Search Documents

By N. A. Gokcen

THE data of Chaudron,1 Tonosaki,2 and Collins³ on the thermodynamic properties of MOO, disagree widely. These authors, by using essentially similar methods, studied the following reaction: 1/2MoO2(s) + H2(g) == i/2Mo(s) + Ph,o H2O(g),K = —----- [1] Ph2 Tonosaki used a vacuum system consisting of a furnace containing MOO, and a water saturator whose temperature was kept at 25 °C with a thermostat. After repeated evacuation, hydrogen was admitted slowly into the system. The experiments were based upon the fact that at a constant furnace temperature and constant partial pressure of water, the total pressure of gas mixture over MOO? + Mo is constant. Any attempt to vary the pressure by external forces would vary only the amounts of MoO2, and Mo, after which the pressure should return to the equilibrium value in accordance with the equilibrium constant of reaction 1. The actual value of K was determined from the total equilibrium pressure (sum of Ph2o + Ph2) at each temperature. The total pressure of gas was varied within the range of 80.2 to 125.4 mm Hg, within a temperature range of 645" to 823 °C. The results were summarized as log K = 0.9413 — 1444.6/T for reaction 1. The ratio of H2O/H2 was considered to be uniform in spite of the presence of a thermal gradient across the static gas phase. It was shown by Rosenqvist and Cox,' however, that in somewhat similar circumstances the error resulting from thermal diffusion may be large. Collins³ improved Tonosaki's method by attempting to avoid thermal diffusion errors. His equilibrium data were obtained at 700°, 800°, and 900° C, and the result for reaction 1 was expressed as log K = 1.258 — 1822/T. The purpose of this investigation was to study reaction 1, avoiding the thermal diffusion errors, and to obtain equilibrium data in a considerably wide temperature range for the reliable extrapolation of the resulting thermodynamic functions. Experimental Procedure The diagram of the apparatus is shown in Fig. 1. Tank hydrogen was passed through a tube containing platinized asbestos at 425 °C in order to convert a trace of oxygen into water vapor. The flow rate was carefully controlled with a capillary-type flow-meter B and a bubbling column D. The gas was then presaturated sufficiently at P and led into a condenser system immersed in a thermostat, controlled to within ±0.002C. The temperature of the thermostat was measured with a thermometer calibrated against a certified standard. The temperature of P was adjusted to avoid the condensation of unduly large amounts of water as judged from the rate of flow out of the capillary tube M. Argon was purified by passing it through magnesium chips kept at 630°C. After passing through the flowmeter B', it was mixed with moist hydrogen emerging from the thermostat. The resulting gas mixture was then led into the hot zone of the furnace through the heated glass tubing and the silica tube S, thus insuring the same ratio of PII2o/Ph2 from the condenser to the reaction chamber, thus avoiding thermal diffusion. The entire gas system was of all-glass construction, except at the magnesium train. The furnace comprised a glazed alumina tube over which a 15-in. platinum coil was wound. The lower end of the alumina tube was tightly closed with a brass bottom and a silicone rubber gasket, and the upper end with two glass disks, each with a hole of 1/16 in. in diameter, through which the gas mixture escaped into the atmosphere. A back-up coil of kanthal wire facilitated the temperature control of the furnace. A coil of annealed molybdenum strip of 99.99 pct purity, 0.005 in. thick and 0.050 in. wide, and weighing 17 g was hung in the furnace with a 0.010-in. platinum wire attached to one end of a sensitive analytical balance. The temperature of the furnace was measured with a Pt-Pt-10 pct Rh thermocouple checked against a standard. The experimental procedure consisted of heating the gas purification trains, adjusting the gas flow rates, attaining a constant thermostatic temperature, flushing the entire system for 2 hr while heating the furnace to well above the expected equilibrium temperature and then cooling it at a rate of 0.3°C per min during which time the change in the weight of molybdenum was observed on the balance. For a given thermostatic temperature, i.e., a constant Prr,o/Px,, molybdenum oxidized upon cooling slightly below the equilibrium temperature. The procedure was then repeated by heating the furnace and thus reaching a temperature slightly above the equilibrium value. The average of the two temperatures, differing by 2" to 3"C, was considered to be the true equilibrium temperature. In order to determine the stoichiometric composition of the oxide phase present in this investigation,

Jan 1, 1954

By H. A. Guess

For a number of years I have used for the commercial wet assay of lead generally the ammonium molydate, and occa-sionally the ferrocyanide method. These well-known methods need no detailed description here. In the ore-selling and ore-buying establiahments of the West, 90 per cent. of all wet lead-assays are made by one or the other, and at least nine-tenths of this proportion by the molybdate method. A procedure so well-established must have merit; and, in

Jan 1, 1905

By G. F. Comstock

A serious disagreement as to the effect of titanium on the hardenability of steel exists in published references to this subject. Kramer, Hafner and Toleman reported1 that acid-soluble titanium decreased the hardenability, with multiplying factors less than unity according to Grossmann's system for calculating hardenability from the composition. Crafts and Lamont, on the other hand, showed2 how titanium increased the hardenability, with multiplying fdctors up to nearly I.; for about 0.1 per cent titanium, though reducing the hardenability with higher titanium. Their data, however, were obtained almost exclusively from steels containing more than 1.4 per cent manganese, and thus should be considered as applying mainly to manganese steels. Likewise, the results of Kramer, Hafner and Toleman regarding titanium are subject to the limitation that although they eliminated the effect of the insoluble titanium compounds from their calculations, they did not make a similar correc- tion for the carbon that was combined with titanium and therefore occurred in a similarly ineffective form. It is suggested by the literature referred to that titanium may have different effects on hardenability, depending on the mode of its occurrence in the steel. The different effects on strength, ductility, etc., have already been discussed by the author.3 In the present discussion some comparisons, on the basis of hardenability as revealed by the Jominy end-quench test, are given between three titanium and two non-titanium steels heat-treated in the same ways, and between other titanium steels heat-treated in several different ways. Comparison of Plain-carbon, Vanadium and Titanium Steels The five steels used for these experiments were cominercially melted and rolled products received in the form of 1.5-in. rounds from three different mills. Their analyses are given in Table I. Steels 2, 3, and 4 are from the same basic electric heat1 containing 0.009 per cent of phosphorus and the same amount of sulphur. They were made by adding aluminum and low-carbon ferrotitanium to different ingots. No. I is a plain carbon

Jan 1, 1947

By G. F. Comstock

A serious disagreement as to the effect of titanium on the hardenability of steel exists in published references to this subject. Kramer, Hafner and Toleman reported1 that acid-soluble titanium decreased the hardenability, with multiplying factors less than unity according to Grossmann's system for calculating hardenability from the composition. Crafts and Lamont, on the other hand, showed2 how titanium increased the hardenability, with multiplying fdctors up to nearly I.; for about 0.1 per cent titanium, though reducing the hardenability with higher titanium. Their data, however, were obtained almost exclusively from steels containing more than 1.4 per cent manganese, and thus should be considered as applying mainly to manganese steels. Likewise, the results of Kramer, Hafner and Toleman regarding titanium are subject to the limitation that although they eliminated the effect of the insoluble titanium compounds from their calculations, they did not make a similar correc- tion for the carbon that was combined with titanium and therefore occurred in a similarly ineffective form. It is suggested by the literature referred to that titanium may have different effects on hardenability, depending on the mode of its occurrence in the steel. The different effects on strength, ductility, etc., have already been discussed by the author.3 In the present discussion some comparisons, on the basis of hardenability as revealed by the Jominy end-quench test, are given between three titanium and two non-titanium steels heat-treated in the same ways, and between other titanium steels heat-treated in several different ways. Comparison of Plain-carbon, Vanadium and Titanium Steels The five steels used for these experiments were cominercially melted and rolled products received in the form of 1.5-in. rounds from three different mills. Their analyses are given in Table I. Steels 2, 3, and 4 are from the same basic electric heat1 containing 0.009 per cent of phosphorus and the same amount of sulphur. They were made by adding aluminum and low-carbon ferrotitanium to different ingots. No. I is a plain carbon

Jan 1, 1947

By Walter H. Bruckner, George B. Clark

SINCE the end of World War II interest has been increasing in the use of shaped charges in the mining industry and in other industries using explosives for blasting purposes. Shaped charges employ the principle known as the "Munroe effect," which was discovered by Charles E. Munroe more than 50 years ago (in 1888). Details of their design have been explained e1sewhere.l,2,3 Fig I shows the essential features of design of two types of shaped charges (with conical and hemispherical cavities) and a schematic sketch of their action upon detonation. The following discussion deals with the behavior of the metal in the cavity liners when they are subjected to intense pressures exerted when the explosive charge is detonated. Among the conclusions reached in research on shaped explosive charges, the following have been established concerning cavity liners: 1,2 I. The optimum wall thickness of a conical cavity liner is dependent upon the apex angle of the cone as well as on the base diameter of the charge. Acute apex angles require thinner walls for optimum performance and more obtuse angles require thicker walls for the same base diameter. 2. Cones were more effective in forming a penetrating jet when the walls were tapered; i.e., the thickness of the wall of the cone increased from the apex down. 3. The physical and mechanical proper- ties of metals have a marked effect upon their performance as cavity-liner material. Boiling point, ductility, malleability, tensile strength, and hardness are among the properties that influence the effectiveness of a metal used as a cavity liner. Lead, for example, makes a wide, flat crater in steel plates. Aluminum makes a deeper crater than lead, and an aluminum alloy having a high tensile strength makes a deeper hole, but slightly smaller in diameter. Cast iron makes a deep, narrow hole. These findings, together with the following analysis under Metallographic Survey of Slug, offer solutions to many of the problems involved in solving the mechanism of the formation of Munroe jets. It has been fairly well established that cavity liners collapse in a manner similar to that indicated in Fig 2. Conical liners are known to collapse upon themselves while hemispherical liners are believed to turn inside out in the process of jet formation. The first has been definitely proved by recovery of collapsed portions of cones, while liners from partly detonated charges show that hemispheres may turn inside out. Fig 3 shows a sketch of a recovered slug from a 6-in. shaped charge using a 45° cone made of cast iron. (This size of charge drilled holes up to 3 ft in depth in solid granodiorite.)

Jan 1, 1947

By C. H. Jr. Herty

DURING the past few years frequent reference has been made to a certain type of iron known generally as "bad iron," "dirty iron," etc., both by steelmakers and producers of iron castings.1 Open-hearth operators have claimed that such iron was entirely within the specified limits as to ordinary analysis but it was difficult to make good steel from it. It has been suggested that unreduced material in the iron is responsible, also that most trouble is experienced with the iron when the blast furnace is delivering a product whose analysis is more or less variable. Other reasons suggested are the use of scrap or borings, unsintered flue dust in the burden, a cold hearth, too high a proportion of unsuitable grade of ore, or the form of the carbon in the iron. Accordingly, a subcommittee was appointed at the fall meeting of the Open-hearth Committee of the American Institute of Mining and Metallurgical Engineers held in Pittsburgh in October, 1926, to investigate the reasons for the occurrence of this bad iron and suggest methods for preventing its appearance. This committee enlisted the cooperation of the U. S: Bureau of Mines Experiment Station at Pittsburgh in undertaking a study of pig-iron quality as affecting the open hearth. The following is a report of the findings to date:

Jan 1, 1929

By Paul T. Allsman, E. W. Newman

Trenching, sampling, and core drilling in Stillwater and Sweetgrass Counties, Mont., by the Bureau of Mines have delimited over 5,000,000 tons of chromite ore containing more than 20 per cent chromic oxide. The Benbow and Mouat-Sampson mines have been developed and are fully equipped for mining and milling 500 tons and 2000 tons a day, respectively. Introduction The Montana chromite deposits were the first to be explored under the Strategic Minerals Act of 1939. In June of that year, the Bureau of Mines started exploration by trenching, test pitting, sampling and diamond drilling, and completed the project in March 1943. The U. S. Geological Survey cooperated by mapping the geology and logging the cores. The project was to determine the extent and grade of the chromite ore and to indicate sufficient reserves to justify development and exploitation of the deposits for the national emergency. Exploration has indicated that the district contains the largest and most important reserve of chromite ore in the United States. The Benbow and Mouat-Sampson mines have been developed and a 500-ton concentrating mill has been constructed on the Benhow property and a 2000-ton mill on the Mouat-Sampson property. Concentrates were produced from the Benbow mill three months after the attack on Pearl Harbor, when the nation's major chromite supplies from foreign sources were cut off. History It has been known for 50 to 60 years that some chromite deposits existed in an east-west belt along the north escarpment of the Beartooth Mountains about 25 miles north of Yellowstone Park, but nothing was known of their size and extent until the war demand of 1917 and 1918 stimulated the search. In those years two properties in the Stillwater region were actively developed, but no shipments were made. The Benbow property was located in 1918 by a local group. The property comprised seven claims along the strike at the east end of the belt. An adit was driven several hundred feet on the Eclipse claim. The seven claims were sold to the Chromium Products Corporation of Livingston, Mont., and were subsequently patented. In 1929, an eastern group obtained an option, installed some equipment, and erected several log cabins. The "crash" in the market in 1929 caused the operators to drop their lease, and the property remained inactive until 1939, when the Bureau of Mines began its exploration. Fourteen claims were located on the Boulder River in 1918 and subsequently patented by the U. S. Chrome Corporation.

Jan 1, 1949

By Paul T. Allsman, E. W. Newman

Trenching, sampling, and core drilling in Stillwater and Sweetgrass Counties, Mont., by the Bureau of Mines have delimited over 5,000,000 tons of chromite ore containing more than 20 per cent chromic oxide. The Benbow and Mouat-Sampson mines have been developed and are fully equipped for mining and milling 500 tons and 2000 tons a day, respectively. Introduction The Montana chromite deposits were the first to be explored under the Strategic Minerals Act of 1939. In June of that year, the Bureau of Mines started exploration by trenching, test pitting, sampling and diamond drilling, and completed the project in March 1943. The U. S. Geological Survey cooperated by mapping the geology and logging the cores. The project was to determine the extent and grade of the chromite ore and to indicate sufficient reserves to justify development and exploitation of the deposits for the national emergency. Exploration has indicated that the district contains the largest and most important reserve of chromite ore in the United States. The Benbow and Mouat-Sampson mines have been developed and a 500-ton concentrating mill has been constructed on the Benhow property and a 2000-ton mill on the Mouat-Sampson property. Concentrates were produced from the Benbow mill three months after the attack on Pearl Harbor, when the nation's major chromite supplies from foreign sources were cut off. History It has been known for 50 to 60 years that some chromite deposits existed in an east-west belt along the north escarpment of the Beartooth Mountains about 25 miles north of Yellowstone Park, but nothing was known of their size and extent until the war demand of 1917 and 1918 stimulated the search. In those years two properties in the Stillwater region were actively developed, but no shipments were made. The Benbow property was located in 1918 by a local group. The property comprised seven claims along the strike at the east end of the belt. An adit was driven several hundred feet on the Eclipse claim. The seven claims were sold to the Chromium Products Corporation of Livingston, Mont., and were subsequently patented. In 1929, an eastern group obtained an option, installed some equipment, and erected several log cabins. The "crash" in the market in 1929 caused the operators to drop their lease, and the property remained inactive until 1939, when the Bureau of Mines began its exploration. Fourteen claims were located on the Boulder River in 1918 and subsequently patented by the U. S. Chrome Corporation.

Jan 1, 1949

By F. A. Schaufelberger

Early work on chemical precipitation of metals from metal salt solutions is reviewed. The chemistry and thermodynamics of precipitating copper, nickel, cobalt, and cadmium metals by reaction with hydrogen are discussed. Mechanisms of metal precipitation, nu-cleation, growth, and agglomeration are reviewed, as well as some solubility phenomena of cleation,gases and solids at elevated temperatures. Experimental data presented deal mainly with the reaction of copper sulfate solution with Hz. METAL can be recovered from a leach solution either indirectly by precipitation as a compound that is later reduced or directly by electrolysis, cementation, or chemical reduction, for example, with hydrogen. The widely used electrowinning processes suffer from the inefficiency of converting fuel to low voltage dc and from low current efficiency when complete recovery is attempted. With the batch hydrogen reduction methods outlined here, a unit of fuel converted to hydrogen in modern gas reform plants will make two to three times as much metal as can be obtained with electrolysis. With continuous hydrogen reduction, four to six times as much metal is obtained. Precipitation by reducing a metal salt solution with H, has been known for almost 100 years.' Commercial use of the process, however, awaited the research and development program initiated by Chemical Construction Corp. Within the last few years this program has brought about construction of commercial plants, listed on p. 701. Ideal hydrogen reduction will precipitate a pure metal from a solution obtained by commercial leaching methods at a rapid rate without excessive temperatures and pressures. The metal precipitate will be of desired size and density, less than a percent left in the vessel being deposited on the wetted parts. The present discussion will outline Chemical Construction Corp.'s early development program and will discuss the chemistry and mechanics of reducing copper, nickel, cobalt, and cadmium from solution by H2. Work on selective reduction of nickel from cobalt has been described earlier.2 The article is not concerned with precipitation of copper by disproportionation of cuprous solutions where yield is limited" to 50 pet.* It does not discuss use of gaseous reducing agents other than hydrogen, such as SCV which may lead to contamination with sulfur, or CO," which is considerably more expensive than hydrogen and produces a gaseous reaction product, CO2.† The article does not include use of other nongaseous reducing agents: which are far more expensive than CO. Also, notes on the history, engineering design, and performance of commercial plants have been given elsewhere." It will be shown that a pure metal can be precipitated by reduction with hydrogen from solutions obtained by commercial leaching methods when the solution cohposition is controlled and proper acidity, proper metal ion concentration through controlled complex formation and hydrolysis, and adequate agitation for suspension of metal and for transfer of reducing gas are maintained. Reasonable temperatures and pressures are used which are less excessive than those used by previous workers, although they are maintained at above equilibrium values because of process kinetics.' It has also been found necessary to induce nuclea-tion and to control growth and agglomeration in order to get a powder product of suitable physical properties. Review of the Literature Muller, Schlecht, and Schubardt of I. G. Farbenm claimed a successive reduction of silver, copper, nickel, cobalt, and zinc from ammoniacal solution by applying progressively higher temperatures and hydrogen pressures. Metals produced by this technique were not pure, since no attempt was made to adjust the solution composition between the different reductions. It is doubtful that the zinc product contained any metallic zinc. The major contribution to the literature" was made by the Ipatiews,12 who prepared platinum, iridium, copper, nickel, cobalt, lead, tin, arsenic. antimony, and bismuth at often extreme conditions, up to the critical temperature of water (373"C), at 1500 to 7500 psi, for as long as several days. Even cadmium and zinc were claimed to have been observed in trace quantities precipitated together with basic salts. In the early experiments solutions were not stirred. Extensive formation of oxides and basic salts occurred. probably long before sufficient hydrogen could be supplied in the unstirred liquid to decrease the metal concentration in solution by reduction. The importance of hydrogen pressure was

Jan 1, 1957

By Dennis A. Clark, Brent Larsson

Tunnelling today is a lot more than drilling and blasting. The developments in drilling and blasting technique have made it pos¬sible to save costs both by increasing the advance per round and optimizing the demands on the final contour. Increasing the hole depth by using longer feeds and bigger dril¬ling rigs make the drilling time shorter compared to the set up time. It is important that the deeper holes are followed up by using a suitable cut. The most common cut in Sweden today is a parallel hole cut with one or more large holes; with a diameter corresponding to the hole depth and wanted advance per round. It is often specified that smooth blasting is to be carried out with a specific drill hole spacing. It is extremely rare, however, for specifications to be issued concerning the alignment of the raw of holes closest to the contour holes. It is very easy to ruin the effect of smooth blasting altogether by firing the rest of the round carelessly with an excessively high charge distribution. The drilling and blasting of the contour holes and the line of holes closest to the contour holes is therefore an extremely important part of any underground work. Accuracy and care in connection with the drilling of contour holes is also extremely important since it is possible to reduce the amount of overbreak, the result being more rapid mucking out, smoother and more durable surfaces and also less consumption of concrete for lining purposes.

Jan 1, 1983

By R. D. Carnahan, J. E. White

A study of dispersion strengthening in TD-Nickel (nickel plus 2 vol pct Tho2) was conducted employing microstrain techniques at ambient room temperature. It was found that optimum strength was due primarily to the incorporation of stored energy developed by a variety of thermal-mechanical treatments. The relatively low strength of the recrys-tallized condition implies that the dispersed particles themselves offer only token resistance to deformation. The development of resistance to large-scale recovery or recrystallization at temperatures near the melting point requires a more extensive sequence of strain-anneal cycles than does the development of optimum strength. A micro-Bauschinger effect was observed which appears to be related to the lattice resistance to the movement of free dislocations. The effect was nearly identical to that in pure nickel indicating that the presence of the dispersed phase and considerably increased dislocation density (stored energy) only alters the number or effectiveness of barriers. THE early stages of deformation of engineering materials can be conveniently studied by utilizing strain-gage techniques which permit resolution of strains less than 5 X 10-7 in. per in. for testing in four-point bending (Carnahan and white1). The present investigation, part of a continuing study on the very early stages of deformation, was designed to reveal the true role of a dispersed phase in promoting high strength in a commercially available dispersion-strengthened alloy. Although this technique has been used for some time to study microdeformation in pure metals and alloys, it has just recently received attention as a means of investigating dispersion strengthening. Studying the very early stages of deformation in alloys which depend upon a finely dispersed inert phase for strength may prove to be a very important method for a better understanding of these materials. It is essential to obtain considerable clarification of actual dislocation movement and the kinds of deformation barriers which exist before optimum properties can be designed into this type of material with any degree of confidence. Considerable research on a variety of dispersion-strengthened materials has resulted in two different schools of thought regarding the strengthening mechanism. One faction2-4 favors the idea that the particles themselves resist the motion of dislocations. The criterion for yielding is the fracture of the dispersed second-phase particles due to an array of piled-up dislocations. Other invesfigators5-a have shown that particles are effective primarily by allowing a greater buildup of stored energy or dislocation density through thermal-mechanical treatments in the composite than the pure matrix material. The particles themselves, then, are not exclusive obstacles, but the complex network of particles, dislocation tangles, subboundaries, and grain boundaries are strength determining. The development of such a complex dislocation network in SAP has been studied recently in some detail by Goodrich and Ansell. The ability of dispersion-strengthened alloys to resist softening or recrystallization is also of considerable importance; however, the criteria for maximum stability may not necessarily be those for maximum strength. In this study, in addition to the evaluation of the microstrain properties of TD-Nickel, it is felt that considerable clarification of the true dependence of strength and stability on the dispersed phase is shown. I) MATERIAL AND PROCEDURE TD-Nickel is a dispersion-strengthened alloy developed by the E. I. DuPont de Nemours Co., which contains 2 vol pct thoria (Tho2) in a pure-nickel matrix. The average ThO2 particle size is approximately 0.1 p and the interparticle spacing is less than 1 u. The material was supplied by DuPont in two conditions: hot-extruded bar stock, and stress-relieved cold-rolled sheet 0.025 in. in thickness. The bar was extruded at 2200°F from a cold-pressed and sintered billet. The sheet stock was prepared from the extruded material by a process involving ten or more 50-pct cold reductions by rolling with intermediate anneals at 1800° to 2000°F. Test specimens used in this study were prepared in the form of rectangular parallelepipeds measuring 0.375 by 1.375 in. in thicknesses ranging from 0.025 to 0.040 in. Samples prepared from sheet and extruded stock were mechanically polished before heat treatment and were handled with extreme

Jan 1, 1964

By A. L. Holmes

Significant technologic advances were made in open pit mining during 1973. The industry faced mounting problems on one front where expansion of stripping activities encountered enlarged public resistance and on another where manpower and materials were in short supply. These challenges, along with the challenge and opportunity to meet the increased demand for mining products including materials for energy production, placed a premium on technical developments and their application. The demands on technology also included the providing of facilities and methods to economically extract minerals from deposits of lower grade, lesser accessibility, and where other uses of land approached the value of its minerals. Detection of Failures in Slope Walls The Bureau of Mines has undertaken research directed towards providing a mine operator with the opportunity to take corrective action before a potential slide becomes a problem.

Jan 2, 1974

By Nicholas J. Grant, William H. Ferguson, Bill C. Giessen

Ta-lr alloys have been examined over the complete range of compositions using metallographic and X-ray techniques. The terminal solid-solubility limits, solidus temperatures, and intermediate phases were determined. There are four inter-mediate phases: o, tetragonal, analogous to a (Fe-Cr); 0,. orthorhombic; az, tetragonal; and a TaZr,, cubic, AuCu, structure. Of these, o and a, melt peritecticaLly, a, decomposes peritectoidally, and a TaIrs has a congruent melting point. Three peri-tectic and one eutectic reactions occur. 1 HE Ta-Ir phase diagram has not been treated in the literature. Intermetallic phases and terminal solid solubilities have been described and estimated.'-4 The previous findings have been confirmed in this work. A complete diagram with additional phases and solidus curves is presented. EXPERIMENTAL METHODS Starting materials were tantalum powder of 99.8 pct purity, supplied by the National Research Corp., Cambridge, Mass., and iridium powder of 99.9 pct purity, supplied by the Bishop Co., Malvern, Pa. Both powders were -200 mesh. Table I lists the analyses as given by the suppliers. A standard procedure was employed in making the alloy buttons, which was described in detail in Refs. 5 and 6, and which included repeated arc-melting of powder compacts and determination of the composition by the weight-balance method. This is especially justifiable due to the similar vapor pressures of tantalum and iridium. In the critical parts of the diagram, a spacing of 1/2 at. pct was used, based on premelted master alloy material. The observed structures and X-ray spectra were consistent with the composition sequence of the alloys. Table II lists the final alloy atomic percentages with the calculated percent error of composition. Cross sections representative in grain size and composition were selected for the study, as described in Ref. 5. Based on prior experience, no contamination from the tungsten electrode was considered. Temperature measurements were obtained using a Leeds and Northrup optical pyrometer and have been described extensively in Refs. 5 and 6. All heat treatments were made in the high-vacuum tantalum tube furnace mentioned in Ref. 5. Samples annealed in tantalum containers cooled from 1800" to 1000"~ in 5 sec; those annealed in ceramic crucibles cooled over the same range in 15 to 30 sec. The thermal treatments are listed in Table 111. All specimens were homogenized at 1735°C for 24 hr. Tantalum-rich compositions were treated in tantalum buckets. Iridium-rich compositions were annealed in tantalum buckets below the eutectic temperature of 1950°C; up to 2200°C, tungsten-lined tantalum baskets were used; and above 2200°C thoria crucibles were used. It was found that refractory oxides (in early stages of the investigation alumina crucibles were used up to 1800°C and thoria crucibles were used to 2400"~) give off minute amounts of oxygen and thereby influence the microstructure considerably, or react directly with the alloys.

Jan 1, 1963

By R. A. Ritter, J. P. Batycky

A numerical technique has been developed to permit estimating the pressure gradient associated with laminar flow of thixotropic liquids through long Pipelines. For this purpose the pipeline is divided into a number of radial and longitudinal increments within which rheological properties of the fluid may be considered as constant at any time. Then, provided only that the fluid flow curve is defined at every duration of shear, it is possible to predict the instantaneous pressure gradient at any cross-section along the pipeline for each desired flow rate and pipe size. The technique consists of an iterative integration of shear rate to establish the appropriate value of the wall shear stress at each location. Consistency of fluid in the increment is determined by the flow history of that increment, while the radial flow associated with variations in velocity profile is accounted for by adjusting the width and radial position of the increment. A number of pressure profiles, computed at each of several flow rates, provide a convenient basis for pipeline design and pump selection. INTRODUCTION In recent years considerable attention has been given to predicting pressure drop associated with the isothermal laminar flow of time-independent non-Newtonian fluids in pipes and annuli. 6,11,12 The approach generally has been to develop analytical relationships between flow rate and pressure drop based on simple constitutive models which hopefully provide an approximate description of the rheological properties of the fluid. Analytical solutions are highly desirable since the influence of all pertinent parameters can be readily determined. Unfortunately, however, this approach is restricted to simple flow geometries and- frequently leads to erroneous results due to inadequacies in the model. In certain cases a solution may be obtained through applying appropriate numerical techniques.l,14 For example, a digital computer program is available for predicting the velocity profile and pressure drop encountered by any Newtonian or time-independent non-Newtonian fluid flowing under laminar conditions in a cylindrical pipe or annulus.l In this paper the consistency behavior of the fluid need only be described in terms of basic rheological data. Analyzing flow systems involving fluids with time-dependent rheological characteristics is considerably more complicated since substantial changes in consistency may occur because of sustained shear action. This sensitivity to shear frequently persists for several hours. Consequently, variations in pressure drop and/or flow rate resulting from the aging process and addition of unsheared or partially sheared fluid to the system must be considered for purposes of pipeline design. This paper outlines a numerical method for predicting the transient and steady-state laminar flow behavior of a thixotropic liquid in a pipeline of arbitrary length (i.e., at a specified constant flow rate, the instantaneous pressure gradient may be determined at any time after start up and at any location along the pipeline). Several such pressure gradient profiles, computed at several flow rates, may be combined to produce a complete portrait of the system response. This flow portrait provides a reasonable basis for pipeline design and for selecting a suitable pump characteristic. TIME-DEPENDENT RHEOLOGICAL BEHAVIOR The most familiar time-dependent rheological properties are those exhibited by thixotropic liquids. Many of these materials, particularly thixotropic crude oils, generally display an apparent yield stress in that a finite pressure gradient is required to initiate flow. Then, under the influence of sustained shear at a constant shear rate, the consistency systematically decreases to some final limiting value. The shear stress obtained at

By Alan Morris

SEASON cracking of brass has received wide attention and there is a wealth of technical literature on the subject. Its causes are fairly well understood and means for its prevention are inexpensive and effective, .so that the frequency of failures from this source has diminished of recent years. But its sister phenomenon, the failure of annealed brass by reason of applied tensile stress plus a certain type of corrosion, has received less attention, though it has been responsible for occasional more or less troublesome cases of cracking of brass in service. The work described in the following pages was undertaken about two years ago to determine the relative resistance of various commercial brass mixtures to stress-corrosion cracking, and to learn something of the controlling factors. By stress-corrosion cracking we mean the cracking of brass free- from internal stresses by reason of applied tensile stress and simultaneous attack by certain corrosive agents. Rogers,1 in discussing a paper by Hatfield and Thirkell, says : "He had also applied a solution of mercuric salt to tensile test pieces of brass whilst they were under stress in the testing machine. At very moderate stresses such test pieces cracked, and very readily broke." Moore, Beckinsale and Mallinson2 subjected test pieces to simultane-us corrosion and tensile stress. In order to determine the minimum stress detectable in brass by the mercurous nitrate test, tensile samples were placed under stress and treated with mercurous nitrate solution. They found that brass stressed below a minimum did not crack.

Jan 1, 1930

By R. M. Brick

AN increased demand for information in regard to the effect of gaseous elements in steel has accompanied the recognition of the importance of grain size. Attempts to correlate grain-size characteristics with gas con-tent, particularly oxygen in solution or in the form of included metallic oxides, have not been universally successful. Certain definite effects of dissolved gases are recognized; specifically, the role of hydrogen in causing internal cracks or "flakes" and that of nitrogen in preventing excessive grain growth of ferritic chromium steels. When irregular behavior or properties are found in a well-known steel and no definite cause for the abnormality may be assigned on the basis of chemical and metallographic tests, dissolved gases are frequently blamed as the culprits. The solubilities of hydrogen1 and nitrogen2 in pure liquid iron are known but of the ternary systems, iron-alloying element-gas, only the Fe-Si-N3 and Fe-Cr-N systems have received attention and here the study was confined to liquid alloys. Krivobok4 published a curve show-ing the solubility of nitrogen in liquid Fe-Cr alloys but gave no informa-tion on the experimental procedure employed. The considerable experimental work reported on the Cr-N binary alloys has been reviewed by Hansen.5 It is generally agreed that the nitride CrN is a stable phase although the existence of nitrides within limited temperature ranges of stability, viz., Cr3N2 and Cr2N, has been disputed, Adcock6 and others7 have reported a eutectic between Cr and CrN at 1580°C., although the supporting evidence is not complete.

Jan 1, 1940

By Dick Whittington, W. R. Taylor

GENERAL In mid-1974, a representative of ARCO Petroleum Company walked into our Austin offices and asked for a permit for ARCO's first Clay West Mine site. This was the first in situ uranium mining permit issued in the United States. That initial permit, issued in January 1975, was for three acres. The four years since have been characterized by growth and change. Today there are 16 permits approved for approximately 1,540 production acres issued to five companies at eight sites in four counties. There are approximately seven additional permit applications being processed or on the verge of being submitted for an estimated 2,000 additional acres of production. As a rough gauge of the financial scope of this activity, at the typical 40 production wells per acre and an estimated $2,000/well, operators hale installed or committed $122 million for production wells. This does not account for the exploration and development wells installed to delineate the ore or the cost of processing facilities for extracting the uranium. HISTORY OF URANIUM MINING IN TEXAS Information I have concerning early in situ uranium mining activities is "sketchy" but the apparent first on-site test of in situ uranium mining was conducted between 1967 and 1971 at the Dueterstat site, north of Yorktown in Gonzales County, by City Service. Others ran tests at the Bruni site in Webb County and the Burns and Clay West sites in Live Oak County in the mid-70's. During this period, Texas Water Quality Board personnel in the central and district offices maintained a general surveillance of these various test activities. Regulation of in situ uranium mining was formalized with the issuance of a permit in January 1975 with the advent of ARCO's initial production scale (3 acre) effort in the Clay West area at the Moser mine site. Since 1975, the accelerating rate of mining and exploration activity is noticeable. There were 16 exploratory rigs operating early in 1977. This year, the rig count is averaging 46--a 287% increase. HISTORY OF LEGISLATION Paralleling this mining activity was state and federal legislation which subjected in situ mining to environmental regulation. The following is a brief chronology of the legislation that is directly or indirectly related to uranium mining. As most of you know, disposal wells are an integral part of most in situ uranium mines operating in Texas. They are used both during production and during aquifer restoration following production. The wells are regulated by the Texas Injection Well Act, enacted in 1961 by the Texas Legislature. In 1967, the Water Quality Act established the Texas Water Quality Board, and provided for the regulation of water quality by the so-called permit system. In 1969, the Solid Waste Act was enacted by the Texas Legislature. The legislation provides for control of wastes from manufacturing, mining, and agriculture. This Act regulated uranium surface mining activities until 1975 when the Texas Surface and Mining Reclamation Act placed responsibility with the Railroad Commission for uranium open-pit mining and surface mining of coal and lignite. In 1972, the Federal Water Pollution Control Act (Public Law 92-500) was passed. This legislation forms the legal base for the NPDES (National Pollutant Discharge Elimination System) and the subsequent point source effluent guidelines and standards. The November 6, 1975 issue of the Federal Register published interim final rules for Best Practical Treatment levels for effluent discharges from ore mining and dressing operations. Litigation was immediately initiated by eleven companies against these proposed rules, and they are currently being reconsidered for reissuance in 1979. In 1974, the Federal Safe Drinking Water Act (Public Law 93-523) was enacted. A part of this legislation is the Underground Injection Congrol Program. The regulations implementing this program have undergone various public hearings and it is expected that they will be published in the Federal Register before the end of 1978. In 1975, the Texas Surface Mining and Reclamation Act (Senate Bill 55), providing for the Railroad Commission's authority to require reclamation of surface mines, was passed. In 1977, an amendment to Senate Bill 55 was introduced that proposed to place regulation of in situ mining of coal, lignite, and

Jan 1, 1979

By Alan Morris

Season cracking of brass has received wide attention and there is a wealth of technical literature on the subject. Its causes arc fairly well understood and means for its prevention are inexpensive and effective, so that the frequency of failures from this source has diminished of recent years. But its sister phenomenon, the failure of annealed brass by reason of applied tensile stress plus a certain type of corrosion, has received less attention, though it has been responsible for occasional more or less troublesome cases of cracking of brass in service. The work described in the following pages was undertaken about two years ago to determine the relative resistance of various commercial brass mixtures to stress-corrosion cracking, and to learn something of the controlling factors. By stress-corrosion cracking we mean the cracking of brass free from internal stresses by reason of applied tensile stress and simultaneous attack by certain corrosive agents. Rogers,' in discussing a paper by Hatfield and Thirkell, says: " He had also applied a solution of mercuric salt to tensile test pieces of brass whilst they were under stress in the testing machine. At very moderate stresses such test pieces cracked, and very readily broke." Moore, Beckinsale and Mallinson2 subjected test pieces to simultaneous corrosion and tensile stress. In order to determine the minimum stress detectable in brass by the mercurous nitrate test, tensile samples were placed under stress and treated with mercurous nitrate solution. They found that brass stressed below a minimum did not crack. Dr. McAdam3 has investigated the effect of corrosion on the fatigue limit of brasses, among other materials. He directed a stream of either fresh or salt water against the specimen while it was undergoing fatigue test. The corrosion-fatigue limits thus determined may be considerably lower than the endurance limit without coincident corrosion. The exact

Jan 1, 1930

By Ian Wark

IT has been shown1 that in the absence of heavy metal salts, the nature of the alkali used to promote differential flotation-whether caustic soda, lime or sodium carbonate-is unimportant. The hydroxyl ion is the active depressant upon which differentiation depends, and the pH value determines whether a film of collector forms on any given mineral surface. Even when sodium cyanide is used in conjunction with alkalies, it is the pH value and not the nature of the alkali or its concentration that is important, for upon the pH value alone depends the fraction of the added sodium cyanide that is present as cyanide ion, which is the true depressant. When heavy metal salts become dissolved from partly oxidized ores, or are added intentionally as activators, conditions are different, and metallurgists have found that lime and sodium carbonate do not give identical results, even when added in amounts sufficient to produce the same pH value. In the few instances in which we had attempted to confirm this view, we had failed to do so, for, with nothing to guide us, we had inadvertently chosen solutions that gave contact curves of a "stand-ard type," which correspond to conditions of ready floatability. Now, however, we find that, in the presence of copper salts, and within a restricted range of reagent concentrations, the nature of the anions present is important, and that sodium carbonate does influence the results, apart from the usual effect due to its influence on pH value. With the recognition of this anion effect, and with the control of temperature already introduced,' it appears that the factors of major importance in connection with this set of reagents have been taken into consideration, and that the results obtained and the conclusions drawn from contact tests will be of more immediate value to the operator.

Jan 1, 1939

By W. Francis

OF THE methods that have been used for studying the chemical composition of coal, attack by reagents has not, in general, yielded much information. Most of the reagents used have been strong oxidants such as nitric acid or Schulze's solution. The use of a milder oxidizing agent, such as air at low temperatures, enables progressive changes in the character of the coal substance to be studied and thus helps toward an understanding of its constitution. British bituminous coals frequently have a banded structure. These bands (of four types) can be separated one from another and have been found to possess markedly different chemical characteristics, even when taken from contiguous portions of the same lump coal. It has been found convenient to give each of the ingredients of banded coal a distinctive name, more or less descriptive of its appearance, and the study of the chemistry of bituminous "coal" in England has resolved itself into a study of each ingredient separately. . The coal chosen for this work was taken from the Top Hard seam at East Kirkby colliery, Nottinghamshire, a detailed chemical analysis of which has been recorded by Baranov and Francis.1 The banded structure was well marked and the bands could readily be separated. The research was confined to the brilliant vitreous bands (vitrain), the dull hard bands (durain) and the "sooty partings" (fusain); for previous work had shown that the fourth type, to which the name clarain has been given, is intermediate in character, chemically, between vitrain and durain.

Jan 3, 1925