Search Documents

By Liangying Wen, Feng Xia, Chenguang Bai

"The situation of the Ti-V-Magnetite samples reduced with microwave has been investigated in laboratory. Firstly, the paper focuses on the heating behaviors of vanadium-titanium magnetite and characteristics of carbothermic reduction of V-Ti-magnetite in the microwave field. The effect of concentrate's size, quality on heating behaviors and reduction processes were researched. Results show that microwave heating may be a new heating resource replace of carbonic combustion reaction in reducing reaction. When the allocation of carbon is (16.7-30)%, carbothermic reduction of V-Ti-magnetite in the microwave field can proceed; with the increasing of carbon mixed, the metallization rate increases; and Fe, V can be reduced from their oxides in the microwave field; Titanic low oxide can be reduced from TiO2.1. IntroductionThe resource of Ti-V-Magnetite is abundant in the western area of Panzhihua in China, so far a mineral deposit of 4.64 billion tons have been proved up, it contains 14.75 million tons of V2O S which accounted for 87% of the vanadium and 5.93 hundred million tons of TiO2 accounted for 94% of the titanium resource respectively in China. The previous study proved that the major composition of mineral of the Ti-V-magnetite are Ti-magnetite, limonite, iron spinel, magnesium spinel etc, and the main elements of the Ti-V-magnetite in this area are Fe, Ti, V, Cr, Co, Ni, Ga, Sc etc[1] Due to the restrict of the BF-BOF process technical, during the smelting of the iron, the level of extracting the vanadium, titanium as well as other metal elements is limited. This results serious wasting of resources. To develop a new reduction process of Ti-V-magnetite is on the agenda, the microwave assistant reduction could meets this need, based on its characteristic of easy controlling of heating rate. To make use of the microwave energy to substitute the released heat sources of carbon combustion with air, use the solid phase state reduction at a relative lower temperature, make the beneficial element in Ti-V-magnetite transferred into the metal phase, then separated from the impurity. It is well worth to point out that once the microwave based reduction method has its industrial scale, it will take an outstanding position by its less release of carbon dioxide. This new environment-friendly process will play a vital role in the development of social industry and economy."

Jan 1, 2008

By E. vanHuyssteen

A method of establishing the relationship between the mineralogy of a sinter and its subsequent processing behaviour in a lead blast furnace is demonstrated. It involves: 1) analyzing the Zn-spinels, hardystonite, larsenite, Pb-silicates, Pb-arsenates, Pb-(Ca)-sulphates and other femtes with an electron microprobe; 2) determining the extent of elemental substitutions in various mineral structures; 3) establishing a sequence in which the various phases formed during sintering. In this manner the relationship between the bulk chemistry of a sinter formulation and the speciation of elements into various phases in the sinter can be established. Specifically, the-substitution of Mg for Zn in hardystonite significantly influences sinter production. Mg substitution releases Zn into the surrounding matrix. This Zn reacts with the Pb-silicate to form larsenite thereby reducing the amount of Pb-silicate available for anhydrite digestion. Excessive amounts of residual anhydrite thus result if the sinter formulation is based solely on the CaO/Si& ratio.

Jan 1, 1993

By Shulan Wang, Xuan Liu, Li Li

"Electrochemistry of Fe(III) in 69CaCl2-12CaF2-19KF and 81CaCl2-19KF (mole percentage, %) was investigated at 827 oC on molybdenum electrode by cyclic voltammetry, chronoamperometry and galvanostatic electrolysis using Fe2O3 as the Fe(III) source. The reduction of Fe(III) to Fe was conducted in one step and controlled by diffusion process. Fe(III) shown greater reduction rate and diffusion coefficient in molten 81CaCl2-19KF than in 69CaCl2- 12CaF2-19KF. Galvanostic electrolysis of Fe was performed in both molten salts with a cylindrical cathode rotating at 200 r/min and dendritic iron deposit was obtained.Keywords: iron; electrolysis; electrochemistry; molten saltIntroductionThe production of iron and steel causes huge emissions of CO2. Iron electrowinning in molten salts with dissolved Fe2O3 using an inert oxygen evolving anode is an alternative process to reduce or eliminate the formation of CO2. Research on novel process of producing metal has been reported recently [1-2] by using CaCl2 as the main electrolyte and dissolving CaO in CaCl2 due to the high solubility of CaO in the melt. This process has been used in preparing many active metals and alloys [3-14]. In the present work, the electrochemical behavior of iron in CaCl2-KF was studied and transport property of iron ion in the melt was discussed.ExperimentalCaCl2,CaF2 and KF (in analytical purity) were dried in air for 48 h. Mixed salts used in experiments were placed in a graphite crucible (??58 mm inner diameter). The graphite crucible together with the salts was heated at 473 K for 12 h in a furnace with flowing Ar (99.99%) before further heating. Temperature inside the furnace was measured by an S type thermocouple. Electrochemical measurements, such as cyclic voltammetry and chronocoulometry, were performed in a three electrode cell by EG&G PAR273A potentiostat/galvanostatand. Galvanostatic electrodepositon of iron was conducted in a two electrode cell. Molybdenum (??2 mm) and iron (??5 mm) were used as the working electrode (WE) and the reference electrode, respectively. A graphite crucible and a magnetite rod (??25 mm ) consisted of 100% magnetite and sintered at 950 oC in argon atmosphere for 2 h with electrical conductivity of 366 O-1m-1 at room temperature were used as the counter electrodes in the galvanostatic electrolysis experiment. Carbon (??10 mm) was used as the counter electrode in electrochemical measurement. The deposits were washed in distilled water bubbled with argon and dried in air before being characterized by X-ray diffraction (PW3040/60 diffractometer) and scanning electron microscope (SEM, SSX-550)."

Jan 1, 2014

By Shu Bin, Lin Chen, Tian-zu Yang, Wei-feng Liu, Wan-da Bin

"Antimony resources are rich in china, its reserves and productions are ranking the first in the world. The Chinese antimony mineral resources are mainly existed in the form of three types, such as stibnite, antimony-gold ores andjamesonite. The antimonial dust that produced from lead smelting process is an important secondary antimony resource. The different process that was adopted to extract antimony depends on the different raw materials. The process of blast furnace volatilization smelting is mainly used to treat stibnite and antimony-gold ores. But jamesonite is treated by the process of roasting-sintering-blast furnace smelting. And antimonial dust is treated in the reverberatory furnace. Many new technologies that are applied in these traditional antimony smelting processes play important roles, such as deleading agent, antimony white production, air-oxidation method, direct-blowing method, bath smelting technology, and so on. At the same time, the development of antimony smelting technology in china is prospected according to the requirement of the state environmental protection.IntroductionThere are five countries that produce antimony in the world, such as china, Tajikistan, Bolivia, Russia, and South africa, but China is the largest country of antimony production in the world. In the world, the antimony productions of 2008, 2009, and 2010 are 182,000 tons, 154,000 tons, and 167.000 tons respectively, but Chinese antimony productions are 166.000 tons, 140,000 tons, and 150,000 tons respectively. So Chinese antimony production was accounted for more than 89% of the world in 2010. It indicates that China have irreplaceable advantages in antimony resource and production all over the world."

Jan 1, 2013

By T. Sakaguehi

Some attempts were made to recover and remove of uranium that may be present in refining effluents, mine waste Water, and other waste sources by using microbial biomass. To establish which microorganisms accumulate the most uranium, 135 species of microorganisms (42 bacteria, 26 yeasts, 34 fungi and 33 actinomycetes) were screened. Of these 135 species of microorganisms tested, extremely high uranium absorbing ability was found in Pseudomonas stuzeri, Neurospora sitophila, Streptomyces albus and Streptomvces viridochromogenes. In addition to the research on uranium uptake, thorium recovery by using microorganisms was investigated. High abilities were found in Streptomyces levoris and Bacillus subtilis. The selective accumulation of heavy metal ions by various microorganisms has also been examined. Uranyl, mercury and lead ions were readily accumulated by almost all of the species of microorganisms tested. Actinomycetes and fungi differ from many bacteria and most yeasts in their selective accumulation of uranium, and mercury. The basic features of uranium uptake by Streptomyces viridochromogenes, a microorganisms with high uranium-uptake ability, were investigated systematically. Synthesizing these results, we suggested that the accumulation of uranium into these microbial cells is not directly mediated by any metabolic process:, but almost completely dependent upon physicochemical adsorption on the cell components. In addition to this fundamental research, uranium recovery was investigated in immobilized Streptomyces viridochromogenes. These immobilized cells adsorbed, uranium readily and selectively. The immobilized cells recovered uranium almost quantitatively and almost all uranium adsorbed was desorbed with 0.1 N Na2CO3, These results showed that microbial cells are more stable after Immobilization and can be used repeatedly for the process of uranium adsorption-desorption. These results suggested that these microbial cells can be used for the recovery and removal of nuclear fuel elements, such as uranium and thorium, from refining effluents and mine waste water.

Jan 1, 1991

By A. McLean, Y. Uchida, M. Iwase, M. Myochin, K. Wiikimoto

"Phase diagrams of FeO-containing ternary systems could be derived from experimental data for the activities of FeO. The systems investigated are CaO-CaF2-FeO, SrO-SrF2-FeO; BaO-BaF2-FeO, CaO-CaCl2-FeO, SrO-SrC12-FeO, BaO-BaC12-FeO, CaO-A12O3-FeO and BaO-SiO2-FeO.IntroductionThe importance of phase diagram cannot be overemphasized. In a book, ""Alloy Phase Equilibria""[l], the author, Professor A Prince, states, ""A metallurgist has been defined as a person who thinks in terms of phase diagram"". Whether one accepts this statement or not, it is self-evident that an ability to interpret phase equilibria is essential to the professional metallurgists.The physical chemistry studies of iron and steelmaking process often require phase diagrams of FeO-containing slags. Iso-thermal section of the phase· diagrams of such systems can be derived from experimental data for chemical potentials of FeO. Due to the recent developments in the area of solid state electrochemistry, rapid determinations of the FeO activities have become possible. The present paper is aimed at documenting the derivation of the phase diagrams of FeO containing slags.Experimental AspectsAn electrochemical method incorporating stabilized zirconia can be used for the measurements of the activities of FeO in various slags and fluxes[2]. For the details of the experimental technique, reference should be made to reference 2"

Jan 1, 2000

By K. Robinson

Following the longest Smelter campaign in BCL?s history it was planned to completely rebuild the flash smelting furnace in 1987. This was the fourth major overhaul and the most extensive so far attempted. Detailed planning took place over several year$ preceding the shutdown and implementation was completed in 54 days. The key to minimising shutdown time was the method designed for installation of the new uptake shaft and reaction shaft. Major repair work was also undertaken in the waste heat boiler and electric furnaces. Both of these activities had an impact on the critical path of the flash smelting furnace overhaul.

Jan 1, 1993

By Djona M. Gaballah I.

Selective chlorination of unroasted and roasted spent hydrorefming catalysts was studied between 300 and 600°C using the following gas mixtures : C12+CO, C12+N2 and CI2+air. Such materials contain Co, Ni and Mo compounds supported by alumina and/ or silica. They also contain variable amounts of V compounds, C, S, etc., accumulated during the life time of the catalyst. Direct oxychlorination of the C+S rich sample allows higher extraction rates than those obtained by the carbochlorination of the same roasted one. It seems that the roasting step doesn't favor the economic metals' recovery. Results of the chlorination of C+S poor spent catalysts, in the presence of CO, in the chlorinating gas mixture, or of carbon added to the sample, were comparable. Cobalt and nickel chlorides were .extracted from the chlorination residues by their dissolution with acidified water, whereas molybdenum and vanadium chlorinated compounds were recovered by selective condensation from the vapor phase. The recovery rates of valuable metals as well as the selectivity were higher for the chlorination of spent catalysts than results obtained by the hydrometallurgical processing of the same sample. Results of the scale-up of the oxychlorination of the unroasted sample confirmed those of the laboratory scale. The global recovery rates were about 88 pct of cobalt, 93 pct of molybdenum and 76 pct of vanadium. The carbochlorination was applied to the recovery of W and Ti from Denox catalyst that is a carbon and sulfur free one. Recovery rates higher than 99 pct at temperatures lower than 500 °C could be obtained. This may indicate that the chlorination process can be applied to the treatment of various industrial wastes or by-product containing transition and/or refractory metal compounds A flow - sheet for the pretreatment of these materials is proposed.

Jan 1, 1995

By Lin Li, Wen Shi, Hua Wang

"Specimens of the ultra-low carbon bake hardening steel were soaked for 1 min to 5 min, and then cooled by water quenching. The internal friction experiments were carried out to detect the spectra of the specimens. Results show that Snoek peaks are present in all the specimens, however, an obvious Snoek-Koster peak is found only in the 5 min-annealed specimen. Besides, tensile results indicate that the bake hardening values increase with the annealing time prolonging from 1 min to 3 min, but decrease as the annealing time prolongs further to 5 min. The solute distributions in the specimens were characterized by three dimensional atom probe. Some segregated C and V are found in the 1 min-annealed specimen, and the C and V contents decrease as annealing time prolongs to 5 min.1. IntroductionAs an excellent member of automotive body panel materials, various types of bake hardening (BH) steels have been developed since 1980s. Bake hardening property, as one of the most important mechanical properties, has been studied by many researchers [ 1-5]. As is known, BH phenomenon is generally controlled by the interaction between solute C and dislocations. The Snoek peak of internal friction (IF) is very popular in the investigation of solute C [6-9]. However, result of internal friction cannot suggest the distribution pattern of solute C as well as its influence on BH phenomenon.Three dimensional atom probe (3DAP) can diagnose solute element atoms as well as nano-sized precipitates, and it is the only instrument that currently can identify the identities of individual atoms in a material and measure their spatial coordinates with the resolution close to 0.3 nm [10]. There have been a number of studies about using 3DAP to detect solute elements as well as nanometer sized precipitates [11-19]. For example, Hono et al. [16] used 3DAP to determine the solute elements in an age-hardened Mg-Ca-Zn alloy, and they also obtained the distribution patterns of the observed elements."

Jan 1, 2011

By M. Girgis

The behavior of arsenic III during electrolytic refining of copper in acidic copper ?sulphate electrolytes was studied by different electrochemical methods such as, linear potential sweep, cyclic voltammetry, chronoamperometry and chronopotentiometry. The study showed that arsenic behaves as a depolarizing ion and has a deleterious effect on copper deposit. Three substrates; Pb, Cu and Ag were used during the refining process and the electrode kinetics were found similar for both Cu and Pb electrodes while a little difference was found for the Ag electrode. A microscopic study by scanning electron microscope was undertaken to show the influence of arsenic on deposit's morphology. Surface analyses of the deposit were carried out by some electronspectroscopic techniques such as Auger electron spectroscopy (AES) and X-ray photoelectron spectroscopy (XPS). The results showed that arsenic coexists with copper deposit at potential?~ -0.25 V.

Jan 1, 1987

By Shaohua Ju, Feng Jiang, Chuanhua Li, Jinhui Peng, Libo Zhang

A T-junction microchannel is proposed to overcome the existing problems in conventional solvent extraction of indium from zinc hydrometallurgical process. Experiments were performed to separate In3+, Fe3+ and Zn2+ from sulfate solutions using Di-(2-ethylhexyl)phosphoric acid (D2EHPA) as the extractant. The effect of parameters such as pH, microchannel size and contact time on the extraction behavior of In3+, Fe3+ and Zn2+ was investigated. At contact time of 2.52 s and initial solution pH of 0.48, the extraction efficiency of In3+, Fe3+ and Zn2+ was 99.13%, 8.31% and 2.45%, respectively and separation factor of In3+/Fe3+ and In3+/Zn2+ were almost 1229.54 and 4864.98, respectively. Then, the loaded organic phase was stripped in T-junction microchannel. At contact time of 33.6 s, 99.64% of stripping efficiency of In3+ and stripping equilibrium were reached, while concentration of Fe3+ and Zn2+ was lower than 0.01 g/L with good separation of In3+ from Fe3+ and Zn2+.

Jan 1, 2016

By Stephen W. Paff

The EPA has estimated that there are over 3,000 sites across the United States contaminated with lead. Techniques to remediate these sites include standard stabilization/disposal technologies, reclamation of lead using secondary lead smelters, soil washing, and biological removal technologies. In this paper, the current technologies used for lead remediation will be reviewed. Factors affecting the use of each technology, such as range of applicable concentrations, soil types, interferences from other contaminants, economics, and current technology status will be assessed. The paper will also focus on the results of a recent study completed by the Center for Hazardous Materials Research (CHMR), in conjunction with a major lead smelter, which demonstrates that secondary lead smelters may be used economically to reclaim lead from a wide range of lead-containing materials frequently found at Superfund sites. Such materials include battery case materials, lead dross, and debris containing between 3 and 70% lead. The results of development work completed by CHMR on the Acid Extraction Treatment System (AETS), which has been demonstrated to extract Lead from soils containing up to 30,000 mg/kg lead, will also be presented. The use of these technologies will be compared with other options for the remediation of sites.

Jan 1, 1994

By Kafui Nyavor

The indirect, and the direct contact mechanisms of bacteria oxidation of sulfides were studied using Thiobacillus ferrooxidans and pyrite. The aim was to determine which of the two generally aeeepted mechanisms played a dominant role, if any, during acid mine drainage (AMD) formation from the oxidation of sulfide minerals. The results show that at a pH of 4.5 where T. ferrooxidans are quite active, but where initial chemical oxidation of pyrite to Fe2+ is limited, the bacteria were unable to directly oxidize pyrite to any significant extent. Whereas, in the presence of Fe2+, T. ferrooxidallS assisted oxidation of pyrite by the indirect mechanism was observed and sustained over the pH and Eb range where the bacteria is active. The results lead to the conclusion that the direct contactmechanism of pyrite oxidition by T. ferrooxidans is insignificant. The predominant, and possibly the only, pathway involves the indirect bacteria oxidation of available Fe2+ to Fe3+, which in turn oxidizes FeS2 to generate additional Fe2+ and acidity in a cyclic process.

Jan 1, 1996

By P. Henry

A novel electrochemical cell has been developed for the recovery of MnO2 from residue of pyrolusite ore leading loaded with Fe, Al Ni, Co and Si impurities, This new process can be considered as an alternative to the traditional methods : S02, H2O2 or bioleaching. It has been observed to proceed fairly rapidly and could prove to be a more economically viable process, as well as being more environmentally acceptable. Electrochemical characterization and kinetic studies have shown that MnO2 is effectively leached by electrogenerated ferrous ions at high current density from a pulp containing less than 5 g8 Fe. The chemical reactions are : Cathode (inox) : 2F23+ + 2e ? 2 Fe2+ Bulk: MnO2 + 2 fe2+ 4H+ ? Mn2+ + 2 Fe3+ + 2 H2O Anode (Pb-Ag) : H2O ? ½ O2 + 2H+ + 2e Global: MnO2 +2H+ Fe2+ = Mn2+ + H2O + 1/2 O2 The catholyte (MnO2 pulp) circulates upward in the expanded mesh cathode separated from the sulfuric acid solution anolyte by a separator which shows high mechanical resistance, low porosity, low potential drop, and reasonable cost. Laboratory and mini-pilot tests have led to the construction of an OT crating pilot plant (100 kg/hr) able to leach more than 95% of Mn, Ni, Co at 1000-1200 A/m2, 50°C with high faradic yield (> 95 %) and low power consumption (3.2 kWh/kg kWh/kg &4D). New applications like the treatment of spent Zn-Mn batteries, polluted soils, spent catalysts and oxide ore (cobalt, nickel) with electrogenerated redox species are now investigated at a laboratory and mini-pilot scale.

Jan 1, 2000

By Toshio Suzuki, Machiko Ode, Won Tae Kim, Seong Gyoon Kim

"The Ostwald ripening and growth and coarsening of the secondary dendrite arm are studied using a phase-field model. The phase-field parameters are obtained at a thin interface limit proposed by Kim et al. In Ostwald ripening analysis, the difference of the concentration due ·to· the curvature effect is shown. The third power of the average particle radius Rav is proportional to time and the ripening constant shows a good agreement with the value by Deppers et al. The particle radii distribution shows the transition behavior to attain a self-similar stationary shape. The growth and coarsening behavior of the secondary dendrite arm is also analyzed using a phase-field model. The estimated arm spacing and its dependence on time are in good agreements with experimental data.IntroductionThe ripening or coarsening process controls the microstructure during the late stage of solidification. The ripening phenomena are recognized firstly by the Ostwald [1]. The first quantitative analysis for the Ostwald ripening in the limit of vanishing solid fraction was provided by Lifshitz, Slyozov and Wagner (LSW) [2,3]. In their study, that the mean radius grows proportional to the cubic root of time and the size distribution of precipitations shows a ""self-similar"" shape are shown. Most of the studies for the Ostwald ripening confirm or predict these two general rules above. In case of finite solid fraction, the general rules are observed but the ripening constant is larger and the self-similar shape is wider than the LSW prediction respectively [4-6]. To analyze· the high solid fraction system, the theories that consider the solute field correlation are proposed [4,7-8]. In the theory, however, since the particle is treated as the point, the effect of the concentration field deviation from the monopole field should be taken into account. Recently the numerical simulation, in which not only diffusive transportation of solute but also convection effect is considered, has been done using a phase-field model [9]."

Jan 1, 2000

By Miguel Barron

Recently, a new lance design for BOF steelmaking has been proposed in the literature. This lance, in addition to six peripheral inclined supersonic nozzles, contains a vertical centered nozzle whose oxygen flow is independent from the main oxygen supply. The above authors affirm that their lance maximizes the droplet generation without causing spitting. In this work, the performance of a lance with four peripheral nozzles and one vertical centered nozzle is numerically modeled by means of Computational Fluid Dynamics software. Transient two dimensional computer simulations were carried out considering two phases, namely molten steel and gaseous oxygen. Numerical results confirm that bath agitation and droplet generation are enhanced as a result of the vertical centered nozzle, however a proper performance of this lance, related to a conventional one, strongly depends on the Mach number of the oxygen jets and the lance height.

Jan 1, 2008

By Toshiki Kabutomori

In fuel cell powered automobiles, hydrogen is required to be stored in materials that have a hydrogen storage density of over 4 mass%; further, these materials should be capable of supplying hydrogen by using the waste heat from a fuel cell, which is at a temperature of 373 K, in order to match the mileage of gasoline-powered vehicles. A Ti-Cr-V alloy, which exhibits a BCC structure and forms a solid solution, is a promising candidate for onboard hydrogen storage materials. Although it has a large hydrogen storage capacity of over 3.9 mass%, the rechargeable hydrogen capacity is limited to approximately 2.6 mass%. In this study, the effects of fine pulverization of the alloy on PCT (hydrogen pressure-composition-isotherm) characteristics were investigated in order to improve the rechargeable hydrogen storage capacity of the alloy. From the PCT measurements of the finely pulverized samples of the alloy, a plateau in the absorption curve was observed to begin at a hydrogen concentration of 0.5 mass%; further, a rechargeable hydrogen storage capacity of 3.3 mass% was obtained. This was greater than that obtained from the sample that was not finely pulverized, i.e., 2.5 mass%. However, the plateau width in the desorption curve was 2.5 mass%, which was the same as that observed for the sample that was not finely pulverized. The increase in the rechargeable hydrogen capacity during absorption is attributed to the precipitation of the -hydride phase (MH~2) directly from the metal phase (phase). The precipitation of the phase (MH~0.5), which should be formed in low hydrogen concentrations, is suppressed as a result of a possible reduction in the internal defects such as dislocations, vacancies, and grain boundaries by fine pulverization and annealing of the alloy.

Jan 1, 2006

By Xiao-hui Fan, Li-shun Yuan, Xu-ling Chen, Wei Lv, Min Gan, Yi Wang

"As the amount of ferrous scrap increases every year, it becomes more and more urgent to deal with this iron-bearing resource properly. This paper puts forward a method on resource-oriented utilization of ferrous scrap (cold-bonded pelletizing), and these cold-bonded pellets can be used as coolant in a converter. The influence on the pellets qualities by using different kinds of chloride as rust agents is studied, and results show that the strength of cold-bonded pellets increases significantly by using a combination of the three kinds of chloride -NaCl,MgClz,FeCh, their best dosages are 1.2%, 0.2%, 0.1% respectively. Other iron-bearing materials also have an effect upon the pellets strength, by adding 5% iron powder and maintaining for 48h, the compressive strength of the clumps surpass 2500N/A, dropping strength surpass 4 times/ A, and 10% iron slag or 20% steel slag can replace 5% iron powder while obtaining the comparative quality. The influence of different ratios of three ferrous scrap (converter mud, iron scale and dust) is further studied, and results show that when the ratio is 30% : 30% : 40%, the pellet strength reaches the maximum. After maintaining for 24~48h, the clumps can meet the mechanical as well as the physical-chemical requirements as BOF steelmaking refrigerant.IntroductionGreat amounts of converter mud, dust and iron scale are produced in steel production process. These materials are of great values, and their accumulation not only leads to environmental pollution, but also wastes the precious resources, which restricts the sustainable development of the steel industry [1,2] The main approach at present to dealing with the ferrous scrap is to add them into sintering. But in this way, the utilization factor of sintering and the quality of sinter decline while the energy consumption increases [3].Therefore, more advanced and efficient technology is needed to make the best of these iron resources. Cold consolidation of ferrous scrap is a simple process that has many advantages such as less investment, quicker effect, lower energy and lower cost [4-5] But the conventional maintaining period is too long, usually up to four-six weeks, and the pellet strength is low. Therefore, the key points of the cold-bonded pelletizing are to develop a new adhesive [4,5] to shorten the natural maintenance cycle and to improve the strength of the pellets. A method on resource-oriented utilization of ferrous scrap (cold-bonded pelletizing) is brought forward, and these cold-bonded pellets can be used as coolant in converter. After maintaining for 48h, these cold-bonded pellets can satisfy the mechanical requirements to replace the converter coolant [6]."

Jan 1, 2013

By T. J. White

Each year, thousands of tons of toxic concentrates are produced as the unwanted byproducts of industrial operations and smelting activities. The fate of these materials remains open, as in general their consumption is limited and potential markets contracting. Xtaltite (pronounced crystal-tight) is a Synthetic Mineral Immobilization Technology (SMITE) optimized for the concentration, detoxification and consolidation of toxic metal wastes. In this approach, we seek to mimic nature to produce durable synthetic minerals that survive for aeons in well characterized geological settings. This approach has high public acceptability because the concept is easily understood by the layperson and the long term stability of the waste form may be predicted with confidence. In addition, where Xtaltite is used for mine backfill, a system of ecologically sustainable mining development is established. This paper details the design and fabrication of Xtaltite under oxidizing and reducing conditions. To illustrate and contrast these stabilization regimes, specific reference will be made to the treatment of thallium, chrom~um and arsenic wastes. Waste form performance under TCLP, dynamic boiling water tests and in other leaching media will be compared and discussed with respect to their relevance to different disposal options.

Jan 1, 1995

By Yichi Lu, Haydn N. G. Wadley, Douglas T. Queheillalt

"Using a 3-D ray tracing methodology combined with laser ultrasonically measured elastic constant data near the melting point, ultrasonic propagation in cylindrical single crystal bodies containing either a convex or a concave solid-liquid interface have been simulated and used to design new sensing concepts. Ray paths, wavefronts and time-of-flight (TOF) of rays that travel from a source to an arbitrarily positioned receiver have been calculated. Experimentally measured TOF data have been collected using laser generated/detected ultrasound on model systems with independently known interface shapes. Both numerically simulated data and experimental results have shown that the solidification (interfacial) region can be identified from ultrasonic transmission TOF data. Since convex and concave solid-liquid interfaces result in distinctively different TOF data. When TOF data collected in the diametral plane are used in a nonlinear least squares algorithm, the interface curvature has been successfully reconstructed and ultrasonic velocities of both the solid and liquid obtained. The reconstruction errors were found to be less than 5%.IntroductionMany of today's single crystal semiconductors are grown by variants of a vertical Bridgman technique in which a cylindrical ampoule of a molten semiconductor is translated through a thermal gradient, resulting in directional solidification and the growth of a single crystal, Fig. 1.1 It has long been recognized that during crystal growth the velocity and the shape of the solid-liquid interface, together with the local temperature gradient, control the mechanism of solidification (i.e. planar, cellular or dendritic), the likelihood of secondary grain nucleation/ twin formation (i.e. the loss of single crystallinity), solute (dopant) segregation, dislocation generation, etc. They thus determine the crystals' resulting quality.2-4 The solidification rate and the solid-liquid interface shape are also sensitive functions of the internal temperature gradient (both axial and radial) during solidification.5•6 This in turn is governed by the heat flux distribution incident upon the ampoule, the latent heat release at the interface, and heat transport (by a combination of conduction, buoyancy and surface tension driven convection, and radiation) within the ampoule. The solid-liquid interface's instantaneous position, velocity and shape during crystal growth are therefore difficult to predict and uncontrolled during growth, especially for those semiconductor materials with low thermal conductivity (e.g. CdTe).4-6 The development of technologies to non-invasively sense the interface position and shape throughout the vertical Bridgman crystal growth process has therefore become a key step toward developing a better understanding of the growth process, for enabling sensor-based process control, and thus ultimately for improving the yield and quality of difficult to grow semiconductor materials like CdTe."

Jan 1, 1997