Search Documents

By James E. Lawver, Jose M. Pastrana

Some of toe magnetic properties of minnesotaite (general formula: Fe3(OH)2Si4O10) were examined. Toe paramagnetic susceptibility values at various temperatures were determined from toe slope of toe magnetizing curve. These values were then compared with toe theoretical values estimated using toe Bohr magneton numbers for toe paramagnetic ions contained in toe missesotaite.

Jan 1, 1975

By E. I. Larsen, E. F. Swazy, F. R. Hensel

EXPERIENCE has indicated that hard bronzes are not suitable for bearing applications where high bearing loads and speeds are involved. It is the general practice to utilize softer materials for these purposes, such as copper, lead, silver, babbitt, lead-base alloys, and more recently aluminum-base alloys, preferably supported by a steel backing. It was the objective of the present investigation to study a new material produced by powder metallurgical methods susceptible to precipitation-hardening. TEST MATERIALS Preliminary tests were made with compacts containing copper, nickel and silicon in quantities sufficient to form 3 to 5 per cent nickel silicide. It was found that this type of alloy was susceptible to the formation of a soft surface shell when sintered in tank hydrogen. The depth of the shell depended on the length of sintering time and sintering temperature, and varied in thickness from a few thousandths to as much as one eighth inch. This soft shell resulted from the preferential oxidation of silicon, thereby reducing the efficiency of age-hardening by the nickel silicide compound. The body of the sintered compacts below the soft shell could be precipitation-hardened to a hardness of 70 to 85 Rockwell B, by quenching from. 900°C. and age-hardening at 450°C. A series of tests was made with various addition agents, in order to decrease the rate of preferential oxidation, and it was found that phosphorus was most beneficial in this respect. After considerable experimentation, the following nominal composition was accepted as standard: 2.4 per cent nickel; 0.8 silicon; 0.3 phosphorus; balance copper. The physical properties and certain bearing properties of this alloy are described in the present paper. PREPARATION OF COMPACTS Several methods of incorporating the hardening ingredient (nickel silicide) were studied. Compacts formed from copper, nickel and silicon powders were found to be inferior to those fabricated from prealloyed nickel silicide master alloys, because of the rapid oxidation of pure silicon during sintering. The use of a prealloyed nickel silicide hardener containing 25 per cent silicon and 75 per cent nickel could be further improved by preparing a master alloy, incorporating nickel, silicon, phosphorus and copper, having the following nominal composition: 25 per cent nickel; 7 silicon; 3 phosphorus; 64 copper. This alloy is brittle in. the cast condition and can be readily powdered. SINTERING PROCEDURE The blended powders were pressed at 25 to 40 tons per sq. in., the pressure depending on the size and shape of the compacts. Sintering was carried out in hydrogen or cracked ammonia atmospheres at

Jan 1, 1946

By J. R. Thoenen

The Bureau of Mines has used various sizes of core barrels above 2 in. and below 10 in. in diameter to core manganese, potash, coal, brown iron ore and bauxite. The paper describes in some detail the methods and types of equipment used to obtain maximum sampling accuracy. Introduction On December 11, 1946, R. D. Longyear, in his capacity as Chairman of the Subcommittee on Exploration Drilling, wrote the author requesting him to prepare a paper presenting the collective ideas of engineers in the Bureau of Mines on the design, standardization and application of core barrels using diamonds or other hard cutting media for drilling holes larger than two inches and less than ten inches in diameter. In subsequent correspondence it was indicated that similar papers covering the experience of other government agencies would be solicited and all such papers received would be combined in a symposium on the subject for discussion at the March 1947 meeting of the Mining Methods Committee AIME. In soliciting such information from other Bureau engineers, it developed that most Bureau experience had been confined to standard core size, two inches or less in diameter, and that larger sizes had been used only for special purposes. It is hoped the data contained herein will be of help to other operators in solving problems encountered in the field. Acknowledgments This paper was made possible by the request of Lowell B. Moon, Chief, Mining Division, Bureau of Mines, to all Division engineers to send to the author any data they had on the subject. Engineers of the Mining Division contributing were: M. H. Kline, Chief, Raleigh Branch. Paul T. Allsman, Chief, Salt Lake City Branch. J. H. Hedges, Chief, Tucson Branch. C. H. Johnson, Chief, Rolla Branch. A. M. Evans, Mining Engineer, College Park Branch. Wing Agnew, Engineer in charge, Mount Weather, Virginia. Andrew Brown, Mining Engineer, Tus-caloosa Branch. In addition Albert L. Toenges, Supervising Engineer, Bituminous Coal Mining Section, Pittsburgh, contributed his experience in coring coal beds. The author's experience in the use of cores within the limits stated has been confined to the brown iron-ore work described by Brown and coring bauxite and clay in Arkansas. Design and Standardization of Core Barrels Bureau engineers are primarily interested in obtaining core that will best represent

Jan 1, 1949

By J. R. Thoenen

The Bureau of Mines has used various sizes of core barrels above 2 in. and below 10 in. in diameter to core manganese, potash, coal, brown iron ore and bauxite. The paper describes in some detail the methods and types of equipment used to obtain maximum sampling accuracy. Introduction On December 11, 1946, R. D. Longyear, in his capacity as Chairman of the Subcommittee on Exploration Drilling, wrote the author requesting him to prepare a paper presenting the collective ideas of engineers in the Bureau of Mines on the design, standardization and application of core barrels using diamonds or other hard cutting media for drilling holes larger than two inches and less than ten inches in diameter. In subsequent correspondence it was indicated that similar papers covering the experience of other government agencies would be solicited and all such papers received would be combined in a symposium on the subject for discussion at the March 1947 meeting of the Mining Methods Committee AIME. In soliciting such information from other Bureau engineers, it developed that most Bureau experience had been confined to standard core size, two inches or less in diameter, and that larger sizes had been used only for special purposes. It is hoped the data contained herein will be of help to other operators in solving problems encountered in the field. Acknowledgments This paper was made possible by the request of Lowell B. Moon, Chief, Mining Division, Bureau of Mines, to all Division engineers to send to the author any data they had on the subject. Engineers of the Mining Division contributing were: M. H. Kline, Chief, Raleigh Branch. Paul T. Allsman, Chief, Salt Lake City Branch. J. H. Hedges, Chief, Tucson Branch. C. H. Johnson, Chief, Rolla Branch. A. M. Evans, Mining Engineer, College Park Branch. Wing Agnew, Engineer in charge, Mount Weather, Virginia. Andrew Brown, Mining Engineer, Tus-caloosa Branch. In addition Albert L. Toenges, Supervising Engineer, Bituminous Coal Mining Section, Pittsburgh, contributed his experience in coring coal beds. The author's experience in the use of cores within the limits stated has been confined to the brown iron-ore work described by Brown and coring bauxite and clay in Arkansas. Design and Standardization of Core Barrels Bureau engineers are primarily interested in obtaining core that will best represent

Jan 1, 1949

OF what use is the federation to me and why should I support it?" is a question that has been asked by many members of the constituent societies of the F. A. E. S. during the last year; a question that is asked because the speakers do not realize what the Federated is doing or what is the field of its activities. "What is it doing for the profession and for mankind?" would be a more appropriate question, the answer to which is found in the closing chapter of Prof. Cassius J. Keyser's "Mathematical Philosophy."' The chapter is entitled "Science and Engineering." Professor Keyser writes from the layman's point of view. He is looking at the profession and at engineers from the outside. We have in his thoughts the oppor-tunity that Burns sought when he wrote "Oh wad some power the giftie gie us to see oursels as ithers see us." With the permission of the author and the publisher, we quote the following paragraphs: A layman, viewing a profession from the outside, seeking thus to ascertain its proper relations to the common weal, may bring to the task a certain freedom, which, were he a member of the profession, he might have lost. "Men trained in a profession," said Prof. David Swing, "come by degrees into the profession's channel, and flow only in one direction, and always between the same banks. The master of a learned profession at last becomes its slave. He who follows faithfully any calling wears at last a soul of that call-ing's shape. You remember the death scene of the poor old schoolmaster. He had assembled the boys and girls in the winter mornings and had dismissed them winter evenings after sundown, and had done this for fifty long years. One winter morning he did not appear. Death had struck his old and feeble pulse; but, dying, his mind followed its beautiful but narrow river-bed, and his last words were: It is growing dark-the school is dismissed-let the .girls pass out first."' I shall not be so much concerned with the present status of the science as with its potency and promise. Of individual engineers the ideals may be high or low, worthy or unworthy; but of engineering itself the ideal is great and mighty. It is of that ideal that I intend to speak.

Jan 9, 1922

By Thomas Egleston

The uncertainty of finding the exact equivalents fortechnical expressions in different languages has led me to think that a glossary of furnace-terms would be useful to members of the profession. I was led, some years ago, to prepare a small one, which has been found so very useful, that I have arranged one for presentation to the Institute, for four different 'types of furnaces, in the hope that it may prove of use to those who are in the habit of consulting foreign technical journals, I was further induced to make the attempt in the hope that it might tend to make the terminology less complicated than it now is, and also to make it more uniform over larger districts. The idea of referring to a drawing which expresses exactly what is meant, resulted from the necessity of presenting such subjects to students, and will, it is hoped, prove much more useful than the mere dictionary arrangement in alphabetical order. The drawing of the blast-furnace was prepared for me by Mr. J. P. Witherow, of Pitsburgh ; the drawing of the open-hearth furnace by Mr. S. T. Wellman, of Cleveland, and the reverberatory furnace by Mr. John Fritz, of Bethlehem. The bloomary-furnace is taken from my own paper* on Bloomaries, but, in order to have a complete furnace, I have introduced into the drawing of those used at Saranac the guard-plate used at Ironville. The interest which has been taken in the preparation of this paper by those gentlemen who have contributed the drawings, has been supplemented by gentlemen in Europe who have taken the trouble to read the proof. In France it has been read by Mr. Lodin, of the School of Mines, and by Mr. Chaper, of Paris, and in Germany by Dr. Wedding, of Berlin, and Mr. Luhrman, of Osnabruck. The preparation of the paper has been much more difficult than was anticipated, and its value has been very much enhanced by Dr. Raymond's kind assistance and cooperation; and to him, as well as to all the other gentlemen, Iam very much indebted. It was at first proposed to add to the paper the names of all the tools used in these various furnaces. It was found, however, that this would make such

Jan 1, 1888

By R. W. Raymond

In a former paper (Trans., xvi., 770) I gave the text of the archaic mining law of the State of New York, together with some comments upon its curious provisions. In that connection I pointed out two facts : first, that the law seemed to have originated in the schemes of private parties, who were satisfied with those parts of it which concerned them particularly; and secondly, that the remaining provisions had been hitherto quite inoperative, for the reason that mines of the character to which they referred had not been discovered in the State. Since 1888, when that paper was written, the New York Legislature has passed several acts relating to mines as follows: 1. Chapter 394, Laws of 1890. This provides for an inspection

Jan 1, 1895

By A. T. Yu

As the first year of full-scale shiploading operations nears completion, Chile's twin ports of Chafiaral and Caldera have proved instrumental in promoting the growth of that nation's iron ore industry. Located on the Iron Coast several hundred miles below Antofagasta, the two ports boast of new conveyor shiploading facilities uniquely adapted to their coastal environment. Until recently, iron ore producers in this region of Chile have been hampered by antiquated methods of loading crushed ore on ships for transportation to foreign buyers. Use of the "truck-to-lighter- to-ship" method, which dominated heretofore, was too slow and costly to permit expansion of productive mines and exploitation of new high-grade discoveries to meet the growing world demand for such ore.

Jan 8, 1960

By Charles M. Cooley

In these troubled times free enterprise is maintaining vital molybdenum output, while expanding plant, and bringing in new low grade ore reserves, at Climax, the world's largest known molybdenum deposit. Climax Molybdenum Co. is putting $25 million into additional surface plant facilities and other millions into underground development. The expansion program to be operating by 1954 includes a new mining level, crushing plant, 4000-ft conveyor, milling units, by-products plant, and housing for 198 families. Completion of this program and low grade plant will add 10,000 tons per day to present capacity and several million tons to ore reserves.

Jan 1, 1953

By R. G. Davies

Isothermal annealing of quenched Fe3Al reveals that the superlattice forms by the nucleation and growth of ordered domains. The activation energy for isothermal ordering and initial domain growth is -29 keal per mole, which is thought to he the activation energy for vacancy migration. Domain growth, in the absence of excess vacancies, has an activation energy of -100 keal per mole. A maximum in the hardness is observed when the structure consists Of ordered domains, -35-4 in size, growing into a short-range ordered matrix and, also as a function of degree of order, S, with an infinite domain size at S = 0.4 to 0.5. It is proposed that both maxima are due to a transition from deformation by unit dislocations to deformation by superdislocntions. FE-AL alloys containing more than -23 at. pet Al, when quenched from above the critical temperature for the Fe3A1 type of order, always contain the maximum possible amount of FeAl (B2) type of order' (see Fig. 1). Thus when the Fe3A1 superlattice forms, in a 25 at, pet A1 alloy, it does so from an imperfect FeAl structure. The formation of the Fe3Al superlattice has been the subject of several recent X-ray,1, 2 electrical-resistivity,3"6 and dilatometric3 investigations. McQueen and Kuczynski3 concluded that the isotherma1 ordering of Fe3Al, after quenching from 800°C (T,, the critical temperature for order, is 55O°C), takes place by the nucleation and growth of ordered domains. However, Feder and Cahn4 found that the isothermal ordering was complex but more like a homogeneous nucleation process than a nucleation and growth process. Lawley and Cahn2 reported that the degree of order is a continuous function of temperature which is a characteristic of a homogeneous nucleation process. Thus, the evidence is conflicting as to the nature of the Fe3Al ordering reaction. Lipson7 was the first to suggest that ordered domains should exist in the Fe3A1 structure since, as

Jan 1, 1964

By Chairman Hill H. H.

The Round Table Discussion on Petroleum Engineering Research was planned for two purposes. First, to review the work that has been done by petroleum engineers during the past few years on problems that have confronted the industry and, second, to suggest new studies that should be made either on the problems that have been the subject of research during the past or on problems that have arisen only recently. It was believed that by holding an informal discussion of the problems in which the petroleum engineer is vitally interested it would be possible to bring out new ideas as to the relative importance of the different problems that should be studied and to suggest new methods for attacking some of the problems that have resisted the energies of research workers throughout the industry. It was also believed that by arranging for an exchange of experiences between the different engineers it would be possible to prevent a large amount of duplication of effort in conducting research work. Those engaged in petroleum engineering research realize that there is a broad field for study and by coordinating the work it will be possible to obtain the maximum amount of information in the shortest possible time. In planning the program on Petroleum Engineering Research, nine subjects were selected for discussion and each was assigned to a man who is doing work on that subject. These men were asked to lead the discussion on the problem assigned to each one. An effort was made to choose problems of a practical nature and upon which considerable work is being conducted at the present time. Some of the men who were asked to lead the discussion were unable to attend the meeting but most of them submitted a written discussion- of the subject assigned, with the result that there was a discussion of eight of the nine problems. Professor Uren, who was asked to lead the discussion on the subject of Recent Developments in Methods for Reducing Gas-oil Ratios, was unable to attend the meeting and advised that he did not have any new ideas to contribute.

Jan 1, 1928

By John D. Erickson

The concepts of long-range, open pit planning presented here are not new. The new idea is how the factors that control the location of the final pit limits can be considered altogether as one large, simultaneous equation. The X, or unknown quantity that is being solved for, is a long-range pit design that fulfills the desired objectives. The objectives of a final pit plan are determination of the extent and location of ore reserves, the allowable stripping necessary to uncover the ore, the final pit surface intercept, final pit topography and the contained metal values in both ore and waste.

Jan 4, 1968

By I. B. Cadoff, J. C. Bilello, R. Rosenberg

Diffiusion of magnesium into the surface of LiF crystals to controlled depths and subsequent heat treatments provided a wide range of surface zone harahesses and structure, The bend strength of the LiF crystals was increased by as much as an or-dev of magnitude. Ductility was achieved when dislocation generation occurred in the diffusion zone or when dislocations penetrated to the surface from the intevior. A critical surface hardness of 130 to 140 kg per sq mm was found helozu which generation could take place in the diffusion zone and ahoue which the zone was impenetrable, This hardness was obtainable by several methods, among them the aging of quenched MgF2 -LiF solutions to produce MgF, precipitation. Maximum hardness was ohtained in quenched specimens with no visihle evidence of MgF,. Diffusion-zone formation followed a parabolic rate law and an activation energy of 20.9 kcal per mole was obtained for the process. RECENTLY, the properties of ionic crystals as related to surface condition have been receiving much attention, specifically the transitions between ductile and brittle behavior. Originally Joffe 1 showed that NaCl crystals could be made ductile by immersion in water and related this to the elimination of surface microcracks. Aerts and DeKeyser 2 and Gorur 3' have subsequently shown that ionic crystals are inherently ductile and are embrittled through contact with air. Machlin and Murray4 hypothesized that a layer of NaCIO3 produced by contact of ozone with NaCl induced embrittlement by acting as a barrier to outward dislocation flow. westwood,' Rosenberg and Cadoff,9 and Bilello and cadoff' have reported surface strengthening of LiF crystals by coating with a magnesium compound and then heat treating for adherence. The major effect of the coat was to inhibit dislocation-slip lines from reaching the specimen surface. westwoods showed microcrack formation and fracture to be caused by slip-band interactions at the surface. The material presented in this paper is an extension of the work reported earlier by Bilello, Rosenberg, and cadoff'6,7 and illustrates the wide range of surface properties and bulk behavior obtainable by use of heat-treated magnesium-diffused surface regions in LiF crystals. EXPERIMENTAL PROCEDURE The LiF single crystals were obtained from the Harshaw Chemical Co. Some batch to batch variation was observed; therefore all specimens for a given test series were cleaved from the same crystal. The typical dimension used was 1 by 0.1 by 0.40 in. Surface damage resulting from cleavage was removed by chemically polishing in a 2 pct NH4OH solution. Each group of specimens was given a vacuum anneal at 700°C for 4 hr to provide a base standard for measuring comparative effects of various surface treatments. To produce the reacted surface zone, the annealed specimens were immersed in a boiling suspension of MgF, in doubly distilled HzO, agitated slbwly for 30 sec, removed, and dried at room temperature. Uniform coatings of MgF, were deposited with a thickness of approximately 5 mils. It should be noted that this technique can be modified for use with crystals which are soluble in water by using boiling absolute alcohol as the dissolving medium. This was found effective for the coating of NaCl with MgF2. The diffused surface zone was obtained by annealing the coated samples at elevated temperatures in a vacuum of lob4 mm Hg. Penetration depth was controlled by varying the annealing time from 1/2 to 28 hr. After heat treatment, the samples were tested for bend strength and hardness. Load was applied by four-point bending in a hard-beam testing jig. Four-point rather than three-point bending was used to provide a wide area of constant stress and to minimize the effect of localized inhomogenities in the specimen. The deflection rate was 8 x min-' and the distance between knife edges was 1/4 in. Load-time curves were obtained from a chart recorder coupled to the machine and converted to resolved shear stress on the shear plane vs deflection, as plotted in the figures. The unstressed portions of the sample outside of the two outer knife edges were used for the microhardness studies. Microhardness measurements were made with a Bergsman tester attached to a Reichert metallograph. All hardness impres-

Jan 1, 1964

By R. I. Jaffee, C. M. Craighead, G. A. Lenning

The a-p type alloys are subject to a loss of tensile ductility with increasing hydrogen content. No hydride phase is visible in embrittled a-B type alloys. The embrittlement encountered appeared to be of the strain-aging type. Both compositional and structural factors are shown to influence the hydrogen tolerance of a-B type alloys. IN previous papers by the authors, the effects of hydrogen on the structure and mechanical properties of high-purity and commercial-purity titanium were described. It was shown that the presence of hydrogen in these materials results in a hydride phase having low solubility at room temperature. This insoluble phase had little effect on the room temperature tensile properties, but did decrease the notch-bar toughness to a large degree. The binary Ti-H systemz indicates that hydrogen is much more soluble in £ than in a-titanium. Hence, it is not expected that the embrittling effects of hydrogen in a-fi alloys will be similar to that found in a alloys. Materials of this type studied in the present investigation included two commercial a-/3 alloys, Ti-8Mn and Ti-4A1-4Mn; three high-purity Ti-Mn alloys containing 3, 6, and 9 pct Mn; and four high-purity Ti-Mo alloys, Ti-SMo, Ti-10.9M0, Ti-13.1 M0, and Ti-20M0, of the a-B and B types. Materials and Fabrication—The high-purity base alloys, composed of iodide titanium and high-purity metals, were prepared by double arc melting under argon in a water-cooled copper crucible, using a water-cooled tungsten electrode. Radiographic examination showed homogeneous Ti-Mo alloys. The analyses of the alloys used in this investigation and their as-fabricated hydrogen content, where determined, are listed in Table I. The two commercial alloys were 1/2 and % in. diam bar stock. No analyses other than hydrogen content were made. In order to maintain the a-B relationship existing in the two commercial alloys, vacuum annealing and hydrogenation were carried out in the B field prior to final fabrication. Fabrication then was done by The three high-purity Ti-Mn alloys were forged to 3/4 in. diam rods at 1600°F, and hot swaged to 1/2 in. diam at 1380°F. Machined and degreased bar stock was vacuum annealed or hydrogenated, fabricated to 1/8 in. diam rod by hot swaging, annealed in argon for 1 hr at 1380°F !75O°C), and water quenched. The six yz lb Ti-Mo ingots were forged to Wi in. diam rods at 1600°F and then hot swaged to % in. diam. Machined and degreased specimens were vacuum annealed or hydrogenated in the /3 field, prior to fabrication, by swaging to Y4 in. rod at 1400°F. After fabrication, the 5 and 10.9 pct Mo alloys were annealed in argon for 16 hr at 1290°F and water quenched to give equiaxed a-B structures. The higher molybdenum content alloys were argon annealed 4 hr at 1470°F and water quenched to give all £ structures.

Jan 1, 1957

By W. C. Thurber, C. J. McHargue

THE deformation textures of metals have been extensively studied because of both the practical implications in metal fabrication and the fundamental insight into the behavior of the metal during deformation. Most studies have been concerned with pure metals or solid-solution alloys and relatively little attention has been directed toward more complex alloy systems. Barrett' and Brick2 have summarized work on multiphase systems in terms of the relative ease of deformation of the phases. Thus, if the phases are deformed about equally, each develops its usual texture for the particular fabrication process. This behavior has been reported for Ag-Cu and Cd-Zn alloys3 and 62-38 brass.4 A dispersion of hard particles in a softer matrix interferes with the normal reorientation of the matrix lattice during deformation, thus distorting the texture or in some cases preventing its development. Increasing the amount of carbon in steel has been observed to increase the randomness of the ferrite5 and almost random textures have been reported for A1-12 pct Si eutectic alloy wires.6 It has also been noted that if the second phase is platelike, deformation causes the platelets to line up in a common direction. The present work concerns a quantitative study of the deformation textures in aluminum-uranium alloys containing 5 or 13 wt pct U. Alloys in this composition range are characterized by a pure aluminum matrix in which the intermetallic compound UA14, is dispersed. From a fundamental standpoint, this system affords the opportunity for studying the effects of a dispersed phase on texture development in an essentially pure metal matrix. Further, these alloys are commonly used as fuels for nuclear research and testing reactors, and a knowledge of the preferred orientation may be useful in evaluating physical and mechanical properties as well as response to fabrication. The deformation textures in sheets of aluminum (99.996 pct), Al-5 pct U alloy, and Al-13 pct U alloy were determined for reductions in thickness of 90 pct by cold rolling. The texture in an alloy rod of the latter composition which had been extruded at 455°C was also determined. It can be readily ascertained from the aluminum-uranium phase diagram that the 5 pct U alloy is hypoeutectic and contains 7.3 wt pct (3.4 vol. pct) UAl4. The 13 pct U alloy has the eutectic composition and contains 18.9 wt pct (9.4 vol. pct) UAl,; however, because of nonequilibrium solidification conditions, the typical eutectic microstructure was not developed. The alloys were prepared by open-air melting in graphite crucibles. The slab castings were cropped and cold reduced 90 pct in thickness on a two-high mill. The slabs were reversed after each pass. Although the uranium-bearing alloys exhibited edge cracking, they could be cold rolled to the desired thickness. Small coupons 1.5 by 0.75 by 0.1 in. thick were sheared from the center of the rolled plate with a major axis parallel to the rolling direction. To obtain a specimen of sufficient thickness for machining of the X-ray diffraction specimen, three coupons were laminated into a single three-ply sandwich with a suitable adhesive. Adhesives which could be cured at room temperatures were selected in order to prevent recrystallization during bonding. Bondmaster M-648 (Rubber and Asbestos Corp.) was used for the pure aluminum laminate and Armstrong A-6 (Armstrong Products Co.) was used for the alloys. The alloy for extrusion was cast in a cylindrical graphite mold! cropped and machined into a 3-in. diam by 4-in. long billet. This billet was preheated to 455°C, upset to 3.125 in. diam, and extruded on a 700-ton hydraulic press at a speed of 6 fpm through a flat-face, 1-in. diam die. The rod was quenched with a water spray as it emerged from the die. Pole-distribution data were obtained using the diffractometric method described by Jetter and Borie.7 A spherical X-ray diffraction specimen of

Jan 1, 1961

By D. G. Swarthout, J. W. Savage, R. W. Guard

The Nb-N constitution diagvam has been examined from 1100° to 1450°C at 1 atm N2 pressure. On the basis of- our work plus that of Brauer and coworkers the stable nitvide Phases are: a) a solid solutlion, basic niobium (bcc) with nitrogen contained interstitially; NbN,, x = <0.40; b) ß NhNx,x = 0.39 to 0.45; hexagonal (W2C type) (NbzN); a =3.058A,c = 4.961 + 0.001A c) y NbNx x = 0.75 to 0.80; tetragonal (distorted NaCl type) (Nb4N3); a = 4.386A,c = 4.332 + 0.001A; d) 6 NbN,, x = 0.88 to 0.91; cubic (NaCl type); a = 4.3885 + 0.0007A; e) E NbNx x = 0.92 to 1.00; hexagonal (Tip type); a = 2.958A, c = 11.272 * 0.0015A. In addition, a metastuble transition phase 6&apos; has been observed and occurs only during the transition 6 — E. 6&apos; NbN has these distinguishing parameters: NbNx,x = 0.96; hexagonal (anti-NiAs type); a = 2.94A, c = 5 .46A. The high-temperature phase fields in the system are governed by two reactions: a) 6 + Y + E, a entectoid reaction occurring at 1270" ± 20° C; b) o + N2 = E, a 2 012 1 reaction occurring at 1370" ± 20° C. As part of a study of the electronic low-temperature. properties of transition metal nitrides, a number of specimens of niobium nitride were prepared. Preliminary observations on these specimens showed several points of disagreement with data already in the literature. It was, therefore, decided to determine the constitution diagram for the Nb-N system between 1100" and 1450°C. The objective of this research was to define the temperature and composition regions of stability of the various phases and to explain the differences among previously proposed diagrams. Review of Previous Literature. The research on the Nb-N system to 1964 has been summarized by storms.&apos; Although he does not present a phase diagram, his review covers the research on the system thoroughly. One of the earliest works on NbN is that of Ascher-mann and coworkers2 who studied the superconductivity of the cubic 6 NbN. Subsequent work by Horn and ziegler,3 Cook, Zemansky, and Boorse,1 Rögener:5 Schroder6 and sellmaier7 has qualitatively confirmed the first results on superconductivity, although their methods of preparation differed considerably. The constitution diagrams proposed for the system by Brauer and Esselborn8 and Elliott9 are shown in Fig. l(a)and (b). The diagram in l(a) has been modified by more recent results in Brauer&apos;s laboratory (private communication). Although 6&apos; is shown on this diagram, Brauer has indicated that he now believes 6&apos; to be a metastable phase in the temperature range shown. The diagram of Elliott, Fig. l(b), is based primarily on the results of Elliott and Komjathy10 on ni-trided niobium strip or rod specimens examined by X-ray diffraction and metallography. It will be noted that these proposed diagrams are in conflict with respect to the temperature and composition ranges of

Jan 1, 1968

By George A. Roberts, Arthur H. Grobe

Tensile, hardness and density properties are presented for a new 18-8 stainless steel powder for the —50, —100, and —140 mesh cuts and also for a prepared blend containing 62 pct —325 mesh powder. The data were obtained for sintering temperatures of 2100° to 2350°F and for compacting pressures of 30 to 50 tons per sq in. A NEED has existed for a stainless steel powder of uniform composition from particle to particle, which could be readily molded and sintered, and which would yield moderate to high strength and ductility when processed into parts by standard powder metallurgy techniques. The literature reveals that previously available powders have been lacking in one or several of these desirable characteristics. Originally attempts to produce stainless steel powder by blending and diffusing elemental metal powders were unsuccessfu1.l A truly alloyed stainless steel powder reported by Dale in 1947 yielded reasonable mechanical properties but required an exceptionally high sintering temperature of 2400°F in pure dry hydrogen.&apos; A later development reported in 1950 by Stern provided a stainless type powder of excellent molding properties&apos; but this powder likewise required sintering at temperatures over 2350 °F and did not yield properties as high as those previously reported. The powder was not truly alloyed prior to sintering. A prealloyed stainless steel powder has been developed that is readily moldable at 30 to 50 tons per sq in., can be sintered at low temperatures (2100" to 2300°F), and which yields compacts with both high strength and ductility. The powder is prepared by the liquid disintegration method," direct from molten metal. Early attempts to make 18 pct Cr, 8 pct Ni stainless steel powder by this method did not produce a usable powder for pressing and sintering because of a preponderance of spherical particles with relatively high, surface oxide content. It was learned that silicon additions to iron alloys, powdered by this process, gave bright powder of low-oxide content and such additions were made to 18-8 stainless with similar results. An attendant change in particle shape occurred reducing the number of spheroids materially. The optimum composition which has been studied and is reported here contains approximately 2.5 pct Si. Silicon additions to stainless steel of the 18-8 type improve the resistance to high-temperature oxidation and promote the formation of ferrite. Corrosion resistance is, however, controlled by chromium content and even though ferrite may exist the corrosion resistance is not generally impaired.4 Experimental Procedure A detailed study of the 18-8, 2.5 pct Si powder has been made in accordance with the following outline: 1. Four blends a. — 50 mesh b. —100 mesh

Jan 1, 1952

By F. L. Wolf, A. A. Grubb

There is a tendency on the part of practical foundrymen to accept with reluctance the results of tests on sands, binders, and such materials made in the chemical laboratory alone. They feel that such tests frequently emphasize and measure properties that are of minor importance and fail to take account of characteristics that are important in determining the value of the material in actual practice. Experience seems to indicate that the most thorough and conclusive test for any new foundry material is an actual run in the foundry alongside of a standard material of known value. Such a test, however, involves certain difficulties and necessitates certain precautions. It is not always easy to obtain a fail trial for a new material. We all have certain prejuclices, which unconsciously affect our judgment to a marked degree. A practical test frequently involves so many workmen, each of whom reacts in a different manner to the test, that the personal equation becomes very complex and the true results of the test are obscured. There are times, too, when a thorough experimental trial of a material would interfere too much with the. rush of work in a department or would hazard the quality of the product to such an extent as to make it inadvisable. Under such conditions a laboratory test is advisable before the material is sent into the foundry. These tests should be made as practical as possible and so closely related to foundry practice as to give a true index to the value of a product for the purpose desired. Core sands and molding sands are as numerous "as the sands of the sea" and valy as much in quality. Old sources of supply are continually failing and new ones must be opened, so that we must continually search for new and better grades of sand. During the past year, the Ohio Brass Co. has developed tests for sands, cores, and binders which bear a close relation to the particular use to which these materials are put in the foundry and which arc fairly indicative of their value. While the tests thus far have been confined to cores and core sands, it is expected that tests for molding sand will bc developed in the future.

Jan 1, 1921

By D. R. Shreve, L. W. Welch

An analysis for predicting the behavior of reservoirs exploited by a combined gas drive and gravity draintrge mechanism is presented. The method allows the prediction of gas-oil ratio, oil production rate, and cumlulative oil recovery for high relief pools in which pressure is maintained either by gas injection in the crest of the structure or by a combined gas and water injection program. The reservoir is represented by a model of communicating vertical prisms, with production or injection at the upper or lower boundaries of each prism. The theory of macroscopic gravitational segregation of two fluids within a reservoir is discussed in detail for all ranges of saturation. A description of an application of the analysis to a typical field problem is also presented. INTRODUCTION The importance of gravity drainage as a producing mechanism has become more evident during recent years. However, many of the reservoir engineering methods which have been used in the past for predicting the behavior of reservoirs producing by this mechanism have required such drastic, simplifying assumptions that the calculated performance in some cases does not resemble the actual pool behavior. The mechanism of fluid displacement in porous media has been described by Buckley and Leverett,1 and a simplified "one zone" method based on this development has been used by engineers to evaluate the performance of gravity drainage pools. Welge2 has modi- fied this approach so that the calculation time has been markedly decreased. In addition, many other authors3-9 have analyzed various phases of the gravity drainage producing mechanism during the past several years. In a high relief reservoir in which gravity may affect the recovery mechanism, there are two main types of exploitation programs which can be employed: 1. Reservoir pressure is maintained by injecting gas into the upper portions of the reservoir. In this case gas is not released from solution and, if dynamic pressure drops are small compared to the total pressure of the system, the gas and oil may be considered to be immiscible and to have constant fluid characteristics. 2. Reservoir pressure is not maintained and a "natural depletion" mechanism prevails. The term "natural depletion" can be used to describe the production history of a reservoir in which a gradual decline of average pressure and the associated release of solution gas continue throughout the producing life. In this mechanism gas is released throughout the reservoir and there is a continuous change in the characteristics of both the gas and the oil phases. It is the purpose of this paper to present the results of mathematical developments by which a method has been devised for evaluating the performance of reservoirs which are depleted by the first type of exploitation program discussed above. It should be mentioned that, although throughout the analysis gas and oil represent the two fluids existing in the reservoir, the method is equally applicable to gravity drainage in water-oil systems. STATEMENT OF PROBLEM In reservoirs of pronounced structural relief, where the closure of the oil section is great or the angle of

Jan 1, 1957

By Luther Wagoner

Having given in a former paper1 the results of assays of sea-water, bay-mud, dredgings from San Francisco bay, etc., and believing it might be interesting to extend the work to include some deep-sea dredgings, I procured from the Smithsonian Institution six samples taken by the U. S. steamer Albatross, and marked as follows: Depth in No. station. Locality. Latitude. Longitude. Fathoms. 1. 2103. Off Delaware bay. 38&apos; 47&apos; 20" N., 72o 37&apos; W., 1,091. 2. 2265 to Between Chesapeake 35° 37&apos; N., 74O to 75O W., 49 to 70. 2297. bay and Hatteras. 3. 2420. Off Chesapeake bay. 37&apos; 03&apos; 20" N., 74O 31&apos; 40" W., 104. 4. 2528. East of Georges 41° 47&apos; N., 65o 37&apos; 30" W., 677. bank. 5. 2572. SE. of Georges bank. 40° 29&apos; N., 66O 041 W., 1,769. 6. 2681 South of Nantucket. 39&apos; 43&apos; N., 70&apos; 29&apos; W., 990. The above samples were assayed by the cyanide-method, described in my former paper (p. 807), about 30 g. of sample being used, and the following results were obtained: Value in Milligrams Per Metric Ton. No. Station. Gold. Silver. 1. 2103. 145 1,014 2. 2265 to 2297. 44 304 3. 2420. 15 353 4. 2628. 267 1,963 5. 2572. 125 377 6. 2681. 66 414 No. 4, Station 2528, consisting of red clay and volcanic ash, mas re-assayed ; 35 g. was roasted at a low heat for one hour and weighed 34.05 g. after roasting; the color was changed to a deep brick-red; and when assayed by the cyanide-method

Jan 1, 1908