By Ann M. Hagni

Microscopic and sub-microscopic gold commonly occurs in the sulfides pyrite (FeS2) and arsenopyrite (FeAsS). To recover refractory gold from pyrite and arsenopyrite, these sulfides are roasted to create porosity and permeability prior to cyanide leaching. A new technique of adding Ca(OH)2 and roasting. lime roasting. is being tested for retention of contaminant sulfur and arsenic and effectiveness of gold extraction. The lime roasting of pyrite at 500°C contains anhydrite (CaS04). oldhamite (CaS). calcium sulfite (CaS03). hematite (Fe2O:J), magnetite (Fe304). and minor amounts of pyrrhotite (Fe1.xS) and pyrite. At 600°C. 650°C and 700°C. the main constituents are anhydrite. oldhamite. and hematite. At 750°C. 800°C. and 850°C. anhydrite and hematite are the predominant phases with minor oldhamite. The roasted arsenopyrite at 450°C contains arsenic sulfides. calcium sulfite. hematite. and minor oldhamite. magnetite. and pyrrhotite. At 650°C. 700°C, 750°C. and 800°C, anhydrite, oldhamite. arsenic sulfides, and hematite are present. At 850°C. the same minerals are present with only minor oldhamite. The textures indicate excellent porosity and permeability at high temperatures. At lower temperatures, rims of low porosity and permeability surround many of the pyrite and arsenopyrite particles, and the complete oxidation process from pyrite to pyrrhotite to magnetite to hematite can be observed in individual particles. Additional process mineralogy techniques employed in this study are electron spectroscopy for chemical analysis (ESCA) and cathodoluminescence microscopy (CIM) in the determination of the calcium-sulfur-oxygen phases. Automated scanning electron microscopy-energy dispersive spectroscopy was utilized to analyze particles for gold content. Reflected light microscopy (RIM) revealed arsenopyrite and pyrite encapsulated in quartz particles of the gold-bearing concentrate, gold roast calcine, and cyanide leach residue.

Jan 1, 1991

By G. D. Sandrock

The science and technology of roan temperature rechargeable metal hydrides began about 1969 with the discoveries that the intermetallic Compounds LaNi5 and TiFe could be, conveniently hydrided and dehydrided at roan temperature and modest H2 pressures. Subsequently, this lead to the development of a broad family of REE-containing AB5 hydrides and numerous applications that make use of the extraordinary H2-absorption and reaction-heat properties of these materials. Some of the applications include H2 storage, compression and separation, as well as heat pumping, heat to mechanical energy conversion and electric energy storage. This paper briefly reviews the fundamental phenomenology of metal hydrides, the history of the use of REE's in rechargeable metal hydrides, the practical engineering properties of these materials and the applications that have evolved around them. The rechargeable nickel metal hydride battery, a new vial alternative to NiCd cells, stands at the forefront of the applications.

Jan 1, 1992

Segregation roasting tests were carried out on Zaire cobalt oxide ores assaying about 2% Co and 3.5 to 6.5% Cu. The major parameters tested during the laboratory investigations were temperature, dosage and type of reducing agent, dosage and type of chloridizing agent, and particle size. Results showed that standard conditions suited to the segregation of copper ores, i.e. low temperature and low dosages of reducing and chloridizing agents, resulted in the segregation of copper only, while conditions suited to the segregation of lateritic nickel, i.e. higher temperature and increased dosages of reducing and chloridizing agents, led to a successful segregation of both copper and cobalt. Under the best conditions, 88% of the cobalt and 98% of the copper could be recovered in a concentrate assaying 32.5% Cu and 8.5% Co. Alternatives to process such a concentrate are briefly reviewed.

Jan 1, 1993

By Chris Doyle

From 1997-2000. PT INCO undertook the Fourth Line Expansion Project (FLEX) to increase annual production rates from 90-100 to 150 Mlbs Ni/year (68,000 MT Ni/yr). In 2003, PT INCO nickel production underwent a major sustainable step jump that finally exceeded the targeted rate. This paper presents the changes that led to this achievement. The focus of mining changed. Improving Ni grade was important but only if electric furnace feed met target chemistry so that on-specification slag could be produced. The intensity of diamond core drilling for exploration was dramatically upgraded, mine planning strategy was totally re- vamped and an ore chemistry quality assurance team was formed. In the processing plant, measurement systems were upgraded for better control. Teamwork between sections vastly improved. The final step jump in production occurred when the fifth hydro-electric power generator was added to the furnace grid to allow the power-starved furnaces to cruise in operation at 70+ MW. Keywords: Free cash flow, Ore Chemistry, Measure, Control, Improve

Jan 1, 2004

By Semih Perdahcioglu, Arthur E. Morris

"The curricula for the majority of Materials Science and Engineering programs is devoid of all but the most rudimentary coverage of the principles of material and energy balance calculations. As a result, graduated engineers that need to make such calculations are faced with three unpalatable options. First, attempt to learn the subject by attending workshops or short courses sponsored by corporations or industry groups. Second, outsource the needed work to a consulting engineering company. Third, purchase a software package that's capable of simulating a process. Each of these options require a considerable investment of employee time and effort. The first option might be the best if suitable computational software was readily available. We review the recent development of such software, which is entirely based in Excel. The software tools include a thermodynamic database, tools for multiple computations, and a flowsheet simulation program. These tools employ teaching by simulation.IntroductionPracticing engineers often come up with situations where they must learn a technical subject that they didn't cover in their college classes. One possibility is to obtain a couple of texts on the subject, and delve in. Or, they may sign up for an intensive short course where they can get personal instruction and guidance. But the first option requires a lot of study time, and the second option may not provide the specific instruction (or intensity of instruction) required to appropriately master the subject. Here we look at ways of using simulation techniques to learn the methodology for making material and energy balances on industrial processes.Industrial heating processes have undergone many changes over the past dozen years, as vendors have introduced new heating equipment designed to recover the greatest possible amount of heat from the fuel, and to meet stringent environmental challenges for emissions (especially NOx). Even though the recent unprecedented drop in price of natural gas may have altered the urgency for improving a plant's energy efficiency, the need is still there. Until recently, there was a dearth of readily-available software for process engineers to use for simulating a plant's flowsheet. The good news now is the existence of several Excel-based software tools that make the calculational process much easier. [ 1]. Plant engineers may also be interested in a DOEsponsored program[2] which allows plant-wide and ""what-if' analyses of the energy balance."

Jan 1, 2013

By Young-Chul Kang

The Onsan Copper Smelter of LG-Nikko Copper Inc. is a unique plant, which has been operating two smelting processes since 1998. The operation of the first one was started in 1979 with a capacity of 80,000tpy of copper in concentrates utilizing Outokumpu flash- smelting technology. The other one was started in 1998 based on Mitsubishi continuous process with a capacity of 160,000tpy of copper in concentrates. Through several expansion projects, the total smelting capacity of both processes is expected to reach 430,000tpy of copper in concentrates towards the end of 2002. This article describes operation advantages of having two different processes at one plant and comparative operation results in terms of productivity, impurity distribution, energy consumption and environment issues and etc?

Jan 1, 2003

By H. Senoh

For the purpose of clarifying the reason caused a drastic decrease of discharge capacity for MmNi3.6Mn0.4Al0.3Co0.7 electrode at relatively low temperatures, various factors influencing the charge-discharge processes were investigated in the temperature range of 25°C to -40°C. The charge efficiency obviously decreased at low temperatures less than 0°C due to a decrease in the rate of the charge-transfer reaction on the electrode surface. Moreover, both the rate of the hydrogen diffusion from the alloy bulk to surface and the rate of the charge-transfer reaction significantly influenced the high-rate dischargeability. The addition of Mo to MmNi3.6Mn0.4Al0.3Co0.7 alloy was found to be effective for improving the electrocatalytic activity, leading to the improvements of the charge efficiency and the high-rate dischargeability at relatively low temperatures.

Jan 1, 2002

By P. K. N. Raghavan

This paper identifies potential technologies for Carbon dioxide abatement from the mining and metal industry with special reference to the Aluminium industry. Mine reclamation could contribute to this effort to successfully reach the greenhouse gas (GHG) emissions reduction commitments for a nation. An overview of GHG production by the mining and metal industry together with a review of principles used to set the context in which specific options for GHG reduction are described. Options for GHG reduction in the mining and metal industry include reforestation, Addition of soil amendments or neutralizing agents, CO2 capture and storage, initiatives towards energy reduction, waste heat recovery and alternative energy use. An analysis and quantification of the potential GHG reduction of potential carbon sinks and sequestration options for the mining and metal industry are provided. Cost estimates for different options are provided. The paper also identifies sources that could fund research regarding GHG reduction options. The paper concludes with recommendations.

Jan 1, 2011

By B. Q. Li

A numerical study of the developing fluid flow and thermal aspects during the staning phase of aluminum continuous casting processes is presented. The deforming finite element method, coupled with a quasi-Lagrangian formulation, is used to represent the growth of an ingot and the dynamic fluid flow and thermal behavior that evolves in the growing ingot. The mathematical formulation of the problem and the numerical treatment are discussed. The algorithm solves the free moving nodes as part of total unknowns with an automatic time step control for time integration. This permits an optimal computing efficiency while still keeping the computational errors under control. A selection of the results obtained using the algorithm is presented. The results are concerned with the evolution of fluid flow, temperature and solidification phenomena during a DC round ingot casting process, as it evolves from the beginning of casting operation to a steady state. These results show that the time-varying, complex fluid flow and thermal phenomena during continuous casting processes can be very well represented by the computational algorithm. The results also illustrate that, during the casting process, ~e fluid flow and temperature fields change drastically at the initial stage but evolve slowly afterwards

Jan 1, 1993

By Murali Thirukkonda, Rahul Shah, Srinivas Tangrila, Shankar Rachakonda, Jan Kajuch, Arthur Gurson

"High-temperature superconductors have potential for a variety of applications such as power generators, superconducting magnets for mine sweepers or ship propulsion motors, and magnetic levitation transportation systems. Interest in the use of superconducting wires and tapes increased dramatically after the discovery of high-critical-temperature (high-Tc) oxide superconducting compounds, which offer operating temperatures above that of liquid nitrogen. Several techniques have been proposed to produce commercially viable high-Tc oxide based superconducting wires. One of the promising methods involves multi-pass powder-in-tube (PIT) wire drawing followed by rolling and heat treatment. This work focuses on the development of a numerical model to simulate the PIT drawing process for fabrication of long lengths of silver sheathed Bi-2212 superconducting wires. The finite element based model was used to predict densification of the oxide powder, wire drawing forces, and silver sheath thickness during drawing. A cap-type pressure dependent constitutive equation was implemented in the model to simulate the powder behavior. The model incorporated experimentally obtained material data for the silver and powder. Results indicate that powder densification is increased by decreasing the initial silver thickness and increasing the silver strength. Data from wire drawing experiments were used to verify model predictions. IntroductionSuperconducting wires and tapes can be used to carry large dc currents with no measurable loss due to resistivity. When used in superconducting magnets for power generators, motors, levitation devices, magnetic detectors, or energy storage devices, they could potentially result in significantly reduced energy losses. In the past, most prototypes were tested in liquid helium at 4.2K [1]. However, the necessity to provide liquid-helium cooling systems proved to be a serious limitation in commercialization. In 1986 high-critical-temperature (high-Tc) oxide superconductors were discovered [2], which could allow for higher operating temperatures above liquid nitrogen (77 K). Since then, both academia and industry have concentrated their efforts on the development of high-Tc oxide superconducting wires, tapes and coils. As yet, large scale fabrication of long lengths of these wires with the required current carrying capacity and mechanical properties remains an enormous challenge."

Jan 1, 1994

By Adam Powell

A Cahn-Hilliard phase field model is formulated to describe transport-limited electrochemical reactions coupled with fluid flow in a metal reduction cell. When the reaction is limited by mass transfer of metal ions from the electrolyte to the cathode, the metal-electrolyte interface at the cathode exhibits a Mullins-Sekerka instability, leading to the growth of dendrite-like "streamers" of liquid metal into the electrolyte, which in turn significantly enhance the apparent mass transfer coefficient there. Model results for iron reduction from ferrous oxide in slag show formation of these streamers. Although the double-layer is not included in this model, the related phenomenon of electrocapillarity can be represented by a gradient penalty term which includes the electric potential gradient, such that interfacial energy is a function of the electric field normal to the interface.

Jan 1, 2003

By Keith M. Axler

This report addresses issues specific to the generation of hydrogen fluoride via reaction of calcium fluoride with sulfuric acid. This process has been established on a commercial scale and is under consideration for treatment of calcium fluoride residues from uranium processing. Magnesium fluoride slags are also available as a product of uranium processing. The technique of using sulfuric acid for the production of hydrogen fluoride from magnesium fluoride is also under consideration as a residue processing scheme. In the current study, thermodynamic modeling was used to investigate these chemical processing systems. The results presented herein reveal information relevant to the selection of processing temperatures and conditions. Details include predicted effects in system composition based on operating temperatures for both the calcium fluoride and the magnesium fluoride systems.

Jan 1, 1996

By S. Eckert, G. Gerbeth, K. Timmel, B. Willers, T. Wondrak, N. Shevchenko, M. Röder

The quality of the produced steel in the continuous casting process is significantly governed by the melt flow in the mold. However, direct flow measurements in liquid metals are still rather scarce. In order to investigate these flow phenomena, three experimental facilities operating with low melting liquid metals were installed at Helmholtz-Zentrum Dresden-Rossendorf (HZDR). The melt flow in the models is measured by the Ultrasonic Doppler Velocimetry (UDV) or the Contactless Inductive Flow Tomography (CIFT), multi-phase flows can be visualized by X-ray imaging. The obtained measurement results are primarily used for validation of numerical models. In this paper we will investigate the fluid flow in the mold and the behavior of the surface of the liquid metal using flow measurements by UDV and surface profile measurement by a laser scanner, respectively. Strong fluctuations and deviations of the free surface were observed in case of a static magnetic field

Jan 1, 2016

By Lichao Ding, Jingbiao Fan, Yunnen Chen

"With the development of industrial production, more and more wastewater containing high concentration ammonia nitrogen was discharge into the environmemt, which caused serious harm to the environmemt. Treating the wastewater has great significance to protect water resources. Using air-stripping combined with oxidation to uptake high concentration of ammonia nitrogen wastewater. The influence of operating parameters was investigated. Experimental results revealed that pH of solution, aeration time and aeration strength showed heavy influence on ammonia nitrogen removal. Air-stripping combined with oxidation can be considered as an alternative approach for the removal of high concentration of ammonia nitrogen from practical metallurgical wastewater. When pH was 11, aeration time 20 min, aeration strength 1040 Lh-1, and oxidation with 10 % NaClO solution 10 min, the initial ammonia nitrogen 2130 mgr1 could reduce to 12 mgr1. Other items could also be removed to meet the ""Integrated wastewater discharge standard (GB8978-88)"".1. IntroductionThe rapid development of human activities has caused a worldwide increase of nitrogen in rivers, lakes and coastal waters. It leads to considerable eutrophication and an increase in the frequency of toxic algae blooms [1,2]. The concentrations of nitrogen in the water of China are pervading high [3]. The discharge of wastewater containing high concentration of ammonia nitrogen is one of the most important factors. Great efforts have been devoted to the removal of ammonia nitrogen from wastewater. Traditional methods include biological denitrication [ 4 ], chemical precipitation with magnesium ammonium phosphate [5], electrochemical conversion [6], air-stripping [7] and so on. Biological denitrication is the most common process in the treatment of ammonia nitrogen wastewater. But the process is only suitable for the removal of relatively low ammonia concentration due to the requirement of appropriate C/N ratio [8]. Chemical precipitation needs additional reagents, which may introduce new pollutants to water body. Electrochemical method often uses expensive metal or metal oxide as electrodes, and also consumes large quantity of energy [6].Although air-stripping makes use of stripping tower and consumes energy, it is very suitable for the removal of relatively high ammonia concentration. Different air-stripping conditions would appear different removal efficiency. And only air-stripping the effluent can not be attained the ""Integrated wastewater discharge standard (GB8978-88)"". In this study, we use air-stripping and oxidation to removal high concentration of ammonia nitrogen from simulated and real ammonia nitrogen wastewater."

Jan 1, 2011

By Gordon D. Jarvinen

Polymer Filtration (PF) Is an innovative, selecthle metal removal technology. Chelating, water-soluble polymers are used to selectively bind the desired metal ions and ultrafiltration is used to concentrate the polymer-metal complex producing a permeate with low levels of the targeted metal ion. When applied to the treatment of, Industrial metal-bearing aqueous process streams, the permeate water can often be reused within the process and the metal ions reclaimed. This technology is applicable to many types of industrial aqueous streams with widely varying chemistries. Application of PF to 'aqueous streams from nuclear materials processing and electroplating operations will be described.

Jan 1, 1999

By Xuefeng She, Qingguo Xue, Jingsong Wang, Guang Wang

Iron nugget could be got at high temperature using carbon composite pellet, which were made by the mixture of ludwigite and reducing agent. In order to reduce sulfur content in the nugget, effects of additives on the desulfurization was investigated. The sulfur content could be dramatically reduced if the CaO was introduced into the pellet and the sulfur content was as low as 0.046wt.% when the addition amount of CaO was 5wt.%. However, the melting separation of pellet became increasingly difficult and the yield of iron decreased when CaO content in the pellet gradually increased. Na2CO3 could also reduce the sulfur content in the iron nugget and made the iron and slag separate difficultly as well. When 6wt.% Na2CO3 was added into the pellet, the pellet was too difficult to melt separation and the sulfur content in the nugget was 0.084wt.%, which didn’t meet the need of steel making.

Jan 1, 2015

By Milorad Cirkovic

Kinetics of copper concentrate oxidation in roasting processes in a fluidized bed reactor has been studied at temperatures between 600°C and 720°C using particles of 0.038 to 2.5 mm in average size. The analysis of composition of samples has been done by chemical methods. Phase composition has been determined by Siemens X-ray equipment with Cu anticathode and Ni filters at a voltage of 40 kV and a current of 18 mA. The content of sulphur has decreased from 33.23 to 19.02 mass percent with the increase of temperature, but the content of Fe304 has increased from 0.15 to 17.14 mass percent. The new mechanism of copper concentrate oxidation in a fluidized bed reactor is proposed in this study. It has been shown from the mathematical model that the velocity of oxidation of copper concentrate between 600°C and 720°C is virtually controlled by the rate of diffusion of 02 through the layer of reaction product.

Jan 1, 1999

By N. Shi, T. C. Lowe, S. J. Zhou, M. L. Lovato, Y. T. Zhu, J. A. Valdez, W. R. Blumenthal, M. G. Stout

"A major problem of short-fiber composites is that the interfaces between the fiber and matrix become a limiting factor in improving mechanical properties such as strength. For a short fiber, a strong interface is desired to effectively transfer load from matrix to fiber, thus reducing the ineffective fiber length. However, a strong interface will make it difficult to relieve fiber stress concentration in front of an approaching crack. Stress concentrations result in fiber breakage. We report in this paper an innovative approach to overcome this problem: reinforcement morphology design. Short-fibers with enlarged ends are processed and used to reinforce a polyester matrix. The initial results show that the bone-shaped short-fibers produce a composite with significantly higher strength than can be attained with conventional short, straight fibers.IntroductionThese interfaces between the fiber and the matrix in short-fiber composites play a critical role and, in many cases, become a limiting factor in improving such mechanical properties as strength and toughness of the composites (1-4). For a short fiber, a strong interface is desired to effectively transfer load from matrix to fiber. A stronger interface can reduce the ineffective length at both ends of the fiber and, therefore, can increase the effective length that carries load (5-9). However, with a strong interface it is difficult to relieve fiber stress concentration -in front of an approaching crack; and such stress concentration can result in fiber breakage (10, 11). This effect is particularly severe for ceramic matrix composites, because of their low matrix toughness and lack of plasticity. Even for a composite with a highly ductile matrix, such as plastics, too strong an interface may still cause successive adjacent fiber breakage and subsequently reduce composite toughness (1, 11). On the other hand, a weak interface significantly decreases the fiber load-carrying length due to ineffective load transfer and complete fiber interfacial debonding and pullout during loading. A compromise in the interfacial bond strength will also compromise the load-carrying potential of short fibers."

Jan 1, 1998

By M. A. Neri

A lead-free solder alloy Sn-57.5Bi-0.5Ag has been developed by mechanical alloying and foundry processes, and has great potential as a lead-free solder system, to low temperature applications. The mechanical alloying powders show a microstructure different to the microstructure obtained by the foundry process for the same alloy. Its melting point of 142°C is slightly higher than that of eutectic tin- bismuth solder. Examination of the microstructure revealed that eutectic microstructure is refined by the mechanical alloying process Ag additions. The lamellar structure of tin-bismuth gradually disappeared with the process of mechanical alloying, while intermetallic compounds AgaSn phase was formed. The Cu-Sn intermetallic compound layer formed at solder-copper interface is the Cu6Sn5 phase. Keywords: Lead-free solder, Microstructure. Mechanical alloying

Jan 1, 2003

By Emil B. Milosavljevic, Ljiljana Solujic

Cyanide is exceptionally reactive, and in typical gold/silver processing liquors, cyanide may be transformed into various species and forms depending on the mineralogy of the ore and chemical make-up of the process water. The exact speciation and relative concentrations depend on the Eh and pH values, as well as the free CN concentration in the system. Very good cyanide balances can be achieved by the judicious selection of the analytical techniques used. The choices an analyst has to make (which analytical methods to use and which ones to avoid) in order to gain better understanding of cyanide speciation and balances in a particular system under investigation will be discussed. Examples of cyanide balances obtained for the laboratory scale tests (agitated leach and column tests) will be presented and discussed.

Jan 1, 1999