"This presentation will cover the physical properties of waste heat recovery. It is a two part presentation. The first deals with actually recovering the heat with new state of the art heat exchangers and applying that heat to the furnace combustion and the second part will cover what other processes you can enhance with this ""free"" heat. It will also talk about converting it to steam, hot air or electricity to be used or sold back to the utility company. The economics of various schemes will be reviewed. A brief discussion on State and Federal grants and subsidies will be presented.IntroductionThere are large quantities of wasted heat in the usual aluminum melting process. And, there are several techniques for reducing and/or using some of that wasted heat as you have seen. Any technique that can make use of wasted heat is a form of recovery. This can range from simply preheating aluminum billets prior to melting, to more complicated processes like air-to-air heat exchangers using the boiling and condensing characteristics of special fluids in “heat pipes.” The objective of this type energy recovery process is to move the wasted heat from the hot and dirty exhaust gas stream into some useful process.Waste Heat Recovery in the Aluminum Melting Furnace.There are considerations, of course:1) What might the value be of the recovered energy?2) Can the recovered energy be used within the process? Within the plant? Or by theneighbors?3) What is the capital cost?4) Is the recovery process complicated?5) Will it take additional staff?6) Will it cause additional downtime on the melting line?7) Will the operations staff need to be licensed?Ideally, the process will be simple and inexpensive, the recovered energy will be very valuable, and the whole effort will cause little distraction to the aluminum melting process itself. These would be ideal."

Jan 1, 2011

By J. P. Downey, T. Salisbury, M. Berlin, E. Rosenberg, G. Pinson, R. Christianson, K. Gleason, W. Gleason, S. Davis

"The Center for Advanced Mineral and Metallurgical Processing is developing membrane production technology based on autocatalytic reduction of palladium from solution onto a unique, porous substrate. Surface membranes and catalytic structures are critically important to applications that range from hydrogen purification membranes to petroleum refining. Autocatalytic reduction processes represent a cost effective method of producing stable surface layered structures that have good working lives. These attributes are particularly important in the production of palladium alloy purification membranes used in hydrogen production. Although considerable research has investigated the interaction of hydrogen and palladium alloys, the mechanisms in play while the membranes form are not well understood. Preliminary research has identified three distinct deposition mechanisms and it appears that substantial control over the resulting membrane is possible.IntroductionPalladium-based membranes separate hydrogen from other gases because hydrogen is uniquely soluble in and readily passes through bulk palladium. As currently produced, palladium-based membranes are expensive and have short service lives. These circumstances are due in part to the lack of a complete understanding of palladium or palladium alloy deposition. The Center for Advanced Mineral and Metallurgical Processes (CAMP), in collaboration with the Metallurgical and Materials Engineering Department at Montana Tech and the Chemistry Department at the University of Montana, is engaged in the development of new methods and materials for hydrogen purification membrane production.In membrane production, the palladium requirement depends on substrate surface properties such as surface chemistry, porosity, and roughness. Thin, defect-free membranes have been successfully produced on substrates of porous glass, alumina, and stainless steel. However, the differences in the thermal expansion coefficients of palladium membranes and porous glass or alumina substrates cause problems at operating temperatures. The use of stainless steel substrates is advantageous because stainless steels have thermal expansion coefficients similar to that of palladium and they are stable at the required operating temperatures (Wicke, E., Brodowsky, H. and Ziichner, H. ). Stainless steel is also readily available and relatively inexpensive."

Jan 1, 2012

By Qionghua Zhou, Wei Liu

"Nanocrystalline silver bulk material with average grain size of 20.3 nm was prepared by warmvacuum- compaction method. The as-prepared nanocrystalline silver was characterized by X-ray diffraction (XRD), differential scanning calarmeutry analysis (DSC), thermogravimetric analysis (TG), and 6157 type Electrometer test, respectivily. The experimental results show that the average grain size and microstrain of the nanocrystalline silver are 20.3 nm and 0.088%. The melting point and melting enthalpy are 1228.7 Kand 82.34 Jig, which are lower than that of coarse-grained silver by 6 Kand 22.6 Jig, respectively. The electrical resistivity of nanocrystlline silver increases with higher temperature when the range of temperature is between 233K and 293K. The electrical resistivity at 293 K is 1.475xlO -7 Q·m, which is higher than that of coarsegrained silver by a factor of 9.IntroductionN anocrystaline ( nc) materials or nano structured ( ns) materials are three-dimensional (3 D) bulk materials with average grain size typically smaller than 100 nm. Ne materials have been of great interest for their unique properties, such as superior tensile strength [1-2], high microhardness [3- 4], superplasticity [5-6], magnetically quasi-isotropic [7-8] , and so on, making them one of the most promising nano-scale materials with wide applications. Ne materials with average grain size of 5-10 nm were firstly fabricated by Gleiter et al. [9] in 1980s, using inert gas condensation (IGC) method. Unfortunately, the large surface to volume ratio creates a high surface energy component in the total free energy of the system and results in a metastable state in the materials. Therefore, due to the signfica nt disordered grain boundary regions, nanomaterials are thermally unstable and are subjected to a strong driving force for grain growth. The grain growth even occurred at room temperature [10].The conflict or deviation of measured date, e.g. strength, microhardness, thermal stability, partly due to the grain boundary ratio or the distribution of grain size, and partly derived from imperfections such as voids and microcracks while earlier processing techniques are known to result in incomplete dens:fication [11-12]. Therefore, the higher quality samples produced in subsequently years still show such a general trend."

Jan 1, 2011

By A. Tsubouchi, F. Noguchi, T. Takasu

"A high current density operation is desired to improve the productivity in copper electrorefining. However, a lot of problems still remain such as passivation at anode, dendritic deposition at cathode and impurity behavior during the electro refining.Effects of the current densitY on the morphology of copper deposition on the cathode, and passivation at the anode were investigated at various fluid velocity of electrolyte in the present study.Although a granular appearance of the copper deposition was obtained with increasing high current density, it was depressed by an increase of the fluid velocity of the electrolyte. A uniform deposition on the cathode was also observed when the fluid velocity of the electrolyte become higher. It was ascertained that passivation at the anode was suppressed by circulating electrolyte during electrolysis. INTRODUCTIONIt is desirable to operate at high current density in copper electrorefining in order to improve plant productivity without enlarging the size of electrodes(1). However, there are many problems in copper electrorefining at high current density with the usual commercial practice, for example, anode passivation, dendritic deposition and an increase of impurities in the cathode.In general, it is effective to agitate the electrolyte in order to suppress these problems(2). Smith et a1.(3) have performed electro refining experiments at various current densities in the range of 8 to 32 Aldm2 and at electrolyte fluid velocities in the range of 40 to 120 mlmin, and they obtained well consolidated, void free copper even at high current density in a high electrolyte velocity. However, they did not discuss the recovery ratio and the passivation behaviour at the anode. Walsh et a1.(4)(5)(6) experimented with the rotating cylinder electrode, and ascertained that electrolysis can be carried out at high current densities under the condition of pure electrolyte.With regards to anode passivation, there are several papers by previous workers(7)(8). Our group ascertained the process of producing anode slime during electrolysis(9). However, these experiments were carried out without forced circulation of electrolyte. Therefore, in the present study, to solve these problems, we electrolyzed at current densities in the range of 4 to 50 Aldm2 with circulating electrolyte in the range of 0 to 48 mlrnin. The effect of electrolyte fluid velocity on the surface morphology of deposited copper at cathode and passivation at anode were investigated when electrolysis were carried out with circulating electrolyte at high fluid velocity and at high current density."

Jan 1, 1997

By H. J. Thevik, A. K. Dahle

"A mathematical model that calculates the stress development in a coherent and stationary dendritic network due to interdendritic flow is proposed. The fluid flow is assumed to be related to the solidification shrinkage, and under the assumption of no porosity formation and unidirectional solidification, the shrinkage-induced flow within the mushy zone is calculated analytically. The interdendritic melt flow exerts a force on the solid network and an analytical expression for the stress build-up in the network is developed. Parameter studies illustrating the influence of cooling conditions, mushy zone length, dendrite coherency, fraction solid, volume fraction of eutectic, and solidification shrinkage upon the stress development within the solid network are presented. Comparing the magnitude of the calculated stresses to measurements of the strength in equiaxed mushy zones shows that it is possible for the stresses to exceed the strength, thereby resulting in reorientation or collapse of the dendritic network.IntroductionInterdendritic fluid flow is at present regarded as a very important mechanism for feeding of shrinkage during solidification of metal alloys. Solidification of many alloys is often characterised by heterogeneous nucleation of the primary phase on substrates in the melt with subsequent evolution of equiaxed dendrites. These equiaxed dendrites can initially grow freely, but impinge on each other and form a continuous dendritic network, ie. dendrite coherency, quite early in the solidification process. Measurements of the dendrite coherency point have shown that the dendritic network is established at solid fractions ranging between 0.1 and 0.5, and most often around about 0.2 [l]. Depending on the alloy composition this means that as much as 70 to 80% of the volumetric shrinkage has to be compensated by flow of liquid through the interdendritic network. Interdendritic flow occurs with a much larger resistance compared to free flow of the liquid and flow of a liquid with dispersed crystals. The pressure drop associated with the interdendritic flow increases rapidly with decreasing fraction ofliquid."

Jan 1, 1999

By Ling-yun Yi, Yuan-bo Zhang, Bing Hu, Zhu-Cheng Huang, Zhen-yuan Liao

"Nucleation and growth mechanism of iron crystal grain in coal-based shaft furnace direct reduction process by microwave heating were investigated by optical microscope, scanning electron microscope and EDX. The results indicate that microwave has selectivity on various minerals which absorb microwaves. The high temperature in certain area of pellets and thermal stress on the interface of minerals are formed, results in the wustite grain smashed along the joints, and iron crystal grains turned out a spherical shape obviously. The iron crystal nucleus is formed firstly at the edge of wustite, on the interface between grains and in the holes in pellets, and grows gradually while reduction carries on from surface layer to inner core. Microwave heating promotes the rate of transportation and accumulation of the iron crystal grain, increases growth rate of iron crystal grain and contributes to formation of dense iron-jointed crystal texture eventually.IntroductionMicrowave energy as a new energy, which selectively heating materials through internal energy dissipation, has the advantages of heating uniformity, high thermal efficiency, fast heating, clean and pollution-free compared to conventional heating motheds. Microwave energy also has obvious superiority in increasing productivity. Thus, it has been widely used in many areas, including electronics, food processing, chemical, medicine, environmental protection, and family life etc [1]. As a rapidly developed green metallurgical method, microwave heating also has been widely recognized by areas of grinding, pretreatment, pre-reduction, drying, furnacing, metal extraction, and waste materials processing and utilization. Some research achievements are gradually putting into practice, showing great potential in chemical and metallurgical industry [2-3]."

Jan 1, 2011

By Sadegh Firoozi

Experiments measuring the kinetics of oxidation and making visual observations of the oxidation of approximately 6 g static lead baths containing arsenic, antimony and tin were conducted in the temperature range from 500 to 600 oC. A range of repeatable behaviours were observed, notably: the formation of a coherent, solid oxide layers on pure lead and lead-tin alloys; the formation of liquid oxide droplets during the initial oxidation of lead-arsenic and lead-antimony alloys and the eventual formation of a complete oxide layer covering the entire free surface of these alloys. Thermogravimetric measurements revealed that the rate of oxygen uptake was strongly influenced by the form of oxides being generated at the melt/gas interface. Compared to the rates of oxidation of pure lead, arsenic increased the rate of oxygen uptake throughout the temperature range via the formation of liquid oxidation products. The presence of antimony resulted in a moderate increase in the rate of oxygen uptake as compared to arsenic. Tin was effective in lowering the rate of oxidation even in the presence of arsenic because the oxidation product was always a coherent layer that acted as a physical barrier to oxygen transport to the underlying alloy.

Jan 1, 2006

By Ashish D. Patel, Ramesh S. Minisandram

"Vacuum Arc Remelting (VAR) is the final and, hence, critical melting step for the production of a sound, segregation-free ingot for the manufacture of alloys used in rotating components in aircraft engines. A mathematical model for this process has been developed by the Specialty Metal Processing Consortium (SMPC). The model predicts temperature distribution in the solidifying ingot, flow in the molten metal pool, and the electromagnetic field in the ingot. These predictions may be used to estimate the effect of melting parameters on the pool profile in the ingot. In this paper, typical pool shapes and flow fields during VAR of Alloy 718 and Ti-6Al-4V are presented. The differences in the pool profile are primarily due to vastly different melting conditions. The model predictions are compared to the observed pool shapes from industrial-size VAR ingots.1. IntroductionVacuum Arc Remelting (VAR) is a process in which an electrode is melted in vacuum by the heat from a DC electric arc. Metal droplets from the electrode fall into the molten metal pool, which solidifies in a water-cooled copper crucible to form the ingot, as shown in Figure I. The ingot obtained from VAR is sound, and has superior cleanliness and chemical homogeneity. Hence, the process is the final melting process for most nickel-base superalloys and titanium alloys used in the manufacture of critical rotating components (discs & blades) of aircraft engines. Modeling of this process provides an insight into the effect of melting parameters on the molten metal pool in the solidifying ingot, which is a key first step in process optimization and defect prevention. In this paper, typical pool shapes, both measured and predicted, for VAR of Alloy 718 and Ti-6Al-4Vare presented. Alloy 718 is the most common VAR-processed nickel-base superalloy; whereas Ti-6Al-4V is the ''workhorse"" alloy for titanium-based alloys."

Jan 1, 2004

By Chikabumi Yamauchi, Mitsuru Tanahashi, Tsuyoshi Taniguchi, Nobuo Furuta, Toshiharu Fujisawa

"It is essential to clarify the equilibrium relations among nonmetallic inclusions of the Mn0-SiO2-CrOx system and molten stainless steel in order to control non-metallic inclusions formed by the deoxidation of stainless steel with silicon. In the present study, the phase equilibria of the MnO-SiO2-CrOx system were measured by conducting the following experiments under controlled oxygen partial pressure, Po2, at 1873 K:1) Phase equilibria of the MnO-Cr20 3 binary system were measured for Po2 = 2 x 10-6 ~2 x 102 Pa.2) Phase equilibria of the MnO-SiO2-CrOx ternary system were measured for Po2 = 2 X 10-6 Pa.Based on the results, the phase diagram of this ternary system was established under the condition of the Si-deoxidation process of stainless steel (Po2 = 2 x 10-6 Pa and T = 1873 K).IntroductionAt the deoxidation stage in steelmaking process, generally multiple deoxidizers participate in deoxidation reactions, and the composition of deoxidation products ""non-metallic inclusions"" greatly varies depending on deoxidizing efoments and their contents. In order to control non-metallic inclusions formed by the refining process of steel, it is essential to clarify the equilibrium relations among non-metallic inclusions and molten steel.Especially, during the refining process of stainless steel, nonmetallic inclusions in molten steel seem to- change as follows. After the oxidation refining, Mn-chromite is formed in molten steel as non-metallic inclusion. By the deoxidation with silicon addition (mainly less than 1 mass%), Mn-chromite inclusions are changed their compositions to Mn-silicate. Segawa et al.[l] have reported the effect of amount of silicon addition on composition and mass ratio· of non-metallic inclusions during the Sideoxidation process of 18Cr-8Ni stainless steel at 1873 K, as shown in Figuri; L At higher silicon content than 0.5 mass%, only Mn-silicate was identified as non-metallic inclusion. On the other hand, at lower silicon content, both of Mn-chromite (MnO Cr2O 3) and Mn-silicate were identified. However, the thermodynamic and the kinetic analyses of the above-mentioned Sicdeoxidation process have not been made due to lack in the thermodynamic data for the non-metallic inclusions· of the MnO-SiO2-CrOx system, such as the phase diagrams, the activities of the components, and the free energy of intermediate compounds. In relation to the phase diagram of this system, those of the MnO-SiO2 [2] and the SiO2-Cr2O 3 [3] binary systems have been only reported"

Jan 1, 2000

By M Phil Schwarz

"A CFD model for the gas-side of an impinging jet iron bath reactor has been developed to assist in the interpretation and design of oxidizing gas-melt reaction rate experiments. Heat transfer and reaction at the surface have been included. A free surface model, which solves for the liquid motion within the bath as well as the gas motion above the bath, has also been developed. This model also predicts extent and shape of the dimple formed on the liquid surface by the impinging jet. Both models have been run for conditions typical of jet impingement experiments using CO2 , H2O and O2• The main conclusions are• Results from the model for gas-side mass transport are in good agreement with the empirical correlation of Belton and Belton (1980)• Experimentally determined rates of decarburization by CO2 should be corrected for mass transfer because the experiments are often carried out under mixed rate control, eg for gas flow rate 10 L/min when the sulphur concentration is lower than 0.045• If the rate constant for oxygen reaction is greater than about 5 mol/m2.s.atm, it cannot be determined using a gas flow rate of 10 L/min or lower because of mass transfer control.• A cavity of depth 4.5 mm is predicted for a gas flow rate of 10 L/min and this substantially changes the flow field (and hence reaction rate) compared with a simulation in which the surface is assumed to be flat."

Jan 1, 1999

By Lin Yang, Minjun Tang, Shuishi Liu, Jianfeng Zhou, Linjiang Qing, Xiaolei Song, Yufeng Guo, Tao Jiang

"The dynamics of oolitic hematite magnetic roasting was studied. The results show that oolitic hematite magnetic roasting was controlled by the internal diffusion, and the diffusion coefficient was 9.018x10-7 m2·s-1when the oolitic hematite was roasted at 650°C. Magnetic susceptibility improves when temperature increases and roasted time prolonges under the condition of roasting at 650°Cfor 50min, with the magnetic susceptibility is 39.88%. CaF2 and Na2C03 can significantly improve the magnetic susceptibility at the same roasting condition, and the magnetic susceptibility was 63.35% and 57.99% respectively, thus the reduction of oolimic hematite was promoted.IntroductionWith the continual depletion of free-milling iron ores and its rising price, developing the abundant resources of oolitic hematite has become one of the main research areas. The oolitic hematite accounts for 10% of China's iron ore reserve, and it also accounts for 30% of red ore reserve in China [1]. In order to exploit the oolitic hematite, there are many beneficiation research methods, including fine grinding/selective flocculation/high intensity magnetic separation or flotation, high-gradient magnetic separation, low intensity magnetic separation/high intensity magnetic separation/reverse flotation, chloridizing roasting/acid pickling, magnetic roasting/leaching process etc [2]. However, the oolitic hematite is easy to slim and the valuable mineral is covered by the slim, because of the tiny granule of value mineral, then the ooides are formed due to the state of layer morphology formed by iron ore and ganaue minerals [3, 4]. Fairly good separation indexes were hard to be obtained by traditional separation due to its structural features, so the magnetic property of the iron minerals will be changed with the use of the magnetic roasting [5, 6], which result in hematite variably altered to magnetite and simplified technological process so that a good separation indexes will be obtained by using the low intensity magnetic separation. Therefore, in order to provide theoretical direction of how to use the oolitic hematite effectively through the magnetic roasting, the oolitic hematite of GuiZhou province was studied, which emphasized on researching the dynamics of oolitic hematite magnetic roasting."

Jan 1, 2013

By K. Fukushima, K. Baba, H. Kurokawa, M. Yamagiwa

"The Toyo smelter has expanded its anode production capacity from 126,500 to 239,000 t/year by introducing technical oxygen into blast air for flash and converter furnaces and improving smelting facilities. Significant efforts were made in the expansion not to increase the number of workers, which mean development of some automation systems for the copper converters and anode casting wheel. The efforts have resulted in the above-mentioned increase in productivity and a saving of production cost as well as a decrease in the number of workers for the anode casting operation.IntroductionThe Toyo smelter has been performing a highly stable and pollution free operation since its commencement in 1971 (1). Its distinctive features are the on-line control by process computer (2) and the high productivity without trouble. But owing to the so-called oil crisis in 1979, we were faced with a sharp increase in production cost. To decrease the production cost, some measures for saving of energy were planned and carried out, such as conversion from oil to coal in a flash furnace (3), the heat recovery from converter slag and the introduction of technical oxygen in blast air with the intention of energy saving as much as possible.The first increase in production capacity and some savings of production cost were attained in 1982 by the introduction of technical oxygen in blast air for the flash furnace without major modification of the furnace as shown in Table I. The capacity of an oxygen plant is 7,800 Nm3/H as 90% O2 . Part of oxygen from the plant is also supplied to tuyeres of copper converters through an oxygen holding tank with a volume of 830 m3 at 7 kg/cm2-G."

Jan 1, 1989

By Thomas Niehoff

"Oxyfuel combustion systems are state of the art for many melting operations. Airfuel systems have been stepwise modified to oxygen enrichment, oxygen lancing and oxyfuel. Every change of the melting process will have consequences with regards to emissions and energy usage. The uniqueness of many operations requires unique skills to resolve potential issues. This paper will give some examples of how airfuel systems can successfully be converted to oxyfuel.IntroductionOxyfuel technology – meaning the combustion of fossil fuels such as natural gas, oil or coal with technical oxygen instead of air for industrial melting or heating processes is widely used in many industries these days. Even though oxygen production, storage and handling has been state of the art for decades other opinions exist. Often oxyfuel is regarded with fear and potential hazards like: “Oxygen makes the process too hot.”, “Oxygen will melt away the refractory.”, Liquid oxygen is dangerous.”, “Oxygen will cause explosions.”, ……etc.Typically a more detailed discussion about a specific industrial process and how oxygen can be applied in a safe and economic way the seeming issues go away."

Jan 1, 2010

By Liu Zhonghua

Hydrogen reduction of cobalt sulfide (Co9S8) was experimentally investigated in the temperature range 813-1053 K. The results revealed that the reaction kinetics can be described by the shrinking core mod¬el in chemical control regime at low temperatures, it is of first order with respect to hydrogen concentration, and the reaction activation energy is 67.4 kJ/mol. The SEM second electron images of the samples before and after experiments showed that the swelling of the sample above 973 K is due to the formation of metallic cobalt whiskers.

Jan 1, 1992

By Antti Roine

Sulfidic zinc concentrates are usually roasted in a fluidized bed furnace into sulfur-free oxide form. Metallic zinc is produced from this oxidic calcine using hydrometallurgical leaching, solution purification and electrowinning stages. The roasting step is necessary because zinc oxides are easier to dissolve using traditional leaching methods than zinc sulfides. The Kokkola Zinc smelter uses various types of zinc concentrates and secondary materials as feed mixture. This makes it difficult to find optimum process parameters for the roaster when the composition and particle size distribution of the feed mixture varies even on a daily basis. Certain conditions may even cause difficult accretion problems or increase the amount of calcine in the process off-gas line excessively. A thermochemical heat and material balance model was developed for process advisor, in order to estimate the effects of different process parameters (temperature, process air coefficient, concentrate feed, oxygen enrichment, water feed, etc.) on the heat balance, roasting temperature and calcine composition. This model was constructed using the heat balance module of HSC Chemistry 4.0 software. The prevailing chemical compounds in the concentrate and calcine were verified using mineralogical analyses and equilibrium calculations. The roasting process seems to operate near chemical equilibrium conditions, if the behavior of the main components is considered. This paper describes briefly the basic principles of the calculation model and outlines the results with several diagrams and discussion. The calculated results were in reasonable agreement with the recent process air oxygen enrichment and water feed test campaigns carried out at Kokkola in 1999.

Jan 1, 2000

By Guangchun Yao, Chuan Li, Hongjie Luo, Zhuokun Cao

"The expansion rate and collapse time of liquid aluminum foams are essential for the determination of operating time and quality of the resulting foam. In the present paper, liquid aluminum foams was fabricated by adding in TiH2 as blowing agent, and the variation of expansion rate with foaming time was non-contact detected by a laser distance measurer. The influence of different stabilizing agent and alloying elements was studied. The results show the fact that the fraction of stabilizing agent only perform little effects on the maximum expansion rate of liquid aluminum foams, while the influence of alloy elements are remarkable. The maximum expansion rate would increase much when Mg is added, and the liquid foam also collapse at a shorter time. Comparison was made between experimental results and mathematic calculations, which reveal the fact that it is the change of TiH2 decomposition responsible for the change.IntroductionMetal foams, combining light weight with other unique mechanical and physical properties, have gained wide interest and been developing fast during past few decades. However, manufacture of this new material is quite challenging since it involves simultaneous occurrence of gas, liquid and solid phase at high temperature [1-2].Quite some manufacture routes have been developed for manufacturing metal foams, and the structure and quality of resulting foam are remarkably improved during the last decades. However, most of the past works seems to be experiential, and because the lack of basic knowledge of foaming process, the start material is limited and the production technologies are far from reliable and reproducible.[3-4]In direct foaming process, decomposition of blowing agents, TiH2 for example, is the main force for foam expansion. The density and foam structure changes with time during the foaming process, so it is expected that foams of certain structure can be obtained by solidification of the liquid foam at a certain time [5-6]. However, the foaming process is weak in reproducibility and the influence of stabilization additives and alloying elements is unclear."

Jan 1, 2011

By Victor Zavodinsky, Sergey Rogov

"Pseudo-potential fully relaxed total energy calculations are used to predict a hypothetical Si1-xCxO2 (x<0.5) compound formed from SiO2 ß -cristobalite by substitution of some SiO2 complexes by CO2 molecules. The simulation shows that the Si1-xCxO2 compound can be quasi stable if the CO2 content is less than fifty per cent. It is assumed that six-molecule Si6-nCnO12 (n=3) rings can play a role of nucleuses for formation of the Si1-xCxO2 compound from SiO2 and CO2 molecules. Thus, silicon dioxide can be considered as a possible solid store for gaseous CO2.IntroductionThe problem of increasing of CO2 in the Earth atmosphere is one of the main modern problems of mankind. One of conceivable ways to decrease the harmful value of CO2 is to convert a part of it to solid state. Iota et al. [1] reported a polymeric (quartz-like) phase of CO2 solid synthesized at high pressure (~40 GPa) and at high temperature (~1800 K). Shortly after this experimental work, Serra et al. [2] reported a total energy calculation of several possible phases of CO2 using plane wave pseudo-potential density functional theory. They concluded that there should be a transition from a molecular phase to a phase isostructural to SiO2 -quartz in the range of 35 to 60 GPa. The latest calculations by Dong et al. [3] have shown that the more favored solid CO2 phase is ß -cristobalite. Recently, Kume et al. [4] have demonstrated the polymerization of CO2 even at room temperature at high pressures up to 80 GPa. Transformations of gaseous CO2 to different solid phases were studied recently experimentally and theoretically [5-8]. The main obstacle for using synthesized CO2 solid as a solution for the CO2 problem is its pressure instability. However the SiO2 ß -cristobalite with the same structure is stable.The question is whether a silicon-oxide system in which a part of atoms of silicon is replaced by atoms of carbon will be stable? If the answer is positive, this system can be considered, in our opinion, as a possible store for CO2."

Jan 1, 2009

By Suzzann Nordwick

The metallurgical treatment of mercury-containing materials for precious or base metals recovery imposes many processing and environmental challenges. Mercury is usually present as elemental or cinnabar. Historically, mercury has been removed from mined ores pyrometallurgically by roasting, but hydrometallurgical methods have also been employed. For example, alkaline sodium sulfide solution acts as an universal solvent for most mercury compounds. While, most other metals are highly insoluble in this solution. This allows for a high degree of selective separation of mercury from other metals with the exception of tin, antimony and arsenic. Mercury leached with a solution of sodium hydroxide and sodium sulfide or sulfur can be re-covered by cementation or stabilized through sulfide precipitation. Hydrometallurgical technology for the pretreatment of mercury removal from gold, silver, and base metal ores using alkaline sulfide leaching will be discussed with a focus on alkaline sulfide leaching of mercury sulfide-containing materials.

Jan 1, 2003

By Cesar Garban

The samples of the washings are characterized of the ore for physical, chemical and metalurgical properties for representivity. the optimum values are determined for the recuperation of gold of the washings of the gold ore from the zone El Callao, Venezuela by acidic solutions of thiourea of the following parameters: Ph , contact time, composition of the liquid mixture, ratio of solid to liquid, grade of liberation, in an apparatus designed for contacting solid powder of the mineral with liquid solution of thiourea mantained in suspension by bubles of compressed air. The experimental results showed that the velocity of lixivation in primier time of (20) minutes is rapid and practically 2/3 part of the reaction is completed. For experimental design of parameters, the optimum conditions of recuperation of gold determind in this experimental investigation are:

Jan 1, 1999

By Berndt Moeller

Mercury-cell chlor-alkali production plants generate mercury contaminated wastewater streams from which mercury must be precipitated and filtered, resulting in a sludge containing 2% mercury (designated KI06) that cannot be landfilled in the United States without treatment. REMERC is a chemical treatment process used to recover 99% of the mercury from wastewater sludge generated at these plants. The process uses leaching to oxidize mercury compounds to mercuric chloride, washing and filtration to separate mercuric chloride from the treated sludge, and cementation to reduce the mercuric chloride to metallic mercury. Mercury not recovered in cementation is recycled to the wastewater process for precipitation and filtration. Treated sludge contains less than 260 ppm total mercury and 0.2 ppm TCLP, meeting the USEPA low mercury subcategory specifications that allow landfill disposal. REMERC uses readily available chemicals, is straightforward to control and inexpensive to operate, has no mercury emissions to air, and recovers metallic mercury. REMERC enabled significant cost savings including lower solids disposal costs, recovery and reuse of metallic mercury in the chlor-alkali process, and ability to treat non-wastewater sludge. No new EPA permits were required. REMERC was shown to be a viable process for recovery of metallic mercury from K106 designated sludge.

Jan 1, 2003