By J. H. Swisher

The solubility of graphite in CaO-S2O2-Al,O3 slags was measured by equilibrating slag samples with graphite crucibles and CO gas. Carbon contents as high as 2 ut pct were obtained in CaO-saturated, CaO-A1,O3 slags, and 1.3 wt pct in slags of the composition CaO.Si0,. Although the observed conditions for Sic formation were in agreement with those predicted from thermodynamic data, CaC, was found to form at a lower temperature than predicted frotn thermodynamic data. From measurements of the equilibrium carbon content as a function of CO Partial pressure, it was found that carbide ions dissolve in CaO-A12O3 melts with a valence of minus two. The carbon content increased with CaO concentration in Ca0-Al,O3 melts and increased with SiO, content along the CaO'AlO3-CaOSi0 join in the ternary system. When solid CaC2 was added to CaO-A12O3 and CaO-SiO2-A12O3 slags, it was found that one of the oxides in the slag was reduced by the carbide (Al2O3 in the forrner and SiOz in the latter). In electric furnace steelmaking, a double-slag practice is frequently used to meet alloy specifications. Initially a flush slag, which is oxidizing in nature, is used to remove phosphorus and carbon from the steel bath. Later in the refining period, the flush slag is replaced by a highly reducing carbidic slag. When calcium carbide is formed in or added to a finishing slag, the slag is effective as a desulfurizing agent and also permits alloying elements such as chromium, vanadium, and tungsten to be added to the slag in the form of oxides. The oxides are readily reduced by calcium carbide, thereby minimizing the use of expensive ferroalloys. More work has been done on the thermodynamics of silicon carbide in slags than on calcium carbide. Baird and alor' and Kay and alor' determined the free energy of formation of Sic by measuring the partial pressure of CO in equilibrium with solid silica, silicon carbide, and graphite. Using a similar technique, they determined SiOz activities in CaO-SiOz and Ca0-Si0,-A1203 slags. Rein and chipman3 also determined the free energy of formation of Sic using slag-metal equilibrium measurements. A literature survey has uncovered only one experimental study of the behavior of CaC, in slag systems. Shanahan and cooke4 report the results of some preliminary experiments on the solubility and stability of CaC, in a CaO-A1,03 and a Ca0-Si0-A1,03 slag at a temperature of about 1500". The carbon solubility as CaC, in a slag containing 50 pct CaO and 50 pct A1203 was reported to be 0.6 pct. They also review earlier work on the binary CaO-CaC, system. A eutectic exists in this system, but various investigators disagree on the eutectic temperature and composition. eal has given an explanation for carbide furnace erruptions in terms of the thermodynamic properties of CaC,; his analysis is not based on experimental data, but on compiled data for the free energies of formation of CaC, and CO.' , These data for steel-making temperatures are all extrapolated from the results of low-temperature measurements. In the experiments described in this paper, slag samples were equilibrated with graphite crucibles and with mixtures of CO and argon or with CO gas at 1 atm total pressure for measurement of the carbon solubility. Most of the work was done on Ca0-A1203 binary slags, although in some experiments CaO-SiO, and Ca0-Si0,-A1,03 slags were used. EXPERIMENTAL Slag samples of the desired composition for the solubility measurements were obtained by blending pre-fused master slags. The master slags were prepared by fusing mixtures of reagent-grade CaC03 with either A1,03 or Si0, in a graphite crucible. The master slags were crushed, then decarburized in air in a muffle furnace at 1200O C. A schematic diagram of the apparatus is shown in Fig. 1. The source of carbon for the solubility meas-

Jan 1, 1969

This briefing was sponsored by the Bureau of Mines to summarize ongoing and recently completed chromium-chromite research and resource assessment activities by the Bureau. Through the series of 18 presentations compiled herein, Bureau personnel covered a wide range of topics including U.S. chromite and chromium trends and usage patterns; foreign and domestic resources; and research activities on mineral characterization and beneficiation, chemical and pryometallurgical processing of chromite and chromium-bearing wastes, new low-chromium alloy and coating substitutes, corrosion- and oxidation-resistant stainless steels, and chromium-containing refractories.

Jan 1, 1986

By Michael Mancuso

This report summarizes the problems of topsail handling as related to present requirements of law and current equipment availability. The most prevalent topsoiling systems are reviewed along with a listing of advantages/disadvantages and best features of each system. Seven mining regions are included, along with an analysis of prevailing land use, types of soils and attendant physical, chemical am biological characteristics. There are several probable areas of future research "lined which can benefit mining, minimize the social impact of mined lands and speed the return of mined lands to more productive long-term use.

Jan 1, 1981

By P. Nicholls

Patent records show that the idea that the burning of fuels can be improved by mixing or pretreating them with chemicals 6 dates back to the early years of the last century. By 1845, English and French patents included the specific beneficiations of elimination or reduction of smoke, soot, and clinker; reduction of the ashes, presumably meaning the total weight of refuse from the ashpit; elimination of sulphur fumes; increase in the rate of burning; increase in the time a given charge of fuel would last; and, in most patents, a saving of fuel. The earlier patents specified additions up to 80 pounds or more per ton of fuel, but after 1860 the quantity was rarely more than 4 pounds. There is no record of the extent to which these patents were commercialized, but after 1884 many American patents were assigned to companies specializing in treatment of coal, so it is probable that the products were marketed on a considerable scale at least as early as that date. From 1900 on, many companies marketed proprietary products that were sold under the general name of "fuel savers." Since its establishment in 1910, the Bureau of Mines has continually received inquiries about these products and, at the request of other govern-mental departments, has tested some used in accordance with the instructions of the purveyors; the results were all negative and, within the accuracy of measurements, the products had no effect on the burning.

Jan 1, 1937

By N. A. Gokcen, J. Chipman

A revised treatment of the authors' published data eliminates the complex relation previously proposed between concentration of silicon and activity coefficient of oxygen in liquid iron. Revised values of the thermodynamic properties of the liquid solution are presented. IN a recent experimental study of the reaction SiO2 (s) = Si+ 2O; Kf, = [% Si] [% O]² [1] the authors' found a substantially constant equilibrium product in liquid iron at 1600°C of 2.8x10-5 They also reported extensive data on the reactions: SiO2 (s) + 2H2 (8) = Si- + 2H2O (g); K'2= [% Si] (H2O/H2 [2] and H, (g) + 0 = H2O (g); K'3 =( H2 O [31 (H2) [%O] From the results on reaction 3 and earlier data of Dastur² on this same reaction in the absence of silicon, they determined the activity coefficient of oxygen, f0, on the basis of the definition K3 = (H2O)/ (H2)f0 [% 0] where K, is the equilibrium constant and f0, is taken as unity in the pure Fe-0 system. Similarly values of fsi were deduced from results on reaction 2. In a more recent study" of analogous reactions in the system Fe-A1-0, it was found impossible to reconcile the results on reaction 3 with Dastur's data; accordingly the latter were ignored and the equilibrium results were extrapolated to find a value of K, at zero concentration of aluminum. This procedure failed to locate the cause of the discrepancy but it did yield reasonable values of activity coefficients. It also avoided introduction of the complex empirical relation between the oxygen activity coefficient and the concentration of the added element. The same type of discrepancy exists for system Fe-Si-0.' In the earlier paper an attempt was made to fit both sets of data by a single curved line (Fig. 6 of ref. l), the form of which is contrary to the theoretical requirement of a finite slope at infinite dilution. In the light of experience on the Fe-A1-0 system the discrepancy must be recognized as one which can be resolved only by more refined measurements. Accordingly Figs. 6 and 10 are retracted. It is pointed out also that until the discrepancy is resolved Figs. 7, 8, and 11 are subject to some uncertainty. Qualitatively the following conclusions still appear valid: 1—The activity coefficient of oxygen is reduced by addition of silicon. 2—In dilute solutions the activity coefficient of silicon increases with its concentration. 3—With respect to equilibrium in reaction 1, the above effects are approximately compensating. The discussion of K'1 in the previous paper requires no revision. It was pointed out that the constancy of the product [% Si] [% 0]² ndicated a compensating effect of the activity coefficients of silicon and oxygen. Therefore, as a very good approximation, K1 = K'1 and the following average values are suggested both for K, and K', at the temperatures 1550°, 1600°, and 1650", respectively, 1.0x10-", 2.8~10-" and 5.5 ~lo-'. Revision of the thermodynamic treatment is necessitated by the recent appearance of new data, based on a combination of combustion and solution calorimetry,' which yields for the heat of formation of low-cristobalite from the elements, the value —209,330 ±250 cal per mol at 25°C. This is about 4000 cal larger than the value previously accepted. The new value for cristobalite is used, together with Kelley's tables of high-temperature heat contents" and entropies and with Korber and Oelsen's' heat of fusion of silicon to obtain the following equation for the standard free energy of cristobalite in the temperature range 1700" to 2000°K: Si (1) + 02 (g) = Si02 (crist.); ?F° = -217,700 + 47.OT [4] The free energy of solution of 0, in liquid iron is:8 O2 (g) = 20 (in Fe); AF° = -55,860 - 1.14T [5] and these two equations are combined to give: Si (1) + 20 = SiO, (crist.); AF° = -161,840 + 48.14T [6] ?F°1873 = -71,700 cal. From the experimental value of K, = 2.8x10-5, Si + 20 = SiO2 (crist.); ?F°1873 = -39,000 cal. [7] The combination of Eqs. 6 and 7 yields the free energy change when liquid silicon dissolves in iron to form the dilute solution of unit activity (1 pct). Si (1) = Si; ?F°1873 = -32,700 cal. [8] The heat effect in this process according to Korber and Oelsen' is an evolution of 28,500 cal per gram

Jan 1, 1954

By D. E. Spiller

Introduction Precious metals recovery from ore can generally be accomplished using gravity concentration, flotation, and/or hydrometallurgical (leaching) techniques. The objective of this paper is to show why gravity concentration can be an important part of recovery systems that employ leaching as the primary unit operation. A brief discussion of modem gravity concentration equipment is also presented. Discussion Gravity concentration of ores has generated increasing interest in recent years. Reasons for this interest include: • Gravity concentration is environmentally attractive. There is little or no use of reagents. Hence, it is relatively nonpolluting. • The cost of cyanide has continued to increase. Therefore, cost savings may be realized whenever leaching feed tonnage can be reduced by preconcentration. • Compared to flotation and leaching, gravity equipment costs are low per processed ton. Field installation costs for gravity circuits usually are less because many' units are supplied as self-contained modules. Also, the cost required to supply services, particularly power, to a gravity plant site are also less. In situations where preconcentration at coarse particle size is applicable, significant grinding equipment savings may be possible. • Gravity circuit operating costs are also relatively low compared to typical flotation and leaching circuits. Reagents, power, maintenance, and manpower savings in a well-engineered gravity plant may be realized. Again, if grinding is reduced, significant power and steel (media and liners) savings are possible. •In recent years, more efficient gravity concentrating devices have been developed. Benefits to Precious Metal Leaching Gravity beneficiation can complement precious metal leaching in two ways. First, the recovery of coarse liberated values before leaching may reduce leach time requirements and may reduce reagent consumption. Second, gravity preconcentration can reduce the size of a leach plant by decreasing the quantity of material to be leached. Coarse gold and silver have been shown to leach rather slowly. Kameda (1949) and Habashi (1967) have investigated the kinetics of cyanide leaching systems. They concur that in a heterogeneous reaction, the rate of gold and silver dissolution is directly proportional to the surface area. Thus, the instantaneous rate of dissolution for spherical 0.37 mm (400 mesh) gold is theoretically -25 times faster than for the same amount of gold at .841 mm (20 mesh), based on data from Fuerstenau, Chander, and Abouzeid (1979). Conversely, coarse liberated, +.841 mm (20 mesh), gold is more readily recovered by gravity concentration than is fine, -.037 mm (400 mesh) gold. Therefore, it is apparent that the two recovery systems complement one another. Figure 1 data demonstrates the potential synergism. A sample of - 3.327 mm (6 mesh) Nevada gold-bearing ore was cyanide leached using conventional bottle-roll test procedures. Gold extraction was determined as a function of leaching time. A second sample split from the same leach feed material was hand jigged to remove a coarse heavy mineral fraction, including virtually all of the +.210 mm (65 mesh) liberated free gold. This second sample, with the coarse gold and heavy minerals removed, was subjected to an identical cyanide leach procedure. Figure 1 presents the resulting comparative extraction data. Note that the percent gold extraction for the sample containing no +.210 mm (65 mesh) free gold includes the coarse gold recovered by gravity. The data show that the sample containing coarse gold required about 72 hours of leaching time to achieve 80% extraction. This compared to about 22 hours of leaching time for 80% gold recovery from the sample that contained only -.210 mm (65 mesh) free gold. Thus, there was a 69% reduction in leaching time. The improved extraction data is not wholly attributable to coarse gold removal, but rather it was the combination of gold removal and rejection of other heavy mineral cyanide consumers or leach retardants. Further investigation was not warranted at this time. Preconcentration is the second manner in which leaching systems can benefit from gravity concentration. The premise is that preconcentration can reduce the quantity of leach feed, which, in turn, may reduce leaching costs. Figure 2 presents preliminary data developed by CSMRI for US Minerals Exploration (USMX). Centennial Exploration Inc., in agreement with USMX, is proceeding with evaluations to determine the suitability of various processing schemes for recovery of gold values from the Montana Tunnels property. The data shows how the ore can be preconcentrated by gravity techniques to result in a reduced feed tonnage to secondary extraction techniques, presumably flotation or cyanide leaching. Testing has shown that Reichert cones, followed by treating the cone concentrate on spirals, can deliver about 88% gold recovery in about 13% weight, that is, 87% weight rejection. Consequently, fine grinding and reagent costs are attributable to only 13% of the plant feed rate. Cost data is not yet available, but the potential exists for significant cost savings.

Jan 1, 1985

By R. B. Crookston

Oil shales differ from coals in that they contain less carbonaceous material, convertible to volatile hydrocarbons, and more inorganic rock. In all pre-commercial oil shale development, involving extensive full scale mining operations, there have been no explosions. However, large scale mine tests with oil shale dusts by the Bureau of fines showed that propagating explosions could be induced under certain circumstances. Laboratory tests were conducted on a broad spectrum of oil shale dusts to define chemical properties and to seek correlations with subsequently determined fire and explosivity properties. These latter properties, indicative of safety hazards, increased as the Fischer assay oil yield of the dusts increased and as particle size decreased. Laboratory data were used to relate fire and explosivity properties of oil shales to those of coals and other carbonaceous materials and to assist in the identification and evaluation of potential hazardous situations which may be encountered in oil shale mining and processing.

Jan 1, 1978

By Donald B. Lindsay

This report presents the findings of an investigation into the characteristics of a number of techniques for cleaning ambient air with special emphasis on their applicability to the removal of the short-lived radioactive decay products of 222-radon, the so-called " radon daughters" that have been identified with the induction of lung cancer in underground uranium miners. The purpose of the study was to review the requirements for control of radon daughter concentrations in mine air, and to examine all techniques whose feasibility has been demonstrated in principle and which in our judgment would be capable of meeting those requirements. The study has included a review of all pertinent literature, both technical and proprietary, on the subject of the control of miner exposure to the radon daughters and in the area of potentially applicable air cleaning technology. Information about the nature of the problem and about the experience of the uranium mining industry in applying air cleaning methods to its solution was obtained by visiting mines where such methods are in use, and by written correspondence and telephone conversations with other industry sources. Information on performance characteristics and costs of applicable air cleaning methods and equipment was obtained from the experience of our own engineering staff and by visits, interviews, and correspondence with manufacturers of industrial air cleaning equipment.

Jan 1, 1978

As part of the United States Department of the Interior, Bureau of Mines Health and Safety Research Program, Walter C. McCrone Associates, Incorporated has examined 71 samples of airborne mine dusts using the techniques of x-ray diffraction, electron microprobe analysis and light microscopy. This report details the procedures which were used in this work and documents the results which were obtained.

Jan 1, 2011

By FREDERICK H. WILLCOX

In the past the blast-furnace industry was under the stigma of being one of the most prolific sources of killed or seriously inj ured and permanently disabled workmen of any of the industries of the country. In the popular mind, labor at blast furnaces was little less hazardous than mining, powder making, or railroad work. This impression wasbased not so much on definite knowledge of the number actnally injured and the causes of injury as on the spectacular nature of the accidents that from time to time were described in the press. As with a mine disaster or a railroad wreck so with many furnace accidents, the number fatally injured in such accidents constitutes only a minor proportion of the workmen who suffer more or less serious injuries. However, the reader of the daily paper receives a distinct impression-of frightful and sudden disaster which is apt to be associated henceforth in his mind with work at blast furnaces. It is true that in the past this impression has not been without warrant, for from the time of the advent of Mesabi ores, taller furnaces, and faster smelting, which begain in the early nineties, the newspapers have chronicled a large number of blastfurnace disasters. Blast-furnace men have never assumed to tolerate failures in construction or defective control of furnaces. But the admitted hazards of the work are many, and the slow development of improvements in the construction and control of the furnace and its auxiliaries have occasionally given rise to a tendency to accept as a part of the day's work not only the unforeseen and difficultly controlled accidents but accidents whose recurrence might be stopped by the adoption of suitable preventive measures. In the smelting of iron, even more than in many other industries, safety is inseparably related to efficiency in production, and. the accidents strictly incident to work about the furnace are proportional in some degree to the success with which obstacles to smooth working are overcome. This relation does not hold, however, in regard .to such accidents as are incident to hand labor, falls, falling and flying objects, machinery, and the use of hand tools.

Jan 1, 1917

By E. G. King

An earlier Bureau of Mines report4 provided low-temperature heat-capacity and entropy data for three sodium vanadates. This report continues the study of vanadates by presenting analogous data for three crystalline calcium vanadates - calcium metavanadate (CaV206), calcium pyrovanadate (Ca2V2O7), and calcium orthovanadate (Ca3V208). No similar data for these compounds have been published previously. MATERIALS All three vanadate samples were prepared by the Bureau of Mines by heating stoichiometric mixtures of reagent-grade calcium carbonate and vanadium pentoxide.5 Calcium metavanadate was prepared at 610° to 660° C. A stoichiometric mixture was heated for 17 days with intervening grindings, mixings, and adjustments of composition, as shown necessary by chemical analysis. The final analysis gave calcium oxide, 23.48 pct. (theoretical, 23.57 pct.) and vanadium pentoxide, 76.32 pct. (theoretical, 76.43 pct.). The sample also contained 0.11 pct. acid-insoluble matter. The X-ray diffracton pattern showed no lines of free calcium or vanadium oxides. No X-ray diffraction patterns were found in the literature for any of these substances.

Jan 1, 1961

By D. R. Irving

Prior to this time, ample supplies of high grade mineral fillers, such as clay, have been available close to consuming centers. Now depletion of these accessible deposits, coupled with other factors such as increasing demand due to population expansion and standard of living rise, has made development of upgrading techniques attractive to producers. Various investigations being carried out by the U.S. Bureau of Mines are described. Factors making the development of improved methods for upgrading clays attractive to producers include: depletion of accessible deposits of high-grade clays, rising transportation and labor costs, more exacting specifications, and increased demand resulting from an expanding population and a constantly rising standard of living. Industry recognizes the need for upgrading presently unusable materials and has cooperated with the U.S. Bureau of Mines by providing samples from submarginal deposits and by evaluating the products that USBM upgrades. Following are some examples of recent clay beneficiation work by the Bureau. FIRE CLAY BENEFICIATION At the Rolla Metallurgical Center, Rolla, Mo., the Bureau is conducting research to develop technically and economically feasible mineral-dressing methods to remove quartz, pyrite, and other impurities from submarginal fire clays. The research has been spurred by the growing shortage of high-grade bur-ley, flint, and plastic clays in the Missouri fire-clay district resulting from increased consumption and the low rate of discovery of new deposits of adequate quality. There apparently is ample tonnage of submarginal flint and plastic clays to maintain the industry for many years if such material can be upgraded to commercial quality. Samples have been submitted to USBM by several major producers of refractories, including A. P. Green Fire Brick Co.; Harbison-Walker Refractories Co.; Mexico Refractories Div., Kaiser Aluminum and Chemical Corp.; and Wellsville Fire Brick Co. Research on some samples has been completed and still is in progress on others. The Bureau has found that specimens containing quartz or pyrite in grains coarser than the accompanying clay generally can be upgraded either with a gravity table or hydraulic cyclone. The improvement in quality is notable not only in chemical analysis but in an increase in pyrometric cone equivalent (PCE) of one or more cones. As an example, consider the results attained on a sandy flint—a fine-grained mixture of kaolin and halloysite with quartz and minor quantities of iron and manganese oxides. Chemical analysis was: 35.4 pct alumina (A12O3) and 47.8 pct silica (SiO2). The sample contained 9.2 pct free silica as quartz. The PCE was 33. The sample was crushed to -10-mesh, blunged with water, and then stage-ground to -48-mesh. The ground sample was tabled to yield a clay fraction containing 37.6 pct A12O3, and 45.3 pct SiO2 of which 2.4 pct was free silica. The PCE was 34. Recovery of alumina by this process was 73.6 pct. Concentration of the same clay in the hydraulic cyclone was even more effective in respect to quartz removal. The clay fraction analyzed 38.6 pct A12O3, 45.0 pct SiO2 of which 0.5 pct was free silica as quartz, and had a PCE of 34. Recovery of alumina was 71.9 pct. The hydraulic cyclone was also effective in reducing the pyrite content of a plastic clay which likewise was a mixture of kaolin and halloysite, plus some pyrite, quartz, and carbonaceous material. It analyzed 30.6 pct Al2O3, 52.3 pct SiO2, 2.3 pct Fe2O3, and 0.76 pct S. The sample was blunged and screened through 10-mesh to remove some coarse pyrite, then ground to -65-mesh and cycloned to remove most of the remainder. The final product recovered 81.8 pct of the alumina at a grade of 32.3 pct A12O3, 50.9 pct SiO2, 1.4 pct Fe2O3, and 0.1 pct S. The PCE was 32-1/2, compared with a PCE of 31-1/2 for the crude clay. The fine beneficiated clays, of course, must be pelletized and dried or fired to meet commercial acceptance. This operation has already been solved by industry. Little progress has been made on two remaining problems. One is that of fine-grained impurities, not separable by table or cyclone. Flotation is being investigated to solve this. Although fine pyrite is readily rejected, a satisfactory quartz-clay separation has not been attained. The second problem, a stubborn one, is that of alkali. Samples containing as much as 5 pct potas-

Jan 1, 1961

By G. V. Jere, C. C. Patel

Chlorination of the various constituents of ilmenite by different chlorinating agents in presence of various reducing agents, have been considered on the basis of the standard free energy and standard enthalpy changes as a function of temperature. The standard free energy change considerations show that it is beneficial to chlorinate ilmenite by chlorine in the presence of carbon and also that iron constituent of ilmenite can be preferentially chlorinated by clzlorine, titanium tetrachloride or their mixture. These findilzgs have been corroborated from the published work. METALLURGICAL processes involving the use of titanium tetrachloride have gained in importance because of the use of the latter in the manufacture of titanium metal. Since ilmenite is more abundant in nature than any other titanium mineral, the future of the metallurgical processes depends on the utilization of ilmenite for the production of titanium tetrachloride. In these laboratories, investigations have been carried out on the chlorination of ilmenite under a variety of conditions.1'2 During these studies, it was noticed that 1) preferential chlorination of iron was effected at low temperatures (400° to 600°C) and at low carbon content (6 to 7 pct), 2) carbonyl chloride retarded the chlorination of iron oxides and titania perceptibly, while 3) carbon-tetrachloride, compounds of sulphur and some other catalysts favored the chlorination. Moles3 has found that oxides of iron are chlorinated in preference to titania at high temperatures, while wilcox4 has claimed the preferential chlorination of titania between 1200" and 1500°C. It has been shown in this paper that preferential chlorination of titania claimed by Wilcox is not likely to occur. Daubenspeck and coworkers5,6 have claimed the preferential chlorination of iron by chlorine or by a mixture of titanium tetrachloride and chlorine between 700° and 1050°C in the absence of carbon. Even when plain titanium tetrachloride is employed as the chlorinating agent, pascaud7 noticed the preferential chlorination of iron and other oxides. The purpose of this paper is to explain from thermodynamical considerations, the various chlorination reactions studied so far. ILMENITE CONSTITUENTS AND THEIR CHLORINATION PRODUCTS Although the general composition of the ilmenite mineral is represented as FeTiO,, most of the ilmenites found in nature have variable quantities of TiO2 (44.6 to 64 pct), FeO (4.7 to 36 pct) and Fe2O3 (6.9 to 28 pct).8 The higher content of ferric iron in ilmenites was attributed by Millerg to the presence of arizonite (Fe2O3.3TiO2). But the X-ray studies by Overholt, Vaw, and odd" have shown that arizonite is a mixture of haematite, ilmenite, anatase, and rutile. Except for the anatase, similar views have been advanced by Lynd, Sigurdson, North, and Anderson8 from magnetic, X-ray, and optical and electron microscope studies. The ilmenite ores can, therefore, be assumed to consist of mineral aggregates of ilmenite, rutile and haematite. From the free energy of formation of ilmenite (FeTiO3), it has been shown by Kelley, Todd, and King11 that ilmenite is stable even up to its melting point (1367°C) and would not undergo decomposition into its constituent oxides. Schomate, Naylor, and Boericke12 have found that in the presence of a reducing agent the iron constituent of ilmenite is selectively reduced. The reaction of chlorine with ilmenite in presence of a reducing agent can, therefore, be synonymous with that of the reaction of chlorine with the constituents of ilmenite, viz., TiO2, FeO, and Fe2O3. Most of the reaction products of chlorination of ilmenite in the presence of reducing agents will be in equilibrium with their dissociation products, depending on the temperature. The titanium tetrachloride is, however, quite stable up to 1500°C due to its covalent nature. The equilibrium for the ferric chloride system has been investigated by Kangro and Bernstorff, 13, schafer14 and Kangro and petersen,15 and the results are summarized in Fig. 1, curves a, b, and c respectively. From these results, it is clear that the ferric chloride disociates as follows: 324° to 700°C FeaCl6(g) ?2FeCl2(c) + Cl2(g) [1] 324°to 900°C Fe2Cl6(g) =2 Fe Cl2 Reaction [I] (curve a) occurs in the forward direction to about 6 pct at 400°C but falls off very rapidly with increase in temperature and beyond 600°C, it is practically negligible, perhaps due to the formation of the stable monomer, FeC13(g). As the temperature is further increased, the amount of FeCl,(g) in-

Jan 1, 1961

By W. L. EGY, GEORGES. RICE, L. M. JONES, J. K. CLEMENT

This report has been prepared, not only for the purpose of recording the results of the first series of coal-dust tests conducted in the experimental mine of the Bureau of Mines, but also to place before the mining public a description of the mine and an account of the objects sought in its establishment. Soon after the organization of the technologic branch of the United States Geological Survey, J. A. Holmes, then chief of the branch, concluded that for the solution of various problems relating to the causes and prevention of mine explosions it would be best to carry on large-scale tests in a mine rather than in a surface gallery. The idea of utilizing the underground passage of a mine for making explosion experiments did not at' first meet with general approval among investigators in this country or abroad. Many thought a mine passage was not a proper place in which scientific tests could be conducted, as great difficulty in controlling conditions was expected. However, after all arguments for and against such an investigation had been carefully considered, plans for opening an experimental mine were definitely adopted by the Bureau of Mines in 1910, and an allotment of funds was made to carry out the project. The first endeavor was to find an existing mine suitable for the purpose, but the mines offered by owners were either worked out, were wet, had poor roofs, or presented complications of various kinds, so that it was finally decided to open a mine if a site could be obtained having natural conditions that would fill the various requirements. A most desirable location was found on property of the Pittsburgh Coal Co., near Bruceton, Pa. The president of this company, Mr. W. K. Field, the general manager, Mr. G. W. Schluederberg, and the chief engineer, Mr. E. J. Taylor, rendered every possible service in

Jan 1, 1913

By J. W. Thompson

MEANING OF TERM, The term "minerals" when used in grants or in reservations or instruments of conveyance is not limited to metals or metalliferous deposits, whether contained in veins that have well-defined walls or in beds or deposits that are irregular and are found at or near the surface or otherwise. Byron v. Utah Copper Co., Utah, 178 Pacific 53, p. 58. The term "mineral" in its commercial sense has been defined as any organic substance found in nature having sufficient value sepa- rate from its situs as part of the earth to be mined, quarried, or dug for its own sake or its own specific use. Rockhouse Fork Land Co. v. Raleigh Brick & Tile Co., - W. Va., 97 South- eastern 684, p. 685. CONSTRUCTION AND MEANING. It can not be said that the term "minerals" includes only such substances as are procured by tunnelling and shafting, as much gold is procured by placer mining and rich deposits of manganese and other like ores are found upon the surface of the earth and are some- times obtained without either quarrying or mining. Rockhouse Fork Land Co. v. Raleigh Brick & Tile Co., W. Va. ——, 97 South- eastern 684, p. 685. GRANITE AS MINERAL. It has been determined that granite was included in a grant of minerals. Rockhouse Fork Land Co. v. Raleigh Brick & Tile Co., -W. Va., 97 South eastern 684, p. 685. See Armstrong v. Lake Champlain Granite Co., 147 N. Y. 495, 42 Northeastern 186.

Jan 1, 1919

By A. E. Bibb, F. W. Kunz

A platelet form of zirconium hydride was found in zirconium and ZY-1 wt pct U single crystals containing hydvogen in the range of 50 to 100 ppm. The habit planes for the hydride plateletg in the zirconium crystals were found to be {1012}, {1121}, and (1122) while the habit planes in the ZY-1 wt pct U crystals were {1121), {1123}, and (1.231). With the exception of the {1231} plane, these have been identified as the twin planes in zirconium. The different effect of hydridc on the mechanical puoperlies of zirconium at high and low strain rates has been explained in terms of the defornzation mechanism and the habit planes of the hydride. ZIRCONIUM and zirconium-base alloys are considered for many nuclear reactor applications, where the pick-up of hydrogen is a distinct possibility, if not an unavoidable occurrence. An excellent example of this is the absorption of hydrogen by zirconium and its alloys during aqueous corrosion, where as much as 30 pct of the hydrogen produced by the corrosion reaction is picked up by the metal. Under the proper conditions, the absorbed hydrogen would precipitate as zirconium hydride and consequently alter the mechanical and physical properties of the zirconium-base alloys. The knowledge obtained from a study of the crystallographic aspects of the hydride precipitation is necessary for the interpretation of the observed changes in the mechanical and physical properties. The deleterious effect of hydrogen on zirconium-base materials is not always observed in normal slow tensile loadings at or above room temperature, but becomes immediately obvious under impact loading, where the energy absorbed decreases with increasing hydrogen content,' and in notched specimens where triaxial loadings are attained.2 This effect is of serious consequence in the applications of Zr where shock loads or high strain rates are experienced. The purpose of this investigation was to determine the crystallographic planes of the Zr and Zr-1 wt pct U matrices upon which zirconium hydride will precipitate and to correlate these with the observed mechanical property data. PROCEDURE Crystal Growth—Single crystals of Zr and Zr-1 wt pct U alloy were used in this investigation. The Zr crystals were made from sponge that had a typical analysis as shown in Table I. Large grains were grown in this material by rapid cooling an arc-melted charge in a button furnace. This operation undoubtedly lowered the volatile impurity concentration below those listed in Table I. Back-reflection Laue patterns of these large grains showed the presence of considerable substructure and lattice distortion within each grain. It was found that an 18-day anneal in an argon atmosphere at 840°C (a high a heat-treatment) followed by furnace cooling, resulted in the further growth of the large grains and removed the detectable substructure ana lattice distortion. Equiaxed crystals with a cube edge of approximately 1/4 in. were produced in this manner. Large crystals of Zircaloy-2 (1.5 wt pct Sn, 0.15 wt pct Fe, 0.1 wt pct Cr, 0.05 wt pct Ni) also were produced by this technique but the large amount of substructure formed could not be removed by annealing. The Zr-1 wt pct U solid solution crystals were produced from an alloy rod consisting of Westing-house-Foote hafnium-free crystal bar zirconium and depleted uranium. The chemical analysis of the alloy is also given in Table I. Three-inch sections were cut from an 0.120-in.-diameter alloy rod and tapered to a fine point on each end. The samples were sealed in evacuated Vycor tubes, homogenized for 5 hr at 1000°C in the ß-phase field, and slowly lowered in a gradient furnace into the a phase (800°C), annealed for 60 hr at this temperature to produce grain growth and furnace cooled. This technique produced large grains approximately 1/2 to 3/4 in. long over the entire cross section of the rod, which were free of observable substructure. Metallographic examination up to X1000 did not show the existence of any second phase in these grains. Crystal Orientation—All crystals were abraded on fine emery paper to produce two flat surfaces 90 deg to each other. The crystals were analyzed by the standard Back-Reflection Laue technique to obtain the crystal orientation with respect to the abraded surfaces. The Back-Reflection Laue Photograms of all crystals used were clear and sharp indicating that the crystals were free from any substructure that could be detected by these means. Hydriding—Only samples containing four to five grains were used for hydriding. Samples that exhibited fine grained patches were discarded. The samples were hydrided using the following technique. After etching in 48 vol. pct HNO3, 48 vol. pct H2O, and 4 vol. pct HF (48 pct) solution, the specimens

Jan 1, 1961

By B. Cousins

Copper, nickel, zinc and other ?penalty? metals are found with gold together in nature, and have a similar chemical affinity for cyanide used in leaching operations4. As a result, solutions that come from the heap leach pads contain a significant concentration of penalty metals along with the desired gold. In solution, gold and cyanide form the complex Au(CN)2- that is readily adsorbed onto activated carbon. Penalty metals as individual metal ions also load onto activated carbon and, depending on the concentration of cyanide and the pH of the solution, can form various cyanide complexes. Some of these complexes can also load onto carbon while some are significantly inhibited from loading. Copper, for example, can form the dicyanide complex Cu(CN)2-, the tricyanide complex Cu(CN)32-, and the tetracyanide complex Cu(CN)43-. At a low pH and a low concentration of cyanide, the dicyanide complex predominates. At a higher pH and a higher concentration of cyanide, the tetracyanide complex predominates. Without excess cyanide, however, individual copper ions can remain present. Activated carbon is used in gold extraction because it is highly selective for gold and less so for other metals, such as copper3. However, copper has the ability to adsorb (?load?) onto activated carbon and block the adsorption of gold when it is in the dicyanide form and in a high enough concentration. When copper is in the tetracyanide form, copper loading is significantly inhibited, allowing for the maximum gold recovery. In order to ensure the tetracyanide complex is formed, a combination of both available cyanide and elevated pH must be present. In the South Area of Newmont Mining Corporation?s Gold Quarry mine in Carlin, Nevada, copper and nickel loading becomes a problem when certain acid generating zones of the heap are leached. Copper, nickel, zinc and other penalty metals become leachable and the lower pH uses up more of the cyanide and creates carbon loading conditions for the metals. This decreases the carbon?s ability to extract the gold from solution, decreasing the recovery and increasing the concentration of gold in the barren solution that leaves the carbon columns. In this study, operational data from March through to May of 2007 is presented to show how Newmont developed a quick fix to lower pH and elevated metal concentrations that were causing low gold loadings on activated carbon at their South Area Leach (SAL) heap leach operations. Laboratory tested were also conducted to examine the chemical kinetics of metal loading and the individual effects of increased cyanide concentrations. THEORY Copper I ions form four different complexes with cyanide in solution: the monocyanide species CuCN, the dicyanide species Cu(CN)2-, the tricyanide species Cu(CN)32-, and the tetracyanide species Cu(CN)43-. The species are formed from the following reactions: [Cu)(?+-+ K1 (1) Cu ß2 (2) --+?+23)(3CNCuCNCu ß3 (3) --+?+34)(4CNCuCNCu ß4 (4) ] where K1 equals 1019.50, ß2 equals 1024.03, ß3 equals 1028.65, and ß4 equals 1030.35. Along with these complexing reactions, hydrogen cyanide and water also dissociate in solution, as per the following reactions: [H?+-+ KH (5) OHOHH2?+-+ KW (6)] where KH has a value of 109.24 and KW has a 1014 value2. These six chemical equations compete with each other, with domination of one over the others dependent on the CN- and H+ concentrations. Each complex also has different properties when it comes to its loading behavior on activated carbon. The dicyanide copper complex and the monocyanide copper complex have an affinity for adsorption onto activated carbon that is greater than the affinity of gold cyanide for adsorption. They also have a lower solubility in water, which enhances adsorption. The tricyanide copper complex and the tetracyanide copper complex are water soluble and have an affinity for loading adsorption on activated carbon that is less than the affinity of gold cyanide for loading adsorption1. There are three prime reasons for this phenomenon. First, the extra cyanides mask the metal ion more, which blocks the main adsorption characteristic of the complex. Second, the complexes are also larger, making it harder to physically fit into the active sites on the carbon. This helps make the latter two complexes kinetically inhibited from adsorption, freeing carbon active site to load with gold cyanide complexes. Third, it is also important to consider the expressions of the mass and charge balance. These balances describe all the overall concentration of copper and cyanide in solution, as well as marking overall charges of the ions in solution4. This is important because significantly changing the charge from positive/neutral to more negative is another reason for activated carbon to reject adsorbing the higher cyanide complexes. The speciation of copper and other penalty metal cyanide complexes in solution is dependent on the pH. At lower pH values, increased hydrogen ions (H+) can out-compete metals for cyanide ions. Lower free cyanide in the system leads to the lower cyanide species of copper cyanide predominating, with a noticeable concentration of the free metal, monocyanide and dicyanide species of copper cyanide. At higher pH values, hydrogen ions are significantly reduced, reducing the kinetics of HCN formation. More free cyanide remains in the system, allowing for more complexing. With this higher amount of cyanide in the system, the tetracyanide species of copper cyanide predominates, also with a noticeable concentration of the tricyanide species of copper cyanide. Higher copper concentrations, however, require more

Jan 1, 2009

By D. Turnbull, J. H. Hollomon, J. C. Fisher

Application of the concepts of nu-cleation and growth to the analysis of experimental transformation data has led to valuable descriptions of phase transformations, an outstanding example being the transformation austenite —* pearlite which has been examined with particular care by Mehl and co-workers.&apos;-5 In addition to the pearlite transformation, the proeutectoid fer-rite and proeutectoid carbide transformations are known to proceed by nucleation and growth. Martensite, on the contrary, until recently was thought to form by a mechanism involving neither nucleation nor growth; however, extension of standard nucleation theory6 suggests that martensite, bain-ite, and the other products of austenite decomposition all grow from nuclei in the parent phase. The theory that martensite forms by nucleation and growth is strongly supported by recent experimental work of Kurdjumov and Maksimova.7 The concepts of nucleatioli and growth have been fruitful also in providing a sound basis for quantitative theoretical treatments of the kinetics of phase transformations. For example, Volmer and Weber8 and Becker and Döring9 developed the theory of nucleation from fundamental considerations to a point where excellent agreement was obtained with the results of experiments on the condensation of supercooled vapors. As a result of their analysis, the kinetics of vapor-liquid transformations now can be predicted. It seems probable that application of the theories of nucleation and growth to a quantitative study of austenite decomposition similarly will clarify the nature of the individual transfor: mations involved, and will enable the calculation of austenite transformation kinetics. In the present paper, the theories of nucleation and growth are applied to the austenite ? martensite transformation in steels. The analysis begins with a discussion of nucleation in single component systems. Martensite appears to be coherent with the parent austenite, hence the nucleation theory is modified to include the effects of elastic distortion. Nucleation in the two component iron-carbon system then is discussed, for most steels are primarily alloys of these two elements. Finally, M. temperatures and martensite transformation curves are calculated for each of several alloy steels of varying carbon and chromium content, and are compared with those determined experimentally by Lyman and Troiano10 and Harris and Cohen.11 Nucleation Theory NUCLEATION IN SINGLE COMPONENT SYSTEMS6,12-14 The work required for reversible formation of a region of phase within the parent a phase is expressed conveniently as the sum of two terms: W1 = Aa, the product of the area of the interface and the interfacial free energy, and W2 = VAf, the product of the volume of the region and the free energy increase per unit volume associated with the transformation. The total work is therefore W = Aa + VAf. When a is more stable than ß, Af is positive and W increases without limit as the volume increases. The transformation a ?ß does not occur. It is nevertheless true that small regions of phase ß enjoy temporary existence here and there in the a. The equilibrium number of ß regions of given size is proportional to exp(— W/kT) per unit volume of a, assuring that larger (ß regions occur with diminishing probability. When a is less stable than ß, Af is negative and W passes through a maximum as V increases. Assuming for simplicity that regions of ß are spherical, as is true when the interfacial tension is isotropic and there are no elastic strains, W = 4r2a + (4/3)*r3Af The maximum value of W is W* = 16iro3/3Af2 [1] for regions with radius r* = -2o/Af. [2] For single component condensed systems it has been shown14 that the steady rate of nucleation of 0 per unit volume of untransformed a is nearly proportional to exp[- (W* + Q)/kT] where Q is the activation energy for the unit processes of adding or removing one atom from an embryo or nucleus. If To is the temperature at which a and ß are in equilibrium, the rate of nucleation is a maximum at a temperature 0 < T < To where (W* + Q)/kT is a minimum. P regions smaller than critical size are called embryos; they tend to grow smaller and disappear, only exceptionally growing larger. Regions equal to or larger than critical size are called nuclei. A critical size nucleus may grow indefinitely large or may shrink back to a, either process decreasing the free energy of the region.

Jan 1, 1950

By J. W. Spretnak, D. A. Chatfield, G. W. Powell, J. R. Eifert

In nzost cases, the driving force for a lattice transformation is produced by supercooling below the equilibriunz transformation temperature. The interfnce reaction in isothermally annealed, multiphase diffusion couples may involve a luttice transformation which also requires a driving force. Direct experinzental evidence has been obtained for the existence of the driring force in the form of a supersaturated phase at the aocc)-0@cc) interface in Cu:Cu-12.5 ult pct A1 couples; the super saturation is equivalent to an excess free energy of approximately 3 cal per mol at 905. A tentatiue interpretation of the dynanzic situation a1 the interface based on the free energy-composition diagram is proposed. THE presently accepted theory of diffusion in multiphase couples1 states that there will be a phase layer in the diffusion zone for every region which has three degrees of freedom and which is crossed by the diffusion path in the equilibrium phase diagram. For binary systems, this restriction excludes all but single-phase fields and, for ternary systems, only one- and two-phase fields are included. In addition, Rhines"~ as well as other investigators3 6 have reported that the compositions of the various phases adjacent to the interfaces are, for all practical purposes, the compositions given by the intersections of the diffusion path with the solubility limits of the single-phase fields of the equilibrium phase diagram. Some studies of the rate of thickening of these intermediate diffusion layers indicate that the thickness of the layer changes para-bolically with time, or: where x is the position of the interface relative to an origin xo, t is the diffusion time, and k is a temperature-dependent factor. crank7 shows mathematically that, if the compositions at an interface are independent of time and the motion of the interface is controlled by the diffusion of the elements to and from the interface, then the segments of the concentration penetration curve for a semi-infinite step-function couple will be described by an equation of the form: hence, Eq. [l] follows from Eq. (21 if the interface compositions are fixed and if the motion of the interface is diffusion-controlled. Although the concept of local equilibrium being attained at interfaces has assumed a prominent role in the theory of diffusion in multiphase couples, experimental evidence and theoretical discussions which challenge the general validity of this concept have been reported in the literature. arkeen&apos; has stated that strict obedience to the conditions set by the equilibrium phase diagram cannot be expected in any system in which diffusion is occurring because diffusion takes place only in the presence of an activity gradient. Darken also noted that it is usually assumed that equilibrium is attained locally at the interface although the system as a whole is not at equilibrium, the implication being that the transformation at the interface is rapid in comparison with the rate of supply of the elements by diffusion. ISirkaldy3 indicates agreement with Darken in that he believes the concept of local equilibrium is at best an approximation because the motion of the phase boundary requires that there be a free-energy difference and, hence, a departure from the equilibrium composition at the interface. Seebold and Birks9 have stated that diffusion couples cannot be in true equilibrium, but the results obtained are often in good agreement with the phase diagram. The initial deviation from equilibrium in a diffusion couple will be quite large because alloys of significantly different compositions are usually joined together. Kirkaldy feels that the transition time for the attainment of constant interface compositions (essentially the equilibrium values) will be small, although in some cases finite. Castleman and sieglelo observed such transition times in multiphase A1-Ni couples, but at low annealing temperatures these times were quite long. Similarly, ~asing" found departures, which persisted for more than 20 hr, at phase interfaces in Au-Ni and Fe-Mo diffusion couples. Braun and Powell&apos;s12 measurements of the solubility limits of the intermediate phases in the Au-In system as determined by microprobe analysis of diffusion couples do not agree with the limits reported by Hiscocks and Hume-Rothery13 who used equilibrated samples. Finally, Borovskii and ~archukova&apos;~ have stated that the determination of the solubility limits of phase diagrams using high-resolution micro-analyzer measurements at the interfaces of multiphase couples is not an accurate technique because of deviations from the equilibrium compositions at a moving interface; diffusion couples may be used to map out the phase boundaries in the equilibrium diagram, but the final determination of the solubility iimits should be made with equilibrated samples. The purpose of this work was to investigate the conditions prevailing at an interface in a multiphase diffusion couple and to compare the interface compositions with those associated with true thermodynamic equilibrium between the two phases. Microanalyzer techniques were used to measure interface compositions in two-phase Cu-A1 diffusion couples annealed at 80@, 905", and 1000°C for various times.

Jan 1, 1969

By A. S. Venkatadri, H. B. Bell

The equilibrium sulfur distribution between molten iron and Ca0-Mg0-Al203 slags containing iron oxide was investigated at 1550°C. The results were used to derive the iron oxide activities at low iron oxide concentrations in the slag by combining the sulfide capacity data obtained from gas-slag work with the free energies of both the sulfur solution in iron and the iron oxide formation in slag. The derived ferrous oxide activities were compared with values based on Tem-kin&apos;s kin&apos;s and Flood&apos;s ionic models. One difficulty in using these models is that the nature of the aluminate ion in slag is uncertain. Nevertheless, such indirect methods, in particular, those described in the present paper, are of value because of the difficulty of measuring small amounts of oxygen in liquid iron in equilibrium with slag. It is shown that these methods confirm the consistency of thermodynamics data on liquid iron and slags. It is well established that decreasing the iron oxide activity in the slag increases the desulfurization of molten iron at constant slag basicity. This effect is most pronounced at the very low iron oxide activities, characteristic of blast furnace slags. Yet a precise quantitative determination of the significance of low iron oxide contents in slag in blast furnace desulfuri-zation is not possible for the following reasons: a) difficulty of separation of iron "shots" from the slag, and b) errors in chemical analysis of small amounts of iron oxide in slags. In view of these obstacles, one must resort to indirect methods of calculating iron oxide activities. EXPERIMENTAL TECHNIQUE The apparatus for providing the sulfur equilibrium data has been described previously1 and was similar to that used by ell&apos; in connection with the study of slag-metal manganese equilibrium. The procedure consisted of: a) melting about 50 g of Armco iron in a magnesia crucible in a platinum furnace, b) adding a mixture of about 15 g of lime-alumina slag and varying amounts of Fe2O3 and CaS, and c) maintaining the temperature at 1550°C for more than an hour in an atmosphere of argon to enable the sulfur equilibrium to be attained. Several melts were made using lime-alumina slags with basic composition 55, 50, and 45 pct lime. During the experiment the temperature was controlled manually using a Pt/10 pet Rh-Pt thermocouple. After the experiment, the Power was shut off and the flow rate of argon was increased to freeze the melt as quickly as possible. The analysis of sulfur in the metal was carried out by the oxygen combustion method3 using uniform drillings from the top and bottom of the metal button. After crushing and grinding and removal of any iron particles with the aid of a hand magnet, the slag was analyzed for sulfur by the CO2 combustion method.4 The E.D.T.A. method was employed for the analysis of lime5,6 and magnesia,= the ceric sulfate method7 for the analysis of slag iron oxide, and the perchloric acid dehydration method5 for the analysis of silica. The remaining amount was taken to be Al2O3 precipitation with ammonium hydroxide in several preliminary melts had confirmed the propriety of using this simple procedure. RESULTS The activity of iron oxide in binary, ternary, and more complex slags has been the object of numerous investigations, and the two experimental methods for its determination are: 1) Equilibrating the metal with the slag in question and measuring the oxygen content of the metal. The ferrous oxide activity is then given by aFeO L%OJSat where [%0]sat is the oxygen content of the metal in equilibrium with pure iron oxide slag. This method was used by Chipman et al.8,9 2) Equilibrating the slag in iron crucibles with known partial pressures of H2/H2O or CO/CO2 mix-tures.10-12 This method is limited to temperatures between 1265" and 1500°C. The very low oxygen content of the melts in this investigation made it impossible to derive the ferrous oxide activity by the first of these methods. Therefore, the iron oxide activities were computed by means of: Sulfide capacity data from the gas-slag work" Temkin&apos;s concept14 Flood&apos;s approach15 a FeO from Sulfide Capacity. The method of calculating the aFeO involves the sulfide capacity of the slag (c,), the sulfur distribution coefficient (Ls), the free energy of dissolution of sulfur in iron, and the free energy of formation of iron oxide in the slag. Bell and Kalyanram13 have investigated the sulfur absorption characteristics of lime-alumina slags containing magnesia by the Carter-Macfarlane method16 (based on comparing the sulfide capacity of the slag in question with that of a standard slag of unit lime activity) and have derived lime activity values. The relation between sulfide capacity and their lime activity a&apos;CaO is given by: Cs= 3—: Xa&apos;CaO at 1500°C

Jan 1, 1970