AT bottom of this page is a photograph recently taken by a student-John E. Stewart-of the most northerly situated college in the world, the Alaska Agricultural College and School of Mines. It is situated at College, near Fairbanks, Alaska, approximately on the 65th parallel of latitude, and therefore just south of the Arctic Circle. It is farther north than Hudson Bay, and in about the same latitude as southern Greenland.

Jan 1, 1932

By B. M. Larsen, T. E. Brower

In two previous paperslJ dealing with the carbon-oxygcn reaction, and the simultaneous content of each, in liquid steel in the furnace, we have made use of the quantity A[O], defined as the excess oxygen beyond what would be in equilibrium with carbon then present if the pressure of carbon monoxide were I atm.; that is, if [C] X [O] is taken as 0.00222, A[O] = [O] - 0.0022[C] where [O] is the percentage of oxygen by weight as measured by the method described earlier.3 This quantity ?[O] proves to be substantially independent of carbon content over the range 0.08 to I,z per cent, as well as of the basicity of the slag, and is nearly always within the limits o.o15 to o.oz5 per cent when the bath is boiling normally and is in what we have termed a steady state, Apparently it must be at least about 0.014 per cent before boiling occurs; but this threshold value seems to depend upon the ease of bubble formation at the metal-hearth interface, hence upon the condition of the surface of the hearth. In any case, ~(01, on the average, changes considerably following any disturbance of the bath, as by addition of ore. The present paper deals with the average changes in A[O] level following addition of spiegel or crop ends, or after procedures to promote stirring, or by tapping of the steel from the furnace. The observations were made on a large number of commercial heats, and consequently are subject to the influence of various disturbing factors; the results have the compensating merit of showing the consistency obtainable under the limitations imposed by practical operation. Variability of Excess Oxygen in Normal Open-hearth Operation The preceding genera' statements refer to the average value of A[0] particularly in heats that are boiling actively; on individual heats, which are less active, there may be a variable time lag between the disturbance and its effect, which complicates the interpretation of what is going on. For instance, if in the normal refining process boiling is sluggish, the slag usually is gaining Oxygen from the gas phase above it, Or from added Ore$ faster than it is losing oxygen to the metal; Yet when the bath starts to boil vigorously, the opposite condition may prevail for Some time. The consequence of this lag is a variation of A[o], the interpretation of which in a sing1e heat may not be immediately obvious. This condition is illustrated in Figs. I and 2. In Fig. 1, A[0] at the beginning of the test period was near the lower limit of its usual range (dashed lines) in the steady state as a consequence of the lime boil, which had ended about as indicated. The bath is now cold, carbon drop is slow, and the first small orc feed causes only a small rise in A[O]; as the temperature rises and as lime dissolves in the slag, and the bath becomes more active, the

Jan 1, 1948

By B. M. Larsen, T. E. Brower

In two previous paperslJ dealing with the carbon-oxygcn reaction, and the simultaneous content of each, in liquid steel in the furnace, we have made use of the quantity A[O], defined as the excess oxygen beyond what would be in equilibrium with carbon then present if the pressure of carbon monoxide were I atm.; that is, if [C] X [O] is taken as 0.00222, A[O] = [O] - 0.0022[C] where [O] is the percentage of oxygen by weight as measured by the method described earlier.3 This quantity ?[O] proves to be substantially independent of carbon content over the range 0.08 to I,z per cent, as well as of the basicity of the slag, and is nearly always within the limits o.o15 to o.oz5 per cent when the bath is boiling normally and is in what we have termed a steady state, Apparently it must be at least about 0.014 per cent before boiling occurs; but this threshold value seems to depend upon the ease of bubble formation at the metal-hearth interface, hence upon the condition of the surface of the hearth. In any case, ~(01, on the average, changes considerably following any disturbance of the bath, as by addition of ore. The present paper deals with the average changes in A[O] level following addition of spiegel or crop ends, or after procedures to promote stirring, or by tapping of the steel from the furnace. The observations were made on a large number of commercial heats, and consequently are subject to the influence of various disturbing factors; the results have the compensating merit of showing the consistency obtainable under the limitations imposed by practical operation. Variability of Excess Oxygen in Normal Open-hearth Operation The preceding genera' statements refer to the average value of A[0] particularly in heats that are boiling actively; on individual heats, which are less active, there may be a variable time lag between the disturbance and its effect, which complicates the interpretation of what is going on. For instance, if in the normal refining process boiling is sluggish, the slag usually is gaining Oxygen from the gas phase above it, Or from added Ore$ faster than it is losing oxygen to the metal; Yet when the bath starts to boil vigorously, the opposite condition may prevail for Some time. The consequence of this lag is a variation of A[o], the interpretation of which in a sing1e heat may not be immediately obvious. This condition is illustrated in Figs. I and 2. In Fig. 1, A[0] at the beginning of the test period was near the lower limit of its usual range (dashed lines) in the steady state as a consequence of the lime boil, which had ended about as indicated. The bath is now cold, carbon drop is slow, and the first small orc feed causes only a small rise in A[O]; as the temperature rises and as lime dissolves in the slag, and the bath becomes more active, the

Jan 1, 1948

By Mark C. Malamphy

MAJOR JUAREZ TAVORA, who recently accepted the post of Minister of Agriculture in Brazil, has reorganized his department. Not least among those sub: divisions of the "Ministerio" which underwent radical changes in the general reform was the Serviqo Geologico e Mineralogico do Brasil. This well- known organization was declared extinct, and in its place was created a new cleparttnent ' termed "Departamento Nacional cle Producqao Mineral," which immediately took over all the work of the olcl Servico Geologico ill addition to certain new duties. Dr. .. Domingos Fleury- da Rocha, former head of the School of Mines of Ouro Preto, was called to Xio to assume the newly created post of Director General of the department of Mineral Production. His department will have live divisions :

Jan 1, 1934

By Raymond M. Howe

Some time ago, a prominent engineer asked a representative of the firebrick industry to prepare a comprehensive paper on blast-furnace refractories. It was to have been the purpose of this paper to gather practical experiences from widely different sources, in the hope of determining what kind or kinds of firebrick were best adapted for certain uses. This engineer sent questionnaires to the large consumers of blast-furrace linings and stovebrick and received very detailed replies as to their experiences. These replies are conflicting, but, having been turned over to the writer, form the basis of this attempt to meet the request. Because of the impossibility of making final recommendations at this time, a few of the more interesting and commonly known methods of studying refractories are also discussed, as well as the more recent developments in this field. The first reply to the questionnaire stated that good service was being secured from the linings. This satisfactory condition was attributed to the use of a very good distributor. The writer believed that manufacturers try to and do produce a good product and that the proper handling of equipment is of the utmost importance, if good results are to be secured. The type of bricks used was not mentioned. The second reply stated that good life was secured from the furnace linings, but that the writer had had soft-fired stovebrick crumble and, for that reason, preferred a hard-fired product for use in this position. The type of bricks used was not mentioned. The third reply stated that firebrick had crumbled from the mantle up; the cause was not known. The fourth reply stated that the stove linings were satisfactory. Hand-made furnace linings failed after.4 years' service so a steam-pressed lining- was installed which was still good after 4 years of service. Consequently, a second steam-pressed lining was installed but this disintegrated at the top after the furnace had been in blast 7 months. The firebrick manufacturer attributed this failure to the expansion of iron blocks that had been installed at the stock line to prevent erosion. The fifth reply stated that the present "hard-burned" hand-made furnace lining had worn away very uniformly to the depth of only 5 in.

Jan 1, 1920

By R. E. Grace

WHEN an Fe-C alloy, partially reacted to pearl-ite, is quenched rapidly enough to suddenly stop the growth process, it may be expected that any carbon concentration gradients will freeze in situ in the newly formed martensite. A short tempering treatment should precipitate finely dispersed iron carbide particles in approximately the same distribution in which carbon existed during the growth process. Examination with the electron microscope of areas of tempered martensite adjacent to the pearlite-martensite interface should reveal the existence of preferred areas of precipitation. Fig. 1 is an example of an electron micrograph used in this study. Small sections of a commercial steel (0.9 pct C, 1.6 pct Mn, 0.25 pct Si) were austenitized at 945°C in air for 45 min, furnace-cooled to 697°C, iso-thermally reacted to pearlite for 30 min, and quenched into iced brine. Two samples were tempered 5 and 20 min, respectively, in air at 498°C and were subsequently quenched in water. The samples were mechanically polished and etched in 1 pct picral. Collodion replicas were made by the conventional technique; these were shadowed with chromium at about 650' from the horizontal, and electron micrographs were taken at a linear magnification of 14,200X. Prints were made at a magnification of 44,100X. Lineal analysis of the prints was made as a function of the interlamellar spacing and volume percent of iron carbide. Straight lines were drawn into tempered martensite between adjacent lamellae at a distance S/4 or S/6 apart, where S is defined as the interlamellar spacing measured at the pearlite-martensite interface. The volume percent of iron carbide was measured along each of these traces with a "gage length" of S/10. The results of analyses of two samples are shown in Table I. The area included between the S/2 and S distance from the interface could be considered homogeneous within the sensitivity of the measuring technique. This value was used as a proportionality factor to evaluate an arbitrary carbon content of homogeneous austenite, and also as a parameter by which error in measurements could be evaluated. Results of the lineal analysis are shown in Figs. 2 and 3. Fig. 4 shows the statistical nature of the interlamellar spacing for all lamellae measured in this

Jan 1, 1954

By R. H. Richman

Coarse-grained Fe-Ni-C martensites formed at subzero temperatures were strained in compression at room temperature and the plastic deformation modes examined as a funclion of carbon content. At very low carbon levels, defovmation occurs hy wavy slip; commencing at about 0.05 pct C, mechanical twinning accounts for an increasing proportion of the plastic flow. Beyond approximately 0.4 pct C the deformation appears to be entirely by mechanical twinning. The habit planes of the operative twin modes were determined to be (113), (0131, and "(089)" in decreasing frequency of occurrence. Some of the implicaticms of Ihe o6served deformation modes upon the structure and properties of ferrous martensites are discussed. METALLURGISTS have long sought to explain the mechanical properties of ferrous martensites, particularly the extraordinary hardness and strength of the high-carbon varieties. Until recently the lack of precise knowledge of the structure of martensite crystals was the most serious barrier to understanding; however, the advent of thin-foil techniques for transmission electron microscopy has removed much of the mystery from martensite structure. Observations by Kelly and Nutting,"' and many others since, indicate that Fe-C based martensite crystals are internally twinned to a degree dependent upon the carbon content, and that a martensite plate containing 0.8 wt pct C or more consists of a stack of twin-related lamellae with each lamella on the order of l00A thick. Such a structure would be expected to influence greatly all aspects of metallurgical behavior, and many of the properties of Fe-C based martensites have been rationalized accordingly. Recent independent experiments led Winchell and cohen3 to conclude that the strength of ferrous martensite is derived primarily from solid solution hardening of the iron lattice by interstitial carbon atoms. Strength contributions from precipitation, dislocation-atmosphere interactions, clustering, short-range order, crystallite size, and so forth, were considered to be of secondary importance. In the view of Winchell and Cohen, the twinned structure of martensite serves mainly to limit the effective length of dislocation lines in the lattice, and thereby confers an added measure of hardening. Few properties of metallic crystals are as sensitive to metallurgical structure as are deformation mechanisms. It is somewhat surprising therefore, that, except for metallographic evidence of mechanical twins in strained martensite,4 no systematic examination of plastic deformation

Jan 1, 1963

W. R. Ingalls, since 1905 editor of the Engineering and Mining Journal, retires from that position with the issue of Mar. 22, to open offices in New York City as a consulting engineer. The severing of this connection .will not be complete, however, as Mr. Ingalls will continue as consulting editor, and will handle the metal-market quotations in the Journal which are now the accepted authority for the government settlements of ore importations and the basis of practically all the ore settlements between miners and smelters throughout' the country. No greater compliment can be paid to Mr. Ingalls than this, unless it is the recognized fact that these quotations have been made what they are by his ability and his integrity, which secured for him channels of information vital to the accurate estimating of the market, but denied to anyone else. The Journal, under the. strong hand of Mr. Ingalls, has always been the acme of ethics in technical journalism, and the best wish that can he given to his successor, not yet announced, is that the Journal may long continue to live up to the standards not originated, but so consistently maintained and strengthened by Mr. Ingalls. His spelter statistics are accepted as authoritative wherever the English language is read and zinc ore is mined. He has found time during his very arduous years on the Journal to he the author of several works on the resources and metallurgy of zinc, lead, cadmium, etc.; for 5 years was the editor of Mineral Industry; and was consulting engineer for the Bureau of Mines and joint author of their voluminous and authoritative work on mine safety rules. His retirement from the Journal is a distinct loss to every one of the Journal's readers individually and to the profession as a whole. Universal good wishes go with Mr. Ingalls to his new field, which has for a long time been offering him professional attractions that his confining editorial work has not permitted him to accept.

Jan 4, 1919

By H. A. Baumann, C. C. Wright, T. S. Spicer

A LTHOUGH the efficiency of coal utilization has A improved steadily since the turn of the century as a result of continued research and development, little of this increase in efficiency can be credited to improvements in the single retort stoker. There are still numerous problems connected with the burning of coal on this type of unit, the solution of which would be a stimulus to coal and stoker sales and a boon to the user. Among the more critical of these problems is that of burning slack bituminous coal of strong caking tendency and containing large percentages of fine material. With the increased trend toward mechanical mining, it may be expected that in the future an even larger percentage of the coal available for use on this class of stokers will contain higher percentages of the fine sizes, thus aggravating an already serious problem. During the war, the problem of efficient and economic burning of available coals on the single retort industrial stoker, particularly the class 4 stokers (301 to 1200 lb per hr), became quite critical in many localities. In addition to the inherent problems associated with the use of this class stoker, the coals available were frequently not those best suited for use on this equipment and the manpower shortage made it difficult as well as expensive for the consumer to provide the labor necessary to keep the iires in reasonably satisfactory condition. Although exact figures on the number of class 4 stokers are not available, the yearly tonnages of coal consumed are of considerable consequence and have been estimated* at between 15 and 20 million the stoker research staff of the Mineral Industries Experiment Station of The Pennsylvania State College was requested to study the performance of the single retort industrial stoker and to undertake a program of research on the more efficient burning of bituminous coal on this class of unit. Various aspects of overall problem have been investigated since the inception of this program in 1942, only one of which is here reported. General Considerations There are numerous factors which appear directly or indirectly to affect the overall performance of bituminous coal underfeed stokers, such as the caking or matting properties of the coal, the contact relationships between coal and air, the ash fusion characteristics, the burning rate, and the design of the stoker and furnace in which the coal is burned. An analysis of the influence of each of

Jan 1, 1951

By H. A. Baumann, T. S. Spicer, C. C. Wright

A LTHOUGH the efficiency of coal utilization has A improved steadily since the turn of the century as a result of continued research and development, little of this increase in efficiency can be credited to improvements in the single retort stoker. There are still numerous problems connected with the burning of coal on this type of unit, the solution of which would be a stimulus to coal and stoker sales and a boon to the user. Among the more critical of these problems is that of burning slack bituminous coal of strong caking tendency and containing large percentages of fine material. With the increased trend toward mechanical mining, it may be expected that in the future an even larger percentage of the coal available for use on this class of stokers will contain higher percentages of the fine sizes, thus aggravating an already serious problem. During the war, the problem of efficient and economic burning of available coals on the single retort industrial stoker, particularly the class 4 stokers (301 to 1200 lb per hr), became quite critical in many localities. In addition to the inherent problems associated with the use of this class stoker, the coals available were frequently not those best suited for use on this equipment and the manpower shortage made it difficult as well as expensive for the consumer to provide the labor necessary to keep the iires in reasonably satisfactory condition. Although exact figures on the number of class 4 stokers are not available, the yearly tonnages of coal consumed are of considerable consequence and have been estimated* at between 15 and 20 million the stoker research staff of the Mineral Industries Experiment Station of The Pennsylvania State College was requested to study the performance of the single retort industrial stoker and to undertake a program of research on the more efficient burning of bituminous coal on this class of unit. Various aspects of overall problem have been investigated since the inception of this program in 1942, only one of which is here reported. General Considerations There are numerous factors which appear directly or indirectly to affect the overall performance of bituminous coal underfeed stokers, such as the caking or matting properties of the coal, the contact relationships between coal and air, the ash fusion characteristics, the burning rate, and the design of the stoker and furnace in which the coal is burned. An analysis of the influence of each of

Jan 1, 1951

By W. Edeburn, H. R. Fife

An extended study of dustproofing Freeport-seam coal has emphasized several fundamental features in the successful treating of bituminous coals. The extent of the exposed surface area and its absorption propcrties for the dust-retaining film were found to be the most critical factors affecting the efficiency of fly-dust prevention. From recently published screen data and specific surface-area measurements on United Kingdom coals, an approximation of the surface exposed by mine-run coal and by 1-in. slack was made. The total surface area exposed by an average tori of this mine-run coal was estimated at 3768 sq. yd., while a ton of 1-in. slack represents a total surface area of 8779 sq. yd. with no additions for porosity. It is important in coal treating to consider that in mine-run coal the fraction above 1/4 in. in size represents 79.5 per cent of the total weight, but only 4 per cent of the total surface, while the fraction below 150 mesh contains 47 per cent of the total surface and only 1.2 per cent of the total weight. Also, one should appreciate that, in a 1-in. slack, the domestic stoker fraction (1 in. to 8 mesh) contains 76.3 per cent of the weight and 8.2 per cent of the surface, while the fraction below 150 mesh represents 3.3 per cent by weight and 54.8 per cent by surface area. Wax extraction data on 1-in. to 0 slack from mine-run treated Freeport-searn coal showed that the coating was distributed uniformly as a function of exposed surface; hence, nonuniformly on a weight basis. This distribution of the coating on mine-run coal therefore limits the extent of treating that is desirable on bituminous coal at this point in the preparation. The treatment of Freeport mine-run coal before it reached the tipple gave a 70 to 80 per cent reduction of fly-dust in the tipple, a satisfactory treated commercial slack coal, and an indicated change in the trend of tipple degradation. The premium-treated domestic sizes required a supplemental treatment for complete dustproofness. The actual cost of the pretipple and supplemental treatments was very low per ton of coal treated, while the net or true cost was sufficiently

Jan 1, 1938

By W. Edeburn, H. R. Fife

An extended study of dustproofing Freeport-seam coal has emphasized several fundamental features in the successful treating of bituminous coals. The extent of the exposed surface area and its absorption propcrties for the dust-retaining film were found to be the most critical factors affecting the efficiency of fly-dust prevention. From recently published screen data and specific surface-area measurements on United Kingdom coals, an approximation of the surface exposed by mine-run coal and by 1-in. slack was made. The total surface area exposed by an average tori of this mine-run coal was estimated at 3768 sq. yd., while a ton of 1-in. slack represents a total surface area of 8779 sq. yd. with no additions for porosity. It is important in coal treating to consider that in mine-run coal the fraction above 1/4 in. in size represents 79.5 per cent of the total weight, but only 4 per cent of the total surface, while the fraction below 150 mesh contains 47 per cent of the total surface and only 1.2 per cent of the total weight. Also, one should appreciate that, in a 1-in. slack, the domestic stoker fraction (1 in. to 8 mesh) contains 76.3 per cent of the weight and 8.2 per cent of the surface, while the fraction below 150 mesh represents 3.3 per cent by weight and 54.8 per cent by surface area. Wax extraction data on 1-in. to 0 slack from mine-run treated Freeport-searn coal showed that the coating was distributed uniformly as a function of exposed surface; hence, nonuniformly on a weight basis. This distribution of the coating on mine-run coal therefore limits the extent of treating that is desirable on bituminous coal at this point in the preparation. The treatment of Freeport mine-run coal before it reached the tipple gave a 70 to 80 per cent reduction of fly-dust in the tipple, a satisfactory treated commercial slack coal, and an indicated change in the trend of tipple degradation. The premium-treated domestic sizes required a supplemental treatment for complete dustproofness. The actual cost of the pretipple and supplemental treatments was very low per ton of coal treated, while the net or true cost was sufficiently

Jan 1, 1938

By Frederic Benard

RECOVERY of selenium and tellurium at Copper Cliff by the Ontario Refining Co. has been previously described by the writer.1 During 1935 a new building was erected to house this operation and description of the new plant and process form the subject of this paper. The building, of modern steel and tile construction, covers an area of 5900 sq. ft. with a volume of approximately 165,000 cu. ft. The large monitored center bay is flanked by two smaller outside bays, one of which is devoted to the tellurium section. All equipment, ceilings and upper walls, are treated with aluminum paint, giving good illumination and facilitating good housekeeping, essential from a health standpoint in handling material of this nature.

Jan 1, 1938

By David R. Poirier

Activity data of carbon as a function of both temperature and composition throughout the stable austenite range is correlated by mearts of an equation derived from a quasi-chemical model. The carbon activity data of austmite for temperatures between 800° and 1200°C are utilized in conjunction with the activity of carbon calculated for the y solidus using the activity of carbon in liquid iron and published austenite-liquid equilibria. The results agree very well with Chip-man's correlation; however, a small difference in the activity of carbon in the high-temperature range of the austenite field is evident. Excellent agreement is found for the heat of solution of graphite in infinitely dilute austenite; from this study the value is 10,550 cal as compared with Chipman's value of 10,680 cal. AS part of a program to study microsegregation in dendritic solidification of ternary Fe-C-Cr alloys, it was desirable to be able to describe the equilibria between austenite and liquid iron in Fe-C-Cr alloys. In this regard, it was necessary to correlate existing data on the activity of carbon in Fe-C austenite as a function of both temperature and composition. At that time, Chipman's analysis1 of the thermodynamics of binary Fe-C austenite was not available. It will be shown that this study and Chipman's study agree rather well throughout the stable austenite range of temperature and composition; however, some small differences appear at temperatures greater than the eutectic temperature. Benz and Elliott 2 presented isoactivity lines for austenite superimposed on their revised Fe-C phase diagram. Using an expression from Darken and Gury 3 representing Smith's4 activity data between 800" and 1000°C, they found that the activities extrapolated above 1000°C to the solidus did not agree with the activities determined from the corresponding liquidus compositions. It is the purpose of the following argument to reconcile carbon activity data of austenite with the activity in liquid Fe-C alloys as determined by Rist and Chipman. 5 In addition, a simple analytical expression is sought for computational convenience. ACTIVITY DATA OF CARBON IN ZRON Fig. 1 shows the activity of carbon in Fe-C austenite as determined by Smith, 4 Schenck and Kaiser, 6 Scheil et a1.,7 and Bungardt et al.' The lines are merely drawn to separate the data into the respective isotherms. These data are inadequate to determine the activity of carbon at temperatures greater than 1200°C. The activity coefficient in Fe-C liquid alloys was assumed by Rist and chipmans to obey the following

Jan 1, 1969

By P. D. Hunt, B. Tani, M. G. Chasanov, R. Schablaske

The Zn-Vphase diagram was studied by thermal. metallographic, X-ray, and sampling techniques. Three ternary phase equilibria were observed: Mutual solid solubilities in vanadium and zinc appear to be negligible. The liquidus line is retrograde from 670° to 756°C. 1 HE only information in the literature relating to the Zn-V system was a study of corrosion of vanadium by liquid zinc' and an examination of the effectiveness of zinc coatings in protecting vanadium-base alloys from oxidation at high temperatures.2 Establishment of the Zn-V phase diagram was undertaken as part of a study of transition metal solubilities in liquid metal solvents. Chemical, metallographic, thermal, and X-ray diffraction analyses were used to determine the diagram. MATERIALS AND EXPERIMENTAL PROCEDURES Vanadium (99.86 pct) in the form of powder and small chips was employed. Stick zinc (99.99 pct; major impurities: 10 to 15 ppm Pb and 20 ppm Cu) was used in the liquidus determinations and thermal analyses; zinc powder (98.80 pct) was used to prepare intermediate compositions. The liquidus lines were determined by chemical analysis of filtered samples of the saturated melts. The apparatus and sampling techniques were similar to those described by Martin, et al.3 The entire metal sample was dissolved to preclude analytical errors due to segregation on cooling. Vanadium was determined amperometrically, using iron (11) as the titrant,4 to an estimated accuracy of 1 pct. Standard techniques of thermal analysis were employed to examine alloy specimens contained in alumina crucibles under helium. Heating and cooling rates were about 1°C per min. At least five heating and cooling cycles over the range 420° to 700°C were performed for each of two Zn-15 pct V alloys. A Zn-0.2 pct V alloy was used in the determination of the eutectic temperature. The separation of intermediate phases from zinc-rich alloys was carried out by selective leaching with ammonium nitrate solutions. For further investigation of intermediate phases 1/4 in. diam powder compacts were prepared by pressing at 80,000 psi and were annealed in argon at 415" to 450°C for 10 days. Larger quantities of intermediate phases were prepared in sealed tantalum capsules heated in a rocking furnace. Temperatures were determined to an estimated accuracy of 0.5°C with a Pt/Pt-10 pct Rh thermo-

Jan 1, 1963

By J. Rogers, H. F. A. Hergt, K. L. Sutherland

IN 1938 Ralston4 reviewed the many attempts to find a satisfactory collector for the separation of cassiterite from its ores and in 1944 Dean and Ambrose2 summarized some further attempts. Generally, soaps and amines are effective but nonselective collectors. We have discovered that reagents containing either the polar group -SO4- or _S03- are excellent collectors for cassiterite and promise to be selective.1 The response to these reagents of cassiterite and of minerals commonly associated with it was studied, using the captive-bubble technique. Using these fundamental data, the practicability of separation and concentration of tin was investigated by flotation tests in a 2000gram Denver cell. EXPERIMENTAL METHODS Reagents All inorganic reagents were of Analar grade. The preparation and purification of sodium cetyl sulphate, cetyl trimethyl-ammonium bromide, laurylamine and cetylamine have been previously described.5 The other collectors were commercial surface-active agents, which were used without purification. Tests Captive-bubble Tests and Cylinder Flotation Tests have been previously described.5-10 The full lines shown in the figures relating solution composition to contact (flotation) distinguish solutions in which contact (flotation) is possible from those in which it is not. The curve is derived by successive approximation and the accuracy is ±0.2 pH units and ± 5 mg. per liter of collector or depressant. Solution compositions for which it was shown experimentally that contact or flotation is possible are marked by a circle, those for which it is not possible, by a cross, and those for which it is doubtful by a cross within a circle. It is assumed that at all other solution compositions within (without) the curve, contact or flotation is possible (not possible). After testing in the collector solution, the mineral was removed, washed, and tested by the captive-bubble method in water, or floated in a cylinder with frother only. In this way the composition of solutions in which a mineral was conditioned but in which properties of the collector solution prevented contact or flotation can be defined. The composition of solutions in which conditioning was possible lie between the full and broken curve, and the experimental results are indicated by a square. The curves show the limits of composition of solutions in which flotation in a cell would be possible but many factors other than those considered in these tests determine recovery and grade of a given mineral in practice. Flotation Tests in 500 and 2000-gram Denver Submachines.--Melbourne tap water, containing 12 parts calcium, 6 parts

Jan 1, 1947

By R. Priestner, R. F. Krause

Solid, cylindrical crystals of a iron have been fractured at 10°K by the simultaneous application of tension and torsion stresses. Thus, a complex distribution of normal (sN) and shear (ss) stresses existed in a cleavage plane at fracture. In every crystal the clearage-plane normal was inclined to the specimen axis, so that a unique point, M*, in the operative cleavage plane was defined where the quantities sn and s2 N + s2 S) were maximized. It is shown that the maxirrzum resolved normal stress on the cleavage plane at fracture decreased as the resolved shear stress in the cleavage plane at M* increased. Thus, a normal stress la?*! for fracture was not satisfied. A fracture law which takes shear stress into account. and which predicts that (s2 N +s2S) should be constant, is to be preferred. However, the data is best represented by a linear dependence of sN on sS, sS which 110 physical significance can be attached. It is suggested that the fracture-nucleating -mechanism is a short-range one. A critical stress law has not yet been unequivocally established for the propagation of cracks in metals. Measurements of the tensile fracture stresses of variously oriented zinc single crystals1 failed to establish the normal stress law expressed by In Eq. [1], sN is the fracture stress, P, resolved normal to the fracture plane, and 0 is the angle between the fracture -plane normal and the stress axis. Similarly, a comprehensive investigation failed to verify the normal stress law for the tensile fracture of a-iron single crystals.' However, a subsequent investigation,3 using iron from the same ingot, presented fracture data which obeyed the normal stress law. It has been shown previously4,5 that the Griffith criterion for fracture6 does not predict such a normal stress law. This result is of particular significance in considering the fracture of metals, such as zinc and iron, which may fail by cleavage. In these metals fracture propagates in a well-defined "cleavage" plane, whether or not an applied stress is normal to it. When the cleavage-plane normal deviates from the direction of application of a uniaxial stress, for example, the crack propagates under the combined action of normal (sN) and shear (ss) stresses. When the presence of a resolved shear stress in the crack plane is taken into account, the Griffith criterion is expressed by4

Jan 1, 1967

By H. E. Howe, A. A. Smith

The creep properties of lead alloys have been studied by a number of investigators but most of the work has been done on extruded material and the amount of data available on rolled alloys is surprisingly limited. Greenwood1 and his collaborators investigated various rolled commercial leads containing relatively small amounts of impurities, Phillips2 likewise studied rolled commercial leads, although he did include a few alloys— such as tellurium lead and one per cent antimonial lead. But as far as the authors are aware no data on the creep properties of so-called "hard leads"-—i.e., containing from 4 to 8 per cent antimony—have been published. In this paper some data are presented on a few antimonial lead alloys and compared with a copper-bearing lead. Preparation OF Specimens All the alloys used in this investigation were cast at a temperature of 400°C. into an open cast-iron mold preheated to Ioo°C., the resultant casting being % by I by 10 in. The copper-bearing alloy was cold-rolled by 10 per cent passes to a thickness of 0.100 in. Creep specimens 16 in. long were prepared by clamping the strips between wooden blocks and machining the edges of the strips parallel by means of a plane. Careful manipulation gave parallel specimens with no reduced section and with a minimum of distortion. The antimonial lead castings were hot-rolled in 10 per cent passes at a temperature of I50°C. to a thickness of 0.400 in., the heating being carried out in an electric oven after each pass through the rolls. After the castings had been broken down to 0.400 in., they were allowed to cool to room temperature and then cold-rolled to 0.100 in. with the usual Io per cent passes. Sufficient time was allowed after each pass for the strips to cool to room temperature. The apparatus and method of measuring strain have been adequately described in a previous paper3 and essentially the same practice was used in obtaining the present data. Time-extension curves for only two alloys are given, since these are typical of all. Figs. I and 2 show the time-extension Curves for the copper-bearing alloy A at 30°C. and loo°C., and Figs. 3 and 4 show

Jan 1, 1945

By J. H. Hamilton, J. R. Lewis, J. C. Nixon, C. L. Graverson

Recently there has been much speculation concerning the advantages of using oxygen enriched air or pure oxygen in pyrometallurgical processes. The advantage of using oxygen in the iron blast furnace and elsewhere in ferrous production metallurgy has been given careful consideration and, as a result, several experiments have been tried and a number of papers have recently appeared on this subject.1,2 The use of oxygen in nonferrous smelting likewise poses interesting problems, therefore any experimental data obtained in this area should likewise be of general interest.3 Ashcroft4 in 1933 claimed to have obtained improved results when copper concentrates were roasted in pure oxygen. However, his paper gives neither data nor experimental details. A few years ago a research program was started in this laboratory which had for its objective the determination of the mechanism of oxidation of metallic sulphides under varying conditions. To date we have studied the oxidation of galena,5 sphalerite, and chalcocite. It is a well known fact that copper sul-phde minerals are oxidized slowly by weathering agents, so that the sulphides of copper which find their way into a tailing pond are gradually changed into water-soluble and acid-soluble compounds. Commercially, the oxidation of copper sulphide minerals is accomplished by roasting them at elevated temperatures in air using a suitable (usually multiple hearth) roaster. Most copper smelters are equipped with such roasters. In this phase of the study we were especially interested in determining the effect of temperature on: (I) the air oxidation of chalcocite and (2) the oxidation of chalcocite using commercial oxygen. The amount of sulphur removed as sulphur dioxide, the percentages of water-soluble copper, and of acid-soluble copper were determined for the air oxidation tests. In the tests using commercial oxygen, the percentages of sulphur dioxide, water-soluble copper, acid-soluble copper, water-soluble sulphur and acid-soluble sulphur were determined. For these experiments the temperature was varied from 250 to 700°C. Experimental Preparalion of Chalcocite (Cu2S) Natural chalcocite is not pure, Minerals such as bornite, covellite, and chalcopy-rite may be present. It was decided, therefore, to prepare some chalcocite in our own laboratory. An intimate mixture of sulphur and hool divided metallic copper in the ratio of 4 g of copper to I g of sulphur was prepared. TO this was added a slight excess of

Jan 1, 1949

By R. W. Bartlett

Hydrometallurgical processes for copper flotation concentrates avoid the SO2 emission problems associated with smelting, but they require oxidation of copper to obtain solubilization during leaching. The resulting copper ions must be reduced to metal, which normally requires large amounts of energy or energy equivalent reagents such as hydrogen or iron. The conventional reduction method is electrowinning which is labor intensive and involves 35 to 40% of both the entire operating and capital cost of the better hydrometallurgical processes. There is considerable incentive to reduce the cost and energy required for producing copper ions from solution. Furthermore, it is thermodynamically possible to do this using sulfur contained in the concentrate itself. In fact, the thermodynamic potential of oxidizing sulfur from S+4 to the S+6 state is greater than required to reduce cupric ion to metallic copper.1 Realization of this potential in a practical process would significantly reduce the cost of hydrometallurgical processing of sulfide concentrates because sulfur would become a cost-free reducing agent. An apparently practical method is to use SO: and HSO3 ions, obtained by ammonia scrubbing of SO2 from a concentrate roaster gas, to reduce leached copper to metal in an autoclave. This reduction step is the Jumau 1907 A series of steps, including sulfite reduction, constituting a crude flowsheet was suggested by Parker in 1976.3 The present paper describes a detailed complete. sulfite process flowsheet based on materials and energy balances, discusses the chemistry, and discusses further work that is required to develop this process. Process materials, utilities costs, and energy requirements are projected to be unusually low because of the utilization of sulfur from the concentrate. Process Description The sulfite reduction process requires a copper concentrate containing approximately as much sulfur on a weight basis as copper. For those few concentrates that are deficient in sulfur, additional sulfur can generally be obtained by allowing more pyrite to float in the concentration process. The process steps, shown in [Fig. 1], are (1) a fluid bed roast of the concentrate, (2) a leach of the roaster calcine using recycled barren liquor from the reduction autoclave, (3) scrubbing of the SO2 gas with ammonium sulfite liquor to produce ammonium bisulfite, (4) reduction and precipitation of copper in an autoclave by combining part of the SO2 scrubber effluent (SO5