This paper describes, in detail, results obtained from a research study of a complex iron ore aiming to produce a pellet feed concentrate with at least 65% of Fe and less than 3.5% of SiO2 in the final concentrate. The work includes an ore desliming followed by column flotation at laboratory scale. The ore sample was from Carajás province - Brazil and represents a complex low grade compact itabirite ore, analyzing 35.9% Fe, 45.1% SiO2 and 0.57% of Al2O3. Yet, the feed was treated previously by magnetic separation and grounded to 97% < 20 µm; this sample was named MAG 2. The chemical and mineralogical characterization of the MAG 2 sample showed that Fe and SiO2 grades were 50.7% and 24.3% respectively and was composed mainly by hematite, goethite and quartz. The particle size distribution, using a laser diffraction technique, showed that 90% of the particles were < 18 µm; 50% less than 8 µm and 10% minor than 1 µm. When the cationic reverse flotation without desliming was tested the selectivity of the process was very low and did not meet the concentrate metallurgical goals of the pellet feed product. However, when desliming was applied prior to flotation, a concentrate product with chemical characteristics of the pellet feed was obtained. The best results after desliming and column flotation achieved global iron metallurgical recovery of 72% with Fe grade in the concentrate of 66.5% and 2.1% SiO2 using starch as depressant for the iron oxides minerals at 1200 g/t ? 1500 g/t and an amine as the quartz collector at 100 g/t concentration (pH constant, at 10.5). It is believed that the desliming stage was key in the separation of the iron bearing particles and has a high potential for the flotation process of this type of ores.

Sep 1, 2012

By H. M. Gao

According to the difficulty of dolomite removal from collophanite,normal-reverse floatation process has been adopted in floatation with the use of highly selective collector G-4 and depressant S721. Good indexes of flotation have been obtained with the run-of-mine ore containing 17.96 % P2O5 and 2.31 % MgO being upgraded to a concentrate containing more than 30% P2O5 and less than 1% MgO. The reagent interaction mechanism in low grade collophanite flotation has been stu-died by FTIR analysis and theoretical calculation. The results indicate that the interaction between collector G-4 and collophanite is the result of chemical adsorption in combination with physical ad-sorption with chemical adsorption playing the major role. Depressant S721 adsorbs on dolomite surface to form a water film and effectively depresses the flotation of dolomite and reduces the MgO content in the concentrate.

Jan 1, 2014

By T. Wajima

We tried to convert paper sludge ash (PSA) into zeolitic product with high cation exchange capacity (CEC) through acid leaching. Typically, PSA from incineration of paper sludge contains a high percentage of calcium in the form of anorthite (CaAl2Si2O8) and gehlenite (Ca2Al2SiO7). It is difficult to convert the ash with a high Ca content into zeolites, or at least into more desirable zeolite phases. Acid leaching with HCl was applied to reduce the Ca content to synthesize zeolitic product with high CEC. The raw ash was treated with 1 M, 3 M, and 5 M HCl solution for 0.5~24 hours (the ratio of the ash to volume of HCl solution was 1/4), and then zeolitic product was synthesized from leached ash through the reaction with 2.5 M NaOH solution at 80 oC for 24 hours. During acid leaching, gehlenite is readily dissolved in a lower HCl concentration solution than anorthite. With increasing HCl concentration, the amounts of Ca, Mg, Si, Al, Fe and Ti extracted from the ash increased. Ca and Mg contents were easily extracted from ash than other elements. The contents of Ca and Mg extracted rapidly at initial stage, and then levelled off. The saturation times of Mg and Ca are almost 0.5 h using all concentrations of HCl solutions. After the synthesis from leached ashes, zeolite-A and -P were synthesized from ash leached in 1 M HCl solution, and 3 M and 5 M HCl solutions, respectively, regardless of leaching time. With in-creasing HCl concentration, the Ca content eluted from the product decreased, due to the removal of Ca via acid leaching before the synthesis, while the Na content eluted from the product increased to 3 M HCl and then decreased, which was almost similar to the CEC of the product, due to the ion exchange of Na-type zeolitic phase in the product. The change of zeolite phases in the product and the CEC of the product depend on the concentrations of Si and Al in the solution during the synthesis. The highest CEC of the product is about 220 cmol/ kg, which was synthesized from the ash leached in 3 M HCl solution.

Jan 1, 2014

By S. N. Shahcheraghi

Grinding is one of the most important and expensive steps in mineral processing allocating about 70% of the total energy in the plants. Nowadays, for optimizing the energy consumption in these equipments, the rock behavior and its size distribution during the crushing have been normally predicted using selection and breakage functions to be able to optimally model and design grinding circuits. For this purpose, the case of Miduk copper mine in Kerman province, Iran was studied. The samples were taken from primary ball mills feed and were subject to screen analysis to achieve uniform sizes. Then, selection and breakage functions were determined at the different grinding times in laboratorial ball mill. Finally, ore size distribution in different grinding times was estimated using MATLAB software

Sep 1, 2012

By Ashish Agarwal

For a correct evaluation of the performance of any process, it is important to reconcile the data gathered in the plant from the material balance point of view for all the streams flowing in and flowing out of the process unit. There are two main approaches to reconciliation of data, which involve minimization of the sum of the squares of: (i) the closure residuals and (ii) the component adjustments; both weighed with the estimated variances of the components. Though, these approaches have served us well, it has not been possible to ascertain if the reconciled values for various components and the split factors obtained using these approaches are truly the best estimates. In this paper, this aspect has been investigated by analyzing pseudo-experimental data of known error structure on size classification of particles in a hydrocyclone. Three types of basic error structures were considered for the measured component values: absolute error, relative error and chi-square error. The error structure was modified by adding a random component of error using normally distributed random numbers corresponding to zero mean and different levels of variance. By carrying out a large number of simulation experiments, it has been shown that in the presence of random errors, irrespective of the basic error structure of data, which is usually unknown, the chi-square error minimization criterion can be used to obtain most reliable results. Keywords: data reconciliation methods, chi-square error minimization

Sep 1, 2012

By V. Sheikhzadeh, M. Saghaeian, R. Hejazi, M. Zare

High Pressure Grinding Roll (HPGR) plays a major role in increasing specific surface area of iron ore concentrate for producing pellet feed. HPGR grinding mechanism implies that material be compressed between the two rolls, therefore layer of material must be able to resist required pressure for achieving suitable grinding conditions. In this study for determining a simple relationship between material pressure resistance ability and HPGR main design parameters, piston press tests were performed on different iron ore concentrate samples along with HPGR Blaine increasing tests. Piston press tests results showed that by decreasing moisture content, material pressure resistance increased and in constant moisture content this parameter will change based on material specifications. HPGR Blaine increasing tests results showed that by decreasing moisture content, HPGR specific throughput and working gap increased and in constant moisture content this parameter will change based on material specifications. For all of the studied samples at worst condition, we got the results including: HPGR delta gap equal to zero, specific throughput lower than 200 ts/hm3.According to the tests results, HPGR Applicability Index (HAI) can be introduced at four different class types from 1 (weak) to 4 (excellent). This index determines achievable specific throughput and possibility of using HPGR according to material specifications, i.e. for HAI 1-4 the pressure resistance is <90, 90 to<125, 125 to <150 and = 150 bar, respectively. Similarly for HAI 1-4 specific throughput is <200, =200, =220 and =250, respectively. So based on design moisture content, if concentrate HAI is 3 or 4, HPGR is a correct choice. For HAI 2, HPGR can also be used. But for a material with HAI equal to 1, HPGR is not a good solution. As a result in order to apply HPGR for HAI 1, material condition such as moisture or slime content should be decreased.

Jan 1, 2018

By Z. G. Li

The large-scale vibrating screen has been applied widely in coal industry and other industrial areas as a kind of important device. As vibration mechanical device, it works very hardly and works in very bad environment so that the structure of screen is damaged easily. Therefore, it is very important that how to detect the fault of structure as early as possible to make the repair schedule reasonably and economically and to avoid the body hurt and device damage. As a kind of important structure of vibrating screen, the lower crossbeam is the main carrying structure and it is easily damaged, so it is regarded as a researched object in this thesis and it is tested under the load in the laboratory. Based on the test, acoustic emission wave signals can be got-ten by modern acoustic emission testing technique. Then, the ?wavelet packet - energy? from the characteristics of acquiring signals is used as neural network input vector. In the BP network structure design, the design of a hidden layer with variable number of BP network is established. Based on the error by contrast, the best nerve number can be identified in the hidden layer. Through integrated analysis, using Levenberg-Marquard BP study algorithm, network-training errors are relatively small, the acoustic emission signal is used in BP neural network as a pattern of recognition. In Matlab6.5, neural network model identification is created and taking advantage of nonlinearity and the ability of learning and memory of Neural Network, this model is fixed by training structure of network with training samples. The work presented shows that acoustical emission signal processing and research on early fatigue fault diagnosis based on the wavelet and the neural network is viable.

Jan 1, 2014

By ?. Kostadinov

Theoretical study of the behavior of grinding medium presented by TBP (tetraballpebs) was conducted by computer modeling of the position of grinding medium at different speeds and different drum fill factor. For the modeling were used known equations of motion derived for the ball load. Algorithm was created by SolidWorks software, allowing determination of center of gravity of the load in the mill and energy for grinding. These results were compared with similar results obtained by ball grinding medium. The capabilities of both grinding media are demonstrated by graphics under the following conditions: 1.Equal dimensions of the experimental model of the mill; 2.Equal mass of the grinding loads; 3.Comparison of grinding bodies with the same number, mass and density. Keywords: simulation, behavior, grinding medium, balls, tetraballpebs

Sep 1, 2012

By Ahmad Amini, Hadi Abdollahi, Pouya Karimi

Due to detrimental effects of cyanidation process on the environment in gold industry, application of cyanide alternatives such as thiourea are being highly considered in recent projects. In this study, the extraction of gold from poly metal ore, using thiourea was precisely investigated. The representative sample contained 2.5 ppm Au and 160 ppm Ag. The sample was categorized as oxide gold ore, because the main part of its pyrite was changed to iron oxide and hydroxide such as goethite and lepidocrosite. According to mineralogy, the main gangue mineral was quartz. It shows that gold grains are free and interlocked with quartz matrix. Also, the presence of a high amount of silver in free and sulfide forms and also the low content of other sulfide minerals such as base metal sulfides is a remarkable point of these studies. In the gold extraction process with thiourea, there are several parameters that affect the rate of gold dissolution such as concentrations of thiourea as a gold lixiviant and ferric sulfate as an oxidant, pH and size fraction of feed and leaching time. The influence of these parameters on the gold dissolution rate were investigated and optimized. The results showed that the concentration of thiourea is the most influential parameter which could increase the gold recovery to 71% (at 10 g/kg sample). The optimal amount of ferric sulfate was determined as 6 g/kg sample. Also, the optimal levels of size fraction of feed and pH of solution were 88% under 75 micron and 2 as acidity; respectively. Leaching time was 6 hrs. In addition, this sample was leached with cyanide and the optimized values of size fraction of d88=75 microns, pH=10.45, 2500 ppm of sodium cyanide with time leaching of 24 hours were concluded for maximum recovery of gold in solution. Finally, the results of cyanidation tests were compared to the thiourea dissolution after optimizing all affected parameters in cyanidation process.

Jan 1, 2018

By Caroline Olsen

The objective of this study was to achieve Zn activation control in an industrial Cu flotation circuit treating a complex Cu-Pb-Zn-Au-Ag sulphide ore at the LaRonde Division of Agnico-Eagle Mines Limited (Québec, Canada). In order to provide process relevant results, a laboratory testing methodology was developed to duplicate plant operational parameters. The action mechanisms of ZnSO4, TETA (triethylenetetramine) and NaHSO3used as depressants in order to limit ZnS activation were examined. Laboratory flotation tests with and without Cu2+ions (the ions responsible for ZnSactivation)were performed. All depressants showed equal or better flotation performance relative to baseline tests. For example, in the presence of Cu2+, the Zn recovery reduced from 32.2% to 17.5% in the copper rougher concentrate after adding ZnSO4(with a dosage of 50 g/t). TOF-SIMS analyses confirmed the relative decrease in surface Cu in the samples treated with ZnSO4and TETA. For the case with TETA, this indirectlyindicates the formation of a copper TETA complex in solution, thereby reducing available Cu for transfer. The TOF-SIMS and XPS data indicate that the addition of ZnSO4and NaHSO3resulted in an increase in surface metal hydroxides and SO3 on ZnS grains inhibiting both Cu and collector attachment.ZnSO4 was subsequently tested with success in the LaRonde concentrator. The addition of 40 g/t ZnSO4 at the conditioning (or cleaning) stage led to a 2% reduction in Zn content in the Cu and PM concentrate. Recently, improvements towards the control of copper sulfate addition in the downstream Zn flotation circuit resulted in the reduction of Cu2+ in process water. As this ?cleaner? water is recycled for Cu and PM flotation, the addition of ZnSO4 is now used only as required.

Sep 1, 2012

By L. Y. Feng

The percentage of leached zinc in massive zinc oxide ores (11.7% Zn, >2 mm) is up to 73.3 % in 120 days. Alternatively, crushed to -0.154 mm, mixed with cement 5% (wt), pelletized and solidified. The diameters of the pellets obtained are between 5 mm to 8 mm. When the pellet solidification periods are 3 days, 10 days and 45 days respectively, the alkaline leaching rates of zinc in the pellets are up to 95.8%, 89.1% and 76.4% respectively. Decreasing the solidification time can re-duce reaction time, increase dissolution of zinc in pellets and lower the effect of initial zinc concentration on leaching rate. The experiment results show that the minimum solidification time is three days, and the kinetic study indicates that alkaline leaching of the low grade zinc oxide pellets is controlled by the diffusion of the leach liquor through the gangue layer in the whole leach process, and the apparent rate constants are 3.33×10-2 day-1, 9.18×10-3 day-1, 5.82×10-3 day-1 respectively.

Jan 1, 2014

By P. T. Nguyen

The analysis of particle capture by an air bubble by two separate phenomena of collision and attachment has been difficult due to the uncertainty in determining when and where the two phenomena begin and terminate at the bubble surface, respectively. Therefore, a unified analysis was developed by solving the motion equation for the particle capture as one process. No distinction be-tween collision and attachment was made. Both the liquid film described by the micro-hydrodynamic resistance functions and the surface forces were included in the new model. The model predictions with the DLVO (Derjaguin-Landau-Verwey-Overbeek) surface forces did not agree with the experimental trajectories of latex and silica spheres. The model predictions with the inclusion of the non-DLVO attractive surface force agreed with the experimental data. The non-DLVO force reduced the repulsion between the non-attaching particle and the bubble, and significantly increased the attraction between the attaching particle and the bubble. The unified analysis is capable of predicting particle capture without the use of the induction time. The unified analysis also shows significant influence of the short-range hydrodynamic interactions on the collision which has been previously ignored.

Jan 1, 2014

By Juan B. Yianatos

"After almost 100 years, since the first commercial application began in Australia, flotation has shown an extraordinary growth and nearly 2 billion tons of ore per year are presently treated by flotation processes. During this time flotation has promoted a wide scope of research activities ranging from fundamental chemistry and hydrodynamic studies to studies of industrial operations. In general, fundamental studies have been mainly related to ideal situations. In recent years, however, large efforts have been focusing on achieving a better insight into the actual sub-processes provided by the development of new and more sophisticated instrumentation. Since the massive incorporation of flotation columns, around 15 years ago, a renewed interest in flotation fundamental studies, process modelling and new cell designs have been observed worldwide. The key role of the froth has been recognized as an independent and sometimes rate limiting process step. Thus, separation of pulp and froth process stages seems the most appropriate in terms of process modelling, diagnostic, design and scale-up purposes.In relation to flotation equipment development, until the middle of the 1970’s, only the sub-aeration mechanical cells were dominant. Since the 1980’s, the use of pneumatic cells and forced air mechanical cells has emerged strongly. Also, in the last decade, flotation equipment has shown a dramatic increase in size, reaching values of 200m3 in unitary mechanical cells and more than 300m3 in columns. The general feeling, however, is that, despite the great advance observed in terms of process knowledge, the mechanisms and principles of industrial flotation cells design and scale-up are still not fully understood.Advances in process instrumentation and control now in use allow for more efficient operations, both in metallurgical performance and savings in operating costs."

Jan 1, 2003

By Jim Petrie, Mary Stewart, Damien Giurco

This paper describes a generic approach to analysing the environmental and economic performance of a global mineral/metal value chain, with the express view of improving the quality of prospective decision-making within the industry in order to ensure more sustainable outcomes. The starting point for this analysis is the development of a global stocks flows and transformations model, for the metal of interest. Any aspect of the value chain, e.g. “metals refining, “goods manufacture”, “use and disposal”, can be assessed, either relative to other stages in the value chain, or in more detail by focusing on the technologies used within that stage. The use of this model as a decision support tool is explored here for the case of copper. Both primary and secondary production routes are enumerated, covering a range of processes, for seven distinct geographic regions round the globe. The value of the modelling approach is explored for different energy mixes. In particular, the case study examines the impact of increased recycling on the (re) distribution of global and regional environmental impacts for technologies-in-place in these different regions.

Jan 1, 2003

By Shailin Lalloo, Allan B. Nesbitt

A fluidised bed was exposed to high gravities by placing it in a centrifuge. The bed expansions were measured and compared with the bed expansions predicted by the Richardson-Zaki model (1954). The Richardson-Zaki model was found to predict effectively the fluidisation behaviour of defined particles in this increased gravity environment.

Jan 1, 2003

By P. K. Sen, Mrinal K. Ghose

Tailing slurry is usually abrasive and possesses high viscosity. This paper examines the existing iron ore beneficiation process and focuses on some of the key environmental issues related to the disposal of tailings. It identifies that almost 32% of the iron ore extracted ends up as tailings and they are usually disposed in slurry form in tailing ponds. By the year 2000, 27 Mt of iron ore tailings were generated in India, which has become one of the biggest waste handling problems to the industry. Characteristics of the tailings vary widely. So the physical nature of tailings cannot be considered separately in isolation without considering the mill effluent from the beneficiation plant. In the present investigation, studies were carried out in three iron ore mines in India to evaluate the characteristics of tailings from the beneficiation plant. The tailing samples were collected from different locations during a time period of one year and analyzed. The results will be discussed and the characteristics of the tailings have been evaluated. The disposal system of tailings at the three mines was evaluated. The research on the settling characteristics of tailings indicates that the area provided in the existing tailing ponds in India is much more than that of the experimental results. This paper concludes that sedimentation tests are essential to design appropriate tailings pond with respect to size. In the proposed scheme it is suggested that an additional unit process, i.e. sedimentation tank be added to the process before the disposal of tailings to the tailing pond.

Jan 1, 2003

By G. Y. Zhou

During Zijinshan copper heap bioleaching, pyrite was leached in plenty resulting in high ferric concentration in solution. It has affected bioleaching and extraction processing greatly. It results much acid and iron in solution and bad effect to extraction processing. The paper studied the influence factors in the course of pyrite leaching and ferric ion chemical oxidation, especially studied the redox potential for copper bioleaching so as to find key factors affecting the dissolution difference between chalcocite and pyrite. The results show that the redox potential is important factor. Copper and pyrite leaching rates are 95% and 11% respectively and there is great dissolution difference between them at redox potential 700 mV (SHE). During pyrite bioleaching, the indirect action of bacteria gives priority to bioleaching cooperating with the direct attack of microbial cells attached to the mineral surface. Redox potential is determined by ratio of ferric and ferrous, ferric in solution was supplied by the way of oxidation of T. f bacteria, sufficient bacteria concentration and active character were two vial factors of controlling redox potential. It is indicated that copper can be selectively bioleached during copper bioleaching by controlling redox potential of bioleaching. The conclusion will provide theoretic foundation on balance of acid and iron during bioleaching for copper of higher S/Cu ratio. The experinment proved that bacteria activation was decreased on condition of both low pH value and intermittent aeratation during bioleaching. It resulted that the oxidation velocity of ferrous ion was decreased and redox potential was controlled. The dissolution of pyrite was depressed. It would be possible to actualize selective leaching of secondary sulfide copper ore during bioleaching process.

Jan 1, 2014

By Y. B. Zhang

China is rich in iron ore resources, but most of these ores are low-grade, polymetallic and refrac-tory ones. Furthermore, with the rapid development of chinese iron & steel industry, the comprehen-sive recovery of these ores is becoming more and more important. The tin, zinc-containing complex iron ores are typical polymetallic and intractable ones, and great reserves of them are found in China. At present, they have not been efficiently utilized. In this paper, based on the investigation of basic physicochemical properties of the tin, zinc-bearing iron concentrates, taken from a mineral processing plant, the mineralogy reason that these concentrates are so intractable and refractory is found out, using advanced microscopic testing methods, such as optical microscope (OM), Scanning Electronic Microscope (SEM), X-ray diffrac-tion (XRD), etc. It is found that the symbiotic relationship of iron, tin and zinc metallic minerals are very complicated, and magnetite in the concentrate is closely symbiotic or enwrapped by fine cassi-terite and sphalerite. So it is difficult to separate tin and zinc completely from the iron concentrates by simple regrinding and physical separation method. This investigation provides theoretical guid-ance for developing new approaches for utilizing these concentrates.

Jan 1, 2014

By Vinay Jain, Dharmendr Kumar, Beena Rai, Venugopal Tammishetti

"Selective dispersion-flocculation is considered to be an effective process for the beneficiation of ultrafine particles. This process is based on the preferential adsorption of a flocculant on the mineral particles to be flocculated, leaving rest of the mineral suspended. It has been successfully implemented at plant scales for the beneficiation of ultrafine particles of iron ores, for which conventional methods such as gravity separation, magnetic separation and flotation do not work efficiently. However, the key element responsible for the success of any selective flocculation process is the appropriate choice of the flocculant used for achieving the desired selectivity. At our lab, we are working on design and development of such selective reagents for mineral processing applications, including the beneficiation of iron ore slimes, using a combined molecular modeling and experimental approach. In this study we have employed density functional theory (DFT) to calculate the interaction energies and explain the interaction mechanisms of chitosan with the main minerals present in iron ore slimes, namely, hematite [a-Fe2O3], goethite [a-FeO(OH)], gibbsite [a-Al(OH)3] and kaolinite [Al2Si2O5(OH)4]. The magnitudes of the computed interaction energies follow the trend: Hematite > Goethite > Gibbsite ~ Kaolinite Al-OH terminated > Kaolinite Si-O terminated Analysis of the optimized geometries and electronic structures reveals that the O & N atoms of chitosan molecule form coordinate bonds with surface Fe-atoms of hematite while only weak hydrogen bonds are formed in the case of goethite, gibbsite and kaolinite surfaces thus explaining reasons behind the stronger interactions with the hematite surface. The theoretical findings were validated by performing selective flocculation experiments using chitosan as a flocculant. The selective flocculation experimental results show that a final concentrate of ~60% Fe can be obtained from a feed containing 53.13% Fe with Fe recovery of 74%. The mineral estimation in the obtained concentrate indicated that hematite and goethite are recovered in concentrate while gibbsite and kaolinite are rejected in the tails. These observations were consistent with our theoretical findings. Our work highlights the promising role molecular modeling techniques such as DFT can play in the design and development of selective reagents for beneficiation of alumina-rich iron ore slimes."

Jan 1, 2018

By Tom Liu

This paper is a fundamental study of bubble-particle collision efficiency in turbulent flows. A CFD-based microscale scheme for the prediction of turbulent bubble-particle collision efficiency in a 3D isotropic turbulent flow is developed, and in this way, turbulence effects on particle-bubble collision efficiency are taken into account for the first time. By comparing the computed results with experimental data from the literature, the CFD simulation is shown to correctly predict the bubble-particle collision efficiency in a quiescent environment. The CFD method was then applied to the investigation of bubble-particle collision efficiency in a turbulent flow, and the simulation results are shown to be qualitatively consistent with the real observations. The predicted collision efficiency can be used in a multiscale modelling scheme, which would account for all control variables in a flotation cell, such as impeller structure and tip speed, air nozzle structure and air flow rate This study indicates how microscale simulations of bubble and particle behaviours, coupled to macroscale CFD simulations of flotation cells, can provide a powerful tool predicting the flotation rate in a real flotation cell.

Jan 1, 2014