Search Documents

By Molly Gleiser, John Chipman

The standard free energy of formation of WC was obtained from determination of the equilibrium WC + CO2 = W + 2CO between 1215° and 1266°K. Its uallie is -8340 * 300 cal Per mole over the above range of temperature. AS a part of a program devoted to measuring the stabilities of the carbides, a study was made of the free energy of formation of tungsten carbide, WC. The homogeneity range of this compound is very small,' and it is generally accepted and is dealt with here as a stoichiometric compound. The heat of formation, ?H°f, of WC has been accurately measured by Huff, Squitieri, and snyder.2 The only attempt, however, to measure the free energy of formation of this compound was made by Schenck, Kurzen, and wesselkock3 who brought tungsten carbides into equilibrium with H2 and CH4. Unfortunately their results are not sufficiently accurate nor consistent enough to permit the calculation of free energies. METHOD Heating mixtures of tungsten and carbon powders in hydrogen for 4 days at 1050°C led to formation of some WC without any trace of W2C. It was deduced, therefore, that at least below this temperature W2C will not be formed during experiments with mixtures of tungsten and WC. This was subsequently shown to be correct. The method chosen was the measurement of the equilibrium of the reaction

Jan 1, 1962

By John H. Hall

The Frémont test for measuring the energy consumed in breaking a notched bar of steel is not so well known in this country as it deserves to be. The test specimen used in this test is about # by 6 by about 16 in., notched with a hack saw on the lower side to cause the piece to break at a fixed point. A weight of 10 kg. falling 4 m., and provided with a knife or chisel which strikes the specimen, breaks the test piece by impact. The residual force in the falling weight after it has broken the specimen is recorded by a suitable device, and the difference between the total energy and the residual energy of the weight (in kilogrammeters) is the force consumed in breaking the specimen. An experience of several years with the Frémont testing machine has shown its great value in readily detecting brittleness not revealed by tensile testing or slow bending testing. In this paper it is proposed to discuss (1) the supersensitiveness of the test as applied to cast steel and (2) its value in revealing the effect of heat treatment under certain conditions. In testing coupons cut from castings heat treated by quenching and annealing, attention was drawn to the wide variations in the value of the Frémont test of specimens cut from different parts of the coupon. The latter was of the form and dimensions shown in Fig. 1, and Fremont test pieces were cut from two parts of this coupon, marked A and B in that figure. The results of the tests are shown below, tests A and B in each instance being from the same coupon: A. B. A. B. Coupon. Kilogram- Kilogram- Coupon. Kilogram- Kilogram- meters. meters. meters. meters. 1,........ 12.0 12.5 9,........ 27.5 32.5 2,........ 11.0 32.5 10,........17.5 31.0 3,........ 11.5 30.0 11,........ 14.5 31.0 4,........ 20.0 33.0 12,........ 15.0 27.5 5,........ 17.5 33.0 13,........ 19.0 30.0 6,........ 17.5 20.0 14,........ 17.5 25.5 7,........ 17.5 13.0 15,........15.0 30.0 8,........ 10.0 30.0

Jan 1, 1914

By J. Chipman, N. J. Grant, H. L. Bishop

Lime and dicalcium-silicate crucibles were equilibrated with molten iron and liquid slags containing iron oxide and small amounts of sulfur. The oxygen content of metal, iron oxide activities, and desulfurization values of the slags were determined in the temperature range 1530 to 1700°C. The influence of magnesia in the slag and the temperature dependence of the solubility of lime in liquid iron oxide and the ferric oxide content were established. The temperature contour of the liquidus surface of iron-silicate slags saturated with lime and dicalcium silicate was also established at 1600°C. THE importance of the role that slag composition plays in the refining of steel has been known for many years. Numerous studies have been made using actual plant data in order to establish the relationship between the composition of the slag and metal during the refining of a heat of liquid steel. These results rarely represent equilibrium conditions since completion of the various chemical reactions involved in steelmaking is seldom realized. In order to establish quantitatively the equilibrium conditions existing between the slag and metal, several laboratory studies have been conducted in the past 20 years to determine the reactions important in slag control. These investigations have included studies of simple liquid basic and acid slags as well as more complex slag systems which approach those commonly found during the refining of a heat of steel. Since most of the previous studies of simple basic iron-oxide slags equilibriated with molten iron were made in magnesia crucibles, it was not possible to establish the distribution of sulfur and oxygen between molten iron and slags consisting only of the three essential components, lime, silica, and iron oxide. This investigation was undertaken to establish the equilibrium conditions for simple lime-iron oxide and lime-silica-iron oxide slags. Accordingly, it was expedient to prepare crucibles both of lime and dicalcium silicate to establish the equilibrium conditions between molten iron and iron-oxide slags saturated with the refractory materials and free from other components. The only other studies of the equilibrium between molten iron and lime-saturated slags are those of Fischer and vom Ende, 1, 2 in which the solubility of oxygen was determined in an air atmosphere. The

Jan 1, 1959

By R. D. Pehlke, P. D. Goodell, R. W. Dunlap

The rate of dissolution of steel bars in molten pig iron has been measured experimentally in the temperature range 2300° to 2650° F. The rate of solution is shown to be a .function of bath composition, temperature, and stirring. A kinetic model based on carbon diffusion in the liquid phase has been derived to fit the experimental results. THE rate of scrap melting has long been an important variable in steelmaking operations. With the advent of the oxygen steelmaking process and the accompanying shorter heat times, the rate of scrap melting has now become one of the rate-limiting factors in steel production. As observed in commercial practice, the solution rate is influenced by the compositions of liquid and solid, the temperature, agitation, and time. However, no definitive work has been done on the Fe-C system, and there is very little information in the literature regarding the relative effects of these variables in steelmaking systems. A number of questions have been raised in regard to scrap utilization in basic oxygen steelmaking operations. Consideration has been given to the optimum size and shape of scrap, and to the use of preheated scrap as a means for decreasing the pig-iron requirement in oxygen blowing. The determination of an optimum scrap practice for a specific installation depends to a large extent upon the economics of the scrap market and also upon the behavior of scrap in the vessel. The present research was undertaken as a preliminary study in evaluating the behavior of steel in a pig-iron bath under various conditions of temperature, composition, and agitation, as might be encountered in oxygen converter operations or in any steelmaking operation where scrap behavior is an important process variable. Related studies have been carried out on non-ferrous systems. The solution rate of solid aluminum in a molten A1-Si alloy has been studied.' Furthermore, the increasing use of liquid metals has created considerable interest in studies related to dissolution of a solid in a liquid, or mass transfer taking place between a solid interface and a liquid metallic phase.2-10 In an effort to clarify the relative importance of factors influencing the dissolution of scrap in Fe-C alloys, this paper presents the results of a study of the rate of dissolution of a low-carbon steel cylinder in a molten Fe-C bath at various bath compositions, temperatures, and conditions of agitation. An attempt has been made to determine the mechanism of solution, and a model has been derived to fit the experimental results. The rate of heat transfer between the molten pig-iron bath and the solid-steel cylinder has also been studied. EXPERIMENTAL PROCEDURE A molten bath of pig iron (nominal composition 4.2 pct C, 0.5 pct Mn, 0.8 pct Si)* was held in a 200- *In view of the fact that the composition of the pig-iron bath was slowly changing with time because of steel dissolution and reaction with the surrounding atmosphere, intermittent samples of the liquid bath were taken throughout each experiment, Table 1. lb induction melting unit. The internal diameter of the furnace was 8-1/2 in. and the bath depth approximately 14 in. Cold-finished 1020 steel cylinders of 1/2-, 3/4-, 1-, 1-1/2-, and 2-in. diameters were cut into 1 -ft lengths for use as test specimens. One end of each bar was machined to fit a hand-driven, mechanical stirring device which rested on top of the furnace. This fixture permitted 7 to 8 in. of the bar to be immersed in the melt. The steel cylinders were cleaned to free the surface of grease and oxide. The rods, at ambient temperature, were immersed into the molten pig-iron bath. The melt temperatures studied in this investigation were 2300°, 2500°, and 2650°F. Different agitation conditions were achieved by operating with a) the power to the furnace, giving induction stirring; b) induction stirring plus mechanical stirring, using hand rotation with a chain and sprocket assembly at approximately 200 rpm; c) mechanical stirring alone with the power off; and d) the power off and no mechanical stirring resulting in minimum agitation, i.e., only that caused by natural convection currents in the bath. The samples were immersed in the melt for prescribed times ranging from 30 sec up to 6 min. Immersion times were measured with a stopwatch and temperature control of the melt was achieved by power adjustment following temperature measurement with an optical pyrometer. The measurements with the calibrated pyrometer were checked out to within less than 10°F with simultaneous thermocouple measurements. Following immersion, the bars were water-quenched and the diameters were measured with a micrometer at several positions on the reduced area, and by volumetric displacement. The dissolution rates calculated from the

Jan 1, 1965

By M. J. Blackburn

The ordering reaction and its effect on dislocation awangements in alloys based on Mg3Cd has been studied by transmission electron microscopy. Ordering occurs by the growth of ordered domains until they impinge, thus producing an antiphase domain boundary (APB) network. In the disordered alloy, slip is confined to the basal plane while in the ordered condition slip occurs on the basal, prism, and pyramidal planes. Superdislocations have been identuied on these planes and their origin and expected spacings are discussed and compared with the observations. The APBs between the dislocation pairs have been resolved and have proved useful in the identification of superdislocations. Observed slip structures are related to the changes in mechanical properties produced by ordering. At high temperatures magnesium and cadmium form a continuous series of disordered hexagonal solid solutions. At lower temperatures three ordering reactions occur; two based on the compositions Mg3Cd and MgCd3 are transformations to DO19-type superlattices while alloys based on the composition MgCd transform to a B19 lattice. The ordering process in alloys near the composition Mg3Cd has been studied by several workers'-4 and it has been shown to be a first-order type transformation. The variation of mechanical properties with the degree of order and temperature have been reported in some detail by Stoloff and Davies.5 It was shown that the disordered alloy was stronger and less ductile than the ordered alloy, the differences being attributed to changes in the number of active slip planes and to the presence of short-range order in the disordered alloy. In this investigation the ordering reaction has been qualitatively followed by transmission electron microscopy. The effect of this ordering transformation on the dislocation arrangements in deformed specimens has been studied in some detail. EXPERIMENTAL Alloys were melted in a stainless-steel crucible under a flux and chill cast; both melting and casting were performed in an argon atmosphere. The ingots were hot-rolled and tensile specimens cut from the resultant strips. Some large-grained specimens were grown by the strain-anneal method. Heat treatment was carried out in inert atmosphere furnaces and in oil baths at the lower temperatures. Thin foils for transmission electron microscopy were produced by electropolishing in a cooled solution (temp = -40°C) containing 50 cu cm of nitric acid and 180 cu cm of methanol at a potential of 10 v. The ordering reaction was followed by transmission electron microscopy, X-ray, and electrical resistivity measurements but this paper will be concerned chiefly with the electron-microscopy results. Much of the work described in this paper was performed on an alloy containing 26.10 at. pct Cd although two of the micrographs are taken from work on a 25.55 at. pct Cd alloy. RESULTS i) The Quenched Solid Solution. Specimens which were quenched from above the critical temperature showed diffuse superlattice reflections. sark-field analysis on these reflections failed to reveal the presence of ordered domains and thus the superlattice reflections were assumed to arise from regions of short-range order. Quenching from temperatures of 400" to 450°C results in the formation of dislocation loops and helical dislocations. Such defects have been observed and analyzed in detail in several hexagonal metals6-' and as the crystallography and interactions of such loops appear similar in this alloy they will not be reported in detail. Fig. 1 shows a high density of loops

Jan 1, 1968

By G. W. P. Rengstorff, R. B. Fischer

A study was made of the effect of impurities on the bend ductility of cast molybdenum. High purity molybdenum was repared by re-melting under high vacuum. The ductility of "transverse-grain" specimens indicated that intergranular brittleness decreased with an increase in purity of the metal. THE production of as-cast molybdenum with high ductility at room temperature would make working of the metal easier and increase the usefulness of the as-cast metal. Furthermore, a .knowledge of the factors that influence the ductility of as-cast molybdenum might be applied to the problem of making fusion weldments having satisfactory room-temperature ductility. Individual grains of commercial as-cast molybdenum are slightly ductile at room temperature. However, the presence of carbides at the grain boundaries may cause the metal to fracture in a brittle manner. This behavior has been discussed.' The amount and distribution of the impurities in as-cast molybdenum would be expected, from previous research on the metal, to have considerable influence on its ductility. Some effects of oxygen and carbon on the mechanical behavior of the metal were discussed by Parke and Ham,2 Woodside,3 and Zappfe. Landgraf, and Worden.4 Parke and Ham2 found that, if a sufficient number of molybdenum oxide particles were present at the grain boundaries, the intergranular cohesion was reduced to the extent that arc-melted molybdenum would rupture intergranularly during hot forging. They also found that if the oxygen content was less than 0.003 pct, the cast molybdenum was hot forgeable. It is suspected, however, that forgeable molybdenum may contain a small amount of oxide that could reduce the ductility of the as-cast metal at room temperature. Also, there is the possibility of the unfavorable distribution of other impurities having a detrimental effect on the ductility of cast molybdenum. The results of a study of the influence of purity on the room-temperature ductility of cast molybdenum are presented here. Vacuum Arc-Melting to Produce High Purity Mo One way of determining the effect of impurities on the ductility of molybdenum is to prepare and test metal as free of all impurities as possible. Accordingly, the present investigation was undertaken with this in view. Arc melting in high vacuum (less than 0.1 micron of mercury) was chosen as the method for reducing the impurities below the concentrations occurring in commercial molybdenum. Commercial arc melting of molybdenum is carried out at about 50 microns pressure. During the arc melting, carbon and oxygen in the metal react to form carbon monoxide. By virtue of the vacuum process, the partial pressure of carbon monoxide is maintained at such a low value that the reaction greatly lowers oxygen and carbon contents. An excess of at least 0.03 pct C is used in commercial arc melting to insure that the oxygen content will be below 0.003 pct. The excess carbon remaining after the deoxidation step forms carbides on freezing. Some of the carbides precipitate at the grain boundaries and, as will be shown, have an unfavorable effect on the room-temperature ductility. In the present work, only the small amount of carbon (0.003 pct) contained in the commercial powder-metallurgy molybdenum used for melting stock was present. Partial removal of oxygen from the melt probably occurred as the result of the volatilization of molybdenum oxides, or by distillation of oxygen at the high melting tem-

Jan 1, 1953

By R. B. Snow

This paper describes a technique of polishing and etching specimens of open-hearth furnace slags or hearth aggregates for identification of the crystalline constituents —lime (CaO), tricalcium silicate (3CaO.SiO2), dicalcium silicate (2CaO.-SiO2), rnonticellite (CaO.MgO.SiO2), or forsterile (2MgO.SiO2), with especial em-phasis on the mineral merwinite (3CaO.-MgO.2SiO2). With proper standardization, this identification does not require the use of the petrographic microscope. The composition of basic open-hearth slags and furnace bottoms falls, almost without exception, within systems containing CaO, MgO, 'IFeO,,, MnO and SiOz, in which the number of basic molecules so greatly exceeds the orthosilicate ratio (two molecules of base to one of silica) that free basic oxides, and combinations between them such as alumi-nates or ferrites, are present in cooled specimens. Orthosilicates of (CaO + NgO) are the most common in such specimens, since in nearly all cases, except premelt slags, the molecular ratio of (CaO + MgO) to SiO, is more than 2 to I. When sufficient lime is available it combines with the silica to form dicalcium silicate (2Ca0.Si02), which contains little, if any, IvfgO, FeO or MnO in solid solution whereas the latter oxides combine to form the oxide solid solution known as periclase. If the lime present is insufficient to form dicalcium silicate (2Ca0.Si02) it combines with Mgo to form either merwillite or moIlticellite (SiOz); these minerals take little if any FeO or MnO into solid solution and the remaining MgO, FeO and hInO combine as periclase. This generalization seems to be valid for basic slags and furnace bottoms, since minerals such as Ca0.MnOSi02 and CaO.FeO.SiOz are found only in slags in which the lime-silica ratio is less than 2 and are not observed in 'pecimens from furnace bottoms. The identification of crystalline constituents in such materials, especially of fine crystals in the groundmass, is difficult under the petrographic microscope. They are often masked by their neighbors because of their small size in relation to the thickness of the thin section and because of the presence of Opaque Or colored constituents. The indices of refraction and the optical sign of the mineral are sometimes difficult to determine because of the small size or because Of twinning or of inclusions within the crystal. Moreover, the positive identification of merwinite (3Ca0.Mg0.2Si02) from its optical properties is usually difficult in the presence of dicalcium silicate (zCaO.SiO2). CaO, MgO, jCa0.Si02 and 2Ca0.SiOz in open-hearth 'lags have been identified for a number of years in the U.S. Steel Corporation Laboratory by the usual

Jan 1, 1948

By R. B. Snow

This paper describes a technique of polishing and etching specimens of open-hearth furnace slags or hearth aggregates for identification of the crystalline constituents —lime (CaO), tricalcium silicate (3CaO.SiO2), dicalcium silicate (2CaO.-SiO2), rnonticellite (CaO.MgO.SiO2), or forsterile (2MgO.SiO2), with especial em-phasis on the mineral merwinite (3CaO.-MgO.2SiO2). With proper standardization, this identification does not require the use of the petrographic microscope. The composition of basic open-hearth slags and furnace bottoms falls, almost without exception, within systems containing CaO, MgO, 'IFeO,,, MnO and SiOz, in which the number of basic molecules so greatly exceeds the orthosilicate ratio (two molecules of base to one of silica) that free basic oxides, and combinations between them such as alumi-nates or ferrites, are present in cooled specimens. Orthosilicates of (CaO + NgO) are the most common in such specimens, since in nearly all cases, except premelt slags, the molecular ratio of (CaO + MgO) to SiO, is more than 2 to I. When sufficient lime is available it combines with the silica to form dicalcium silicate (2Ca0.Si02), which contains little, if any, IvfgO, FeO or MnO in solid solution whereas the latter oxides combine to form the oxide solid solution known as periclase. If the lime present is insufficient to form dicalcium silicate (2Ca0.Si02) it combines with Mgo to form either merwillite or moIlticellite (SiOz); these minerals take little if any FeO or MnO into solid solution and the remaining MgO, FeO and hInO combine as periclase. This generalization seems to be valid for basic slags and furnace bottoms, since minerals such as Ca0.MnOSi02 and CaO.FeO.SiOz are found only in slags in which the lime-silica ratio is less than 2 and are not observed in 'pecimens from furnace bottoms. The identification of crystalline constituents in such materials, especially of fine crystals in the groundmass, is difficult under the petrographic microscope. They are often masked by their neighbors because of their small size in relation to the thickness of the thin section and because of the presence of Opaque Or colored constituents. The indices of refraction and the optical sign of the mineral are sometimes difficult to determine because of the small size or because Of twinning or of inclusions within the crystal. Moreover, the positive identification of merwinite (3Ca0.Mg0.2Si02) from its optical properties is usually difficult in the presence of dicalcium silicate (zCaO.SiO2). CaO, MgO, jCa0.Si02 and 2Ca0.SiOz in open-hearth 'lags have been identified for a number of years in the U.S. Steel Corporation Laboratory by the usual

Jan 1, 1948

By Robert A. Rapp

The standard molar free energy of formation of MOO,was determined between 750o to 1050o C in galvanic cell measurements involving the solid electrolyte Zr0.85 Ca0.15 O1.85. Use of the reference electrodes Fe + FexO and Ni + NiO Provided two independent determinations of FoMoo2. The data may be represented by the equation FMoO2 = -137,500 +40.0T(°K) which is in good agreement with previous CO/CO, gas equilibrium measurements of Gleiser and Chipman. The standard molar free energy of formation of molybdenum dioxide has recently been reported over a large range of high temperatures from the calorimetric experiments of King, Weller, and christensen.' Gleiser and chipman2 have also recently determined ?FmoO2 from 926o to 1068oC in CO/CO2 gas equilibrium measurements. Earlier gas equilibrium studies have been made and reviewed by Gokcen.' Over the temperature range studied by Gleiser and Chipman their values for ?FoMoO2 differed from the calorimetric data by about 700 cal. This investigation was undertaken to resolve this difference and thereby establish the two phase mixture of Mo + MOO, as an electrode of well-known oxygen potential for galvanic cell applications at very high temperatures. The galvanic cell technique involving the Zr,.,, Ca,0.15 01.85 solid electrolyte was introduced for the

Jan 1, 1963

By G. R. Belton, Y. K. Rao

A galvanic cell, using liquid MgCl2 or MgC12-CaC12 mixtures as the electrolyte, has been used to determine activities in Mg-A1 liquid alloys between 700' and 880°C. The incovporation of a chlorine electrode in the cell also allowed measurements to be made of the standard free energy of formation of MgCl2(l). The results are shown to be in good agreement with thermo-chetrlical values from the literature, and this is taken as evidence that the small, known solubility of magnesium in iMgCl2 introduces no significant error in galcanic cell measurements. Within experimental error, the activity coefficients and relative partial molar enthalpies at 800°C are shown to be represented by the following "subregular" solution equations: logy~~ =-0.68(1 -xMgj3 log yAL =-1.02(1 - XMf + 0.68(1 - XMf H.M = -4400(1 - %)3 / cal Mg 7Ag' HZ =-6600(1 - xA1)' + 4400(1 - XMf cal SCHNEIDER and toll' have used a transpiration technique to measure the vapor pressures of magnesium over Mg-A1 alloys between 544" and 594°C. amsstad,' however, has since suggested that the extrapolation to zero flow rate, used by these authors in interpreting their apparent pressure vs flow rate data, gives unreliable results. Rogers, Tomlinson, and Richardson,3 in interpreting the results of solution equilibria between Mg-A1 alloys and liquid MgC12, also considered the measurements of Schneider and Stoll to be unreliable and preferred to derive activities for the alloys from the earlier boiling point determinations of ~eit~ebel~ and the partial molar heats recommended by Kubaschewski and ~atterall.~ These latter heats were based substantially on the early calorimetric work of Kawa-kami but, unfortunately, his work on other systems has sometimes been found to be inaccurate.7 Rogers et al., in the above-mentioned paper,3 tentatively concluded that the most likely species responsible for the limited solubility (0.3 mole pct at 800°C) of magnesium in MgC12 were Mg° (neutral) and Mg2++. Two more recent studies8,9 have supported Mg2++ as the soluble species. In the present study, activities in Mg-A1 alloys have been determined by means of a galvanic cell involving liquid MgCl2 or MgC12CaCl, mixtures as the electrolyte. Since the reactive nature of magnesium precluded simple Faraday yield experiments, a chlorine electrode was incorporated in the cell in order that the performance of the cell could be checked by measurements of the heat and free energy of formation of MgC12. This procedure was considered necessary since it has been suggested1' that the solubility of a metal in a molten salt might introduce electronic conductivity; also, previous determinations of the standard electrode potential for MgC12 differed by as much as 70 mv11-13 EXPERIMENTAL Materials. Analyses of the materials used in preparing the alloys and the electrolyte mixtures are presented in Table I. The alloys were prepared by induction melting weighed amounts of the metals in a graphite crucible held under an argon atmosphere. Pure anhydrous magnesium chloride was prepared by heating the mixture MgCl, . 6H20 +NH4C1(1:1) to 650°C, followed by melting under dry argon. The melting point of the dry MgC12 was found by differential thermal analysis to be 714.8oC, which compares well with the accepted value of 714C.14 This agreement was taken to be an indication of the high purity of the dried salt. Table I. Compositions of Materials, wt pn Impurity Mg Al MgCI2 CaCI, Ba - - 0.005 Ca - - 0.010 Cu 0.02 0.02 Fe - 0.10 0.001 0.010 Pb 0.01 - 0.001 0.005 Mn 0.15 0.001 Si - 0.10 Sr - - 0.005 MBSO* - 0.040 ARGON TUNGSTEN CHLORINE LEAD—411 11 II ALUMINA 'A I / ave GRAPHITE on irA~_ ( ^"l ROD MAGNESIUM S>ILICA~^ /, OR ALLOY-. I /A] ___________ -«^- _ ELECTROLYTE I y FRITTED DISCS Fig. l—Arrangement of chlorine and metal electrodes in electrolytic cell.

Jan 1, 1970

By Lawrence K. Jetter, Robert F. Mehl

SOME advances have been made recently in the theory of the kinetics of precipitation from metallic solid solution despite the complexities of the problem, but there is surprisingly little quantitative information available on rates of precipitation with which to test present theory or upon which to build new theory.‡ Attempts to measure rates of precipitation have been beset with difficulties which originate both in the anomalies that attend the changes in the properties selected for measurement, as, for example, in electrical conductivity or mechanical properties, and also in the complexities in the structural changes in some systems, as in the aluminum-copper system. If the functional relationship between the quantity of precipitate and the value of the selected property is uncertain, measurements of that property are obviously of uncertain utility in determining absolute rates of precipitation. If the precipitating system passes through one or more transition stages, the interpretation of measured rates lacks definiteness; in such cases, it is necessary to measure the rate of reaction in each separate stage, if the rate measurements are to have any significance from the kinetic point of view.* These difficulties cannot be wholly avoided, for at least in some measure they are characteristic of the process of precipitation from solid solution, but they can be minimized both by the selection of a simple system and by the use of a method of measurement relatively free from anomalous behavior. The present paper reports dilatometric measurements on the rate of precipitation of silicon from the aluminum-rich solid solution in the aluminum-silicon system-a study that approaches the desiderata of simplicity. The aluminum-silicon system offers advantages from these points of view: there are no known anomalies in the property changes accompanying precipitation; 2.3,4 there are no known transition stages; the precipitate is an element, not a compound, and both matrix and precipitate are cubic, and while the structures are not identical (the solid solution is face-centered cubic and the precipitate is diamond cubic), the system at least approaches the ideal case of a crystal precipitating from a matrix of the same crystal type-the ideal case which Becker5 assumed in treating the precipitation process theoretically. The dilatometric method, while not free from disturbing effects, as the subsequent dis-

Jan 1, 1942

By Charles W. Dickson

Jan 1, 1904

By C. B. Alcock, M. G. Hocking

The kinetics of the growth of sulfate layers on blocks of Cu20 has been studied between 688" and 800°C. At 788c the over-all weight increases followed the parabolic rate law, with k = 216 30 sq mg per cm4 min, using a 1:1 entering gas mixture of SO2:02. At 757 after an initial linear period the parabolic rate law was followed, with k = 57.8 10 sq mg per cm4 min. The gas mixture required a platinum catalyst to produce the maximum SOs pressure. The sulfation rate at 757' and 788c was high until all the CUZO had changed into a core of CuO, when it became very much lower. At 757°C marker experiments showed that the sulfates (CuO. CuS04 and CuSO4) grow outwards from the oxide surface, but CuO. CuS04 mixed with CuO was found beneath the markers. At 688 markers were found at the CuO. CuS04/CuS04 interface. Visual observations at 757 showed a liquid eutectic moving beneath the sulfate surface. causing very rapid sulfation and extruding to solidify as thick 'needles" up to 8 mm long. Marker experiments have shown conclusi.cely that CuO grows on Cu20 in air by the outward migration of copper. ThermODYNAMIC measurements on the sulfate and basic sulfate of copper, reported recently,' are followed here by measurements of the rates of formation of these sulfates on cuprous oxide, in order to provide a background for the understanding of roasting processes. peretti2 and McCabe and Morgan3 have shown that the phase Cu20 lies next to Cu2S when the sulfide is roasted under conditions where sulfates will be formed. Since this would present too complex a system for kinetic study, the present work4 has been based on the kinetics of sulfation of the oxide phase. The results of a study of the kinetics and mechanism of the sulfation of cobaltous oxide have recently been reported.4,5 Results on the sulfation of cuprous oxide have also appeared,6 but are at variance with those to be reported here. This seems to be because the previous workers6 did not obtain constant SO3 pressures from the SO2/O2 sulfating gas mixtures used, as will be discussed later. Wadsworth, Leiter, Porter, and Lewis found that the sulfates produced when SO2/O2 mixtures are passed over Cu20 at red heats are CuS04 and the basic sulfate CuO.CuSO4. When the decomposition of CuS04 was followed' by differential thermal analysis, a stage corresponding to CuO .CuS04 was reached before decomposition into the oxide occurred. APPARATUS The vertical furnace used for quantitative studies was a conventional resistance-heated and propor- tionately controlled furnace with an even zone (1 deg) which was 4 cm long. The gas mixtures of SO2 and 02 were made by mixing measured flows from capillary flowmeters and drying over phosphorous pentoxide before passing them into the Pyrex top-piece of the furnace assembly. A mullite tube of bore 2% cm was used as reaction vessel and at the bottom of this tube was a trap for SO3, which condensed as a colorless liquid. The residual gas was led into a fume cupboard for ventilation to the atmosphere. The furnace used for visual observations of needle growth and other phenomena consisted of a transparent silica reaction tube of bore 3 cm, having an optically flat silica window sealed into its wall. The reaction tube was clamped vertically, inside a mullite tube of bore 4 cm and length 42 cm which was heated by Kanthal windings. The window in the silica reaction tube was arranged opposite a hole 3 cm wide and 2 cm tall which had been cut in the wall of the mullite winding tube 19 cm from its top end. A binocular microscope was used to look through the window, illumination being provided by a focusing microscope-lamp offset sideways and downwards. The oxide block to be sulfated was suspended from the removable Pyrex top-piece to the reaction tube, by means of which it was inserted at the start of the experiment, and through which entered the S02/02 gas mixture. The variation of the temperature inside the reaction tube with horizontal and vertical displacement from the window was investigated, and, while it can be said that the temperature was constant 1 deg, its value at a given position was known only to 12 deg. In both furnaces, the oxide block to be sulfated was suspended from a small silica hook immediately downstream from a platinum thimble used as catalyst, which was held on a long silica rod from a Pyrex spring attached to the removable Pyrex top-piece of the furnace. The spring was only included in the quantitative sulfating furnace; its sensitivity was 1.4 cm per g and it was found to be free from creep in a 16-hr test when carrying the working load. The extensions were followed by a cathetometer which could be read to 0.001 cm, corresponding to i0.7 mg. Extensions of the spring were measured on adding weights between 5 and 500 mg to the working load (thimble + oxide block), and Hooke's law was closely obeyed. SAMPLES Cuprous oxide blocks were prepared by oxidizing Johnson Matthey "Specpure" copper sheet of 1 mm thickness (impurities: iron at 3 ppm, silver at 2 ppm, lead, nickel, sodium, and silicon each at 1 ppm, calcium, chromium, magnesium, and manganese each at less than 1 ppm) for 6 days in air at 1000°C in a re-crystallized alumina boat. It has been reported7 that when Cu20 is prepared by heating copper sheet for 1 day the central plane of the blocks produced consists

Jan 1, 1967

By Charles A. Chase

This paper, descriptive of a single mine, is presented in the belief that it may furnish useful suggestions to mine-managers encountering similar problems; and it includes the details which will enable them to estimate the value of the methods employed—especially where these depart from common practice. Tt should be added, however, that this mine is not typical of the San Juan district, but differs markedly from neighboring mines in physical conditions and metallurgical requirements. The Liberty Bell mine is situated in San Miguel county, Colo., on the west front of the San Juan mountains, 2 miles north of Telluride. The vein was discovered in 1876 by Wm. L. Cornett, who, with subsequeilt locators, took up claims along the apex. A few hundred feet of development-work was accomplished, and a few? tons of ore were smelted or milled; but profitable working proved impossible under existing

Jan 1, 1912

By J. W. Powell, F. H. Spedding

A complete review of the use of chelating agents in the sepa ration of rare earths by ion-exchange is given as well as a concise description of the recent pilot-plant operations of the Ames Laboratory. The two chelating agents which show the greatest promise are ethylenediamine-N,N,N',N'-tetraacetic acid and N'-(2-hydroxyethyl)ethylenediarnine-N,N,N '-triacetic acid. The first successful separations of rare earths by ion exchange were reported in a collection of papers which appeared in the November, 1947, issue of the Journal of the American Chemical Society.1'9 Some of this work was performed at the Ames Laboratory of the A.E.C., the remainder at the Oak Ridge National Laboratory. The processes developed at Oak Ridge, as well as some of the early Arnes methods, employed 5 pct citric acid-ammonium citrate eluant at low pH and were carried out on either H+-state or NH:-state resin beds. These techniques were successful for the separation of small quantities of either naturally occurring or radioactive rare earths and are still used for the isolation of rare-earth activities from fission products. Concentrated citrate is not economical, however, for use in moderate or large-scale rare-earth separations. For this reason, the Ames Laboratory turned its attention to lower concentrations and higher pH's in order to make more effective use of the eluting agent.10-14 Although elutions have been performed successfully over a wide range of conditions, 0.1 pct citrate at a pH of 8.0 is highly recommended for use on H+-state resin beds.15,16 Elu-tion with 0.1 pct citrate in the pH range from 5 to 9 brings about the separation of the constituent rare earths into a series of flat-topped elution bands which progress down the resin bed, head to tail, without actually pulling apart as do the rare-earth peaks which develop when trace quantities are eluted with 0.25M (5 pct) citrate at low pH's. Because of this, elution with 0.1 pct citrate at pH 8.0 do not produce pure rare earths unless sufficient quantities are present to provide developed bands which are at least several inches long on the columns. Although other eluting agents have proved more effective than citrate solutions, articles concerning the use of citric acid for separating rare earths still appear in the literature occasionally. For example, Ketelle and Boyd17 reported some further studies on the separation of rare earths with 5 pct citrate in 1951. They used 270 to 325 mesh Dowex-50 columns at 100°C and a pH of 3.28. vickery18 compared the effectiveness of a number of eluants for the separation of rare earths on NH+4 state Dowex-50 in 1952. He found that citric acid was more efficient than acetic, malic, tartaric, and aminoacetic acids. In 1953, Mayer and Freiling18 reported that citrate was inferior to malate, glycolate, lactate, and EDTA for the resolution of Sm-Eu and Y-Tb mixtures on 250 to 500 mesh, NH+4-state, Dowex-50 at 87°C. pinta20 used 5 pct citrate in the pH range 2.8 to 3.4 to obtain some rare earths for analytical work the same year. Trombe and Loriers21 reported the use of citric acid in their laboratory to separate rare earths in kilogram quantities. Lariers and Quesney22 reported some separations with citrate in 1954. They used 5 pct citrate at pH 2.8 to separate yttrium and the yttrium-group rare earths from the cerium-group rare earths. briers23 used 5 pct citrate at pH 3.2 and 90°C as late as 1956 to isolate thulium in fair purity. For the separation of tracer quantities of rare earths, Mayer and Freiling19 have recommended pH 5.00, 0.24M lactate at 87 °C on 250 to 500 mesh, NH+4-form Dowex-50. Freiling and Bunney24 have also employed lactic acid for the separation of fission-product rare earths. Cunninghame, Size-land, Willis, Eakins, and Mercer25 have reported a 4-hr separation of Y, Eu, Sm, Pm, Nd, and Pr with 1M lactic acid at pH 3.25 on Zeokarb-225 at 87°C. Stewart, et al.,26 reported separation factors for rare earths distributing between Dowex-50 and 0.25M glycolic acid. stewart27 also reported a 30-61 separation of Y, Tm, Er, Tb, and Lu tracers with buffered, 0.25M glycolic acid containing 0.05 pct Aerosol OT. The resin bed was 400-mesh Dowex-50 (X12). The pH of the ammonia-buffered eluant was 3.5. Various aminopolyacetic acids have also been used to obtain varying degrees of separation of the rare earths. In 1951, Fitch and Russell28 investigated iminodiacetic acid (IDA) and nitrilotriacetic

Jan 1, 1960

By K. A. Jackson, G. A. Chadwick, A. Klugert

The diffusion field ahead of a lamellar interfnce is analyzed using an electrical analog. A self-consistent solution is obtained for the shape of the interfnce and the diffusion field by an iterative process. The solutions presented here are for a 50-50 eutectoid or eutectic, The shape of the interface is found to he independent of growth velocity and lamellar spacing, and to depend on the relative values of interfacial free energies at the phase houndaries . The mode of growth of lamellar eutectics and eutectoids has been a subject of much interest for many years.1-4 Mehl and Hagel 1 have shown photomicrographs taken by Tardif when he attempted to determine experimentally the shape of an advancing pearlite interface; the results are completely ambiguous. Brandt' and schei13 have made approximate calculations of the composition ahead of a lamellar growth front. The shape of the advancing front and the composition distribution ahead of the front are difficult to calculate because one depends on the other. It is the purpose of the present paper to describe a method by which this calculation has been done. Lamellar-eutectic growth usually occurs under conditions where the growth is fairly rapid, and the interface temperature is close to the eutectic temperature. The growth rate is usually determined by heat flow. Eutectoid growth, on the other hand, can best be studied by quenching to some temperature, and allowing growth to proceed isother-mally. In both cases the growth is believed to be controlled by diffusion* rather than by the atomic kinetics of the transformation. This being the case, a single treatment of the diffusion equation will apply to both cases, provided the region of the interface in a eutectic may be considered to be isothermal. If a part of the interface could appreciably change its thermodynamic driving force by advancing ahead of or lagging behind the mean interface, then the two cases would not be similar. Eutectics normally grow in temperature gradients of the or-der of a few degrees per centimeter. The normal eutectic spacing is the order of a few microns. Part of the interface would have to extend many lamellar spacings ahead of the mean interface before it experienced sensibly different conditions. The interface temperature is usually a few tenths of a degree below the eutectic temperature so that temperature differences of the order of one-thousandths of a degree (a displacement of one lamellar spacing) would be unimportant. Protrusions large compared to the mean spacing do occur when one phase only grows into a eutectic liquid. This is usually a dendritic type of growth, and easily distinguishable from the lamellar mode of growth. A single treatment of lamellar growth will apply equally well to both eutectic and eutectoid decomposition. At the interface, which as shown above is essentially isothermal, the difference between the equilibrium eutectic temperature Teu and the actual interface temperature Ti, can be divided into two parts: 1) the composition varies across the interface, so that the local equilibrium temperature is not Teu; and 2) the interface is curved, so that the local equilibrium temperature is depressed according to the Gibbs-Thompson relationship. This undercooling can be written as Teu-Ti =?T = mAC(x) + a/r(x) [1] where ?C(X) is the departure of the composition at a point x on the interface from the eutectic composition, see Fig. 1, r(x) is the local radius of curvature at a point x on the interface, m is the slope of the liquidus line on the phase diagram, and a is a constant given by where s is the interfacial free energy, TE is the equilibrium temperature, and L is the latent heat of fusion. The calculations in this paper will be made only for the case where the phase diagram is symmetric, that is, the eutectic occurs at 50 pct, the liquidi have the same magnitude slope m at the eutectic temperature, and C,, the amount of B rejected when unit volume of a freezes, see Fig. 2(a), is the same for both phases. As shown in Fig. 2(b), the composition ahead of the a phase will be rich in B, the composition ahead of the ß phase will be rich in A. The composition at the phase boundary is the eutectic composition. The difference between the local liquidus temperature and the actual tempera-

Jan 1, 1964

By Cornelius F. Kelley

AT the Annual Meeting of the A.1.M.E. last February, Cornelius F. Kelley, chairman of the Anaconda Copper Mining Co., was presented with the Charles F. Rand Memorial Medal for "conspicuous success as administrative head of great enter- prises engaged in the production of nonferrous metals at home and abroad; for inspiring leadership of an organization that has trained able engineers for service wherever ores are mined and metals are recovered; and for enhancing the prestige of metal mining in the financial and industrial world." Mr. Kelley's acceptance speech follows: I am not unmindful of the fact that the distinction is not to be considered a personal one, but that by the language of the citation itself it is rather a recognition of the service that has been performed by the many trained men of an industrial organization that in the arts of mining and metallurgy and in the fabrication of metal products has performed a distinct service to the industry and to mankind. In that spirit, the award is accepted, and on behalf of the organization I represent and myself, I thank you and assure you that the honor is deeply appreciated.

Jan 1, 1944

By Harold B. Goldman, Don Reining

The sand and gravel industry is the largest nonfuel mineral industry in the nation. In 1981, the production of sand and gravel totaled 755 million tons valued at $2.3 billion. California, which leads the nation with more than 110 million tons, together with Alaska, Texas, Michigan, and Ohio, account for 36% of the total production in the nation (Table 1). In commercial usage, sand applies to rock or mineral fragments ranging in size from particles retained on a No. 200 sieve (0.074 mm openings) to those passing a No. 4 sieve (4.76 mm openings). Gravel consists of rock or mineral fragments larger than 4.76 mm, ranging up to 88.9 mm (3 ½ -in.) maximum size. The construction industry consumes 97% of the sand and gravel produced; the remainder is sand used for specialized products such as glass (see the chapter on "Silica and Silicon"). Utilization The building industry uses sand and gravel chiefly as aggregate in portland cement concrete, mortar, and plaster; the paving industry uses sand and gravel in both asphaltic mixtures and portland cement concrete. Aggregate is commonly designated as the inert fragmental material which is bound into a conglomerate mass by a cementing material such as portland cement, asphalt, or gypsum plaster. Portland Cement Concrete Aggregates Portland cement concrete consists of sand and gravel surrounded and held together by hardened portland cement paste. Concrete mixes commonly contain 15-20% water, 7-14% cement, and 66-78% aggregate. Sand and gravel used as concrete aggregate have to meet many requirements (Goldman, 1956). Premature deterioration of concrete has been traced in many instances to the use of unsuitable aggregates. Asphaltic Aggregate Asphaltic mixtures used predominantly for paving consist of combinations of sand, gravel, and mineral filler (material finer than 0.003 in.), uniformly coated and mixed with asphalt produced in the refining of petroleum. Except for the addition of mineral filler, sand and gravel used as asphaltic aggregate must meet the same general physical requirements as materials used for portland cement concrete aggregate. General Requirements of Aggregates Construction aggregate has many requirements that are difficult to meet if only unprocessed material from natural deposits is used. Suitable material is composed of clean, uncoated, properly shaped particles which are sound and durable. Soundness and durability are terms used to denote the ability of aggre- [ ]

Jan 1, 1983

By W. P. Rawles

In the foreword by C. K. Leith, Chairman of The Mineral Inquiry, it is pointed out that the ordinary mineral production tables do not show the commercial control, and that some knowledge of the situation is desirable as a background for the consideration of problems involving mineral raw materials. The report consists principally of tables, accompanied by a brief text, giving the production and an analysis of the control, according to nationality, of 18 minerals: aluminum, chromite, copper, iron and steel, lead, manganese ore, mercury, molybdenum, nickel, nitrates, petroleum, potash, silver, sulfur, tin, tungsten, vanadium, and zinc. For the most part, the production figures for 1929 and the latest figures for reserves have been used. When feasible, the control has been shown at the various stages of production; mining, smelting and refining. American capital was dominant in the production of 10 mineral commodities, including six of the most important; British capital, in four instances; while Spanish, German, Chilean or Chinese interests cach led in the control of one. British, French, German, and Dutch capital occupied second place in the control of most of the important minerals. Between two-thirds and three-fourths of the world's mincral production is controlled by British and American capital.

Jan 1, 1934

By P. M. Kelly, E. P. Butler

The stability of a 70/30 Mn-Cu alloy aged to peak damping has been investigated using electron microscopy, X-ray diffraction, and torsional pendulum measurements. Storage at room temperature or at 100" C causes a reduction in damping capacity. This is shown to be due to the formation of subdomains which "lock" the main domain structure and so hinder their movement. After storage the damping capacity can be restored by a retransformation treatment, which generates structures identical to those found in newly aged specimens. Plastic deformation by rolling also causes a decrease in damping capacity. In this case the damping capacity can only be restored by retransformation if the amount of deformation is less than about 5 pct. THE general metallography and structure of these high damping capacity alloys has been discussed in Part I of this work.1 Part II deals with some of the variables that affect the damping capacity. In particular, the stability of the damping capacity of a 70/30 alloy aged for 2 hr at 425° C and quenched has been investigated. The temperature sensitivity of the damping capacity of a 70/30 alloy aged for 2 hr at 450° C has been reported by Birchon.2 The damping capacity begins to decrease with increasing temperature, and is very low above the M, temperature of 125°C. The cubic — tetragonal transformation is completely reversible and there is no apparent thermal hysteresis associated with the change in damping capacity. Another important effect was first reported by Dean and his coworkers.3 They noticed a decrease in the damping capacity with time for specimens of a quenched tetragonal alloy. More recently workers at the Admiralty Materials Laboratory 4 have studied the stability of an aged 70/30 alloy. They found that the damping capacity decreased to half its original value after about 1000 hr at room temperature. EXPERIMENTAL The techniques used for electron microscopy and X-ray diffraction have been described in Part I. The damping capacity was measured by means of a torsional pendulum, using rectangular specimens, 3 by 0.3 mm with a 6 cm gage length. The specific damping capacity, S.D.C., was calculated as a percent amplitude decay in free vibrations over 10 cycles, starting at an amplitude which corresponded to a 700 psi surface shear stress. Because of the stress dependence of the damping,' the values obtained were about a third those reported for a 5000 psi surface shear stress.' RESULTS a) Effect of Aging Temperature. The effect of aging temperature on the damping capacity is shown in Fig. 1. The damping capacity reaches a peak of 12 pct after aging at 400° to 425°C) then begins to decrease as the volume fraction of a Mn increases. At higher aging temperatures the structure becomes cubic again with a low damping capacity. b) Stability of the Aged Structure. The damping capacity of the aged alloy decreases with time at room temperature. This process could be accelerated by storing at 100°C, when about 100 hr were required for the damping to fall to half its original value. The results of room temperature and 100°C storage, for times up to 1000 hr, are shown in Fig. 2. The damping capacity starts to decrease after about 24 hr at 18° C and 1 to 2 hr at 100°C. It was found, however, that the damping could be almost completely restored by retransformation. The specimens were held at a temperature above the M, for a short time, 250° C for 5 min, and then quenched. The values of damping capacity for specimens that were aged, stored, and then retransformed are shown by the full points in Fig. 2. X-ray measurements of the c/a ratio and hardness readings on the specimens did

Jan 1, 1969