By R. G. Bowman

Discussions of processes for the manufacture of white lead generally open with the statement that white lead is the oldest chemical pigment known to man. This fact is of more than historical interest; in the light of the present extensive use of white lead, it indicates that the compound possesses characteristics that make it unique among white pigments, and superior to all in its particular field. A greater variety of processes have been proposed for manufacturing white lend than for any other one chemical compound. Only a few of these processes have come into commercial use, however, and a large part of the present production here and abroad is made by the process used in ancient times. The outstanding disadvantages of the old process are that it is slow and laborious, affords no control of the product, and yields at best an impure material lacking in uniformity. Improved processes, sometimes classed all together as "quick processes," have had as their main object the shortening of the time required. Most of them accomplish this and some have yielded a superior product as well, but only two or three are now in use commercially. For centuries the manufacture and mixing of paints have been treated as an art, and the practice has been much influenced by tradition and precedent. There is a reluctance to abandon old materials for this purpose, and as few new uses for white lead have been developed, the adoption of the quick processes has been slow. The electrolytic production of white lead is not new, a large number of processes and forms of apparatus have been proposed and patented within the past 25 years, all directed toward the production of white lead, wholly or in part, by electrolysis. One or two of these processes were tried commercially but proved unsuccessful. Process The Sperry process, used by the Anaconda Lead Products Co., is the invention of Elmer A. Sperry, and was worked out to a commercial basis at the East Chicago plant. It resembles, in a general way, earlier methods, but embodies the features that make it possible to operate

Jan 1, 1926

By C. M. Wayman, J. F. Breedis

The crystallography of the martensitic transformation in the Fe-30 Ni alloy was reinvestigated. The scatter in the habit Plane as determined from measurements on the mid-rib plane was smaller than reported previously, and the orientation relationship was determined from a martensite plate having known direction cosines. From agreement with crystallographic theory and from observations of the morphnlogy of the martensite plates, it is suggested that the mid-rib plane represents the starting region of the transformation. THE crystallography of the martensitic transformation in the iron-nickel system has been the subject of many investigations.&apos;-7 However, for iron alloys containing approximately 30 wt pct Ni, a wide scatter in the reported habit planes exists. In only one instance has a Laue determination of the orientation relationship been made, but the habit plane of the martensite plate studied was not determined experimentally. Because the most successful thermodynamic and kinetic analyses8 of the martensite transformation have been based on Fe-30 Ni alloys, it was considered desirable to reinvestigate the crystallographic features of the transformation in this alloy. Lieberman9 suggested that the most significant information for use in a theoretical treatment involves the determination of all the crystallographic observables from a single plate of the product phase. This was first done in essence by Greninger and Troiano10 for Fe-22 wt pct Ni-0.8 wt pct C, and is the method followed in this investigation. Some theoretical approaches11-13 in describing the martensitic transformation consider the overall transformation distortion to be comprised of a Bain distortion, or lattice deformation (PI, which produces the structure change, and a lattice invariant deformation (G), such as twinning, which together leave the interface or habit plane un-distorted. The incorporation of a rigid body rotation (R) results in a transformation distortion (E) such that the interface plane is left both undistorted and unrotated. In matrix notation, E = RPG where the lattice invariant deformation has "taken place" in the austenite. Bowles and Mackenzie14-16 in formulating a theoretical approach proposed an adjustable scaler quantity, denoted as 6, which represents a uniform dilation in the interface plane. This dilation acts to adjust the lattice spacings of the parent and product structures at the plane of contact. Using the dilation parameter as a variable, these authors were able to account for a continuous variation of habit planes in steels along a curve in the stereogram between {225}A and {259}A. she invariant line strain14 of the transformation is 6 RP, and the corresponding transformation distortion is E/6.) With the dilation parameter known, the invariant line is computed as the triple coincidence of the habit plane, the shear plane of the lattice invariant deformation, and the initial Bain cone.14 The contraction axis for the Bain distortion can be taken9&apos;17 as [010]A, and the correct permutation of the habit plane indices used. Kelly and Nutting 18 have established the shear plane (of twinning) in the tetragonal martensite of Fe-22 Ni-0.8C to be {112)M by means of transmission electron microscopy. The reasonable shear system is then {112}M which is equivalent to {011}A <01l>A. The as-

Jan 1, 1962

By Strathmore R. B. Cooke, Thomas E. Bam

The paper discusses the mineralogy, structure, and strength of magnetite pellets fired in air and in a neutral atmosphere at various temperatures. The information obtained from this investigation is used to explain the origin of the structures occurring in pellets produced by pilot-plant operation. MUCH experimental work has been performed on i-VL the mechanism of agglomeration and pelletiz-ing of moist ore and concentrates and on the process of firing agglomerates, but except for the work of Tigerschiold and Ilmonil much of the published information is empirical, and the literature contains no information concerning the structure of fired pellets. Results of a preliminary study of the micro-structures occurring in pellets produced both in the laboratory and on a pilot-plant scale are presented in this paper. Most of the results were obtained from pellets prepared from Mesabi magnetic taconite, but through the courtesy of the staffs of the Minnesota Mines Experiment Station and the Bethlehem Steel Co., fired pellets produced from limonite and hematite ores and from Lebanon magnetite have also been examined. The work has been restricted almost entirely to pellets produced without additives, the exceptions being those in which coal was added to the filter cake before rolling. Schwartz has described the microstructures occurring in ore sinters produced under reducing conditions.&apos; Many of the structures and constituents he describes are common to fired pellets, but the constituents normally occur in markedly different proportions. His statement that "in all satisfactory sinter the amount of hematite is small, perhaps not over 2 or 3 per cent" is inapplicable to pellets produced by pilot plant operation or by any process in which air is not deliberately excluded. Pilot plant pellets contain over 90 pct by weight of hematite, and those produced in the smaller furnaces of the Minnesota Mines Experiment Station contain more than 80 pct of that constituent. Preparation of Specimens It is difficult to examine unfired pellets microscopically because of their insufficient coherency to withstand sectioning and polishing. Fired pellets sometimes lack coherency and frequently contain holes which are troublesome during polishing. Impregnation of both air-dried and fired pellets is readily accomplished by the use of methyl metha-crylate monomer." The dry pellets are covered in a test tube with excess monomer, to which a small amount of accelerator has been added. When the test tube is placed in a cooling bath and evacuated with an aspirator, most of the entrapped air is removed, and disruption of weak pellets by boiling of the monomer is reduced to a minimum. Polymerization is then effected by immersion of the test tube in a water-bath at about 45"C, this temperature being held for 4 or 5 days. The test tube may then be broken away from the solidified mass and the pellets sectioned by a carborundum wheel or a diamond saw. Where time is important, impregnation is carried out at a higher temperature by Meyer&apos;s method.&apos; Air-dried pellets must be impregnated with especial care; otherwise swelling occurs and the solids are displaced. It is more important to be certain that the monomer forms a reasonably complete network throughout the specimen than that all entrained air is removed, and for this reason the vacuum technique may be omitted. Impregnated agglomerated products and pellets are extremely coherent, section well, and may be polished either by hand or by machine. Hand polishing is not satisfactory for the examination of conditions existing at the boundaries of grains, and for this machine polishing must be used. The Graton-Vanderwilt machine gives excellent results, provided that pressure on the specimen is considerably in excess of that recommended by the manufacturer. Mineralogy of Fired Pellets Only two opaque iron minerals, magnetite and hematite, have been recognized in pellets. The complete identity of, these artificial minerals with their corresponding natural counterparts is shown by their mineralographic characteristics and their X-ray structures. Wiistite has not been found. Slag is the most common transparent constituent of fired pellets. Occasionally conditions have been appropriate for the crystallization of fayalite from the slag, and at other times another crystalline sil-

Jan 1, 1953

By Strathmore R. B. Cooke, Thomas E. Bam

The paper discusses the mineralogy, structure, and strength of magnetite pellets fired in air and in a neutral atmosphere at various temperatures. The information obtained from this investigation is used to explain the origin of the structures occurring in pellets produced by pilot-plant operation. MUCH experimental work has been performed on i-VL the mechanism of agglomeration and pelletiz-ing of moist ore and concentrates and on the process of firing agglomerates, but except for the work of Tigerschiold and Ilmonil much of the published information is empirical, and the literature contains no information concerning the structure of fired pellets. Results of a preliminary study of the micro-structures occurring in pellets produced both in the laboratory and on a pilot-plant scale are presented in this paper. Most of the results were obtained from pellets prepared from Mesabi magnetic taconite, but through the courtesy of the staffs of the Minnesota Mines Experiment Station and the Bethlehem Steel Co., fired pellets produced from limonite and hematite ores and from Lebanon magnetite have also been examined. The work has been restricted almost entirely to pellets produced without additives, the exceptions being those in which coal was added to the filter cake before rolling. Schwartz has described the microstructures occurring in ore sinters produced under reducing conditions.&apos; Many of the structures and constituents he describes are common to fired pellets, but the constituents normally occur in markedly different proportions. His statement that "in all satisfactory sinter the amount of hematite is small, perhaps not over 2 or 3 per cent" is inapplicable to pellets produced by pilot plant operation or by any process in which air is not deliberately excluded. Pilot plant pellets contain over 90 pct by weight of hematite, and those produced in the smaller furnaces of the Minnesota Mines Experiment Station contain more than 80 pct of that constituent. Preparation of Specimens It is difficult to examine unfired pellets microscopically because of their insufficient coherency to withstand sectioning and polishing. Fired pellets sometimes lack coherency and frequently contain holes which are troublesome during polishing. Impregnation of both air-dried and fired pellets is readily accomplished by the use of methyl metha-crylate monomer." The dry pellets are covered in a test tube with excess monomer, to which a small amount of accelerator has been added. When the test tube is placed in a cooling bath and evacuated with an aspirator, most of the entrapped air is removed, and disruption of weak pellets by boiling of the monomer is reduced to a minimum. Polymerization is then effected by immersion of the test tube in a water-bath at about 45"C, this temperature being held for 4 or 5 days. The test tube may then be broken away from the solidified mass and the pellets sectioned by a carborundum wheel or a diamond saw. Where time is important, impregnation is carried out at a higher temperature by Meyer&apos;s method.&apos; Air-dried pellets must be impregnated with especial care; otherwise swelling occurs and the solids are displaced. It is more important to be certain that the monomer forms a reasonably complete network throughout the specimen than that all entrained air is removed, and for this reason the vacuum technique may be omitted. Impregnated agglomerated products and pellets are extremely coherent, section well, and may be polished either by hand or by machine. Hand polishing is not satisfactory for the examination of conditions existing at the boundaries of grains, and for this machine polishing must be used. The Graton-Vanderwilt machine gives excellent results, provided that pressure on the specimen is considerably in excess of that recommended by the manufacturer. Mineralogy of Fired Pellets Only two opaque iron minerals, magnetite and hematite, have been recognized in pellets. The complete identity of, these artificial minerals with their corresponding natural counterparts is shown by their mineralographic characteristics and their X-ray structures. Wiistite has not been found. Slag is the most common transparent constituent of fired pellets. Occasionally conditions have been appropriate for the crystallization of fayalite from the slag, and at other times another crystalline sil-

Jan 1, 1953

By M. E. Straumanis, J. -P. Krumme

In basic ([KOH + KCl] with a total polarity of 2) or acidic (2N H2SO4) electrolytes and at anodic current densities of more thun 2 to 4 ma per sq cnz, n-type GaAs single crystals of lozo resistivity preferentially dissol~je forming etch tunnels with triangular or civc~ilay cross sections and of a width between 0.5 arid 5 p. These etch tunnels are oriented along any one of the four possible (111) directions of GaAs. However, their growth occurs only in one direction of a given (111) whick apparently is determined by the atomic sequence Ga —As (and not the rezlerse) in respect to an individual valence bridge in the crystal. It is concluded from comparison with the cubic lattice structure of GaAs that the etch tunnels represent macroscopic evidence for the tetrahedral bonds and their polar properties. If the anodic current density is increased the tunnel fomation results in the development of a fibrous surface layer consisting of GaAs. The latter separates frorn the substrate (in an anodic s~irface disintegration process) by the growth pressure of an As,0, filnz forming in the interior of the fibrous layer, 100 to 200 µ under the surface, at more than about 50 ma per sq cni. The fibrous GaAs film has the same crystallographic orientation as the substvate and represents a skeleton of the original crystal. Since the etch-tunnel density in a separated GaAs layer is about 108 c?n-&apos;, and the etch tunnels develop only along (111) in a given polar direction, it is assurraed tlmt the dislocations have no influence on the growth of these tunnels. ElECTROLYTIC treatment of smooth surfaces of poly- and single-crystalline GaAs at high anodic current densities causes the formation of porous surface layers.&apos; This phenomenon suggests comparison with effects being observed with magnesium,&apos; indium,, gallium,4 and aluminum5 and known as "anodic disintegration". The purpose of the present paper is to explore and to explain the reasons for the formation of such surface layers on GaAs and, in particular, to investigate the influence of the lattice polarity of this III-V compound semiconductor in the (111) direction on the anodic dissolution behavior. GaAs SINGLE CRYSTALS For the experiments described below GaAs single crystals from the Monsanto Co., St. Louis, Mo., were used. Their impurity levels were below 1 ppm and their dopant levels between 1 and 100 ppm. They were grown in (111) using the Czochralski or the gradient-freeze technique. The crystals had n-type conductivity and electric resistivities between 1 and 5 ohm-cm. EXPERIMENTAL The GaAs single-crystal rods were cut perpendicularly to (111) into wafers of about 1 mm thickness using a wire-blade crystal slicer and an aqueous slurry of Sic or a diamond saw. The orientation of the faces of these wafers were checked by Laue back-reflection patterns. If there was a deviation from (111) the faces were abraded under a certain angle using grinding paper and distilled water. The damaged surface layer was removed from each crystal by chemical etching with a mixture of 1HF:1HNO3: 1H20 or 2HF:1HNO3:2HAc (glacial). {110) faces were obtained by mechanical cleavage, producing surfaces which did not require a further treatment. The GaAs wafers were mounted using "alligator" clamps instead of soldered electrical contacts.&apos; Only the bare crystal surfaces were dipped into the electrolyte. The clamps were coated with insulating wax to prevent any contact with the electrolyte. The experiments were carried out in aqueous 2 N H2so4,&apos; or in an aqueous solution of KOH and KCl1 (1 mole KOH + 1 mole KCl in 1000 cu cm solution). Anodic current densities up to several hundred ma per sq cm were applied for periods between 30 sec and 2 hr. For the purpose of investigating the initial steps of disintegration the anodic current density applied never exceeded 20 ma per sq cm. The films which partially separated from the anodic surfaces under high-field conditions were treated with KOH to further their detachment by dissolving the As2O3 formed. The washed and dried films were pasted to strips of filter paper, and Laue pictures were made. The back-reflection patterns obtained were compared with those of the original anode surface before and after anodic dissolution. Furthermore, space reciprocal lattices7 were constructed from asymmetric rotation crystal patternsa which permitted the determination of the crystallographic orientation of the detached films of the corrugated anodic surfaces. The disintegration products were identified from assymmetric powder patterns.8 The polarity of the {111) faces was determined by chemical etching with mixtures of 1HF:1H2O2(30 pct): 2H2O or 1HNO3:2H2O. Different patterns on each of two inverse (111) sides appeared.&apos;-l8 The correlation of these patterns to the Ga{111) or the As(111) side has already been established by the use of light figures,18-20 by X-ray diffraction near the absorption edges of gallium and arsenic,&apos;lmZ4 and by LEED measurements.25 The geometric structure of these surfaces and the interior of the anodically attacked crystals were observed and photographed with a high-power microscope using oil immersion objectives up to magnification of X1720.

Jan 1, 1968

R. B. BRINSMADE, Ixmiquilpan, Hgo, Mexico* (written discussion). As the discussion of Mr. Graton&apos;s paper by Messrs. Norris, Patterson, and Crane has been from the standpoint of the mineral land-value owners, a few remarks in the interest of the "under dog"-the average taxpayer and citizen-may prove timely. In my discussion of Doctor Raymond&apos;s Paper1 and of the papers of Messrs. Gibson2 and Godson, 3 have endeavored to demonstrate, from both political economy and history, that our existing system of unrestricted private ownership of land is incompatible with equality of economic opportunity and, therefore, subversive of our democratic political institutions. In Mr. Graton&apos;s paper, the same land problem is important, though camouflaged by the failure of the Federal income tax laws to distinguish between land and capital, in the requirements for valuation, or between earned and unearned incomes in the levying of taxes. I disagree with Mr. Graton&apos;s statement, on p. 2967, as follows: The immense majority of mining ventures are failures. A multitude of disappointments is relieved by occasional success. Were it not for the chance of great rewards, all the vitally necessary but mainly unremunerative work of exploration would not be undertaken. In contrast with nearly all other fields of endeavor, it is altogether unlikely that, on the whole, the gains in the successful mining ventures suffice to offset the losses in the unsuccessful.

Jan 3, 1920

By H. J. French

WITHIN the past few years, particularly because of the rapid growth of the airplane industry during the war, considerable attention has been paid to the manufacture of light-wall cold-drawn seamless and welded steel tubing for structural purposes. While the manufacture of such tubing is not, in itself, a difficult matter, some difficulties have. been encountered in producing the same under specifications requiring definite physical properties. It is the purpose of this paper to describe the methods of manufacture and the properties that may be obtained by such methods for tubing coming within about ½ to 2 in. (12.7 to 50.8 mm.) outside diameter and 10 to 22 Birmingham wire gage (0.134 to 0.028 in. wall thickness). Such tubing is largely used as structural material in the aircraft industry, and it is of the utmost importance that the physical and chemical properties should be known, and also that the various factors entering into the manufacture should be under such control as to allow these properties to be varied and held within definite limits. In general, tubing may be divided into four classes: namely, specialty tubing, such as riveted-sheet or plate, lock jointed, etc.; brazed tubing; welded tubing; and seamless tubing. Welded tubing may be divided into hot product, such as lap welded and butt, welded, and cold product, such as acetylene and electric welded. Seamless tubing may be hot rolled or cold drawn.

Jan 9, 1919

By Erland Johnson

BRINE was discovered at Avery Island, La., in 1790, but it was not until 1862 that rock salt was found about 13 ft below surface-the first discovery of rock salt on the continent. Maximum elevation of the island is 152 ft and elevation at the shaft 31 ft. The mining level is 530 ft below elevation at the shaft and the shallowest salt about 12 ft below surface. A shaft was sunk in 1869 when the mining operation started. In 1898 the present shaft was sunk, and the mine has been operated by International Salt Co. ever since.

Jan 6, 1957

By John V. Beall

There is an underlying surge to mining in the Philippines." So said A. R. "Ham" Reed, general manager Itogon-Suyoc Mines, Inc., to this reporter last November. Itogon-Suyoc is a small company with a struggling gold mine, a mixed sulfide mine and some prospects. In the Republic of Philippines (ROP), politics, which have an effect on mining, create some uncertainties. By July 1974, no mining company may have more than 40% foreign ownership. The ownership provision is a matter of concern to such important companies as Atlas and Benguet Consolidated and is generally considered a deterrent to new foreign investment. Under these circumstances, Reed&apos;s comments are of interest. On foreign prospectors: Don&apos;t come in cold; find a Philippine partner or buy into a company already here. Physical conditions of exploration are tough-terrain, communications -but the mineral potential is excellent.

Jan 4, 1969

By Chauncey L. Berrien

The United Verde Copper Company&apos;s mine is at Jerome, Ariz. The orebodies arc of the schist replacement type, the main sulfide mass being a large lens-shaped body approximately 7 acres in cross-sectional area. In general, the mineralization is found along the iron schist contact, with the orebodies extending about 1000 ft. along this contact and varying from a few feet to 250 ft. in width. Three types of ore are mined; schist porphyry and the so-called "heavy" or "massive sulfide" ore. Approximately 50 per cent. of the total tonnage mined at present is of the latter class. A representative analysis of this ore indicates 42 to 46 per cent. sulfur. Because of the high sulfur content, blasting in this ore is an extremely hazardous operation. not only does it endanger the lives of men who may be in the mine at blasting time but it also becomes a potential fire menace when timber is in close proximity to shots being fired in these massive sulfides. The origin of the fires of 38 years ago, embers of which are glowing to this day, may perhaps be attributed to dust explosions due to blasting in the massive sulfides of those early square-set stopes. Dust Explosions Dust explosions in coal mines are a common source of mine disasters. That such explosions may be of common occurrence in metal mines is not generally known, but it is known that metal-mine dust will explode and such explosions have been investigated by the U. S. Bureau of Mines at the Pittsburgh Experiment Station. Samples of "heavy sulfide" ore from the United Verde mine were used in the tests. After studying the results of the tests it was concluded1 that: 1. Dust explosions were initiated in sulfide ore dust in the gallery with a charge of as low as 75 g. of 60 per cent. gelatin dynamite. 2. The exploding dust generated considerable pressure.

Jan 1, 1930

By Donald H. Yardley, A. Aly Selim

Abstract-An economic simulation model was developed to predict the amount of copper recovered from copper oxide deposits, and the cost of producing it as a function of the deposit parameters. The economic simulation model includes programs for fragmentation design and cost, copper extraction, solution distribution and recovery, effluent solution cutoff grade, and financial analysis. Cost and price indices were also developed to evaluate the economic feasibility of in situ leaching operations as a function of their starting date. Application of the models to various hypothetical properties having the same area and different ore thickness shows that the effluent solution cutoff grade does not vary with the ore thickness nor with its grade. The percent of copper recovery is, however, shown to increase with the increase in the ore thickness and is independent of the ore grade. It is also shown that while the profit per unit of extracted copper increases with the increase in ore grade or ore thickness, the rate of return on total investment does not show any correlation.

Jan 1, 1978

By Walter J. Johnson

The coals in northern Wyoming and Montana are free-burning and non-caking and range from lignite to bituminous C in rank. Strip and underground mining are employed to supply railroad, utility, industrial, and domestic fuel. The market area includes Iowa, Nebraska, Minnesota, North and South Dakotas, Wyoming, Montana, the Pacific Northwest, and western Canada. THE larger producing coal mines in northern Wyoming are located in the Powder River Basin lying between the Black Hills region of South Dakota, eastern Wyoming, and the Big Horn Mountains in north central Wyoming, see Fig. 1. The mines are located particularly in the area along the route of the Chicago, Burlington & Quincy Railroad from Gillette, Wyo., to a point approximately 15 miles northeast of Sheridan, Wyo. Fig. 2 is a graph of coal production in the state of Wyoming from 1918 to 1951. Across the Big Horn Mountains lies the Big Horn Basin, situated between the Big Horn Mountains and the Rocky Mountains proper. Mining in the Big Horn Basin is almost entirely confined to a small area known as the Gebo Field, near the town of Kirby, which is located on the Chicago, Burlington & Quincy Railroad. This paper will describe present operating areas, making only brief reference to the history of mining and marketing primarily because of the large area to be discussed. The coal beds presently mined in the Powder River Basin are all of Tertiary age and are of Fort Union and Wasatch formations of Paleocene and Eocene ages, see Fig. 3. The Fort Union formation, consisting of 2000 to 3200 ft of alternate sandstone, shale, and coal, is divided from oldest to youngest into the Tullock, Lebo Shale, and Tongue River members. Most of the mineable coal is in the Tongue River member, which is 500 to 800 ft thick. The Carney coal bed, varying from 7 to 20 ft in thickness, is considered the base of the Tongue River member. About 85 ft above the Carney is the Monarch bed, ranging from 18 to 42 ft in thickness. At approximately 210 ft above the Monarch is what is locally known in the Sheridan district as Dietz No. 3 bed, which varies from 12 to 30 ft in thickness. One hundred feet above the Dietz No. 3 is Dietz No. 2 bed, which is 7 to 12 ft thick. At about 100 ft above the Dietz No. 2 is Dietz No. 1 bed, 7 to 15 feet in thickness. Two hundred and fifteen feet above Dietz No. 1 is the Smith bed, approximately 5 ft thick. One hundred twenty-five feet above the Smith is the Roland bed, which is estimated to be approximately 13 ft thick. The Roland bed is considered the base of the Wasatch formation, which in the Powder River Basin is 1000 to 3500 ft thick and is composed largely of shale, sandstone, and coal. The foregoing measures are the only ones above the Tongue River member that have been mined in the Sheridan field. To the east of the Sheridan field, particularly in the area of Gillette, the Roland bed is considerably thicker and is considered the thickest and most extensive coal bed in Wyoming, reaching a maximum thickness of 106 ft. From 125 to 225 ft above the Roland lies the Arvada bed, average thickness 9 ft. Three hundred seventy-five to four hundred feet above the Arvada is the Felix bed, which reaches its maximum thickness of 30 ft near Echeta on the Chicago, Burlington & Quincy Railroad. East of the Powder River the bed averages more than 10 ft in thickness, but it thins in a northwesterly direction. The highest mineable coal in the Powder River field is the Healy bed, about 400 ft above the Felix bed and exposed only in the highest parts of the area where much of it has been burned along the outcrop. Where it has not been burned, the thickness at most of the outcrops is 10 to 15 ft.

Jan 1, 1954

By O. B. Bucklen, P. G. Meikle

INTRODUCTION The trend in the coal industry for many years has been to make every- thing "bigger and faster." This also held true for loading and storage facilities. Where once a million ton per year mine was rare, three to five million ton per year mines are not uncommon today in the bituminous industry. This greatly increased production, made possible through mechanization, required greatly improved loading facilities just to get the coal away from the mine. Also, there is a trend toward combining production from more than one mine and cleaning it in a single preparation plant. In addition to increased loading capacity, this frequently necessitates raw coal storage and blending facilities. The development of the unit train with its attendant economics, more than any other factor, has contributed to the widespread construction of storage and high-speed loading facilities. In the export market, the construction of ever larger coal colliers has contributed to a need for faster and larger loading facilities. In this climate of rapidly changing technology, any written account is faced with the possibility of obsolescence before its appearance. Thus, this chapter seeks to define the common and current practice in coal loading and storage facilities with the full knowledge that this practice is an ever-moving target. FUNDAMENTALS OF COAL STORAGE Storage of coal is becoming an increasingly important part of coal handling systems at mines, particularly since the advent of the unit train concept in transportation. In order to take advantage of reduced transportation rates on trainload shipments of coal offered by unit train movement, operators have found that storage is an economic necessity. In unit train practice large predetermined quantities must be loaded in relatively short periods of time as opposed to conventional practice where coal is loaded at a speed dependent on the production capacity of the mine and/or the cleaning capacity of the preparation plant. Two surveys of storage practices at mines reveal several objectives for storage.1, 2 Raw and/or clean coal storage is generally practiced in order to accomplish one, or a combination, of the following objectives: 1. To improve plant efficiency by distributing plant feed over the entire operating time, or to allow a preparation rate different from the production rate. 2. To limit interruptions of supply, ie, allow mine and plant to function independently with delays in one not affecting the operation of the other.

Jan 1, 1968

By Robert B. Kistler, Ward C. Smith

The borate industry is one of the few sectors of the mining and mineral-processing industry which the United States still dominates. Since about 1927, the United States has supplied over half of the world&apos;s total boron and borate raw materials, and many of the chemical derivatives as well. Chiefly responsible for this record are companies producing sodium borates from two large deposits in southern California, at Boron (Kramer) and Searles Lake. The sodium borates, or products derived from borax and borax-containing brines, are the preferred borates for industry because they are soluble in water and combine readily with most other chemicals. Calcium borates are required for certain end uses, and these are produced from smaller colemanite-ulexite-probertite bodies. Sodium-free borate compounds also are produced from boric acid, which can be manufactured from either sodium or nonsodium borate minerals. During the past hundred years, the use of boron compounds throughout the world has risen from a few tons per year to the equivalent of over a million tons of B2O3. Leadership in supplying borates shifted from country to country and from region to region during this period, generally as the result of the development of newly discovered deposits that were better in quality, more accessible, or more economically exploitable than previous sources (Table 1). Primary Products and End Uses The principal borate products offered by primary producers in the United States are listed in Table 2. In general, these products are utilized worldwide by almost all consumers, regardless of the original source of the primary borates, In the United States, the primary borates all originate in southern California. Colemanite is produced as crude or processed crude ore from the Death Valley area and is utilized by the fiber glass and ceramic industries without further treatment. Production from Searles Lake, CA is from brines that are processed in chemical plants where borax and other compounds are recovered and the principal borate products are produced. At Boron, CA, the world&apos;s leading producer is mining a deposit of mineral borax and operating a chemical refinery. The mineral borax is mined together with included clay, and refined borax or "10-mol" is one of the refinery products. The mineral and the chemical compound are identical, Na2B4O7 • 10H2O. In addition to ship¬ping all major refined borate products from [ ]

Jan 1, 1983

By R. R. Harvey

Recent evidence has indicated that the films forming at crude oil-water interfaces are the result of naturally occurring su,rface-active components in the crude oil rather than oxidation products resulting from exposure of the oil to air. Since the presence of such films may strongly affect the displacement of oil from porous media, a knowledge of their composition and formatiorz is of fundamental importance. In this study, without the assumption of a specific mechanism, film formation is considered to involve the transfer of a weakly surface-active species in solution in the oil to the oil-water interface. The film gas law and the Gibbs adsorption equation may thus he applied to the system. The rigid films which form upon decrease of the oil-water interfacial area are considered a result of the very slow rate of re-solution of the film material into the oil. When the shrinkage of the interface is very rapid, the amount of film material leaving the interface is negligible, and the system may then be treated in the same manner as an insoluble film. The combination of these treatments leads to a new concept of the film factor in which it may he quantitatively related to the concentration of film-forming material at the interface. Suitable experiments can then yield the following information. 1. Original concentration of surface-active species in the oil. 2. The change of concentration with time. 3. Concentration of surface active species at the interface. 4. The change of this concentration with time. 5. Interfacial tension of the system at any time and its variation with time. 6. Equilibriunz concentrations for a given set of conditions. 7. Concentration requirements for solid film formation. 8. Molecular diameter of the adrorbed species. These calculations may be made solely from data taken from measurements on the original oil. While using the pendant drop method of interfacial tension measurement of crude oil-water systems, Bartell and Niederhauser&apos; remarked on the thin, transparent, pliable, solid films or membranes which were often formed at the interface between crude oil and water. As a result of their observations of these films, Bar-tell and Niederhauser concluded: 1. The films are formed by material from the oil adsorbed at the interface rather than by a reaction at the interface. 2. The adsorption of the film-forming material is a rather slow process. 3. There are good indications that the process is reversible; i.e., the film constituents may re-dissolve into the oil. 4. The film will spontaneously spread over any new surface formed. 5. The process of adsorption at the interface is accompanied by a decrease in the interfacial tension of the system. Although they had proved that film formation was not due to a reaction at the interface, Bartell and Niederhauser were unable to demonstrate conclusively whether these film-forming constituents were present in the original reservoir oil or whether they were formed as oxidation products after exposure of the oil to air. Recent evidence seems to point to their presence in the original oil. Although the true nature of the film-forming constituents is still uncertain, these conditions would be fulfilled by the assumption of the presence of a slightly soluble surface-active component in the original oil. This component would migrate to a freshly formed interface because it would thereby lower the free energy of the system. The component at the surface constitutes an expanded monolayer which would become compressed, upon retraction of drop, due to the slow rate of re-solution of the film components into the bulk of the oil. It is possible, by involved extraction processes, to separate or at least concentrate this film-forming fraction. However, using the assumptions made above, the technique of monolayer film study may be applied to reveal much of the nature of the adsorbing material without resorting to an actual separation of the film-forming constituents.

By H. H. Evinger, M. Muskat

Although the shooting of oil wells for the purpose of increasing production has been practiced since 1866, present-day shooting technique has been arrived at almost wholly by a process of trial and error. The difficulties attending either a theoretical analysis of the problem or an experimental attack become apparent when one actually embarks on a theoretical investigation or attempts to formulate an intelligent experimental program. The literature on the subject consists mainly of descriptions of current practice, scattered eye-witness accounts of events following the shooting of a well, and vague speculations on the mechanical processes involved. In contrast to quarry blasting, the results of oil-well shooting cannot be determined by means of visual inspection, and it is perhaps for this reason that only one attempt at what approaches a direct experimental attack has been reported in the literature.&apos; In these experiments, charges of liquid nitroglycerin were exploded in holes drilled in a sandstone outcrop. In order to observe the character and extent of the resulting fractures, the rock was blasted away so as to expose the original shot holes. After all this had been done it was found impossible to distinguish the fracturing due to the original shots from that due to the subsequent blasting. The enlargement of the holes due to the pulverizing action of the shots was measured and an attempt was made to determine the effectiveness if sand tamping. Only five shots were made and few definite conclusions could be drawn. Some small-scale experiments to deter-mine the effect of tamping were performed by Snelling and IIalL2 Small charges (zo grams) of dynamite were detonated at the bottom of a cylindrical hole in a lead block and the resulting enlargement of the hole was taken as a measure of the effectiveness of the explosion. It was found that when the shot was tamped with a sufficient amount of sand or clay, the volume enlargement was approximately double that found when no stemming had been used. The properties of the explosives have been the subject of much study by the manufacturers, the U. S. Bureau of Mines, and various other agencies. For example, velocities of detonation for many commercial explosives are to be found in the Blasters&apos; Handbook, issued by the Du Pont company. Many other properties are given in a treatise on the subject by Naoum.~ The shock wave that accompanies the detonation of high explosives has been studied photographically by Payman4 and others. The hydrodynamical theory of the shock wave has received much attention, and an extended theoretical treatment is given by Bateman.6 Two aspects of the well-shooting problem will be considered in this paper; namely, the fracturing of subsurface strata, and possible damage to casing. With respect to the former of these, several calculations have been made giving the stresses in the rocks surrounding the shot. In order to arrive at numerical results at all, however, it is necessary to introduce a great many simplifying

Jan 1, 1941

By M. Muskat, H. H. Evinger

Although the shooting of oil wells for the purpose of increasing production has been practiced since 1866, present-day shooting technique has been arrived at almost wholly by a process of trial and error. The difficulties attending either a theoretical analysis of the problem or an experimental attack become apparent when one actually embarks on a theoretical investigation or attempts to formulate an intelligent experimental program. The literature on the subject consists mainly of descriptions of current practice, scattered eye-witness accounts of events following the shooting of a well, and vague speculations on the mechanical processes involved. In contrast to quarry blasting, the results of oil-well shooting cannot be determined by means of visual inspection, and it is perhaps for this reason that only one attempt at what approaches a direct experimental attack has been reported in the literature.&apos; In these experiments, charges of liquid nitroglycerin were exploded in holes drilled in a sandstone outcrop. In order to observe the character and extent of the resulting fractures, the rock was blasted away so as to expose the original shot holes. After all this had been done it was found impossible to distinguish the fracturing due to the original shots from that due to the subsequent blasting. The enlargement of the holes due to the pulverizing action of the shots was measured and an attempt was made to determine the effectiveness if sand tamping. Only five shots were made and few definite conclusions could be drawn. Some small-scale experiments to deter-mine the effect of tamping were performed by Snelling and IIalL2 Small charges (zo grams) of dynamite were detonated at the bottom of a cylindrical hole in a lead block and the resulting enlargement of the hole was taken as a measure of the effectiveness of the explosion. It was found that when the shot was tamped with a sufficient amount of sand or clay, the volume enlargement was approximately double that found when no stemming had been used. The properties of the explosives have been the subject of much study by the manufacturers, the U. S. Bureau of Mines, and various other agencies. For example, velocities of detonation for many commercial explosives are to be found in the Blasters&apos; Handbook, issued by the Du Pont company. Many other properties are given in a treatise on the subject by Naoum.~ The shock wave that accompanies the detonation of high explosives has been studied photographically by Payman4 and others. The hydrodynamical theory of the shock wave has received much attention, and an extended theoretical treatment is given by Bateman.6 Two aspects of the well-shooting problem will be considered in this paper; namely, the fracturing of subsurface strata, and possible damage to casing. With respect to the former of these, several calculations have been made giving the stresses in the rocks surrounding the shot. In order to arrive at numerical results at all, however, it is necessary to introduce a great many simplifying

Jan 1, 1941

By Hermann Bach, Walther Hänig, Willi Gehrhardt, Ernst Theurich, Walter Langner

With the construction of the Magdeburg zinc works, the Georg von Giesche&apos;s Erben Mining Co. of Breslau has to a certain extent completed the program of reconstruction which it set as its goal after the boundaries of Upper Silesia were drawn by the Treaty of Versailles. During its history, covering.more than two centuries, zinc and lead mining has been its chief activity. Through the new boundaries established, it lost to Poland all its mines and smelters, including five distillation smelters. Of its extensive properties, there remained only an apparently unimportant and unexplored portion of the old Bleischarley ore field which, however, happily made possible the resumption of its old business. In 1925 the Deutsch-Bleischarley shaft-only a few kilometers from the old Bleischarley shaft—was sunk and developed, and in May 1926 production of lead and zinc ore was resumed. As facilities for smelting were lacking, the ore was at first delivered to the neighboring smelters, which had now become Polish. Realization of the plan to build its own zinc works had to be postponed at first for lack of capital. In the meantime, however, plans for the new works were worked out in all details. After extensive experimentation in a semicommercial pilot plant it was decided, at the end of 1928 and the beginning of 1929, to use the electrolytic process and, for economic reasons, to place the works at Magdeburg. With zinc at the approximate price level that had ruled since the Deutsch-Bleischarley mine had begun working, it was hoped that the plan could be completed in 1930 with the company&apos;s own resources. However, falling metal prices, already noticeable in 1929, made this impossible, and further postponement for a time became necessary. Finally, at the end of July 1933, the funds for building the works became available, in the form of a loan granted under the first employment

Jan 1, 1937

By Zay Jeffries

It has been known for centuries that iron and steel could be hardened by cold hammering and that the metal could be restored to the normal condition by heating to a red heat arid cooling, either rapidly or slowly with nearly pure iron, but slowly with steels containing considerable carbon. The art of tempering steels is also very old. When a medium- or high-carbon steel is quenched from a cherry-red heat, the hardness is increased; this hardness can be reduced by heating to various temperatures below the lower thermal critical point,, which is near 700" C. The present paper will not consider these old and well known changes in iron and steel below the thermal critical range but will confine itself to the more unusual changes, some of which have been studied recently. Stromeyer,1 for example, In 1886, reports that both working steel and heat treatment of steel in the blue-heat range arc highly injurious. Recently, however, some metallurgists believe that the straiglltening of warped steel forgings at a blue heat produces a beneficial effect on the metal2 The Engineering Division of the National Research Council has constituted a committee on Physical Changes in Iron and Steel below the Thermal Critical Range, which has the following personnel: K. R. -Abbott, H. C. Boynton, William Campbell, J. V. Emmons, F. B. Foley, H. J. French, H. M. Howe, Zay Jeffries (chairman), F. C. Langenberg, J. A. Mathews, P. D. Merica, A. H. Miller, J. H. Nelson, G. A. Reinhardt, W. E. Ruder, H. F. Wood. This committee is studying several aspects of the physical changes in iron and steel. The results, reported in the literature and obtained by recent experimentation, will be given; this will be followed by a general theoretical discussion of the more important

Jan 1, 1922

By Zay Jeffries

It has been known for centuries that iron and steel could be hardened by cold hammering and that the metal could be restored to the normal condition by heating to a red heat arid cooling, either rapidly or slowly with nearly pure iron, but slowly with steels containing considerable carbon. The art of tempering steels is also very old. When a medium- or high-carbon steel is quenched from a cherry-red heat, the hardness is increased; this hardness can be reduced by heating to various temperatures below the lower thermal critical point,, which is near 700" C. The present paper will not consider these old and well known changes in iron and steel below the thermal critical range but will confine itself to the more unusual changes, some of which have been studied recently. Stromeyer,1 for example, In 1886, reports that both working steel and heat treatment of steel in the blue-heat range arc highly injurious. Recently, however, some metallurgists believe that the straiglltening of warped steel forgings at a blue heat produces a beneficial effect on the metal2 The Engineering Division of the National Research Council has constituted a committee on Physical Changes in Iron and Steel below the Thermal Critical Range, which has the following personnel: K. R. -Abbott, H. C. Boynton, William Campbell, J. V. Emmons, F. B. Foley, H. J. French, H. M. Howe, Zay Jeffries (chairman), F. C. Langenberg, J. A. Mathews, P. D. Merica, A. H. Miller, J. H. Nelson, G. A. Reinhardt, W. E. Ruder, H. F. Wood. This committee is studying several aspects of the physical changes in iron and steel. The results, reported in the literature and obtained by recent experimentation, will be given; this will be followed by a general theoretical discussion of the more important

Jan 1, 1922