By I. Iwasaki

Flotation characteristics of pyrrhotite by itself and in complex sulfide ores are reviewed with respect to the effects of oxidation, grinding media and other electroactive minerals.

Jan 1, 1988

By Hongmin Zhu, Guihua Wang, Xiangsheng Wang

"The anode process of carbon electrode in fluoride melt was studied by voltammetry and chronoamperometry. Anode gases were analyzed by gas chromatography on-line during controlled-potential electrolysis. Two peaks were observed on the cyclic voltammograms. According to the results of gas chromatography, the first peak was corresponded to the discharge of residual oxide ions, with the formation of CO and CO2. Discharge of fluoride ions occurred at 4.1 V vs. Li+/Li, and leading to the anode effect. With the occurrence of anode effect, small amount of CF4 was detected. As the potential reached 4.5 V, CF4 and C2F6 gas evolution occurred, and the current increased to form the second peak.1.IntroductionIn the primary production of Aluminum and some rare earth metals like neodymium, a departure from normal cell operation known as anode effect results in the generation of perfluorocarbons (PFCs), which have high global warming potentials [1]. Owing to the pressure of environmental protection, considerable research has been carried out to clarify the mechanism of anode effect and PFC generation of industry and laboratory cells in the aluminum electrolysis system [2-9]. The common result on PFC generation is that the PFCs are emitted from Hall-Heroult cells only when they are on anode effect. In this article, we selected LiF, the main electrolyte for the neodymium electrolysis [10-11], to perform further investigation on the underlying kinetics of PFC generation and the nature of the reactions at the electrode.2. ExperimentalAll experiments were carried out in an alumina tube reactor, which was filled with high purity helium atmosphere. Spectrographic graphite crucibles were used, which played the dual role of molten fluoride container and the counter electrode. Lithium fluoride was analytical grade. The experiments were carried out at 900 °C."

Jan 1, 2011

By Mei Song, Qingyu Deng, Xuewei Lv, Lu Liu, Chenguang Bai, Meilong Hu

"The carbochlorination of several silica materials was carried out in the temperature range from 900 °C to 1200 °C. In this study, silica oxides and gaseous chlorine with carbon as reductant were used. The optimal carbon silica mole ratio in different temperature was calculated by Factsage software and the results showed that the optimal values are 1.2, 1.4, 1.6, 1.8 at 900 °C, 1000 °C, 1100 °C, 1200 °C, respectively. According to the experiments, the chlorination ratios of several silica materials were increased with temperature increasing. In the same temperature, the chlorination ratio of diatomite is the maximum and the chlorination ratio reaches 79%% when C/SiO2 reaches 3 at 1100 °C.1, IntroductionPolycrystalline silicon is the main material to manufacture the silicon polished section, solar battery[1] and high purity silicon wafers[2], also which is the most basic function material of semi-conductor industry, electronic information industry and solar photovoltaic battery industry[3]. The conventional manufacturing process of polycrystalline silicon would be divided into three parts: the improved Siemens method, which was introduced and became the main process to produce the polysilicon products in China. Silane method and fluidized bed method. Silicon tetrachloride and chlorosilans have been employed as by-products in several fields like electronic, telecounications and metallurgy[4-6]• At present, the main applications of silicon tetrachloride include production of trichlorosilane by catalytic hydrogenation, synthesis of fumed silica and ethyl orthosilicate, production of optical fiber grade silicon tetrachloride.The conventional routes for the silicon tetrachloride production have been reported, including the direct chlorination and the chlorination process of ferrosilicon, abandon catalyst and silica[7]."

Jan 1, 2013

By Nozomu Hasegawa

The phase diagrams and microstructures of the slags in the Mitsubishi Continuous Copper Smelting and Converting Process were studied for the prevention of the magnetite troubles such as accretion build-up on furnace hearths and launders, blockages at the melt outlet, slag viscosity increases and so on. According to the results of those studies, the silica and lime contents in the silicate slag at the smelting furnace, and the lime content in the lime-ferrite slag at the converting furnace were changed, resulting in lower and more consistent copper levels in the discard slag, with much less need for operators to clean melt outlets and launders. However, these changes may decrease the desirable amount of accretion-coating inside the furnaces and thereby reduce furnace campaign lives. Therefore, a method of estimating the magnetite level in the melts was developed, and slag compositions and temperatures have been controlled within the appropriate ranges to prolong furnace lives and also prevent magnetite troubles.

Jan 1, 2003

By Peter Brown

The present work involves the study of Chemical Vapor Deposition (CVD) of silicon carbide from the methyltrichlorosilane (MTS) - hydrogen system. A computer program, SOLGASMIX has been employed to calculate the equilibrium compositions of the gaseous and condensed phases in the MTS - H2 system. The results indicate the range of parameters such as temperature, pressure and species concentrations, required to deposit the single phase Sic under thermodynamic equilibrium conditions. A mathematical model for describing the transport phenomena and the rate of deposition of Sic onto a thin rod in a vertically-oriented hot-walled CVD reactor has been developed. Exper iments were conducted using the same operating conditions as those used in the model in order to validate the mathematical predictions. The predicted rates of deposition were found to be in good agreement with those obtained experimentally. The model can be used to study the effects of various operating parameters on the rate of Sic deposition on a fiber.

Jan 1, 1992

By Anne C. Chinellato, Alejandra T. Soria, Nelida L. del Mastro, Amanda C. S. Pereiral, Esperidiana A. B. Moura, Anibal V. Abreu

"This work presents a comparative study of the thermo-mechanical and morphological properties of sugarcane bagasse fiber/HDPE composite treated with electron-beam and gamma radiation. The composite samples obtained by extrusion and injection molding processes were irradiated at 50 and 90 kGy using either a 1.5 MeV electron beam accelerator or gamma irradiator EMI-9, at room temperature in presence of air. The irradiated and non-irradiated samples were submitted to mechanical and MPI tests, differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), scanning electron microscopy (SEM), sol-gel analysis and X-Rays Diffraction (XRD) and the correlation between their properties was discussed. Improvement of the bagasse fiber/HDPE composite properties, using electron-beam or gamma radiation, was found.IntroductionResidues of sugarcane bagasse fiber are widely produced in Latin America and other countries: in Southern Africa, Egypt, South-Eastern Asia, India, China, Australia, Cuba, among other producers, as by-products of the sugar and bioethanol industry. The sugarcane industry in Brazil and Uruguay is well established and expanding with large potential to increase the production of sugarcane bagasse in the next years [1-3]. Although the major portion of the bagasse is currently burnt for energy supply in the sugarcane industry, the disposal of this byproduct is still inefficient and, consequently, it is critical for agricu1ture profitability and environmental protection. Sugarcane bagasse is a lignocellu1ose fiber mainly constituted by around 46 % cellu1ose, containing hemicellu1ose, lignin, fat and waxes, silica and other elements [3, 4]. Studies have reported that sugarcane bagasse can be used to produce thermoplastic polymeric composites with excellent properties for many applications. [5-8]. Based on this survey, the transformation of bagasse into high quality industrial products, such as bagasse-polymer composites, can provide its more effective utilization."

Jan 1, 2012

By Anestis Vlyssides, Elli Maria Barampouti, Sofia Mai, ?postolos Vlyssides

"A new anaerobic reactor variation, the UASB/CO2-stripper reactor was conceived. It consisted of a conventional UASB reactor that recirculated the biogas produced. The sludge characteristics of this system were examined when treating high strength wastewater. From the data collected, it was obvious that the UASB/CO2-stripper system can satisfactorily operate at higher loading rates (25 g COD·L-1·d-1). A pronounced effect on the quality of the granular sludge was observed. The VSS/TSS ratio decreased sharply. A considerable decrease in the mean granule diameter was observed, while the specific gravity of the granules increased. The sludge bed porosity increased significantly leading to a considerable expansion of the sludge bed. These changes in the sludge properties led to a gradual shift of the system towards a fluidized bed process as far as its hydraulic characteristics were concerned.IntroductionIn recent years energy considerations and environmental concerns have increased the interest in direct anaerobic treatment of industrial wastes. The anaerobic method of waste treatment offers, under the present circumstances, a number of significant advantages with trivial or more serious drawbacks over other treatment methods. The major obstacle to the application of the process for this specific purpose is perhaps the difficulty of extending it to a stable and simple operational form. A number of reactor configurations has been developed leading to high biomass concentrations, e.g. the contact process, the filter reactor, the UASB reactor, and the fluidized bed systems, but the process stability problem still remains [1].A prime objective in the operation of anaerobic waste treatment process is the maintenance of a proper pH range. Thus, a possible solution to the process stability problem could be obtained by increasing alkalinity in the anaerobic systems. Therefore, the main objective of this paper is to present and evaluate the results of a system (UASB/ CO2-stripper) with increased alkalinity concentrations."

Jan 1, 2008

By XUEWEN WANG, Xingming Wang, Xuehui Liu, Mingyu Wang

The Panzhihua titanium concentrate contains high contents impurity of Mg and Al, and it is difficult to prepare high grade titanium slag. To solve this problem, a sodium salt roasting-acid leaching process was proposed for removing the impurities in titanium concentrate. Na2CO3 and titanium concentrate were mixed with the proportion of 1:4, and then the mixture was roasted at 700 for 2h. After roasting, the calcine was leached with HCl solution. The experimental results showed that the removal rate of silicon and aluminum can reach more than 85% and 80%, respectively, at leaching temperature of 70 , leaching time of 4h, HCl addition of 5ml and liquid-solid ratio of 4:1.

Jan 1, 2016

By Matthew D. Andriese, Jiann-Yang Hwang, Zhiwei Peng

"It has been demonstrated that metallic-bearing minerals are physically liberated from host rock when exposed to microwave (MW) energy. The metallic minerals are iron sulfides and spinel oxide minerals contained in peridotite rock. Experimental evidence has shown ore particles readily couple with MW energy at 2.45 GHz, 1000 W resulting in rapid heating. Thermal stresses are generated by highly absorbing metallic-bearing minerals resulting in cracking and embrittlement of ore particles that assists in crushing and grinding processes. The liberated metallic-bearing minerals are shown to report to coarser size fractions as a result of MW exposure.IntroductionComminution of ore material during beneficiation is a large energy expenditure for the mineral processing industry. Crushing and grinding operations alone consume 50-70% amount of energy used in mineral processing [1]. Size reduction becomes increasingly difficult with decreasing particle size making grinding the most energy-intensive step of comminution. The aim of comminution is to maximize liberation of economically valuable minerals from the host rock [2]. Overall, the less material that needs to be handled, then grinded, to create a useful product for hydro/pyro metallurgical processes will achieve the greatest reduction of energy.Much of the scientific interest for use of microwave (MW) energy in mineral processing has been for improved hydro/pyro metallurgical techniques [3-6]. Early authors have employed MW energy for improved grinding of ore particles but most conclude the energy savings do not justify the energy input [7-9]. The effectiveness of MW assisted grinding is dependent on the ore mineralogy and the absorptive properties of minerals contained within it. Ore containing magnetic minerals should prove successful with MW assisted breakage from highly absorptive properties."

Jan 1, 2012

Today’s world relies upon advanced green technologies that are made of critical elements with unique properties. Examples include rare earth elements (REEs) that are critical in the manufacturing of wind turbines and electric/hybrid vehicle batteries, key components of a greener future that face supply uncertainty and near zero recycling. To tackle their supply challenges, activities have begun for urban mining from waste electrical and electronic equipment (WEEE) that contain considerable amount of REEs, but their current level of recycling is less than 1%. Current recycling practices use either pyrometallurgy, which is energy intensive, or hydrometallurgy that utilizes large volumes of acids and solvents and generates large volumes of hazardous waste. In this study, we developed a novel and sustainable process to recycle REEs from WEEE, NiMH batteries in particular. The developed process relies on supercritical fluid extraction (SCFE) utilizing CO2 as the solvent, which is abundant, safe, cost effective, and inert. The effect of seven operating parameters, namely temperature, pressure, residence time, sample to chelating agent ratio, agitation rate, complex formulation, and methanol addition on REE extraction efficiency was investigated, and optimum operating conditions were determined. This work is the first to utilize a very efficient and safe process that runs at low temperature to extract metals from postconsumer products with minimum hazardous waste generation, while offering about 90% leaching efficiency for REEs. We expect our process to find widespread applicability in urban mining of REEs using green chemistry.

By C. M. Iheagwara

This paper has addressed the issues that constitute major obstacles to the cost- effective and efficient operation of metallurgical vessels from the refractory standpoint. Refractories generally withstand severe conditions of high temperature reactions as well as physical loading/impingement and hence degenerate and need replacement. Scarcity of some refractory materials especially high alumina and magnesite ores in some places, the prohibitive cost and the frequency of replacement of damaged refractories threaten the continued support for metallurgical operations. Some of the causes, prevention and cure for refractory wear have been discussed and rational strategies (short and long term) have been recommended which if implemented should go a long way towards arresting the perennial problems they portend.

Jan 1, 1991

By Munyaradzi Kwatara, Ron Schonewille, Edgar Peek, Juzer Tayabally

"The potential recovery of nickel from a South-American saprolitic laterite ore using the segregation roasting technique was investigated. The ore was heated to temperatures that ranged between 900 and 1 000°C in a rotary kiln. In all the tests, the laterite ore was first mixed with a predetermined amount of calcium chloride and either coal or coke. By varying the temperature, calcium chloride and reductant in the different tests, a preliminary set of optimal conditions was established for the specific laterite ore that was tested. A combination of chemical analysis and electron-probe-micro-analysis (EPMA) were used to determine and evaluate the effectiveness of segregation roasting on the recovery of nickel. The present paper describes the test procedure and the results that were obtained.IntroductionIt is known that laterite ore resources account for an estimated 72% of the world's nickel resources, with sulfide sources accounting for the remaining 28%. Yet sulfide resources account for 58% of the world's primary nickel production while laterite resources account for the remaining 42% [I]. There are numerous reasons for this discrepancy, but the most important one is the mineralogical and compositional complexity that is associated with laterite ore deposits. For example, this complexity currently offers only limited opportunities for upgrading, thereby creating capital intensive whole ore processing facilities. It then follows logically that the identification and application of a low-cost processing option for the treatment of laterites could potentially open up an opportunity for exploiting these vast untapped laterite resources.To this end, a preliminary screening investigation was initiated by Xstrata Process Support to evaluate the potential application of the so-called (nickel) segregation process as a unit operation that could potentially be integrated into a laterite processing flow sheet. Laboratory bench tests were performed on this segregation process and this paper details some of the findings from this preliminary investigation."

Jan 1, 2011

By Georgette Smits

The gun-sprayed refractory lining of electrothermal furnaces used for the manufacture of carbon disulphide from liquid sulphur and charcoal at between 800 and l000°C are severely attacked during the process. A mineralogical study of samples of eroded refractory material disclosed that carbon disulphide had penetrated the lining, causing the precipitation of sulphides and carbon, and the decomposition of mullite, a major constituent of the lining, to corundum and amorphous silica. Calcium, iron, titanium, and chromium are undesirable cations in a refractory that is used in furnaces for the production of carbon disulphide, since they react readily with this substance. A series of tests, in which samples were exposed to different amounts of carbon disulphide for various residence times and at different temperatures, was carried out with eight types of aluminosilicate-based castable and brick refractory materials, to compare their resistance to attack by carbon disulphide. Mineralogical investigation of the test cores showed that castable refractory materials are unsuitable for this type of process because of the presence of calcium aluminates and other impurities in the cement. Of all the refractories that were tested, a mullite brick of low porosity, containing a minimum amount of impurities, appeared to be the most suitable for use in this type of operation.

Jan 1, 1989

By Alexander V. Derevyanko, Victor P. Popov, Alexander I. Raitchenko

"If an electric current flows along some electroconductive suspension in columnar form the solid particles are 'experienced thermal, mechanical, and electromagnetic influences.The objects were suspension Sn (liquid) - Ni-Cr-Mo-W alloy (solid particles). This is refractory alloy on the Ni base. The direct constant current (with density -106 A/m2 ) flowed through the named suspension during 180+300 sec. At the beginning of experiments samples were ones containing particles suspended uniformly in volume. Although density of solid particles was ~9x103 kg/m3 , i. e. higher than density of liquid Sn (-6.8x103 kg/m3 ), after end of this processing, the non-uniform distribution of particles in volume of samples was observed: concentration of Ni-alloy particles in lower part was smaller than their concentration in upper part of samples, and simultaneously their concentration is increased near outer surface. There was probably the natural convection of Benard-Rayleigh type which had carried, so lid particles upwards, and, in same time, there was the action of spatial Lorentz-forces directed to center forcing the radial movement.The knowledge of named phenomena can be useful for elaboration of technology of gradient dispersed materials and development of some materials science fields.IntroductionThe liquid metal with the electric current or under the alternating magnetic field is experienced compression. This action causes the pressure within metal and the change of the surface of the metal column (see, for example, [1-4]). One of results of such an electromagnetic compression is extraction of the foreign solid particles from a cylindrical liquid sample to surface in the radial directions. However, more complicated paths of the inclusions are observed under some conditions of electric treatment."

Jan 1, 1999

By Richard L. Werner

The petrographic microscope as a tool in determining impurities and grain size of limestones, clays, sand and coal ash for possible use as raw materials is discussed. Its use in the determination of the mineral composition of various size fractions of the raw mix, after fine grinding in ball mills, and of the waste dust from the rotary kiln. A description is given of the typical clinker crystals; alite, belite, tricalcium aluminate and ferrite. The process problems indicated by various changes in the crystal characteristics are listed with possible solutions. Finally the microscope as used in relation to field problems with concrete such as air void volume, percent hydration of the cement, cement aggregate bonding and the determination of solid additives, is presented.

Jan 1, 1982

By Rush Kramer

A bulk compositional chemical analysis often provides incomplete information to help the mineral processor when faced with the problem of removing troublesome contaminants in low concentrations. Michigan Tech has developed a unique approach for addressing this problem. A combination of Scanning Electron Microscopy (SEM). Energy Dispersive Spectroscopy (EDS). and image analysis was successfully used to characterize the species responsible for phosphorus contamination of less than .05 weight percent in iron ore. An automated routine acquired the chemical signature of each particle on a backscattered electron image. The few particles containing phosphorus were identified from the hundreds of particles examined. and the phosphate phases present were easily characterized.

Jan 1, 1991

By J. E. Murphy

Neodymium was electrowon into a Mg-Cd molten cathode at 650 °C from NdC1,-KC1 electrolyte. With the chloride system, neodymium was deposited into the molten alloy cathode until the neodymium concentration reached 20 wt pct. The alloy was then vacuum melted to remove the Mg and Cd. The current efficiency exceeded 80 pct under optimum conditions and the purity of the metal was 99.9 pct after vacuum melting. As an alternative approach, neodymium was electrowon at 1,030 °C from Nd,O, dissolved in a molten fluoride eleotrolyte. With the oxide-fluoride electrolyte, the metal was electrowon in a molten state with current efficiencies up to 60 pct. The purity of the metal was 99.8 pct with oxygen and carbon as major impurities. A number of problems were encountered including anode effect, low oxide solubility in the electrolyte, high neodymium metal solubility in the electrolyte, and reactivity of the metal with the cell materials. Approaches to improved cell, operation and prospects for commercial adoption of the electrolytic production of neodymium metal are discussed.

Jan 1, 1995

By C. Carreno, A. D. Gonzalez Escarcega, M. A. Neri, A. Martinez –Villafane, O. Cobarrubias-Alvarado

"Waspaloy is a superalloy used to manufacture some aeronautical parts subjected to high temperatures and stresses. During thermo-mechanical processing cracks are generated, causing some parts to be rejected. In order to determine the causes of these cracks, this alloy was characterized using techniques such as chemical analysis, optical microscopy, scanning electron microscopy, and EDX analysis. Heterogeneous grain sizes in the microstructure cause a non-uniform strain distribution in these parts, creating cracks in zones with different grain sizes.IntroductionNickel-base superalloys are important materials for high-temperature service applications. The manufacture of components from these materials is typically based on solidification or powder-metallurgy processes [1]. Solidification techniques comprise either the direct casting of parts or the casting of ingots which subsequently undergo a series of thermo-mechanical-processing steps to refine the microstructure. During solidification, microsegregation is usually unavoidable. The primary solidification product is a disordered nickel solid solution with an fee crystal structure (?). In many alloys, the material which solidifies last is a mixture of ã and an ordered fee phase (? '). In prototypical nickel-base superalloys, the ?'-phase is Ni3(Al,Ti) [2-3].Waspaloy is a superalloy that is used in demanding high-temperature environments in which good creep and fatigue resistance are required. One of the most common applications of Waspaloy is for turbine engine rings. To ensure the required mechanical properties, the rings are usually forged and heat treated (Figure 1). Two distinct types of microstructures are usually found to be attractive for such applications: a) A microstructure with a grain size of ASTM 10 to 14 for tensile strength, ductility, and resistance to crack nucleation in low-cycle fatigue; or b) A microstructure with a grain size of ASTM 4 to 8 required for creep strength and resistance to crack propagation [4]. Because it is impossible to refine the grain size through heat treatment, a skillfully designed forging process is crucial for the control of the grain size and, hence the properties of the forged ring [5-6]."

Jan 1, 2012

By Eduard Ouerra, Nuo Jin

"The use of polytetrafluoroethylene, PTFE, as a solid sorbent for elemental sulfur during pressure oxidation of chalcopyrite was investigated. The effects of agitation, PTFE particle size and lingin sulfonate addition were evaluated using leaching conditions that were otherwise similar to those employed in the CESL process. The effects of these factors and their interactions on chalcopyrite oxidation are explained in terms of interfacial forces and solid-solid interactions. Using relatively fine PTFE powder with vigorous agitation resulted in about 100% copper extraction in less than 90 minutes without the need for grinding of the flotation concentrate.IntroductionThe extraction of copper from sulfide ores has always been dominated by the conventional pyrometallurgical smelting process. Though much effort has been made to develop various hydrometallurgical processing routes, smelting remains as the dominant process, treating approximately 80% of the chalcopyrite concentrates worldwide [1]. However, some of recently emerged techniques for treating chalcopyrite through hydrometallurgical routes are showing results that are competitive with smelting in terms of economical feasibility. Representative methods include: Activox Process, CESL Process, Anglo/UBC Process, High Temperature Pressure Oxidation, and Bio-Oxidation. Among these, the CESL processes operate at a medium temperature range (typically 140-150GC) and oxygen pressure of 100 psi, with chloride as a catalyst, and reportedly achieve copper extractions of about 95% with a light regrinding of flotation concentrate to a p95 of 45 ìðé [2]. In spite of this satisfactory extraction result, the leach residues contain significant amounts of conglomerates which contain a small amount of unreacted concentrate [2], The conglomerations are formed because the elemental sulfur generated is liquid and sticky (melting point of sulfur being 119°C), and has a tendency to wet the sulfide mineral surface, a fact which inhibits the oxidation of the minerals. The overall process chemistry of the CESL process may be summarized as follows [3]:"

Jan 1, 2012

By Hideki Yamamoto, Shigeno Matsumoto, Junji Shibata

"Some fundamental studies were carried out in order to produce composite powders comprising of two or three metal oxides ~y using liquid-liquid extraction and to develop the control technology of the particle size. The combination of samarium and cobalt was selected as the two component composite powders. Both stripping and crystallization occurred at the same time by emulsifying the organic phase loading the two metals extracted with Versatic Acid 10 and the aqueous solution containing oxalic acid. The effect of aqueous pH, oxalic acid concentration and agitation speed was examined on some properties such as crystallization percent, particle size and shape of each metal oxide powders obtained in this process. The analysis by using EDX showed that the two metal oxides were distributed uniformly.IntroductionComposite metal and metal oxide powders with high purity are indispensable as industrial materials in the fields of electrical engineering, electronics and metallurgy. It is difficult to mix metal powders or metal oxide powders uniformly for the production of alloy powders. If insoluble metal salts are allowed to collect as crystallization products in the crystallization-stripping process, the conventional melting and crushing process can be avoided. After mixing of the organic phase containing metals in fixed composition, fine metal and metal oxide powders of alloy composition are produced by using a crystallization-stripping method. Versatic Acid 10 and D2EHPA, both acidic extractants, were chosen in this experiment, and the metal oxide powders were produced by using oxalic acid as a crystallization reagent. Mixed metal oxalates containing samarium and cobalt were precipitated from the mixed organic phase containing these metals. Furthermore, the physical properties of the powders, such as particle size, shape and thermal decomposition, were measured in order to evaluate them for industrial purposes."

Jan 1, 2000