By Alfred Boyles

"HEREDITY"' in cast iron has been a subject of much discussion. Numerous experimenters have found that the properties of gray iron may vary greatly without corresponding variations in composition or thermal treatment. The main structural difference in such cases is in the size and distribution of the graphite flakes and the explanations given usually attribute this difference to some chemical element not shown by ordinary analysis or to some physical factor, such as inclusions in the melt. It cannot be said that any of these theories is completely satisfactory. Much remains to be learned about cast iron and for this reason a study of the material was undertaken as a part of the program of fundamental research at Battelle Memorial Institute. A review of the literature indicated that very little systematic work had been done on the mecha-nism of freezing in cast iron. The experiments described below are largely concerned with that problem.

Jan 1, 1937

By K. A. Jackson, J. D. Hunt

A general theory for the growth of lamellar and rod eutectics is presented. These modes of growth depend on the interplay between the diffusion required for phase separation and the formation of interphase boundaries. The present analysis of these factors provides a justification for earlier approximate theovies. The conditions for stability of rod and Lanlellar structures are consitleved in terms of the mechanisms by which the structure can change. The mechanisms considered include both small adjustments to the lnnzellar spacing due to the motion of lamellar faults, and catastrophic changes due to instabilities. It is concluded that stable growth occurs at or near the minimum interface undevcooling for a gizierz growth rate. The conseqrlences of the existence of a diffusion boundary layer at the interface are discussed. The experimental results for the variation of growth rate, undercooling, and Lanzellar spacing are cornpared with the theory. We believe that the theory presented in this paper provides an adequate basis for understanding the complex phenomena of lanzellar and rod eutectic growth. The growth of lamellar eutectics has been the subject of several theoretical and many experimental studies. The foundations for the theoretical work were laid by zenerl and Brandt2 in their analyses of the growth of pearlite. Zener estimated the effect cf diffusion, and took into account the surface energy of the lamellar structure. He found that the lamellar structure could grow in a range of growth rates at a given undercooling provided the lamellar spacing was appropriate for the growth rate. Since pearlite grows with only one growth rate and one lamellar spacing at a given undercooling, there is clearly an ambiguity in the theory. Zener removed this ambiguity by postulating that the growth rate was the maximum possible at the given undercooling. He predicted then that the product of the growth velocity v and the square of the lamellar spacing A should be constant, i.e., A2v = const. Brandt2 started out by assuming that the interface between the lamellae and austenite was sinusoidal. Because of this, the ambiguity encountered by Zener did not arise. Brandt was able to obtain an approximate solution to the diffusion equation, but, since he did not take into account the surface energy, his considerations are incomplete. Tiller3 applied some of these ideas to the growth of eutectics, and proposed a minimum undercooling condition to replace the maximum velocity condition used by Zener. These conditions are formally identical. Hillert4 extended the work of Zener. He found a solution to the diffusion equation assuming the interface to be plane. Taking surface energy into account, and applying Zener's maximum condition, he was able to calculate an approximate shape of the interface. Jackson et al.5 used an iterative method employing an electric analog to the diffusion problem to refine the calculation of interface shape. It was found that the interface shape calculated from a plane-interface solution to the diffusion equation was negligibly different from the exact solution. The method provided an analog only for eutectics for which the volumes of the two phases are equal, growing from a melt of exactly eu-tectic composition. There has also been considerable experimental work on eutectics, Several experimenters8-10 found that A2v is constant as predicted by Zener.1 Hunt and chilton10 demonstrated that ?T/v1/2 is also a constant for the Pb-Sn system as predicted. Lemkey et al.11have recently found A2v to be constant for a rod eutectic. In the present paper, we present the steady-state solution for the diffusion equation for a lamellar eutectic growing with a plane interface, for the general case, that is, with no restriction on the relative volumes of the two phases, and with the melt on or off eutectic composition. A similar solution is also found for a rod-type eutectic. Expressions are obtained for the average composition at the interface and the average curvature of the interface. These equations for the average composition and curvature are similar in form to those derived by Zener1 and Tiller,3 and provide a justification for some of the approximations made by these authors. The mechanisms by which the spacing in a lamellar structure can change are considered. The important mechanism for small changes in lamellar spacing involves a lamellar fault. Examination of the stability of lamellar faults leads to the conclusion that the growth occurs at or near the extremum.* The insta- bilities which can develop in a rodlike structure are also discussed, resulting in the conclusion that this structure also grows at or near the extremum. Comparison of the conditions for rod and lamellar growth permits a prediction of the surface-energy anisotropy required to produce rods or lamellae for various volume-fraction ratios. The diffusion equation predicts the existence of a diffusion boundary layer at the eutectic interface unless the eutectic has 0.5 volume fraction of each phase and is growing into a liquid of eutectic composition. This boundary layer is such as to make the composition in the liquid at the interface approximately equal to the eutectic composition. This boundary layer permits changes in composition during the zone refining of eutectics. Photographs of the eutectic interface of a growing transparent organic eutectic system have been made. Both the components of this eutectic are transparent organic compounds that freeze as metals do.12 The in-

Jan 1, 1967

By H. O. Hofman

INSTITUTE OF TECHNOLOGY, In deternlining experimentally the fusibility of clays, two kinds of methods may be distinguished—the direct and the indirect. Of the direct methods, that of Seger has found

Jan 1, 1899

By AIME AIME

ARRANGEMENTS for the Annual Meeting of the Institute were well advanced at the end of December as the following program will show. Heretofore this has been printed separately, but its inclusion in the Annual Review issue of MINING AND METALLURGY will, it is hoped, make it more easily available for reference until the final program is issued, which will be distributed at the meeting. Added details will appear in the February issue. Last year's meeting drew a record crowd of over 2300 which should be exceeded this year. Early reservations at the headquarters hotel, the Waldorf-Astoria, or any other convenient hotel are desirable, as are prompt reservations for the Annual Dinner. No one need worry about too much speechmaking this year, for the honors will be awarded and accepted in a few words instead of a few paragraphs, in seconds rather than minutes.

Jan 1, 1939

By Benjamin C. Craft

A review of development in North Louisiana during 1936 centers around the Rodessa field, in Caddo Parish. Continued extension of the

Jan 1, 1937

By Thomas T., Read

T HE preceding chapter has recorded the initiation of mineral industry education during the period 1890-1910 in numerous institutions that had not previously offered it. It should also be emphasized that in many institutions where instruction had begun before 1890, as recorded in earlier chapters, but had not yet become firmly established,, this period was one of marked growth and development. This was not universally true, however, for at the Universities of Pennsylvania, Michigan, Illinois, Wisconsin, Washington (St. Louis), Iowa, Vanderbilt and Tennessee, and at the Polytechnic College of Pennsylvania, mineral industry instruction was being dropped during this period, instead of gaining in strength. It is necessary to emphasize this, because writers on the subject have not infrequently , attempted to make a much too simple correlation between mineral -discovery or production and the intensity of student interest in mineral industry curricula. It would naturally be true that periods of large mineral production would, in general, coincide with cycles of business prosperity, and the latter are conducive to starting new ventures, educational as well as business. It should be equally evident that opportunities for business and professional success might, in such periods, appear to increase at a more rapid rate in industries other than mineral, or in the utilization of minerals rather than in their production. The author has not been able to perceive any simple and clear relation between interest in mineral industry education and mineral discovery, production, and utilization, or general business prosperity. On the contrary, the more the problem is studied the more complex the factors involved in it appear to be. In a later chapter an attempt will be made to analyze them in more detail.

Jan 1, 1941

By John Birkinbine

Secretary's Note.—In printing this paper in the present volume, the figures given in the pamphlet edition have been brought more nearly up to date, the product of 1899 being in many instances inserted. Iron-Ore Resources. In a paper presented to the Institute in 1897,* I discussed the iron-resources of the United States as then developed, calling attention to some principal sources upon which other countries depended. The following statement will give a general idea of the amounts, as compiled from the latest official records, of ores won, and metal produced, in the nations which are important contributors to the world's output. Unfortunately these are not all contemporaneous, since in some countries the statistics do not appear until after one or more years. The statement covers not only pig-iron and iron-ore, but also manganese-ore —the manganese mined being principally used in the production of spiegeleisen or ferro-manganese, and these alloys being generally included in the pig-iron output. Table I, which epitomizes the present situation, shows respectively the countries and the quantities of iron-ore and man-

Jan 1, 1901

By Eugene Guccione

Fear of inflation is one important reason for the rebirth of interest in the stock market, and natural resources are the best investment in an era of rapid inflation.

Jan 6, 1976

By L. E. Tanner

A study was made of the transformation kinetics of the commercial titanium-base alloys, Ti-2.5Al-16V and Ti-4A1-3Mo-1V, using two different heat treatment cycles: 1) step-quenching to aging temperatures from a ß solution anneal and 2) water-quenching from an a+ß solution anneal followed by reheating to aging temperatures. Metallographic examination and hardness testing provided the major portion of the data, while electrical resistivity, dynamic elastic modulus, and X-ray diffraction techniques were also used to obtain critical or confirnzatory data. TTT diagrams were constructed from these results. The sheet alloys, Ti-2.5Al-16V and Ti-4Al-3Mo-lV, are of current interest to the Department of Defense. As an aid to the planning of their respective heat treatments, a program was carried out to determine the transformation kinetics of these alloys using ß and a + ß reference states. This paper presents the TTT diagrams constructed from data obtained by metallographic examination and hardness testing, as well as by X-ray diffraction, electrical resistivity, and dynamic elastic modulus determinations. EXPERIMENTAL PROCEDURE Materials—Sheets of the alloys were obtained from the producers in the "mill anneal'' condition and were tested prior to shipment to assure their meeting mill specifications. Chemical analyses were also supplied and are presented in Table I. Heat Treatment—The majority of the data presented in this study were obtained from hardness testing and metallographic examination. Sample coupons were cut from the alloy sheets and heat treated on a mass scale. The annealing cycles were operated in the following manner: 1) The ß solution anneals were carried out in a horizontal tube furnace with the bare samples protected by a dynamic helium atmosphere. Following this treatment, the samples were quickly transferred to lead, solder, or oil-bath furnaces for aging. After prescribed times at the various reaction temperatures they were water-quenched. 2) The second cycle simulated commercial practice, which requires the alloys be quenched to room temperature following the a + ß sotution anneal. This anneal was carried out in a muffle furnace with a dynamic helium atmosphere. The specimens were then reheated from room temperature to the reaction temperatures in lead, solder, or oil-bath furnaces, followed by water-quenching after prescribed times at these temperatures. Information concerning the critical temperatures of the alloys was obtained from the literature and solution treatments were based on these values. A summary of the solution annealing treatments is found in Tables II and 111. The aging temperatures for the (a - ß alloys ranged in 50°C intervals from 200°C (392oF) to approximately 50°C below the ß/a + ß transus in the first cycle and approximately 50°C below the a + ß solution temperature in the second. The transformations in these alloys were known to be rather rapid, and thus aging times started at 0.5 min and went to a maximum of 7000 min. Hardness Testing and Metallographic Preparation— Heat-treated samples were sheared and mounted in Bakelite with their cut edges exposed. After a flat surface was ground, the hardness was determined in Vpn on an Armstrong-Vickers machine utilizing a 20-kg load. Three to four impressions were made on each specimen. After this procedure, the hardness impressions were removed and the edge surfaces of the specimens were prepared for metallographic examination in the usual manner. The etchant was 20 pct HF and 20 pct HNO3 in glycerine. Electrical Resistivity—It has been shown that the isothermal reactions in titanium-base alloys can be followed by measuring the changes in e1etrical resistivity attending these transformations. As mentioned earlier, the reaction kinetics of a-ß alloys are rather rapid; thus, it would be expected that resistivity data obtained from these alloys would be more significant if measurements were made continuously at the respective aging temperatures. To accomplish this end a special apparatus, based on the current-potential principle, was assembled. Its design was derived from earlier devices constructed by Colner and zmeska1 4 and Levinson.5 The set-up provided for the heat treatment zof machined specimens (approximately 2 x l0-4in. in cross section by 3 in. in length) and the determination of their relative

Jan 1, 1962

By H. T. Sumsion, A. U. Seybolt

The results of an investigation of vanadium-rich V-O solid solutions are presented, indicating the structure and lattice parameters of two solutions, a and ß, and their approximate temperature-composition existence. The a solution is the terminal body-centered cubic one, and contains up to 3.2 atomic pct 0. The ß solution has an ordered body-centered tetragonal structure, is formed at 1270°C, and exists from about 15 to 22 atomic pct 0. From the evidence available, the various phase boundaries have no appreciable temperature dependence. Evidence has been found for a polymorphic transformation in pure vanadium at 1550°C. IN an earlier investigation' dealing with the preparation of pure vanadium by calcium reduction of the oxide, it was found that small amounts of oxygen drastically reduced the ductility of the metal. Because this effect was so marked, it was decided to make a study of the solubility of oxygen in solid vanadium. This report deals principally with this solubility and the nature of the phase relationships in the vanadium-rich region, particularly at temperatures below 1300 °C. However, during the investigation enough data on the V-0 system were obtained to make it appear worthwhile to present a tentative phase diagram up to the composition VO. The only significant prior work found on this system are the contributions of Klemm and Grimm,' and Mathewson et al.3 Klemm and Grimm prepared a wide range of V-O compositions by powder techniques including the compositions VO.l, VO.2, VO.3 and VO4 (9.1, 16.8, 23, and 28.6 atomic pct 0, respectively). The first three compositions were found to consist of a body-centered tetragonal solid solution, while the last also showed lines of VO (NaCl structure). They found that the parameter c, increased and the parameter a, decreased with increasing concentration of oxygen. For their composition VO.27, or about 16.8 atomic pct O, they cite the values a, = 2.948A, c, = 3.53A, and c/a = 1.2. Klemm and Grimm made no attempt to determine the solid solubility limit nor to construct a phase diagram. They did, however, give some data on the homogeneity range of VO, and they proposed a structure for the body-centered tetragonal solid solution; these points will be taken up later. Materials and Preparation of Samples The vanadium used in this investigation was prepared in the laboratory by the method previously mentioned.' A typical analysis is as follows: Fe, 0.007 pct; Si, 0.02; Ca, 0.06; C, 0.224; O2, 0.044; N,, 0.0017; H2, 0.003; and V, 99.34 ±0.3 (assay). The vanadium assay is probably low by about the error given. The impurities total about 0.36 which, if subtracted from 100, gives a purity of about 99.6. At the time material was being prepared for this work no suitable technique was available for melting vanadium without appreciable contamination. The procedure adopted therefore was to cut the calcium-reduced regulii into slices which were then rolled to strip about 0.025 in. thick for oxygen diffusion. Pieces of rolled vanadium of approximately 0.025xY4xl in. and weighing about 0.3 g were suspended in a vertical fused-silica tube which was part of an ordinary gas absorption apparatus. The silica tube was heated by an electric resistance-tube furnace which could be raised around the silica tube or lowered away from it as desired. This apparatus had no novel features which require detailed description. Other than the silica tube and furnace, it consisted of a glass system evacuated by a liquid nitrogen trapped mercury diffusion pump, a mercury-operated gas burette, a McLeod and a Pirani gage, and a mercury manometer. It was also equipped with suitably located stopcocks for isolating various parts of the system; the vacuum ordinarily attained was between 10" and 10-6 mm of mercury. Oxygen generated by decomposing MnO2 was passed through anhydrous magnesium perchlo-rate before introducing it into the gas burette and thence to the absorption chamber.

Jan 1, 1954

By R. M. Genevray, M. B. Bever, E. J. Suoninen

THE martensitic transformation in the ß-phase of the Cu-Zn system has been the subject of several investigations. The transformation is known to be reversible and to be affected by stress. Its temperature range has been determined as a function of composition. In the investigation reported here, the effect of tensile stresses on the transformation was investigated quantitatively. Some information was also obtained on the thermoelastic behavior of the martensite formed in the first stages of the transformation. Most of the experiments were done with alloy E of an earlier investigation;' this alloy analyzed 60.49 pct Cu and 39.51 pet Zn by weight. The methods of shaping and heat treatment were also essentially the same as those previously used. The stress was applied to the specimen immersed in a cooling liquid. The transformation was followed by measuring the electrical resistance with a Kelvin bridge and the elongation with a cathetometer. Fig. 1 shows the M, temperature as a function of stress. Resistance and strain measurements gave essentially identical values. The results suggest a roughly linear relation between M. and in the range investigated, up to 12 kg s mm". At higher stresses, plastic deformation begins to interfere seriously with this relationship. The increase of M, with stress is consistent with published work on the effect of stress on the martensitic transformation. The slope of the curve, 4°C per kg mm ", is of the same order of magnitude as the corresponding value calculated for steel.' Fig. 1 also shows the difference, AM, between the temperature of 50 pct transformation on cooling, as measured by changes in length, and that of 50 pct reverse transformation on heating. This difference, which may be considered a measure of the hysteresis, increases with stress; the decrease at highest stresses is probably associated with plastic deformation. Preliminary work using only resistance measurements was done with an alloy containing 60.15 pct Cu and 39.79 pct Zn by weight. The results indicated higher values o-F M, in agreement with the known variation of M. with composition.' The effect of stress on M, (2°C per kg mm-') was of the same order of magnitude as that shown in Fig. 1 for composition E. An increase in hysteresis with stress was also found. The following experiment was made in order to investigate a partially transformed structure. A specimen of alloy E was cooled to — 85°C under a stress of 4.7 kg mm-'. Under these conditions, the martensitic transformation started but did not go to completion. The stress was then released and the specimen cooled to — 105°C. Fig. 2 shows the measured elongation c. The first change in the slope of the curve indicates the beginning of the transformation under stress. Removing the load at —85°C caused a decrease in length to the value corresponding to the elastic elongation of the parent phase resulting from the applied stress. Hence, the marten-site formed in the first part of the experiment apparently disappears completely and without hysteresis upon the release of the stress. The increase in length on further cooling indicates renewed formation of martensite. These conclusions are consistent with the concept of "thermoelastic" martensite," which has been confirmed by test." Acknowledgments The authors are greatly indebted to Professor M. Cohen for his advice and encouragement. They also thank F. Paxton for assistance. Thanks are due the American Brass Co. which supplied the alloys. References E. Kaminsky and G. V. Kurdjumov: Zhur. Tekhn. Fiziki SSSR (1936) 6, p. 984. A. B. Greninger and V. G. Mooradian: Trans. AIME (1938) 128, p. 337. "J. E. Reynolds, Jr. and M. B. Bever: Trans. AIME (1952) 194, p. 1065; Journal of Metals (October 1952). 'A. L. Titchener and M. B. Bever: Trai~s. AIME (1954) 200, p. 303; Journal of Metals (February 1954). " 3. A. Kulin, M. Cohen, and B. L. Averbach: Trans. AIME (1952) 194. p. 661; Journal of Metals (June 1952). "J. K. Pate1 and M. Cohen: Acta Metallurgica (1953) 1, p. 531. 'C. Crussard: Comptes Rendus (1953) 237, p. 1709. ' G. V. Kurdjumov: Zhur. Tekhn. Fiziki SSSR (1948) 18, p. 999. G. V. Kurdjumov and L. G. Khandros: Dokl Akad. Nouk. SSSR (1949) 66. p. 211.

Jan 1, 1957

By C. Graeme-Barber, R. L. Bell, T. G. Langdon

An analysis is made of the formulas and ,methods used to estimate the contribution of grain boundary sliding to the overall strain of a polycrystal. The errors involved in the approximations and/or ,mistakes in earlier work are assessed quantitatively so as to make possible the critical use of previously published data. SINCE it has been found that, under conditions of very slow creep, the strain due to grain boundary sliding (?gb) may contribute as much as 80 pct of the total creep strain,1,2 it is obviously important to have reliable methods for estimating this grain boundary strain. In two recent papers Stevens3,4 has drawn attention to the pitfalls encountered in assessing ?gb. He criticizes 1) the assumptions made in the derivation of some of the formulas for ?gb, and 2) the indiscriminate averaging procedures used for obtaining the quantities substituted in these formulas. These and further criticisms of earlier work are mostly valid. Unfortunately the only formulas and procedures recommended are either impossible or very difficult to apply in practice. Furthermore no attempt is made to assess the errors involved by the earlier approximations or mistakes, and so it is not possible to make critical use of any of these early dab. The present article attempts to improve on these shortcomings by reference to empirical verification of easily applied formulas whose theoretical derivations involve some otherwise unjustifiable assumptions, and by a quantitative assessment of the errors in previous work. DEFINITIONS First it is necessary to define the terms and symbols to be used. The choice of symbols preferred here is a logical combination and extension of the v introduced by McLean5 and the u by Brunner and rant.' In Fig. 1 the two grains X and Y are displaced by the sliding vector AC. u is the component of sliding resolved along the stress axis, v is that measured perpendicular both to the stress axis and to the specimen surface, and w is that measured perpendicular to the stress axis but in the plane of the surface. Two angles define the orientation of the grain boundary: 8, between the stress axis and the surface trace of the boundary, and +, the internal angle on a longitudinal section cut perpendicular to the surface. In computing the strain resulting from the boundary displacement at all the in- dividual boundaries in a polycrystal the components u, v, or w are sometimes averaged along a longitudinal line (i.e., parallel to the stress axis), sometimes along a transverse line, and sometimes at randomly chosen boundaries. Averages obtained in these three ways are given subscripts 1, t, and r, respectively. Stevens rightly calls attention to the possibility of non-equiaxed grain shapes either at the start or at the end of deformation. In this article all values of numbers of grains per unit length will refer to measurements made before deformation. The subscripts 1 and t will be used for the number of grains per unit length obtained along longitudinal and transverse lines, r for that obtained by averaging along a number of randomly directed lines. FORMULAS FOR ?gb ?gt, as a Function of u. An obvious truth is that cgb can, in principle, be obtained by summation of all the v components at the boundaries intersected by a longitudinal line of known length I, viz.: where nl is the number of grains per unit length, parallel to the stress axis, in the unstrained specimen. There are assumptions in the analytic derivation of Eq. [I] due to Brunner and rant' but ~achinger' arrived at Eq. [la] by a rigorous method. Unfortunately the experimental procedure required by Eq. [ la] proves very difficult as boundary migration tends to obscure the points at which the longitudinal line meets the grain boundary and the errors on such measurements tend to be large, see Fig. 2. For example, on a specimen of Magnox AL 80 at a creep strain of 9.7 pct, 300 measurements of u obtained from the points of intersection of a longitudinal line with the grain boundaries gave ul = 8.95 ± 3.58 pm, or an error of ±40 pct, at the 95 pct confidence limit. These large errors due to migration may be avoided by measuring u from the separation of the segments

Jan 1, 1968

By A. D. K. Laird, C. A. Johnson

Drag coefficients for a cylinder being towed through water at constant velocity and also at constant linear acceleration were measured. Drag coefficients for constant velocity towing showed reasonable agreement with previous results. The drag coefficients found for constant acceleration showed little correlation with either the magnitude of the acceleration or the value of the modulus AD/V2 and tended to be slightly lower than those for constant velocity. INTRODUCTION For the design of offshore structures, wave forces acting on immersed cylinders are of importance. Several investigations have been made of these forces and of how they can be predicted from wave theories. A paper by Crooke' summarizes much of the work already done. More recent research by the Wave Research Laboratory at the University of California, Berkeley, has added much to the body of data collected under ocean wave conditions, but has not found a reliable method of force prediction from basic theories of wave motion. The present investigation is part of a long-range program to collect data with which to test current and future theories and correlations. The immediate objective was to measure drag forces on a circular cylinder subjected to linear accelerations over the range of Reynolds numbers between l04 and 105 where the drag coefficient was a constant for constant velocities. In particular, the effect of constant acceleration from rest and from uniform motion was to be investigated. The effect of acceleration may be evaluated in terms of drag coefficients. A useful resistance coefficient, C, is defined by the equation for total drag force, D, exerted by the fluid on the cylinder. DT =CSp V2/2.........(1) The coefficient C may be plotted as a function of the parameter AD/V2. Here D is the diameter and S is the projected area of the cylinder. The acceleration and velocity are A and V. The mass density of the fluid is p. An alternate drag coefficient, C, corresponds to the total force of the fluid opposing the motion minus the virtual mass force. This drag coefficient, arising from the velocity of the fluid, may be compared with that for the same cylinder in uniform motion. The similarities and differences between this coefficient as calculated for accelerated and for steady motion are of interest in the inverse process of predicting drag forces on cylinders under arbitrary conditions. One serious difficulty in this method is the specification of the virtual mass which depends also on the flow picture about the cylinder.1 EXPERIMENTAL EQUIPMENT The experiment was performed in the combination wave and towing tank at the Engineering Field Station of the University of California. The tank is 200 ft long, 8 ft wide, and 6 ft deep. The tow carriage is externally propelled by a cable, and the velocity of the carriage is maintained essentially constant by means of an am-plidyne. For the purpose of the present investigation, the speed control of the amplidyne was modified by inserting a linear speed control rheostat, which was rotated at a constant speed by a small d-c motor equipped with a slip-clutch. Accelerations which were constant over a reasonable length of time were thus produced. The magnitude of the acceleration depended upon the speed of the d-c motor and the limiting speed of the carriage. Data were obtained for a range of accelerations of 2 to 10 ft/sec,2 and a range of velocities of 2 to 15 ft/sec. An accelerometer (Statham Type C-2-350) with a range of ±2g was attached to the carriage and connected to a Brush analyzer and penmotor. A continuous coil of wire with 10 turns/ft wound around a fixed wooden form extending for a distance of 40 ft along the length of the tank was connected by an electrical contact mounted on the carriage to a Brush analyzer and penmotor, to give the time-position history for each run. The test cylinder was machined from solid aluminum alloy, 17-ST. to a diameter of 1.250 in., and could be

Jan 1, 1957

By D. G. Westlake

Alloys of poly crystalline Nb-H have been tensile tested at 77" and 120°K after slow-cooling and after quenching from room temperature. A rationale has been developed to explain the effect of cooling rate on ductility in terms of microstructure. The inferior ductility of the slow-cooled alloys in this temperature range can be attributed to the precipitation of coarse hydride particles that fracture in the early stages of plastic deformation. Quenching Produced much smaller hydride particles and a decreased tendency for initia-tion and popagation of cracks. Prismatic dislocation loops, punched into the matrix of quenched alloys, eliminate the yield point and may Play some role in the low temperature ductility of the quenched alloys. The difference in ductility between quenched and slow-cooled V-H alloys was even greater than that observed in the N b-H alloys. It is well known that the ductility of Nb-H and V-H alloys decreases with increasing hydrogen concentra-tion and with decreasing temperature.1-l1 The follow-ing are some of the numerous mechanisms that have been adopted in attempts to explain these observations: 1) hydrogen-dislocation interarction,4'6 2) lowering of the crack surface energy by adsorbed hydrogen,9'10 3) localized lowering of the niobium bond strength,9 and 4) exertion of pressure inside voids by molecular hydrogen.6 A recent study1' indicates that, in some way, the embrittlement is related to the precipitation of a hydrogen-rich phase, because embrittlement and hydrogen solubility have the same temperature dependence. Most of the investigators observed that at very low temperatures there was a return of the ductility. Thus, hydrogenated niobium and vanadium may be said to exhibit a low temperature ductility minimum."1'8'9 It has been reasoned by most observers that diffusion is required for the embrittlement mechanism to be operative, and that as hydrogen becomes immobile at very low temperatures, the ductility increases. This investigation of the mechanical behavior of Nb-H al-loys under various conditions is an attempt to gain a better understanding of the low temperature ductility minimum. EXPERIMENTAL Tensile specimens, with gage length dimensions 20 by 3 mm, were machined from sheet stock" and both faces were ground on wet 600 grit Sic paper to obtain a final thickness of 0.5 mm. Annealing as described earlier12 resulted in average grain diameters of 0.3 mm. The recrystallized niobium tensile specimens were electropolished in 90 parts H2S04, 10 parts HF (48.9 pct) by volume, at 287°K and 30 v. Hydrogen, which may have been present in the starting material and/or added during specimen preparation, was removed by annealing at 1073°K in a dynamic vacuum of 2 X 10-6 torr. Hydrogenated specimens (1.15 at. pct H) were prepared by reaction with a known quantity of pure hydrogen (obtained by thermal decomposition of UH3) at 1073oK, followed by cooling at the rate of 100" per hr. These were vacuum encapsulated, homogenized at 573°K for 3 to 5 hr, and furnace-cooled. Tensile tests were conducted on an Instron machine at a strain rate of 4 x l0-5 per sec. The gripping device was such that the specimen was positioned below the crosshead. Thus, subambient test temperatures could be obtained by immersion of the device in a cooling bath of either liquid nitrogen or Freon-12. The temperature of the Freon-12 was controlled within ± 0.1°K of the desired temperature by automatically monitoring the flow of liquid nitrogen through a copper coil in the bath. Slow-cooling to 77°K was accomplished as follows. The testing device was surrounded by a rubber jacket, open at the top and with small holes in the bottom. Liquid nitrogen, brought up to the bottom of the jacket, entered the holes and vaporized quickly. The temperature was monitored at the specimen with a copper-constantan thermocouple, and a constant cooling rate of 2 deg per min was easily achieved by controlling the level of the liquid nitrogen outside the jacket. RESULTS AND DISCUSSION Low Temperature Ductility Minimum. Resistometric studies of both Nb-H12 and V-H13 indicated that at tem-peratures less than 150°K, virtually all of the hydrogen

Jan 1, 1970

By Rossiter W. Raymond

(Canal Zone Meeting, November, 1910.) THE death of Professor Blake removes the oldest of American economic geologists and mining engineers, and deprives this Institute of one of its, earliest and most illustrious members. To many of us it brings a personal loss also, the loss of a friend. William Phipps Blake was born June 21, 1826, in New York City. -His father, Elihu Blake, was a surgeon-dentist of eminence, a direct descendant of William Blake, who settled in the Massachusetts Bay Colony about 1630. He was prepared for college at private schools in New York, and entered the Sheffield School of Yale, where he was graduated as Ph.B. in the chemical course, class of 1852, the first graduating-class of the institution. In the same year he became chemist and mineralogist of the New Jersey Zinc Co., and chemist of chemical works at Baltimore, Md. In 1853, lie started the Department of Mineralogy of the World's Fair at New York City. In 1854, 1855 and 1856, he was mineralogist and geologist of the United States Pacific Railroad Surveys of Williamson, Pope, and Whipple, and for the War Department at Washington. His writings, during this period comprise reports on the geology and mineralogy of California and other parts of the Southwest, and constitute well nigh the earliest scientific accounts of the regions described. One of them. was a translation of the Resume and Field Notes of Jules Marcou, of Whipple's expedition. From 1856 to 1859, he was engaged in explorations of the geology and mineral deposits of North Carolina, :and other parts of the country. In 1859, he became editor and proprietor of The Mining Magazine. This was a monthly periodical, founded in 1853 by W. J. Tenny, who conducted it until 1858, when it passed into the hands of Thomas McElrath, a New York publisher, and appeared in May of that year as The Mining and Statistic Magazine, with the name of

Sep 1, 1910

By Carl R. Christiansen

Since the first pay hole in Missouri's "New Lead Belt" was drilled in 1955, this district has become one of the world's leading sources of lead. The belt extends from north of Viburnum in a southerly direction to near Eminence, a distance of about 35 miles. The St. Joseph Lead Company was the discoverer and first to develop new mines in the Viburnum area. Since the discovery of the New Lead Belt, many companies have engaged in exploration programs and several major companies have become active in development of new mines. These include Cominco American, Inc., which operates a joint venture with Dresser Industries; Ozark Lead Company, a subsidiary of Kennecott Copper Company; and Missouri Lead Operating Company, a joint venture of Arnax and Homestake. St. Joseph Lead Company, with over 100 years of experience in the Old Lead Belt, has served as a leader in development of equipment and mining techniques, making its properties some of the most efficient mining operations in the world. The new producers give the district the benefit of fresh viewpoints, as their engineers are mostly from outside of Missouri and their previous experience has been considerably different from conventional lead belt practices. While all operations are similar in that they are room-and-pillar, the diverse experience of the operators has produced a group of mines that employ a variety of equipment and mining techniques to give increased efficiency

Jan 1, 1970

By Finney, W. R.

MUCH has been said and written of the "Big Inch," of the terrific obstacles encountered in its construction, of the colorful and tough men engaged in its building, but little has been publicized of the engineering and economic problems behind the scenes. Long before Pearl Harbor it was apparent to the petroleum industry that a critical oil shortage could be expected along the Atlantic seaboard, owing to delay in tanker deliveries as a result of convoy movements, and to allocation of vessels for foreign shipments. This area, with a normal consumption of approximately 1,800,000 barrels per day of oil and products, was almost entirely supplied by tanker. Pipe lines supplied an average of only 20,000 barrels per day in 1939, 40,300 barrels per day in 1940, and 55,000 barrels per day in 1941. A small amount of oil and products was also delivered via barge.

Jan 1, 1943

By Stanly A. Easton

SEVEN years ago there was installed in the hospital of the Bunker Hill & Sullivan Mining & Concentrating Co. at Kellogg, Idaho, an ultra-violet ray quartz lamp, the standard equipment which is found everywhere in the offices of physicians and among usual hospital equipment. The use of this lamp was con- fined largely to treatment of pathological cases, still treatment of under-nourished children, run-down anemic people, both men and women, and, as a general tonic, was part of the routine hospital procedure. At the latitude of the Ceur d'Alene district and especially because of the position of the towns in deep canyons, with much overcast and cloudy weather, sunshine is not plentiful at any time of the year; for many of the winter months there is scarcely any. Underground workers, particularly during the winter, have little sun- shine; it is not unusual to have none at all for weeks at a time. Treatment by the ultra-violet ray lamp in the hospital has resulted in many extraordinary benefits but the use of the lamp is expensive and limited. Some weeks ago attention was directed to the automatic solarium equipment of the Burdick Corporation. The doctors strongly recommended the increased use of the ultra-violet lamp for its curative powers and tonic effects, urging that it be made accessible to all employees. Real interest was . . also displayed by employees with the possibility of securing ultra-violet ray treatment for themselves and families under better conditions than it was possible to have by the limited use of the lamp at the hospital. This resulted in the installation of the so-called sun room or automatic solarium as an adjunct to the mine change-house. An annex was built to the change-house, with dressing rooms for women, children and men from other departments, and the outfit put into use on Sept. 5, 1929. The installation consists of an escalator, or

Jan 1, 1929

By John W. Burd

A system is described for the simultaneous deposition of epitaxial layers on as many as eight substrates. A high degree of uniformity of both physical and electrical characteristics is achieved in the films. Variation of film thicknesses is consistently less than ±10pct within a wafer and from wafer to wafer within a run with the variation typically on the order of 55 pct. Composition variation of GaAs1-x PX layers within a wafer and from wafer to wafer within a run is consistently less than 51 pct. Electrical evaluation of the films by several techniques indicates excellent doping uniformity within a wafer and from wafer to wafer within a run. Mobilities for lightly doped GaAs films at 300°K are consistently >6000 cm2 v-1 sec-1 and mobilities > 7000 cm2 v- 1 sec-1 are regularly attainable. Techniques for the preparation of material with carrier concentrations from 1 x 1015cm-3 to 1 x 1019 cm-3 n-type and 5 x 1016 to 5 x 1018 cm-3 p-type are discussed. METHODS for the preparation of 111-V compounds by vapor phase reactions have been extensively reported in the literature.1-6 Almost all of the apparatus described for these various methods are suitable for processing one or at the most a very limited number of wafers simultaneously. With the recent rapid advances in the use of vapor grown GaAs for microwave oscillators and GaAs1-xPx as visible light emitters the requirements for these materials are steadily increasing. In order to satisfy these requirements it is necessary to move from a laboratory scale apparatus to one which is capable of processing a large number of wafers simultaneously. Desirable features would be a high degree of uniformity among the wafers and good reproducibility from run to run. The apparatus to be described fulfills these requirements very well. DISCUSSION The various methods reported in the literature can be classified under three headings: 1) closed tube, 2) open tube, and 3) the close-spaced method. Of these three the open-tube method is the most amenable for scale-up to a manufacturing process. It is the most versatile and the various operating conditions can be more precisely controlled than with the other two methods. A number of chemical reactions may be used to achieve vapor-phase growth of 111-V compounds. Sev-era1 of the more generally used reactions are shown in Fig. 1. All of these reactions have the following points in common: 1) generation of a volatile group III(Ga) species by the reaction of the transport agent (halide or HC1) with either Ga or GaAs, 2) introduction of the Group V(As and/or PI component, 3) a method of adding dopant, if desired, and 4) a region in which deposition from the vapor will occur and form as a single crystal epitaxial film on the substrates. The laboratory scale reactors permit the hot re-actant gases to flow into the relatively cooler deposition zone and pass successively over the several substrates which are arrayed along the long axis of the tube parallel to the gas flow. With this arrangement the composition of the reactant stream is continually changing as solid material is deposited on each successive substrate. As a result of this changing gas composition the reaction driving force also changes from substrate to substrate and the degree of uniformity of layer thickness, doping level, and so forth, is poor. This effect can be partially overcome by imposing a controlled temperature gradient along the deposition region to compensate for change in gas composition. However, even when this is done variations in layer thickness on the order of 30 to 40 pct are common and as high as 50 pct are frequently experienced between adjacent wafers in the tube. To expand this arrangement to a large number of wafers would only increase the nonuniformity from the first to last wafer in the line. From the above discussion the two undesirable features of changing gas composition and temperature gradient become evident. A reactor system which eliminates or minimizes these undesirable features is one in which the apparatus is mounted vertically as shown schematically in Fig. 2. The vertical mounting permits the disposition of a number of substrates on a suitable support so that all wafers are at the same vertical height in the furnace and hence at essentially the same temperature. By using only a single row of wafers the reactant gas mixture passes over only one substrate in its path through the reactor. Thus the two undesirable features of changing gas composition and temperature gradient are minimized. An additional design feature which further minimizes temperature variations is rotation of the substrate holder. Rotation serves to integrate any radial temperature gradient existing around the resistance heated furnace. A photograph of a reactor assembly at the completion of a run is shown in Fig. 3. MATERIAL PREPARATION Apparatus. Although any of the several chemical systems shown in Fig. 1 are adaptable for use in this apparatus the one generally used is System 2, the hydride synthesis system. This system has been de-

Jan 1, 1970

By J. G. Faller, L. P. Skolnick

The distribution of cobalt and vanadium over non-equivalent crystallographic sites in C14-type Zr(VCo), alloys has been investigated. An anomalous X-ray scattering technique developed by Skolnick, Kondo. and lavine7 by which the separation in the scattering factors of two similar atoms can be enhanced was employed. Six alloys spanning the pseudobinary section ZrV1.6Co0.4-ZrVO.6CO1.4 at 10pct steps showed a nonrandom compositionally dependent distribution. Specifically, at high vanadium content cobalt preferentially occupied sites of type (6h) and vanadium, sites of type (2a; at low vanadium content the reverse was observed. In addition to the distribution fraction the structural parameters x and z were obtained. There was no significant deviation of these parameters from those obtained in the ideal C14 structure. Certain suggestions are made to account for the observed nonrandomness in the distribution of atoms on the two types of sites. INTERMETALLIC compounds of formula AB2 iso-morphous with MgCu2, MgZn2, and MgNi2 are known as Laves phases. Because Laves phases exhibit high symmetry and coordination numbers, the highest possible for an AB2-type compound,1 they are among the most frequently observed compounds in nature. In recent years interest has centered about the purely transition metal Laves phases2-' in efforts to understand the function of atomic size and electronic structure in the formation of these compounds. It has been observed that pseudobinary Laves phase systems often show a variation of structure across the phase diagram. Such a system is the ZrV2-ZrCo2 in which the structure varies from cubic MgCu2 to hexagonal MgZn2 to cubic MgCu2.4 Some understanding about the conditions under which the second modification is stable can perhaps be gained by studying the distribution of cobalt and vanadium atoms on lattice sites in the MgZn2 modification of the system ZrV2-ZrCo2. In both the MgZn2 and MgNi2-types there exist nonequivalent positions open to occupancy by the B element, whereas in the MgCu2 prototype all sites are equivalent. Skolnick, Kondo, and La-vine7 have developed an anomalous scattering technique suitable for this type of investigation. Whereas the influence of size on the formation of a Laves phase is well recognized, no substantial evidence has been put forth in support of the size ratio dependence of a particular prototype. Berry and Raynor8 suggested that RA /RB ratio does indeed affect the type of structure that is chosen, MgZn2 compounds tending to cluster about 1.225 while MgCu2 compounds were found at larger deviations from this ratio. Dwight,3 however, from a study of 164 Laves phases does not believe this generalization to be justified. Electronic effects are certain to play a part in the stability of Laves phases in general and in the choice of a structure type in particular. For example, size along would favor the formation of Laves compounds of Ti, Zr, Hf, Ta, or Nb as the A element with nickel or copper as the B element. The absence of such is attributed to an unfavorable electron : atom ratio by Elliott and rostoker.4 Early experiments of Laves and witte9 with pseudobinary and pseudoternary systems of the three prototypes established the dependence of crystal structure upon electron: atom ratios. They observed that the MgCu2 structure dissolved elements of higher valency until the electron: atom ratio of =1.8 was reached; the MgZn2 likewise dissolved elements of lower valency replacing zinc. witte,6 from calculations of the electron : atom volumes of Brillouin Zones, obtained limits of stability for the prototypes MgCu2 and MgZn2. Elliott and Rostoker4 used these limits with considerable success in the all-transition element Laves phases they investigated. According to witte,6 compounds between the electron :atom ratios of 1.80 and 2.32 were of the MgZn2 type; those above and below exhibited the MgCu2-type structure. On the basis of these limits and an assumed valency of zirconium based upon the near tetra-valence of titanium, Elliott and Rostoker obtained valencies for the first transition series elements. For the Laves phases with which this investigation is concerned, ZrV2 and ZrCo2, the authors calculated electron :atom ratios of 2.54 and 1.56, respectively. These ratios are for the MgCu2-type structure and straddle the stability band of the MgZn2 modification. One could, therefore, predict that a pseudobinary system ZrV2-ZrCo2 should pass through the MgZn2 modification in traversing the composition diagram from one end to the other. Implicit in this assumption is a smooth change of the electron: atom ratio from 2'54 to 1.56. MOSS10 states that his finding the low temperature structure of ZrCr2 to be C15 instead of C14 alters greatly Elliott's valency of zirconium and hence the assumed valencies of the other metals. Such a quantitative correlation of structure with electron : atom

Jan 1, 1963