By J. M. Ohm, Carl M. Bunker

Two special tools for recovering gamma-ray probes and logging cable from drillholes have been designed by Ohm and Bunker and constructed by Ohm. Though intended specifically for U. S. Geological Survey equipment, they may be used with other equipment of the same general type. Fishing Tool for Probes: A fishing tool of the overshot type (Fig. 1) was designed to retrieve logging probes (sondes) that become disconnected from the logging cable and are trapped in the drillhole. When the tool slides over the top of the gamma-ray probe, studs on the bottom engage the shoulder near the top of the probe (Fig. 2), which is then pulled to surface.

Jan 10, 1959

By Donald W. Scott

GENERALLY speaking, there is nothing very difficult about taking good micrographs of photogenic thin sections or grains with a petrographic micro-scopecamera setup. However, sometimes it is desired to show some detail that cannot be illustrated satisfactorily by the usual micrographs taken with parallel polarized light, with crossed nicols, or even with two micrographs. A simple procedure giving good results has been used at Battelle Memorial Institute for subjects falling into this classification, and it is believed to be of interest, especially to research people who must sell a point to executives through the medium of well-illustrated reports. The following problem illustrates a typical application: It is desired to photograph a thin section of an iron ore to illustrate the character and association of the iron oxides and the individual quartz crystals. A magnification of 75 dia. is acceptable. A micrograph of the field in question (Fig. I[a]) was taken with parallel polarized light. Due precaution was taken to provide critical illumination, correct exposure, a sharp focus, a good darkroom technique, and other essential conditions. It illustrates correctly the iron oxides, but it fails to show the individual quartz crystals. A micrograph of the identical field (Fig. I[b]) was taken under the same precise conditions, but with crossed nicols. It gives a better idea of the character of the individual quartz crystals but is likely to be misinterpreted unless accompanied by a lengthy descriptive note. This micrograph suggests that the centrally located, large black area is composed entirely of iron oxides. That this is an incorrect interpretation is evident by reexamining the micrograph of Fig. I[a]. The correct interpretation is that the dark area contains quartz crystals oriented with their optical directions parallel to, or nearly parallel to, the vibration directions of the polarizer and analyzer of the microscope. Thus, the executive, or anyone who had not done the work personally, would get no more than a fair interpretation, even if two micrographs were included; and in the interests of both brevity and clarity, one micrograph usually is more desirable. Exactly how many quartz crystals occur in this region cannot be told from the two micrographs, and a printing of the two negatives in register would likewise not show the detail desired. Thus, it is evident that some subjects cannot be satisfactorily illustrated by the usual procedures. In photographing Fig. is the light was subdued and, during the entire exposure of 75 sec., the analyzer nicol was rotated uniformly in its mounting from a crossed position to 45° uncrossed position to introduce the desired amount of contrast in the various individual quartz crystals. The true reproduction of the character and association of the iron oxides, and the additional structure and detail in the quartz areas, is apparent. It might be

Jan 1, 1946

By G. R. Speich

The precipitation of the Feab and Fe,Ti Laves phases (MgZn, type, C14) from Fe-Nb and Fe-Ti solid solutions, respectively, has been studied in the temperature range 500" to 800°C using hardness measurements, light and electron microscopy, and X-ray and electron diffraction. The Fe-Nb alloys contained 0.96, 1.67, and 3.80 pct Nb and the Fe-Ti alloys 3.5, 5.8, and 8.8 pct Ti. In both systems only the equilibrium Laves phase is formed, with nucleation occurring at grain boundaries, at dislocations, and in the matrix. No cellular precipitation or transition phases were observed. The precipitation of the Laves phase in a fine dispersion leads to significant hardening in both systems. The hardness of the aged alloys is proportional to the reciprocal of the square root of the interparticle spacing. The maximum solid solubility of titanium in a! iron is 9.0 pct Ti at 1280°C. THE precipitation of the FezNb and FezTi Laves phases (MgZn2 type, C 14) from Fe-Nb and Fe-Ti solid solutions, respectively, has been investigated as part of a continuing study of the mechanisms of precipitation from ferritic binary iron-base alloys. The iron-rich portions of the Fe-Nb and Fe-Ti phase diagrams are shown in Fig. l(a) and l(b). The Fe-Nb diagram is essentially that given by ansen' with the more recent work of Hume-Rothery and Gibson2 added. Goldschmidt3 indicates that the FezNb Laves phase has a solubility extending from 32 to 55 wt pct Nb. The Fe-Ti diagram is also essentially that reported by Hansen.l The recent results of Nishimura and kamei, Murakami, Kimura, and Nishimura,' indicate that the FezTi Laves phase has a solubility extending from 22.5 to 30.5 wt pct Ti. The L/6 + FezTi eutectic temperature of 1298°C indicated by Kornilov and oriskina' has been adopted. The addition of niobium or titanium to iron lowers the 6 — y transformation temperature and raises the y — a! transformation temperature. This results in a closed y field in the Fe-Ti system, but the lower solubility of niobium in a! (6) iron results in a eutec-toid, 6 — y + FezNb, at 1200°C, and a peritectoid, y + FezNb —-a, at 989°C in the Fe-Nb system. The maximum solubility of niobium is reported to be 4.5 wt pct in 6 iron,' 1.0 wt pct in y iron,7 and 1.8 wt pct in a iron.' Some results from the present work indicate that the maximum solubility in a! iron is actually less than 0.96 wt pct Nb. The maximum solubility of titanium in a! (6) iron is somewhat uncertain since the early work of To faute and Butting-haus indicated a value of 6.0 wt pct while later work of Kornilov and Boriskina6 yielded a value of 14.0 wt pct. The present work indicates that the maximum solubility is actually 9.0 wt pct. In both systems the phase in equilibrium with the iron-base solid solutions is a Laves phase (Mg znztype, C14), FezNb or FezTi. Both of these Laves phases have a wide range of Solubility. The precipitation-hardening behavior of Fe-Nb or Fe-Ti alloys has not been studied extensively. Genders and Harrison' reported that binary Fe-Nb alloys hardened upon aging. Peter and Fisher7 studied the mechanical properties of Fe-Nb and Fe-Ti alloys quenched from different phase fields.

Jan 1, 1962

By W. C. Winegard, J. E. Gruzleski

The stages in the development of cells in the Sn-Cd eutectic have been studied by unidirectionally solidifying specimens under known conditions of growth rate, temperature gradient, and impurity concentration. By means of a quenching technique, the shape of the solid-liquid interface during solidification could be observed. Cells are shown to develop from defects or depressions which exist on the solid-liquid interface of even a pure eutectic. Th,e container wall, grain boundaries , and fault lines in the micro structure play an important role in cell development. A two-phase eutectic dendrite found at high impurity concentrations is described. L HE cellular or colony structure formed during eutectic solidification caused much confusion among early workers in their attempts to classify eutectic structure, and a major advance in our understanding of eutectic solidification was made when the colony structure was identified with a cellular interface caused by the presence of impurity elements.1'2 To date, however, no detailed investigation of the stages in cell development in eutectics has appeared, and little work has been done on the cell morphology. The present paper presents the results of such an investigation. EXPERIMENTAL The Sn-Cd eutectic was used in this investigation with lead as the impurity element to promote cell formation. Materials of 99.999 pct purity were zone-refined to an approximate purity of 99.9999 pct. Alloys as close as possible to the eutectic composition, 67.75 wt pct Sn, were prepared using zone-refined tin and cadmium. The alloys were then zone-melted to the exact eutectic composition, as described by Yue and Clark,3 using a total of twenty to twenty-five passes on each eutectic bar. Only those portions of the bars which contained no primary phases were used in subsequent experiments. Master ternary alloys were prepared by melting together the required amounts of lead and the Sn-Cd eutectic in a sealed Pyrex tube under argon, and these alloys were then diluted with pure Sn-Cd eutectic as required. Unidirectional solidification was conducted vertically upward using the two-element resistance furnace shown schematically in Fig. 1. With this apparatus, it was possible to obtain a range of growth rates and temperature gradients so that the cell structure could be studied under different growth conditions. Growth rates in the range of 0.4 to 9.1 cm per hr and temperature gradients from 2.25° to 1475°C per cm were used. To ensure steady-state solidification, power to the furnace was stabilized, and the entire apparatus was enclosed in a large box in which the temperature was controlled to within ± 0.2°C. The apparatus was arranged so that the specimen could be quenched in situ during solidification by pouring a large quantity of water down the central vycor tube. Excellent delineation of the solid-liquid interface at the time of the quench was obtained because of the structural changes accompanying the rapid solidification of the remaining liquid. The quenching rate was always extremely rapid as no evidence of a transition in the lamellar spacing at the interface was ever observed. The alloys to be solidified were contained in degassed, high-purity graphite tubes, 1 cm OD and 0.6 cm ID. The specimens were about 18 cm in length. After the alloy had been cast into the tubes, three 0.8-mm holes were drilled in the tube to the center of the specimen. One hole was placed 1 cm from the bottom of the ingot, and the other holes were placed at 8 and 9 cm, respectively, from the base of the ingot. Thirty-four-gage chromel-alumel thermocouples were sealed in the holes. The lower thermocouple was used to position the solid-liquid interface at the start of each experiment,

Jan 1, 1969

By D. H. Polonis, Gary A. Dreyer

This investigation involved a study of the reactions occurring during aging of supersaturated a phase in a CIL-Si alloy. The aging processes at temperatures below 552°C were studied by means of metallography, microhardness, and electrical resistivity measurements. During the initial stage of aging in the temperature range 275o to 525oC an anisotropic phase, which is visible in the form of striations in the micro-structure formed prior to the appearance of the -phase. This transition phase has been designated k' due to its structural similarity to the k phase. The rate of K' formation during aging increased with aging temperature. At 450o and 525°C the reaction appeared to reach completion before significant amounts of precipitation were observed. The overall precipitation reaction in this system involved four stages: formation of formation of at a grain boundaries, growth of particles in 7-egions, and coagulation of into large particles. The relative role of each of these processes is dependent on the temperature of aging. The formation of phase from supersaturated a during aging increases the electrical resistivity and slightly increases the hardness of a 4.9 pct silicon alloy. The formation of during aging decreases the electrical resistivity and increases the hardness until coalescence of particles begins during the final stages of aging. The coalescence of results in a decrease of both electvical resistivity and hardness. THE available literature does not record a detailed analysis of the aging processes in Cu-Si alloys. Such an analysis has been difficult due to both the limited data available and misleading microstructural observations which have been reported. Previous work suggests that a rather complicated series of processes may be involved in the aging of supersaturated a. The present investigation is concerned with an analysis of the sequence of these aging processes in a 4.9 pct Si alloy. The currently accepted version of the Cu-Si equilibrium diagram, Fig. 1, was published by C. S. Smith in 1940.' This diagram shows a eutectoid at 5.2 pct Si with the high temperature phase, having its composition range entirely to the right of this value. By quenching alloys in the composition range 4.6 to 5.2 pct Si from the region, Smith was able to retain the phase. However, this phase exhibited a striated microstructure which was anisotropic to polarized light. These striations were suggested by Smith to be duplex twins. Using an oscillating crystal X-ray method Barrett2 studied alloys containing 4.0 to 5.4 pct Si quenched from the and regions. The striations observed in quenched specimens were attributed by Barrett to quenching stresses. He found that striations could also be formed by deformation after quenching and identified them as stacking faults in alloys containing 4.0 to 5.0 pct Si. Barrett related the striations in alloys containing 5.0 to 5.4 pct Si both to stacking faults and to a metastable phase which he called The striated structure reported by smith' was also obtained by Hoffmann, et al. 3 By deeply etching their specimens the anisotropic phase on the surface was removed, leaving a structure which was microscopically similar to pure copper. By means of X-ray analysis before and after deformation at room temperature it was concluded that the anisotropic phase was metastable This conclusion has been questioned by Barrett who attributes the discrepancy to superposition of k and lines on the powder patterns of Hoffmann, et alm3 The decomposition of supersaturated according to smith' and Anderson,4 is very sluggish. However, Nony and Dreyer,5 and Hoffmann, et al.' found that deformation increases the rate of decomposition. X-ray studies by Hoffmann, et al on

Jan 1, 1962

By Paul D. Merica

One of the most useful, and at the same time least commonly used, methods of thermal analysis for the determination of transformations in metals and alloys consists in the recording of the time intervals required for successive increments of temperature change during heating or cooling, the temperature of the furnace containing the specimen being altered at a uniform rate. The curve obtained by plotting these time intervals as a function of the mean temperature of the specimen durnig the interval is called the inverse-rate curve. It is probably due to the fact that no simple and convenient method has apparently been available for the measurement of the successive time intervals that this method has not been so generally used as, for example, the differential method, for which several types of automatic or semi-automatic apparatus have been designed. Whenever this method has been used, the intervals have usually been measured with the use of a chronograph; its operation as practised at the Bureau of Standards1 is as follows: The temperature of the specimen is measured by a thermocouple and a dial potentiometer. The operator sets the potentiometer at successive values of the electromotive force differing by equal increments, usually 0.02 millivolt, and records the exact instant on the chronograph, by pressing a contact key, at which the galvanometer coil passes through its null position. Two-second intervals are also recorded on the chronograph record, and the number of seconds elapsing between successive signals is afterward counted from the record and plotted as a function of the electromotive force or of the temperature. This is an admirable method and by it most minute thermal arrests may be detected, but it requires a good chronograph, which is generally difficult to obtain, and the time of one operator during the recording and, subsequently, to read the intervals from the record; the latter operation often takes from one to two hours. There is here suggested a simple, convenient, and, it is believed, equally accurate method of recording the successive time intervals, by which the

Jan 1, 1921

By Ernest Stütz

The problem of increasing blast-furnace efficiency through diminution of flue-dust production while operating with burdens consisting largely of fine ores has of recent years attracted the attention of metallurgists, whether directly or indirectly interested in the economies of iron smelting, and the various methods evolved from theory or practice have been submitted to wide discussion. After the very thorough and, at that time, exhaustive view of the whole subject, which was afforded to the industry by the meeting of this Institute in February, 1912, the subject was again taken up at the meeting of the Verein deutscher Eisenh?ttenleute at D?sseldorf in December, 1912. While American and German conditions are not entirely identical, it may be of interest to give here the words of the gentleman summing up the discussion at the Diisseldorf meeting: " The chief advantage offered by the use of briquettes lies in the fact that disturbances in the furnace, caused mostly by the presence of fine ores in the burden, are avoided, and that blast pressure can be considerably reduced. The resulting economies cannot be overrated, as, with lower blast consumption per ton of product, the installation will be able to take care of increased production. In consequence of lower pressure and speed of blast, heat is more efficiently utilized, flue gas temperature is lowered, and coke particles are less liable to be carried along with the flue dust, of which considerably less is produced. Finally, by increased regularity of operation and higher temperature in the lower parts of the furnace, the quality of the product is improved. The question of briquetting iron ores has grown to be one of the most important in the iron industry, and it is not any more a question of what is the cost of briquetting a ton of ore, but what, in using ore briquettes, is the cost of production of a ton of iron." Dr. A. Weiskopf, of Hannover, admirably condenses in these words

Jan 1, 1914

By M. E. Fine

IN the apparatus for measuring internal friction shown in fig. 1, a modification of that described by Kê,1,2 the parasitic energy loss or background is equivalent to a Q-1 of approximately 4x10-5. This low value of background was obtained by using a jeweler's collet of appropriate size for the upper support, eliminating lateral motion without immersing the bob in oil, and designing the bob to reduce air resistance. The pendulum is supported on the frame through a snug fitting, sliding rotary joint (fig. I-B). A slight twist of the top imparts essentially pure torsional motion to the pendulum. No evidence of energy loss in the sliding joint has been observed. In the bob (E) steel balls are used in the torsion arm, and the bottom is filled with lead giving a total weight of 94 g. A lighter bob may be used for small diameter specimens. Another bob was a solid disc with provision for adding discs to change the frequency. The oscillating image of the filament is recorded on a revolving drum camera (fig. 1-3) driven by a synchronous motor. This allows use of frequencies higher than can be measured visually on a glass scale. Samples varying in diameter from 0.020 to 0.075 in. have been measured, the frequencies have ranged from 1 to 12 cps, and the maximum strain varied from 0.5 to 10x10-5. With appropriate modification the sample may be placed in a thermostat. The apparatus may also be used to measure the shear modulus. In the examples of measurement given in table I the internal friction of Permendur and the 46.8 Ni-Fe alloy are due, for the most part, to magneto-mechanical hysteresis8 (elastic hysteresis accompanying stress-induced magnetostriction) which depends on strain amplitude and increases with annealing. The internal friction of most materials decreases with annealing. References IT. S. K6: Physics Review (1947) 71, 533. 2 T. S. Kê: Transactions AIME (1948) 176, 448; Metals Technology (June 1948) TP 23703. 3 R. Becker and W. Döring: Ferromagnetismus. 365 (1939). J. Springer.

Jan 1, 1951

By Nicholas Chlumecky

To date information is somewhat limited concerning the strength and bearing capacity of floor strata, which is of great importance where proper roof control is desired. If the bearing strength of strata is not known, the support may be excessively strong in relation to the support capacity of the floor, with the result that strong props sink into the floor strata, giving them dubious value as a roof support. The method described is used to determine how tests are made on dry rock to determine the required support area for the base of props or other structures which may rest on rock strata in mines. Relationships were established for the bearing capacity of rocks which were subjected to loads by means of bearing areas of various sizes ranging from 0.09 sq cm (.014 sq in.) to 700 sq cm (108.5 sq in.). This permits the evaluation of the bearing capacity of rocks by testing small areas for the de- termination of the capacity of larger areas.

Jan 3, 1968

By W. F. Stowasser

Robert E. Hagen (Oliver Iron Mining Div., U. S. Steel Corp.)—Mr. Stowasser and his associates are to be congratulated on their achievements in developing the design of a pilot agglomerating plant, based on information obtained from experiments made in a laboratory sinter pot, and subsequently constructing and successfully operating this plant. In his Transactions article, May 1955 (vol. 201) Mr. Stowasser stated that the output of his heat treating strand was about 2 Lt per sq ft of grate area per day and that the fuel consumption was 0.7 to 0.8 million Btu per Lt of product. If it is assumed that the burning zone extends from the back of the ignition furnace to the beginning of the recuperation windbox, only about 1/3 of the grate area over the windboxes is utilized for burning pellets, and the actual rate at which partially dried pellets are burned is about 6 Lt per sq ft of grate area per day. It may be interesting to compare the above operating data with that obtained at the Extaca plant, where taconite concentrate is treated on a conventional sin- tering machine using limestone or hydrated lime additives with no recuperation of heat. The entire windbox area is used for burning, and a production rate of 2.5 Lt per sq ft of windbox area per day has been attained at a fuel consumption of 1.8 to 2.0 million Btu per Lt of product, the latter being considerably in excess of that reported by Mr. Stowasser, partly because a circulating load of returns amounting to 28 to 30 pct of the machine feed is used and because no attempt is made to recuperate heat from the waste gases. With the high capital and labor costs prevailing today, it seems that future development of the downdraft grate pelletizing process should be directed toward taking advantage of the high burning rate of predried pellets and increasing capacity, perhaps at the expense of fuel economy, by decreasing the proportion of grate area utilized by ancillary functions. For example, eliminating the cooling zone and using this area for burning would increase the proportion of grate area available for burning from 33 to 50 pct of the total windbox area, and a proportionate increase in capacity would result.

Jan 1, 1956

By W. E. C. Eustis

1st. THE fine iron ore is mixed with a sufficient proportion of fine coking coal, and is coked in any of the ordinary methods for making coke. The effect of this is to convert the iron oxide into sponge in such a shape that the usual trouble of oxidation is avoided. 2d. The resulting mixture of coke and sponge is melted down in an ordinary cupola, the coke furnishing more than sufficient fuel for that purpose. I may briefly point out here that in the first place the iron is sponged, and this sponge, as is well known, contain-, no phosphorus or silicon when the reduction takes place at a low temperature; and in the second place this sponge is melted down in a cupola in which there is no zone of reduction for phosphorus or silicon, and that con¬sequently the resulting iron should be free from both of these impu¬rities. 3d. The liquid sponge, now carburized, is run into an open-hearth furnace, where the requisite degree of hardness or softness is obtained by adding some of the fine ore, and the usual dose of ferronmanganose. I have merely given above the rough outlines of the process, but it is my intention, as early as possible, to bring the process more fully before the Institute.

Jan 1, 1881

By David A. Rice

This note describes a simple, rapid technique for measuring the apparent volume and density of individual bits of porous materials such as iron ore pellets or pieces of coke. The method consists of determining the weight recorded on a balance when a particle is depressed below the surface of mercury, and calculating the apparent volume from the known density of mercury. The apparent density is calculated after weighing the particle in air. The method is particularly well suited for applications where a great number of determinations are to be made. An additional benefit is the minimal handling of the mercury. In any event, the usual recommended safety precautions should be adhered to.

Jan 1, 1982

By L. M. Higgins

Dust or fume control systems are devices for capturing contaminants at their source and preventing their discharge to atmosphere. The Primary Components Of Any Dust Control System Include: An enclosure around any potential dust source such as conveyor belt transfer, crusher, screening machine, bin loading and loadout. Ductwork including hood takeoffs (transitions) to convey the collected dust laden air away from the source of dust generation to a convenient location. A dust collector for separation of particulate matter from the air stream prior to its discharge to the atmosphere. A prime mover generally a fan, to draw air into an enclosure and to overcome resistance to flow in the ductwork, dust collector and stack.

Jan 1, 1978

By T. S. Lundy, R. E. Pawel

Effects of short-circuiting paths on observed diffusion behavior in real crystalline systems are considered. It is concluded that experimentally measured diffusion coefficients may vary widely from values associated with true lattice diffusion to those appropriate for short-circuiting paths alone depending upon the conditions of the experiment and the sensitivity and completeness of the data. IN 1961 Harrison1 classified experimentally observed diffusion behavior in systems involving both lattice and dislocation-enhanced atomic transport into three categories. His types A and C were limiting cases where the measured diffusion coefficients using the usual serial sectioning techniques were representative of lattice diffusion (with only slight effects of dislocations) and dislocation-network diffusion (with only slight effects from lattice diffusion), respectively. In both cases A and C for a sectioning experiment in which the diffusion couple has the semi-infinite geometry and unidirectional diffusion takes place from a plane source located at the origin of the coordinate system, he pointed out that Gaussian penetration behavior should be observed. For case A the lattice coefficient should be slightly enhanced by dislocation contributions, and the model of Hart2 can be used to predict the amount of this enhancement. For case C the observed coefficient should be that for the dislocation network and have little or nothing to do with lattice diffusion. Hart's model in its general form is still applicable, but the apparent diffusion coefficient for this case is virtually independent of dislocation density. Harrison's case B is that for which non-negligible contributions exist for transport by both mechanisms and "the concentration distribution does not approximate to any simple form." With the possible exception of very low temperatures where diffusion distances approach atomic dimensions, any real diffusion specimen will in general show non-Gaussian behavior provided the data are complete enough to uncover it. Thus, a "complete" set of data for any real system cannot be expected to be totally amenable to treatment by a simple mathematical model which does not take into account the relative distribution of transport by the various modes or submodes. For a particular sensitivity of specimen analysis and at a given temperature of annealing if the concentration profile could be observed as a function of time, "the behavior will initially be type C, and will develop into type B. and ultimately type A".1 Thus, it appears that the type of diffusion behavior which is experimentally observed in a given system depends very much upon the particular experimental conditions and the particular tools available to obtain the data. Interpreted in this fashion, Harrison's classification refers not to the diffusion behavior as a whole but to the relative sensitivity of the method of examination and completeness of the data. In the present paper we will: 1) assume that the measured penetration behavior follows the same general classification as that proposed by Harrison; 2) give, for diffusion in tungsten, examples of the range of diffusion coefficients that it is possible to obtain in a single experiment; and 3) speculate that some arguments which consider the possibility of short-circuiting effects being responsible for "anomalous" diffusion in several bcc metals may have been discarded prematurely.3 Both monocrystalline and polycrystalline tungsten were used in this work. The former was obtained as triple-pass, electron-beam zone-refined 6.0-mm-diam rod from Materials Research Corp.. Orange-burg. N.Y. The latter was swaged, high-purity bar stock which was annealed for 2 hr at 2200°C and 10-9 torr to yield an average grain diameter of about 25 /i. The tracer Nb95 was received in oxalate solution from the Isotopes Division, Oak Ridge National Laboratory. Experimental procedures of specimen preparation, isothermal diffusion annealing, serial sectioning by anodizing-and-stripping, and y counting of the individual sections to determine the tracer penetration profile after a given diffusion anneal have been described elsewhere.4 However, it should be noted that the anodizing-stripping sectioning technique has the particular advantage for this research of permitting sectioning to be accomplished over a wide range of

Jan 1, 1970

By S. C. Geol, C. H. Page

INTRODUCTION Mining at Mindola Mine, Rokana Division of Nchanga Consolidated Copper Mines Limited is the deepest on the Zambian Copperbelt. Mining extends to 1150 metre depth so far and the present plans extend to 1500 metres, although reserves exist below this level. Mindola Mine is the major producer of copper/cobalt ore at Rokana Division and produces approximately 200,000 tonnes of copper/cobalt ore per month. A standard open stoping method is the only method used for mining with minor variations in positioning drilling drives and other development, figure 1. The standard main haulage interval is 75m but in flat dipping areas the full stope height is split into two or three panels. In 1970 severe mining problems were experienced when mining deeper than 850111 below surface. The main problems included: - Heavy support requirements in drilling drives near stope face. - Premature closure of blast holes necessitating pre-charging of the holes with explosives immediately after drilling and well before the day of blasting. - Severe bumping and spitting due to rock movements on drive surfaces and remotely within the rock mass under high stress. - Low mining efficiency due to dilution from the waste hangingwall. - These stress related factors also caused some premature detonations of precharged but unprimed blast holes which became a serious safety hazard. A number of alternatives have been considered to overcome these problems. A search for leas sensitive explosives to avoid the premature detonation problem has been partially successful, however, the need for a method of reducing stress levels at the mining face is still considered essential as the mine goes deeper. This paper describes experiments with Regional Support Pillars as a method of reducing stresses at the mining face.

Jan 1, 1981

By C. L. Magee, H. W. Paxton

PREVIOUS workersl'% ave found that as-quenched ferrous martensites can be plastically deformed at low stresses. They have also found that the stress to obtain small strains can be significantly increased by aging at temperatures up to 150°C. This behavior has been interpreted in two ways: 1) that the deformation at low applied stress is due to internal stresses and thus the aging phenomenon is due to relaxation of the internal stresses;' 2) that the microdeformation arises through the motion of unpinned dislocations and the aging process is the diffusion of carbon to the dislocations to pin them.293 In a recent paper,4 we have shown that under certain conditions the dominant microdeformation mechanism of as-quenched Fe-31Ni marten-site-austenite aggregates is the transformation of retained austenite. Our results on resistance changes during deformation and temperature dependence of the deformation also established that, at temperatures above 300° K, the microdeformation was not due to this transformation. The purpose of this note is to report results of experiments which indicate that explanation 1 is appropriate for this deformation. All results presented here are from conditions where transformation does not make a measurable contribution to the microplastic deformation, in Fe-31Ni-0.002C, or in Fe-29Ni-0.02C-0.25Ti. The experimental techniques that were used for measurement of the plastic deformation are described4 and analyzed5 elsewhere. Fig. 1 shows the microplastic response of 100 pct austenite at 300" and 350° K. The microplastic response of an austenite-martensite aggregate is also given in Fig. 1 and it is seen that, after formation of martensite, the initial plastic deformation occurs at lower stresses. Thus, the softness is not entirely due to retained austenite—the quenched structure can be deformed at lower stresses despite the fact that the macroscopic strength is significantly higher. A result which allows a distinction to be drawn between the alternative explanations for this behavior is derived from aging experiments on the low-carbon alloy containing titanium. We have previously shown4 that the presence of titanium in this alloy reduced the free carbon to a sufficiently low level that thermal stabilization of the austenite-martensite transformation was not detected. Despite this, Fig. 2 shows that the microplastic response is decreased by aging treatments. A similar aging effect in Fe-ZONi, with some titanium, has previously been reported by . Thus, carbon is not necessary for the aging process and explanation 2 is at best incomplete. Since internal stress relief can occur independently of carbon (any temperature dependence of the flow stress can result in decreased internal

Jan 1, 1969

By John B. Gayle

PRESENT flotation processes depend almost entirely on the buoyant properties of air bubbles to effect separations of mineral and gangue, but there is no convenient method for measuring aeration in flotation cells. Consequently the relation between aeration and cell performance has not been definitely established. In connection with a comparative study of kerosene and froth flotation processes, a modification of the displacement method' was developed in which air escaping from the cell surface is measured with a wet-test meter. The arrangement shown in Fig. 1 is satisfactory for use with a number of cells and is not critical, except that care must be taken to use connections and tubing large enough to avoid excessive back pressures. Attempts to use smaller tubing resulted in back pressures that caused displacement of the liquid level in the receiver, so that some air was lost around the sides, an occurrence readily visible when measurements were taken with only water passing through the cell. With the arrangement shown, the manometer indicated an average reading of about ½ -in. water pressure. No loss of air was evident.

Jan 7, 1958

By J. T. Richards

ELASTIC constants, including E-modulus, G-modulus, Poisson's ratio, and compressibility, are affected by temperature, but not necessarily to the same degree nor in the same direction. Theoretical expressions relating the temperature coefficients for the various elastic constants have been introduced by Gruneisen. In considering the thermoelastic characteristics

Jan 1, 1955

By Victor Phillips

Cyclone thickeners have emerged from the development stage and now can be accepted as useful tools for the recovery of fine coal from a preparation plant circulating water. As primary thickeners in a closed water circuit operation, their advantages over conventional thickening methods are twofold-the lower initial investment and reduced area requirements.

Jan 8, 1951

By R. T. C. Rasmussen, L. H. Banning, W. E. Anable

In the rapidly growing industry of elemental-phosphorus production from western phosphates, most of the vanadium and chromium contained in the phosphate rock collect in the byproduct ferro-phosphorus. Results are presented of a completed laboratory project, which developed a tristage crystallization and hydrolysis process for recovering strategic vanadium and chromium, as well as a valuable phosphorus product, after extracting these elements from the ferro-phosphorus by roasting and leaching. THE Phosphoria formation in Idaho, Montana, Wyoming, and Utah contains the Nation's largest reserve of phosphate rock. A unique feature of the Phosphoria beds is their content of a fraction of a percentage each of vanadium, chromium, nickel, and molybdenum. Vanadium is the most important as to quantity and value. Small-scale tests by the Bureau of Mines at Albany, Oregon, in 1947, indicated that most of the vanadium in the phosphate rock collects in the ferrophosphorus product of smelting. Subsequent electric smelting operations to produce elemental phosphorus from western phosphate rock (experimentally by TVA and industrially at Pocatello, Idaho) have shown that the vanadium and other metals in the rock are to a large extent recovered in concentrated form in the ferrophosphorus byproduct. This paper reports the results of completed laboratory research on the recovery of vanadium from ferrophosphorus, which was undertaken by the Bureau of Mines at Albany in 1948 as the first phase of a project entitled, "Vanadium and Fluorine from Western Phosphates." The various vanadium-recovery methods investigated, including the roast-leach method that showed most promise and was studied in greatest detail, are discussed in an earlier publication.' Subsequent systematic study of the roast-leach method of extracting vanadium from western ferrophosphorus developed the more effi- cient tristage crystallization process, which is the subject of this paper. Process Development The investigations were made on ferrophosphorus produced in the electric smelting of elemental phosphorus from western phosphate rock. The TVA provided two sample lots of ferrophosphorus produced in pilot plant smelting of phosphatic shale from the Fort Hall Indian Reservation in Idaho. The Westvaco Chemical Div. of the Food Machinery & Chemical Corp. supplied two sample lots of ferrophosphorus produced by its phosphorus smelter at Pocatello, Idaho. The analyses of all four lots are shown in Table I. Westvaco lot B was the starting material for the more recent tests. The roast-leach process for recovering vanadium from western ferrophosphorus, as originally developed, employed the following principal steps: Roasting of a mixture of pulverized ferrophosphorus, soda ash, and salt; extraction of the water-soluble vanadium, phosphorus, and chromium compounds from the calcine by leaching, settling, and decanta-tion of the pregnant solution; primary crystallization of trisodium phosphate from the pregnant solution; purification of the trisodium phosphate crystals by dissolution in water and secondary crystallization; purification of the pregnant vanadium solution from the primary crystallization step by adding calcium chloride to precipitate calcium phosphate; and hydrolysis of vanadium red cake from the puri-

Jan 1, 1954