By Itavahn Alves da Silva, Izabela Diniz Duarte, Carlos Antonio da Silva, Varadarajan Seshadri

Mathematical modeling using computational fluid dynamics has been employed to assess the thermal losses in a steelmaking ladle. Thermal losses lead to thermal stratification and convective flow inside the ladle. The effects of preheating, mineralogical and physical characteristics of the lining as well as thickness of slag cover have been studied and the results obtained from application of the model have been discussed.

Jan 1, 2016

By Roberto Parra

The selective reduction smelting of Cu2O in Cu2O-FeOx-SiO2 melts has been studied at laboratory level, using as a feed a dead roasted calcine from a copper concentrate. The purpose of the study was to evaluate the kinetic and mechanisms of the indirect reduction with CO and the direct reduction with graphite from 1260°C to 1350°C. The reduction rate by CO was found to be 10-2 to 10-1 mole Cu2O m-2s-1. The graphite reduction macrokinetics for FeO and. Fe2O3 containing melts, was found to be a first order reaction with respect to the Cu2O concentration, with a kinetic constant of 104 to 10-3 s-1. The reduction rate was not sensitive to temperature nor to stirring, in the range studied. The measured reduction rate is almost one order of magnitude larger than the observed rate for the direct reduction of FeO.

Jan 1, 1999

By C. W. Whitten

Solis from an abandoned Pb battery processing facility were characterized prior to the selection of the extraction technique. Reflected light microscopy and electron beam methods were used to locate Pb-bearing phases and to quantify the compositions of the phases. It was found that the soils are composed primarily of quartz and feldspars with minor amounts of iron and titanium oxides. Lead is primarily present as an oxide or sulfate that is associated with the silicate minerals. Specific phases identified were PbO; Pb02; cerrusite, PbCO3; angleslte, PbSO4; galena, PbS; and magnetoplumbite, 2PbO3Fe2O3; or plumboferrite PbO2Fe2O3?

Jan 1, 1989

By Toshihide Takenaka

The management of radioactivated stainless steel from a terminated nuclear reactor will become an important subject in the near future. The separation of the elements in stainless steel should be effective to reduce the management labor. In this study, the separation of the elements in stainless steel by an electrorefining tcchnique was investigated in an aqueous solution. The electrochemical reactions of the elements in stainless steel werc studied by voltammetry and potentio-static electrolysis was carried out. A stainless steel anode was dissolved electro-chcmically with good anodic current etliciency in a chloride solution. The residue, where Ni was concentrated, was found on the anode after electrolysis. The electrodeposit in a stainless steel cathode consisted mainly of Fe and Cr and the Ni content in it was less than 0.5wt% under suitable condition. It is concluded that an electrorefining technique is effective for the separation of the elements in stainless steel.

Jan 1, 2003

By Charles A. Sorrell

Two red muds, two fly ashes, and several aluminosilicate minerals were subjected to direct treatment with concentrated H2SO4 at temperatures of 175°C and below. X-ray analysis showed that virtually all the sulfate reaction products remained in the solid residue because of their low solubilities in x SO Substantial portions of the Al2O3 Fe2O3TiO2, Na2O, and K2O components of the materials reacted to form water soluble sulfates, which were then removed by H2O leaching at 55°C. The solid residue after water leaching consisted largely of amorphous silica and, in lime bearing compounds, CaSO4, The reaction and leaching processes were effective in removing all or nearly all the Al2O3. Fe2O3, TiO2, Na2O, and in lime components in the fly ashes, red muds, china clay, bentonites, the nephelioe fraction of nepheline syenite, and a plaster insulating brick composed of anorthite and mullite. Reaction with potassium feldspar and petalite took place, with formation of alkali aluminum sulfates, but the reaction rates and yields were extremely low. Potassium feldspar can be heated with Na2O and x O in air at 700°C for 24 hours, or with CaO at 1000°C for 24 hours, after which the reaction product kaliophilite, nepheline, and leucite-like phases, prove to be very susceptible to H2SO4, reaction and H2O leaching, providing yields near 100% of the Al2O2 content. An alternative method of H SO treatment consists of heating the sample in a silica tube and passing H2SO4 vapor over it. Preliminary results indicate that this method can be effective in enhancing the kinetics of reaction with the Al O component of potassium feldspar and offer the possibility that formation of Al2 (SO ) Fe2(SO4)3 and TiOSO4 can be accomplished selectively by taking advantage of the fact that the upper stability limits of the respective sulfates in the presence of H2SO4 vapor will be different.

Jan 1, 1982

By Gordon Irons, Kevin Graham, Krishnakumar Krishnapisharody

Ladle or secondary metallurgy in steelmaking is an essential process step for the production of high-quality steel. Professor David Robertson was a pioneer in the modeling of these processes, in particular gas-metal fluid dynamic interactions and the rates of slag-metal reactions. This is now a highly active area of research, and some of the recent developments in this area will be reviewed.

Jan 1, 2014

By A. F. Giamei, F. Landis, M. O. Duffy, R. J. Mador

"The directional solidification of complex advanced gas turbine airfoils must be carried out without the nucleation of undesirable grains and with minimal shrinkage. Such problems are typically eliminated by using a number of mold design and process iterations. A more efficient approach is envisioned where a solidification model is generated and utilized to accelerate process development. Towards this end, the directional solidification (DS) of simple geometrical shapes in a crystal grower apparatus has been simulated with MARC finite element nonlinear thermal analyses.The finite element models of cylindrical (2D) and rectangular (3D) cross-section bars in the DS environment are presented. Temperature dependent properties, the impact of latent heat of fusion and a time-dependent radiation boundary condition constitute the more salient features of the MARC models. Solidification zone thermal behavior is predicted during the withdrawal transient for the specific case of nickel based superalloys grown in ceramic shell molds. Comparisons of analytical results with experiments demonstrate notable prediction accuracy. INTRODUCTIONSingle crystal and uni-directional crystal turbine blades require tightly controlled conditions if metallurgically and mechanically acceptable parts are to be produced. Gated blade geometry and process parameters must be precisely determined if incorrect grain structure, orientation and shrinkage are to be avoided. Since purely experimental development programs designed to evaluate these parameters can be excessively costly and time-consuming, an effort combining engineering analysis and verification by experiment has been initiated at Pratt & Whitney. Comparison of analytical predictions and measured data for geometries simpler than a turbine blade, namely cylindrical and rectangular bars, comprised the initial stage of this effort. Subsequent tasks involve modeling geometries of increasing complexity and ultimately the simulation of the directional solidification of the turbine blade, shown schematically in Figure 1. This paper summarizes the results of the initial stage of the effort."

Jan 1, 1986

By Shuqiang Guo, Gonghui Yang, Xingxing Zhang, Yuyang Bian, Song Chen, Weizhong Ding, Yinhe Liu, Lan Jiang

One of the most promising refractory materials for application is zirconia in melting superalloy. In this work, the properties and phase composition of magnesia partially stabilized zirconia ceramics (MgO-PSZ) under different sintering temperatures were systematically investigated. Commercial magnesia partially stabilized zirconia (MgO-PSZ) powders were selected as the starting materials. The magnesia partially stabilized zirconia phase composition was measured by X-ray diffraction (XRD), the density of sintered samples was tested by vacuum density instrument, the thermal expansion were obtained by thermal dilatometer from ambient temperature up to 1450°C, and the microstructures of MgO-PSZ were characterised by scanning electron microscope (SEM). The results indicated that the properties of thermal expansion, densification, microstructures and phase composition were significantly affected by sintering temperature. Densification was consistent with SEM micrographs of MgO-PSZ at different sintering temperatures.

Jan 1, 2015

By Toshiaki Tsuru, Takeshi Ohgai, Hisaaki Fukushima, Shigeo Kobayashi, Tetsuya Akiyama

"Electrodeposition behavior of Zn-Cr alloys from the methanol baths was investigated. In the methanol baths of low Cr3+ concentration, Cr (III) compound was incorporated in the deposits and no lusfrous Zn-Cr alloys was deposited. However, Cr was existed as metallic state in the deposits obtained from the baths of higher Cr3+ concentration. With an increase in water content in the baths, the chemical state of Cr in the deposits changed from metallic to trivalent state. Under the condition that metallic Cr can be electrodeposited, Zn deposition was significantly polarized to the potential of Cr deposition.INTRODUCTIONAn attention has been paid to Zn-Cr alloy plated steel sheet because of its excellent properties for body panels of automobile and electrical appliances [1]-[4]. This plating process can be operated using the sulfate solutions containing Cr3+ ion [1] - [6].In decorative single Cr plating, on the other hand, many attempts have been made to electroplate Cr from trivalent electrolytes, which is motived by environmental deficiencies of the presently used hexavalent process [7]. [8]. However, it has been reported that in the aqueous solutions the behavior of the electroreduction of 0 3+ is atypical due to the complicated nature of the chemistry and electrochemistry of cr3+ species [9]-[11]. Even in Zn-Cr alloy plating, it is difficult to codeposit metallic Cr with Zn in simple sulfate electrolytes [l]-[4], [12]. Therefore, it can be expected that the electrodeposition behaviors of Zn-Cr alloys as well as Cr are significantly changed when the electrodeposition is conducted in non-aqueous plating solutions.In this study, the electrodeposition of Zn-Cr alloy was conducted from methanol solutions to clarify the electroreduction mechanism of Cr3·-Cr0 in the alloy deposition process."

Jan 1, 2000

By Shunsuke Yagi

A surface alloying technique was investigated using alternating pulsed electrolysis in an aqueous solution containing a single metal component for the formation of an Fe-Cr layer on an iron substrate. In the process, the iron substrate was dissolved during each anodic polarization of the pulsed electrolysis, providing iron ions in the vicinity of the substrate, while the Fe-Cr alloy was electrodeposited during subsequent cathodic polarizations. A bright, flat, and crack-free Fe-Cr layer with a composition gradient was obtained using a solution containing a trivalent chromium component and a complex forming agent together with some supporting or buffering salts.

Jan 1, 2006

By Li Kaihua, Li Liang, Miao Qingdong, Wang Cong

The current process of production of titanium sponge involves the use of TiCl4 as a feed material and a huge amount of heat is generated during the magnesiothermic reduction process. For this reason, it is possible to agglomerate into a titanium lump with the partial high temperature. And, it is difficult to obtain soft titanium sponge with low content of impurities. In order to solve the current problems in the titanium sponge production process, process optimization experiments study of TiCl4 feeding speed, vacuum distillation temperature, system pressure and time control had been conducted for obtain high quality titanium sponge. Experimental results show that lower feeding speed can improve the output capacity of titanium sponge and softer products can be obtained. The product grade rate of titanium sponge improved significantly.

Jan 1, 2015

By Ole Rud Bendixen

Topsoe has developed a Wet gas Sulphuric Acid (WSA) process which effectively recovers SO2 in off-gases from non-ferrous smelters and roosters. The product is concentrated sulphuric acid of typically more than 96 wt% irrespective of SO, concentration in off-gas. The process does not generate any waste products or waste water and does not use any absorbents or other chemicals. In the process, up to 99.3% of the SO2 is converted catalytically into SO3, which reacts with water in the gas, hereby forming gaseous sulphuric acid. The acid is condensed in a WSA condenser of proprietary design. Excellent heat economy and practically no sensitivity to the water balance mean that no extra sulphur burning is required at any S02 concentration, The process is especially well suited for treating off-gases where the SO2 content is lower than approx. 5-6%, and it is a good alternative to a complete renovation of a smelter. However, also off-gas from flash smelter may be treated. The process has found good use in both molybdenum and lead roosters. An example from a molybdenum roaster in Chile shows that 97-98wt% acid is produced from a 2.3 % S02 gas. This plant is situated in the outskirts of Santiago and represented a major local source of SO2. The plan was started in May 1993.

Jan 1, 1996

By Kazuyoshi Shimakage, Shinji Hirai, Kenji Wada

"An amorphous zirconium oxide coating was prepared by the sol-gel process using zirconium tetra-n-butoxide on the surface of aluminum to improve the corrosion resistance to salt, acid and alkaline attacks. The coating films formed on the smooth aluminum substrates under UV-irradiation indicated an excellent corrosion resistance for salt, acid and alkaline attack tests. For example, the corroded area of coating film in salt attack test for 3600ks in the order of sol-gel coating· film< chromate film <boehmite film, and the sol-gel coating film had the best corrosion resistance. The coating film prepared on the coarse aluminum substrate by a boiling treatment after heat treatment at 573K also had greater corrosion resistance, and a water-avid surface appeared a contact angle of approximately 3°.IntroductionAs given in a previous paper1; a composite film consisting of a porous layer of anodically grown aluminum oxide filled with amorphous zirconium oxide and an amorphous zirconium oxide coating layer deposited thereon via the sol-gel process utilizing the dip-coating technique, was prepared to improve the alkaline corrosion resistance of aluminum. The alkaline corrosion resistance of these composite films was increased in the range of 24 to 50 times those of conventional anodic oxide films anodized in sulfuric acid. As a result, it was proved that heat treatment at 573K after dip-coating was an important process to .remove organic component from gel film and to accelerate the densification of coating layer. Furthermore, the effect of ultraviolet (UV) irradiation at ambient temperature on the densification of coating layer was also examined to lower the heat-treatment temperature2.Then, a sol-gel film prepared by UV irradiation at ambient temperature indicated that alkaline corrosion resistance of aluminum was superior in the range of 2.4 times to 2. 6 times that of the conventional composite film heated at 573K."

Jan 1, 2000

By Hsing Kuang Lin

Extraction of zinc from chloride solution with dibutyl butylphosphonate (DBBP) in Escaid 110 has been investigated. The distribution coefficient of zinc was found to be independent of equilibrium pH. This independence indicates that the mechanism of the extraction may be solvation. Slope analysis for the system of dilute zinc chloride solution reveals that two moles of DBBP react with one mole of zinc. A series of tests were conducted to bring DBBP to its full loading capacity and the analysis of the results confirms this stoichiometric factor of 2. Extraction isotherms were established by varying either the AIO ratio or the concentration of zinc in the aqueous feed. Both curves were found to be identical.

Jan 1, 1990

By Toshia Ishii, Jun Kubota, Noriko Kubo

"For steel continuous castings, it is essential to control molten steel velocity at the meniscus, since the velocity is closely related to surface defects on the resultant products. Argon gas is supplied with molten steel into the mold through the submerged entry nozzle to prevent nozzle clogging. In this study, to investigate the influence of argon gas on molten steel flow, a numerical simulation was carried out by a two-phase model. Simulation results indicate that as argon gas bubbles ascend near the nozzle by their buoyancy, they induce the molten steel flow with them and resulted a meniscus molten steel flow from the nozzle to the narrow face of the mold. This flow direction is opposite to the case without argon gas. The calculated data are compared with the experimental data. The comparison shows generally good agreement between the measured and the calculated data. IntroductionIn a steelmaking process, molten steel carried by a ladle is first fed into a buffer vessel called tundish. From the tundish, it is then fed into a continuous casting mold. Molten steel solidifies gradually in the mold (the primary cooling zone) forming a solidified shell. As the solidified shell is just thick enough to support the molten steel at the mold exit, it is withdrawn through the mold by pinch rolls. It is progressively thicken as it is further cooled with water sprays in the secondary cooling zone. At the end of guide roll zone, completely solidified steel is cut into desirable lengths. Schematic view of a typical continuous casting is shown in Figure 1."

Jan 1, 1999

By Jingyuan Wang, Hengyi Zhang, Peng Lan, Ruitian Zhang, Jiaquan Zhang, Yang Li

"For the determination of mould taper and wall thickness, a 3-D numerical model of ingot-mould-hot top system has been made to evaluate the related ingot solidification process and the final soundness. The effect of mould wall thickness and the taper of its hot faces on the thermal history and the as cast structure of steel ingot has been revealed through the numerical simulation. It is shown that the ingot soundness can be improved remarkably by increasing the mould wall thickness, which is possibly beneficial to the mould life as well owning to an improved mould thermal state. The mould taper is vital to the ingot soundness but much less coherent to the mould temperature profiles. Under given casting situations, a larger mould taper can lead to a less intensity of the shrinkage porosities at the top part of ingot.IntroductionIngot casting is still one of important processes for steel production, which is adopted especially for the supply of large-sized semi-products of high quality special steels. The understanding to the solidification process is vital to both the yield improvement of casting production and the quality control of steel ingots, such as their soundness and homogeneity.The ingot processing and service performance are closely related to its defects, such as porosities and pipes[1,2], which are the most common but serious defects during ingots casting. In the late 1960s, Mahadevan and Murthy et al.[3], Irani and Kondic[4] began to analyze criteria for the prediction of shrinkage porosities in light metal casting. In 1980s, Niyama and Uchida[5], Hansen and Sahm[6,7] et al have successfully presented some related porosities and pipes criteria for steel casting. At the same time, numerical solidification simulation was well developed and applied to ingot quality studies[8-10]. However, due to the quick development of continuous casting, less emphasis has been given to the further study on ingot casting process. There leaves much work to be made for the comprehensive understanding to ingot quality improvement and the mould design by the aid of modern solidification technology[11, 12]. In this paper, the effects of mould taper and wall thickness on its thermal history, ingot solidification and the final soundness are numerically studied through solidification simulation, which has been adopted in mould design and industrial production of both the mould and its steel ingot."

Jan 1, 2012

By Marcelo Mourao, Adolfo Pillihuaman, Alberto Nogueira, Cyro Takano

"The self-reduction is an alternative and promising process for production of pig iron because offers decisive benefits such as enhancing the reaction kinetic with decrease in fuel consumption and C02 emissions. The self-reduction mixture of iron ore fines, carbonaceous reducer and additives for slag forming components, without agglomeration, was tested in a laboratory rotary kiln. The additives for slag were defined for presenting two different estimated liquidus temperatures (1623 Kand 1773 K) to verify the effect of these temperatures on the iron-carbon nuggets coalescence process. These mixtures were tested at 1673 and 1773 Kin an experimental rotary kiln. After reduction-melting and coalescence processes the samples were disaggregated and the iron nuggets were classified by size. It was considered that nuggets larger than 7,93mm would be a good reference for coalescence index. Low liquidus temperature slag presented 37% of this larger fraction against only 13.5% for high liquidus temperature one. The low liquidus temperature slag would facilitate contact between the particles of iron-carbon in a rotary kiln, enhancing the coalescence.IntroductionThe slag composition usually depends on the reducer ash composition, the ore gangue, the binder composition and any fluxing material [l], and the mechanism of carbon transportation in slag that contains iron oxide reducible by carbon can be explained by the oxide reduction and the metal carburization. During carbon transportation, the carburized particle is transported to slag-metal interphases by the gravity effect, being assimilated by the metallic phase [2]. When the slag's iron oxide comes in contact with the solid carbon, it is immediately reduced, forming Fe particles and CO bubbles as it is shown in the figure l(a). The Fe particles are carburized by carbon particles; they are liquefied simultaneously in the carbon-slag interphase. The Fe-C liquid particles are transported from the slag-carbon interphase to iron-slag interphase as a result of slag flow, based on the surface tension difference (Marangoni effect), figure l(b). The Fe-C liquid particles coalesce on the iron surface and the carbon is immediately diffused in the iron as it is shown in figure l(c). The reduced iron is carburized continuously by repeated sequences [3]."

Jan 1, 2013

By Xiang-dong XING, Zhen-yang wang, Jian-Liang Zhang

Distribution behavior of titanium between CaO-SiO2-MgO-Al2O3-TiO2 and hot metal was studied between 1350 °C to 1600 °C. Experimental results indicate that the reaction temperature influenced the activity coefficients of titanium and resulted in the variation of equilibrium constant. Finally, the Gibbs free energy formula of titanium carbothermic reduction was fit out using the thermodynamic model of Wagner and congregated electron phase models.

Jan 1, 2015

By Takeshi Yoshikawa, Kazuki Morita, Kunitoshi Matsunaga

"In metallurgical grade silicon (MG-Si), most impurities mainly exist at the grain boundaries and distribute in silicon grains at extremely small contents. Grain boundary phases in MG-Si transform into liquid above the eutectic temperature, and migrate towards high temperature regions when heated under a temperature gradient. With the migration of all liquid phases in MG-Si to the surface, the impurity contents will be decreased less than their solubilities in principle.In the present work, the fundamental research was conducted to discuss the possibility for purification using the liquid phase migration technique. The purification limit was estimated by thermodynamic calculations, and metallic impurities were estimated to be effectively removed except for Fe and Al. The migration behavior of the liquid phase in the synthesized silicon substrate was investigated by unidirectional heating under infrared radiation at 1523-1548 K, and the proceeding of migration was confirmed. The migration velocity was 1.4--2.0xl0-7 mis, and found to be controlled by the liquid phase diffusion.IntroductionPhotovoltaic energy is one of promising energy resources in a sustainable society because of its inexhaustibility and cleanliness. Although the production and installation of solar cells have increased significantly during the last decade, the cost of solar cell installation is still high. To enable the widespread use of photovoltaics and for the photovoltaic electricity price to reach grid parity, a low-cost and abundant feedstock of solar grade silicon (SOG-Si) is essential. Recently, a modified Siemens process and a fluidized bed reactor process were developed to address the cost and energy issues associated with the conventional Siemens process. However, their cost reduction potential is limited because of the large energy consumption needed to convert silicon into gaseous compounds. Purification of silicon through metallurgical routes offers a promising way for producing SOG-Si from metallurgical grade silicon (MG-Si), because it enhances productivity and can also lower the process costs. Although several metallurgical processes such as directional solidification [l ], vacuum refining [2-4] and plasma oxidation [5-7], have been developed, processing times and refining efficiencies still have to be optimized."

Jan 1, 2013

By Jiang Fan, Liu Shi, Wang Haigang

Winter-time natural convection in gravel embankments has been suggested as a technique to provide passive cooling and thereby avoid thaw-settlement of roadways located in permafrost areas. Numerical simulation by finite volume method on the proposed model is perf9rmed using the software FLUENT. A gravels model, in which the embankment is composed of stones and air, has been adopted to investigate the temperature and velocity fields in embankment. Simulation results show that in summer, a weak clockwise circulation of the pore air extending throughout most of the embankment. The pore-air motion is very weak which results in relatively straight horizontal isotherm lines. And heat transfer is mainly maintained through conduction. But in winter, pore-air velocities are higher and multiple vortexes are formed in the embankment. Natural convection then becomes the dominant influence on the isotherm shapes within the embankment. As a result of low ambient temperatures exerted on the embankment surface during winter months, an unstable air density gradient develops within the embankment. This convection increases the heat flux out of the embankment. Therefore, the winter-time convection can further reduce the temperature of the foundation soil beneath the open-graded embankment. In addition, the effects of the size of the stones within the embankment have been analyzed and compared in the gravel model. It shows that in winter, 200mm stones lead to stronger vortexes in the embankment compared with those of 60mm stones. Consequently, the zone oflow-temperature beneath the embankment is extended.

Jan 1, 2004