By A. V. UDELL

OF all the metals that have from time to time been called the "Wonder Metal," mercury, often called quicksilver, is probably the most deserving of this designation. A wonder metal it must have been to those workers of an earlier day who named it after that Latin god of commerce and gain, characterized as the fleet messenger of the gods and the conductor of souls to the lower world. The word mercury has been used to indicate a carrier of tidings, a bearer of news, a nimble or clever person, a hawker, and a skillful thief. All of these attributes, and more, are recognizable in this metal, the technical terminology of which is "Hydragyrum," meaning water-silver, and from which the chemical symbol "Hg" is derived. Fickle in its occurrence in nature, simple in its metallurgy, illusive in captivity, it serves man in life or death, in war or peace, in commerce, science and arts, in mining, agriculture, and forestry with a versatility found in no other element.

Jan 1, 1929

By D. J. Jr. McAdam

PART I.-OUTLINE OF INVESTIGATION, DESCRIPTION OF METHODS AND MATERIAL Previous Investigation of the Influence of Stress on Corrosion IN 1917 Haigh1 presented evidence that under simultaneous corrosion and cyclic stress metals may fail at lower stresses than if the corrosion is prior to the cyclic stress. In 1926 the author, while investigating the cooling effect of water on the fatigue resistance of metals, found that under these conditions steel specimens fail at stresses far below the endurance limit.2 (By "endurance limit" is here meant the fatigue limit obtained with specimens as free as possible from stress concentration and corrosive influences.) This led to an investigation (at the Naval Engineering Experiment Station, Annapolis, Md.) of the influence of cyclic stress on corrosion. This investigation maybe divided into three parts. The first part was a general survey of the conditions necessary to cause complete failure under corrosion and cyclic stress of relatively high frequency. The entire process by which metals fail under these conditions was-called "corrosion-fatigue." "Corrosion-fatigue limits" for a large number of metals were determined and the relationships of these limits to chemical composition, heat treatment and physical properties were established. The conclusion was reached that corrosion-fatigue is due to the accelerating influence of cyclic stress on corrosion. Results of this part of the investigation were presented in five papers.2-6 The second part of the investigation was a preliminary study of the influence of cyclic stress on corrosion. Each experiment was conducted in two stages. The first was a corrosion stage in which the specimen was corroded under cyclic stress; the second was a fatigue stage, in which the previously corroded specimen was tested (without further corrosion) to determine its fatigue limit. The difference between this fatigue limit and the endurance limit was used as a criterion of the "damage" due to

Jan 1, 1931

By R. D. Pehlke, P. D. Goodell, R. W. Dunlap

The rate of dissolution of steel bars in molten pig iron has been measured experimentally in the temperature range 2300° to 2650° F. The rate of solution is shown to be a .function of bath composition, temperature, and stirring. A kinetic model based on carbon diffusion in the liquid phase has been derived to fit the experimental results. THE rate of scrap melting has long been an important variable in steelmaking operations. With the advent of the oxygen steelmaking process and the accompanying shorter heat times, the rate of scrap melting has now become one of the rate-limiting factors in steel production. As observed in commercial practice, the solution rate is influenced by the compositions of liquid and solid, the temperature, agitation, and time. However, no definitive work has been done on the Fe-C system, and there is very little information in the literature regarding the relative effects of these variables in steelmaking systems. A number of questions have been raised in regard to scrap utilization in basic oxygen steelmaking operations. Consideration has been given to the optimum size and shape of scrap, and to the use of preheated scrap as a means for decreasing the pig-iron requirement in oxygen blowing. The determination of an optimum scrap practice for a specific installation depends to a large extent upon the economics of the scrap market and also upon the behavior of scrap in the vessel. The present research was undertaken as a preliminary study in evaluating the behavior of steel in a pig-iron bath under various conditions of temperature, composition, and agitation, as might be encountered in oxygen converter operations or in any steelmaking operation where scrap behavior is an important process variable. Related studies have been carried out on non-ferrous systems. The solution rate of solid aluminum in a molten A1-Si alloy has been studied.' Furthermore, the increasing use of liquid metals has created considerable interest in studies related to dissolution of a solid in a liquid, or mass transfer taking place between a solid interface and a liquid metallic phase.2-10 In an effort to clarify the relative importance of factors influencing the dissolution of scrap in Fe-C alloys, this paper presents the results of a study of the rate of dissolution of a low-carbon steel cylinder in a molten Fe-C bath at various bath compositions, temperatures, and conditions of agitation. An attempt has been made to determine the mechanism of solution, and a model has been derived to fit the experimental results. The rate of heat transfer between the molten pig-iron bath and the solid-steel cylinder has also been studied. EXPERIMENTAL PROCEDURE A molten bath of pig iron (nominal composition 4.2 pct C, 0.5 pct Mn, 0.8 pct Si)* was held in a 200- *In view of the fact that the composition of the pig-iron bath was slowly changing with time because of steel dissolution and reaction with the surrounding atmosphere, intermittent samples of the liquid bath were taken throughout each experiment, Table 1. lb induction melting unit. The internal diameter of the furnace was 8-1/2 in. and the bath depth approximately 14 in. Cold-finished 1020 steel cylinders of 1/2-, 3/4-, 1-, 1-1/2-, and 2-in. diameters were cut into 1 -ft lengths for use as test specimens. One end of each bar was machined to fit a hand-driven, mechanical stirring device which rested on top of the furnace. This fixture permitted 7 to 8 in. of the bar to be immersed in the melt. The steel cylinders were cleaned to free the surface of grease and oxide. The rods, at ambient temperature, were immersed into the molten pig-iron bath. The melt temperatures studied in this investigation were 2300°, 2500°, and 2650°F. Different agitation conditions were achieved by operating with a) the power to the furnace, giving induction stirring; b) induction stirring plus mechanical stirring, using hand rotation with a chain and sprocket assembly at approximately 200 rpm; c) mechanical stirring alone with the power off; and d) the power off and no mechanical stirring resulting in minimum agitation, i.e., only that caused by natural convection currents in the bath. The samples were immersed in the melt for prescribed times ranging from 30 sec up to 6 min. Immersion times were measured with a stopwatch and temperature control of the melt was achieved by power adjustment following temperature measurement with an optical pyrometer. The measurements with the calibrated pyrometer were checked out to within less than 10°F with simultaneous thermocouple measurements. Following immersion, the bars were water-quenched and the diameters were measured with a micrometer at several positions on the reduced area, and by volumetric displacement. The dissolution rates calculated from the

Jan 1, 1965

By C. M. Haight

THE mine blacksmith and drill-steel sharpening shop at the Franklin mine of the New Jersey Zinc Co. is on the surface, adjoining the main shaft. It is a brick building, 51 by 30 ft. inside dimensions, with a corrugated iron roof and concrete floor. About two-thirds of the steels used are brought up through the main shaft; the remainder through two auxiliary shafts. The latter are carried to the shop by team or truck. At each shaft sufficiently large stocks of sharp drills of various types are kept to replace all the dull steels that may be sent up; while at the shop enough sharp drills are kept to replace the dull steels in. the stocks kept at the auxiliary shafts. Though this entails keeping a larger number of drill steels in service than might be required by other methods, there is less hurry in the sharpening shop and the steels have a longer period of rest. If a rest from use enables steel to recover from fatigue strains, this method secures that rest. The forms shown in Fig. 1 are supplied to each shift boss in books of 100. These are used to requisition sharp drills from the shaft stocks and enable the men at the tops of the shafts to sort out the required sizes and to have them ready to be sent to the various shaft stations. At one of the auxiliary shafts, the dull drills are placed on a platform from which they are dumped into the body of the wagon that takes them to the shop.

Jan 2, 1926

By R. R. Harvey

Recent evidence has indicated that the films forming at crude oil-water interfaces are the result of naturally occurring su,rface-active components in the crude oil rather than oxidation products resulting from exposure of the oil to air. Since the presence of such films may strongly affect the displacement of oil from porous media, a knowledge of their composition and formatiorz is of fundamental importance. In this study, without the assumption of a specific mechanism, film formation is considered to involve the transfer of a weakly surface-active species in solution in the oil to the oil-water interface. The film gas law and the Gibbs adsorption equation may thus he applied to the system. The rigid films which form upon decrease of the oil-water interfacial area are considered a result of the very slow rate of re-solution of the film material into the oil. When the shrinkage of the interface is very rapid, the amount of film material leaving the interface is negligible, and the system may then be treated in the same manner as an insoluble film. The combination of these treatments leads to a new concept of the film factor in which it may he quantitatively related to the concentration of film-forming material at the interface. Suitable experiments can then yield the following information. 1. Original concentration of surface-active species in the oil. 2. The change of concentration with time. 3. Concentration of surface active species at the interface. 4. The change of this concentration with time. 5. Interfacial tension of the system at any time and its variation with time. 6. Equilibriunz concentrations for a given set of conditions. 7. Concentration requirements for solid film formation. 8. Molecular diameter of the adrorbed species. These calculations may be made solely from data taken from measurements on the original oil. While using the pendant drop method of interfacial tension measurement of crude oil-water systems, Bartell and Niederhauser' remarked on the thin, transparent, pliable, solid films or membranes which were often formed at the interface between crude oil and water. As a result of their observations of these films, Bar-tell and Niederhauser concluded: 1. The films are formed by material from the oil adsorbed at the interface rather than by a reaction at the interface. 2. The adsorption of the film-forming material is a rather slow process. 3. There are good indications that the process is reversible; i.e., the film constituents may re-dissolve into the oil. 4. The film will spontaneously spread over any new surface formed. 5. The process of adsorption at the interface is accompanied by a decrease in the interfacial tension of the system. Although they had proved that film formation was not due to a reaction at the interface, Bartell and Niederhauser were unable to demonstrate conclusively whether these film-forming constituents were present in the original reservoir oil or whether they were formed as oxidation products after exposure of the oil to air. Recent evidence seems to point to their presence in the original oil. Although the true nature of the film-forming constituents is still uncertain, these conditions would be fulfilled by the assumption of the presence of a slightly soluble surface-active component in the original oil. This component would migrate to a freshly formed interface because it would thereby lower the free energy of the system. The component at the surface constitutes an expanded monolayer which would become compressed, upon retraction of drop, due to the slow rate of re-solution of the film components into the bulk of the oil. It is possible, by involved extraction processes, to separate or at least concentrate this film-forming fraction. However, using the assumptions made above, the technique of monolayer film study may be applied to reveal much of the nature of the adsorbing material without resorting to an actual separation of the film-forming constituents.

By Hugh S. Spence

IN the winter of 1941-42, muscovite mica was discovered by a young prospector, Justin Purdy, in the township of Mattawan, Nipissing District, Ontario, a few miles north of the small settlement of Eau Claire, which lies on the main Transcontinental Highway (No. 17) between Mattawa and North Bay. Muscovite had been known for many years to occur in the general Mattawa region, and various small efforts at production had previously been made by individuals working scattered deposits in the area. These minor activities, however, had never led to production of any consequence or the discovery of any important mica bodies. The Purdy finds were made in a heavily timbered, mountainous area lying about three miles north of the low-lying settled land along the highway, and in a section not hitherto prospected. The mica taken by Purdy and two partners from surface outcrops proved so remarkable in point of size of trimmed sheets that the find attracted considerable attention, and the area surrounding the three claims taken up by the prospectors was quickly blanket-staked by various interests. Though a number of other mica-bearing pegmatite dikes were 'found later on these stakings, none proved as rich as those on the original Purdy ground; very little commercial mica was obtained from them and attempts to develop them were short-lived. Purdy and his partners sold their initial production to dealers in Ottawa and Hull, where the Canadian mica industry long has centered. Young Purdy, unfortunately was killed in a motor accident in the early summer of 1942. His father continued mining operations for a few months and produced and sold a considerable amount of mica. In October 1942 the Purdy holdings were acquired by Inspiration Mining and Development Co. of Amos, Quebec, which had been active in staking in the area. This company formed a subsidiary, Purdy Mica Mines, Limited, to develop the property. Under the energetic management of Joseph R. Norrie, rapid progress was made, and production soon attained important proportions. Realizing from the outset the unusual character and potential value in the war effort of the Purdy discovery, the Metals Controller, Department of Munitions and Supply, at once arranged with the Department of Mines and Resources for an official geological report on the area, and also drew the attention of the War Production Board in Washington to what seemed likely to prove a highly important source of strategic-quality mica. Officials of WPB were sent up in the summer of 1942 to inspect the property,

Jan 1, 1947

By W. T. Roberts, N. G. Turner

A study of the fatigue properties of several grades of commercially pure titanium has established that the strain-aging process is of minor importance in the development of a fatigue limit and a relatively high fatigue strength ratio. Metallographic observations and damping measurements at room temperature indicate that striations are able to spread from grain to grain only at stress levels above the fatigue limit. This suggests that the fatigue limit represents the stress above which large-scale dislocation unlocking takes place. Fatigue tests on annealed material at - 60" and - 196" c showed that under conditions when a thermally activated diffusion process would be suppressed the fatigue limit is not eliminated. Prestraining at room temperature did not have a detrimental effect on fatigue strength at room temperature but a decrease was recorded at — 60°C. This is further evidence that initial dislocation locking is a important strengthening mechanism. TITANIUM and titanium alloys have S-N curves with a definite fatigue limit, and a high ratio of fatigue limit to UTS can be attained. Other materials which show similar fatigue characteristics are mild steel and some Al-Mg alloys. The fatigue limit of these materials has been associated with their strain-aging capacity. It is well-known that commercial-purity titanium contains interstitial impurities which can give rise to a sharp yield point, and a small strain-aging effect following static strain has been demonstrated.7 This type of aging reaction is differentiated from the dynamic aging process when aging occurs during plastic deformation, and which is generally observed at elevated temperatures. In a titanium at room temperature, dislocation locking is associated with the interaction of interstitial oxygen, nitrogen, and carbon atoms with dislocations. Ehr-lich has shown that the distortion produced by introduction of these atoms into the hcp lattice has no shear stress component and hence there is no interaction between the stress field and the screw component of a dislocation. Thus the dislocations as a whole are only weakly locked. It is clear that strain-aging effects in hcp a titanium will be much less pronounced than those observed in bcc iron and steel. In recent years, the attribution of the fatigue limit solely to strain aging has been questioned. It has been pointed out that a definite fatigue limit is observed at temperatures as low as -196°C in some titanium alloys,' and strain aging is not expected to be effective at this temperature. The role of initial locking of dislocations in determining fatigue behavior has been examined in low-carbon steel by Oates and Wilson. They showed that under conditions in which the aging potential is low the factors which control the buildup of local stresses and hence affect dislocation unlocking, e.g., grain size, are important. There are indications that other metals can have a definite fatigue limit with no established strain-aging capacity, an example being magnesium12 which has the same crystal structure as a titanium. The spread of plasticity from grain to grain in hexagonal metals may be more difficult than in cubic metals because of the limited number of slip systems in the former, and this may account in part for their fatigue behavior. The present work was undertaken to elucidate the relative importance of crystal structure, strain aging, and initial dislocation locking in determining the properties of commercially pure titanium when subjected to cyclic stressing. 1) EXPERIMENTAL METHODS Three grades of commercial-purity titanium were used and a material of lower interstitial content was prepared by melting high-purity Japanese sponge titanium (referred to as H.P. Ti). The compositions and typical mechanical properties of the materials are shown in Table I. Fatigue tests were made in push-pull (zero mean stress) using an Amsler Vibraphore machine at a frequency of about 160 cps. Two types of fatigue specimen were used—one with a waisted gage length for determination of S-N curves and the other with a parallel gage length for metallographic studies and damping measurements. After careful machining and mechanical polishing, all specimens were electropolished prior to fatigue testing. The electrolyte consisted of 10 parts methyl alcohol, 6 parts 2-butoxyethanol, and 1 part perchloric acid (SG 1.54) and it was maintained at a temperature of -10" to -20°C during polishing. Tests at room temperature were normally carried out with the specimen immersed in a silicone oil bath which could be heated for elevated-temperature tests.

Jan 1, 1969

By J. W. Freeman, J. P. Rowe, R. F. Decker

HEAT-to-heat variations in properties of an alloy of constant nominal chemical composition have been a perplexing problem to the metallurgist. These heat-to-heat differences have been especially baffling in high-temperature metallurgy. In order to establish fundamental reasons for these heat-to-heat variations, the National Advisory Committee for Aeronautics has sponsored and financially assisted an extended research program on heat-resistant alloys at the University of Michigan. As part of the program to find the contribution of processing variables, Frey, Freeman, and white' studied effects of heat treating on nickel-base alloys and Ewing and reeman' investigated effects of hot-working practice on N155 alloy. To extend the program to the study of effects of melting practice on high-temperature properties, a 55 Ni-20 Cr-15 Co-4 Mo-3 Ti-3 pct A1 composition was selected for experimentation. The objective of this program was to establish the melting-practice variables which influenced the hot-working characteristics and creep-rupture properties and, at the same time, establish the metallurgical mechanisms for the effects. During the course of the investigation of practices using vacuum melting, it became increasingly evident through chemical analyses supplied by industrial concerns that a major variable was melt reaction with the crucible. This paper is devoted to the results of this phase of the melting-practice study. EXPERIMENTAL PROCEDURES Experimental 10-lb heats were induction melted in the University of Michigan vacuum-melting unit with the melting practices outlined in Table I. Aim analysis for the basic alloy, in wt pct, for all heats was as follows: Cr Co Mo Ti Al 20.0 15.0 4.0 3.1 3.1 Mn Si C Ni 0.12 0.12 0.08-0.15 Bal. Small amounts of boron and zirconium were added to certain heats as listed in Table I. These additions

Jan 1, 1959

By C. F. Weinaug, P. M. Blair

Many difference equations used to approximate reservoir flow problems treat the phase pressures implicitly but not the mobility-density coefficients. Such difference equations are neither wholly explicit nor implicit, but might be described as mixed. Mixed equations are relatively easy to apply. But the associated time truncation error is relatively large, and when used to solve problems characterized by high flow rates, these equations may be unstable for practical size time steps. This paper outlines the development of a completely implicit difference analogue for reservoir simulation, along with a Newtonian iterative method for solving the resulting nonlinear set of algebraic equations that arise at each time step. While this implicit equation requires two to three times more work than does the mixed equation, it is shown to markedly decrease the time truncation error and to yield a stable solution for much larger time steps than does the mixed equation. INTRODUCTION Calculation of multiphase, multidimensional flow in porous media is generally accomplished by numerical methods that involve approximating systems of partial differential equations by systems of partial difference equations. The early development of difference equation techniques was directed toward the solution of linear differential systems. However, the equations of multiphase fluid flow through porous media are highly nonlinear in that mobility and density often are strong functions of pressure and saturation. Thus, solution of the flow problems by difference equations involves solving sets of algebraic equations whose coefficients change from step to step of the calculations. Current practice is to evaluate most coefficients at the beginning of a time step and then to apply difference methods well suited for solving linear problems. At least two major difficulties arise from the use of this practice. First, evaluation of coefficients at the old time level and evaluation of pressures at the new time level results in larger time truncation errors near displacement fronts than if all quantities in the distance derivative were evaluated at the same time level. Second, evaluation of mobility coefficients at old time levels results in an unstable difference equation in regions of high flow rate. The first of these difficulties often results in optimistic recovery behind the displacement front, and the second requires the use of small time steps or special techniques in solving coning problems1 or problems of gas percolation.2 Evaluation of all quantities in the distance differences at the new time level results in a completely implicit difference system. Such a difference system has a lower time truncation error than equations in which mobilities are evaluated at the old level and pressures evaluated at the new level. The algebraic equations resulting from the fully implicit difference equation are, in this case, nonlinear and require some iterative method for their solution. This paper develops fully implicit difference equations for two-phase flow in porous media, describes their solution by Newtonian iteration, and gives examples of problems more easily solved by the new method than by previous methods. EVOLUTION OF DIFFERENCE EQUATIONS FOR NONLINEAR PROCESSES The completely implicit difference equation used in these calculations results from evolution beginning with explicit difference equations, proceeding through what we will call "mixed" equations, and arriving now at a completely implicit equation. Let us illustrate the evolution by considering different analogs of the nonlinear equation

Jan 1, 1970

By Howard N. Eavenson

WASTE of coal, or perhaps more properly the percentage of its recovery in mining, has keenly interested me during an experience of over a half century in coal mining. In the early part of that time and until a few ears after World War I the use of better mining plans and supervision resulted in an increased recovery. Since then, and particularly since controlled prices have been effective and mechanized mining has been extensively practiced, the tendency has all been toward lesser recovery in mining. The purpose of this paper is not to criticize the methods being used, which after all are the result of economic forces, nor to point to any particular mining method or to any locality where the best recovery is obtained. but to call attention to the tremendous waste of our national coal resources that is constantly continuing. A possible method of reducing this loss will be suggested. but without any illusions that it will be followed or that much attention will be paid to it.

Jan 1, 1946

By D. G. Russell

Two techniques have been developed with which the applicability of pressure build-up analyses can be extended to include pressure data which previously have been considered virtually unusable. One of the interpretation methods makes possible the analysis of pressure build-up performance during the wellbore fill-up or after production period which occurs soon after a well is closed in. The other technique is an extension of a method for analyzing pressure build-up performance during the late-time portion of the pressure build-up which occurs after boundary eflects first begin to alter the shape of a conventional pressure build-up curve. With both of these methods it is possible to obtain estitnates of the kh product, the skin factor and the reservoir pressure. In addition, with the late-time analysis technique it is possible to obtain an estimate of the contributory drainage volume of the well being tested. This means that in some cases a check on reservoir limit test and (or) material-balance calculations can now be obtained from pressure build-ups. Both methods are slightly more time-consuming than conventional pressure build-up analysis methods because trial-and-error plots of pressure data must be made. The late-time method for analysis of pressure build-ups is in principle applicable to the late-time portion of a two-rate flow test or a pressure drawdown test. The interpretation formulas and procedures for these types of tests are also outlined. In these cases, as with pressure build-ups, it is significant that an estimate of the contributory pore volume is also obtained. On the basis of limited experience with the new techniques, it appears that satisfactory estimates of the kh product, skin factor, reservoir pressure and, for late-time analysis, contributory drainage volume can be obtained. INTRODUCTION The analysis of bottom-hole pressure build-up behavior in closed-in wells has been a a subject of interest in petroleum engineering circles for many years. In fact, few other subjects have received as much attention as pressure buildup analysis methods have. The cause for this interest is essentially twofold in nature. First, the pressure behavior of a well can normally be measured with a reasonably high degree of accuracy so that good data for analysis can be obtained. Secondly, over a fairly wide range of operating conditions, valuable information as to the quality of the reservoir rock and completion efficiency of the well can be obtained at a nominal cost. In recent years, numerous papers have been prepared on the effects of various operating conditions and reservoir heterogeneities on pressure buildup behavior. Very little work has been done, however, on extension of pressure build-up analysis methods to those pressure data which are not amenable to analysis by the present methods. The theory upon which the analysis of shut-in bottom-hole pressure build-up data is based is derived from the solution of the radial flow equation for a slightly compressible fluid for constant-rate conditions. It requires that the well be closed in for a sufficient period of time to obtain a clearly defined linear portion on the plot of observed bottom-hole pressure vs log (t + ?t)/ ?t (where At is shut-in time, and t is producing time to the instant of shut-in). From the slope of the plot and other normally obtainable data, the formation permeability, the well damage or skin factor, and the reservoir pressure at infinite shut-in time (if the reservoir were infinite) can be estimated. The successful application of this procedure depends on being able to recognize the straight-line section on the basic pressure build-up plot. The presently used pressure build-up interpretation theory also assumes that a well is closed in at the sand face and that no production into the well occurs after shut-in. In practice, of course, the well is closed in at the surface, and inflow into the well continues until the well fills sufficiently to transmit the effect of closing-in to the formation. This adjustment period is commonly referred to as the "afterproduction" or "fill-up" portion of the pressure build-up. During the period that the well fill-up effect is most pronounced, the basic pressure build-up plot is nonlinear. At later shut-in times after the effects of a drainage boundary have been felt at the well, deviation from the straight-line behavior of the pressure build-up plot also results. In many cases either of these effects or a combination of both can make the straight-line portion on the pressure build-up plot difficult to recognize. Obviously, an extension of pressure build-up analysis methods to include the afterproduction period and the period in which boundary effects are being felt would be desirable and might render valuable pressure data which for years have been considered virtually unusable. The principal reference of note concerning pressure buildup analysis during the afterproduction period is a paper by Gladfelter, Tracy and Wilsey.1 In the approach of these authors it is necessary to measure the rate of influx into the well during the afterproduction period. This is done through sonic measurements or through measurement of tubing-head and casing-head pressures simultaneously with

Jan 1, 1967

By Lawrence A. Soltis

Senior engineering or executive management positions are filled by engineers who are evaluated on their performance, knowledge, skill, and maturity. Not only is technical expertise required but a knowledge of sales and marketing, finance, law, industrial relations, and public affairs is necessary. The University of Wisconsin-Extension offers an innovative post-baccalaureate degree program blending technical and professional subjects the Professional Development Degree in engineering (PDD)-designed to bring various opportunities for learn-

Jan 4, 1978

By T. C. Campbell

Copper is extracted from the Chuquicamata oxide ore by a hydro-metallurgical process. The ore is crushed to 3/8-in. sizing, and leached with a sulfuric acid electrolyte. Chlorine is precipitated. and the ferric iron reduced in the enriched electrolyte, after which the copper is recovered by electrolysis with insoluble Chilex and lead-antimony anodes, the spent electrolyte being returned to leaching. Cathodes are melted and refined in market furnaces and cast into commercial wire-bar and cake shapes. Sulfuric acid for the process is supplied by the brochantite in the ore. Water for washing the ore is advanced through the solution system and finally after cutting by electrolysis to from 6 to 16.0 grams per liter is completely stripped by the cuprous chloride method and run to waste. The cuprous chloride so obtained plus that resulting from precipitation of chlorine from strong solution is dissolved in ferrous chloride brine and the copper cemented on scrap iron. The cement so obtained is in part used to reduce ferric iron in electrolyte, and as it is of exceptional purity is also furnace refined and cast into an exceptional quality of fire-refined copper. Fig. 1 is flow sheet of the operation. The reduction plant is composed of seven divisions as follows: (1) crushing, (2) leaching, (3) tailings disposal, (4) dechloridizing, (5) sulfur dioxide treatment, (6) electrolytic tank house, (7) smelting and melting. A brief description of each of these divisions will be given. Crushing Ore that is frequently blocky and up to 5 ft. in section is crushed in four stages to 3/8-in. mesh. The first stage of crushing is called primary and the next three stages are known as secondary crushing. The first stage is accomplished with two 60-in. Superior McCully gyratory breakers by which the ore is broken to 9 in. The second coarse gyratory breakers crush the ore to 3-in. sizing. There are seven No. 10 McCully gyratories in this service, for one of which recently has been substituted a No. 7 cone crusher. The third and fourth stages of crushing are accomplished by fifty 48-in. disk crushers. In the third stage 14 disk crushers break the ore to 1 in., and in the last stage 36 disk crushers turn out the final product of 0.371-in. sizing. Reference to the flow sheets of Figs. 2 and 3

Jan 1, 1934

By S. W. Miller

Most of the steel welding done at the present time is in material containing not over 0.3 per cent. carbon, and the tests here described were in similar material. These tests are not as yet completed but it is hoped that more results and more reasons for the conclusions may be presented at the meeting in February. From the time the author found the peculiar structure in electric welds referred to in a previous paper,' that is, needles or plates in the grains and similar material, in larger spots, at the grain boundaries, he has felt that these plates which may be iron nitride and probably contain some carbon, were at least partly responsible for the brittleness of electric welds. He has found but few traces of similar lines in oxyacetylene welds until the last 2 mo., he has since found large numbers under certain conditions. In the top of these welds, they are quite numerous. In the body of heavy oxyacetylene welds, they appear at times, but not nearly to the extent that they do in electric welds; the author has never seen them in the body of welds in material less than % in. (19 mm.) thick. They are shown in Fig. 82. The reason they were not noticed before is undoubtedly due to the fact that in making tests of welded pieces the weld was always ground off level with the plate, and as this structure only appears in the top 1/16 in (1-5 mm.) of the weld, they were removed by the grinding or machining; also, welds 3/4 in. thick had not been examined. It did not appear, in making bending tests, that this structure had much influence on the strength of oxyacetylene welds; while electric welds are noticeably brittle. Further, oxyacetylene welds made with certain special materials were exceedingly brittle even after the tops of the welds were removed; this was true in cases where there was no sign of the plates whatever and where the welds were remarkably free from oxide and the other usual defects. It appeared, therefore, that this brittleness did not depend on any variable that had been noticed so far, and it was decided to find where the rupture occurred in various kinds of welds made

Jan 1, 1920

By R. Floyd Farris

A method is presented for determining minimum waiting-on-cement time, which takes into account the differences that exist between types and brands of cements and such individual well conditions as depth, temperature, and pressure. The basis for the method was determined by laboratory tests. Being a laboratory development, several steps were required to prove its merit. The first step consisted of laboratory tests designed to determine the minimum cement strength required in wells. Basis was found for setting a minimum value of 8 Ib. per sq. in. tensile strength. Next, it was shown by laboratory tests that the time to 8 Ib. per sq. in. tensile strength may be expressed as a function of consistometer stirring time to loo "poises," the approximate relation being "the time to 8 Ib. per sq. in. tensile strength equals the time to I00 'poises' times three." Next, it was shown that the time of maximum temperature development in cement slurries, due to heat of hydration, is also related to consistometer stirring time to loo poises, but only by a factor of approximately two. It was shown also that the shut-in casing pressure will build up after cement is placed and register a maximum pressure at approximately the same time the slurry down the hole attains maximum temperature. From this and the relationships listed above, the general rule was established that minimum waiting-on-cement time (time to 8 Ib. per sq. in.) after casing cement jobs in any well is equal to the time when the shut-in casing pressure reaches a maximum, as measured from the initial mixing of cement, times a factor of 1.5. Cement plugs drilled in the field at the time prescribed by this formula were found to drill "firm to hard," thus confirming the laboratory tests. These tests prove that many of the present regulations for waiting on cement require a longer time than is absolutely necessary. Use of the method herein proposed offers the possibility of a saving of $1200 per well. Introduction The length of time allowed for cement to set after casing is determined either by state-wide rules, field rules, or self-imposed rules written into drilling contracts. In general, the time is dictated by experience and common practice. However, owing to differences in opinion and in experience of the various groups involved, waiting-on-cement time often varies from one area to the next. For example, an operator in an area where no rules exist may drill out of surface pipe at 24 to 36 hr., while another operator in another area may wait 48 hr. or more to comply with state or field rules, although the depth of the well, hole size, type of cement, and other data are identical. An even greater difference in practices will be found by making similar comparisons with respect to oil-string cement jobs. Differences in waiting-on-cement times of 36 to 48 hr. are common. Further complicating the picture is the rather common practice of allowing more waiting time for cement to set at the greater depths than is allowed at the shallow depths. This practice has existed for years in spite of the common knowl-edge1,2,3 that the temperature of the earth at the usual setting depths of surface

Jan 1, 1946

By R. Floyd Farris

A method is presented for determining minimum waiting-on-cement time, which takes into account the differences that exist between types and brands of cements and such individual well conditions as depth, temperature, and pressure. The basis for the method was determined by laboratory tests. Being a laboratory development, several steps were required to prove its merit. The first step consisted of laboratory tests designed to determine the minimum cement strength required in wells. Basis was found for setting a minimum value of 8 Ib. per sq. in. tensile strength. Next, it was shown by laboratory tests that the time to 8 Ib. per sq. in. tensile strength may be expressed as a function of consistometer stirring time to loo "poises," the approximate relation being "the time to 8 Ib. per sq. in. tensile strength equals the time to I00 'poises' times three." Next, it was shown that the time of maximum temperature development in cement slurries, due to heat of hydration, is also related to consistometer stirring time to loo poises, but only by a factor of approximately two. It was shown also that the shut-in casing pressure will build up after cement is placed and register a maximum pressure at approximately the same time the slurry down the hole attains maximum temperature. From this and the relationships listed above, the general rule was established that minimum waiting-on-cement time (time to 8 Ib. per sq. in.) after casing cement jobs in any well is equal to the time when the shut-in casing pressure reaches a maximum, as measured from the initial mixing of cement, times a factor of 1.5. Cement plugs drilled in the field at the time prescribed by this formula were found to drill "firm to hard," thus confirming the laboratory tests. These tests prove that many of the present regulations for waiting on cement require a longer time than is absolutely necessary. Use of the method herein proposed offers the possibility of a saving of $1200 per well. Introduction The length of time allowed for cement to set after casing is determined either by state-wide rules, field rules, or self-imposed rules written into drilling contracts. In general, the time is dictated by experience and common practice. However, owing to differences in opinion and in experience of the various groups involved, waiting-on-cement time often varies from one area to the next. For example, an operator in an area where no rules exist may drill out of surface pipe at 24 to 36 hr., while another operator in another area may wait 48 hr. or more to comply with state or field rules, although the depth of the well, hole size, type of cement, and other data are identical. An even greater difference in practices will be found by making similar comparisons with respect to oil-string cement jobs. Differences in waiting-on-cement times of 36 to 48 hr. are common. Further complicating the picture is the rather common practice of allowing more waiting time for cement to set at the greater depths than is allowed at the shallow depths. This practice has existed for years in spite of the common knowl-edge1,2,3 that the temperature of the earth at the usual setting depths of surface

Jan 1, 1946

By Gregoire Gutzeit

THE development reported in this paper was begun by the author a number of years ago, while he was a lecturer on complex chemistry and metallurgy at the University of Geneva, Switzerland, and in charge of that institution's research laboratory. Completion of the development and reduction to practice did not occur until last year at the Westport mill, laboratories and testing plant of the Dorr Company, where this method is now in general use for identifying and localizing the mineral constituents of both metallic and nonmetallic ores. It has proved to be a practical tool of the metallurgical staff at the Westport mill, devising unusual milling flowsheets for complex and refractory ore bodies. In a number of instances the findings have been successfully used as fundamental factors in the design and specification of complete metallurgical plants. Seven examples of the use of this method in solving practical milling problems are included in this paper. GENERAL OUTLINE The microscopic study of an ore, at first only of scientific interest, has proved extremely useful both in practical geology and in ore dressing. The binocular magnifying lenses for rough observation of the products of an ore-dressing plant have been in use for a long time; but only within the last few years has a systematic microscopical examination of ore samples become a normal tool of any research laboratory dealing with ore-dressing problems. Such an investigation avoids considerable loss of time as well as empirical trials and useless experimentation. It will generally indicate the correct grinding and often will suggest the proper method of treatment. The petrographic determination of transparent minerals in thin sections, or even in grains, has been perfected, and very accurate methods have been devised to meet any requirement, such as Feodorof's rotating stage on the petrographic microscope. Almost all transparent minerals can be positively identified by their optical properties; i.e., isotropism, anisotropism, color, pleochroism, refractory index, cleavage, crystal form, birefringence, and others. The identification of opaque minerals is a much more difficult problem and can be done only by using polished specimens. Unfortunately, most of the valuable metallic ores, and even some of the nonmetallic ones, are not transparent; therefore it has been necessary to develop a special technique for the determination of these minerals. Some optical properties-for instance, isotropism, anisotropism, color, cleavage, reflecting power-are often adequate in roughly classifying the mineral. Only "reflecting power" is a measurable value, provided special photometric equipment (ocular photometer or Orcel's photoelectric cell) is available. The other optical properties mentioned are more or less relative,

Jan 1, 1942

By R. K. Ham, M. L. Wayman

TD-Nickel has been broken in tension and in fatigue at voom temperature. Rod specimens failed in tension by necking, with axial cracks attributed to voids elongated in the extrusion direction. Fatigue specimens failed in shear. Thin-film electron microscopy showed that the subgrain structure of TD-Nickel was very stable, and that particle-matrix detachment was very difficult, in tension and fatigue. TD-Nickel softened slightly during fatigue but had a high fatigue ratio (0.5at 10' cycles). Fractography suggested that Stage I fatigue crack propagation is greatly extended in TD-Nickel. Td-NICKEL* is a dispersion of 2 pct by volume of thoria (ThO2) in nickel, produced by powder-metallurgical methods including compaction, sintering, and extrusion. The spherical thoria particles, which may have a mean diameter of a few hundred angstroms, are dispersed with a mean planar spacing of a few thousand angstroms. By a combination of cold working and annealing, a subgrain or cell structure of dislocations intimately associated with the dispersion can be produced.' This gives the material useful tensile properties which are extremely resistant to exposure to high temperatures.'-= At the same time, the material shows considerable ductility.3'4 At the beginning of the present work, it was considered of great interest to investigate the mechanical stability of TD-Nickel under conditions of fatigue. On the one hand, materials which derive strength from a cold-worked structure are unstable in that they are susceptible to fatigue softening: in addition, the presence of discontinuities such as the particle-matrix interfaces might be expected to assist in the initiation and propagation of fatigue cracks, in that they may provide local concentrations of internal stress and sites for the initiation of voids." On the other hand, the substantial ductility of TD-Nickel suggests that if it obeys Coffin's relation8 (or the more refined form proposed by Manson9) it should have good fatigue resistance. The initial purpose of this investigation was to assess the importance of these factors. Also, relatively little fundamental work has been done on the mechanism of fatigue in dispersion-strengthened materials. Work on overaged A1-4 pct CU10-12 revealed a very large Bauschinger effect indicative of internal stresses at the particles, and very great fatigue hardening1' presumably due to the multiple slip stimulated by these internal stresses, followed by softening which was initially due to softening in the matrix, but later might have arisen from cracking at the particle-matrix interfaces. The study of overaged Al-4 pct Cu could not settle this latter point by the electron microscopy of thin films, since the dispersion is too coarse. A previous study of the fatigue of internally oxidized copper13 was complicated by inter granular failure, attributed to oxide particles at grain bouhdaries; internal oxidation of single crystals, however, improved their fatigue properties.'3 Investigations of SAP (sintered aluminum powder) are complicated by the complex particle shapes, and the possibility of continuous internal oxide films.14 It was hoped to avoid these difficulties with TD-Nickel, which had the further advantages that it was commercially available and suitable for study by the thin-film technique. 1) MATERIALS AND EXPERIMENTAL PROCEDURE TD-Nickel was purchased from the Driver-Harris Co. as 3/9-in.-diam rod which had been extruded, swaged, and "stress-relieved" (normally at 1010°C for 1 hr). Continuous-radius fatigue specimens with a minimum diameter of -0.1 in. were ground to shape and electropolished in 40 pct phosphoric, 35 pct sul-furic, 25 pct water at 25oC, with a stainless-steel cathode, at -6 v. Fatigue tests were carried out at room temperature with a Sonntag SF-1-U machine operating in push-pull at 1800 cycles per min, and in an Instron TT-C-L modified for reversed stressing at 26 cycles per min as described elsewhere.10 Round tensile specimens were ground with 0.85-in. gage lengths of 0.135 in, diam, electropolished, and tested in a Tinius Olsen hydraulic machine. The surfaces of fatigue specimens were examined with a Reichert metallograph. Discs for electron microscopy with a Siemens Elmiskop I were spark-cut 0.01 in. thick with a modified Servomet 11 employing a tool of moving molybdenum wire, cleaned in 50 pct acetic, 30 pct nitric, 10 pct phosphoric, and 10pctsul-furic at 85oC, and thinned by the window method in the electropolishing solution at -20°C and -6 v. Two-stage replicas (parlodion, then Pt-50 pct C self-shadowed at 40 deg) were taken from fatigue fracture surfaces for electron microscopy. Plane sections parallel to the specimen axis and containing the direction of fatigue crack propagation were polished, etched with Carapella's reagent, and examined optically. Transmission Laue X-ray photographs of as-received material electropolished to a point were used to determine preferred orientation. 2) RESULTS 2.1) The Structure of As-Received Material. Grains -1 µ diam and elongated 20 to 30 u in the direction of the rod axis were observed, With' elongated "intergran-ular" voids (-4 p diam and -90 µ long and identified as such using longitudinal and transverse sections and

Jan 1, 1968

By E. R. Parker, R. H. Thielemann

The conventional short-time tensile test provides a reliable means of predicting the sustained load-carrying capacity of steels only when the temperature is such that continuous plastic flow does not occur. At elevated temperatures, stresses considerably less than the short-time rupture value may produce continuous flow, with fracture occurring only after long periods of time. The amount of flow or creep accompanying failure varies for different steels, and depends, to a large extent, on the temperature and the duration of the test. Service records of cracking stills, steam superheaters and high-temperature boilers have shown that brittle fractures sometimes occur with little or no warning. In installations of this type, localized stresses are often encountered, and steels must be capable of withstanding a certain amount of deformation without fracture. The sustained-load rupture test determines the expected life and corresponding ductility of steels at various stresses and temperatures. It also yields additional information regarding the effect of micro-structure and metallurgical stability on the high-temperature properties. Present Status of Sustained-load Rupture Test The sustained-load rupture test conducted at elevated temperatures is not entirely new. Dr. Zay Jeffriesl presented in 1919 the results of a large number of rupture tests made on copper, iron and tungsten. These tests were made with various strain rates and at temperatures ranging from the boiling point of liquid air to 1000° C. At that time he observed the interesting phenomenon characteristic of metals, that a temperature exists below which a metal is ductile and breaks with a transcrystalline fracture (through the grain) and above which the metal is brittle and breaks with an intergranular fracture (through the grain boundaries). He observed that this temperature varied with the testing speed, and that a minimum temperature, slightly above the recrystallization temperature, existed at which the cohesion of the grains themselves was

Jan 1, 1939

By R. H. Thielemann, E. R. Parker

The conventional short-time tensile test provides a reliable means of predicting the sustained load-carrying capacity of steels only when the temperature is such that continuous plastic flow does not occur. At elevated temperatures, stresses considerably less than the short-time rupture value may produce continuous flow, with fracture occurring only after long periods of time. The amount of flow or creep accompanying failure varies for different steels, and depends, to a large extent, on the temperature and the duration of the test. Service records of cracking stills, steam superheaters and high-temperature boilers have shown that brittle fractures sometimes occur with little or no warning. In installations of this type, localized stresses are often encountered, and steels must be capable of withstanding a certain amount of deformation without fracture. The sustained-load rupture test determines the expected life and corresponding ductility of steels at various stresses and temperatures. It also yields additional information regarding the effect of micro-structure and metallurgical stability on the high-temperature properties. Present Status of Sustained-load Rupture Test The sustained-load rupture test conducted at elevated temperatures is not entirely new. Dr. Zay Jeffriesl presented in 1919 the results of a large number of rupture tests made on copper, iron and tungsten. These tests were made with various strain rates and at temperatures ranging from the boiling point of liquid air to 1000° C. At that time he observed the interesting phenomenon characteristic of metals, that a temperature exists below which a metal is ductile and breaks with a transcrystalline fracture (through the grain) and above which the metal is brittle and breaks with an intergranular fracture (through the grain boundaries). He observed that this temperature varied with the testing speed, and that a minimum temperature, slightly above the recrystallization temperature, existed at which the cohesion of the grains themselves was

Jan 1, 1939