Search Documents

By Cesar Garban

The samples of the washings are characterized of the ore for physical, chemical and metalurgical properties for representivity. the optimum values are determined for the recuperation of gold of the washings of the gold ore from the zone El Callao, Venezuela by acidic solutions of thiourea of the following parameters: Ph , contact time, composition of the liquid mixture, ratio of solid to liquid, grade of liberation, in an apparatus designed for contacting solid powder of the mineral with liquid solution of thiourea mantained in suspension by bubles of compressed air. The experimental results showed that the velocity of lixivation in primier time of (20) minutes is rapid and practically 2/3 part of the reaction is completed. For experimental design of parameters, the optimum conditions of recuperation of gold determind in this experimental investigation are:

Jan 1, 1999

The direct removal of lead ions from D2EHPA-kerosene using metallic zinc as the reducing agent was evaluated. The electrochemical process, called galvanic stripping, is a potential alternative stripping technique when standard chemical methods are not adequate. Four parameters found to be important in the rate of lead removal were studied in a factorially designed experiment. The variable evaluated included D2EHPA concentration, temperature, zinc surface area and solution agitation. Temperature and surface area were found to be the most significant, while agitation and D2EHPA concentration had less influence on the reaction. An activation energy of 22.5 Kcal/mole was calculated indicating a chemically-controlled process. The reaction was also sensitive to the concentration of oxygen in the system. The zinc required was considerably in excess of stoichiometry, possibly due to the dissolution and redeposition of lead: In general, the results were encouraging and demonstrated that lead impurities could be removed from D2EHPA using cementation type reactions.

Jan 1, 1995

By Takaaki Ishikawa

The distribution equilibria of lead, zinc and copper between CaO-Si02-Ah03 melts and liquid copper were measured at 1623K under a controlled H2-C02 atmosphere. The distribution ratios were plotted against the oxygen partial pressure, and reasonable oxide forms dissolved in the melts were estimated from the slopes of the plots. The activity coefficients of zinc oxide (ZnO), lead oxide (PbO) and cuprous oxide (CuOQs) increased with increasing slag basicity, defined by Xcao /XSiO, The temperature dependence of the activity coefficients was also measured.

Jan 1, 2003

By P. G. McCormick

The refining of rare earth metals by the direct solid state reduction of their respective chlorides during mechanical alloying has been studied. Erbium and gadolinium were synthesised by milling their respective chlorides with calcium. The mechanical alloying of SmC13 with calcium resulted in partial reduction of SmC12. Examination of the milled powders using X- ray diffraction and analytical electron microscopy has enabled characterisation of product structure and morphology. The synthesis of Fe17Nd2 by the mechanical alloying of NdC13 and Fe with calcium has also been studied. The Fe17Nd2 phase forms during heat treatment of the mechanically alloyed powder.

Jan 1, 1992

By Hui Zhang

The leaching behavior of palladium powder in aqueous solutions containing NaCI or N'H4Cl was investigated. Cupric ion was used as an oxidant for the dissolution reaction. The effect of a number of leaching parameters such as temperature, concentration, stirring speed and surface area on the leaching rate was studied. The leaching system containing chloride and cupric ion was found to be very effective for the dissolution of metallic palladium. Based on the experimental results the overall leaching rate was believed to be controlled by a chemical reaction step. The dissolution rate of palladium was found to be first order with respect to the concentration of cupric ion and second order with respect to the concentration of chloride.

Jan 1, 1996

By Kang-In Rhee

Nonferrous metal recycling not only provides energy saving and environmental benefits but also is a significant factor in the supply of various types of metals used in our society. Recycling plays an important role in establishing the sustainability of materials. The total amount of recycled nonferrous metals by weight accounts for less than 5% but their value is larger than 50% compared to ferrous metal recycling which consists of about half of the total metal recycling in weight. This paper describes trends and typical achievements in nonferrous metal recycling and overviews the present and future of nonferrous metal recycling technology and business in Korea.

Jan 1, 2006

By Takaaki Ishikawa

The distribution equilibria of lead, zinc and copper between CaO-Si02-Ah03 melts and liquid copper were measured at 1623K under a controlled H2-C02 atmosphere. The distribution ratios were plotted against the oxygen partial pressure, and reasonable oxide forms dissolved in the melts were estimated from the slopes of the plots. The activity coefficients of zinc oxide (ZnO), lead oxide (PbO) and cuprous oxide (CuO0.5) increased with increasing slag basicity, defined by XCao/Xsio2 The temperature dependence of the activity coefficients was also measured.

Jan 1, 2003

By Yong J. Kim, J. M. Park

"Solid/melt interface shape during continuous casting process has a strong influence on the resulting microstructure of the ingot. The interface shape is primarily governed by the heat flow condition between the molten metal and mold (or container). The roll of the microstructural transition resulting from various solid/melt interface shapes is discussed using the Sn-22.6wt%Pb alloy. Three different types of mold such as cold mold, resistantly heated mold, and electromagnetically heated mold were used to generate those interfaces having different curvatures. Experimental measurements of complete temperature profile along the axis and surface of the ingot during downward continuous casting are presented to determine the solid/melt interface geometry. The results provide an explanation of the ingot property with emphasis on microstructure.IntroductionA large scale of continuous casting process of alloys often has a rather deep V channel type of solid/melt interface resulting from a limited heat flow condition. As a result, the deep V type solid/melt interface shape entraps defects such as pores and inclusions and also creates canter segregation. In order to reduce the defects concentration, electromagnetic stirring(EMS) mechanism has been applied to the melt in the channel[l]. Speith and Bungeroth introduced first experimental EMS device to the continuous caster in 1952.[2] Today, with wide ranges of benefit, a large variety of such technique is available. Electromagnetic field on the melt can be divided into three aspects. First, eddy current is induced on the metal surface by alternating magnetic field with high frequency, which results in heating the metal. Second, electromagnetic body force which is generated by the magnetic field and the eddy current reduces the melt pressure on mold or support the melt not to contact with the mold[3,4,5]. This force is used for electromagnetic casting process(EMC). Finally, it causes stirring in the melt. Many research efforts have been done on the EMC process to improve surface quality of slab[6] and control meniscus shape where three phases such as melt, solidified metal, and mold powder coexist[7,8]. However, the eddy current heating effect on the surface of the ingot was less considered. It is worth noting that induced eddy current on the surface of slab melts the solidified shell and thus changes the heat flow condition between the mold and melt. Mold heating effect was first proposed by A. Ohno[9] and its processing conditions were identified in details[ 10, 11]. The so-called Ohno process is based on the fact that by keeping the mold temperature slightly above the melting temperature of the liquid, no grain can be nucleated on the mold wall[12]."

Jan 1, 1998

By Gordon Irons, Kevin Graham, Krishnakumar Krishnapisharody

Ladle or secondary metallurgy in steelmaking is an essential process step for the production of high-quality steel. Professor David Robertson was a pioneer in the modeling of these processes, in particular gas-metal fluid dynamic interactions and the rates of slag-metal reactions. This is now a highly active area of research, and some of the recent developments in this area will be reviewed.

Jan 1, 2014

By Marisa Di Sabatino, Michael Phan Knudson, Mari Juel, Eivind Øvrelid

"A p-type Czochralski silicon ingot doped with boron was characterized for resistivity, minority carrier lifetime, interstitial oxygen, and metallic impurities. Analyses show a peak in resistivity and a dip in lifetime both occur 5 cm from the top of the ingot crown. This peak in resistivity deviates from the expected trend based on Scheil's equation for boron distribution. High concentration of interstitial oxygen in this area suggests that other oxygen-related defects, such as thermal donors and precipitates, may also be present here, and the observed peak in resistivity and dip in lifetime could be attributed to such defects. The low lifetime of 15-30 µs at minority carrier density of 7.5 x 1014 cm-3 is likely due to copper contamination.IntroductionSolar energy resources vastly exceed all other alternative energy resources, ensuring that solar power must play a crucial role in the evolving energy market. The economic viability of solar power in competition with other energy resources depends upon finding efficient, cost-effective, reliable, and controlled methods for solar cell production. In this regard, minimizing waste (such as material with unsuitable electrical properties that hinder solar cell performance) is a vital component of making solar cell manufacturing cost-effective. Impurities affect electrical properties of solar cell silicon in different ways (i.e. [1, 2, 3, 4, 5, 6]). In this work we focus on the role of oxygen and metallic impurities. Understanding oxygen impurities in silicon is critical to solar cell development because oxygen has been attributed with influencing critical electrical properties including resistivity and minority carrier lifetime and thereby potentially hindering solar cell performance or rendering material unsuitable for solar cells.[1, 2] Furthermore, oxygen is a common impurity in the standard type of solar cell silicon, Czochralski (CZ) silicon, due to diffusion of oxygen from the silica crucible into the melt during crystallization. [7] This study investigates the effects oxygen impurities have on the electrical properties of p-type CZ silicon."

Jan 1, 2013

By S. Yin, A. Bogno, H. Henein, P. Natzke

Impulse Atomization (IA) (a single fluid atomization technique) was used to rapidly solidify Al- 4.5wt%Cu and Al-4.5wt%Cu-0.4wt%Sc under argon atmosphere. In addition to the IA-generated droplets, the same technique was used to produce strips by Spray Deposition (SD) of the same alloys on a copper substrate with and without oil coating. The rapid solidification microstructures were analyzed using Scanning Electron Microscopy (SEM). From the SEM images, the amount of eutectic and the secondary dendrite arm spacing (SDAS) were measured. These SDAS results lead to the estimation of cooling rate. The eutectic fraction coupled with the metastable extension of the solidus and liquidus lines of Al-Cu (Sc) phase diagram lead to the estimation of primary and eutectic undercoolings. A comparison of the solidification path of the droplets and the strips was done as well as the analysis of the effects of scandium.

Jan 1, 2015

By Anne Kvithydl

Printed circuited boards contain considerable quantities of valuable metal, while also containing many environmental pollutants making them unsuitable for landfill. In this study the decomposition of common plastics used in printed circuit boards were studied. Polytetrafluoroethylene (PTFE), polyvinyl chloride (PVC) and polyethylene (PE) were heated in both CO, and argon atmospheres using a thermo-gravimetric furnace (TG) coupled to a mass spectrometer (MS). Soda ash Na,C03 and baking soda NaHC03 were used as reactants. The degradation temperatures and evolved gases are presented for single plastics and mixtures. Mixed plastics are shown to behave as a sum of the individual plastics. The mass loss temperature is the same in CO, and argon. However, less residue is formed when heated in CO,.

Jan 1, 2008

By Yuanyuan Zhang, Patrick J. Masset

"The reduction of FexO in slag is one of the fundamental reactions in iron and steelmaking technology, including the blast furnace process (BF). Experiments on the reduction reaction of iron oxide using CaO-SiO2-Al2O3-FexO-C mixtures were carried out using thermogravimetric analysis (TGA) under reducing conditions at temperatures up to 1100°C. The composition of the primary slag was chosen so that the FexO concentration varied between 0 and 75 wt % and the CaO/SiO2 ratio being kept constant to 0.90. From the TGA curves recorded isothermally at different temperatures the kinetic parameters of the iron oxide reduction were determined.IntroductionIn blast furnace the iron ores and coke are charged in layers from the top. The reduction of iron oxide by coke is one of the fundamental reactions in the blast furnace process. Although a great amount of work has been done on the topic of reduction of composites [1, 2, 3], gasification of carbon [4, 5] and reduction of iron oxides by CO [4, 5, 6], the mechanism of reduction in iron oxide - carbon powder mixtures is not fully understood. Fruehan [1] and Rao [2] studied the reaction rate of the reduction of iron oxide by different types of carbon and concluded that the reaction mechanism is controlled by the oxidation of carbon at temperatures up to 1200°C. Rao [2] studied the reaction of hematite with graphite as carbon source up to 1080°C. An activation energy close to 300 kJ/mol was calculated within the temperature range of 950°C to 1087°C. In his study, Fruehan [1] determined the rate of reduction of Fe2O3 and FeO by coal, coke and coconut charcoal as carbon sources within the 900°C to 1200°C temperature range. He found that the reduction of Fe2O3 by carbon occurs in two stages and that the reduction of Fe2O3 to FeO is faster than that of FeO to Fe. This is due to the fact that the CO2/CO equilibrium ratio is higher, and hence, the rate of oxidation of carbon is faster. Fortini and Fruehan [3] have studied the reduction reaction of wustite by graphite and wood charcoal. They found that the wustite reduction can have a significant effect on the overall rate of reduction in composites at high temperatures or in the presence of a large excess of carbon. The calculated activation energy of the reduction reaction by wood charcoal was close to 368 kJ/mol, while the activation energy of the reduction reaction by graphite was 444 kJ/mol."

Jan 1, 2011

By William E. Torres

The Southern Peru Limited smelter, in Ilo, operates two reverberatory furnaces, seven Peirce-Smith converters, one Teniente Converter, two casting wheels and a single contact acid plant. The Teniente Converter was commissioned in August 1995 and was designed to smelt 744 dry metric tons (820 dry short tons) of concentrate per day. The process off-gas is collected in a water-cooled hood, cooled in a spray chamber, and cleaned in a Joy electrostatic precipitator for further treatment in the Acid Plant. This paper presents the current Teniente Converter operating practices and control philosophy. Relevant improvements and modifications to achieve a 379 day campaign without tuyere replacement and a daily average smelting rate of 862 dry metric tons (940 dry short tons) of concentrate are discussed.

Jan 1, 1998

By E. Açma

Sivas-Divrigi flotation plant has a capacity of 90,000 tpy. Beneficiation of the tailings of iron ore magnetic separator seems to be attractive, because of its Cu, Co, and Ni contents. In the experimental work, sulfidic flotation concentrate is produced from these tailings. A roasting-leaching-H2S precipitation procedure is used to treat this concentrate, containing 0.55% Cu, 0.51% Co, 0.74% Ni, and 0.027% Zn. Sulfatizing roasting is carried out in a rotary furnace at 690°C. Roasted product is leached with 10 gpl HzSOl at 70°C and 30% pulp density. For the precipitation of desired metal, H2S is bubbled through the concentrated solution of repeated leaching, under controlled temperature and pH. Final metal recoveries of 91% Cu, 91% Co, and 50% Ni, and 92% Zn are attained. Roasting gases with their 13% SO2 content are suitable for H2SO4 production and the leach residues can be integrated with the iron ore processing plant as they contain 57.4% Fe and very low non-ferrous metals.

Jan 1, 1993

By Xiang-dong XING, Zhen-yang wang, Jian-Liang Zhang

Distribution behavior of titanium between CaO-SiO2-MgO-Al2O3-TiO2 and hot metal was studied between 1350 °C to 1600 °C. Experimental results indicate that the reaction temperature influenced the activity coefficients of titanium and resulted in the variation of equilibrium constant. Finally, the Gibbs free energy formula of titanium carbothermic reduction was fit out using the thermodynamic model of Wagner and congregated electron phase models.

Jan 1, 2015

By Hong Ro Lee, Seang Suk Cho, Byung Sun Chun, Chang Whan Won

"The preparation of Al203-SiC-TiC composite powders was studied by SHS process using silica (source of Si02) powder instead of Si which is expensive. And, aluminum powder was used as reducing agent of silica and charcoal activated was used as carbon source. Effects of the molar ratio in raw material mixtures and compaction pressure and initial temperature of reactant on the products and combustion process were studied. The most important variable affecting the synthesis of Al203-SiC-TiC was the molar ratio of carbon. The combustion reaction generated in powder state without preheating. But the unreactants exist in the product on all molar ratio. When the preheating temperature is over 400 °C, the combustion reaction was able to be generated in pellet state. Without preheating, the combustion reaction was possible by Ti02 addition. The optimum condition in this system was the molar ratio of Si02:Ti02:Al:C=2.5:0.5:4:3.1. INTRODUCTIONCeramics have demonstrated a capability as a cutting tool, especially in competition with WC-Co cermets (ceramic-metal composites) as inserts for metal turning and milling operation. The advantage of ceramics compared with carbides is retention of high hardness, strength, and chemical inertness to temperatures in excess of 1000 ·c . This allows use of the ceramics at much higher machining speeds than can be tolerated by carbides. However, the ceramics have lower toughness than the carbide materials, and have only been used successfully in the limited operations of turning and milling. There are several classes of cutting tools. The addition of TiC or PSZ, or both, and reinforcement with SiC overcame the poor fracture toughness and thermal-shock resistance that limited Al203 use in the past [1]."

Jan 1, 1998

By L. Lewczuk

A detailed mineralogical and liberation study was performed on the iron ore mill products from the Scully concentrator of Wabush Mines, Newfoundland. Automated image analysis techniques were applied to deter-mine grain size distribution and liberation of all mineral components of the ore. As a result of the study it was indicated that iron recovery can be improved and the Mn minerals reduced in the iron ore concentrate by (a) increasing spiral middlings, (b) regrinding the middlings, and (c) separating the Mn minerals from the iron minerals in the reground middlings.

Jan 1, 1988

By Takeshi Yoshikawa, Kazuki Morita, Kunitoshi Matsunaga

"In metallurgical grade silicon (MG-Si), most impurities mainly exist at the grain boundaries and distribute in silicon grains at extremely small contents. Grain boundary phases in MG-Si transform into liquid above the eutectic temperature, and migrate towards high temperature regions when heated under a temperature gradient. With the migration of all liquid phases in MG-Si to the surface, the impurity contents will be decreased less than their solubilities in principle.In the present work, the fundamental research was conducted to discuss the possibility for purification using the liquid phase migration technique. The purification limit was estimated by thermodynamic calculations, and metallic impurities were estimated to be effectively removed except for Fe and Al. The migration behavior of the liquid phase in the synthesized silicon substrate was investigated by unidirectional heating under infrared radiation at 1523-1548 K, and the proceeding of migration was confirmed. The migration velocity was 1.4--2.0xl0-7 mis, and found to be controlled by the liquid phase diffusion.IntroductionPhotovoltaic energy is one of promising energy resources in a sustainable society because of its inexhaustibility and cleanliness. Although the production and installation of solar cells have increased significantly during the last decade, the cost of solar cell installation is still high. To enable the widespread use of photovoltaics and for the photovoltaic electricity price to reach grid parity, a low-cost and abundant feedstock of solar grade silicon (SOG-Si) is essential. Recently, a modified Siemens process and a fluidized bed reactor process were developed to address the cost and energy issues associated with the conventional Siemens process. However, their cost reduction potential is limited because of the large energy consumption needed to convert silicon into gaseous compounds. Purification of silicon through metallurgical routes offers a promising way for producing SOG-Si from metallurgical grade silicon (MG-Si), because it enhances productivity and can also lower the process costs. Although several metallurgical processes such as directional solidification [l ], vacuum refining [2-4] and plasma oxidation [5-7], have been developed, processing times and refining efficiencies still have to be optimized."

Jan 1, 2013

By J. Etay, S. Daugan, Y. Fautrelle

"New type of electromagnetic parametric instabilities arising at the free surface of liquid metal in the presence of a low frequency magnetic field are presented. First, the mechanism of the instability is analysed in an idealised case. Then, the experimental device working with mercury is described. Various shapes, both regular and irregular, of free surface are found. A experimental stability diagram is obtained. Measurements of the deformation performed on photographs are compared with physical orders of magnitude.IntroductionWhen a liquid metal pool of electroconductivity a is submitted to an A.C. magnetic field B = B0 cos mt, electrical currents j are induced in the liquid metal and interact with the applied magnetic field to create electromagnetic body forces F = j x B. Those Lorentz forces comprise both a mean value (time average) and an oscillating part. Those forces are widely used in many metallurgical processes to stirr a liquid metal or to control its free surface, e. g., in aluminium continuous casting or electromagnetic levitation problems (1-3). When liquid metal free surfaces are submitted to AC. magnetic fields, the shape of those interfaces may interact with the applied field and leads to a various instabilities. A review of these instabilities may be found in Fautrelle (4). That instabilities may be a problem for the control of processing as electromagnetic levitation or quasi-levitation."

Jan 1, 1999