By K. E. Brown, F. W. Jessen

By utilizing an 8,000-ft experimental field well equipped with 10 gas-lift valves and 10 Maihak pressure recorders, gas-lift tests were conducted with port sizes ranging from 5/16 through I in. The well was equipped to provide accurate means of measuring surface pressures, temperatures, quantity of injection gas and fluid production. The tests were conducted in 2%-in. OD tubing, and the well was making 95 per cent water. A complete evaluation of gas-lift-valve port sizes shows the relationship of per cent recovery, gas-liquid ratios, minimum pressure created at the operating valve and horsepower requirements for each port. The length of time necessary for the fluid in the tubing to reach equilib.rium conditions after each cycle was recorded. Fallback of fluid at depths of 477, 969, 1,685, 2,493 and 4,290 ft was noted. For each port size, pressure loads of 2.50, 300, 350, 400 and 450 psi were lifted with a valve operating at approximately 550 psi at 6,000 ft. Gas-liquid ratios for each load were varied from excess gas to a gas volume per cycle whereby the load failed to reach the surface. Numerous curves are presented in evaluating the accumulated dara. The results show a 1-in. port to be the most efficient under all conditions. The production of intermittent liquid slugs against different-sized surface chokes was evaluated. These tests were conducted from a 7/16-in. ported valve at 4,072 ft. Tests indicate that, when possible, a %-in. in diameter choke or larger should be used at the surface. In the past few years most of the advancement in gas-lift operations has been made in continuous-flow operations. Yet, it is estimated that at least 70 per cent of the wells on gas lift in the United States are of the intermittent type. Since the term "slug flow" is sometimes used in both intermittent- and continuous-flow operations, it would be well to distinguish between the two types of flow. Continuous-flow gas lift is defined as a method whereby the fluids are produced at a continuous rate at the surface. This generally requires a continuous injection of gas through a surface choke; however, various other control devices sometimes are installed to eliminate freezing, to shut-off gas during natural flow periods, etc. The actual flow of fluids in the tubing may be of the slug type (one of many flow patterns known to exist in continuous flow). Intermittent flow is defined as a method of gas lift whereby the liquid is produced in separate piston-type slugs. Perhaps this type of flow could best be thought of as a ballistic-type flow where the liquid leaves bottom as a piston, propelled by a slug of expanding gas. Gas generally is injected through some type of control at the surface at predetermined intervals. However, the valve may have characteristics whereby gas can be injected through a small choke and still result in a ballistic-type flow. The purpose of the experimental work was to evaluate the most efficient port size to be used on the operating valve for the ballistic type of lift and, in addition, to establish the importance of utilizing a surface choke large enough to allow slugs to be produced without detrimental effects. This work is part of a compre- hensive study of both intermittent-and continuous-flow gas lift, representing a joint project conducted by the Ohio Oil Co., the Sun Oil Co., Otis Engineering Corp, and The U. of Texas. The problem of evaluating port sizes has been given little previous attention. Some work undoubtedly has been done which has not been published to date. Some tests were conducted when the wireline, mechanically-opened valve (Nixon) first came on the market. This valve was capable of utilizing full tubing area as its port size. It is known that this was a very efficient valve, but to the authors' knowledge the results of tests have never been published. EXPERIMENTAL EQUIPMENT These tests were conducted on an actual field well, the Ohio-Sun Unit Well No. 2-E, in the North Markham-North Bay City field, Matagorda County, Tex. The well incorporated 23/8-in. OD tubing and produced 95 per cent water. Since the running of equipment was to be quite elaborate and expensive, a well was selected in which both intermittent- and continuous-flow tests could be conducted. This particular well was capable of producing in excess of 1,000 B/D of liquid (95 per cent salt water), yet with a 3/64-in. in diameter bottom-hole choke, production was controlled to 82 B/D. Most of the intermittent tests were conducted at this low rate. Figs. 1 and 2 show all the surface and down-hole equipment. As can be seen, every attempt was made to insure that ample equipment was available for reliable testing procedures. Fig. 1 shows the surface testing equipment. The input gas was controlled first by a regulator, then

The Institute has no available copies of Bulletin No. 7, January, 1906, and Bulletin No. 105, September, 191.5. The sum of 30.50 per copy will be paid for these Bulletins.

Jan 6, 1917

By J. R. Cooper, A. Bruynesteyn

The final results of the operation of the Cananea test dumps are discussed. Scale-up factors between shake-flask tests, column tests and the large test dumps are established for the Cananea ore. The formation of clay layers, which formed inside the dumps and markedly affected extraction, as well as secondary enrichment, are discussed.

Jan 1, 1974

The Jeffrey operation of Canadian Johns -Manville Co. , Ltd., at Asbestos, Quebec, is considered to be the world's largest asbestos mine. It accounts for approximately 37% of Canadian production of chysotile asbestos and about 13% of world production. Rated capacity is over 600,000 stpy (540,000 mtpy) of fiber, of which well over 90% is exported to the United States and seventy other countries. During the early 1970's the company completed a five-year modernization and expansion program which included the installation of a unique 72 in. by 93 in. gyratory crusher to handle the extremely blocky serpentinized peridotite ore. Because of the large diameter of this crusher the top ring of the shell was made in two halves which were bolted together. Hundred-ton trucks dump from two sides of the crusher into the 200 st (180 mt) dump pocket which is equipped with dust collecting ducts in the walls of the other two sides. The installation was designed to accommodate the eventual use of 200 -ton trucks. Crushed ore at a. size of 7 ½ in. (191 mm) falls into a uniquely designed crushed ore pocket equipped with three sloping steel sides and one vertical side, which make it totally live. Infrared heaters installed in back of the hopper sides prevent the ore from sticking to the steel. Another interesting feature is an eccentric removal bridge which is permanently mounted inside the crushed ore pocket. The two halves of the bridge are let down by electric winches to form a platform on which the eccentric cart travels and from where maintenance is done. Level indications in the crushed ore pocket are by radioactive indicators. Under the crushed ore pocket is a 72 in. by 28 ft (1.83 m by 8.5 m) apron feeder which operates at 7. 2 to 50 fpm (2. 3 to 15. 3 mpm). Crushed ore is discharged to a picking belt for tramp removal. A crossbelt magnetic separator is also mounted over this belt. Permanently mounted belt reels are also situated over the picking belt to facilitate the changing of this unit. A 60 in. (1. 52 m) wide takeaway belt then elevates the crushed ore to t.he surface facilities. Instead of discharging to a crushed ore stockpile, the takeaway conveyor delivers the ore to a 300-ton distribution bin. The ore is then screened and secondary crushed; and the plus ¾ in. (19 m) is "stored in a 3,000 ton bin while the minus ¾ in. is dried and then sent to storage. This system of directly screening primary crushed ore is similar to that used at both the Endako molybdenum and Gibraltar copper operations in British Columbia. While it would seem connecting processing equipment directly to a primary crusher would have an adverse effect on the crusher availability, the 94% of scheduled time this crusher

Jan 1, 1978

By J. H. Nelson

An outline survey of the economic outlook for the United States export trade in petroleum products resolves itself broadly into two general divisions; first, a consideration of our present position in this trade, and second, a discussion of the visible factors which promise to affect appreciable changes in the immediate future in that trade. The United States PetRoleum Exports of majoR Petroleum Products 1925, 1926 and 1927

Jan 1, 1928

By J. O. Nelson, C. J. Altstetter

Single crystals of hcp cobalt, 3 mm in diameter and up to 35 cm long, were grown using an electron-beam, zone-melting technique. The martensitic-phase transformation was studied in single-crystalline and polycrystalline specimens by making length-change measurements as a function of temperature under various elastic compressive stresses. Upon thermal cycling, single-crystalline or polycrystalline specimens repeatedly transformed almost entirely on the same variant of close-packed plane provided the maximum temperature did not exceed 600°C. Cycling to 1000°C resulted in transformation on more than one {111} variant. This behavior is termed multivariance. The multivariant transformation occurred very rapidly at an M, temperature 2° to 6°C lower than the M, of a transformation which would result in a single-crystal product. Elastic compressive stresses (up to 253 g per sq mm) tended to lower the A, and raise the M, temperatures, decreasing the width of the temperature vs dilatation hysteresis loop. The transformation habit plane and transformation shear direction of an as-grown single crystal were not grossly affected by elastic compressi?ie stress. This was evidenced by similar dilatations on the temperature us dilatation loops joy specimens with and without compressive stress. A dislocation mechanism is proposed to explain the observed results. IT has been shown that, on heating, cobalt transforms martensitically from the hcp to the fcc phase.' The transformation habit plane is (0001)hcp || (lll)fcc and the transformation shear direction is (1010)hcp || (112)fcc. The transformation involves a shear of 1g°28', which may be achieved by a shearing of a/6(112) of every two planes with respect to the plane beneath, thus changing the ABABAB stacking of hcp to the ABCABC stacking of fcc. Associated with the phase change is a 0.3 x 10"3 contraction in the habit plane and a 4.2 X 10"3 expansion perpendicular to the habit plane resulting in a 3.6 x X volume increase on heating.' On cooling, an identical volume decrease takes place. The temperature at which the fcc phase begins to form on heating (A,) is reported as 430°C, and the temperature at which the hcp phase begins to form on cooling from an elevated temperature (A&) is reported as 390oC1,3 Consequently, temperature vs dilatation plots have the form of a hysteresis loop. If heating or cooling is reversed during a transformation, a smaller hysteresis loop results. Upon heating, the transformation is always complete; whereas, fcc is often retained at room temperature as a metastable phase entrapped in the polycrystal-line hexagonal matrix.1,4,5 Two obstacles in the theory of the allotropic-phase transformation of cobalt have been: 1) a detailed knowledge of the product nucleus, and 2) a plausible method of propagation of the transformation. Bilby,8 christian, 7 and seeger 8,9 have suggested a "pole mechanism" as a means of propagation of partiai dislocations from plane to plane. A pole dislocation and a Shockley partial come together at a node. The a/6(112) Shockley partial rotates about the pole dislocation effecting the transformation shear. The pole dislocation must have a 2a/3(111) screw component which causes extension of the transformed region by two atomic planes with each full rotation of the Shockley partial. Bollmannl0 suggested, on the other hand, that transformation propagation occurs due to the stress fields of intersecting (111)-type stacking faults. As faults intersect, a stress distribution is set up about their intersection which is in turn reduced by the emergence of another fault on the second nearest plane. This process continues with the final result of a complete phase transformation. In view of the similarities between deformation and transformation in cobalt, the effect of stress on the transformation would, hopefully, yield valuable information concerning nucleation and propagation. In the present work single-crystalline and polycrystalline specimen length changes were measured as a function of temperature at various compressive loads. PROCEDURE Several orientations of single crystals of hcp cobalt in lengths up to 25 cm were grown by electron-beam floating zone melting from 99.95 and 99.999 pct, 3-mm-diam cobalt rod as supplied by Johnson

Jan 1, 1964

By W. F. Mullen, C. W. Stickler

WITH few exceptions, unit operations in the Pennsylvania slate industry in 1950 did not differ appreciably from production methods described by Behrel and Bowles2-4 several decades ago. Many traditionally picturesque but relatively inefficient hand operations continued to contribute to high operating costs in an industry in which the margin of profit, for various reasons, was admittedly low. As part of a general program in which the Pennsylvania State College has been assisting the slate industry to solve some of its problems, time and method studies were used in an effort to determine the bottlenecks of production flow. The results are as applicable to other stone industries as they are to slate. A study of the basic elements in the production of roofing slate, structural slate, and slate blackboards among selected slate producers revealed comparatively few refinements. Any marked difference in operating method was characterized largely by the available equipment, a noticeable difference in the working properties of the rock quarried by a particular company, and by either the habit thinking or ingenuity of the individual operators. With the hope that significant economies in manufacture might result, all the unit operations were broken down into elements for study and analysis. The greater part of the study encompassed those operations from the quarry rim to the finished product; however, to obtain a reasonable synthesis of time allotments per operation, several analyses of quarrying from the finish of the wire saw cut are included for reference. The complete study of quarrying made by Bowles several years ago resulted in the introduction of the wire saw into the operation; there appears to be a need for as fundamental a change in the processing of finished slate as the wire saw was in the quarrying process. Fig. 1 illustrates the flowsheet of quarried rock from the parent bed to the quarry rim with the basic elements which contribute to the difficulty of removing slate from the ground. In Pennsylvania roofing slate is produced by one of three procedures, many operations of which are quite similar. In the traditional or classical method the quarried rock is reduced by sculping and auxiliary manual treatment to workable size and then is split and dressed (trimmed to size) in the conventional shanty. Archaic as this method might appear, there are several elements that result in substantial savings over more mechanized operations. In a modified version of this method, the block is reduced by sawing and gouging preparatory to splitting and dressing in indoor stations. This method is particularly adaptable to rock which fractures unevenly by conventional sculping methods. In the third and more modern method, reduced block received from the block maker is diamond-sawed to length and finished on a production line. Fig. 2 illustrates the flow pattern in each case. In the modified and more modern plans, dressing is done on mechanically-operated trimming machines, which appreciably reduce the fatigue factor of the operator. However, it should be noted that it is advantageous for the operator to be able to control the speed of the knife to prevent breakage of certain classes of stock. In the classical plan the splitter and dresser normally act as blockmakers also and carry their eighter slabs (equivalent in thickness to eight shingles) into the shanties themselves, all of which adds to fatigue and reduced efficiency. The extremely low investment and operating expense of the classical method has undoubtedly been of paramount importance in its continuation. Production of Mill Stock The production of mill stock is accomplished by less picturesque methods than enter into the production of roofing slate but it is, in the main, relatively more efficient because of the increased use of machinery for handling and for finishing. Mill stock can be classified into two categories as far as difference in production method is concerned: structural slate and blackboards. The significant difference in operation is caused largely by the nature of the rock used for each product with the best and easiest cleaved rock being reserved for blackboards to permit the splitting of large slabs to as little as 1/2 in. in thickness. Structural stock, on the other hand, is split into panels no thinner than 11/2 in. and

Jan 1, 1952

By G. W. P. Rengstorff, L. E. Olds

High purity molybdenum ingots containing controlled amounts of a single impurity element (oxygen, nitrogen, or carbon) were prepared. These ingots were tested for ductility by bending test specimens at various temperatures. The relationship between the plastic behavior of the ingots and their chemical composition has been determined. MANY proposed applications for molybdenum require ductility at or near room temperature. At the present time, it is possible to obtain wrought molybdenum with considerable ductility only if special fabrication techniques are used to control the grain structure. Starting with are-cast or powder metallurgy ingots, the usual methods for obtaining ductility rely on fabrication procedures that result in fibered microstructures in the finished product. Recently, it has been found that the ductility of either powder metallurgy or are-cast molybdenum can be improved by uniform recrystallization of the metal to a very fine equiaxed grain structure.' The need for a fibered or a fine grained structure may limit the practical usefulness of molybdenum. For example, welding. which may be used in fabricating the metal, generally produces coarse grained structures that lead to brittleness. This applies, certainly, to currently available commercial molybdenum. Although commercial molybdenum is brittle when the grains are coarse, it has been shown experimentally that fine grained structures are not always essential for ductility. For instance, as-cast molybdenum with a coarse columnar grain structure is ductile if it is sufficiently pure.' Because high purity cast molybdenum has good ductility even when coarse grained, it is probable that the brittleness in coarse grained commercial molybdenum is caused by the impurity content of the metal. Although the general effects of impurities on the cold ductility of molybdenum have been known in a qualitative manner for some time, no quantitative evaluation of these effects has been available. The present investigation was made in order to determine more accurately the effects of oxygen, nitrogen, and carbon on the cold ductility of cast molybdenum. Oxygen has long been known to be detrimental to ductility, although the minimum amount which will embrittle molybdenum has been open to speculation. Parke and Ham" showed that ingots with oxygen contents above 0.003 pct could not be forged. Maringer and Schwope have described the embrittle-ment of molybdenum wire by oxygen. A discussion on the effects of heat treatment on the distribution of oxygen in molybdenum has been given by Perry, Spacil, and Wulff." Although nitrogen would also be expected to have harmful effects on ductility, no extensive work has been done previously to determine whether this is so. However, Tury and Krausz" found that wires presumably with less than 0.007 pct N were brittle. Carbon is added to commercial cast molybdenum for deoxidation. Parke and Ham" have shown that molybdenum containing as much as 0.06 pct C could be forged if the oxygen was kept below 0.003 pct. Also, Bruckart and others' found that the room temperature ductility of sintered molybdenum improved with carbon contents up to 0.84 pct. However, Rengstorff and Fischer' found that residual carbide particles in cast molybdenum apparently had an unfavorable effect on room temperature ductility.

Jan 1, 1957

By D. C. Bard

THESE notes are based on the megascopic study of a suite of 2,400 specimens of minerals and ores from the Butte mines, combined with field observations at intervals over a period of several years. The estimate of average vein composition is based on field acquaintance with the veins. It is probably correct in its broader proportions, and should be of use for comparison. Chemical and Mineral Composition of Butte Sulphide Vein. Matter. Per Cent. Oxygen 43.00-Quartz, rhodonite, rhodochrosite, barite, calcite, and hübnerite. Silicon 36.00-Quartz, rhodonite, and willemite (very rare). Sulphur 5.00-Sulphides of. iron, zinc, copper, lead,. and sulphates of barium and rarely calcium. Iron 5.00-Ferric sulphides (pyrite, bornite, chalcopyrite), also in sphalerite, tetrahedrite, and rarely hematite and siderite. Manganese, . . . . 2.00-Rhodonite, rhodochrosite, and hübnerite. Zinc, . . . . 1.00-Spha erite, very rare wurtzite and willemite, and tetrahedrite and tennantite.

Jan 8, 1913

By L. A. Roe

Magnetic separation occupies an attractive position in the field of ore beneficiation. It is a simple yet effective method, used for some 150 years and steadily growing more important. This type of beneficiation orginated in 1792, when William Fullarton was issued a British patent covering the separation of iron ore by magnetic attraction. What is magnetism, and why are some materials capable of being magnetized and others not? The study involves many unknowns, and even a partial answer to these questions would be a dissertation in solid state physics and perhaps other fields of science. But the last two decades have revealed basic facts as to why certain materials are magnetic and what happens to them when they are magnetized.

Jan 12, 1958

By J. R. Thompson

It is common practice, and certainly good business as all of us know, to take care of plant operating equipment. Machinery of any type requires periodic inspection and planned maintenance. With this thought in mind a plant operator should at the end of every shutdown period make regular belt inspections and plan for later appropriate care and maintenance. The points mentioned below are understood well by all of us but are sometimes forgotten because belt conveyors are comparatively easy to operate. Maintenance of any conveyor belt is dependent upon the fundamental characteristics of the two component parts-cover and carcass.

Jan 6, 1950

By W. H. Class

The embrittling effects of oxygen, ozone, nitrogen, air, and surface residues, on NaCl has been investigated. The embrittlement by ozone and oxygen was found to be associated with the formation of a NaClO3 surface compound. In these cases the initial crack that was responsible for fracture (in a bend test) always nucleated at the corners between the tension and side faces. The behavior of air was very erratic and on certain days did not produce enzbrittlement. During these periods, crystals that had become embrittled by the ozone treatment completely recovered their ductility after a short exposure to the ambient atmosphere, It was established many years ago1 that considerable ductility could be obtained in NaCl single-crystal specimens if the crystal surfaces were dissolved in water either during or immediately prior to the test. The original interpretation of this effect by Joffe attributed the enhanced ductility to the removal of surface microcracks by dissolution. Later investigations2'3 have suggested that the exclusion of air from the specimen surface is the criterion for extensive plastic flow prior to fracture. The air em-brittlement in this later work was attributed to the diffusion of gaseous atoms into the surface layers of the crystal, thereby impeding the movement of dislocations. This model satisfactorily accounts for the reembrittlement observed after further air exposure subsequent to the water dissolution treatment. However, the situation has recently become more complex by the observations in several laboratories4-t that under certain conditions air exposure does not impair the ductility of NaC1. It has also been recognized5 that improper drying operations after water dissolution can leave surface precipitates that lead to embrittlement. Cleavage defects on as-cleaved crystals can often be another source of embrittlement. In the present work the effect of the gaseous atmospheres nitrogen, argon, air, oxygen, and ozone, on the ductility of rock salt was studied extensively. The embrittlement resulting from oxygen and ozone exposures was found to be associated with the formation of a NaC1O3 surface film. It is suggested that certain atmospheres, one of which often can be ambient air, which inhibit the formation or favor the decomposition of this compound, can promote ductility. Thus one aspect of the Joffe effect is certainly related to the removal of surface compounds or complexes by water dissolution. The effect of surface precipitates that remain after drying operations and of cleavage defects were also studied. In neither of the latter cases was the embrittlement as severe as that found with a NaClO3 surface layer. PROCEDURE AND SPECIMEN PREPARATION The nature of the embrittlement produced by the agents mentioned above was studied by means of microscopy, mechanical testing, and X-ray diffraction. Specimens were cleaved from large crystals of optical quality sodium chloride obtained from the Harshaw Chemical Co., and, except for those tested in the as-cleaved condition, were given a 15- to 20-sec immersion in distilled water followed by a rinse in absolute methyl alcohol. The specimens were then blotted on a soft, absorbent paper, and dried by a few seconds exposure to a stream of warm, dry air. Such a procedure was found to give a control surface which was microscopically free of residues. (A few crystals were intentionally painted with a concentrated NaCl solution in order to investigate the effect of surface residues). All specimens were of 0.140 sq in. cross-section. Crystals prepared in the above manner were immediately placed in a gas train where they could be exposed to the desired gases for preselected periods of time. For the oxygen and nitrogen exposures, pure reagent-grade gases were employed. The ozone was provided in the form of an ozone-oxygen mixture (approximately 10 pct ozone) prepared by passing commercial grade oxygen over a strong ultraviolet light source. All gases were dried prior to their introduction into the train. Since argon was found to be completely inert in its behavior (i.e., residue-free specimens that were exposed to argon were not embrittled), it was periodically utilized to check the control specimen surfaces as well as the condition of the gas train used for aging the specimens. After exposure to the gaseous media in question, the crystals to be used for the measurement of the strain to fracture were transferred from the gas train to a protective oil bath (without further exposure to the atmosphere) where the tests were conducted in three-point bending. The apparatus was so adjusted that the load could be applied at a constant, continuous rate. Other Snecimens from the gas train were deformed

Jan 1, 1962

The term "timbered stope" is here meant to denote stopes in which timbering is the predominant feature of the mining method. Stopes with stull sets, as in the Hecla mine, are types of timbered stopes; these types are probably the best-known. Timbering stopes by means of square sets is not as common as formerly, as the system is not often necessary, yet there are good examples and large tonnages are being mined by the method. The square set may be utilized in ordinary overhand stopes if the orebody is suitable. At some mines, square sets have been abandoned in favor of top-slicing; and at others, the square set has superseded horizontal cut and backfilling. A drift, either in the wall or orebody, is necessary before opening the sill floor. In wide deposits, there may be a grillage of drifts and crosscuts, and at least one raise to the level above is needed in each stope for ventilation and handling timbers and filling. The square sets are filled with waste rock from the hanging wall, sorted from the ore, from development work, or from the level above. As a rule, little timber is recovered. The examples include the Butte district, Mother Lode of California, Bunker Hill & Sullivan, Hecla, and Morning mines.

Jan 1, 1925

By J. F. Wolff

CARL ZAPFFE, Brainerd, Minn. (communication to the Secretary*).¬Unless one has actually directed explorations for iron ore, it is doubtful whether the importance of Mr. Wolff's paper, the value of the information contained, and the large amount of detail work involved in what is set forth can be fully appreciated. It is indeed rare to get such a com-

Jan 3, 1917

By W. P. Sykes

SINCE Honda and Murakami1 in 1918 proposed their constitutional diagram of the carbon-free iron-tungsten system, considerable effort has been expended by several investigators in attempts to define more positively the structural features of the alloys. The existence of an intermediate phase corresponding to the formula Fe3W2 (68.7 per cent W) was proposed from evidence of a purely metallographic nature by one of the present authors2 in 1926. Since that time the identity of this phase has been confirmed by Arnfelt3 and by Takeda,4 both of whom employed X-ray methods as well as the microscope and the chemical analysis of isolated microconstituents. According to Arnfelt, Fe3W2, as crystallized from the iron-rich melts at a temperature above 1450'C., contains by analysis 68.7 per cent W. The lattice of this phase is characterized by trigonal symmetry. Arnfelt, moreover, proposed a second intermediate phase formed at some temperature between 1450° and 1000° C. by a peritectoid reaction involving Fe3W2 and the iron-rich solid solution. A melt containing 25 per cent W was cooled to 1000° C. and heated for. 100 hr. The precipitated tungsten-rich constituent was separated and found by analysis to contain 62.6 per cent W. This composition agrees closely with that represented by the formula Fe2W (62.2 per cent W). Diffraction patterns from the concentrated precipitate showed a hexagonal unit cell. Takeda confirmed the data of Arnfelt regarding Fe3W2 but was unable to detect Arnfelt's second intermediate phase. While Takeda. failed to describe in detail the treatments employed, he stated that in alloys containing 40 per cent W which were quenched after heating at various temperatures between 1200° and 1450° C., no evidence of the second phase (Fe2W) was observed either in the microstructure or in the diffraction patterns of isolated residues. He therefore considered the existence of this low-temperature hexagonal compound as disproved.

Jan 1, 1932

By B. D. Cullity, S. S. Hsu

The stress distribution at the surface of a twisted cylinder is analyzed along the boundary of a slip plane of arbitrary orientation and this analysis is applied to the torsion of cylindrical crystals of magnesium. A criterion for slip is developed and the critical resolved shear stress of magnesium in torsion is found to be 0.038 kg per sq mm. The mechanism of torsional deformation in magnesium and aluminum is described, as well as the relaxation of a twisted crystal at elevated temperatures. THERE has been considerable fundamental study A of the mechanism of slip occurring during deformation in tension and compression but comparatively little attention has been paid to the mechanism of torsional deformation. This paper is concerned with the way in which a single crystal deforms in static torsion and with the phenomenon of untwisting which a twisted crystal undergoes during annealing. Particular attention is paid to the application of the critical resolved shear stress law to torsional deformation. Probably the most likely mode of torsional deformation that can be imagined consists of rotation of one part of the crystal relative to another on the active slip plane. Here the most interesting feature is the slip direction. If a cylindrical single crystal is twisted about its axis and if, to consider the simplest case, the active slip plane is normal to the specimen axis, then the direction of gross slip at any point must always be at right angles to the radius drawn to that point. It follows that the crystallographic direction of slip must be continually changing, in sharp contrast to slip in tension which occurs in a crystallographically constant direction. Extensive investigations of slip in torsion have been made by Gough and his associates.' They made torsional fatigue tests on metal single crystals belonging to a number of different crystal systems and observed, with a microscope, the appearance of slip lines on the surface and of strain markings on the transverse cross section of cylindrical specimens. They concluded that the critical resolved shear stress law was just as valid in torsion as in tension, in the sense that slip occurred on that plane and in that direction in which the resolved shear stress was a maximum. They also established that the operative slip planes and directions were the same as in tension. They did not, however, measure the critical resolved shear stress in torsion nor, in fact, did they establish that a critical value of the resolved shear stress was necessary for the initiation of slip. Their investigations were, moreover, restricted to torsional fatigue tests which necessarily involve small strain amplitudes. Wilman,' studying crystal growth and the abraded surfaces of crystals, observed crystal fragments

Jan 1, 1955

By C. E. Mills

STUDIES of ground movement and subsidence resulting from mining operations cover a broad field. It is also a very important consideration and one that eventually affects nearly every mining operation of any extent. The damage to surface buildings, removal of mine surface plants and replacements of main hoisting shafts must reach an astounding expenditure were these cost figures available over a period of years. Were the subject one of mathematical formula and dependent only on the angle of draw of the walls or country rocks, the problem would be relatively simple. Consideration must be given to depth and extent of workings; structural conditions of the orebodies and enclosing country rock; physical properties of these same rocks, including schistosity, bedding, jointing, slips, dikes, faults, and other structural weaknesses. The method of mining, extent of openings, supporting pillars, and amount of moisture or water underground are other pertinent factors. With such a large number of variable factors, it is apparent that the subject of subsidence is one that must be based largely on experience and results at other mines where conditions are somewhat comparable. In presenting this paper, it is the intent to describe the progressive results of past ground movements at the United Verde, to bring out physical conditions largely responsible for this movement, but to refrain from theorizing on the ultimate extent of subsidence resulting from future mining operations.

Jan 1, 1934

By AIME AIME

Russell B. Paul, Chairman of the Special Committee on Divisional Relationships, presented the interim report of his Committee which was published in the September, 1945, issue of MINING AND METALLURGY and a copy of which is incorporated in the official minutes of this meeting. The following specific actions were taken by the Board of Directors in relation to the six recommendations in the Summary of the Report as published: (1) Mr. Haider, Chairman of the Petroleum Division, presented the formal request of his Executive Committee that the headquarters of the new Secretary of the Petroleum Division be established in Dallas, Texas. After lengthy discussion in which the point was made that the success of this program would depend upon effective co-operation between the Chairman of the Division, the Secretary of the Petroleum Division, and the Secretary of the Institute, the request was approved. The new secretary will be selected by the Division and will be employed by the Institute in the capacity of an Assistant Secretary. (2) The following item in the report was approved:

Jan 1, 1945

By Michael Tenenbaum, T. L. Joseph

Recent researches on the reduction of iron ores have stimulated interest in the effect of increased pressures within the iron blast furnace. From a physicochemical viewpoint, it seems logical to suppose that the increased pressure would increase the rate of reduction of the iron ore within the furnace. This increased reaction velocity would in turn be reflected in an increase in the output of the blast furnace. Any substantial effect of elevated blast-furnace pressures should accordingly be of both technical and economic interest to the operator. It is doubtful whether it is possible to increase the pressure in the stack of the blast furnace beyond two or three atmospheres without incurring severe mechanical difficulties. The benefits to be procured by elevations in pressure must therefore be restricted to pressures below two, or at the most, three atmospheres. Within this range it would seem both economically and mechanically feasible to modify the present design of the upper portion of the blast furnace to accommodate these more stringent operating conditions. This investigation was undertaken to study the effect of moderate pressures on the rate of reduction of iron ore with hydrogen. The use of carbon monoxide is contemplated for later work. Although any results that are obtained in the laboratory cannot be interpreted directly in terms of large-scale commercial operations, it is possible, through such an investigation, to ascertain the order of magnitude of the effects of higher pressure. A more quantitative conception of the effects that would result from the use of increased pressures in the modern blast furnace is needed. In some recent work, Diepschlagl found that, all other factors remaining constant, the degree of reduction of iron ores was much greater when carried out under pressure. Pressures as high as seven atmospheres were used. The degree of reduction was determined from the ferrous and ferric iron in the sponge iron. Results were obtained using both carbon monoxide and hydrogen at temperatures of 400°, 600° and

Jan 1, 1939

By Michael Tenenbaum, T. L. Joseph

Recent researches on the reduction of iron ores have stimulated interest in the effect of increased pressures within the iron blast furnace. From a physicochemical viewpoint, it seems logical to suppose that the increased pressure would increase the rate of reduction of the iron ore within the furnace. This increased reaction velocity would in turn be reflected in an increase in the output of the blast furnace. Any substantial effect of elevated blast-furnace pressures should accordingly be of both technical and economic interest to the operator. It is doubtful whether it is possible to increase the pressure in the stack of the blast furnace beyond two or three atmospheres without incurring severe mechanical difficulties. The benefits to be procured by elevations in pressure must therefore be restricted to pressures below two, or at the most, three atmospheres. Within this range it would seem both economically and mechanically feasible to modify the present design of the upper portion of the blast furnace to accommodate these more stringent operating conditions. This investigation was undertaken to study the effect of moderate pressures on the rate of reduction of iron ore with hydrogen. The use of carbon monoxide is contemplated for later work. Although any results that are obtained in the laboratory cannot be interpreted directly in terms of large-scale commercial operations, it is possible, through such an investigation, to ascertain the order of magnitude of the effects of higher pressure. A more quantitative conception of the effects that would result from the use of increased pressures in the modern blast furnace is needed. In some recent work, Diepschlagl found that, all other factors remaining constant, the degree of reduction of iron ores was much greater when carried out under pressure. Pressures as high as seven atmospheres were used. The degree of reduction was determined from the ferrous and ferric iron in the sponge iron. Results were obtained using both carbon monoxide and hydrogen at temperatures of 400°, 600° and

Jan 1, 1939