By E. F. Vegman, Ndabezinhle Dube

"In the practice of conventional sintering, production is always afflicted with the problem of being unable to get a uniform quality of produced sinter in the bed. Invariably the top layer of the sinter cake is composed of weak but highly sinter, while the bottom layer is over-fused, forming a sinter that is very strong but less reducible. These symptoms point to a variable distribution of the heat balance in the process of sintering which results in a deficit of heat in the top layers of the sinter bed and an excess of heat in the bottom layers, due to an increasing input of regenerated heat in the heat balance down the bed. This causes losses in the productivities of the sinter machine and the blast furnace.The current work was designed to improve on the solution to the above problem through the establishment of a more accurate combustion zone heat balance of the sintering process. This development is mostly on the method of determining the regenerated heat input in the overall heat balance. Previous methods were based on the assumption that the width and the velocity of the combustion zone remain constant through out its whole life, which is not the case since tests have shown that both its width and velocity increase as the combustion zone moves down the bed. In this work, these factors have been taken into account. Tests and calculations using the model were carried out for haematite and limonitic ores. The high sensitivity of the model to changes in the sinter mix composition and sintering conditions was demonstrated.The results present the following prospects:• The minimum theoretically possible coke breeze consumption during the sintering of any type of iron ore fines, under any sintering conditions, can be established.• The model can be used to control the metallurgical quality of the sinter in any point in the sinter bed since calculation data includes desired basicity, combustion zone temperature and FeO content in the sinter produced."

Jan 1, 2001

By Y. Z. Zhang

Cyanide has generated environmental concerns because of its toxicity, and it may not respond to the treatment of complex and refractory gold ores. Gold leaching by thiourea is one of the most promising substitutes of cyanide. However, the high reagent consumption has hindered thiourea from its commercial application in gold extraction. The process chemistry and mechanism of thiourea degradation has been discussed on the basis of chemical bonding theory, thermodynamics and electrochemistry in this paper. Progresses on the decreasing of thiourea consumption have been summarised. The potential application of thiourea in gold extraction has been evaluated.

Jan 1, 1996

By Jan Vrestal, Josef Tomiska, Pavel Broz

"Thermodynamic investigations on fcc solid ternary Fe-Ni-Cr alloys have been performed by means of the computer-aided Knudsen cell mass spectrometry. Ternary T.AP.-series (Thermodynamically adapted power series) are used for the algebraic representation of the thermodynamic excess properties. At 1650 K the molar excess Gibbs energy GE is negative over the whole field of stable fcc phase. The molar heat of mixing HE is exothermic in the predominant part of the fcc phase field. Only between the section with a constant ratio of mole fraction Xcr/XNi = 0.64 and the fcc phase field boundary the HE values are slightly endothermic. The results of this work can be used successfully for phase diagram calculations.IntroductionThermodynamic investigations on multicomponent alloy systems such as the Fe-Ni-Cr ternary system including the three binary boundary systems are very time-wasting and usually beset with considerable experimental difficulties. Additionally, the required experimental equipment is very expansive and the obtained results are not always satistying. Therefore it is understandable that many phase diagram calculations are based only on few experimental values of the molar excess free Gibbs energy GE. Consequently, Kundrat and Elliott [1] as well as Hillert and Qiu [2] used in their reassessments of the phase diagram of the Fe-Ni-Cr system thermodynamic data mainly assumed and/or optimized by means of various reasoning.Lee [3] reported recently, a revision of the used thermodynamic description of the Fe-Ni liquid phase is necessary to obtain a better agreement with the experimental data on the bcc/liquid or fcc/liquid tie lines and liquidus temperatures in the Fe-rich region of the Fe-Ni-Cr ternary system than in the previous assessments. This is 'in full agreement with mass spectrometric investigations of Fe-Ni alloys in the liquid and in the fcc solid phase, published earlier [4,5]. Indeed, phase diagram calculations based upon the molar excess free Gibbs energies GE obtained in these studies yield liquidus and solidus lines in excellent agreement with experimental phase diagram data [5]. Nevertheless, these experimental data have not been considered later on any more, not even in the revision by Lee [3]."

Jan 1, 1996

By F. Kassabji

This publication presents the main experimental and theoretical results on the recovery of aluminum scrap (dross and Used Beverage Can) without use of any addition of fluxing salts. Dross and UBC's processing experiments have been conducted in a rotary plasma furnace operating in the transferred and non-transferred mode, using different plasma gases. The investigation involved the treatment of more than 100 kg of dross and other aluminum residues using plasma torches with less than 100 kW power. The experimental work showed that this process is .far more economical and kind to the environment than the conventional route using a salt flux. An equilibrium thermodynamic calculation at elevated temperature makes possible the prediction of by-products at various temperatures for different plasma gases.

Jan 1, 1994

By H. Bai, B. G. Thomas

"A three-dimensional finite difference model has been developed to study the liquid steel-argon bubble two-phase turbulent flow in continuous casting tundish nozzles. Experiments have been performed on a 0.4-scale water model to verify the computational model by comparing its prediction with velocity measurements using PIV (Particle Image Velocimetry) technology. The computational model was developed using CFX and then employed to investigate the effects of various casting process variables. A fast, simple inverse model to quantify relationships between those process variables was developed, based on interpolation of the numerical model results, using Bernoulli's Equation and advanced multivariable curve fitting methods. Predictions using this model compare well with plant measurements. The model has been applied to present trends and observations on the relationship between casting speed, tundish depth, slide gate opening, and argon gas injection rate. The results can also be used to predict .the theoretical steel flow rate through the nozzle, so that clogging conditions can be identified in the plant.IntroductionTundish nozzle geometry is one of the few variables that are both very influential on the casting process and relatively inexpensive to change. Designing an effective nozzle requires quantitative knowledge of the relationship between nozzle geometry and other process variables on the influential characteristics of the flow exiting the nozzle. This relationship depends on the flow pattern within the nozzle components. Most previous modeling studies of flow in the nozzle have focused on single-phase flow [1-4]. Argon injection into nozzle is an efficient and widely employed method to reduce nozzle clogging, even though the real working mechanism(s) are still not fully understood [5]. Argon injection may greatly affect the flow pattern in the nozzle, and subsequently in the mold. Therefore, two-phase flow modeling is needed to improve understanding of fluid flow in the nozzle."

Jan 1, 2000

By J. L. Hill, M. A. R. Sharif, J. Lin

"A numerical algorithm has been developed to simulate the movement, breakup, and entrapment of the oxide film inclusions encountered during the mold-filling processes of aluminum castings. The flowfield is solved using the well-known Marker and Cell (MAC) method by a time marching process. The Volume of Fluid (VOF) method is used to track the free surface boundaries. A kinematic approach is employed to track the movement and breakup of the oxide films on the free surface or in the bulk liquid metal. The computer program based on the proposed algorithm is able to model the flow behavior and oxide film movement, breakup, and entrapment in mold cavities for aluminum castings.IntroductionMetallographic and fractographic studies of the aluminum castings show tangled networks of oxide films in the castings. These oxide films can form in the furnaces or during the mold filling processes. Green and Campbell [I] concluded that the oxide film defects dominate the strength of aluminum castings. The main cause of oxide film entrapment into the bulk molten metal during the casting processes is the surface turbulence. In film-forming alloys, if the surface breaks, due to a drop, a fountain, or a breaking wave, then the surface film is folded over and incorporated into the bulk liquid. The incorporation of surface films leads to cracks in the casting and other defects that are nucleated by the presence of the folded films, such as porosity and hot tears. Campbell [2] estimated that up to 80% of scrap in light-alloy casting is the result of surface turbulence."

Jan 1, 1999

By Oluwatosin A. Aladejebi, Apsara S. Jayasekara, Raymond J. Longbottom, Mark Reid, Marc in het Panhuis, Brian J. Monaghan

The coke analogue is a new research tool that has been developed to quantify and characterize the effect minerals in coke have on coke reactivity. The analogue material is made from a number of different carbon or carbon containing materials and minerals to in part replicate real industrial coke’s reactivity behavior. Elucidation of the effects of minerals on coke reactivity has proved difficult due to the complex and heterogeneous nature of industrial coke and the potential non-additive effects of minerals on coke reactivity. The coke analogue addresses this complexity and heterogeneity through control of its mineralogy, mineral size and mineral dispersion through the analogue, porosity and carbon structures. Initial studies using the analogue were focused on coke dissolution kinetics in liquid iron but recent work has focused in characterization of its porosity, carbon structure and rate of reaction.

Jan 1, 2014

By Philip Nash, Jie Zhou, Joshua Blackketter

"Large ingots tend to have internal defects such as shrinkage cavities and porosities, which have to be closed during the cogging stage to ensure sound internal quality of forged parts. In this work, finite element methods were used to simulate open die forging passes, with varying parameters that affect the void closure behavior profoundly. Numerical models ware constructed in ABAQUS, DEFORM and FORGE using data taken from footage of the forging process and material mechanical data obtained from the Gleeble compression tests. Forging variables such as pass rotation, reduction per pass, and feed ratio were studied with intense attention paid on the special properties of H13 steel, so that this study can be applied to solve real world problem.IntroductionCenterline defect closure is a frequently studied but still challenging topic in open die forging industry. In practice, open die forging is employed as an effective hot forming process to make desired shape of metal products as well as to ensure center consolidation of internal defects which result from the casting process. Nowadays, remarkable large forgings have been more and more required to meet industries demand. However, the increase in ingot size has tended to result in considerable macrosegregations and shrinkage cavities or voids, which need to be worked thoroughly during the forging process; but the size of the products and limitations of manufacturing capacity, such as the press load, make it difficult to achieve adequate local deformation to close those defects. Therefore, choosing optimal forging parameters under given work condition to ensure good internal quality of forged products is critically important."

Jan 1, 2012

By Ivan Imris

The common problem of new and conventional technology of copper production is the copper losses in the slags, which may be divided into mechanical and physico-chemical losses. In the first group can be included particles of mechanically entrained or floated unsedimented matte particles which coexist with slag. On the other hand, the physico-chemical losses are caused by solubility of copper in the slag in the form of sulphide and oxide. The copper losses in the slags from different processes has been predicted by calculation from thermodynamic data and compared with those determined by microscopic examination and quantitative electron microprobe analysis. Depending on the forms of copper losses in the slag the reduction of copper losses in the slag or the slag cleaning process could be suggested.

Jan 1, 2003

By A. J. Rigby

Refractory linings in converters or anode furnaces used to over-oxidize the blister copper will suffer rapid deterioration, due to prolonged contact with copper oxide-rich slag. Nitrogen stirring with COP KIN porous plugs and use of SEMTECH OPC in converters and anode refining vessels can considerably reduce both refractory wear and processing times. In addition, careful control of the vessel atmosphere and the use of real-time optical process control minimize both slag volume and contact time with the vessel refractory.

Jan 1, 2005

By Yotamu Stephen Rainford Hara

"The aim of our work is to investigate a low energy and clean route for the recovery of copper and cobalt from complex sulphide mineral concentrates. The mineral concentrates were roasted in air, in the presence of CaO (MS + CaO + 202 =MO+ CaS04) at temperatures below 973K. The roasted products containing CuO, CoO and Fe203 were carbothermically reduced at 1073K within an hour to preferentially reduce copper and cobalt. The kinetics of reactions were studied using the thermogravimetric technique and by characterisation ofreaction products using the XRDSEM-EDX techniques. The effects of MS:CaO ratio, roasting temperatures and physical nature of the mineral concentrates were analysed. The method for capturing S02 by forming CaS04 was analysed for reuse in the process. The energy balance for the above process is compared with that of conventional continuous smelting/converting process.1.0 IntroductionCopper sulphide mineral concentrates from Zambia contains substantial amouot of cobalt. The cobalt metal content in the concentrates ranges between 0.7 and 2 % weight, which corresponds to 3 and 9 % weight copper, based on the spot price of copper ($7 386/tone) and cobalt ($31 000/tone). Although the traditional approach using a combination of roasting-leaching-electrowining steps can be applied to recover copper and cobalt from sulphide mineral concentrates [1-4], there are two major draw backs of the traditional process: (i) the S02 emitted during roasting is too lean for economical conversion for sulphuric acid manufacture, which causes serious environmental pollution. (ii) silver and gold which are normally present in the sulphide concentrates are lost out [5] because they are not leachable by H2S04 or HCl which are the common leachants. The above two problems have been overcome by adopting flash smelting in which a rich S02 gas above 20% is produced [1, 5] and successfully converted into sulphuric acid. The precious metals tend to partition to blister copper and recovered during refming. However, nearly all cobalt is lost into the slag phase uoder oxidising condition which prevails during flash smelting. It is important to note that the cobalt content in the slag can be up to 2.6 % weight [6]. The recovery of cobalt from the slag is a process which requires huge amouot of energy since the slag is smelted above 1873K [6]. With a view of minimising the amouot of energy and S02 emission during metal recovery, our investigation involves roasting the sulphide concentrates in the presence of lime and reducing the roasted samples with carbon."

Jan 1, 2013

By J. Pesl, U. Kemey, F. Sauert

"The CONTOP® smelting cyclone is a water-cooled, upright, high-intensity smelting reactor. The technology for the reactor was initially developed and brought into industrial-scale operation in the area of non-ferrous metallurgy. The two largest smelting cyclones were built with a capacity of 32 tons per hour of copper concentrate mix.The newest industrial CONTOP® plant treats up to five tons per hour of zinc-bearing residues including EAF dust. The highly concentrated zinc-lead oxide produced is sold to the zinc industry. The slag fulfills the leaching criteria and is used in waterway construction. The heat transferred to the cyclone cooling system and the off-gas boiler produces steam from which power is generated in a turbine.V AI has erected a new CONTOP® demonstration plant at MEFOS, Lulea, Sweden. A zinc volatilization rate of 90% was achieved during hot commissioning with Swedish EAF dust.Treatment costs in the range of 85 to 100 EUR per ton were estimated in a feasibility study on the treatment of 73,000 and 57 ,000 tons EAF dust for a group of steelmaking mills in Southern Europe."

Jan 1, 2000

By R. Elliott, H. Bayati

"Effect of time and temperature on microstructure and mechanical properties of an austempered ductile iron, ADI, of composition 3.6%C, 2.6%Si, 0.4%Cu, 0.2%Mn are reported. Xray analysis and. microstructural observations indicate that lowering the working temperature, aging temperature, increases the lifetime of ADI significantly. Results show· that lowering the aging temperature increases the strength and reduces the ductility of ADI. DSC traces for ADI austempered at 340°C are presented. Comparison of the DSC analysis and kinetic measurements demonstrates that the DSC traces can be· used to predict the life time of ADI successfully.IntroductionAustempered ductile iron, ADI, is one of the most significant developments in cast iron technology over the past two decades. Outstanding properties of high yield, ultimate strength, ductility, fatigue and wear· resistance make ADI suitable for a range of applications including gears, connecting rods, crankshafts and agriculture machine components. The austempering reaction in cast iron occurs in two stages, Fig. I, in contrast to the single stage reaction in steel. In stage I the relatively low carbon austenite produced during austenitising transforms into ferritic plates and high carbon austenite, a metastable structure called·ausferrite. The high carbon ailstenite and supersaturated ferrite produced in stage I decompose into ferrite and carbide in stage II: to form a structure similar to the bainitic structure in steel. This behaviour exposes a well-defined processing window, t1 - t2, over which the maximum amount of ausferrite is produced, Figure 1. Whereas the bainitic structure determines the properties of austempered steel, ADI properties are mainly affected by volume fraction of retained austenite (VRA), austenite carbon content (ACC), unreacted or martensite volume fraction (UA V), compositiori and amount of carbides, and morphology of ferritic plates[l,2]. Due to the detrimental .effect of martensite and carbides on properties of ADI, an ideal structure of ADI consists only of ausferrite [l,2]. Thus, it is common to determine the processing window for each austempering treatment in order to identify the optimized austempering time. Decomposition of austenite (stage II) signals the end of the life time for an ADI component, therefore, the aging behaviour of ADI at different working conditions can be studied by determining the t2."

Jan 1, 2000

By L. I. Rosato

A novel hydrometallurgical process for the recovery of silver and gold from neutral leach residue that is based upon leaching with thiourea, is described. Laboratory and pilot plant studies have shown that 80-90% of the silver and 60-70% of the gold can be recovered by:? ( i) leaching zinc calcine with 'Spent electrolyte at pH 2.0-3.0 to generate a precious metal-bearing zinc ferrite residue, (ii) leaching of the thickened zinc ferrite with 3-5 g/L thiourea in a six stage carbon-in-pulp circuit, (iii) elution of silver and gold from the loaded carbon with a thiourea- butanol solution, (iv) thermal regeneration of the stripped carbon and (v) recovery of the precious metals from the pregnant eluate by cementation with zinc dust. The reasons for adopting the thiourea CIP leach and the preferred operating parameters for each process step are presented. The requirements for the destruction of any thiourea transferred to the zinc circuit are outlined, and the results of an integrated one tonne/day pilot plant operation at Canadian Electrolytic Zinc are given.

Jan 1, 1990

By Xuemei Zheng, Aiyuan Ma, Chao Liu, Guojiang Li, Chenyu Sun, Jinhui Peng, Libo Zhang, Yongguang Luo

In this paper, the removal of fluorides and chlorides from blast furnace dusts by water vapor enhanced microwave roasting was investigated, combined with the advantages of microwave selective heating and based on a thermodynamic analysis of zinc and lead halides. According to proposed reactions in the process, detailed experiments were systematically conducted to study the effect of roasting temperature, holding time, air flow, water vapor flow rates, and stirring speed on the efficiency of the removal of F and Cl. The results show that 97.26% of F and 64.23% of Cl could be separated when the condition of the roasting temperature of 650°C, stirring speed of 80 rpm, holding time at 60 min, air flow of 350 L/h and water vapor flow rate of 8 mL/min was optimized.

Jan 1, 2016

By B. C. Blakey

Unlike most hydrometallurgical slurries, those containing significant concentrations of goethite are typically highly viscous and shear-thinning, even at solid volume fractions below 5%. The viscosity may also depend upon time. These characteristics must be taken into consideration in slurry transport and heating. The technical literature is replete with apparent contradictions regarding the viscous behavior of these slurries, which may be due, in part, to variations in viscosity-measuring techniques. We present techniques that yield consistent results suitable for use in process design. A striking degree of time-dependent behavior is demonstrated for a laterite slurry. Reliable methods to design and analyze tubular transport and heating systems for time-independent slurries are summarized. Rules of thumb are then offered to account for the effects of time-dependency.

Jan 1, 2000

By J. C. Huyhua

The effect or various oxidants on gold and silver dissolution in thiourea solutions (0.05 M in H2SO4) was studied using the rotating disc technique, a.t 2s c and 600 rpm. These studies were carried out at constant (4:1) initial molar ratio or thiourea to oxidant concentrations, to produce 50 % thiourea. oxidation. The initial dissolution rate of gold was approximately four times higher in the presence. of ferric sulfate (5.37 x 10-3mg cm-2 s-1) than in the presence of hydrogen peroxide (H2O2), potassium persultate (K2S2O3), or monopersulfa.te (KHS06). The dissolution rates for silver were considerably lower than gold for the same oxidants. Oxidation of thiourea in the presence of peroxygen and persulta.te compounds is a. fast reaction and it is completed in less than ten minutes. On the other hand, the oxidation or thiourea with? ferric.sulfate is slow, yielding a second-order reaction rate constant k = 6.09 I mol-1 h-1. Sulfur formation in the ferric thiourea system begins when ferric ion reduction approaches to completion. With hydrogen peroxide, sulfur is observed at lower thiourea concentration than ferric. Suifate. The presence of a large excess or free thiourea i.e., s to 20 % thiourea oxidation) retards sulfur formation and maintains favorable dissolution rates. Finally, carbon-in-leach experiments indicate that thiourea solutions a.re stable for several days, with ferric sulfate or hydrogen peroxide. The dissolution rates of gold and silver doubles in the presence or activated carbon when hydrogen peroxide is used as oxidant.

Jan 1, 1989

By S. Sugiyama, M. Kiuchi

"New metal working processes, such as the mashy-state mixing, mashy-state forging, mashy-state rolling and mashy-state extrusion are developed and applied to manufacture the so-called particle reinforced metals, fiber reinforced metals, particle reinforced cladding metals and so forth. These metal-ceramics composites are made of metal sheets, metal powders, ceramics particles and ceramics fibers. The mashy-state processes are also used to work those composites into bars, wires, tubes, plates, sheets, machine parts and other products. The working conditions necessary to manufacture sound composite products are clarified and the mechanical properties of the products are investigated. Through the investigation, it becomes clear that the mashy-state processes are useful and effective to manufacture metal-ceramics composites. It is al so known that these processes may be applied in various ways to development of new metal matrix compounds. IntroductionThe so-called metal-ceramics composites and processes to manufacture them are now being widely investigated in order to comply with increasing demands for new materials with novel and excellent mechanical properties and functions. The metal-ceramics composites are expected to have superior characteristics with respect to the elastic modulus, hardness, anti-wear resistance, high temperature strength and other mechanical properties to those of conventional metallic materials.The present authors ha v e been investigating into new metal working processes which are based upon the characteristics of metals and their alloys in the mashy-state. In the mashy-state, the metal (or alloy) includes both of the solid and liquid components. According to the fact that the partial melting takes place and the liquid component usually exists at grain boundaries, the metal in the mashy-state has quite different mechanical properties from those of the metal in the solid-state. Because of that the bonding force among grains is very weak due to the partial melting occurred at grain boundaries, the mashy metal has distinctively low flow-stress and high deformability. The mashy metal splits into grains or particles and sticks to others very easily. It is so soft as to be stirred up just like a lump of sherbet, but it is sufficiently viscous to be mixed up with other materials, such as ceramics particles and ceramics short-cut fibers."

Jan 1, 1988

By Musa Karakus

In an attempt to explain the phenomena of lead entrainment during Cu drossing of lead bullion, two different synthetic lead bullions were heated to 1050°C, cooled slowly to various temperatures, and then quenched. The morphology and composition of dross particles that form when Mn is used to desulphurize bullion also were examined. Polished sections of these pyrometallurgical products were examined by process mineralogical techniques to identify the impurity phases, determine their chemical compositions, examine the morphology of the impurity phases and evaluate the potential for lead entrainment in such crystals, and characterize pre-quench and quench-generated phases. The phases crystallized were metallic lead, metallic copper, galena, chalcocite, albandite, Cu14.4Pb2S9. and 5.5Pb2S3.5. Metallic copper formed isometric skeletal crystals, chalcocite formed platy and skeletal crystals, and 1formed crystals and eutectic intergrowth with chalcocite and Cu14.4Pb2S9 or Cu5.5Ph2S3.5. The pre-quench crystals are larger and usually exhibit skeletal forms; the quench-generated phases are only a few micrometers across and disseminated throughout the lead matrix. Skeletal crystals of metallic copper and chalcocite form three dimensional networks that entrain large amounts of metallic lead.

Jan 1, 1989

By F. F. Aplan

Though over 100 minerals are known to contain the rare earth (RE) or lanthanide elements, only a few provide the bulk of the world's source of these elements. The principal RE-containing mineral, monazite [(Ce,La,Th,Y)PO4], is recovered by gravity, magnetic, electrostatic and flotation concentration methods, while the other important source mineral, bastnasite [CeFC03], is concentrated by flotation. The processing of the lesser important source minerals is discussed, as is the recovery of the lanthanides from apatite [Ca5(P04)3(F,OH)] where the rare earth elements are present from trace amounts to over 10% as the mixed oxides.

Jan 1, 1989