Search Documents

By A. Romero-Juarez

This paper is concerned with the effect of propping-agent concentration on flow capacity of a fracture in the case in which there is embedment of the propping agent. Previous published studies have shown definitely that there is a relationship between fracture flow capacity and prop ping-agent concentration, and it has been shown that the theoretical results are confirmed by laboratory experiments. The problem of directly finding sand concentration for maximum flow capacity of a sand-propped fracture is solved, and formulas and charts are given to obtain this concentration under various conditions of effective overburden pressure, medium sand-grain diameter and rock properties. It is shown that, for the same effective overburden pressure and the same rock characteristics, optimum sand concentration in pounds per gallon does not depend on medium sand diameter. For conditions met in bydraulic fracturing operations, it is found that sand concentration in grains per square inch for maximum flow capacity varies within a wide range of values; this indicates the convenience of using data of fracturing pressure and rock characteristics for calculating sand concentration in order to achieve the best results in fracture treatments. INTRODUCTION It has been pointed out in the published literature1 that one important factor controls the success of a hydraulic fracturing operation — the propping of the fracture. The main effect of the propping agent is to hold the fracture open by means of the reaction forces that oppose the pressure due to the overburden. It is assumed in this paper that the propping agent is sand, that the grains are spherical and uniform in size, and that this sand is distributed in a monolayer in the fracture. The existence of a sand concentration value for maximum fracture flow capacity has been recognized since the publication of one of the first studies on the subject.2 In the reference cited, flow capacity was assumed to be proportional to the cube of the fracture volume per square inch not filled by sand. The obtained experimental curves relating to flow capacity and sand concentration had the same appearance as the curves obtained with the afore-mentioned assumption. Recent work3 has shown that fracture permeability, in the case of a monolayer, can be calculated accurately by means of a modified Kozeny-Cacman equation; thus, it can be shown that fracture pqmeability is a function of free volume in the fracture and of the rock and sand wet surfaces. The flow capacity of a fracture is dependent on the permeability of the fracture and on the fracture width. If all excessive quantity of sand is present in the fracture, its width may be large but its permeability i:; low due to the greater flow resistance; too few grains of sand per square inch are present in the fracture, sand embedment in the rock is greater and the width becomes small enough to appreciably decrease the rate of flow. To determine optimum conditions of flow, therefore, it is necessary to know the dependence of fracture width on density or concentration of propping agent. This relation is given in a study4 in which the approach to embedment is similar to the one made in a penetration hardness test of metal. With the equacions presented by Darin and Huitt,3 the number of sand grains per square inch that results in maxirnum fracture capacity can be determined graphically by plotting fracture capacity vs sand concentration. Since the relationship between fracture capacity and sand concentration may be considered known, one is led to formulate the analytical problem of directly determining sand concentration for maximum fracture flow capacity, in order to study the effect of the various quantities that come into the process. The solution of this problem appears to be interesting both from the viewpoint of fluid mechanics and from the practical viewpoint of oil production in hydraulic fracturing treatments. EQUATION FOR FRACTURE FLOW CAPACITY It can be shown3 that the fracture flow capacity of a monolayer is given by the following expression,

By J. J. Strohl, H. J. Schwellenbach

This paper relates the results obtained by decreasing the size of feed to a rod mill screen circuit. As would be expected, added production was gained and a finer grind with no tonnage loss was made possible. THE MacIntyre mill of the National Lead Co. has four parallel sections in which magnetic and gravity separations are made. Ore from a 5000-ton bin is fed by Hardinge constant weight feeders to a 6x12-ft open-end Marcy rod mill in each section. Rod mill discharge is bucket elevated to two 4x10-ft Tyrock screens whose oversize is returned to the rod mill. Screen undersize is pumped to Crockett separators for magnetite removal, and the Crockett tailings are sized and tabled to make an ilmenite concentrate. Minus 200-mesh material, overflowed by the Crockett and Dorrco sizers is thickened, de-slimed, and concentrated by flotation.' By 1948, the development of a successful slime flotation process and numerous improvements in the gravity circuit of the mill had increased the capacity of the available concentrating equipment. At the same time, improvements in the operating techniques of the dry crushing plant and improved feeding of the crusher by the mining department had appreciably increased the production rate per operating hour in that plant. Therefore, it was decided to take advantage of the added crusher capacity to produce a finer rod mill feed and in that way increase grinding capacity. At approximately the same time, finer screens were installed in the rod mill circuits to give finer grind and thus improve liberation of the magnetite and ilmenite from the gangue and from one another. Prior to the first part of 1948, a 3/4-in. limiting screen was used for sizing rod mill feed. The first reduction in crushing plant screen size was to 1/2 in. With this screen, the circulating load in the tertiary crushing circuit was too high and plant capacity dropped below a practical hourly rate. A 9/16-in.-sq opening screen, installed next, proved satisfac-

Jan 1, 1951

By H. J. Schwellenbach, J. J. Strohl

This paper relates the results obtained by decreasing the size of feed to a rod mill screen circuit. As would be expected, added production was gained and a finer grind with no tonnage loss was made possible. THE MacIntyre mill of the National Lead Co. has four parallel sections in which magnetic and gravity separations are made. Ore from a 5000-ton bin is fed by Hardinge constant weight feeders to a 6x12-ft open-end Marcy rod mill in each section. Rod mill discharge is bucket elevated to two 4x10-ft Tyrock screens whose oversize is returned to the rod mill. Screen undersize is pumped to Crockett separators for magnetite removal, and the Crockett tailings are sized and tabled to make an ilmenite concentrate. Minus 200-mesh material, overflowed by the Crockett and Dorrco sizers is thickened, de-slimed, and concentrated by flotation.' By 1948, the development of a successful slime flotation process and numerous improvements in the gravity circuit of the mill had increased the capacity of the available concentrating equipment. At the same time, improvements in the operating techniques of the dry crushing plant and improved feeding of the crusher by the mining department had appreciably increased the production rate per operating hour in that plant. Therefore, it was decided to take advantage of the added crusher capacity to produce a finer rod mill feed and in that way increase grinding capacity. At approximately the same time, finer screens were installed in the rod mill circuits to give finer grind and thus improve liberation of the magnetite and ilmenite from the gangue and from one another. Prior to the first part of 1948, a 3/4-in. limiting screen was used for sizing rod mill feed. The first reduction in crushing plant screen size was to 1/2 in. With this screen, the circulating load in the tertiary crushing circuit was too high and plant capacity dropped below a practical hourly rate. A 9/16-in.-sq opening screen, installed next, proved satisfac-

Jan 1, 1951

By Oberlin Smith

The use of cast-iron tools, with chilled cutting-edges, for lathes, planers, boring-mills, etc., is not, as Gar as I can learn, very extensive in the United States, or perhaps in England and other parts of Europe. I have, however, no data to guide me in regard to foreign

Jan 1, 1891

By James C. Word, R. M. McLouski

This paper will describe the development and application of large-scale integration techniques employed in the fabrication of a germanium multielement array. The array consists of 100 by 228 PNP bipolar transistors fabricated on 5 mi1 centers. Back-biased p-n junction techniques are used for electrical isolation of the individual elements. The end use of the array is a high resolution, large area IR sensor. The monolithic array is fabricated in 1 ohm-cm p-type germanium epitaxially deposited on 6 ohm-cm n-type substrate. Epitaxy was accomplished through the hydrogen reduction of germanium te trachloride. Di-borane was used as the dopant. Base regions are achieved by the diffusion of arsenic from doped oxide or arsine sources. Oxide-masking of the arsenic im-pzlvity was achieved by the chemical deposition of a boron doped glass. The emitter is formed by an aluminum alloy diffusion technique. Vacuum deposited aluminum is used for the emitter, interconnections, and for the contact and bonding pads. ALTHOUGH a great volume of literature pertaining to the development of large scale integration techniques (LSI) has been published for silicon and in particular silicon imaging applications,' to date only a small number of similar devices have been constructed using germanium technology.' Since the physical and chemical properties of germanium are vastly different from those of silicon, the fabrication technology for integrated structures in germanium is also different from that of silicon. In particular germanium does not possess a stable oxide as can be grown on silicon by heating in an oxidizing ambient for masking of dopants and passivation. This paper describes the application of germanium LSI techniques employed in the fabrication of a multielement infrared sensor array. The array is used in a high resolution, large area infrared sensor for operation in the 0.8- to 1.5-u spectral range. Back biased p-n junction techniques are used for electrical isolation of individual elements. Discrete germanium devices have been fabricated routinely for some time. However, mainly due to the lack of a suitable mask for selective doping and the high current leakages inherent in germanium p-n isolation, few monolithic germanium structures have been constructed. THE INFRARED MOSAIC A cross-sectional view of the array is shown in Fig. 1. The monolithic structure consists of 12,800 PNP transistor elements in a 100 by 128 matrix fab- ricated on 5 mil centers. The emitters of each line of transistors are connected together using aluminum interconnects while the strip collectors are connected together in series at right angles to the emitter lines. The selection of this structure is dictated by the readout technique involved. Access to each element transistor is obtained by applying a bias voltage to a particular collector strip and separately interrogating each emitter row. A charge storage, i.e., an integration mode is used for reading out this particular array Construction techniques available for use with germanium do not include a selective p-type diffusion capability for surface concentrations greater than 10" per cu cm and junction depths greater than about 10 u. This fact limits the type of structure that may be used. Therefore, an array of PNP transistors that did not employ p-type diffusions was chosen. The structure was fabricated by growing a 1 ohm-cm p-type epitaxial layer on a carefully prepared 6 ohm-cm n-type substrate. N-type dopants were used for the isolation and base diffusions and alloyed aluminum was used to form the emitter junctions. The array was then completed by evaporation of aluminum interconnections and contact pads. SUBSTRATE AND SUBSTRATE PREPARATION Germanium substrates of (111) orientation grown by both Czochralski and zone leveling techniques were utilized for mosaic fabrication. Czochralski substrates were preferred because of the lower dislocation densities available in this type of material. Dislocation densities for the Czochralski material were typically less than 3000 per sq cm, while those for the zone leveled material were typically less than 5000 per sq cm. All substrates were uncompensated to minimize thermal conversion problems in subsequent epitaxial and diffusion processing. Both in-house and vendor polished wafers were used. The in-house polishing technique employed consisted of an initial gross chemical etch in CP4 to remove saw damage from both surfaces. This was followed by a chemical-mechanical polishing operation of one side of the wafer. The chemical-mechanical polishing solution used was Lustrox 1000 (Tizon Chemical Co.), and consists of zirconium dioxide, sodium hypochlorite, water and a surfactant. The wafer thickness before and after polishing was typically 0.020 and 0.010 in, respectively. THERMAL CONVERSION The problem of thermal conversion of both the substrate and epitaxial layer was particularly acute because of the relatively low carrier concentrations employed in both regions. This problem has been encountered by other workers in the past.3 Without special treatment before epitaxial growth substrate conversion (n-type to p-type) and changes in the re-

Jan 1, 1970

By Harold Powers

THIS paper presents geophysical and subsurface data observed in the vicinity of Shafts No. 1 and and 5 of the National Lead Co. lead mines at Fredericktown, Madison County, Missouri, see Fig. 1. The area selected is an excellent example to illustrate the close correlation between geophysical data and geological facts as revealed by drilling and mining. Such close correlations make geophysical applications appropriate to the development of known ore-bodies as well as the exploration for new orebodies.

Jan 3, 1953

By James E. Lawver, James L. Wright

This paper describes the design of a cell used to measure the electrical conductivity, or the reciprocal resistivity, of granular materials. It also establishes a quantitative relationship between the electrical conductivity and the electrical separation of selected mineral samples. It is estimated' that the free world produces about 13 million tons of mineral concentrates a year by electrostatic or electrodynamic methods. At least 95% of these concentrates are produced by corona discharge type machines that separate minerals by exploiting the differences in their electrical conductivity. But, what is meant by the electrical conductivity of a mineral? How large a difference in the electrical conductivity of two mineral species is necessary to effect a separation? Just what is the role of conductivity in electrical separations with regard to capacity and selectivity? There is a considerable amount of information in the literature on both the mechanisms of conduction and the values of the electrical conductivity of pure single-crystal mineral specimens. In addition, some insight into the role of mineral conductivity can be obtained by referring to a Bureau of Mines publication' in which 95 minerals have been grouped as conductors or insulators as a function of temperature. The classification was made on the basis of the percent of weight that reported as "conductors" in an electrical separator. But, as is often the case in the mineral industry, practical application leads theory — and there is little useful information in the literature giving any kind of quantitative relationship between electrical conductivity and electrical separations. The problem is a bit complex because electrical conductivity per se — which can be rather easily measured on large, single grains — is not sufficiently informative to permit quantitative predictions of the separability of the mineral system. Practical "high-tension"* separations are made at such feed rates that the band of minerals on the rotor is multilayered in thickness. Thus, the effective conductivities of minerals as seen by a high-tension machine include particle-to-particle contact resistance, which is often a controlling factor in making a separation. This is particularly true when the mineral grains are coated with slime or with a dielectric surface film. From a high-tension separation viewpoint, one is actually concerned with the time required for corona-charged grains to lose enough charge so that the centrifugal force acting on the particles exceeds the image force holding the grains to the rotor. This calculation requires a knowledge of the effective mineral conductivity s. (The conductivity of the metal rotor is sufficiently greater than that of the minerals so that it need not be considered in charge decay calculations.) The charge density at time t can be approximated by the relaxation equation.3 where t 5 charge density at time t r, - charge density when t = 0 cr e total electrical conductivity £ = permittivity The time required for the charge density to fall to l/e of its initial value is called the relaxation time and is numerically equal to €/n. AS defined here, u is the conductivity of an element of homogeneous grains making contact with each other and with a grounded rotor. This paper deals with the design of a conductivity cell used to measure a, or its reciprocal p, the electrical resistivity. CELL DESIGN Initial test work was performed with a cell recommended by ASTM.4 Since the reproducibility with the ASTM cell was not satisfactory, it was decided to

Jan 1, 1970

By I. C. White

Only two factors appear to be directly responsible for the geographic distribution of sulfur in the coal fields of West Virginia: these are the stratigraphic position of the coals in question, and the eastward or westward location of the deposits. There appears to be a progressive increase in the sulfur content of West Virginia coals from the oldest Peqnsylvanian deposits in the Pocahontas, New River, and Kanawha Groups of the Pottsville Series up through the Allegheny, Conemaugh, and

Jan 1, 1920

NORTH AMERICA Number Members Alaska 43 Canada 340 Mexico 205 Newfoundland 4 United States Alabama 39 Arizona 120 Arkansas 11 California 699 Colorado 168 Connecticut 89 Delaware 18 District of Columbia 140 Florida 20 Georgia 6 Idaho 78 Illinois 214 Indiana 77 Iowa 12 Kansas 24 Kentucky 33

Jan 1, 1936

By H. F. Silver

Although the literature indicated that a hydrogen-ated coal bitumen might be used as a substitute for petroleum asphalt and road tar, no work could be found in which the material was actually used or evaluated as a road binder.' Therefore, a study was initiated to investigate the production and properties of a road binder made by hydrogenating coal in the presence of a solvent at elevated temperatures and pressures. HYDROGENATlON PROCEDURE Four different samples of sub-bituminous Wyoming coals and three samples of coals from other states, ranking from lignite to a low-volatile bituminous coal,

Jan 1, 1969

By L. S. Birks

The bainite transformation in a 3.5 pct Ni-1.25 pct Cr steel was studied under various conditions of cooling and stress. Several characteristics may be specified: 1) transformation in the bainite region (925° to 575°F) is very little affected by the manner of cooling from the austenitizing temperature at 1600°F to 575°F)tothe upper limit of bainite transformation at 925°F; 2) starting time for the bainite transformation is the same order of magnitude for either isothermal transformation or continuous cooling, but the rate of transformation is somewhat greater for isothermal transformation; 3) tensile stress accelerates both isothermal and continuous cooling transformation, and 32,000 psi stress changes the form of the isothermal transformation diagram to correspond in appearance to the continuous cooling diagram; 4) transformation for nonlinear, continuous cooling may not be determined directly from the linear, continuous cooling transformation diagram, but may be predicted by assuming first that the fractional amount of austenite transformed in a given small temperature interval depends on the approximate linear cooling rate during that temperature interval and then by summing stepwise over the whole temperature range. IN a previous publication' an X-ray spectrometer was described with which the X-ray diffraction from a specimen could be observed continuously under controlled temperature and tensile stress. This instrument has now been applied to a study of the austenite-bainite transformation in a Ni-Cr steel for both isothermal and continuous cooling conditions, with and without stress. Certain characteristics of the transformation lead to a method of predicting the amount of transformation to be expected at a given temperature for any type of cooling curve. Material and Specimen Preparation The steel chosen for the investigation was a Ni-Cr steel having the composition in the following percentages: 0.30 C, 0.27 Mn, 0.019 P and S, 3.50 Ni, and 1.25 Cr. In order to fabricate specimens suitable for the X-ray spectrometer, a 1/4 in. plate was ground down to 0.060 in. and then cold rolled to about 0.035 in. Next it was heat treated by quenching in oil from 1650°F and tempering at 1200°F for 1 hr. Then it was etched in dilute nitric acid to reduce its thickness to 0.014 in. and cut into blanks in the shape of flat tensile specimens 3 1/4 Vi in. long, 7/16 in. wide, with a notch % in. long and 7/32 in. wide; see Fig. 1. X-Ray Technique Since the X-ray spectrometer has been described in detail elsewhere,' only a brief outline of the principles will be repeated here. A focusing, pow- der-diffraction arrangement' was used, as shown schematically in Fig. 1, and the specimen was mounted vertically in a vacuum furnace (not shown in the figure). The X-rays, moving in a horizontal plane, enter and leave the furnace through beryllium windows. As shown in the figure, X-rays diverging from the line source A are diffracted by the specimen B and converge at the detector slit C. The detector D and the slit C may be set at the proper angle in the horizontal plane to receive X-rays diffracted by either the face-centered phase (austenite) or the body-centered form (ferrite, bainite, martensite). The specimen is heated by electrical conduction between connectors E, and E,, and a Pt—Pt-10 pct Rh thermocouple spot-welded to the center of the notched region on the side away from the X-ray beam indicates the temperature continuously on a Brown recorder. Temperature control is exercised manually with a variable transformer on the input to E,-E,. Any desired time-temperature relationship is easily obtained by first drawing the desired curve on the temperature recorder chart and then adjusting the variable transformer during the run so that the thermocouple

Jan 1, 1957

By R. W. Carpenter, J. C. Ogle

It is possible, by using pack-rolling instead of conventional rolling, to reduce a number of metals to thicknesses of 2µm or less. Such thinfoils are generally made at room temperature without intermediate annealing. In addition, pack-rolled foils fail by developing pinholes at thicknesses near 2µm instead of developing the shear cracks usually observed in cold-rolled ductile metals. This paper presents the results of a general investigation of the deformation substructure and texture developed in copper and iron pack -rolled from 130 to about 2µm thickness. Electron microscopy showed that in both metals a fine (0.2 to 0.5?µ m) deformation subgrain structure formed during pack-rolling; in neither case was this substructure grossly different from substructures formed during conventional rolling. The deformation texture formed in pack-rolled iron was quite similar to usual bcc textures; however, in the case of copper, the cube texture was stable during pack-rolling and the normal copper deformation texture was unstable. It is shown analytically that the constraining pack induced a large hydrostatic pressure in the foils during pack-rolling. The pinhole failure mechanism is attributed to the presence of the large hydrostatic pressure during pack-rolling; this strongly suppressed the growth of shear cracks. The stability of the cube texture in copper is also probably due to the unusuul stress distribution developed during pack-rolling. EXPERIMENTS at several laboratories have shown that very thin foils of the common structural metals and many of the rare earths can be made by "pack-rolling". 1-3 The technique was originally developed to make specimens for nuclear scattering experiments and foils for X-ray filters. It is also useful for making experimental laminar metallic composite bodies and foils thin enough for direct examination by ultra-high voltage electron microscopy without the need for special thinning techniques. Pack-rolling in the present context means a three-layer pack, with the material to be rolled into foil comprising the center layer. The outer two layers, which constrain the foil during reduction, are ordinarily austenitic stainless steel. Typically, a 130 µm (0.005 in.) metal strip can be reduced to a final thickness of 2 µm or less by this process. This is accomplished at room temperature, without intermediate annealing. It has been observed that foils produced by this process do not exhibit at any stage of their reduction the severe work-hardening found in strip rolled by conventional cold-rolling methods. Neither is the failure characteristic the same."&apos; Conventionally cold-rolled ductile metal strip fails by developing shear cracks on planes whose normals nearly bisect the angle between the rolling direction and normal to the rolling plane; these are planes of maximum shear stress. In pack-rolling this mechanism has not been observed; failure occurs by the formation of pinholes on the foil surface (penetrating the foil). If pack-rolling is continued the hole density increases. These differences in behavior imply the existence of appreciably different substructure in pack-rolled foils compared to substructure in conventionally rolled material, or perhaps that the geometry of pack-rolling has an effect on the foil behavior. This paper describes an investigation of deformation substructure and texture in some specimens of pack-rolled copper and iron, and some considerations of the stress distribution in the foils during rolling that result from the geometry of pack-rolling. EXPERIMENTAL DETAILS Three different materials were used for pack-rolling in the present work: soft copper sheet (99.8 pct Cu, 0.03 pct 0, electrolytic tough pitch) and two types of iron, Ferrovac E* and Armco iron. Each was "Crucible Stccl Co. initially in the form of 130 µm annealed strip with grain size ranges of approximately 10 to 40 µm. The initial texture of the copper (determined as noted below) was the normally observed cube type (001)[100]; there was evidence of a small amount of material in the cube-twin orientation reported by Beck and Hu.4 The initial texture of the Ferrovac E was similar to that reported for recrystallized iron by Kurdjumov and sachs,5 who list the principal orientations as {111}<112>, {001}<110> 15degfrom RD and a weak component {112}(110) 15 deg from RD. The starting texture of the Armco iron was not determined. Pack-Rolling Procedure. A four-high mill was used for all specimens. The work roll and backing roll diameters were 1.625 and 5.25 in., respectively. The peripheral roll speed of the work rolls was about 2.5 in. per sec. All foils were initially reduced from 130 to 100 µm by conventional straight rolling and then inserted into a pack, without any intermediate annealing, for further reduction. The pack consisted of an 0.033 in. (838 µm) thick 3 by 6 in. polished sheet of austenitic stainless steel, folded to make a 3 by 3 in. jacket. After folding, the jacket was given a small reduction to close the fold tightly before insertion of the foil. During pack-rolling a constant change in roll spacing was made every third pass. The roll-spacing change corresponded to a 5 pct reduction in thickness for a new pack. This approached a 10 pct reduction when the pack had decreased to about half its original thickness. At this point the deformed pack was discarded and a new one

Jan 1, 1970

By D. S. Tannhauser, I. Bransky

Measurements of the electrical conductivity, the thermal electromotive force, and the deviation from stoichiometry by thermogravimetry were made on ferrous oxide (wüstite) single crystals as well as on poly-crystalline samples in the temperature range of -900" to 1330°C. In the region defined by T 2 1000°C and 1.05 5 O/Fe 5 1.10 the electrical conductivity was shown to be proportional to the sixth root of- the oxygen partial pressure and to be linearly dependent on the deviation from stoichiometry. The absolute Seebeck coefficient of single and polycrystalline wüstite was shown to be independent of temperature in the above region and a p to n transition of the Seebeck coefficient was observed at O/Fe = 1.09 in polycrystalline wüstite. Analysis of the results showed that the predominant defects in wüstite in the above region were doubly ionized cation vacancies. The analysis also ruled out the existence of complexes of the type postulated by Roth, except that below 1000°C there is some evidence of &apos;association of defects. Of the three oxides of iron (FeO, Fe3O4, Fe2O3) only FeO (wüstite) can exist within a wide range of the ratio O/Fe. This has been shown by several investigations of the phase diagram using for instance chemical analysis of quenched samples&apos;-4 or thermogravimetric measurements. 5,8 Darken and Gurry&apos;s1 data for example in the temper- ature range 1100o to 1400°C show that the lowest O/Fe ratio obtainable for FeOl +. is about 1.045 and that the existence range extends to O/Fe = 1.20 at 1400oC. On the basis of detailed analysis of thermogravimetric measurements made by Vallet and Raccah6 the existence of three varieties of wüstite at elevated temperatures was suggested by these authors and by Kleman. It is well-established that wüstite has a NaCl structure with vacant cation sites.3, 8 From a neutron-diffraction study of wüstite samples quenched to room temperature Roth9 concluded that defects in wüstite are mostly complexes composed of two cation vacancies and one interstitial cation in a tetrahedral site. The atomic arrangement in the vicinity of such a defect is similar to that in magnetite, where each occupied tetrahedral site is surrounded by four vacant octahedral positions disposed at the corners of a tetrahedron, so arranged that each vacancy is shared by two tetrahedral cations. Thus there is an average of two vacancies per interstitial. Recent X-ray diffraction measurements made by Smuts10 on quenched wüstite samples confirmed the results of Roth&apos;s neutron-diffraction experiments. Roth&apos;s model of defects in FeO can be regarded as a solid solution of Fe3O4 in FeO; salmon1&apos; used this defect model to calculate the activity of Fe3O1 in FeO at high temperature and claimed good agreement with the results obtained experimentally by Darken and Gurry.&apos; Each missing cation in wüstite is accompanied by two trivalent cations, thus preserving charge neutrality. The "holes" which differentiate between the Fe 2+ and Fe3&apos; states of the ions in octahedral positions can overcome the attractive field of the cation vacancies, and are then free to move through the crystal as charge carriers. A similar picture holds for COO, NiO, andMnO.l2, 13 Localization of the charge carriers in transition

Jan 1, 1968

By L. S. Darken

Measurements of the electrical conductivity, the thermal electromotive force, and the deviation from stoichiometry by thermogravimetry were made on ferrous oxide (wüstite) single crystals as well as on poly-crystalline samples in the temperature range of -900" to 1330°C. In the region defined by T 2 1000°C and 1.05 5 O/Fe 5 1.10 the electrical conductivity was shown to be proportional to the sixth root of- the oxygen partial pressure and to be linearly dependent on the deviation from stoichiometry. The absolute Seebeck coefficient of single and polycrystalline wüstite was shown to be independent of temperature in the above region and a p to n transition of the Seebeck coefficient was observed at O/Fe = 1.09 in polycrystalline wüstite. Analysis of the results showed that the predominant defects in wüstite in the above region were doubly ionized cation vacancies. The analysis also ruled out the existence of complexes of the type postulated by Roth, except that below 1000°C there is some evidence of &apos;association of defects. Of the three oxides of iron (FeO, Fe3O4, Fe2O3) only FeO (wüstite) can exist within a wide range of the ratio O/Fe. This has been shown by several investigations of the phase diagram using for instance chemical analysis of quenched samples&apos;-4 or thermogravimetric measurements. 5,8 Darken and Gurry&apos;s1 data for example in the temper- ature range 1100o to 1400°C show that the lowest O/Fe ratio obtainable for FeOl +. is about 1.045 and that the existence range extends to O/Fe = 1.20 at 1400oC. On the basis of detailed analysis of thermogravimetric measurements made by Vallet and Raccah6 the existence of three varieties of wüstite at elevated temperatures was suggested by these authors and by Kleman. It is well-established that wüstite has a NaCl structure with vacant cation sites.3, 8 From a neutron-diffraction study of wüstite samples quenched to room temperature Roth9 concluded that defects in wüstite are mostly complexes composed of two cation vacancies and one interstitial cation in a tetrahedral site. The atomic arrangement in the vicinity of such a defect is similar to that in magnetite, where each occupied tetrahedral site is surrounded by four vacant octahedral positions disposed at the corners of a tetrahedron, so arranged that each vacancy is shared by two tetrahedral cations. Thus there is an average of two vacancies per interstitial. Recent X-ray diffraction measurements made by Smuts10 on quenched wüstite samples confirmed the results of Roth&apos;s neutron-diffraction experiments. Roth&apos;s model of defects in FeO can be regarded as a solid solution of Fe3O4 in FeO; salmon1&apos; used this defect model to calculate the activity of Fe3O1 in FeO at high temperature and claimed good agreement with the results obtained experimentally by Darken and Gurry.&apos; Each missing cation in wüstite is accompanied by two trivalent cations, thus preserving charge neutrality. The "holes" which differentiate between the Fe 2+ and Fe3&apos; states of the ions in octahedral positions can overcome the attractive field of the cation vacancies, and are then free to move through the crystal as charge carriers. A similar picture holds for COO, NiO, andMnO.l2, 13 Localization of the charge carriers in transition

Jan 1, 1968

By Charles C. Templeton

Any explanation of the nature of multiphase fluid flow through porous media must ultimately involve a knowledge of the mechanism of such flow through the individual pores of the medium. To provide quantitative information of the latter type, a study was made of gas-liquid and liquid-liquid displacements in single uniform Pyrex capillaries with diameters as small as 4 microns. Quantitative observation of air-liquid displacements with zero contact. angle indicates the adequacy of a model based on Poiseuille&apos;s Law and the independence of capillary pressure and interfacial velocity. Consequently, this work discounts previous claims that flow is abnormally retarded in very small capillaries. For the displacement of a very viscous oil by water in a capillary initially filled with water, flow is faster than predicted by the above model. This behavior is probably due to the existence of a thin annular film of water between the oil column and the capi1lary wall as postulated by Yuster. INTRODUCTION The need for experimental observation of the microscopic nature of multiphase fluid flow, to further the understanding of the results of macroscopic flow investigations, has been previously recognized. Chatenever and Calhoun1 in connection with the API Project 47B have extensively studied the flow of fluids through layers of glass or lucite spheres between glass or lucite plates. Lowman2 prepared an interesting film concerning flow in a single capillary, using an apparatus which made a moving interface appear stationary in the field of a microscope. The purpose of the present investigation was to deter- mine what contribution might be made to this field by comprehensive quantitative observation of gas-liquid and liquid-liquid displacements in single capillaries of uniform, very small diameter. The techniques used are similar to those of Lowman but incorporate improvements necessary for quantitative work. Quantitative observations must begin with fluids of simple chemical composition to provide a basis for analyzing the more complex behavior that may be expected with natural reservoir fluids. However, some qualitative observations on systems involving crude oils are presented. Experiments of this sort involve the observation of the velocity of the interface separating two fluids, and have been performed in horizontal or vertical capillaries by several investigators.3,4,5,6,7,8 The most general treatment of their mechanics, by Brittin,9 involves forces due to capillarity, viscous resistance, gravity, an "end-drag" effect, and the rate of change of momentum of the capillary contents. Since the range of pore diameters of interest in petroleum reservoirs is about 0.1 to 100 microns, it was desired to perform these experiments in the smallest capillaries possible, to ascertain whether capillary diameter had any effect on the existing theory based on data from larger capillaries.* It was also important to be able more systematically to vary the direction and rate of displacement than was done by previous investigators. Finally, to concentrate attention on viscous and capillary forces by eliminating gravity as a parameter, this study involves only horizontal capillaries. The work of Eley and Pepper&apos; with a "large" (0.766-mm diameter) horizontal capillary is the previous investigation which is most similar to the present method of quantitative observation. Here capillaries with diameters as small as 4 microns will be studied.

Jan 1, 1955

By T. P. Papazoglou, N. A. D. Parlee, W. C. Phelps

PRACTICAL designs for good "home made" molybdenum furnaces are hard to find in the literature. The one described briefly below left something to be desired but was good enough to operate as a rather long (30 in.) two-zone furnace for periods of over 2 months at temperature (1400° to 1600°C) without shutdown. The principal problem in our application was to establish a temperature profile with two distinct constant-temperature zones and no dip between the zones. This and other problems mentioned below would not arise, however, if both zones were operated at the same temperature and if a shorter furnace were acceptable. Since molybdenum windings oxidize very rapidly when heated in air, impervious refractory tubes were used for both the furnace core and the outer jacket tube shown in the accompanying figures. A protective atmosphere of forming gas (10 pct H2, 90 pct N2) was continuously passed through the gas-tight annular volume between the core and outer jacket. The water-cooled copper ends shown in Figs. 1 to 3 sealed the ends of the tubes. Annealed molybdenum wire (40 mil) was wound on the recrys-tallized alumina core (35.5 mm OD by 28.5 mm ID by 30 in.) at a spacing of 0.36 in. The spacing was reduced to 0.29 in. close to the ends to partially compensate for end heat losses. Fig. 2 shows two molybdenum-ground lead taps off the center of the winding to produce the two independect temperature zones. The ground lead was insulated with 1/4-in. alumina tubing and connected to the grounded copper end by passing the wires through the gas port tube and crimping each wire into notches cut at the mouth. To prevent sagging of the core at high temperatures, refractory "troughs" were cut from alumina and mullite tubing to cradle the core. The support "troughs" which were 6 in. long and located about 5 in. from each end of the annular volume also served as radiation shields. In view of the different expansion coefficients and operating temperatures of the core and outer jacket (3.5 in. OD by 3 in. ID by 30 in.), the ends of the tubes were smoothed and squared to produce good sealing surfaces, and the core was ground 1/32 in. shorter than the outer tube. The power terminals were passed through their respective conductor ports which were internally lined with alumina tubing and sealed with Armstrong adhesive A-6 leaving about 1 in. of protruding lead wire for external connections. (Adhesive A-6 is a two-component system consisting of an epoxy-type resin with a mineral fibrous filler and an amine catalyst.) Figs. 1 and 3 show the entire assembly of concentric refractory tubes, copper ends, and sealing o rings, held together with two brass flanges and 3/8-in. bolts with heavy springs for dimensional flexibility. The furnace shell (19 by 19 by 30 in.) consisted of a steel frame with sheets of transite forming a box. The copper ends protruded through two 3.75-in. circular holes cut at the center of each transite square end. Thermal insulation next to the transite exterior was effected by K-23 B&W bricks alld in a central volume of approximately 9 by 9 by 30 in. a row of K-30 bricks was lined up to support the hot assembly. The rest of the volume around the outer

Jan 1, 1965

By Keith C. Hendrick

The mining industry of Canada, stretching from coast to coast and reaching into the most remote regions of the country, is of fundamental importance to the national economy and the well being of many communities outside the main urban areas. The production, processing and transportation of a host of mineral products provide employment for about 9% of the country&apos;s labour force; and their shipment to export markets provides an important contribution to the balance of payments. In 1976 Canada&apos;s metal and mineral production had a value of $5.24 billion, of which zinc and lead accounted for $862 and $129 million respectively, or 19% of the total. By all standards the Canadian zinc and lead industry is large and, therefore, important to the country as a producer and the world as a supplier. This report will review the development, describe the present status and discus current problems and future potential of the industry. The discovery and successful development of the major lead-zinc deposits at Kimberley, British Columbia, provided Canada with a solid base from which to grow. The breakthrough in metallurgical technology using differential flotation to separate the lead and zinc sulphides and the refining of high purity metal by electrolytic methods not only helped Canada to compete with other world producers but also provided a new source of these metals at prices and qualities that encouraged the development of new end uses.

Jan 1, 1977

By N. A. D. Parlee, E. M. Sacris

OVER 55 years ago, Sieverts and Hagenacker1 and Donnan and shaw2 made determinations of the solubility of oxygen in liquid silver, over a rather short range of temperatures (973° to 1125°C), using quartz bulbs, mainly at 1 atm. From the results of their investigations, Mizikar, Grace, and parlee3 plotted % O vs 1/T and obtained the following straight-line equation for solubility at 1 atm: log % O = 723.7/T - 1.0949 Recent work on the kinetics of the Ag-O2 system394 indicated there might have been some error due to reaction with the direct heated silica bulbs. Thus it became important to redetermine the solubility with the silver contained in a better refractory such as alumina, and by induction heating where the walls of the container were not so strongly heated. It was also desirable to extend the temperature range. A modified Sieverts apparatus of fairly standard type was used except that a special type of reaction tube was employed, Fig. 1. Dried argon with a guaranteed purity of 99.9 pet, and dried medical-grade oxygen with a guaranteed purity of 99.6 pet containing a little nitrogen, were the gases used. The measuring system consisted essentially of a manometer and a water-jacketed 100-cc gas buret with an open-end vertical tube parallel to the buret. This tube has the same diameter as the buret in order to give the same capillary effect on the mercury. A screw leveling device was used with the buret leveling bulb to help provide accurate pressure readings. A 2-mm ID capillary line connected the buret to the reaction chamber, helping to reduce the dead volume, which was determined with argon. The heating medium was a 2.5-kw output induction furnace. The induction coil was made of a 3/16-in. copper tubing with eight turns and an inside diameter of 4 cm. The reaction bulb was made of a quartz tube 18 cm long and 3 cm in inside diameter, Fig. 1. Inside the quartz tube were two alumina crucibles (Mor-ganite Triangle RR, XN10 and XN5) one inside the other. Below these two was an alumina disk. The disk prevented the corners of the outer crucible from expanding against the quartz tube. The solid sample (99.994 + pet Ag), which had been previously cleaned by air oxidation and repeated removal of scum, was placed inside the inner crucible. An alumina disk with a hole at the center covered the two crucibles. In order to decrease the dead volume, an evacuated quartz "filler" tube was placed on top of the crucible cover. The part of the reaction tube above the spherical joint was made up of Pyrex glass with a flat glass top. It was here that a prism was placed to facilitate the use of an optical pyrometer, previously calibrated at the freezing point of silver. This type of reaction bulb and furnace assembly was specially designed for this work, and used in preference to the relatively new water-

Jan 1, 1965

By R. B. Falk, F. E. Luborsky

Small iron particles in mercury pow by diffusion of iron atoms through the mercury. Iron particles, with diameters about 200Å, have been stopped from gvowing in size, even up to the boiling point of mercury, by the addition of a third metal. The metal additives were classified according to whether they produced 1) negligible inhibition, 2) some inhibition, or 3) marked inhibition of the growth rate. Metal additives which resulted in a marked inhibition of iron-particle growth form a stable monolayer on the iron particles. Only those metals which may form compounds with iron showed this pronounced effect. The one exception was manganese. Metal additives which resulted in no inhibition of growth, showed no evidence for adsorption and could not form compounds with iron. None of the added metals, even those which strongly inhibited particle gvowth and thus had adsorbed on the particle surface, actually formed any compounds with iron at room temperature at the concentrations required for complete inhibition of growth. ThE stabilization of the size and shape of metallic particles dispersed in liquid metals has important technological implications in "homogeneous" nuclear reactor systems and in elongated particle magnets and is directly related to the problem of corrosion by liquid metals. Growth in these par-ticulate systems may occur by diffusion of atoms from surfaces of high energy, corresponding to a small radius of curvature, to surfaces of low energy or large radius of curvature. Thus, small particles dissolve and large particles grow to increase the average diameter of the particles. reenwood&apos; has analyzed this diffusional growth of a system of particles containing a distribution of sizes and has obtained reasonable agreement with data on the growth of uranium particles in liquid sodium and UPb3 particles in liquid lead. Greenwood concluded from his analysis that the chief factors promoting stability of dispersed particles growing by a diffusion mechanism are large mean radius, high density, and low molecular weight with low values of the solute diffusion coefficient, the solubility, and the interfacial tension. In the case of elongated particle magnets the system of interest is that of iron particles dis- persed in mercury. Previous work,2 concerned with "spherical" particles in mercury, has indicated a diffusional growth mechanism similar to that discussed by Greenwood. It has also been shown3&apos;4 that the addition of certain metals to Fe-Hg dispersions results in the formation of a monatomic layer of adsorbed atoms on the iron particles. In this paper we will show that this adsorbed layer provides the decrease in the iron-atom flux through the mercury necessary for size stabilization. The general features of the stabilization of the iron particles in mercury through the formation of this "coating", with many different metals, will be described. EXPERIMENTAL RESULTS Iron particles in mercury were prepared by elec-trodeposition,2, 4 and measurements2, 4 of coercive force HCi) and saturation induction (Is) were used to follow changes in size and composition during thermal aging in the mercury in the presence of relatively small amounts of an added metal. In Fig. 1 is plotted the aging behavior of spherical particle samples in the presence of some of the added metals to be discussed. The iron particles have an initial average diameter of 180Å. Each sample was aged for 20 min at each temperature in succession in the presence of a twofold to threefold excess of added metal over that required to form a monolayer on the iron particles. These are the same samples used previously3 to study the adsorp-

Jan 1, 1965

By H. S. Wang, Y. P. Gupta

Diffusion of zinc and germanium in liquid silver is measured in the temperature range 975" to 1400°C by use of the capillary-reservoir technique. The ex-perinzental results are discussed in terms of the fluctuation and the "hole" theories of liquid diffusion, assunzing the solute as a point charge equal to the difference in the valences of the solute and solvent atoms. The additional coulombic interaction term due to the excess solute charge is evaluated in terms of the Thomas-Fenni approximation. The theoretical and experimental results agree with both the fluctuation and "hole" theories of liquid diffusion. No perceptible effect on solute diffusion in liquid silver of the size difference between the solute and solvent atoms/ions is apparent. DIFFUSION in liquid silver of electropositive solutes indium, tin, antimony, and homovalent gold has been previously reported by Leak and Swalin1 and Gupta,&apos; respectively. These solutes have nearly the same atomic size but differ principally from one another in excess valence (+2, +3, +4, respectively). The observed differences in the temperature dependence and the rate of solute diffusion were explained in terms of an added coulombic interaction between the solute and the solvent atoms. In the case of diffusion of gold in liquid silver, the data were found to be consistent with an effective valence for gold of -0.85, as proposed by Le Claire.3 Recently, Wang and Gupta4 have reported a study of diffusion of ruthenium, iron, and cobalt in liquid silver. The results of diffusion of these solutes and their temperature dependence were found consistent with the hole theories and the fluctuation theories of liquid diffusion, if ruthenium, iron, and cobalt were diffusing in liquid silver with relative valences -2, -1.3, and -0.5, respectively, instead of -3, -3, and -2 as suggested by the relative position of these elements in the Periodic Table of Elements. Furthermore, the predicted valences for these solutes were observed to be consistent with the sparsely available information on the magnetic properties of some of the dilute alloys of copper and silver with these solutes. In theoretical calculations of solute diffusivity, the solute was assumed as a point excess charge equal to the difference in the valences of the solute and solvent atoms. Both the assumption of a point excess solute charge and the use of the Thomas-Fermi approximation to calculate the potential of a solute charge are less precise for the case of electronegative solutes. Therefore, it was not possible to infer from the data on ruthenium, iron, and cobalt an effect, if any, on solute diffusion of the relative differences in either the Period or the size of the solute and solvent atoms or the solute atoms themselves. A study of the diffusion of Period 4 elements, specifically zinc and germanium was, therefore, undertaken since zinc and germanium, respectively, have relative valences of +1 and +3 in liquid silver and the data obtained on diffusion of these solutes could be compared with the available data on diffusion of Period 5 electropositive solutes, indium, tin, and antimony in liquid silver. From such a comparison, it was hoped to learn something about the effect, if any, of the ion size or the structure of the ion core on impurity diffusion in liquid silver. EXPERIMENT The diffusion of tracer zinc and germanium in liquid silver was studied by the capillary reservoir technique, modified adequately for use at high temperatures. In principle, capillaries containing liquid silver

Jan 1, 1970