By N. Kanari

The thermal decomposition studies of two zinc basic carbonate samples were carried out up to 400 "C by thermogravimetric analysis, boat experiments and differential scanning calorimetry measurements 'DSC'. The initial samples and the solid decomposition products were analyzed by scanning electron microscopy, x-ray diffraction and laser particle size analyzer. The thermal decomposition of both samples started at about 150 "C and the rate of decomposition became significant at temperatures higher than 200 "C. The apparent activation energies 'Ea' in the temperature range 150-240 "C for sample decomposition were between 132 and 153 kJ1mole depending on the sample origin. The XRD analyses of the intermediately decomposed samples and the DSC results up to 400 "C suggest that the decomposition reaction probably occur in a single step.

Jan 1, 2002

By Jorge Alberto Soares Tenório, Romano Espinosa, Felipe Fardin Grillo, José Roberto de Oliveira, Denise Crocce

"The aim of this work was evaluation of the recovery of Zn and Fe of the EAFD added to the hot metal in the form of briquette at temperature of 1500°C. The EAFD was agglomerated by cold briquetting and introduced in the hot metal. This study utilized a bench-scale equipment to melt, during this process to kept a flow rate of inert gas above the bath. Were collected periodically metal samples and the samples were analyzed for determination of the content of total silicon and carbon by chemical analysis. Zinc oxide, zinc ferrite and other oxides were reduced and were volatized and collected by a cleaning system of dust (baghouse) located on top of the oven. More than 98% of iron were recovered from EAFD during the test. It was possible to produce a dust containing about 68% zinc by means of adding of EAFD.IntroductionIn the first semester of 2010, steel production was about 706 million tons, 27.9 % more than in the first half of 2009. Not a significantly increase if 2010 data is compared with the first semester of 2007 (only 7.2 % higher), before the world’s economic crises. Steel production is divided into two main routes. The first one, and most used, is the Basic Oxygen Furnace Process (BOF process), which in 2008 accounted for approximately 67.1 % of steel production. The second route is carried out in the Electric Arc Furnace (EAF) that in 2008 represented 30.6 % [1 ].Electric arc furnace dust (EAFD) is a solid waste generated during the steel making process. It is classi?ed according to NBR 10004 as dangerous solid waste-class I, because the elements Pb e Cd leach in water exceeding the maximum limits permitted by the NBR 10004 [2 ]."

Jan 1, 2012

By Larry G. Twidwell, Jannette L. Chorney, Bryce D. Ruffier, Katelyn M. Lyons, Daniel W. Gaede, Ryan J. Foy, Jerome P. Downey

The Army Research Laboratory (ARL) has an interest in the recovery and processing of rare earth elements. At Montana Tech, elevated temperature chlorination of rare earth oxides is presently being investigated as a potential methods leading to the selective separation and recovery of rare earth elements from mineral ores and concentrates. After preliminary evaluation, ytterbium oxide was selected as a representative surrogate material for more extensive chlorination studies. Methods used to determine the conversion and recovery include X-ray diffraction (XRD) and inductively coupled plasma (ICP) analysis. These data have been used to establish and confirm process conditions that consistently yield high conversion efficiencies. Based on the promising results, further experimentation is underway to ascertain the metallurgical response of other rare earth oxides and carbonates to the roasting process. The end goal is to create a robust process for industrial application that has greater efficiency and reduced costs as compared to current practice.

Jan 1, 2015

By Ajay K. Singh

The surface quality demands for galvanized and galvannealed steel sheets by the automotive and appliance industries have been getting increasingly stringent over the past few years. Intensive efforts by Hot-Dip-Galvanizers to meet these demands have resulted in substantial improvement to the hot dip coating process. However, elimination of zinc bath contaminants which directly affect the coated strip surface quality continues to remain a tough challenge. As part of our effort to improve the zinc bath cleanliness, Inland Steel Company has developed a test method to quantitatively measure the contaminants in incoming zinc spelters and establish a specification for incoming zinc quality. The test is currently being used for auditing the incoming zinc quality. The zinc suppliers are also using this test for quality control purposes. The purpose of this paper is to describe the test method and how it has improved the galvanizing operation at Inland.

Jan 1, 1992

By Bora Derin

The partial pressure ratios of sulfur and oxygen for several copper flash smelting plants were derived using the Reddy-Blander (RB) model and predicted dissolved sulfur contents available in the literature. The sulfide capacities (Cs) of six different flash smelting plants (FeO-CuOo.5- CaO-MgO-FeOu-AlO15-SiO2) slags were calculated. The log (PO2/PS2) versus matte grades of various industrial processes was determined. The PO2/PS2 ratio increased with an increase of copper grade. The calculated partial pressure ratios for the copper flash smelting are in good agreement with those of the experimental data.

Jan 1, 2003

By H. Y. Sohn

The purpose of this article is to analyze critically and quantitatively the effect of chemical equilibrium on the overall rates of fluid-solid reactions. It is shown through a mathematical analysis that a reaction with a small equilibrium constant (a positive standard free energy of reaction) is more likely to be rate-controlled by pore diffusion or mass transfer than a reaction with a large equilibrium constant. The overall reaction rate of the former also tends to be slow. Furthermore, the apparent activation energy of such a reaction approaches the standard enthalpy of reaction (M-f'), rather than the true activation energy of the chemical reaction. The Law of Additive Reaction Times developed by the author is shown to apply to equilibrium-limited fluid-solid reactions and to be useful in quantitatively analyzing the behavior of such reactions.

Jan 1, 2003

By May Nyman

Due to the vast diversity of chemical media in which metal separations are executed, a wide range of ion separation materials are employed, This ,results in an ongoing effort to discover new phases with novel ion exchange properties. We present here the synthesis of a novel class at, thermally and chemically stable microporous, niobate-based materials. Ion exchange studies show these new phases are highly selective for Sr2+ and other bivalent metals.

Jan 1, 1999

By H. Y. Sohn

The purpose of this article is to analyze critically and quantitatively the effect of chemical equilibrium on the overall rates of fluid-solid reactions. It is shown through a mathematical analysis that a reaction with a small equilibrium constant (a positive standard free energy of reaction) is more likely to be rate-controlled by pore diffusion or mass transfer than a reaction with a large equilibrium constant. The overall reaction rate of the former also tends to be slow. Furthermore, the apparent activation energy of such a reaction approaches the standard enthalpy of reaction (Mf'), rather than the true activation energy of the chemical reaction. The Law of Additive Reaction Times developed by the author is shown to apply to equilibrium-limited fluid-solid reactions and to be useful in quantitatively analyzing the behavior of such reactions.

Jan 1, 2003

By I. Perus, M. Fazarinc, G. Kugler, M. Tercelj

"Ledeburitic tool steels are highly alloyed steels used for specific highly loaded applications but are characterized by low and variable hot workability. In this contribution the importance of selecting the right choice of some essential process parameters, i.e. casting temperature, solidification rate and soaking temperature, needed for improving the intrinsic hot deformability of ledeburitic tool steels, is studied. An inappropriate selection of casting temperature and cooling rate results in precipitation of unusual eutectic carbides that decreases the hot workability, whereas with the selection of appropriate soaking temperature the temperature range of safe hot working can be broadened. For each initial as-cast microstructure individually determined soaking temperature should be selected.IntroductionThe surface cracking during hot deformation of ledeburitic tool steels reduces mechanical properties and their industrial yield. These tool steels have high hardness, wear resistance and high tempering resistance on one hand, and high flow stresses and low hot deformability on the other. Decreased hot deformability of the tool steels is attributed to the type, size, shape, distribution, fraction of eutectic carbides and/or other phases, grain growth, etc. at upper limit while precipitation of secondary carbides and decreased recrystallization rate at lower limit of the safe hot deformation temperature range, [1-6].The occurrence of cracks on most exposed areas of workpiece are related to the areas where similar conditions related to upper and/or lower limit of temperature working range prevail, i.e. areas with accelerated cooling, areas with higher value of accumulated strains where also decreased recrystallization rate with simultaneously presence of higher tensile stresses takes place, furthermore areas of workpiece which are due to combustion conditions in furnace heated to higher temperatures, etc. Thus the areas, where combination of previously mentioned conditions prevails, are more exposed to cracking. This additionally requires that hot deformability of ledeburitic tool steel should be considered as a complex problem. Publications in the literature with regards to hot deformability of tool steels are predominately of a partial nature thus all reasons for unexpected occurrence of cracks are not sufficiently explained in available literature so far. Furthermore modern practice proves that previous processing parameters significantly influence the hot deformability and thus this cannot be considered as a constant value. During heating, soaking and hot deformation various processes take place: decay (decomposition) of carbides, formation of new carbides, dissolution of carbides and of alloying elements, etc. Thus depending on variation of process parameters and chemical composition, that consequently influences the processes related to carbides, shifting of decreased deformability at both limits of temperature working range to higher and/or to lower temperatures can occur, [1-14]."

Jan 1, 2012

By Keiji Toyabe

Several purifying techniques have been developed for controlling the impurity levels in the copper electrolyte at Niihama Copper Refinery. These have been carried out as follows; i ) the study of the reaction in liberation made it possible to raise the current efficiency for arsenic removal by more than 50% and to decrease generation of arsine sharply. By applying this method, a good performance was attained at commercial operation. li) the antimony in the electrolyte can be successfully removed by contacting it with activated carbon. This procedure is applicable particularly when there is a large amount of antimony in the copper anode. lli) for the nickel sulphate recovery from the electrolyte, an electric evaporating system was developed. The characteristics of this process are, capability of continuous operation with less manpower, the high recovery ratio of nickel sulphate (more than 85% as nickel) and no black acid formation in the treated solution.

Jan 1, 1987

By D. M. Jones

Dust generation data have been obtained from 19 industrial Outokumpu flash furnaces. Statistical analyses of the data have been carried out and the most significant factors affecting dust generation evaluated. The results indicate that dust production may most effectively be minimized by: 1) Minimizing the distance between the molten slag and the furnace roof 2) Optimizing burner design and combustion parameters.

Jan 1, 1996

By Takahiko Okura

Most non-ferrous raw materials are associated with sulphur. To extract the metals, the sulphur is recovered typically as sulphuric acid or liquid SOz, On the other hand, natural gas may contain over 20% of hydrogen sulphide (HzS) and a huge quantity of elemental sulphur is produced through oil and gas refining processes in the world. A large fraction of the sulphur mined from natural sources is eventually returned to the earth as fertilizers, by-products of desulphurisation and neutralisation processes, or as fugitives to the atmosphere. However, the supply and demand for sulphur are in imbalance. Such situation urges to develop a new smelting process without sulphuric acid production. This paper briefly reviews the global sulphur balance and the technologies for recovering elemental sulphur. The core of this paper is a proposal to convert SO2 gas to elemental sulphur by using organic materials. Some results of thermodynamic calculations and experiments are presented.

Jan 1, 2003

By Junzo Hino

Most of the waste that contains a small portion of copper is landfilled. The recycling process of copper from the waste, such as shredder residue, should be developed in order to save mineral resources and prevent environmental pollution. Shredder residue, generated from disposed automobiles and electric appliances, consists of many types of plastics, glasses and metals. The combustion heat of plastics is efficiently used for smelting in the recycling process that consists of melting and reduction. Because the waste contains numerous components the knowledge of the distribution behaviors of the main components is necessary to develop the recycling process. The distribution behaviors in the recycling process are evaluated by using the thermodynamic calculation program, HSC Chemistry. The calculation results are compared with the practical operation data of the recycling process and discussed.

Jan 1, 2003

By V. I. Lakshmanan

Wastes when produced can be reused or recycled prior to disposal. Industries that cause environmental concerns during manufacturing include primary materials and primary metals. Pollution prevention mechanisms to achieve waste reduction require new separation, reclamation, control and process simulation technologies. Substituting recyclables for virgin resources will reduce energy use, water pollution, air pollution, water use and mining wastes. Shrinking landfill space will spur new technologies for waste treatment and recycling. These situations hence offer opportunities for innovative flowsheets with appropriate separation technologies. Development of innovative flowsheets to treat recyclables offer unique opportunities for process/product development, obtain green products and hence market advantage. The paper will illustrate with selected innovative flowsheets to treat recyclables.

Jan 1, 1996

By Singareddy R. Reddy, Ramana G. Reddy

"The Margules equation is used for interpreting excess Gibbs energy of several ternary systems. An expression for the activity coefficient of a dilute solute, 2(oxygen), in a binary solvent 1-3 is derived. It is used to calculate the logarithmic activity coefficient of oxygen in Pb-O-Gu, Pb-O-Bi, AgO- Sn, Pb-O-Sn and Ag-O-Pb metallic systems. Self interaction parameter of the solute is derived from the partial Gibbs energy of solute using constant compositional path. The derived equation is used successfully to deduce the self interaction parameter of oxygen in Pb-O-Gu and Pb-O-Bi metallic systems. The predicted thermodynamic parameter data i.e activity coefficient and self-interaction parameters are in an excellent agreement with the experimental data and also our predictions are far more accurate than the predictions made by other models.1 IntroductionThe nature of solute interactions such as oxygen, nitrogen and sulfur with the metallic solutions are important for a number of chemical and metallurgical processes. Several theories [1-23] have been developed to evaluate fundamental thermodynamic properties of solutes constituting two elements. The activity of solutes has been calculated using statisticalor quasi- chemical approach.Wagner's [4] Ideal Solvent Model is based on one energy parameter to describe the compositional dependencies of the activity coefficient of nonmetallic solutes such as oxygen in binary metallic solutions. This model depends on a constant energy of interaction for the exchange of atoms from the coordination shell of an oxygen atom to the shell of an interstitial site and cannot account for properties of strongly interacting systems [4]. Therefore, several attempts have been made to improve the Wagner's model for the strongly interacting systems. [10-16]."

Jan 1, 1996

By Tiejun Chun, Jian Pan, Deqing Zhu, Zhiyong Ruan

"In this paper, the desulfuration of pyrite cinder pellets was carried out. Phase analysis shows that most sulfur of pyrite cinder exists in the form of elementary sulfur. Most sulfur was removed in preheating stage. 81.25% sulfur was removed and the average SO2 concentration of exhaust gas was 1365ppm when the pellets were preheated at 950oC for 9 min. The final product, assaying 62.42wt%Fe and 0.02wt%S content at 96.88% desulfuration was achieved under the conditions of preheating at 950? for 9 min and roasting at 1200? for 15 min, which can be used as the burden for blast furnace.IntroductionPyrite cinder, as a subsidiary product of sulfuric acid production by roasting of pyrite ores, was solid waste in sulfuric acid enterprises. According to the statistics, the annual production of pyrite cinder is about 15 million tons in China. Besides, there is lots of pyrite cinder deposited for many years [1-3]. The pyrite cinder consumed in the cement and other industries as auxiliary additives only accounts for less 30% of its total discharge and the left is stored in waste pond, occupying much land and polluting environment in China [4-5]. Moreover, pyrite cinder contains iron between 30-63% which can be utilized as a cheap raw material for ironmaking by sintering or pelletizing processes, which can not only prevent pollution but also provide cheap raw materials for ironmaking [6-7]. However, compared to traditional iron ore concentrate, pyrite cinder possesses higher sulfur content."

Jan 1, 2012

By Ki Joo Sim, Sung Beom An, Joonho Lee, Minsoo Shin

Valorization of the electrical arc furnace oxidizing slag by coke was carried out by the reduction of iron oxide in the slag. Since the reduction of iron oxide by solid carbon is an endothermic reaction, supply of heat energy is required. In addition, slag has a low thermal conductivity; traditional fuel injection is not suitable for this reaction. Microwave can be used to supply heat energy to the system. Commercial oxidizing slag was reduced by coke under the microwave irradiation (1.7 kW, 2.45 GHz). The maximum recovery ratio of iron was 87%. In addition, slag composition modification was attempted to use the remaining slag for a mixture in cement clinker. Free-CaO in the slag was successfully suppressed, and the use of the remaining slag as a potential mixture was confirmed.

Jan 1, 2014

By Baozhong Zhao

Experimental results have shown that fluxing with soda ash (Na:zC03) can remove As and Sb from molten copper at the rate of As>Sb, but is relatively ineffective in removing Hi. The rate of impurity removal is controlled by impurity mass transfer in the metal phase. In this paper, a mathematical model was developed to describe the impurity removal phenomena. The model incorporates the effects of molten bath mixing intensity, soda ash feeding rate, oxygen content in the molten copper and soda ash fluxing by surface addition and injection. The model predictions are in good agreement with experimental results and may be used in designing large scale tests.

Jan 1, 1996

By Zhao wen Wang, Ramana G. Reddy, Min Li

"The electroreduction of Co(II) in l-butyl-3-methylimidazolium tetrafluoroborate (BMlMBF4) ionic liquid was investigated by cyclic volatrnmetry at 353 K. The results show that the reaction of Co(II) to Co is irreversible in one step with two electrons transferred. The diffusion coefficient of Co(II) was estimated to be 7.6 x 10-8 cm2 s·1 at 353 K. Then the electrodeposition of cobalt was studied at different cathodic potentials (-0.80 to -0.95 V) and different temperatures (333 to 363 K) in BMIMBF 4 containing 0.20 mol L-1 Co(BF4)z. The deposits were characterized using scanning electron microscope (SEM), energy-dispersive spectroscopy (EDS), and X-ray diffraction (XRD). SEM images show that a uniform, dense, and compact deposit was obtained at -0.80 V and 333 K. The deposits were identified as high-purity metallic Co for all experiments by EDS and XRD.IntroductionCobalt is known as a hard magnetic material and cobalt alloys have been shown to have excellent magnetic properties with adequate mechanical durability and corrosion resistance, which are needed for high performance magnetic recording applications [1-4]. The electrodeposition of Co alloy in the aqueous solution is generally difficult because of the narrow electrochemical potential window of water, which leads to the low current efficiency and worse quality of deposits due to the hydrogen embrittlement. Thus, aprotic ionic liquids (ILs) are expected to be the ideal alternative media for electrodeposition of cobalt or its alloy since ILs usually provide a wide working potential windows, negligible vapor pressure, and acceptable conductivity for electrolysis without the occurring of hydrogen evolution [5, 6]."

Jan 1, 2014

By J. D. Budai, D. H. Lowndes, D. P. Norton, D. K. Christen, B. C. Chakoumakos, J. R. Thompson, B. C. Sales

"Artificially-layered structures, consisting of (Sr,Ba,Ca)CuO2 layers in the tetragonal, ""infinite layer"" crystal structure, have been grown by pulsed-laser deposition. Superlattice chemical modulation is observed for structures with SrCuO2 and (Sr,Ca)CuO2 layers as thin as a single unit cell (~3.4 Å). In addition, novel thin film superconductors were formed by using the constraint of epitaxy to stabilize SrCuO2/BaCuO2 superlattices in the infinite layer structure. Using this approach, two new structural families, Ba2Srn-1CUn+l O2n+2+ d) and Ba4Srn-1CUn+3O2n+6+ d, have been synthesized which superconduct at temperatures as high as 70 K. These results represent not only the synthesis of new structural families of superconductors, but also demonstrate that pulsed-laser deposition and epitaxial stabilization can be effectively used to engineer artificially-layered thin-film materials.Advances in the understanding of epitaxial thin-film growth of the cuprates have heightened interest in creating artificially layered superconductors.(1-3) The layered structure of the copper oxide superconductors opens the possibility of forming novel materials by carefully controlling the epitaxial growth of sub-units of the crystal structures. Thin-film growth methods offer unique opportunities for the atomic engineering of new high-temperature superconducting (HTSc) materials through the ability to form artificially layered crystal structures.(4,S) Moreover, the surfaces of single-crystal substrates provide an ""atomic template"" that can be used to stabilize epitaxial films in metastable crystal structures.An important development in forming new HTSc compounds by artificially-layered epitaxy has been the epitaxial growth of (Sr,Ca)CuO2 films in the so-called infinite layer structure.(6-17) This material, which can be considered the parent compound of all of the copper oxide superconductors, has a relatively simple, layered structure consisting of CUO2 planes separated by planes of alkaline earth elements.(18) Bulk synthesis of (Sr,Ca)CuO2 with the tetragonal, infinite layer structure generally requires the use of high pressure and high temperature bulk processing techniques.(19-24) However, recent experiments show that this metastable compound can be epitaxially stabilized at less than atmospheric pressure, resulting in the growth of tetragonal (Sr,Ca)CuO2 single crystal thin films of the infinite layer defect perovskite structure by pulsed-laser deposition (PLD) over a wide range of growth conditions.(6-17)"

Jan 1, 1994