Search Documents

By A-A. Bogno, M. Rappaz, J. Valloton, H. Henein

"Rapid solidification of Al-Cu droplets of eutectic composition was carried out using Impulse Atomization in an argon atmosphere, to study the microstructures forming at different cooling rates and undercoolings. Two distinct morphologies were observed within the investigated Al-33wt%Cu droplets microstructures: (i) A regular lamellar morphology and (ii) an undulated morphology. The volume fraction of each type of morphology was measured as a function of the droplet size and the nucleation undercooling was deduced using the hypercooling limit equation. The scale of the microstructures was determined through measurements of inter-lamellar spacing across and along the growth direction. Growth velocity and undercooling were deduced using Jackson and Hunt (1966) eutectic growth theory. Finally, mechanical properties were estimated through micro-hardness analysis using a Vickers hardness tester, revealing exceptional properties for an aluminum-copper alloy. Indeed, the hardness values, increasing with growth rate and undercooling, were 3 times higher than the values obtained in hypo-eutectic Al-Cu alloys.INTRODUCTION Eutectic alloys are very attractive due to their good fluidity allowing ready shaping of parts in casting processes as well as in thermal spray deposition. In addition, they yield microstructures with high mechanical properties, by the virtue of their scale/size which is defined by the solidification parameters and the thermodynamic and thermophysical properties of the given alloy. Therefore, it is important to understand the relationship between the microstructures and the solidification parameters of eutectic alloys in order to control their solidification path and mechanical properties. The latter could be improved by either adding an appropriate strengthening component to a base eutectic material (Böyük, MaraslI, Kaya, ÇadIrlI, & Keslioglu, 2009) or by refining the microstructures for more effective dislocation pinning (Campbell & Campbell, 2003). Tailoring the microstructure can also be beneficial to chemical (Freitas, Osório, Spinelli, & Garcia, 2014; Osório, Freire, Caram, & Garcia, 2012) or electrical (Kaya, 2012) properties of the material. Eutectic-type microstructures, usually formed from liquid (eutectic transformation) or solid (eutectoid transformation), are made up of two or more different phases, generally of lamellar or fibrous (rod like) morphologies (Kurz & Fisher, 1998). In general, a binary eutectic structure can be regular (when both phases are non-faceted) or irregular (one of the two phases is faceted), the two solid phases having roughly the composition of the liquid from which they are formed."

Jan 1, 2017

Of the many organic impurities present in Bayer liquor, sodium oxalate is known to have one of the most detrimental effects on the Bayer process. Because of its limited solubility, it will co-precipitate with gibbsite during the precipitation stage which results in many operational challenges for the refinery. Despite the importance of this phenomenon, the interaction mechanism between gibbsite and sodium oxalate is not well understood. In this study, the growth of sodium oxalate on three main morphologies (random agglomerates, prims and hexagons) of water-washed and caustic-washed gibbsite was observed under synthetic Bayer conditions using in situ optical microscopy. After a short induction period, oxalate started to nucleate on gibbsite crystals, and grew with a needle-shaped morphology which eventually developed into oxalate bundles. In addition, the results indicated that caustic washing was able to partly decompose gibbsite crystals and thus make the gibbsite surface rougher, which provides more potential sites for oxalate nucleation and growth. The growth rate of oxalate crystals on the basal (001) face of water-washed gibbsite was 1.33 µm/min determined by the time-lapse imaging of in situ optical microscope.

Jan 1, 2014

By W. E. Kuhn

Introduction The work, of which some of the results are described in this paper, was started with the object of investigating the properties of certain binary alloys of titanium made from powders. Our main interest was in the possible use of such alloys in gas turbines. We were attracted to titanium, as have been others, by its high melting point (I,724° ± 11°C.), its low density (4.54), and the likelihood that, if a relatively wide use could be found for the metal, it might become available in commercial quantities at a fairly reasonable price. The readiness with which the metal reacts with hydrogen, oxygen, and nitrogen was recognized from the very beginning. At the same time there seemed a good chance that alloys could be produced which, because of the formation of protective films, would resist the attack of these and other corrosive agents. No specifications were drafted to cover the 'quality' of the titanium hydride powder which was used in our work and which was, to judge by the results of a few preliminary experiments, the most useful source of titanium then (1944) available in sufficient amount for our purpose. During the course of our work, the need for such specifications became very clear (see Sections 9 to 12 of this pa per). Even today, lack of knowledge regarding the effects on titanium of impurities, some of which may later be looked upon as essential elements in commercial alloys of titanium, and difficulties in manufacture, make the preparation of specifications for commercial titanium and titanium compounds a doubtful procedure. The papers presented at the 1948 Symposium on Titanium, sponsored by the U.S. Office of Naval Research lend colour to this view. At the time our work was commenced, one had to depend upon the manufacturer to supply what he considered to be his 'best' material. It may be some time before we can ask for more than this, the question as to what is his 'best' being left to the manufacturer to decide. However, in this connection the results of our study may be of some value and on that account we are constrained to publish them.

Jan 1, 1950

By Gordon A. Irons, Diancai Guo

"Uneven movement of scrap during melting in an Electric Arc Furnace causes operation problems: cave-ins interrupt electric power input. The movement also influences the radiation heat loss to water-cooled side panels and roof. An apparatus has been built to simulate the flow of scrap that may be interlocked. It has been observed that flow starts at the point where the suspended length of the pile bottom reaches the average scrap size, and proceeds in the form of cave-ins, but scrap pieces slide with each other as ordinary granules. After a cave-in, the pile angle usually remains much larger than the normally observed angle of repose. The force balance of a partially suspended scrap pile has been analyzed, and the equivalent cohesion due to interlocking estimated. A numerical model has been developed to simulate the scrap flow. Simulated results agree reasonably with observed phenomena.IntroductionWhen one considers the melting of steel scrap in an electric arc furnace (EAF), it is helpful to understand the movement of the material during meltdown. As industrial experience demonstrates, scrap movement greatly affects EAF operation. In a typical operation, scrap is dropped into the furnace from scrap buckets. The roof and electrodes are swung into position, and power is applied to the electrodes situated over the scrap. The electrodes ""bore"" into the scrap by melting into the steel in the immediate vicinity of the electrodes as they are lowered. If solid scrap pieces gradually slide towards the arc area, the electric power supply can be maintained at a high level, with few interruptions or drastic electrode adjustments. This results in a high production rate and low power consumption per tonne of steel produced. On the other hand, if the charge moves down unevenly, i.e. in large surges, usually called cave-ins, the electrodes must be drastically raised, and power supply frequently interrupted. This is also accompanied by a high level of harmonics induced in the power network, deteriorating the quality of electricity supplied to other users.In addition, the movement of scrap in an EAF also influences the furnace heat efficiency, as the scrap pile is much closer to the electric arcs compared to the furnace wall and roof, and absorbs more radiated heat. Early exposure of the wall and roof to the arcs will increase the heat loss due to radiation, and reduce the service life of the furnace."

Jan 1, 2004

By M. Mentser

The exchange of oxygen between carbon dioxide and carbon monoxide that occurs reversibly on carbon surfaces was studied at temperatures of 750° to 850°C and a pressure of 1 atmosphere. Carbon-14 was used to detect and measure the exchange reaction. The extent of oxygen exchange was a linear function of com- position of the gas mixture, and this relationship was used to evaluate the forward and backward rate constants of the reaction. Equilibrium constants, directly determined for oxygen exchange in this study, agreed well with values in the literature that were derived only by indirect procedures. This result establishes the validity of oxygen exchange in the mechanism of carbon gasification by CO2. Rates of carbon gasification were less than an order of magnitude slower than rates of oxygen exchange. Activation energies for these two processes were 58 and 53 kcal/mole, respectively. The closeness in the activation energies argues against any change in the rate-controlling step over a wide temperature span at atmospheric pressure. The role of CO as a retardant on the CO2-C reaction, and the nature of the carbon-oxygen complex are also discussed in view of the data obtained.

Jan 1, 1973

By W. E. Keck

THERE is a considerable tonnage of iron ore in the Menominee Range Michigan that is unsalable only because it has too large a content of sulphur. Beneficiation of such ore is economically desirable, as a rela-tively large quantity of finished concentrate would be obtained (deleteri-ous sulphur mineral content being generally less than 5 per cent) and because large blocks of such ore have been developed incidentally during search for low-sulphur ore. Research on the flotation beneficiation of these high-sulphur ores consisted of: (1) a study of the flotative properties of the principal min-erals in a nearly puree state, (2) flotation of synthetic mixtures of these pure minerals and (3) application of this experimental information to samples of the ores. Gypsum in iron ores is extremely deleterious; but when sufficiently free from impurities it is a valuable commodity. In 1934, the United States produced 1,500,000 tons of calcined and uncalcined gypsum valued at $13,700,000'. Of this quantity and value, Michigan produced approxi-mately 19 per cent4. Thus this investigation may also prove to be of interest in connection with the gypsum industry if minerals separation, such as flotation, becomes necessary in the future processing of gypsum. Data on the flotative properties of gypsum would also be of interest to the science of flotation because such information has been extremely limited. The technical literature reveals one reference to the flotation of gypsum, in which was discussed the use of the mineral, with several others, to determine the relation between the floatability of minerals and the pH of the flotation solution2. This investigation necessarily was not comprehensive in regard to gypsum, but it did show that the mineral could be floated with oleic acid under varying pH conditions.

Jan 1, 1937

By W. E. Keck, Paul Jasberg

THERE is a considerable tonnage of iron ore in the Menominee Range of Michigan that is unsalable only because it has too large a content of sulphur. Beneficiation of such ore is economically desirable, as a relatively large quantity of finished concentrate would be obtained (deleterious sulphur mineral content being generally less than 5 per cent) and because large blocks of such ore have been developed incidentally during search for low-sulphur ore. Research on the flotation beiieficiation of these high-sulphur ores consisted of: (1) a study of the flotative properties of the principal minerals in a nearly pure state, (2) flotation of synthetic mixtures of these pure minerals and (3) application of this experimental information to samples of the ores. Gypsum in iron ores is extremely deleterious; but when sufficiently free from impurities it is a valuable commodity. In 1934, the United States produced 1,500,000 tons of calcined and uncalcined gypsum valued at $13,700,0001. Of this quantity and value, Michigan produced approximately 19 per cent4. Thus this investigation may also prove to be of interest in connection with the gypsum industry if minerals separation, such as flotation, becomes necessary in the future processing of gypsum. Data on the flotative properties of gypsum would also be of interest to the science of flotation because such information has been extremely limited. The technical literature reveals one reference to the flotation of gypsum, in which was discussed the use of the mineral, with several others, to determine the relation between the floatability of minerals and the pH of the flotation solution2. This investigation necessarily was not comprehensive in regard to gypsum, but it did show that the mineral could be floated with oleic acid under varying pH conditions.

Jan 1, 1937

By Frances Hurd

WHEN 60:40 brass is heated to 825° C., given a drastic quench to obtain the beta solid solution, and reheated, various changes take place in the structure. Reheating at 200' C. causes a fine, granular, sorbitic structure to appear which has been considered alpha solid solution. These particles coalesce at higher temperatures of reheating, and at 470° C., the alpha forms twins. A further study of these transformations was considered worth investigating.

Jan 1, 1927

By Fulian He, Jianhang Chen, Shoubao Zhang

"Fully grouted rock bolts have been used in mining industry for many years. Significant research has been conducted to evaluate the load transfer behavior of fully grouted rock bolts with experimental programs. However, compared with that, less work has been conducted with analytical modelling. Therefore, in this paper, the authors used an analytical model to study the load transfer behavior of fully grouted rock bolts. To confirm the credibility of this analytical model, an in-situ pull-out test was used to validate this model. There was a close match between the experimental result and the analytical result. Following this, a parametric study was conducted with this analytical model. The influence of coefficients, Young’s modulus of the rock bolt and the diameter of the rock bolt on the load transfer performance of rock bolts were studied. Furthermore, the load distribution along the fully grouted rock bolt was analytically studied. The results show that the axial load in the rock bolt decayed from the loaded end to the free end independent of the pull-out load. However, the trend of the load distribution curve was influenced by the pull-out load. This paper was beneficial to better understand the load transfer mechanism of fully grouted rock bolts.INTRODUCTIONRock bolts have been used in the mining industry for a long time. They are used as the reinforcement tendons to keep the stability of openings in underground mining and the slope in open-pit mining. Furthermore, rock bolts are commonly used not only in the mining engineering, but also in civil engineering (Thompson, Villaescusa, and Windsor, 2012).The rock bolt is a tendon which can be a rod or a cable inserted into a borehole drilled in rock masses or soils. Traditionally, the material of rock bolts was steel. However, engineering practices showed that the steel rock bolts can be easily corroded by the moist environment in underground mines. Next, Fiber Reinforced Polymer (FRP) was used to manufacture rock bolts, which are termed as FRP rock bolts. Experimental results proved that the FRP rock bolts can effectively reinforce the surrounding rock masses without being corroded (Wang et al., 2018)."

Jan 1, 2019

By T. H. Etsell, P. Kerr, Qi Liu

"The objective of this investigation was to study the reaction mechanisms during the reduction of iron oxides in the presence of calcium chloride and carbon black as a simplified iron segregation process. The gas phase was analyzed by mass spectroscopy and the solid reaction products were analyzed by scanning electron microscopy. Mass spectroscopy, combined with thermogravimetric analysis and differential scanning calorimetry, revealed the presence of several gases at elevated temperatures over time, and the scanning electron microscope in combination with energy dispersive X-ray analysis illustrated the growth of a metallic iron phase on or near the carbon substrate. The results correlated well with similar copper and nickel segregation processes, but also introduced new insights that challenge the simplicity of the current models. The formation and transport of gaseous iron species to the carbon substrate in the presence of steam and hydrogen were evident during the reduction process that was studied; however, there is more happening at a mineralogical level, based on evidence of a liquid phase resulting in substantial growth due to an apparent fluxing effect created by the calcium chloride.These results help to better explain the chemical reactions and, in turn, the thermodynamics and kinetics of iron segregation processes related to the beneficiation of low grade complex iron ores. The results are also applicable to the production of metallic iron and concentrated titanium dioxide from ilmenite ores. The benefit of this process is that it allows ores in which the iron minerals are intimately associated with gangue minerals to be processed in circumstances where conventional mineral processing techniques are unsuitable or incapable of upgrading the material."

Jan 1, 2016

By Jay R. Schafler, Jacob L. Brinkman, Catherine E. Johnson

"The United States coal mining industry is currently experiencing a decline in both demand and commodity price while facing implementation of more stringent air and water pollution regulations. Company profits have decreased significantly, forcing several major companies to declare bankruptcy. The industry was required to adapt to survive. Many of these companies have adjusted by abandoning mines; the last two decades have seen a drastic decrease in the number of mines. To discover the primary causes of this downturn, three major aspects must be studied: properties of abandoned mines, commodity history and regulatory impact. Trends since 1994Each year, U.S. coal mines are required to submit data on a variety of categories to the U.S. Mine Safety and Health Administration (MSHA) and the U.S. Energy Information Administration (EIA). This data include administrative records, production values and information regarding the attributes of the mined material and the mine itself. Each year since 1996, EIA has released a report summarizing the data from two years prior. Additionally, MSHA maintains a database containing a collection of all the most current data. These resources are the primary sources for the figures included in this article. There are several items to note regarding this data:1. The EIA reports from 2016 and 2017 were not released at the time of writing this report.2. The MSHA data set is actively maintained as information is provided. This means the data for 2016 is from June 27, 2016 and data for 2017 is from Aug 24, 2017. All other points represent the end of-year values.3. Each of the figures only includes data pertaining to active mines. EIA defines active mines as both active and temporarily idled mines, and inactive mines as nonproducing and abandoned mines. MSHA separates all four into separate categories, though this paper combines the MSHA values according to the EIA definition for the purpose of comparison."

Jan 10, 2017

By Kihong Park

A hygroscopicity tandem differential mobility analyzer (HTDMA) technique is used to determine size-effect of nanoparticles (NaCl, (NH4)2 SO4, KCl, NH4NO3, MgCl2,CaCl2) on their hygro­scopic properties (deliquescence relative humidity (DRH) and hygroscopic growth factor (GF)). The HTDMA system uses a combination of two nano DMAs and two regular DMAs to measure particle size change in a wide dynamic particle size range. Particles are subsequently analyzed with a transmission electron microscopy to investigate the potential effect of particle structure or morphology on the hygroscopic properties. We found that structural properties of NaCl and (NH4)2SO4 particles also play an important role in determination of the DRH and GF and are more pronounced at smaller diameters. Data show that the DRH of NaCl nanoparticles increased from *75% up to *83% RH at 8 nm and that their GF decreased with decreasing size. The extent to which the GF of NaCl nanoparticles decreased with decreasing size was greater than theoretically predicted with the Kelvin correction. The GF of furnace-generated NaCl nano­particles that have pores and aggregate shape was found to be smaller than that of atomizer-generated particles that are close to perfectly cubic. For the case of atomizer-generated (NH4)2SO4 nanoparticles, we observed no signi?cant size-effect on their DRH, and the measured GF agreed well with predicted values using the Kelvin correction. For furnace-generated (NH4)2SO4 nanoparticles, a gradual growth at moder­ate RH without noticeable deliquescence behavior occurred. Their TEM images showed that contrary to atomizer-generated (NH4)2SO4 nanoparticles the fur­nace-generated (NH4)2SO4 nanoparticles are not perfectly spherical and are often aggregates having pores and holes, which may favor holding residual water even in the dried condition. For atomizer-generated KCl, MgCl2, and CaCl2 nanoparticles, we observed no signi?cant size-effects on their DRH and GF for the mobility size as small as 20 nm.

Jan 1, 2008

By Cem Colakoglu

In this study, nickel containing iron alloys were produced by carbothermal reduction of lateritic nickel ores obtained from Manisa - Caldag region of Turkiye in order to investigate the reaction mechanism of nickel and cobalt. In the experiments, the lateritic ore containing 1.58 wt.% Ni and 0.12 wt.% Co was calcined in a semi-pilot scale rotary furnace at 1100°C for 1 hour. Then, a mixture of calcined ore and metallurgical coke was reacted in sintered alumina crucibles using a graphite resistance tube furnace at different time (0- 60 min) and temperature (1500-1600°C).

Jan 1, 2009

By Ranajit Kumar Sahoo, Shatrughan Soren, Surendra Kumar Biswal, Soumya Sahoo, Sachida Nanda Sahu

The presence of appreciable quantity of clay mineral in Indian hematite ore needs an attrition technique using screw scrubber in the beneficiation circuit to remove the ultrafine clays and avoid downstream operational problems. Spectroscopic analysis revealed that iron ore samples obtained from the Barbil region of Odisha contain a high amount of silica and alumina in the form of clay minerals (e.g., kaolinite) contributed as a loss on ignition (LOI) in the iron-making process. Iron ore fines of below 10 mm size were subjected to a laboratory-scale screw scrubber, and the effectiveness of scrubbing as well as the pelletization of the scrubbed product was investigated. The screw scrubber in the beneficiation circuit helps to remove the clay minerals, causes an increase in iron values from 63.65% Fe(T) to 66.18%Fe(T), with improved physical (CCS of 325 kg/pellet) and metallurgical (RDI of 2.24%) pellet properties.

Aug 31, 2020

By Saeid Pournaderi, Ahmet Geveci, Ender Keskinkilic, Yavuz A. Topkaya

There are mainly three commercial nickel laterites in Turkey: Gordes, Caldag and Sivrihisar. The first two appear in Western Anatolia. The third one, Sivrihisar (Yunusemre) laterites have been found in the first decade of the millennium, in the Central Anatolia region of Turkey. Since then, mining facilities have been continued in Yunusemre. Calcination, prereduction and smelting of Sivrihisar laterites have been extensively studied and published. In the current work, some results of the studies related to characterization of Sivrihisar laterites will be presented.

Jan 1, 2016

By S. P. Narayan

The hot deformation behavior of Pure Mg and Mg-0.29Ce alloy were studied by isothermal hot compression tests in the temperature range of 250 - 500°C and strain rate range of 10-3 - 102 s-1 in a computer-controlled 50kN servo hydraulic universal testing machine (UTM). The results show that the flow stress of Mg pure and Mg-0.29Ce alloy increases with strain rate and decreases after a peak value, indicating dynamic recovery and recrystallization. Process efficiency was increased by nearly 10 to 12% by addition of Ce in Mg. Mg pure exhibits instability zones between 250-275°C at 10 ? 102 s-1 and 400¬500°C at 101 ? 102 s-1 temperatures and strain rates respectively, rest is the safe deformation zone. Wherein, Mg-0.29 Ce exhibits two low efficiency zones from 250 ? 300°C at 10-2? 10° s-1, 400 ? 500°C at 101 ? 102s-1 and high efficiency zone at 450 ? 500°C at 10-3? 10-1s-1. 4D process maps were generated for the above said alloys which illustrate contours of power dissipation and instability in the 3D space of strain rate, temperature and strain.

Jan 1, 2011

By K. Szafran, R. E. L. Seal, M. Tansey

Conversion of hydraulic equipment to fire resistant fluids has been hampered by less than satisfactory component performance and in some cases, catastrophic equipment failure. Concern over identifying possible causes to these problems led to a joint research project between the Potash Corporation of Saskatchewan Mining Limited and the University of Saskatchewan. This paper summarizes some of the results and conclusions derived from this joint project. In this study, the research was limited to evaluating the effects of potash contamination on the performance of hydraulic equipment. Two separate types of tests were conducted in order to provide a basis upon which trends could be established. This study concluded that the presence of potash dust in the hydraulic fluid can induce severe wear over relatively short periods of time. It was also deduced that a contaminant free fluid combined with proper fluid maintenance could extend the performance of hydraulic components using fire resistant fluids even under very severe operating conditions, such as elevated pressures and temperatures. Recommendations as to how to achieve this goal and the practicality of doing so are presented.

Jan 1, 1988

Thermodynamics and kinetics? of the removal of Va elements (As,Sb,Bi) from copper were investigated 1n the fire relining by alkaline carbonate fluxes such as Li 2co3 , Na 2CO3 and K2CO3. The distribution coefficients of As, Sb and Bl between alkaline carbonate fluxes and mo) ten copper were ?obtained at 1200°C under the different oxygen potentials. As and Sb were easily removed from copper to fluxes as pentavalent oxide form. On the other hand, Bi was hardly removed except by a Ll2CO3 flux. The removal rates of Va elements from copper were also measured In the temperature range of 1150°C.- 1250°C. The removal rates of As and Sb were much higher than that of Bi. The removal rates of Va elements showed the same order of the distribution coefficients. The removal rate could be expressed by following equation. (1).

Jan 1, 1987

By Payman Roonasi

Having knowledge of mechanism of magnetite formation is essential in a number of industrial processes including magnetite synthesis and corrosion of iron. In this study, magnetite nanoparticle was synthesized via two different ways; coprecipitation of iron (II) and (III) and oxidation of ferrous hydroxide. The samples were characterized using X-ray diffraction (XRD), Mid-Far IR spectroscopy, scanning electron microscopy (SEM), chemical analysis for determination of Fe II/Fe III ratio and ICP-MS for iron isotopic ratio (56Fe/54Fe) measurement. Since fractionation of iron isotopes depends on reaction rate and bonding strength, interpretation of the isotopic data with respect to the possible mechanisms is discussed. No fractionation of iron isotopes was observed for the magnetite synthesized by coprecipitation, whilst magnetite formed from ferrous hydroxide showed higher abundance of 54Fe compared to 56Fe in the beginning of reaction, implying the significance of the following reaction:

Jan 1, 2009

By Hongshuang Di, Tianyu Zhang, Huiqiang Huang

A CMnSiAl transformation induced plasticity (TRIP) steel was used to study the effect of retained austenite on room-temperature mechanical properties. The steel plates with retained austenite were obtained by hot rolling, cold rolling and subsequent continuous annealing. The starting and finishing temperature of hot rolling are between Ac1 and Ac3. Reduction ratio of cold rolling is 75%. The continuous annealing is carried out at different intercritical temperatures. The relationship between work hardening exponent and retained austenite was discussed. The results show that, the Ac1 and Ac3 were much high because of the alloy elements, and the temperature range between them was wide. Due to the high hot rolling temperature, the grains was hereditarily refined as a result of dynamic recrystallization. Annealing at intercritical temperature of 930 ºC, retained austenite with relatively high stability reached a maximum volume fraction of 25%, a maximum total elongation of 30.2% and a best ultimate tensile strength × total elongation of 20.1 GPa·%. Instantaneous work hardening exponent reflects strengthening mechanisms at different strain stages. The TRIP effect of retained austenite is the main mechanism during deformation. With retained austenite of sufficient amount and high stability, continuous work hardening was observed in the tensile specimen of 930 ºC.

Oct 1, 2019