Stellite-6 coatings were formulated on two Ni-base superalloys, namely Superni 75 and Superni 600, by a shrouded plasma-spray process, and the oxidation behaviour of these coatings has been investigated in air and in an aggressive environment of Na2SO4- 60%V2O5. Accelerated oxidation tests were conducted in a silicon-carbide tube furnace under cyclic conditions at an elevated temperature of 900°C for 50 cycles. Each cycle consisted of 1 h heating and 20 min cooling in air. A thermogravimetric technique was used to approximate the oxidation kinetics. The corrosion scales were characterised by XRD, SEM/EDAX and EPMA analysis. It has been observed that the coatings nearly followed the parabolic rate law of oxidation. Overall weight gain conceived in air was just 51% of that in the aggressive environment in the case of coated Superni 75, whereas in case of coated Superni 600, the cumulative weight gain in air was found to be one-third of that in the Na2SO4-60% V2O5 atmosphere. Furthermore, the coating showed very good adherence to both of the substrates during the course of air oxidation, whereas some superficial cracks were observed near the edges of the specimens during the molten salt induced oxidation. XRD analysis revealed the presence of phase-like CoO, CoCr2O4 and Cr2O3 in the oxide scales, which are reported be protective against high-temperature oxidation. The XRD results were further supported by SEM/EDAX and EPMA.

Jan 1, 2005

By K. Waters, A. Navarra, T. Grammatikopoulos

Strategic decisions to develop a mineral deposit are subject to geological uncertainty, due to the sparsity of drill core samples. The selection of metallurgical equipment is especially critical, since it restricts the processing options that are available to different ore blocks, even as the nature of the deposit is still highly uncertain. Current approaches for long-term mine planning are successful at addressing geological uncertainty, but do not adequately represent alternate modes of operation for the mineral processing plant, nor do they provide sufficient guidance for developing processing options. Nonetheless, recent developments in stochastic optimization and computer data structures have resulted in a framework that can integrate operational modes into strategic mine planning algorithms. A logical next step is to incorporate geometallurgical models that relate mineralogical features to plant performance, as described in this paper.

Jan 1, 2017

By Y. S. Sun, Northeastern University, W. B. Li, P. Gao, Z. Y. Zhang, J. W. Yu

"The boron-bearing iron concentrate was extracted from ludwigite ore by the process of magnetic-gravity separation. In order to fully utilize the refractory ore and meet the boron consumption of China, a novel process for separation of boron from iron in boron-bearing iron concentrate was proposed in this paper. In particular, laboratory scale experiments of improving boron reactivity were performed. Fine boron-bearing iron concentrate briquettes were reduced by bituminous coal completely at 1125 °C for 150 min. The effect of sodium carbonate, which was used as an additive in the roasting process, was investigated. The addition of sodium carbonate decreased the boron reactivity and facilitated the volatilization of boron. The influence of diverse cooling methods of the reduced samples on the boron reactivity was studied. The results indicated that boron reactivity could reach up to 80.76% when the reduced samples were cooled by rapid water quenching. In addition, the magnetic material containing 92.71 % Fe with a recovery of 95.11 % and boron-rich non-magnetic material containing 14.51% B2O3 with a recovery 88.85% could be obtained by low-intensity magnetic separation. The magnetic material and boron-rich non-magnetic material were good raw materials for steel-making and borax production, respectively.INTRODUCTION Ludwigite ore is abundant in Liaoning province of China, with 28.43 Mt B2O3 accounting for 57% of the boron resources of the country (Liu et al., 2006). However, it has not yet been utilized on an industrial scale due to its complex mineralogy and fine mineral dissemination (Wang, Wang, Ding, Ma & Xue, 2012). At present, boron-bearing iron concentrate and boron concentrate can be obtained from ludwigite ore using magnetic-gravity separation. The boron concentrate contains B2O3 12%~16%, which can be used as a high-quality raw material for the boron chemical industry after activated roasting, but the B2O3 content in the iron concentrate reaches up to 4%~6%. In order to further separate boron and iron from boron-bearing iron concentrate, a blast furnace and a solid pre-reduction followed by electric arc furnace melting have been proposed (Liu, Cui & Zhang, 1998; Wang et al., 2012). However, both of these two current routes face the same crucial problem that molten boron-rich slag has to be cooled slowly to obtain the alkali-dissolution activity of boron, which affects the yield of boron resource."

Jan 1, 2016

By J. Kempken, R. Hagmann, C. -P. Reip, W. Hennig

The CSP technology symbolizes a highly productive process for the cost-effective production of steel grades with a range of sophisticated properties comprising both the inner quality of hot strip, its surface formation as well as the relating technological characteristics. Thanks to extensive development work undertaken during the last 15 years, the range of steel grades that can be produced was continuously expanded and the process technology optimized. The present paper describes the ongoing development work concerning the production of higher-strength, microalloyed pipe steels. The resulting hot strip, due to the associated thickness and the potential pipe diameters, is particularly suited for being processed to HFI-welded pipes. Based both on ferrite-pearlite as well as very fine-grained, ferrite-bainite hot-strip microstructures, strength levels of up to grade API X80 can be realized. It can be demonstrated that hot strip produced in a CSP plant has very good toughness values at temperatures down to -60°C and can even make application with required sour-gas resistance possible.

Jan 1, 2005

By J. L. Llanca

The New Level Mine project (NLMP), the planned underground expansion of the El Teniente mine in Rancagua, Chile, is expected to reach a daily extraction rate of 137 to 180 ktpd upon achieving full capacity. Production is planned to start in the year 2017 and the current plan is to meet that target through two development phases, from the year 2012 to 2014 and from the year 2015 to 2017. To achieve the 2012 to 2014 underground development schedule, the ventilation requirements have been estimated in the range of 189 m3/s (400 kcfm), and cannot be made available without significant modifications to the current system of El Teniente. As a result, a certain number of alternatives were explored to find a solution to this shortfall, for example, adding raises to generate parallel airways and installing fans to reinforce the current ventilation system. From the alternatives studied, the installation of a second main fan (system) in parallel to an existing one was identified as the best solution, and selected for implementation, however the location was not ideal and there were concerns as to the operation of both fans once the second fan was installed. This paper presents the study used to estimate the operational points of both the current and the new fan, and to justify the parallel installation of the additional main fan. An additional computational fluid dynamics study was undertaken to validate the operational point, given the particular geometry of the fan?s location and placement, to guarantee a stable operation of the fans. Finally, the protocols arising out of this work for starting the fans, and operating them in parallel to avoid generating a stall condition and damaging the investment are discussed.

Aug 1, 2013

By C. Feng, D. W. M. Arrigan

Arsenic is often associated with gold mining operations and poses a significant health and environmental hazard. While a number of technologies are available for removing arsenic, none of them is effective under all conditions. Although adsorption is a promising approach, most methods focus on the purification of water under neutral or acidic conditions and tend to be less effective in gold mining process waters, operating under alkaline conditions. In this study, the removal of As (III) and As (V) from both arsenic-only solutions and simulated process waters using composite magnetic nanoparticles was investigated. The nanoparticles consisted of magnetite (Fe3O4) or maghemite (?-Fe2O3) cores covered by various metal oxides with Langmuir adsorption capacities of As (III) and As (V) ranging from 31.4 to 79.1 mg/g and 10.2 to 25.5 mg/g, respectively, in arsenic-only solutions at pH 9. Their adsorption capacities were further recognised by the adsorption tests conducted in simulated process waters. The ability to remove As (III) is of particular importance as it is harder to remove it from alkaline solutions. The magnetic cores allow simple and efficient magnetic recovery of the As-loaded nanoparticles.

Jan 1, 2017

By T Salman

The construction and use of the B.E.T. (gas adsorption) apparatus is described. Examples are given for the determination of large and small surface areas using nitrogen and krypton. Introduction A NY study of the milling of ores from crushing to grinding, classification, and concentration and finally dewatering of the products involves solid particles which are either in contact with a gas or a liquid phase. The surface area of the solid and its characteristics constitute important parameters in all mineral dressing operations. The success of any particular operation is dependent on the interaction of the surface of the solid particles with the gas or the liquid phase. Particle size and specific surface (surface area per unit weight) continue to be important parameters in the flotation research associated with the adsorption of collector molecules or ions on mineral particles, as in the early years of mineral dressing research (1). In order to understand the mechanism of the flotation process, it is essential that the surface properties of the adsorbent be known.

Jan 1, 1965

By Robert A. MacGregor

"Following several months of test work, water leaching in mined-out areas at Stanrock commenced on a production basis in February, 1963. A combination of fast high-pres-sure washing and rewashing of stopes on a predetermined cycle, and the intermittent sprinkling of low-grade heaps, using both fresh water and recirculated acid water, has proved most successful. There was also a correlation of daily sampling data points to a relationship between the leach water grade and the grade of the material being washed, the leaching time and the location along the dip. An increasing tolerance for uranium by the acid-producing bacteria is also indicated. A steady production rate of 10,000 to 12,000 lbs. of u.08 per month is being maintained, with an over-all mine water grade of 0.25 lb. per ton and a pH of 2.3."

Jan 1, 1966

By Yuyong Li, Liangman Zhang, Zhaolian Wang, Shun Wang, Ltd. Shandong Huate Magnet Technology Co., Fengliang Liu

"Introduce a newly revolutionary magnetic separator - Raising Concentrate Grade and Decreasing Dregs Content Magnetic Separator Series JCTN (i.e. RCG&DDC MS JCTN). HUATE® JCTN is designed for rinsing, purification, desliming and thickening of the magnetic minerals as per different requirements. Adopting 240°-270° larger magnetic element with multi-poles and magnetic pulsation, and combining the devices of multi-channel rinsing water and top flushing water and new style tank, HUATE® JCTN can improve another 2%-10% concentrate mFe% than the traditional MS without lowering the concentrate recovery rate. Thereby, it solves the uneasy concentrate upgradation problem of the traditional MS resulting from the magnetic aggregation. Now, JCTN has been successfully applied in more than 30 mines in Australia, China and Russia, e.g. Sino Iron of CITIC PACIFIC MINING MANAGERMENT PTY LTD. HUATE® JCTN can optimize the industrial processing line by: 1) improving the discarding rate before milling to discard the necessary tailing ASAP; 2) getting in advance the final concentrate after milling. One JCTN can replace many traditional MS in series. In some way, it can also replace the anti-flotation separation process.INTRODUCTIONWe’re writing to introduce a newly revolutionary magnetic separator - Raising Concentrate Grade and Decreasing Dregs Content Magnetic Separator Series JCTN (i.e. RCG&DDC MS JCTN). HUATE® JCTN is designed for rinsing, purification, desliming and thickening of the magnetic minerals as per different requirements."

Jan 1, 2016

By M. N. Collison

"In 1960, with the opening of the Chisel Lake mine near Snow Lake, Manitoba, the Hudson Bay Mining and Smelting Co., Limited, commenced a new phase in their mining operation -that of bringing ore to Flin Flon over 100 miles of railroad.The schedule of operations required to accomplish this, together with an outline of some of the problems of handling ore at 40° and 50,0 below zero, are discussed. The facilities required to thaw and unload from twenty to fifty cars per working day are also described."

Jan 1, 1966

By W. S. Hargratt

THE present era of exploitation of the Little Long Lac and Sturgeon River areas commenced in 1925, when Beardmore Gold Mines started development of what is now the property of Northern Empire Mines. A shaft was sunk in 1927-28 and a very limited amount of underground work was carried out, following which the property was shut down. It remained idle until 1932, when Empire Star Mines, a Delaware Company, optioned the property. This Company formed the Northern Empire Mines Company, Limited, to operate the mine, and immediately instigated an aggressive programme of surface and underground development. By the summer of 1933, sufficient ore was indicated to justify the installation of a small mill. The decision was also reached to bring in electric power. A power-line was built from Hydro, the Ontario Power Commission's development on the Nipigon river, to the mine, a distance of approximately 50 miles. This work was entirely financed by Northern Empire Mines. Mill construction was commenced in October, 1933, and completed by March, 1934, thus making this mine the first producer in this district.

Jan 1, 1940

By H. J. McQueen

The irregular history of Mg wrought products is briefly described. The temperature and strain rate dependence of microstructural evolution, flow stress and ductility of Mg alloys in hot working, are described. The flow curves rose rapidly to a peak stress which was lower as temperature T rose and strain rate e declined and above 300°C the curves extended into plateaus until failure. Clearly grains not oriented for slip undergo mechanical twinning in the initial stages (a 0.15) at all temperatures. Basal slip proceeds in suitable grains and in the twins. The stress concentrations at grain and twin boundaries lead to slip on non-basal systems and to the formation of subgrains with greater dynamic recovery (DRV) at higher T or lower e. With increasing strain, misorientation builds up resulting in dynamic recrystallization (DRX) first at twin intersections and later at grain boundaries which have become quite serrated. Even after extensive straining at high temperatures, the new grains are found mainly along the boundaries of the original grains, leaving their centers with only basal slip except when nucleation at twins leads to completion of DRX throughout a grain. Despite similar shear modulus and melting point to Al, hot mechanical forming behavior of Mg alloys differ due to differences in crystal slip systems, twinning, and second phases. Moreover, the influences on forming of alloy additions (solutes, segregation in casting, dispersoids, precipitation) and impurities are not as well catalogued as for Al. Despite the benefits from dynamic recrystallization, varied grain orientation effects, heterogeneous substructures and the resulting stress concentrations result in considerably lower ductility for Mg alloys at the same stress level as for Al materials. Application of these theories to extrusion, rolling and forging and the effects on product properties are surveyed.

Jan 1, 2006

By M. M. Helm

Samples sourced from the Goldstrike property in Nevada USA, have been evaluated in terms of their preg-robbing capacity and the physical structure of the graphitic carbon component in the carbonaceous gold ore. The study highlights a wide range in preg-robbing capacity between samples collected from the Betze-Post open pit and Rodeo underground mine. The physical structure of the graphitic carbon was assessed using Raman spectroscopy, and is found to play an important role in influencing preg-robbing behaviour. Differences observed in the physical structure of graphitic carbon are thought to be the result of hydrothermal events that occurred at Goldstrike.

Jan 1, 2011

By Dong-Hyeun Koh, Yun-Soo Lee, Min-Seok Kim, Hyoung-Wook Kim

High strength AA7068 (Al - 7.88 wt.% Zn - 2.68 wt.% Mg - 2.07 wt.% Cu) aluminum alloy strip was successfully fabricated by horizontal-type twin roll casting. A simulation technique was used to obtain the range of casting conditions for fabricating strip without defects. The cast strip with thickness of about 5 mm was hot rolled, intermediate annealed, cold rolled to final thickness and subsequently annealed at various temperatures. Tensile properties of annealed and the aged specimens were evaluated at ambient temperature. Tensile strength and elongation of the annealed sheet are about 365 MPa and 28%, respectively. Also, the tensile and yield strength after the aging at paint baking condition (180 °C x 0.5 h) are 586 MPa and 551 MPa, respectively. Therefore, it is expected to show good formability prior to press or stamping and also provide high dent resistance after paint baking treatment.

Jan 1, 2015

By Luke Meers

Roadway development rates in Australian underground coal mines are failing to keep pace with modern longwall systems and are unlikely to sustain further improvements in longwall productivity into the future unless step change improvements to roadway development equipment and practices are made. Bottlenecks which limit and constrain improved production and impact the safety of operators have been identified through a series of industry surveys, with the manual installation of strata support materials, consumables delivery, coal haulage and monorail installation being highlighted as major areas to improve development performance. This paper looks at research being carried out at the University of Wollongong in designing an integrated system approach for the fully automated handling and installing of development consumables, and the systems required to support these activities. A series of hard automation manipulation devices have been demonstrated in surface trials and the results indicate that rapid roadway development can be achieved.

Aug 1, 2013

By N. Erarslan, M. Ghamgosar

With the increased use of mechanized rock excavation, there have been developed internationally a number of methods to assess the abrasivity of rock materials. These methods range from determination of abrasive and hard mineral content using petrographic thin section analysis to weight loss or rate of wear flat development on specified test pieces. The Cerchar abrasivity index (CAI) test has been widely accepted for the assessment of rock abrasiveness and is determined as the abrasion of a steel pin after scratching over the freshly-broken or saw-cut surface of a rock. Two types of testing devices are in use today: (i) the original ‘Cerchar apparatus’, and (ii) the ‘West apparatus’, which was adopted herein. The CAI is calculated from the measured diameter of the resulting wear flat on the steel pin after 10mm scratching. This test has been considered to provide a reliable indication of rock abrasiveness for isotropic rocks. However, a great amount of rocks in natureis anisotropic. Phyllite is an anisotropic and foliated metamorphic rock and various types of phyllite specimens were tested in this research. Although phyllite is a type of rock primarily composed of quartz and the expected CAI value can be high, mechanical cutting of this rock should not be very problematic compared with igneous rocks have same CAI value. As phyllite is a foliated metamorphic rock, most of the specimens split into sheets through the quartz seam by the tip during scratching normal to the axis of quartz seams. Hence, viability assessment of Cerchar abrasivity test and F-Schimazek index values for the anisotropic rocks is investigated in this research.

Jan 1, 2015

By F. Y. Hsiao, H. C. Kao

Underground excavation in hard rock is normally stable at shallow depth except for wedge failure. However, the excavation depth is rapidly increasing recently. In high overburden stress condition, the integrity of rock would be destroyed with degrading rock strength. Therefore, understanding both the peak and the post-peak strengths of hard rock are necessary to assess the tunnel stability at depths. The characteristic of the post-peak strength is seldom studied in Taiwan in the past. Various estimation methods for the post-peak strength degradation were briefly reviewed in the paper. Based on the Geological Strength Index (GSI) system is widely used in the determination of the rock mass strength, the quantitative residual GSI system was adopted to estimate the possible strength degradation for a hydraulic tunnel in Taiwan. The Mohr-Coulomb model (no strength degradation) and the post-peak strength degradation model (strain softening model) were used to simulate the excavation of the case tunnel at different depths. The analyses demonstrate that the tunnel is in stable condition at 600m of depth. And the effect of the postpeak strength degradation on tunnel deformation is progressively significant with increasing tunnel depth. Approximate 3-5 times of increase in crown settlement and horizontal convergence would occur when post-peak strength degradation are considered at 2400m of depth. Severe tunnel deformation may endanger the tunnel stability. Modeling results reveal that the post-peak strength degradation has a great effect on tunnel stability under high overburden stress condition, which should not neglect in deep tunnel design.

Jan 1, 2015

By Turgut Yalcin

"In this study, potential benefits of focculant usage were explored in the processing of mill tailings by hydrocyclones. Tests conducted on copper-nickel mill tailings have demonstrated that, under suitable conditions, flocculation could significantly enhance solid-liquid separation in hydrocyclones. For example, at a feed pulp density of approximately 9%, focculant-assisted hydrocyclone produced an underflow with over 98% solids recovery, compared to a recovery of less than 53% with conventional hydrocyclone. However, feed pulp density was found to be a critical factor, and tailings with pulp densities of greater than about 15%required a two-stage hydrocyclone operation where the focculant-assisted hydrocyclone was employed at the second stage to process the overfow of a conventional hydrocyclone.The underflow and overflow products obtained from the focculant-assisted hydrocy-clone may be discharged into tailings dams in the same manner as those produced by gravity thickeners. The focculant-assisted hydrocy-clone would, however, provide a higher throughput."

Jan 1, 1996

By M. Mezbahul-Islam

Thermodynamic modeling of the Mg-Cu-Ni system is carried out as a part of multi component thermodynamic database for Mg alloys. This system is being modeled for the first time using the modified quasichemical model, which considers the presence of short range ordering in the liquid. The thermodynamic descriptions of the binaries Mg-Cu, Cu-Ni and Mg-Ni have been extrapolated to the ternary Mg-Cu-Ni system using Toop geometric model. The constructed database has been used to calculate and predict thermodynamic properties, isothermal sections and liquidus projections of the Mg¬Cu-Ni system, which showed very good consistency with the experimental data.

Jan 1, 2011

By D. V. Dorling, J. T. Bowker, J. A. Gianetto

Over the last few years, interest in the development and construction of large diameter, high pressure pipelines from the Mackenzie Delta in northern Canada and Alaska's North Slope has steadily increased as a result of the projected decline in recoverable natural gas from existing reserves in western Canada. The success of such enormous pipeline projects, which will require utilization of a strain-based design approach, is largely based on successful application of high strength line pipe steels, such as X80 and X100. To fully realize the economic benefits of high strength steels, welding processes and procedures must be developed to ensure that the requirements for high strength and good low temperature toughness are confidently obtainable in field girth welds used in the construction of such pipelines. This study aims to provide a better understanding of the factors that control weld metal strength and toughness for a series of mechanized X100 girth welds produced using a range of narrow-gap gas-metal arc welding procedures. The attainment of high yield strength (> 810 MPa) is considered to be an important target to ensure overmatching strength relative to the longitudinal property distribution of X100 line pipe steel. Some factors that have been considered in this evaluation include influences of gas-metal arc welding process variants (single and multi-wire) and changes in welding procedure specifications, including joint preparation. Key components of this work relate to the reliable measurement of weld metal strength variation through-thickness and as a function of position around the circumference of a given girth weld.

Jan 1, 2005