occurred to them. At their suggestion the present paper is offered, not in ally way as a treatise, but merely to suggest a certain point of view, in hope that it may lead others far more familiar with mining-problems to pursue the subject further. I. To Find the Strike. As the simplest and most fundamental problem, let it be required to find the strike of a vein when the location and elevation of three points on the outcrop are known. It mill be assumed for the present that the rein is a plane.

Jan 1, 1911

By S. J. Green, R. D. Perkins

Little data exists on the high strain rate behavior of geologic materials. Uniaxial stress tests by Kumar1 and by Serdengecti and Boozer2 present some results to strain rates in the range 10 to 103 per sec. The two references cited are the only ones the authors found for high strain rates. Techniques for experiments at high strain rates are not well developed and, in general, leave questions with respect to interpretation of data when the material behaves in a brittle manner. The most reliable data at very high strain rates (104 to 106 per sec) are found in some recent flat-plate work3-5 where experimenters have impacted one plate into another, thereby creating a uniaxial strain loading. The standard uniaxial stress-strain curves cannot be obtained directly from these tests; however, yield (or fracture) may be studied by measuring the "elastic" wave magnitude. These data then may be compared to uniaxial stress data by resorting to some preassumed yield/fracture criteria. Even with the most liberal interpretation of existing data, little can be said of the effects of high strain rate on stiffness, yield/fracture, and post-fracture behavior of geologic materials. It is the purpose of this work to begin to add to the understanding. The data presented here are intended to provide material information for use in calculating the response of geologic materials to high rate deformations. These data can be applied directly to determine parameters such as the elastic modulus and Poisson ratio as a function of stress. Furthermore, these data can be used to derive an understanding of yield/fracture and the effect of rate on the yield/fracture surface. The work presented is a first step, and is

Jan 1, 1972

By W. P. Sykes

THIS investigation was undertaken primarily to establish the relations existing between temperature and mechanical properties in molybdenum, nickel, and an aluminum-copper alloy. Molybdenum (m.p. 2500° C.) was chosen because it is partly similar to tungsten and partly similar to the common ductile metals. Also it is known to furnish, by proper treatment, a desirable material to use in studying relation of grain size and physical properties. The molybdenum used was of the quality that is drawn into wire 0.003 in. in diameter for use as filament supports in incandescent lamps; chemical analysis shows less than 0.1 per cent. of impurities. Nickel belongs to the same class as iron. Its melting point is 1450° C. and an allotropic change at about 370° C. results in a loss of magnetism above that temperature. This feature made nickel doubly valuable for the purposes of these tests. The nickel used was obtained from the Driver-Harris Co. as 0.090 in. (2.3-mm.) wire, annealed; analysis showed 99.8 per cent. nickel and 0.150 per cent. iron. Aluminum is one of the low melting-point metals. Some tensile tests at elevated temperatures have been reported by Bengough but the possibility of learning more with the low temperature and sensitive apparatus available recommended this metal. The samples marked Al are an aluminum-copper alloy; they contained 3 per cent. copper, 0.42 per cent. iron, and 0.21 per cent. silicon. The presence of the copper somewhat complicates the analysis of the results; but the action of copper in aluminum has been studied so that its influence might have been foretold, in part at least. The material and analyses were furnished by the Aluminum Castings Co. The nickel wire, which was deformed at 400° C., was drawn under a bath of molten lead and through a die, which also was immersed in the bath. A thermocouple was suspended in the molten metal to indicate

Jan 1, 1921

By William B Price, Ralph W. Bailey

Arsenic, antimony and phosphorus are now used in the brass industry as standard inhibitors in preventing dezincification in condenser tubes. This subject has been thoroughly covered by Barry,l who de- scribed the testing procedure by total immersion of suitable specimens in a I per cent cupric chloride solution at definite temperatures. Effects of dezincification were then determined by loss in tensile strength and elongation of the test specimens after definite periods of immersion. In the crystallography of the chemical elements as tabulated by William Hume-Rothery,2 phosphorus (metallic), arsenic, antimony and bismuth are placed in group V-B and the type of crystal lattice for arsenic, antimony and bismuth is given as rhombohedral. The Metals Handbook3 lists them as 'rhobomhedral hexagonal," with the additional notation that for arsenic this is the ordinary form at 20°C.; other modifications known or probable at other temperatures. In view of these statements and of the fact that phosphorus, arsenic and antimony are effective in increasing the resistance to dezincification, it was natural to assume that bismuth would act in the same manner. A series of tests was therefore carried out employing the methods described by Barry. Much to our surprise, bismuth did not inhibit dezincification, but rather seemed to accelerate it. Tensile-test speci-

Jan 1, 1942

By George Smith

ChillaQoe is situated in latitude 17" S., about 138 miles from the port of Cairns, with which it is now connected by rail. A township has been established on the banks of Chillagoe creek, a perennial stream of irregular volume crossing the field almost at rightrangles, nearly midway between the mining-camps of Calcifer and Mungana, which have been formed at the southeastern and western extremes of the field respectively. This situation was selected because of the water-supply and its proximity to the site most suitable for the erection of reductionworks. By its central position it commands the whole of the mines. The altitude above sea-level is about 1200 ft., whereas that of Calcifer and Mungana is 1400 ft.—a difference sufficient to account for a materially higher temperature at Chillagoe. The surrounding limestone bluffis add by radiation to the heat, and, at the same time, prevent the cool breezes from passing freely through the town; consequently, the temper* ture, which is high throughout the year, and especially so during the summer months, is here ge~ierally very oppressive also. The general trend of the field is southeast and northwest, and its length about 18 miles, with an average width of 5 miles; the approximate area is thus 90 sq. miles. The surrounding mineral-district is, however, much more extensive, and numerous other mines, sprcad over wide areas and producing a variety of minerals, exist in the same or parallel belts of mineralized country, of which Chillagoe proper covers but a very small portion. Immense bluffs of limestone, wollastonite and conglomerate, rising in places to nearly 300 ft., and so~netimes nearly a quarter-mile across, give the field a very picturesque and interesting appearance. The limestone has been classified as Devo-

Jan 1, 1904

By Ralph W. Bailey, William B. Price

Arsenic, antimony and phosphorus are now used in the brass industry as standard inhibitors in preventing dezincification in condenser tubes. This subject has been thoroughly covered by Barry,l who de- scribed the testing procedure by total immersion of suitable specimens in a I per cent cupric chloride solution at definite temperatures. Effects of dezincification were then determined by loss in tensile strength and elongation of the test specimens after definite periods of immersion. In the crystallography of the chemical elements as tabulated by William Hume-Rothery,2 phosphorus (metallic), arsenic, antimony and bismuth are placed in group V-B and the type of crystal lattice for arsenic, antimony and bismuth is given as rhombohedral. The Metals Handbook3 lists them as 'rhobomhedral hexagonal," with the additional notation that for arsenic this is the ordinary form at 20°C.; other modifications known or probable at other temperatures. In view of these statements and of the fact that phosphorus, arsenic and antimony are effective in increasing the resistance to dezincification, it was natural to assume that bismuth would act in the same manner. A series of tests was therefore carried out employing the methods described by Barry. Much to our surprise, bismuth did not inhibit dezincification, but rather seemed to accelerate it. Tensile-test speci-

Jan 1, 1942

By J. Richard Kyle

Lead-zinc ore bodies in the upper part of the Pine Point carbonate barrier complex are localized in paled-solution structures that developed as the result of post-middle Givetian subaerial exposure. Detritus-filled dolines host prismatic ore bodies, and macropores and stratabound permeable zones contain tabular ore bodies. Sulfides are concentrated in these transgressive paleosolution structures that acted as natural bypasses between aquifers and loci for mixing of fluids of different character. Complex ore textures indicate rapid early sulfide precipitation followed by slower sulfide growth. Evidence for both sulfide-carbonate equilibrium and disequilibrium conditions suggest fluctuations in ore fluid composition, perhaps related to periodic supply of reduced sulfur. District and ore body metal distribution pattern may reflect the nature and movement of mineralizing fluids.

Jan 1, 1981

By Oliver C. Ralston, Foster Fraas

INTRODUCTION ELECTROSTATIC methods of separation are used only when some peculiar advantage is gained. Such cases are minerals that are not separable by differences in specific gravity or magnetic response and that are desired in particles as large as 10-mesh, a size on which flotation separation is inefficient. This paper covers several separations of this type and others. It includes studies in the electrostatic behavior of kyanite, sillimanite, and zircon, simple silicates that cannot be called either acid or basic but are more nearly neutral. Kyanite and sillimanite are both desired in 10-mesh size and are difficult to beneficiate from low-grade ores to give that type of concentrate. A separation of garnet from diopside was studied because this mixture had been removed from a wollastonite product by drying and magnetic separation, and no special or extra-preparation for electrostatic separation was necessary. THE SEPARATOR The separator used in these tests is of the nonhomogeneous field type shown in Fig I[a]. It consists of a 11.4-cm-diam rotating metal roll 2 at ground potential over which the dry mixture of minerals is fed. The roll serves as one electrode of the separating field, and the other electrode is that of 3, a smaller 5-cm-diam rotating metal cylinder which is held at a high direct-current potential. In this paper the term "electrode" will be confined to the electrode at 3, roll 2 being designated only as "roll." [ ]

Jan 1, 1947

By W. R. Crane

While professiorlally engaged in the oil- and gas-fields of Kansas, in measuring the pressure and flow of gas-wells, and studying the phenomena attendant upon the production of both oil and gas, I noticed in the flow of gas a peculiar and interesting feature. That there are actual lines of flow in liquids (non-compressible fluids) discharged through an orifice, or a short section of pipe, is shown by the external shape of the discharge—the vena contracts. Such lines of flow are not observable in the discharge of gas from an orifice. It can hardly be questioned that they exist. That they are not apparent is probably due to the very small weight of the gaseous particles, which climinishes the momentum of their movement in a given direction, acquired before they issue from the orifice, and also to the expansion of the gases, which would exert a powerful influence in overcoming any such tendency in their flow. Gas flowing from an orifice, supplied by a large reservoir or blowing-engine, exhibits almost the reverse of what is noticed with liquids. Namely, the gas assumes the form of an inverted truncated cone, of large angle: with its apex-end at the orifice. (See BB, Fig. 1.) This external ahape assunled by the flow of gas shows, however, marked differences under varying conditions of volume and pressure. For instance, a large volume of gas under high pressure, flowing through a 2- or 3-in. pipe, as in the case of a natural gas-well, assumes a more definite conical form, the angle of which increases as the pressure falls. Moreover, outside of the well-defined inverted cone is a thin conical heath or zone of gas, A A, the angle of which is considerably greater than that of the main cone, and increases with +1UNIVERSITY OF KANSAS, LAWRENCE, KANSAS.

Jan 1, 1905

By J. A. Snyder, W. L. Finlay

SEVERAL notable studies of the effects of sub- stitutional solutes have been reported. Outstanding among these for its elucidation of general principles, is the summarized work of Hume-Rothery and coworkers.1 For a systematic study of the effects of substitutional solutes on the mechanical properties of the solvent lattice, the work of Brick, Martin, and Angier² on copper; of Frye and coworkers³,4,5 on copper and silver; and of Lacy and Gensamer6 and of Austin7 on iron may be mentioned. Titanium is one of the few elements offering the possibility of a similar study of interstitial solutes since, unlike most metallic elements, it exhibits extended solid solubility for most of the interstitial solutes—hydrogen, boron, nitrogen, oxygen, and carbon. This paper reports a survey of the effects of dilute solutions of nitrogen, oxygen, and carbon on the mechanical properties of high-purity alpha titanium. Previous Work: Van Arkel and De Boer showed" that high purity titanium was quite ductile and De Boer, Burgers and Fast established".' that not only were oxygen and nitrogen very soluble in solid titanium but that, long before the limit of solid solubility of either had been reached, these interstitial solutes rendered the metal brittle. Their electrical resistance data as a function of

Jan 1, 1951

By G. Krauss, W. Pitsch

The fine structure of the bcc martensite formed in an Fe-33 wt pct ATi single crystal of arrstenite is sho~on by transmission electron microscoPy to consist of combinations of transformation twins, stacking faults, deformation twins, and regular arrays of parallel screw dislocations. These structures constitute evidence for the multiple lattice-invariant deformations which operating during the formation of martensite could produce the real habit-plane scatter measured by a two-surface analysis of the plates formed in the single crystal of this investigation and reported in the literature for other Fe-Ni rnartensites. CRYSTALLOGRAPHIC theories1,2 of martensitic transformation show that the habit plane of martensite in a parent lattice is dependent in part upon an inhomogeneous distortion or lattice-invariant deformation which takes place on a fine scale within a martensite plate during its formation. Several recent theoretical papers3,4 have addressed themselves to an analysis of a wide variety of conceivable lat-tice-invarient deformations and the habit planes which they produce, while experimental investigation have been concerned with either the measurement of habit planes or the description and identification of the martensitic fine structure which reflects the nature of the lattice-invariant deformation operating during transformation. In Fe-Ni alloys with subzero Ms temperatures, the group of alloys with which this paper concerns itself, habit planes have often been found to scatter an amount greater than might be expected from possible experimental errors,5-7 and fine twinning has been identified as a major constituent of the fine structure of martensite.8-11 It has been suggested3,4 that more than one type of invariant shear occurs during martensitic transformation. This possibility has been experimentally supported12,13 by the observation of both dislocation configurations and twinning in a single martensite plate. The purpose of this paper is to report additional evidence for multiple lattice-invariant deformations in martensite and so to account for the real scatter in the habit planes of the martensite plates formed in Fe-Ni alloys. EXPERIMENTAL PROCEDURE The Fe-Ni single crystal was produced by pulling a high-purity iron and nickel charge through a single-crystal vacuum furnace in an alumina crucible. The crystal was double-melted to promote homogeneity and to increase its size by further additions on the second pass. In its final form the crystal was 4 cm in diam and 5 cm long. The nickel and carbon contents were analyzed at 32.9 and 0.006 wt pct, respectively. The austenite of this alloy first transformed to martensite by bursts at about -120°C, and, to preserve as much of the austenite as possible, all transformation was performed just below -120°C. Some observations were made on transformed samples which had been heated for 2 min at 340°C. It is assumed that the features of the martensite of these samples, Figs. 1 and 4, are the same as those of the as-quenched martensite. Orientation of the crystal by X-ray diffraction established 10.735 0.609 0.3161? as the axis of the crystal, an orientation that was checked within 2 deg by neutron diffraction. Further checks by electron diffraction of samples cut normal to the axis confirmed this orientation within the larger limits of error inherent in electron diffraction of thin foils. The X-ray orientation was the one used for the two-surface analysis of the martensite habit planes. A two-surface analysis was performed on the quadrant of the single crystal which had been oriented by both X-ray and neutron-diffraction techniques. Photomicrographs at X50 were made on two surfaces along an edge 2 cm long. Fiducial marks and the fact that many of the plates were almost completely surrounded by retained austenite made good matching of individual plates on two surfaces possible. The habit-plane trace on a surface was taken as the best line parallel to the long axis of a plate. A measure of the accuracy afforded by this criterion was provided by a family of very large plates which appeared at intervals along the entire 2 cm length of the edge. The plates all had habit-plane traces within 2 deg of one another. Many of the plates did not show midribs and, therefore, the use of midribs7 to represent habit-plane traces was not feasible in this investigation. The over-all experimental accuracy is estimated to be better than ±2 deg. Samples for transmission examination in a Siemens Elmiskop I at 100 kv were prepared by cutting 2-mm-thick discs from the single crystal, removing about 0.5 mm by chemical polishing,14 trans-

Jan 1, 1965