By J. J. Talja

An investigation of oxidation of various nickel concentrates was carried out using differential scanning calorimetry (DSC). The aim of this study was to determine the ignition temperature and investigate other oxidation behavior of various sulfide-based nickel concentrates. Variables in the experiments were mineralogy, particle size and partial pressure of oxygen with temperature increasing linearly at 25 K/min from 323 to 1023 K (50-750 °C). The igni¬tion temperature was determined to represent the starting point of rapid oxidation. The reac¬tion enthalpies of the concentrates were determined and the amount of heat generated up to various time were used to calculate the extent of reaction. Mineralogical changes at various stages of oxidation were also investigated. For this purpose a second set of DSC-experiments were carried out in which each experiment was interrupted at a desired temperature between 673-873 K. From these tests the weight loss of samples were determined and changes in the individual constituent of sulfide minerals were analyzed. For pentlandite-based Ni-concentrates the ignition temperature was 705-710 K (approximately 435 °C). Pyrite was the first sulfide to oxidize. Reactivity of the violarite-based concentrate was greater than those of the pentlandite-based concentrates. The stoi-chiometry of pentlandite changed before ignition because of preferential oxidation of iron. Rapid oxidation of the pentlandite mineral occurred at about 823 K (550 °C). By 900 K about 90 % of the iron in pentlandite was converted to hematite, and NiS containing some iron was formed.

Jan 1, 1994

By James C. Barker

Recent investigations of a 55-km long trend of intrusive complexes on southern Prince of Wales Island have identified significant resources of Nb, Y, REE. U, Zr, and a host of potential by-product metals. The northwesterly trend comprises multi-phased sodic alkaline and peralkaline diorite, monzonite, syenite, and riebeckite granite. There are at least three significant deposit types recognized, two of which, 1) pegmatite dikes/vein-dikes that zone laterally from the intrusions and 2) concentrically zoned pegmatites, contain most of the lithophile metals. A third, epigenetic replacement-type mineralization, contains much of the U resource. Other deposit types with minor or unknown resource potential include diatremes, carbonatite, and placers. This report summarizes the deposit evaluations, characterizes the mineralization, and estimates the resources. To date a total of 40.7 million tons of mineralized material is estimated as indicated or inferred. Most of the Y203 plus REO is at a grade exceeding 0.5% and half of the Nb20S exceeds 0.125%. Tonnage estimates would likely be substantially lncreased with additional exploration. Mineralogy is generally fine-grained and complex, and consists of more than a dozen principal REE-Y-Nb-U-Th-Zr phases, the sum of which may compose up to half of the rock. Approximately half of the REE-Y content comprises the heavy yttrium subgroup which is uncommon compared to deposits elsewhere. Although the Alaskan deposits are likely subeconomic at today's metal prices and consumption levels. recent technological advances suggest future demand may increase.

Jan 1, 1988

By M. R. Baren

Unpublished results obtained by Baren on thermodynamic properties of sulfur in liquid Fe. Co. Ni. Fe-Co. Fe-Ni. and Co-Ni are reevaluated. correlated. and interpreted on the basis of recent developments in thermodynamics of alloys:. Existing reliable data are reviewed and compared with the? present results. Sulfur obeys Henry's law up to 0.04 mol fraction. and in this range the standard Gibbs energy of solution of sulfur is expressed as a linear function of temperature for each pure metal. The activity coefficient of sulfur in each binary metal solvent 1s correlated with the composition of alloy.

Jan 1, 1983

By Suresh Sundarraj

A diffusion mass transport model for predicting the microsegregation in a solidifying and coarsening dendritic mushy region of a binary alloy is presented. Two versions of this model are tested; one based on expressing the solute concentration in terms of mole fraction and the other on expressing the solute concentration in terms of mass fraction. On comparing previous model data sets and conditions, used in the analysis of Aluminum-Copper systems, a number of inconsistencies emerge. These inconsistencies are resolved on identifying a single set of data and conditions which take account of compositional density changes, "non-linear" thermodynamics and dynamic coarsening. An additional investigation is carried out to study the effect of assumed cooling mechanisms.

Jan 1, 1992

By H. L. Fraser

A review of the possibilities of performing microchemical analysis in thin sections using a combination of scanning transmission electron microscopy and energy dispersive spectroscopy of x-rays is given. Particular attention is paid to the factors that limit accurate analysis at the highest spatial resolution. As an example of the use of these techniques applied to a potential problem in minerals processing, the identification of iron pyrite and pyrrhotite particles in Illinois, Herrin #6 coal is presented.

Jan 1, 1981

By Daniel K. Kim

The charge for the copper refinery is a mixture of anodes produced at San Manuel from BHP source concentrate and copper purchased from external sources. Control of unwanted impurities in the tankhouse - is very important and beneficial. Currently available removal/recovery technologies were reviewed for the control of bismuth and antimony levels in the electrolyte. Recent studies have focused on solvent extraction (SX) technology and generated successful results for the removal and subsequent recovery of bismuth and antimony. The SX system employs the reagent, ACORGA SBX-50, in conjunction with a patented high chloride stripping system. The latter enables recycle of the eluant, avoiding the high costs associated with conventional systems, such as regeneration of resin. Concerns over potential transfer of organics and chloride ion to the electrolyte were readily addressed, solved and demonstrated using conventional, established technology. This paper describes the benefits of electrolyte purification, the flexibility afforded by the SX system, the operational practices necessary for maintaining adequate control of bismuth and antimony impurities in the electrorefining environment and possibilities for future development /exploitation of the Zeneca SX system at the San Manuel refinery.

Jan 1, 1998

By Roland Loewen

A review of the aqua regia method for the recovery of gold from jewelry shop wastes is given. Also outlined is a specialized procedure for the recovery of the silver that occurs in these wastes. A classic method for the recovery of platinum and palladium is, given. There is a brief review of other gold and silver refining methods. Environmental conditions are discussed and a few perhaps, new and useful processes ,are mentioned. References are by author or editor and are listed alphabetically. Suggestions for further information in the field of precious metals, are given in a final list.

Jan 1, 1989

By D. V. Hughes, J. R. Nyberg

"Since 1985, a comprehensive automation system has been installed at the Outokumpu Oy Zinc Plant, Kokkola, Finland. In leaching and solution purification special sample handling equipment, on-line analyzers and instruments, and a computer-based control system with duplicated supervisory stations have been installed. The system has enabled closer control of the process and more efficient use of labor. Since its installation recovery of zinc has improved, and use of zinc dust, steam, and water have decreased. The system has performed reliably. It includes optimizing programs and process study tools, which facilitate improving process performance. An expert system has been built-up to prompt process personnel to take appropriate action on the basis of process data. In electrolysis a similar system, based on extensive monitoring of the process and of production of zinc cathodes, is used to maximize- current efficiency by maintaining optimum conditions in the process. It is planned that in the future the control systems will be integrated and extended to cover the roasting plant and effluent control.IntroductionThe Zinc PlantThe Zinc Plant of Outokumpu Oy Metallurgical Division at Kokkola, on the West Coast of Finland, has grown from a 90,000 t/a plant founded in 1969 to become, with its present capacity of 170,000 t/a, one of the world's ten largest zinc plants. Especially since the completion in 1988 of a thorough modernization programme, it is also among the world's most modern.The Kokkola plant takes its raw materials from Outokumpu's own mines, Vihanti and Pyhasalmi in Finland, and Tara in Ireland, and from outside sources. Concentrates are roasted in two Lurgi fluid-bed furnaces, and the calcine is leached and iron removed by the Conversion process. Following this copper, cobalt, and cadmium are removed, and zinc is refined by electrowinning. The leaching and purification, and the cell-house are automated under computer-based control, and anode and cathode handling in the cell-house are mechanized and fully automatic."

Jan 1, 1989

By Dinabandhu Ghosh

The stability diagram of the ternary system Ti-C-O is drawn in the present work for four temperatures, 1473 K, 1573 K, 1673 K and 1873 K, showing the stability fields of TiC, Ti, TiO, Ti2O3 and TiO2. An analysis of the system reveals that it is not possible to produce Ti in a carbon-saturated system; instead, the stable product is TiC. However, Ti can be an equilibrium product in a carbon-unsaturated system at prohibitively low values of pCO and pCO2; for example, at 1873 K, these limiting values are: pCO = 10-6.76 atm and pCO2 = 10-13.36 atm, which, when exceeded, produce TiC and TiO respectively. The magnesiothermic reduction is examined through the stability diagram (log pO2 vs. 1/T) of the system Ti-Mg-O, drawn for a number of pMg values, presenting the pairwise stability fields such as Mg(l) + Ti(s), Mg(v) + Ti(s), MgO(s) + Ti(s), etc. The diagram shows that magnesium reduction of TiO to Ti is possible only at T < 1641 K with pMg = 1 atm and only at T < 1569 K with pMg = 0.5 atm. An experimental scheme for Mg vapor reduction of TiO2 is proposed in which an argon stream is passed over a Mg(liquid) evaporator at temperature T1 (say, 1234 K); the resulting Ar-Mg mixture at 1 atm is subsequently flown over a bed of TiO2 at temperature T2. A thermodynamic analysis establishes that complete reduction to Ti is possible and that the best results are obtained when T1 = T2.

Jan 1, 2006

By Junfu Chen, Jiann-Yang Hwang, Yong Zhou, Lijun Lu, Likun Lia, Jixiong Liu

The sheet-like NiS-ZnS heterostructured composites were prepared by the microwave hydrothermal. The fabrication of the heterojunctions broadened the range of light response of ZnS. The photoexcited electrons of ZnS migrated to the redox potential of NiS/Ni2S under visible light irradiation, which can facilitate the effective separation of photogenerated electrons and holes in space. The visible photocatalytic activity towards hydrogen production for NiS/ZnS nanosheet heterostructed composites without co-catalyst achieved 0.28 mmol h–1, and the quantum efficiency was up to 18.6% under the wavelength with 420 nm visible light irradiation.

Jan 1, 2015

By Veena Sahajwalla

The cupola furnace is a coke-fueled shaft furnace used as a primary melting unit in iron foundries. Control of chemical composition of the iron tapped from the cupola is a key factor in productivity and quality control. In an effort to develop a control model for the cupola, a fundamental approach based on physical and chemical principles has been taken to describe the melting process. The behavior of oxidation of the solid charge in the stack of the cupola has been studied. Sulfidation of the charge materials by sulfur-bearing components released to the furnace gases from the coke has been described. Carburization of metal droplets of iron and of steel in separate molten streams has been characterized. Finally, reactions with alloying elements in the hearth (well) of the furnace have been defined. These reactions have been described in a computer-implemented model developed to predict the composition of the iron tapped from the cupola. The model has utilized the thermodynamics and kinetics of the oxidation, sulfidation, and carburization reactions, including temperature and physical aspects, in the various zones of the melting unit. The model predictions have been compared favorably with operating results.

Jan 1, 1992

By S. L. Pohlman

Physical characteristics of possible importance in the acid leaching of Chrysocolla have been evaluated. Surface area studies and pore size distribution indicate: 1) a large surface area (350 m /gm); 2) an average pore size of 13 or 16 Å , depending upon use of the adsorption, or desorption, branch of the Type IV isotherm in the evaluation; ) the presence of a significant fraction of pores of size less than 15 Å determined by the accumulation surface area method. The initial structure is micro- crystalline on the basis of x-ray powder patterns; the silica leach residue is amorphous and has only 24 m2 /gm surface area, and loses integrity when dry. However, readsorption of copper onto the wet leach residue gives a product with integrity and 100 m2 /gm surface area. Visual observation of the leach residues supports evidence of a non-protective diffusion mechanism of leaching which is well correlated by the shrinking core model previously presented.

Jan 1, 1976

By L. Xia

Sodium silicate(s), also known as “water glass”, are one of the oldest and most widely used industrial chemicals. Its first use in Canadian operations can be traced back to around 1925, which coincided with early use of xanthates in mineral flotation. Silicate functions as a sulphide and non-sulphide gangue mineral dispersant, depressant and modifying reagent in grinding and flotation operations. It is believed that soluble sodium silicate promotes selectivity of value added sulphides against gangue minerals, resulting in both grade and recovery improvement. This paper seeks to link improved grade/recovery to the interaction characteristics of minerals and the sodium silicate. A systematic study was performed with individual mineral species, an artificially designed model ore and the feed ore from a copper flotation operation. The function of sodium silicate was evaluated in the context of colloidal chemistry and linked to mineral surface chemistry. Measurement of pulp rheology and mineral zeta potential identified that sodium silicate works as a dispersant. The dispersion is accomplished by increasing a mineral’s net surface charge, resulting in a change in slurry viscosity. Bench scale laboratory flotation tests suggest that better dispersion leads to a diminished interaction of chalcopyrite with gangue. The improved Cu grade and recovery then are likely in response to an increased accessibility to collector along with a linked increase in particle bubble attachment resulting in better separation efficiency. ToF-SIMS surface chemical analysis of the flotation samples found a higher proportion of sodium silicate on minerals from the flotation tailings relative to the concentrates. Moreover, attachment of sodium silicate appears to be mineral specific; the data indicates that sodium silicate favours the surface of gangue phases over the value sulphides.

By Mahesh C. Meyer Jha

AMAX has developed a chloride refining process to produce pure nickel and cobalt metals from mixed sulfide .precipitates, Metal chloride solutions, generated in a hydrochloric acid leaching step and purified in a solvent extraction circuit, are converted to metal oxides .and HCI gas by pyrohydrolysis. A pilot plant consisting of a 30-inch diameter fluidized bed reactor and other ancillary units was designed, constructed, and operated for over one year. Process design was aimed at minimizing energy consumption, maximizing conversion efficiency, and achieving simplicity of operation and control. The operation provided valuable information on process scale up parameters, process control strategies, and materials of construction., Several process variables such as bed temperature, solution composition, solution feeding system, bed particle size distribution, and fines recycle system were investigated to determine their effects on process efficiency and the physical and chemical characteristics of the product.

Jan 1, 1985

By E. J. Peterson

Oil shale retorting induces mineral and chemical reactions to occur on the macroscopic and microscopic levels in the kerogen-bearing marlstone. The nature and extent of the reactions is dependent upon process variables such as maximum temperature, time at temperature, atmosphere, and raw shale composition. This report describes the investigation of the mineral, chemical, and trace element release properties of spent shales retrieved from an experimental in situ retort at Occidental Oil Shale, Inc. &apos;s Logan Wash site in Garfield County, Colorado. Correlation between mineralogy of the spent materials and the mobility of major, minor, and trace elements are indicated, and relationships with important process parameters are discussed. The progress .of carbonate decomposition reactions and silicat ion reactions is indicative of the processing conditions experienced by the shale materials and influences the mobility of major, minor, and trace elements when the solids are contacted by water. Shale minerals that are exposed to the extreme conditions reached in underground retorting form high temperature product phases including akermanite-gehlenite and diopside-augite solid solutions, kalsilite, monticellite, and forsterite. The persistence of relatively thermally stable phases, such as quartz, orthoclase, and albite provide insight into the extremes of processing conditions experienced by the spent shales. Leachate compositions suggest that several trace elements, including vanadium, boron, fluoride, and arsenic are not rendered immobile by the formation of the high-temperature silicate produce phase akermanite-gehlenite.

Jan 1, 1981

By D. Donald Downey

Pilot Testing Ion Exchange Resin (IEX) can go from very simple beaker testing to complicated column testing. Space velocities, regenerant quantities, loading capacities, ion leakage, are all terms that get accumulated together to prove or disprove a resin’s (or resins’) ability to load a single ion (or specific set of ions). Not getting all the resin’s operating parameters correct will disqualify (or at least skew) the results. Laboratory tests for capacity, moisture content, bead size, metals fouling, etc.—what does it all mean? At last count, there were over twenty-five separate ion exchange resin tests (analyses) that were available to end users. Standard testing procedures identify the resin properties but more specific procedures can be used to identify problems with equipment operation. Then, there are the costs to consider; simple cation resin testing (moisture content, total capacity and bead integrity) is in the $200/sample range. However, add to this Chatillon, Russian Ball Mill Test, HIAC particle size, metals and % regeneration test procedures and the lab work can increase to over $1000/sample. In this paper, the author will explain the “must-do” pilot and test procedures and why they are important and the key to understanding how resin performs ion exchange.

The oxidation of zinc vapour plays a very important part in the operation of the Imperial Smelting Process. The kinetics of the reoxidation of zinc vapour by carbon dioxide and water vapour onto quartz and zinc oxide substrates is qualitatively understood and this pertains to the conditions found as the gases are being transferred from the furnace to the splash condenser. However, re-oxidation also occurs in the shaft of the furnace where the solid substrates are sinter and metallurgical coke. It was found that there was a threefold increase in the rate of oxidation on sinter, compared to quartz and a 30 to 300 increase in rate on the coke. This was attributed to the high surface area offered by these materials.

Jan 1, 2003

By J. B. Winter

The present Inspiration Consolidated Copper Company Smelter/Acid Plant complex located near Miami, Arizona, was designed and built specifically to conform to the ambient air quality standards imposed by the Federal Clean Air Act of 1971. The present plant replaced a facility which had been in operation since 1915. The electric furnace, siphon converters and acid plant complex were commissioned in May, 1974 (1). At that time, the Plant was considered to be one of the most extensively monitored and instrumented facilities of its kind in the world. Several control areas were located in close proximity to the controlled process, in addition to so-called central control rooms in the Smelter and Acid Plant. The control rooms were staffed with officials below the foreman level. Instrumentation consisted of conventional analog devices, except for a computer used in monitoring ambient air environmental conditions and limited use of programmable logic controllers. The harsh service conditions prevalent in the plant rendered a significant portion of the instrumentation unreliable and, in many cases, inoperable. Failure of the facility to obtain the total sulfur collection for which it was designed was, in part, due to serious inadequacies in control system logic and sulfur recovery averaged 79% in the early years. After careful study of the smelting process, engineering hardware and high labor cost inherent in the organizational structure, management made a judgement decision to convert to centralized control of the process with high level supervision 24 hours per day. A distributed digital control system with supervisory arid data acquisition/information reporting computers was selected to satisfy the requirement of central control. Operations are now controlled and coordinated from a primary control room in the Smelter and a satellite control area in the Acid Plant.

Jan 1, 1983

By Knut H. Bech, Stein Tore Johansen

"The collision efficiency for small particles relative to 2D spherical bubbles in a developed turbulent flow field were calculated applying an adopted version of the CPD program FLUENT. The turbulence field was related to bubble size and fluid properties. The results were compared with analytical theory. The turbulence intensity was found to be the most important single parameter for collision efficiency. Effects of boundary layer thickness and particle diameter were discussed. IntroductionRemoval of inclusion particles from melted aluminium can be facilitated by means of a rotor system that supplies kinetic energy and gas bubbles to the floating metal. At the surface the inclusions adhere to the surface dross or slagg which is removed at regular intervals by the operators. When applying computational fluid dynamics (CFD) to model such a system, one experiences difficulties with the large range of turbulent length-scales encountered, from the large geometrical scales of the rotor and container, through the bubble size and down to the particle diameter. A mathematical model for the complete system will be both complex and require an extreme spatial resolution. Another way of dealing with the problem is to model the micro-scale phenomena separately and apply the results to create a model for the macroscopic system. In a previous work [12] we addressed these problems and developed a procedure for calculating turbulence enhanced flotation to bubbles. It was found that turbulence may have a profound effect on the collision rate of particles to idealized bubbles. In this study we recognize that only a fraction of the total turbulent kinetic energy generated by the rotor's work on the liquid metal may contribute to enhanced flotation. By using a model spectrum for the turbulence, the fraction of turbulent energy in eddies smaller than the bubble diameter is calculated. A twodimensional CFD model was then constructed to calculate the collision efficiency between particles and bubbles of various sizes."

Jan 1, 1999

By B. Mishra

The application of various bydrometallurgical, pyrometallurgical and electrochemical processes in the extraction, purification and production of radioactive metals as well as the use of various materials, eg. metals and alloys, ceramics, polymers, etc. in the process, construction and handling equipment in the nuclear industry has generated a large stockpile of radioactively contaminated waste material and scrap metal which can not be directly discarded, recycled or considered for long-term storage due to its volume and potential hazards, without the separation of radionuclides. This paper reviews the emerging methods that have been &apos;investigated and suggested for dealing with some of these wastes&apos; and scrap material. The separation technologies studied for the recovery of radioactive components from the pyrometallurgical and electrochemical processing wastes have been discussed in details with results from some of the recent theoretical and physical modeling work as well as the data obtained? from the actual waste treatment. Specific processes shall be described in terms of its advantages and limitations. These emerging separation technologies are being considered by the US Department of Energy as alternatives for dealing with the issues of environmental management [EMI&apos; and decontamination and decommissioning [D&D].

Jan 1, 1996