By A. Tanaka, K. G. Carroll

The existence of local room-temperature plastic flow in germanium, which has been a subject of controversy for nearly two decades, has recently received renewed attention, albeit no more agreement than hitherto. Phenomenologically one major facet of the problem has been reduced to the question whether or not indentation can be effected in germanium without the introduction of cracks. That plastic flow can be induced at room temperature by fracture appears to have been rather convincingly demonstrated recently by Suzuki and Kamada and by Noble and Henisch.1 The literature contains both direct and incidental references to Vickers and Knoop indentations showing no cracks, within resolution of optical microscopy. Recently, however, following a controversy on the subject,2,3 johnson4 made a study of indentations produced by spherical indenters and concluded that these are accompanied by cracking. This study in-

Jan 1, 1969

By G. F. Comstock

A serious disagreement as to the effect of titanium on the hardenability of steel exists in published references to this subject. Kramer, Hafner and Toleman reported1 that acid-soluble titanium decreased the hardenability, with multiplying factors less than unity according to Grossmann's system for calculating hardenability from the composition. Crafts and Lamont, on the other hand, showed2 how titanium increased the hardenability, with multiplying fdctors up to nearly I.; for about 0.1 per cent titanium, though reducing the hardenability with higher titanium. Their data, however, were obtained almost exclusively from steels containing more than 1.4 per cent manganese, and thus should be considered as applying mainly to manganese steels. Likewise, the results of Kramer, Hafner and Toleman regarding titanium are subject to the limitation that although they eliminated the effect of the insoluble titanium compounds from their calculations, they did not make a similar correc- tion for the carbon that was combined with titanium and therefore occurred in a similarly ineffective form. It is suggested by the literature referred to that titanium may have different effects on hardenability, depending on the mode of its occurrence in the steel. The different effects on strength, ductility, etc., have already been discussed by the author.3 In the present discussion some comparisons, on the basis of hardenability as revealed by the Jominy end-quench test, are given between three titanium and two non-titanium steels heat-treated in the same ways, and between other titanium steels heat-treated in several different ways. Comparison of Plain-carbon, Vanadium and Titanium Steels The five steels used for these experiments were cominercially melted and rolled products received in the form of 1.5-in. rounds from three different mills. Their analyses are given in Table I. Steels 2, 3, and 4 are from the same basic electric heat1 containing 0.009 per cent of phosphorus and the same amount of sulphur. They were made by adding aluminum and low-carbon ferrotitanium to different ingots. No. I is a plain carbon

Jan 1, 1947

By G. F. Comstock

A serious disagreement as to the effect of titanium on the hardenability of steel exists in published references to this subject. Kramer, Hafner and Toleman reported1 that acid-soluble titanium decreased the hardenability, with multiplying factors less than unity according to Grossmann's system for calculating hardenability from the composition. Crafts and Lamont, on the other hand, showed2 how titanium increased the hardenability, with multiplying fdctors up to nearly I.; for about 0.1 per cent titanium, though reducing the hardenability with higher titanium. Their data, however, were obtained almost exclusively from steels containing more than 1.4 per cent manganese, and thus should be considered as applying mainly to manganese steels. Likewise, the results of Kramer, Hafner and Toleman regarding titanium are subject to the limitation that although they eliminated the effect of the insoluble titanium compounds from their calculations, they did not make a similar correc- tion for the carbon that was combined with titanium and therefore occurred in a similarly ineffective form. It is suggested by the literature referred to that titanium may have different effects on hardenability, depending on the mode of its occurrence in the steel. The different effects on strength, ductility, etc., have already been discussed by the author.3 In the present discussion some comparisons, on the basis of hardenability as revealed by the Jominy end-quench test, are given between three titanium and two non-titanium steels heat-treated in the same ways, and between other titanium steels heat-treated in several different ways. Comparison of Plain-carbon, Vanadium and Titanium Steels The five steels used for these experiments were cominercially melted and rolled products received in the form of 1.5-in. rounds from three different mills. Their analyses are given in Table I. Steels 2, 3, and 4 are from the same basic electric heat1 containing 0.009 per cent of phosphorus and the same amount of sulphur. They were made by adding aluminum and low-carbon ferrotitanium to different ingots. No. I is a plain carbon

Jan 1, 1947

By J. H. Smith, H. W. Paxton

X HE recent investigation of Butler, McCabe, and paxton' on the vapor pressure of manganese gas in equilibrium with Mn-Fe alloys has been extended to include the iron-rich solutions and alloys in the two phase equilibrium region. The study of the phase equilibrium by Kurnakov and Troneva2 and the extensive reviews of the Mn-Fe system by Hansen,3 and Hellawe114 are not in agreement with regard to the location and extent of the equilibrium between the solid phases of fcc y and complex P in the temperature range above the eutectoid temperature of approximately 975Kwhere 0 decomposes to y and bcc a. An evaluation of the existing equilibrium data is confronted with the conflicting results presented by various investigators who used techniques requiring a quenching treatment to retain the high-temperature equilibrium or encountered temperature hysteresis during thermal analyses. The difficulty of suppressing the transformation of the manganese-rich concentrations of the y-solid solution during quenching has been well etablished.' To avoid this uncertainty the phase equilibrium was investigated at temperature by measuring the partial pressure of manganese gas in equilibrium

Jan 1, 1962

By R. F. Lynch, J. D. Wood

The Al-1.0 pct Mg alloy 565 7 was studied using optical microscopy and electron microprobe X-ray analysis. Constituent particles were found to exist inter-dendritically in the as-cast material in a region of precipitate free a -aluminum. Five phases besides a fine precipitate and a-Al were identified in the cast structure: Fel3, Fe2Al7, Mg2Al3, CUMgAl2, and Cu2FeAl7. Thermal treatments conducted for 100 hr at 1180°, 1130°, 1080°, 1030°, 980°, and 880° F revealed a general dissolution and spheroidization of the in-terdendritic constituent network observed in the cast structure. The principal constituents present in the thermally treated structures were FeAl3 and Fe2Al7 with the relative amount of Fe2A17 to FeAl3 increasing with a decrease in the treatment temperature. The phases Present in the wrought structure were identical to those observed after the thermal treatments, with the constituent particles strung out in the direction of rolling. ALLOY 5657 is a nonheat-treatable commercial purity Al-1.0 pct Mg alloy utilized extensively because of its bright finishing characteristics. This investigation was conducted to determine the constituents present in 5657 alloy, and to study the effect of extended thermal treatments on morphology. Numerous studies have been carried out to establish the equilibrium diagrams for various aluminum systems,1-3 with phase identification based on X-ray analysis, morphology, and the etching response of relatively large particles. Phragmen4 conducted a study of the phases in aluminum eutectic systems and compiled a "corrected" table of etching responses, drawing on his work plus that of Schrader,5 Keller and Wilcox,6 and Mondolfo.7 A review of the original work of Keller and Wilcox, and Mondolfo, which was concerned with the constituents found in commercial alloys, reveals that in numerous cases their etching responses differ from those reported by Phragmen and from each other. These inconsistencies may occur because a specific constituent will react to a given etch in a varying manner depending upon its size, the elements dissolved in the phase, the other constituents surrounding a phase, and the solute content of the matrix. Work with a commercial orientation was conducted on alloys 2024 and 3003 by Sperry8,9 and on alloy 3003 by Barker,10 where the relationship between the phase diagram and the nonequilibrium structure of an alloy was examined. Backerud11 investigated the A1-Fe binary system and found that at high cooling rates the equilibrium eutectic reaction forming a-A1 and FeA13 is replaced by another lower temperature eutectic reaction forming a-A1 and metastable FeAl6, a constituent first identified by Hollingsworth et al.12 Most of the above mentioned studies were conducted on materials having a significantly greater alloy content than 5657 alloy, where the relatively small size and sparse distribution of second phase particles hinders the process of identifying constituents. EXPERIMENTAL PROCEDURE Material with a composition as given in Table I was examined in the as-direct chill cast, hot rolled and cold rolled conditions, and after thermal treatment of the cast structure. Thermal treatments were terminated by a water quench. Microscopic examination was conducted under various lighting conditions following the application of standard etchants as specified in Table 11. A semi-quantitative electron microprobe X-ray analysis was conducted for Al, Mg, Fe, Cu, Si, Zn, and Ti. RESULTS AND DISCUSSION Microstructure of the As-Cast Material. Particles of second phase material were found to exist inter-dendritically, principally in regions of precipitate free a-Al, as illustrated in Fig. 1. Adjacent to the ingot edge was a region of inverse segregation, resulting in an increased amount of second phase material containing large sized particles which aided in phase identification. Phase Identification. Cast Structure. Five phases besides a-Al and a fine precipitate were identified using optical microscopy and electron microprobe X-ray analysis, as presented in Tables II and III, respectively. FeA13 and Fe2A17 are often found with Fe2A17 forming a sheath around the core of FeAl3, resulting from an incomplete peritectoid reaction. These phases have a nearly identical appearance under white light, although they are easily differentiated under crossed polarizers, as characteristically illustrated in Figs. 2(a) and 2(b), respectively. Microprobe analysis con-

Jan 1, 1970

By Ivan E. Goodner, Charles H. Fulton

The subject of the constitution of copper-iron mattes has received considerable attention in recent years by Keller,' Belles,2 Hofman,3 and Gibb and Philp.4 Still more recently Friedrich, Röntgen, Wiedmann, Heyn and Bauer, and Leroux have published, in some instances, elaborate researches on the various systems of the sulphides, and the snlphides and their respective metals, which enter into the constitution of mattes, and have added very greatly to the knowledge of the subject. The work of Friedrich has been especially fruitful. But to' date no effort has been made to correlate the data obtained in the latter researches and apply them to the study of the product called " matte," which is made in such large quantities by copper- and lead-smelters. In this paper we propose to determine, by metallographic and chemical means, the constitution of copper-iron and copper-lead-iron mattes in the light of the recent data above mentioned. We do not discuss copper-nickel mattes or speisses (artificial arsenides). The paper is divided into three sections: I. A review and discussion of the various binary systems of the metallic sulphides, and the binary systems of various metals and their respective sulphides entering into the constitution of mattes; also a discussion of the physical properties of these sulphides. II. A description of the results obtained from the chemical and microscopic examinations of the samples of copper-iron and copper-lead-iron matte obtained from various plants.

Jan 1, 1909

By Alan Morris

Season cracking of brass has received wide attention and there is a wealth of technical literature on the subject. Its causes arc fairly well understood and means for its prevention are inexpensive and effective, so that the frequency of failures from this source has diminished of recent years. But its sister phenomenon, the failure of annealed brass by reason of applied tensile stress plus a certain type of corrosion, has received less attention, though it has been responsible for occasional more or less troublesome cases of cracking of brass in service. The work described in the following pages was undertaken about two years ago to determine the relative resistance of various commercial brass mixtures to stress-corrosion cracking, and to learn something of the controlling factors. By stress-corrosion cracking we mean the cracking of brass free from internal stresses by reason of applied tensile stress and simultaneous attack by certain corrosive agents. Rogers,' in discussing a paper by Hatfield and Thirkell, says: " He had also applied a solution of mercuric salt to tensile test pieces of brass whilst they were under stress in the testing machine. At very moderate stresses such test pieces cracked, and very readily broke." Moore, Beckinsale and Mallinson2 subjected test pieces to simultaneous corrosion and tensile stress. In order to determine the minimum stress detectable in brass by the mercurous nitrate test, tensile samples were placed under stress and treated with mercurous nitrate solution. They found that brass stressed below a minimum did not crack. Dr. McAdam3 has investigated the effect of corrosion on the fatigue limit of brasses, among other materials. He directed a stream of either fresh or salt water against the specimen while it was undergoing fatigue test. The corrosion-fatigue limits thus determined may be considerably lower than the endurance limit without coincident corrosion. The exact

Jan 1, 1930

By Frederick C. Hull, Robert F. Mehl, Robert A. Colton

IT is known that pearlite forms from austenite by a process of nucleation and growth, and that the rate of formation of pearlite may be described by a rate of nucleation and a rate of growth 12 The manner in which these two quantities operate to produce the observed isothermal reaction curve has been analyzed in a paper published in 1939 3 Two types of process were described (I) that in which nucleation occurs at the grain boundaries of the parent phase, with the nodules growing toward the centers of the grains, initially as hemispheres and then after impingement as roughly radial-columnar structures, and (2) that in which nucleation occurs generally, with the nodules growing to full spheres until impingement with other growing nodules restricts growth Both cases are met in the formation of pearlite from austenite (Fig 1),2,3 the former, occurring near the knee of the S-curve has been named "grain-boundary transformation," and the latter, occurring at temperatures near AeI, has been named "group-nodule transformation " In developing our knowledge of the factors that determine the rate of formation of pearlite from austenite, it is important''' to obtain data on the rate of nucleation and the rate of growth of pearlite Such data, when obtained near the knee of the S-curve, will furnish information of use in understanding the actors that affect hardenability, when obtained at higher temperatures, such data will be useful in understanding the behavior of steels that during heat-treatment react to pearlite 2 It is the purpose of this paper to present data on the rate of nucleation and the rate of growth of pearlite in dependence upon composition, grain size, temperature,, and the degree of homogeneity of the parent austenite The studies are restricted chiefly to plain carbon commercial steels PREVIOUS DATA ON RAID OF NUCLEATION AND RATE OF GROWTH Data on the rate of nucleation and the rate of growth of pearlite have been published by Scheil and Lange-Weise,5 by Mirkin and Blanter,6,7 by Mehl,1 and by Dorn, De Garmo and Flanigan22 It is difficult to interpret the data, for in most cases too little information is given on austenitizing temperatures and times, the state of homogeneity of the austenite (presence or absence of carbide, etc ), austenite grain size, and mode of formation of pearlite at the temperatures given

Jan 1, 1942

By Y. C. Liu, H. Margolin

Investigation of martensite habit plane in water-quenched Ti-Mn alloys was carried out in the range of manganese contents between 4.35 and 5.25 pct. On the basis of 22 measurements, the poles were observed to fall into two groups, indicating the existence of two habit planes. The Miller indices of the poles close to these two groups were found to be <334>ß and <344>ß. TITANIUM has an allotropic transformation at 882.1° ± 0.5C1 by which the high temperature ß (body-centered cubic) phase changes to a (hexagonal close-packed) phase. It is well known, as in the case of low carbon steel, that the unalloyed high temperature ß phase cannot be retained no matter how rapid the cooling rate. However, the addition of alloying elements usually lowers the transformation temperature continuously and stabilizes the ß phase to a temperature much lower than the allotropic transformation temperature in pure titanium. A typical example of this behavior is found with manganese-alloying of titanium. Fig. 1 shows the titanium-rich Ti-Mn equilibrium diagram as established by Battelle Memorial Institute.&apos; The addition of manganese lowers the ß transus line and the eutectoid reaction takes place at 550°C, the eutectoid composition being 20 wt pct Mn. However, upon quenching to room temperature from the ß field, the ß phase can be completely retained with much less manganese, see Fig. 2. If the composition is less than that required to stabilize the ß phase completely, a plate-like structure, similar to that of martensite in other alloy systems, appears as shown in Fig. 3. Much lower alloying content merely intensifies the amounts of these transformed structures, as shown in Fig. 4. This paper presents the results of an investigation of the habit plane of these martensitic structures in Ti-Mn alloys. Experimental Procedure Investigation of the pole of a given platelet was made using the two-surface method of analysis." In order that a given martensite trace on two surfaces be readily recognized both at low and high magnifications, it is desirable that only a small amount of martensite be present. From a review of the data obtained at Battelle Memorial Institute4 on quench hardening in Ti-Mn alloys and the results of Duwez" on transformation in Ti-MO alloys, it was decided that the most appropriate Ti-Mn composition for this study would be about 6 pct Mn. A group of alloys containing from 3 to 10 pct Mn was made to bracket this composition. The choice of the 6 pct alloy was apparently proper, since it was later learned that approximately 5.5 to 6 pct Mn is required to stabilize the ß phase on water quenching.

Jan 1, 1954

By R. F. Mehl, G. V. Smith

THE decomposition of austenite in steels, because of its immense practical importance, has been subjected to extensive study in recent years from the point of view of the mechanism of the process.1-3 Although much information has been acquired a number of questions, principally of theoretical interest, remain. One is that of the atomic-crystallographic mechanism by which each of the various reaction products forms. The isothermal reaction products of the eutectoid decomposition in plain carbon steels (to which this study is restricted) have conveniently been classified in three general groupings-pearlite, bainite, and martensite. Of these several products, pearlite and martensite have been studied extensively, but bainite has received only scant attention. As a result, the mechanism of the formation of pearlite and that of martensite are now fairly well understood while a great deal of uncertainty exists regarding bainite. PEARLITE Pearlite forms from austenite by the precipitation of alternate platelets of cementite and ferrite, which grow into the austenite matrix.2-5 The rate of reaction may be described in terms of a rate of nucleation and a rate of growth 2 3 Mehl and Smiths have attempted to determine the lattice relationships existing between the ferrite in pearlite and the parent austenite. Using a pole-figure method of analysis, it was found that a limited number of ferrite orientations resulted from the decomposition of a single grain of austenite; it was not possible,[ ]decide between two assumed ideal relationships, both of which appeared to account for the experimentally determined pole figure. It was definitely shown, however, that the relationship obtaining was quite different from that determined for the proeutectoid separation of ferrite.7 No attempt was made to determine the habit plane (matrix plane to which the precipitate lies parallel) of the pearlite lamellae. Belaiew8 earlier had stated that the number of directions assumed by the pearlite lamellae in a single grain of austenite was 12 (no details were given) and concluded wrongly, as Mehl and Smith&apos; have pointed out, that the lamellae delineate the {210} planes of ferrite.* MARTENSITE It is known that martensite is a transitional constituent of body-centered tetrag-

Jan 1, 1942

By Bradley Stoughton

[Secretary&apos;s Note.—TO avoid repetition of foot-notes, references to authorities are made in this paper by means of figures, referring to a numbered list in the appendix.—J. S. 1 Introduction. This paper gives the results: first,, of a research into the somewhat extensive literature of titanium; and second, of a series of original tests upon the effect of titanium on iron castr ings. New investigations have also been made upon the effect of titanium on steel, but I hope to treat this subject in an independent paper at some later date, and, therefore, will not discuss the experiments in detail here. The combined results of this study, which extended over a period of more than two years, can be briefly summarized as follows : 1. Steel or cast-iron, in which the titanium is properly proportioned, and which has been properly treated, is improved in strength, toughness, and durability against wear, such &apos;as, for example, the wear of railroad-rails, of steel and chilled-iron rolls, car-wheels, etc. 2. These improvemerits seem to be caused, not so much by the direct effect of titanium on the metal, as by its cleansing influence in removing harmful impurities, such as oxygen and oxides, nitrogen, occluded slags, and perhaps also sulphur. It appears also to reduce segregation, which would contribute to the same end. 3. In order that its effects may be fully realized, the treatment of steel or iron with titanium must be correctly performed. There are a few simple, but essential, details to be observed; if they are neglected, the best results cannot be expected. To illustrate by an example: A series of tests on cast-iron

Jan 1, 1913

By Harrison Schmitt

SINCE the U. S. Geological Survey published the data on the Central Mining District collected by Lindgren and Graton1 and by Paige2 much new information has been obtained by development and mapping, but none of it had been published until recently when Kniffin3 published on Fierro, Lasky4 on the Ground Hog mine, Thorne5 on Santa Rita and Landon6 filed a thesis on the Fierro-Hanover-Santa Rita area at the Uni-versity of Chicago. During the years 1927-1930 much of the writer&apos;s time was spent in mapping the geology and ore deposits of this district, particularly in the area of the zinc deposits at Hanover. Some of the data collected are presented here. Previous publications have been freely drawn upon and additional data used that were generously supplied by L. M. Kniffin, Wilfred Wright and Gerald Ballmer. Thanks are due Augustus Locke, Samuel G. Lasky, Kniffin, Wright and Ballmer for suggestions and critical readings of the manuscript, and to the Empire Zinc Co. (a subsidiary of the New Jersey Zinc Co.) for the privilege of publishing material compiled largely at its expense. The relation of the Central. or the Santa Rita-Hanover-Fierro district to the Silver City district is shown on Paige&apos;s geologic map in the Silver City folio.7 Granodiorite porphyry and quartz-monzonite porphyry

Jan 1, 1933

By Eric Jette

THE unusual physical, electrical and magnetic properties of the iron-nickel alloys has given rise to a voluminous literature. This work will be reviewed critically in "The Alloys of Iron and Nickel," a monograph of the Alloys of Iron Research Series, soon to be published. In what follows we shall therefore confine ourselves to those of the earlier investi-gations that involved the use of X-ray crystal-structure methods. The earliest X-ray work on the iron-nickel system was by Miss Andrews1. Using the powder method of X-ray analysis purely as a means of identifying the phases present, she located a region between 20 and 30 weight per cent nickel in which body-centered and face-centered phases coexisted. No lattice constants nor details of heat-treat-ment were reported. Bain2 also reported some qualitative observations. McKeehan3 made a systematic investigation over the whole of the system, giving many of his alloys four and some five different heat-treatments. In alloys furnace-cooled from 900° to 950° C. he found two coexisting phases between 0.15 and 30 per cent nickel. The precision of the lattice-constant measurements was low in comparison with what can be obtained today.. Even for alloys of the same heat-treatment, differences in the constants were often between two and ten parts per thousand. In regions where no change of lattice constant with heat-treatment should occur, differences of the same order of magnitude were found. Since the maximum change in the lattice constant of nickel with change of composition is only about 2 per cent of the constant for pure nickel, these variations in the constants for a given alloy cause the points

Jan 1, 1936

By E. A. Farrell

A comprehensive survey is made of the status of the asbestos industry as it relates to marketing the product. Included are descriptions of the various types of asbestos and the grading and classification systems used. The uses of asbestos, distribution practices, and types of ore bodies are all related to marketing. World production, the producers and their capacities and world consumption for 1966-67 are summarized and statistical data are included. Asbestos is a general term describing a family of fibrous minerals of the serpentine and amphibole mineral groups. Asbestos has a long history going back to the time of the Egyptians, when it was used as a lamp wick. The commercial mining of asbestos started in Canada, Russia, and Africa in the 1800&apos;s, and the first asbestos products were made in Italy and Russia. The five main types of asbestos are: chrysotile, accounting for 95% of the total mined, amosite, crocido-lite, anthophyllite, and tremolite. Canada, Russia, and Africa are the major producers of asbestos. The commercial utility of asbestos was at first based on the heat resistance of the fibrous mineral in the form of packing, at the start of the industrial revolution. Its current utility is based more on its ability to reinforce binders such as portland cement, rubber, and plastics. Its inertness to the chemical nature of most binders is unique. Most important is its ability to maintain its reinforcing utility when the product is exposed to weather and soil conditions as in asbestos cement boards and pipe, and heat, pressure, and chemical exposure as in brake linings and gaskets and packings. The mineral asbestos is also unique because its fibrous form permits it to be spun and woven to cloth or formed into paper. Many asbestos applications are critical to national defense and at the present time, there are no satisfactory substitutes. Grading and Classification Canadian chrysotile asbestos fiber is graded and priced by length since basically the longer the fiber the higher the utility. The Canadian asbestos industry does not, however, classify the fiber by direct length measurement, but by a dry screening test. The method is called the Quebec Standard Screen (QS) test. One pound of fiber is mechanically shaken in four vertically stacked sieve boxes. The relative proportions remaining on the sieves defines the grade. The longer the fiber, the larger is the amount that stays on the top coarse screens and the less on the lower, finer mesh screens. Other tests can be used to further define the length distribution of fiber such as the wet screen Bauer McNett and the Suter Webb Comb (3 group only). The Canadian grading system divides the milled fibers into 5 main groups: group 3, 4, 5, 6, and 7, with 3 group being the longest, and 7 the shortest. Each group is further divided to subgrades, identified in each group by the letters A to Z, with "A" the longest and "Z" the shortest. See Appendix 1 for the Canadian QS classification system. The Russians also use the QS test on chrysotile. The Africans classify their chrysotile into grades similar to Canadian. The African crocidolite and amosite, however, are classified into actual length groups such as l to 2 in. and 2 to 3 in. Amosite and crocidolite are generally longer than chrysotile but also more brittle. Milled asbestos is not composed of staple length fibers like fiber glass or cotton, but of a mixture or blend of fibers ranging from long to short. Milled asbestos has a fiber length distribution similar to the particle size distribution of a powder. For example, the longest group 3 chrysotile grades have a high percentage of the longest fibers (1/2 to 3/4 in.) and low percentage of short fibers (0.003 in.). The figures in Table 1 give the approximate length distribution of the longest, middle, and shortest groups. A second and further method of classifying fiber is the degree to which the fiber bundles are separated to form a larger number of smaller diameter bundles. This property is normally described as the degree of fiberization, openness or surface area. Air permeability tests are used to measure surface area. Asbestos pro-

Jan 1, 1971

By Eugene N. Cameron

Graphite is the hexagonal form of crystal-line carbon. It is found in nature locally as tabular crystals but occurs mostly as disseminated flakes, foliated, platy, or fibrous masses, or microcrystalline compact to earthy material. Graphite is characterized by its gray to black color, metallic luster, black streak, perfect basal cleavage, softness (H = 1-2) and unctuous feel. It is sectile and flexible and has a specific gravity of 2.1 to 2.3. It is an excellent conductor of heat and electricity and is inert to ordinary chemical reagents. It melts at a temperature of about 3500°C and vaporizes at a temperature of about 4500°C. In the presence of oxygen it oxidizes to CO2 in the temperature range 600° to 700°C, but it is stable at ordinary temperature and markedly resistant to chemical weathering. Although some natural graphite is nearly 100 pct pure carbon, most contains mechanical impurities of various kinds; quartz, biotite, muscovite, pyrite, iron oxides, and feldspars are the most common. Commercial graphite products have a wide range of graphite content, but the better grades contain 80 pct graphite or more. Both natural and manufactured (artificial) graphite are used in industry. Natural graphite products are divided into two broad categories based on grain size. Graphite composed of visible crystals is called "crystalline" graphite, whereas graphite so fine-grained that it is not visibly crystalline is termed "amorphous." The distinction is arbitrary, for all natural graphite is crystalline, and all gradations between the two commercial categories are known. Within the two categories the terminology used in industry is confusing and not entirely consistent. Crystalline graphite comes from two principal types of sources. The first consists of rocks containing disseminated flakes of graphite. This source yields the "flake graphite" of industry. The second comprises vein deposits of graphite, of which those in Ceylon are the most important and furnish the Ceylon graphite of industry. Amorphous graphite comes from any of a variety of sources, including some of those that yield crystalline graphite. Manufactured graphite is made by electric furnace processes, mostly from petroleum coke. Occurrence and Distribution of Graphite Deposits GENERAL Graphite is widely distributed in nature, occurring in igneous, sedimentary, and metamorphic rocks, and even in nickel-iron meteorites. Graphite deposits of economic interest, however, occur mostly in metamorphic terranes. Five principal geologic types of deposits are recognized: 1. Deposits consisting of flake graphite disseminated in metamorphosed siliceous sediments. 2. Deposits consisting of flake graphite disseminated in marbles. 3. Deposits formed by thermal or dynamothermal metamorphism of coal or other highly carbonaceous sediments. 4. Vein deposits of the Ceylon type. 5. Contact metasomatic or hydrothermal deposits in marble. DEPOSITS IN METAMORPHOSED SILICEOUS SEDIMENTS Deposits consisting of flake graphite disseminated in metamorphosed siliceous sedi-

Jan 1, 1960

By R. G. Aspden

The cold rolling and annealing textures were studied for 3 pct Si-Fe grains initially (001) [hkl]. A concentration of (001) [loo] primaries were observed only in the annealing textures of crystals initially having [loo] within 8 deg of the rolling direction. Eke annealing textures of the (001) [I101 cold rolling textures were sensitive to the initial orientation of the grains. Single crystal data were used to explain the formation of (001) [loo] in poly-crystalline malerial. CUBE texture formation in 3 pet Si-Fe sheet occurs during the final high temperature anneal. Its formation is dependent on the proper distribution of (001) plane primaries with reference to the rolling direction&apos; and on the growth of these primaries by secondary recrystallization. The selective driving force for these primaries with (001) within 7 deg of rolling plane is derived from the difference in surface energy between the annealing atmosphere and the crystallographic planes exposed at the surface of the sheet.&apos;-= The alignment of [loo] directions of (001) secondaries with the rolling direction is required for optimum magnetic characteristics7 and is dependent on processing.&apos; A high degree of alignment has been observed when the final cold rolled texture has a strong (111) [ll2] type component3 and the normal grain growth texture prior to secondary recrystallization has components with a [loo] parallel to the rolling direction and planes from (001) to (110) parallel to the rolling plane.1,3,8,9 Generally, this (001) component is much weaker than the (110) component. The growth rate of (001) plane primaries to secondaries has been found to be independent of the orientation of the primaries with reference to the rolling direction, i.e., the secondaries have the same degree of alignment of [loo] directions with the rolling direction as the (001) primaries.&apos; Hence, the rolling and annealing textures of individual grains or single crystals are of interest in understanding the development of the (001) [loo] secondary recrystallization texture. (001) components have been observed in the annealing textures of cold rolled grains initially having a [loo] parallel to the rolling direction and an (001) rotated up to 30 deg from the rolling plane. Crystals initially near the (001) [loo] orientation when rolled under the influence of constraints imposed by neighboring grains form deformation bands and ro- tate in both directions toward (001) <110>.10,11 Deformation bands have been reported also for crystals initially with an (001) within 1 deg of the rolling plane and a [loo] within 1 deg of the rolling direction when rolled as a free single crystal.12 These crystals have weak recrystallization textures and contain near an (001) [loo] component.10-12 When near (001) [loo] crystals are rolled as free single crystals no deformation bands form and the crystals rotate by a single rotation toward (001) [110]. Recrystallization after a 70 pct cold reduction yielded near an (001) [loo] component13 and after a 90 pct cold reduction an (001) [I201 component." Crystals initially near (210) [001] had a texture after a reduction of 70 and 84 pct which was similar to the (111) [li2] but rotated 10 to 15 deg in the transverse direction. These crystals recrystallize to (210) [OOl] or (410) [001] and contain an (001) [loo] component.10,13 An (001) component has not been detected in the normal grain growth textures of other single crystals. Crystals initially having orientations between (110) [001] and (111) [ll2] have a cold rolled texture of principally (111) [ll2] .10>16 Other crystals with a [I101 parallel to the cross direction rotate to (111) [112] and/or (001) [110] stable end orientations. Crystals initially having from (001) [110] to (111) [lie] retain this orientation after cold rolling.15 The cold rolled textures having [I101 directions parallel to the rolling direction had components in the annealing textures related to the deformation textures by 25 to 30 deg rotations about common (1 10) poles. Cold rolled textures of the (111) (112) type recrys-tallized to (120) [001] or (110) [00l]. The purpose of the present work was to further the understanding of the alignment of [loo] directions of (001) secondaries with the rolling direction. The cold rolling and annealing textures of grains initially (001) [hkl] were studied. These data were applied to the formation of (001) [loo] by secondary recrystallization. PROCEDURES AND EXPERIMENTAL TECHNIQUES The (001) poles near the sheet normal and rolling direction are given in Fig. 1 for the 10 grains studied. Each of these grains was located in the center of a polycrystalline specimen approximately 25 mm wide and 50 mm long. The lower case lettered grains, a through dl were about 1.2 mm in diam and near the (001) [loo] orientation. Specimens containing these grains were from a commercial 3 pct Si-Fe alloy with the principle orientation of (110) [001] as obtained by impurity inhibition of growth with manganese sulfide inclusions.17,18 Upper case lettered grains, A through F, were about 6 mm in diam and had (001) planes near the rolling plane and [hkl] di-

Jan 1, 1963

By Robert M. Keeney

Important recent developments in the melting and annealing of non-ferrous metals include: 1. Melting of nickel silver in the vertical ring induction furnace. 2. Electric melting of stereotype metal. 3. The rotary-drum gas-fired brass melting furnace. 4. The low-frequency coreless induction furnace. 5. Finishing annealing of brass sheets with city gas1 replacing wood in the large brass-rolling mill. 6. Electric annealing of brass and copper tubing and sheets. 7. Replacement of oil by gas and electricity in the annealing of nickel-silver shells and stampings. Melting Nickel Silver in Vertical Ring Induction Furnace Although over 90 per cent. of the output of the brass rolling mills in the United States is now melted in electric furnaces,2 until recently a considerable part of the output of nickel silver has been the product of the pit fire. The application of the electric furnace to the melting of nickel silver has been slow for several reasons: (I) Until recently no lining has been available that gave a satisfactory life in the vertical ring induction furnace when melting nickel silver; (2) the rocking arc furnace so widely used in the foundry does not appear to have been favored by the rolling mill for melting nickel silver, possibly because the gases present may affect the quality of the alloy; and (3) the exclusive rights to the use of the high-frequency coreless induction furnace (which has proved very satisfactory for melting nickel silver) for the wrought brass industry are controlled by one concern. A little over one year ago the first vertical ring induction furnace to be used for melting nickel silver in the Naugatuck Valley was placed in operation. This was followed by two more in the same mill, and by

Jan 1, 1930

By J. Q. Ehrgott

INTRODUCTION The U. S. Army Engineer Waterways Experiment Station (WES), under sponsorship of the Defense Atomic Support Agency, has recently developed a unique dynamic high-pressure triaxial testing device (DHT). The device permits acquisition of both axial and lateral deformation data while undisturbed soil and/or rock specimens are subjected to various states of controlled impulsive-type stresses produced by varying both the axial stress and the radial stress rapidly with time. The device is used to develop controlled dynamic pressure pulses within the triaxial chamber fluid on soil or rock test specimens to 3 inches in diameter. Controlled dynamic axial pulse loads are delivered to the specimen by a piston driven by an existing pneumatic ram loader (SECO). The DHT consists of a triaxial cell and a pressure supply and decay system which permits the chamber pressure to be varied with time. Together the DHT and SECO operate in a testing program so as to provide time varying confining pressures and axial loads to test specimens at independently controlled but synchronized programmed rise, hold, and decay times. Rise time is defined as the time from zero load or pressure to peak load or pressure; hold time is the time of constant peak load or pressure; and the decay time is the time from peak load or pressure to zero load or pressure. The maximum dynamic confining pressure attainable is approximately 15,000 psi and the fastest rise and decay times are 3 millisecond (msec) and 20 msec, respectively. This paper presents a description of the DHT, the necessary support equipment, and details of the measurement system. Performance evaluation tests conducted on clay siltstone and a Cretaceous sandstone are presented since the results demonstrate some of the capabilities of the device and show some of its characteristics.

Jan 1, 1971

[Trans. No. Place Date Vol. Page 1. Wilkes-Barre, Pa.*...May, &apos;71.. 1 3 2. Bethlehem, Pa Aug., &apos;71.. 1 10 3. Troy, N. Y Nov., &apos;71, , 1 13 4. Phildelphia, Pa Feb., &apos;72.. 1 17 5. New York, N. Y. May, &apos;72 120 6. Pittsburgh, Pa Oct., 7. Boston, Mass Feb., &apos;73.. 1 28 8. Philadelphia, Pa.* ... May, &apos;73.. 2 3 9. Easton, Pa Oct., &apos;73.. 2 7 10. New York, N. Y Feb., &apos;74.. 2 11 11. St. Louis, Mo.* May, &apos;74.. 3 3 12. Hazleton, Pa Oct., &apos;74.. 3 8 13. New Haven, Conn.... Feb., &apos;75.. 3 15]

Jan 1, 1940

Unlike the bituminous part of the coal industry, the production of anthracite has been fairly well publicized; in fact until about 1845 whenever the coal industry of Pennsylvania was mentioned in papers, magazines or books, anthracite only was meant. Beginning with shipments by river in 1820 fairly complete records of shipments were published each year, and as this variety of coal was the only one used for domestic purposes east of the mountains and north of the Potomac, there was considerable interest in the producing fields on the part of the public. Transportation of anthracite was the cause of the building of the early canals in the state, and later, of some of the earliest railroads. In most publications it has been assumed that commencement of shipments in 1820 was the beginning of the industry; this is far from being so, and it is with the earlier developments this chapter will deal, leaving the later and better known records to existing publications. (See Table No. 53.) The first reference to coal in Pennsylvania by Gabriel Thomas in 1698 has already been mentioned,1 it could only have been anthracite in that section; although of course, he never saw any coal there. Little coal was used excepting by smiths for many years after that. In 1728 the Coventry Forge paid the expenses of a man "to town for Sea Coall and Steell for ye hammer;”2 in 1729 New Castle coal was sold in Philadelphia;3 in 1740 an advertisement mentioned, "very good Pitt and Sea Coal at 18 pence a bushel; at which price &apos;tis allowed to be cheaper Fewel for Hearth Fireing than Wood at the present Rates,"4 a view not shared by most of the people there for about eighty years; in 1752 Newcastle coal was again mentioned.5 There are no references to coal in the writings of any of the Moravian missionaries, although some who settled near Mauch Chunk in 1746 said that the Indians there made their pipe heads of a soft black stone, which was much more apt to have been slate than anthracite." Several stream

Jan 1, 1942