By Shigeatsu Nakazawa

Activities of Bi and In in the Bi-In liquid alloy were measured over the whole range of eomposition at the temperatures from 850K to 1050K. An alloy was vaeuum-sealed in a quartz cell and heated at the temperature of interest. The absorption for 307nm radiation from Bi lamp was measured for Bi atom vapor in the cell. By heating a pure metal as a standard and measuring the absorbance as a function of the temperature, an analytical curve for Bi atom vapor was constructed and used for conversion of the absorbance to the vapor density. Bi activity was determined as the ratio of the Bi atom vapor density over the alloy to that over a pure metal. The same procedure was applied to the In 304nm radiation from In lamp and In activity was determined independently of Bi. Results showed that the liquid Bi-In system behaves like a regular solution.

Jan 1, 2003

By Shigeatsu Nakazawa

Activities of Bi and In in the Bi-In liquid alloy were measured over the whole range of composition at the temperatures from 850K to 1050K. An alloy was vacuum-sealed in a quartz cell and heated at the temperature of interest. The absorption for 307nm radiation from Bi lamp was measured for Bi atom vapor in the cell. By heating a pure metal as a standard and measuring the absorbance as a function of the temperature, an analytical curve for Bi atom vapor was constructed and used for conversion of the absorbance to the vapor density. Bi activity was determined as the ratio of the Bi atom vapor density over the alloy to that over a pure metal. The same procedure was applied to the In 304nm radiation from In lamp and In activity was determined independently of Bi. Results showed that the liquid Bi-In system behaves like a regular solution.

Jan 1, 2003

By Jiang Feng, Zhang Libo, Peng Jinhui, Guo Zhanyong, Ju Shaohua, Lei Ting

The basics of microwave drying process of CuCl residue were studied by comparing the dielectric property of the residue with different moisture contents. The dielectric properties were measured by microwave cavity perturbation method. The dielectric constant and dielectric loss factor of the CuCl residue have a linear correlation with the moisture content. With this relationship, we can realize on-line measurement of moisture content of the CuCl residue by dielectric properties. The microwave drying experiments with different thicknesses (1-5cm) of CuCl residue were carried out, and the heating curve of the materials under different microwave powers (250-450W) was made. From these parameters, an optimized operation parameter of microwave roasting technology, the thickness of CuCl residue filter cake to be microwave roasted should be 2cm , was deduced.

Jan 1, 2015

By Preben Ingerslev

Control of the reheating of ingots is based either on surface temperature measurements using optical pyrometers or on furnace set points and reheat time determined empirically. This paper presents a real-time mathematical heat flow model, named BESTT, which calculates the temperature distribution in an ingot cross section when reheated or cooled. The model runs on a 486 PC in less than one minute for a variety of ingot cross sectional shapes such as circular, square and with some considerations octagonal and heavy-cornered square. Initial temperatures can either be uniform or nonuniform while accounting for temperature dependent thermophysical properties. The model was developed and verified using 718 alloy ingots in box type furnaces. When integrated with on-line pyrometric measurements, BESTT can provide for improved feed back in the reheating control loop. The use of BESlT will assist in reducing energy costs, and improving product quality and consistency. EPD Congress 1994 Edited by C. Warren The Minerals, Metals k Materials Sodety, 1993

Jan 1, 1994

By Jilai Xue, Jun Zhu, Baisong Li

"TiB2-C/C Function Gradient Materials (FGM) is used in cathode materials to improve aluminum wettability and melt penetration in aluminum electrolysis. In this investigation, FGM was tested for use as part of the cathode materials, where a 10 mm thick TiB2-rich layer was on the top as an Al-wettable surface, the TiB2-C layers in the middle as a gradient layer and the carbon on the bottom as a base. Electrical resistances ofFGM were determined in the temperature range of25- 9600C in argon atmosphere. The results show that the present of TiB2-C gradient layer can reduce the open porosity and the electrical resistance of the cathodes materials at elevated temperatures. The cathode samples after aluminum electrolysis usually demonstrates an increase in electrical resistance, but the application of FGM layer can compensate such an increase for certain extend due to less variation in porosity and lower the level of melts penetration.IntroductionCarbon is still used for aluminum reduction cathodes dominantly, but it has a poor wetting properties by liquid aluminum and the anode-cathode distance has to be kept about 4-5cm with an additional 1.3-2.0 V voltage drop [l]. TiB2 has better wettability by liquid aluminum with higher electrical conductivity and stronger chemical resistance to the electrolyte attack. And the wettability ofTiB2-C composites cathode on liquid aluminum can be also improved, while liquid aluminum can completely wet the cathode surface ifTiB2 content exceeds 27% [2-4]. However, during the process of TiB2-C composites cathodes preparation and aluminum electrolysis, the deformation by temperature variation or sodium penetration are great disparity between TiB2 and carbon due to their physical properties difference. This will accelerate the cathodes cracking and deterioration."

Jan 1, 2013

By Xiyun Yang, Hui Xu, Xichang Shi, Xiang Xiao

"Rod-like magnetite particles were prepared by precipitation of iron salts with urea under the induction of magnetic field. Temperature and initial Fe3+/Fe2+ ratio have a significant effect on the composition of the product. Magnetite particles change from spherical into rod shape in the presence of a 0.35 T magnetic field, The addition of a small amount of spherical seeds increases the rod-like magnetite particles yield. The seeds are prepared by aging ferrous and ferric solution with sodium hydroxide as precipitator. The aspect ratio of the rod is controlled by varying the volume ratio of seed to iron salt.IntroductionMagnetite, an important member of magnetic materials, has attracted a lot of attentions for its super magnetic properties. The rod-like magnetite particles have high anisotropy and coercive force as well as super magnetic properties compared to other shapes, and are widely used as high magnetic density media, magnetic devices and microwave materials [1-4]. Recent studies have found that magnetic field can direct magnetite growing along easy magnetization axis to get one-dimension particles [5-6]. Chen et al. [7] synthesized single crystalline nanorod magnetite under magnetic field. Wang et al. [8] discovered that magnetite grew along easy-magnetization directions under 0.35T magnetic field. Vereda et al. [9-1 O] found that magnetic field had a dramatic effect on the morphology, inducing the aggregates to line along one direction to form rodlike particles.At present, most of the synthesis methods reported in the literature result in a low yield of rod particles and the aspect ratio are difficult to control. Recently, we developed a seed-mediated growth approach to making rod-like particles in an aqueous solution. The spherical magnetite generated by oxidation serves as a seed. These seeds are then added to a solution containing iron salt and urea, and provide nucleation sites for magnetite rod growth."

Jan 1, 2011

By Richard D. Hagni

Process mineralogy has not been given adequate attention in years past, because geologists have not been sufficiently interested in applying mineralogical techniques to industrial processes, and most process engineers are not adequately trained to use them. Although some individuals and institutions have made efforts to improve the situation, it is only in the last few years that the significance of applying the methods of mineralogy to a wide variety of industrial processes has been fully appreciated. Presently, the formation and organization of several groups devoted to applied mineralogy have created a more amenable climate for the development of process mineralogy. As a result, the presentation, discussion, and publication of the results and case histories of process mineralogy have become fairly common. Short courses affording hands-on experience with applied techniques are now available to the many geologists and process engineers engaged in industrial mineralogical processes. The future role of the process mineralogist is viewed as an expanded one, which will increase in value.

Jan 1, 1982

By Jie Li, Zhongliang Tian, Xun Hu, Kai Zhang, Yanqing Lai, Hongliang Zhang

The Al-Sc Alloys show many advanced properties for a wide range of engineering applications. But the metal Sc must be added into the metal Al in the form of the Al-Sc master alloy, which is usually produced by the thermal reduction process. In this paper, the decomposition voltages of Sc2O3 and Al2O3 in Na3AlF6-K3AlF6-AlF3 melt were calculated based on the Nernst equation. And the Al-Sc master alloy was prepared in the melt at 950°C by electrolysis. The results show that the Al-Sc master alloy can be prepared by the co-deposition of Sc3+ and Al3+ at the cathode if the concentration ratio of Sc2O3 to Al2O3 in the melt is more than 2:1 under the condition of the aluminum electrolysis. SEM and ICP analysis of the product indicates that the Al-Sc master alloy is made of the phase Al and the phase Al3Sc.

Jan 1, 2016

By Ulrich Kerney

In 1996, bath smelting technology for lead recovery from concentrates and secondary materials was introduced in Nordenham to replace the common sinter plant/shaft furnace operation. Since start-up, a continuous improvement of equipment and operation lead to a steady increase of capacity and plant availability. The decision to skip the reduction stage for slag treatment now allows the treatment of 200000 t/a feed materials with a secondary fraction of up to 70 %. The main feed source for the furnace is automotive battery recycling, which offers oxide paste and metallics to be molten under oxidizing conditions in the lance fired furnace. The lead bullion is transferred to the refinery, where copper, silver and other impurities are removed. Silver is recovered as doré quality. All loopings are recycled to the BSF. Inert feed material is collected in a so-called lead concentrate of metallurgical origin, the primary slag, which is sold. It is rather a valuable feed material for further processing than a slag The off-gas is cooled in a flux-flow system, entering then an electrostatic dust precipitator. Having passed a further washing and cooling system, SO2 is oxidized and collected and sold as concentrated sulphuric acid. The presentation will cover a review of the start-up phase, the development of significant production parameters over the last years and actual production routes and figures. A comparison of environmental data between new and old applied technology is made.

Jan 1, 2006

By A. K. Kyllo

A study has been carried out on the dusts from Hudson Bay Mining and Smelting's Flin Flon copper smelter. The aim of the work was to determine the mechanisms of dust formation and the deportment of the various constituents. The work concentrated on the copper converters, but the electrostatic precipitators and baghouse also clean the reverberatory furnace off gas, so some mixing will have occurred. The dust composition was found to vary with distance from the furnace, and to be made up of three major components: solidified droplets, unreacted flux, and condensed particles. The solidified droplets were formed from material ejected from the converter during blowing, while the flux was blown out of the converters immediately after charging. The condensed particles contained the majority of the lead and zinc, as well as the volatile impurities. There was also a significant soluble content of the dusts, increasing with distance from the furnace. The condensed material may be separated from the remainder by a simple washing and sizing technique.

Jan 1, 1996

By W. Petruk

The behaviour of galena, chalcopyrite and tetrahedrite during floration of a fine-grained base metal ore from New Brunswick was investigated by image analysis study of the mill concentrates and tailings. The minerals were analyzed to determine the grades and recoveries as related to free and unliberated mineral grains and their size distributions. The results show that only 37 wt % of the galena was liberated but 88 wt % of the free galena was recovered, indicating good mill performance for the lead. The lead recovery was 65 wt %, with the main loss due to unliberated galena. Most of the unliberated galena lost to mill tailings is so fine-grained that galena liberation and Pb recovery would not improve significantly by re-grinding. Chalcopyrite liberation was 56 wt % but only 75 wt % of the free chalcopyrite was recovered. Copper recovery was 45 wt %, with the chalco-pyrite loss in the mill tailings being both as large free grains, and as small and large unliberated grains. It was calculated that copper recoveries could be improved about 8 to 10 wt % by changing the concentrator operations and by regrinding. Concentrator operations hive already been modified and copper recoveries have improved about 5 wt %. About 29 wt % of the silver was lost to tailings mainly as both free and unliberated, large and very small, Silver-bearing tetrahedrite grains. It was calculated that about 25 wt % of the silver in the tailings might be recovered by improved milling conditions and by regrinding.

Jan 1, 1981

By Jerome P. Downey

The Indium Corporation of America - Colorado School of Mines Indium Separation Technology was evaluated as a potential means of treating smelter flue dusts stockpiled at the Pintlar Corporation property in Kellogg, Idaho. The patented technology represents a method for segregating the contained indium, lead, and other metals in forms acceptable for downstream processing and recovery. Separation is effected by treating the dust with metallic sodium in a bath of molten lead. Process effectiveness was measured by determining the relative distribution of key metals between the bullion and dross products at small pilot plant scale. The study indicated that application of the technology to the Pitlar samples results in a highly efficient concentration of lead in the bullion, while indium is collected in the dross. The distribution of other key metals between the bullion and dross products and the effect of varying selected process parameters are also discussed.

Jan 1, 1994

By Saad Elias Kaskah

"The Box-Behnken Design (BBD) is used to model the sacrificial Cathodic Protection System (SCPS) to find the factors effectiveness behaviour. For protection potential assessment the BBD receives (resistivity of environment, sacrificial anode alloy, distance between anode and cathode and surface area for the structure to be protected) as input and gives the protection potential as output. By applying BBD with their analysis tools we get many results. The important results which are the factors individual effectiveness on the sacrificial cathodic protection (SCP) process are the resistivity which has the greatest effect on the potential protection (rank=l) followed by sacrificial anode alloy type (rank=2), surface area for structure protected required (rank=3) and distance between anode and cathode (rank=4). The interaction of sacrificial anode alloy and cathode area {X2X4 ) has significant effect on CP process with the limits which are used in this work while the other factors interaction (X1X2, X1X3, X1X4,X2X3, X3X4 ) has insignificant effect on the limits which used in this work.IntroductionFor carbon steel in seawater the normal corrosion potential E '°""_is in the range -550 to -600 mV vs. Ag/AgCI [1]. The most effective method to overcome the corrosion is cathodic protection {CP) which represents a control method in the steel wall corrosion. Cathodic protection has been used in several areas including marine and underground structures, storage tanks, and pipelines [2]. Sacrificial anodes system generates protective current which depends upon the inherent potential difference between the anodes and the structure to be protected. If the structure is made of iron or steel, any metal that is more active in the electromotive force series can theoretically be used as anode material [3]. There are many factors influencing on cathodic protection like resistivity (NaCl content), chemical composition of sacrificial anode alloy, distance between anode and cathode, surface area of cathode, temperature, humidity, velocity of solution, dust, impurities, bacteria and etc .. The present work studied four factors: NaCl content, resistivity), chemical composition of sacrificial anode alloy, distance between anode and cathode, surface area of cathode) with different three levels of values for each one. Then this work will find the optimum value from the factors levels that tacked to investigated there influencing on sacrificial cathodic protection system."

Jan 1, 2013

By Wenjie Zhu

Chromite ore processing residue (COPR) is a hazardous waste containing high concentration of chromium. We describe here a pioneer trial of detoxification of COPR in column reactor with an indigenous chromate reducing bacterium Leucobacter sp. Ch1, which showed high chromate reducing ability at high pH. Under the optimum conditions, at 30°C and pH 10.0, pH of leachate decreased from 10.3 to 8.3, and Cr(VI) concentration in solution decreased to zero mg L-1, and 76.4% of Cr(VI) was removed from COPR samples. The leaching toxicity of detoxified residue was 1.1 mg L-1 that was lower than national standard of China.

Jan 1, 2008

By Yanhui Liu, Xuewei Lv, Chenguang Bai

A thermodynamic model for determining the surface tension of molten slag by considering the surface tension and molar volume of the pure oxide component, and their ionic radii was extended to the slag bearing high TiO2 (varying from 80 to 67%) at 1973 K. The iso-surface tension curves for the FeO-TiO2-Ti2O3 ternary system at 1973 K are almost parallel to the FeOTi2O3 line. TiO2 plays a role of surface-active solute, and its surface-active effect is attenuating with increasing the TiO2 content. The iso-surface tension curve shifts away from the TiO2 corner, indicating that the surface tension of the ternary slag decreases along with the addition of SiO2. The reasons include the addition of SiO2 with lower surface tension and the decrease of the total ion moment at the surface. Both CaO and MgO can bring about that the iso-surface tension curve shifts towards the TiO2 corner, indicating that the surface tension of the ternary slag increases along with the addition of CaO or MgO. CaO has a more pronounced effect on increasing the surface tension of the ternary slag than MgO at an equimolar amount addition. The increase of the surface tension results from both the compositional change and the variation of the slag structure.

Jan 1, 2015

By Zhucheng Huang, Ronghai ZHONG, Tao Jiang, Jun ZOU

The method of reduction roasting and magnetic separation of low-grade, micro- fine disseminated refractory iron ore following granulation with coal produced unexpected success. Pellets of iron ore with diameter between 3 and 8mm were granulated with coal, bentonite and water. The raw pellets and reduction products were analyzed by scanning electron microscopy and x-ray diffraction. Results show uniformly distributed coal powders inside the pellets improved the kinetics of the reduction process and accelerated the reduction rate. Reduction time was higher at temperatures below 890℃, which resulted in the formation of substantial amounts of fayalite. When temperature was increased, micro- fine hematite was then quickly reduced to iron metal and the amount of fayalite decreased sharply. When pellets were reduced at 950℃ for 25min, reduction products with 56.73% metallization rate were obtained. After grinding and magnetic separation, a concentrate with 72.18% Fetot was obtained.

Jan 1, 2015

By A. MacRae

Campaign life of the converting furnace has been limited by break-outs through the hearth and walls. Throughput of concentrate has increased by 60% since start-up of the copper operations in 1981. The Furnace Integrity program was initiated at Kidd in 1993 to improve the reliability and safety of the smelting-cleaning-converting furnace line. The converting furnace is undergoing a series of upgrades to overcome severe refractory wear to the roof, walls and hearth. A recent shut-down was held in March 1997 to implement improvements to the roof, walls and slag outlet. Wall modifications included a new upper shell, wall coolers which can be supported during a shut-down from outside of the vessel, and an increase in the number of cooling blocks. Improvements to the roof included increased cooling, a novel brick/cooler suspension system, and roof compression for gas tightness. Design is currently underway to deepen the refractory hearth, to decrease hearth erosion and increase resistance to flotation.

Jan 1, 1998

By Zongliang Zhang

Electrowinning is a significant step in metal extraction processes. Because the nature of electrowinning is to reduce metal from its oxidized state, substantial energy consumption accompanies it. Electrowinning processes of different metals have much in common—the deposition of the metal on the cathode and the counter-reaction on the anode. An advanced model was developed that can be applied to a variety of metal electrowinning processes. A model for specific metals can be readily obtained by modifying parameters such as potential, kinetics, and side reactions in the model. The model incorporates mass transfer, gas-liquid flow, electrochemistry, and deposition, making it a comprehensive electrowinning model. The model is applied to copper, nickel, and zinc and verified with the experimental results. In addition, the parameter settings and results of different metals were compared, showing that this model has great versatility and accuracy, thereby making it an efficient and effective research tool.

By Judy Che, Steven Ceccio, Gretar Tryggvason

"A detailed understanding of drop deformation and solidification is essential for quantitative predictions of geometry and properties of parts made by ballistic particle manufacturing processes. Axisymmetric results of towers built by the deposition of multiple drops are presented. In these computations, fluid flow, heat transfer, and phase change are fully coupled throughout the drop deformation and solidification process. The solution method is based on a single set of conservation equations written for all phases simultaneously. The phase boundaries are treated as imbedded interfaces by adding the appropriate source terms to the conservation equations. A parameter study demonstrates the effect of Weber number, Peclet number, and drop deposition frequency on the final shape of the structure. Numerical results show that most successful method of building uniform towers is when two conditions are met. First, each drop solidifies at the same time in the deformation cycle. Second, the cooling rate is slow enough to allow for good adhesion between drops. The ability to predict the final shape of deposited drops will greatly reduce the amount of experimentation necessary to select the desired set parameters for any artifact.IntroductionMaterial deposition techniques based on layering small molten metal drops holds the promise to build small, coherent three-dimensional structures. In this process, numerous 20-100 µm diameter drops are deposited onto a substrate with a low impact velocity (on the order of 5 mis). Both the momentum and trajectory of each drop are controlled precisely to build up complex parts. This material layering technique differs from processes such as spray forming and splat quenching which involve high impact velocities (on the order of 100 mis) and high frequency deposition with little control over individual drop placement. This process of layering small drops can produce parts with near net shape accuracy, while spray forming produces slabs of material which must then be worked to make a usable part. The ability to computationally predict final drop shape and cooling rate has the advantage of allowing the user to select parameters to produce parts with desired shape and mechanical properties. However, the development of such predictive methods requires a thorough understanding of both drop deformation and solidification"

Jan 1, 1999

By Ting Liu, Qian Li, Peng Deng

The wastewater containing Hg2+ and Pb2+ does great harm to the environment and human bodies. Traditional wastewater treatment cannot fundamentally put a stop to heavy metals pollution for producing secondary pollution. In this paper, Hg2+ and Pb2+ in wastewater were removed and recovered by sulfide precipitation- flotation. Sodium sulfide was used as precipitant and butyl ammonium aerofloat was used as collector. Results indicated that Hg2+ and Pb2+ could be reduce to less than 0.03mg/L and 0.16mg/L respectively by both coprecipitation- floatation and fractional precipitation- floatation. In these two methods, fractional precipitation flotation could not only remove Hg2+ and Pb2+ from wastewater, but also could recover mercury and lead effectively. The infrared spectrograms showed that the adsorption between butyl ammonium aerofloat and mercury precipitate or lead precipitate is chemisorption.

Jan 1, 2015