By Hassan Saalman, Mahmoud Mahmoud, Omneya El Hussaini

The Ferruginous sandstone ore was obtained from Ramlet Hemeyir area, Southwestern Sinai, Egypt, was found to contain 10% rare earth elements (REE). A representative sample has been subjected to sulfuric acid agitation leaching. About 93% of the REE content was released by mixing the ground sample to -100 mesh with concentrated H2SO4 at solid/liquid (S/L) ratio of 1/2 for 5h at a temperature ranged from 250 to 300o C. The REE was precipitated from the prepared sulfate leach liquor of pH 1.0 by adding 35% oxalic acid at 25o C. The precipitation yielded 98% REE. For selective separation of yttrium, the rare earth cake was leached with 31.5% nitric acid. Next, the aqueous solution was contacted with di-(2-ethylhexyl) phosphoric acid (D2EHPA) where 98% yttrium extraction was achieved. Stripping was done with hot H2O (80o C). Finally, a precipitation with oxalic acid was done followed by ignition at 950o C. A yield of 95% yttrium oxide was produced.

Jan 1, 2014

By Tiejun Chun, Jian Pan, Deqing Zhu, Zhiyong Ruan

"In this paper, the desulfuration of pyrite cinder pellets was carried out. Phase analysis shows that most sulfur of pyrite cinder exists in the form of elementary sulfur. Most sulfur was removed in preheating stage. 81.25% sulfur was removed and the average SO2 concentration of exhaust gas was 1365ppm when the pellets were preheated at 950oC for 9 min. The final product, assaying 62.42wt%Fe and 0.02wt%S content at 96.88% desulfuration was achieved under the conditions of preheating at 950? for 9 min and roasting at 1200? for 15 min, which can be used as the burden for blast furnace.IntroductionPyrite cinder, as a subsidiary product of sulfuric acid production by roasting of pyrite ores, was solid waste in sulfuric acid enterprises. According to the statistics, the annual production of pyrite cinder is about 15 million tons in China. Besides, there is lots of pyrite cinder deposited for many years [1-3]. The pyrite cinder consumed in the cement and other industries as auxiliary additives only accounts for less 30% of its total discharge and the left is stored in waste pond, occupying much land and polluting environment in China [4-5]. Moreover, pyrite cinder contains iron between 30-63% which can be utilized as a cheap raw material for ironmaking by sintering or pelletizing processes, which can not only prevent pollution but also provide cheap raw materials for ironmaking [6-7]. However, compared to traditional iron ore concentrate, pyrite cinder possesses higher sulfur content."

Jan 1, 2012

By Onuralp Yucel, Ahmet Turan, Murat Alkan, Hasan Ozer

SHS (Self-propagating High-temperature Synthesis) is one of the important methods to synthesize B4C powders. The process contains the reaction of boron oxide powders (B2O3) with magnesium reducing agent and carbon black carburizer. SHS products are leached in HCl media to purify synthesized B4C powders in the following step. In the present study, effects of various functional additives (KClO3, KHSO4, MgSO4.7H2O, NaCl, MgO and Na2SO4) in the SHS stage were carried out. Various proportions of the additives were mixed with the initial SHS charge mixtures. Two different molar ratios were employed in the initial SHS mixtures as 1:3:0.8 B2O3:Mg:C and 1:2.5:0.8 B2O3:Mg:C. After the SHS step, HCl leaching process was applied to the SHS products. Filter cakes were dried and characterized by using X-Ray Diffraction Spectroscopy, BET and chemical analysis techniques.

Jan 1, 2015

By Naixiang Feng, Shaohu Tao, Zhihui Wang, Yuezhong Di

"A novel vacuum aluminothermic reduction lithium process was developed in present work which used lithium carbonate, alumina and calcium oxide as raw material. The process mainly contained three steps. The first step is that LiA102 clinker is prepared in ambient environment, then metal lithium is vacuum extracted from LiAl02 clinker with aluminum power as reducing agent, and the last step is that alumina is leached from the reduction residue with a mixture of sodium hydroxide and sodium carbonate. The results show that the lithium reduction ratio can be over 95% under the conditions of reduction temperature 1423K, reduction time 3h, and aluminum excess 20%. The main components of reduction residue are CaO· Al203 and 12Ca0·7Alz03. The alumina leaching rate of calcium aluminate in residue is over 80%. High-whiteness aluminum hydroxide can be obtained by carbonation precipitation of the reduction slag leaching solution.IntroductionWith a density about half of water, lithium is with the lowest density of all solids, mere 0.5 g/cm3 at 20 °C [l]. Lithium is widely used in aerospace, aviation, nuclear-generated power and electric battery industry. Nowadays, over 90 % of the world's primary lithium is produced by molten salt electrolysis [2-4]. But the development of molten salt electrolysis will be effected by some factors: cost, environment, and so on. Vacuum thermal reduction may be used extensively in future because of its low-energy consumption, high-purity and short-cycle."

Jan 1, 2013

By Guiqing Zhang, Liansheng Xiao, Zuoying Cao, Li Zeng

A new process of direct solvent extraction of nickel from sulfuric acid leach solutions of low grade and complicated nickel resources using a novel extractant HBL110 was proposed. The basic performance of new organic system was investigated and the continuous pilot plant and the industrial test were conducted. The results indicated that the extractant of HBL110 can be used to directly extract nickel selectively over iron, aluminum, manganese, magnesium, calcium and chromium from sulfuric acid leach solutions. The loaded organic solution can be easily stripped using dilute H2SO4 solutions. Both kinetics of extraction and stripping of nickel were fast. The continuous pilot plant test with the sulfuric acid leach solution of laterite containing 6.22g/L Ni2+, 14.1g/L Fe3+, 0.73g/L Fe2+, 33.9g/L Mg2+, 1.58g/L Al3+, 0.495g/L Ca2+, 0.97g/L Mn2+ and 0.5g/L Cr3+ as feed in mixer-settlers showed that the process had run stably with 98% recovery of nickel. The concentration of nickel in strip liquors reached as high as 50 g/L while the removals of Fe3+, Fe2+, Mg2+, Al3+, Ca2+, Mn2+ and Cr3+ were 98.5%, 91.5%, 99.95%, 99.8%, 99.1%, 98.6% and 99.5%, respectively. The industrial test with the sulfuric acid leach solution of electroplating sludge containing 11.5g/L Ni2+, 2.68g/L Fe3+, 7.54g/L Cr3+, 0.61g/L Mg2+, 2.09g/L Al3+, 0.68g/L Ca2+, 0.022g/L Mn2+ and 0.154g/L SiO2 as feed in mixer-settlers also showed that the process had operated successfully with 99.5% recovery of nickel. The concentration of nickel in strip liquors reached 42.7 g/L while the removals of Fe3+, Cr3+, Mg2+, Al3+, Ca2+, Mn2+ and SiO2 were 99.2%, 99.77%, 99.73%, 99.56%, 99.57%, 98.51% and 98.75%, respectively. The new process exhibited big advantages of short flow sheet, high recovery of nickel, high removal of impurities, low chemical reagent consumption and low cost. Application of this process in industry is expected to make important impact on the extraction of nickel from sulfuric acid leach solutions and to deliver good environmental and economical benefits.

Jan 1, 2016

By Katsuya Kase, Kaname Takeya, Keaji Ohmori, Yoshiyuki Asakawa

"The reduction-diffusion process (the R-D process) using Ca as a reducing agent has been practiced in industry in the production of the SmCos type, the Nd-Fe-B type and the 1b-Fe-Co type magnetic materials. The advantages of the R-D process are the generally high yield of rare earth metals and the single-stage conversion of a mixture of oxides and metal powders into a product of rare earth alloy powders. On the other hand, one of its disadvantages is the slightly high contents of oxygen and calcium. This disadvantage is remarkable in the Nd-Fe-B type. Singe-phase Nd2Fe14B alloy powders with low content of 0 and Ca, is obtained by choosing appropriate raw materials and performing the R-D process in a controlled way. These alloy powders are very suitable for the production of Nd-Fe-B sintered magnets and expected higher magnetic properties by adopting advanced magnet production method.IntroductionThe hard magnetic rare earth transition metal intermetallics, especially, have attained considerable technical importance. Examples are the alloys based on the intermetallics SmCo5[1], SmC017[2], NchFet4B[3], or the recently developed alloy SnuFe11Nx[4]. The reduction-diffusion process using Ca as a reducing agent has been well known as an economical method of producing rare earth based magnet materials[5]. The reduction-diffusion process has been practiced in industry in the production of the SmCos type, the Nd-Fe-B type and the 1b-Fe-Co type magnetic materials. The advantages of the reduction-diffusion process are the generally high yield of rare earth metals, the single-stage conversion of a mixture of oxides and metal powders into a product of rare earth alloy powders, the elimination of the crushing process of the alloy ingot, the inessentiality to special equipment, etc. On the other hand, one of its disadvantages is the slightly high content of oxygen and calcium. This disadvantage is remarkable in the Nd-Fe-B type. An outline of basic studies of the reduction-diffusion process was reviewed from the particular viewpoint of the production of magnet materials by Ogawa [6]."

Jan 1, 1998

By Mei-le He, Min Chen, Xiang Shen, Lei Xu, Lei Liu, Nan Wang, Xue-liang Yin

In the current study, Al2O3-MgO-CaO refractories were prepared at 1400-1600 by the addition of MnO micro-powders, and the effect of MnO addition on densification behavior of the refractory was discussed. The results showed that the doped MnO dissolved to MgAl2O4 phase, and promoted the growth of MgAl2O4 grains by the formation of MgAl2O4 solid solution. As a result, the dense microstructure was obtained, with the apparent porosity decreased from 19.2% to 5.4% and the bulk density increased from 2.78g/cm3 to 3.15g/cm3 after firing at 1600 for 2h by the addition of 4% MnO. In addition, a texture microstructure was observed, which is considered to be favorable to improve mechanical properties and the service life of Al2O3-MgO-CaO system refractories.

Jan 1, 2016

By Shuqiang Guo, Dingsheng Tan, Weizhong Ding, Zunyu Hu

"The mixture of hydrochloric acid and magnesium chloride is a good lixiviant for leaching of laterite. The solution can enhance the leaching ability because of the proton activity deviated positively from ideal. Otherwise, the existence of magnesium chloride in the lixiviant affects the dissolution behavior of magnesia, which may be an advantage of the process with less hydrochloric acid consumption. An investigation of magnesia particle dissolved in strong hydrochloric acid solution has been conducted. Influences of concentration of the magnesium chloride and hydrochloric acid and temperature on magnesia dissolution were studied. The dissolution mechanism was also discussed in this paper.IntroductionThere has recently been much interest in the use of hydrochloric acid leaching processes for recovering metal from ores or secondary resources [l-41_ Compared with sulfuric acid, the use of hydrochloric acid as lixiviant offers significant advantages including faster leaching kinetics even at atmospheric conditions, higher leaching rate and greater solubility for most metal chlorides [5-61 .With the gradual decline of the nickel sulfide supply, the extraction of nickel from laterites has become increasingly attractive [7-s1. Nickel may be co=ercially recovered from laterites both by pyrometallurgical and hydrometallurgical processes. The drawbacks of pyrometallurgical processes include the requirement of high grade ores, substantial energy input and loss of cobalt bound within ores. The extraction of Ni from lower grade nickel laterites ores is suited by hydrometallurgical routes, which play an increasingly important role with depletion of higher grade deposits."

Jan 1, 2014

By Chonghe Li, Xionggang Lu, Wei Xiao, Xingli Zou, Weizhong Ding

The reduction degree and rate of the initial ilmenite concentrate and pre-oxidation samples by hydrogen were investigated by using thermogravimetric analysis system. H2-TPR was used to detected reduction properties of the pre-oxidation products which were oxidized at different temperatures. The phase transformations and micromorphology changes during pre-oxidation and hydrogen reduction were identified by XRD and SEM. The FeTiO3 was decomposed into TiO2 and Fe2O3 at the temperature below 900 oC. With the temperature rising, Fe2TiO5 was the only stable phase in high temperatures. The reduction of pre-oxidation ilmenite concentrate was faster than the natural sample, which was attributed to the micropores generated on the surface of ilmenite concentrate during oxidation. The main phases of the reduction product were metallic iron, ferrous pseuodbrookite.

Jan 1, 2014

By K. J. Cathro

A hydrometallurgical process is described for the recovery of copper from chalcopyrite concentrates. The process is based on a cupric chloride leach, the concentrate having first been "activated" by heating it with sulphur at a temperature near 400°C. This activation process converts most of the iron of the chalcopyrite to pyrite, which is insoluble in the cupric chloride leachant. The copper is converted to the mineral idaite, which dissolves readily in hot cupric chloride: at 106°C, 98% of the copper is extracted in a three-stage countercurrent leach, the leaching tirqe being 1 hour per stage. The sulphur of the chalcopyrite appears as elemental sulphur, which is recycled for the activation of further concentrate, the final leach residue consisting of pyrite, plus the gangue present in the original concentrate. The copper extracted can be recovered by electrowinning, using a diaphragm cell. Current efficiency (one-electron basis) is about 70% but the cell voltage is only about 1 V, so that power consumption is three times lower than for the conventional sulphate electrowinning process. The leachant is simultaneously regenerated in the anode compartment. The behaviour of minor elements in the concentrate has also been studied.

Jan 1, 1976

By Uchil Jayagopal, P. V. Krupakara, S. Manjunath

"This paper deals with the corrosion characterization of quartz particlate ZA-27 alloy metal matrix composites (MMCs). Quartz particles of size 50-80 microns are used as reinforcement. MMC's are prepared according to ASTM standards. Composites containing. 2, 4, and -6% by weight of quartz and unreinforced matrix were tested using 1 -N hydrochloric acid: The composite was found to be more corrosive resistant than matrix alloy. In each test the corrosion resistance of both alloy and composites were found to decrease with the exposure time.1. IntroductionMetal matrix composites- (MMCs) offer designers many added benefits, as they are particularly suited for applications requiring good strength at high temperature, good structural rigidity, dimensional stability, and light weight 1-5. The trend is towards safe usage of the MMC parts in the automobile engine, which work particularly at high temperature and pressure environments Particles reinforced MMCs has been the most popular over the last two decades.ZA alloy MMCs have most popular families being represented by. ZA-27 alloy reinforced with ceramic particulate. Although the incorporation of the second phase into a matrix material can enhance the physical and mechanical properties of the base metal, it could also significantly change the corrosion behavior.ZA alloys have been used extensively in industry. This is attributed to their excellent fludity, castability and good mechanical properties. Among the zinc-based foundry alloys, the ZA family of alloy have been widely used during the past few years. ZA alloys have many advantage over aluminium based ones, especially high strength with a low casting temperature 8."

Jan 1, 2000

By Mingming Zhang, Mallikharjuna R. Bogala, Ramana G. Reddy

Steelmaking desulfurization slag samples were characterized using chemical, X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive spectrometry (EDS) methods. The objective of this work is to investigate the occurrence of sulfur and phosphorus components in the slag samples and to identify their origin and associations with the iron phases. Thermodynamic calculations results confirm the presence of phosphorus and sulfur components in the slag sample at high temperatures (1400 to 1800oC). The main constituents of slag include Ca3SiO5 (28.1%), MgO (9.31%), Ca3(PO4)2 (9.18%), CaS (8.39%) and CaO (5.68%). The major phosphorus and sulfur components of the slag are Ca3PO4 (99.2%) and CaS (79.3%) respectively. Characterization studies indicate the presence of microparticles of different sizes and shapes in the slag sample. Elemental analysis of these particles confirm the presence of major elements (O, Mg, Al, Si, S, Ca and Fe) in the slag sample.

Jan 1, 2015

By Jinxia Nie, Yunnen Chen, Dachao Zhang

"Rare earth resources are strategic and non-renewable resources. But disordered exploitation on rare earth metals leads to resources waste, environmental pollution and ecosystem destroyed. In this paper, soil collected from garden was cultured in thermostated incubator. Adding exogenous rare earth to the soil and the effects of recombination action of rare earth lanthanum, cerium and yttrium on soil enzymatic activities were studied. The results showed that single metal La and Ce can increase urease activity, but Y inhibits its. Coexist La/Y or La/Ce in soil inhibit the urease activity, coexist Y /Ce or coexist three metals promote its. Single metal La, Y and Ce can promote catalase activity, and that of coexist three metals. Pairwise coexist La, Y, Ce in soil inhibit catalase activity. With certain concentration of rare earth recombination action, urease activity in soil has been very significant direct proportion to ionic impulse, but catalase activity been insignificant inverse proportion to its.1. IntroductionThe increase of rare earth element content due to anthropogenic inputs frequently takes place in agro-industrial areas, leading to soil pollution episodes that may cause serious environmental problems because of their potential toxicity to microorganisms, plants, animals and human beings [ 1]. China is abundant in lanthanides resources. Rare earth metals are used in many frontier technologies such as photic devices, magnetic materials, and fine ceramics, and the amount of the rare earth metals used in these industries has been increasing. In addition to their use in industry, rare earth metals are more widely applied to cropland as microelement fertilizers due to their ability to promote growth and productivity of some crops [2]. As a result, more and more rare earth metals are moving into the ecosystems. While a permanent contamination of soils results in populations of micro-organisms with high resistance to rare earth metals, a short-term burden of contaminants at high concentrations could exert inhibitory effects on microbial carbon [3]. They accumulate in soils, bioaccumulate in crops, and enter the food chain, causing a potential problem of rare earth metals environmental pollution in China [4]. This contamination may also severely influence organisms and soil activities [5]."

Jan 1, 2011

By Mingchun Lu, Zhe Wang, Mingming Cao, Xiangdong Xing, Shan Ren, Jianliang Zhang, Zhengjian Liu

"The effect of reduction temperature on the vanadium titano-magnetite carbon composite pellets was investigated by X-ray diffraction (XRD) and scanning electron microscopy (SEM), and the discussion has put emphasis upon the enhanced reduction mechanism of additives containing CaF2 and NaF in this paper. The results showed that the reduction temperature of 1350°C was needed for the generation, mergence and growing up of metallic iron as well as monomer dissociation between metallic iron particles and slag phase in the vanadium titano-magnetite metallization pellets. The iron compound was completely reduced into metal iron, and Fe2Ti04 was mainly transformed into metal iron, (Fe,Mg)Ti205 and FeTi03 at 1350°C. The maximum metallization ratio was only 88.5% at 13500 for 30 min without any additive. However, with the addition of 3.0% CaF2 or NaF, the metallization degree of pellets could reach up to 94.8% and 92.5%, respectively.IntroductionVanadium titano-magnetite which is mainly distributed in the area of Panxi, Chengde and Maanshan in China is a kind of complex iron ore which contains various valuable metal elements such as iron, vanadium, titanium, etc. Among the above areas, Panzhihua (Sichuan Province in China) area possesses the largest deposits of vanadium titano-magnetite and the future reserves are more than 100x108t, and the reserves of Ti existing as Ti02 reach to 8.7x108t which occupy over 91% of the whole nation and ranked No.1 in the world[1]. Lots of researches on the comprehensive utilization of vanadium titano-magnetite have been conducted in the world. And many technological processes have been applied successfully in industrial production. Among these processes, the process of rotary kiln-electric furnace is employed to recover iron and vanadium in South-Africa, while the process of blast furnace-rotary furnace is widely used in Russia and China. Besides, many researchers have made efforts on employing new direct reduction process to realize the effective comprehensive utilization of vanadium titano-magnetite[2-4]. However, the direct reduction process is only researched in laboratory and it has not been used in industry."

Jan 1, 2013

By Tadashi Aiura, Yasuhiro Miura

"A small amount(0.2mass%) of Scandium(Sc) was added to the 7.NOl and 5083 Al alloys as a refiner and stabilizer of microstructure, and the resulting microstructures were discussed in comparison with the effects of the conventional additives. The followings are summarized: 1) in the as-solidified structure, a ·decreased tendency of constitutional supercooling and increased solubility of Mg were recognized for the Sc-added 5083 alloy. Sc is a -better microstructure refiner for the 7N01 alloy than Zr, in a sense that it does not suppress the favorable effect of· coexisting Ti. 2) Sc effectively suppresses recrystallization both in the 5083 and 7N01 alloys. 3) The rod like primary Al3Sc crystals formed during solidification, as well as the fine dispersion of Al3Sc precipitates formed by subsequent heat treatment, can act as a strong recrystallization suppresser. IntroductionThe 7N01 and 5083 alloys are the most popular industrial Al alloys and they are widely' used for various structures because of their superior properties. Fine macro and micro structures of the materials are required for obtaining acceptable sec resistance,consistent appearance of anodized surface and good weldability, as well as good mechanical properties. In order to produce fine grain structures, transition metals, such as Cr, Zr, and Mn, have been conventionally added.It has been reported that Sc is an efficient refiner [l, 2] and can be an alternative for the conventional and also suppresses recrystallization in Al alloys [3,4]. Scandium is the lightest transition element and forms an equilibrium intermetallic phase. The equilibrium phase, Ll2-Al3Sc, is coherent with the matrix, and of _spherical shape. A fine dispersion of the spherical precipitates is obtained by quenching and aging after solutionizing annealing. The authors have already reported a part of the experimental results on the effect of Sc on the as homogenized microstructure of the 5083 alloy [5]. In the present study, the effects of Sc on the macro and micro structures of the industrial high strength Al alloys(7N01 and 5083) for extrusion are investigated, and the superior role of Sc as a grain refiner is shown"

Jan 1, 2000

By Maria K. Kojo

The interaction between various slags and a nickel concentrate containing pyrite, pentlandite, and violarite were investigated by submerging concentrate pellets in molten slags. The slags were contained in MgO-A12O3 spinel crucibles. The slag oxidizes the iron sulfides in the concentrate, resulting in a nickel matte. The amount of S02 gas formed during reaction was measured to determine the oxidation reactivity of the slags. The experimental variables included temperature, the ferric/ferrous ratio of slag, and other slag properties such as the FeO/SiO2 ratio and the MgO and NiO contents. The reactivity of the slag depended in a complex manner on its oxidizing power, viscosity, and interfacial tension. The slag composition for the greatest reactivity was determined to be Fe3+/Fe2+ = 0.3, Fe/SiO2 = 1.3, and % MgO = 2. This slag, however, caused substantial foaming. Increasing the MgO content to 10% or replacing it by 5% MgO + 8% NiO eliminated at a slight decrease in reactivity. The implications of the findings from this work in the bath smelting of nickel sulfide concentrates are discussed.

Jan 1, 1995

By Hongbo Zhu, Jinhui Peng, Linqing Dai

"To optimize the process variables for making direct reduced iron (DRI) by microwave heating, the reduction temperature, reduction time and the ratio of coal to material were studied with the central composite design (CCD) and their interactions on the Metallization rate were also investigated. The predictive polynomial quadratic equations model was analyzed by ANOVA. Optimal conditions of making DRI can be concluded as follows: 28 min at 1139?, the ratio of coal to material is 20.95%. Under these conditions, the metallization rate is up to 97.06%.1. IntroductionThere are some technical problems in making direct reduced iron (DRI) or sponge iron using iron ore concentrates containing coal and lime. In reduction of the iron ore concentrates containing coal with microwave heating, the strength of pellets needn’t to be considered. It reduces the costs and improve quality of materials, but also eliminates the need for pellet preparation process, simplifying the process and achieving a cleaner production.Microwave energy is a clean energy, and has characteristic of selective heating. The speed of heating is also fast. It researched by Chen Jin that when the mole mass of C: O is 0.627 and the microwave power is 15KW, it only spends 15min from 15? to 1021.6? with 1 kg iron ore containing coal with microwave heating [1]. There are many factors affecting metallization rate. In order to find a suitable condition for reduction process, it is necessary to design a series of suitable experiments.Response surface methodology (RSM) is one of the relevant multivariate techniques which can deal with multivariant experimental design strategy, statistical modeling and process optimization [2–5]. It is used to examine the relationship between one or more response variables and a set of quantitative experimental variables or factors. This method is often employed after the identification of the vital controllable factors to find the factor settings that optimize the response. Designs of this type are usually chosen when a curvature in the response surface is suspected. The process optimization of the microwave reduced iron ore was seldom reported in literature. Hence the present work intends to assess the effects of variables such as reduction time, reduction temperature and the ratio of coal to identify the optimum conditions using a central composite design (CCD). The characteristic of product was assessed using scanning electron microscope (SEM)."

Jan 1, 2011

By Cheryl S. Lim

New technologies such as direct reduction and smelting reduction processes are increasingly being used in iron-making and steel-making in addition to conventional blast furnace technology. Critical parameters for control of these processes include the degree of metallization, degree of pre-reduction, and carbon and silica levels. On-line monitoring of these parameters is difficult because measurements often need to be made on hot ores (at or higher than -1000'C) in circumstances where representative sample streams are not readily accessible. A nuclear analyser has been developed which provides continuous, non¬intrusive, real-time measurements of iron, oxygen, carbon and silicon levels in hot ores undergoing reduction. The analyser has been tested in a plant using a direct smelting process on pre-reduced feed to the smelting vessel-, accuracies of 1% relative, 0.5 w'.96 (25% relative) and 1.0 wt.% (9% relative) were obtained for the degree of pre-reduction, carbon and silica respectively. The underlying method, capabilities and potential applications of the analyser will be discussed.

Jan 1, 2001

By Filiz Sahin

This paper presents a synthesis of TiB2 via carbothermal reduction method using a mixture of TiO2, B4C and C prepared in molar ratio of 2:1:3. Reduction experiments were carried out in a high temperature graphite furnace in a graphite crucible under argon atmosphere at different time (0, 15, 30 and 60 min.) and temperatures (1400, 1500 and 1600 °C). The products obtained were investigated using XRD technique.

Jan 1, 2008

By Seksak Asavavisithchai, Natthida Jareankieathbovorn, Areeya Srichaiyaperk

"Recycling of ADC12 alloy scraps for fabrication of open-cell aluminium foams has been conducted via pressure infiltration method of replication process. The scrap, up to 50 wt.%, was melted with pure aluminium billet, followed by infiltration in a replicated mold of polyethylene foam structure. Compared with the pure aluminium foam, the compressive strength and hardness are higher for the foams with recycled scraps. The increase in foam mechanical properties is due to the presence of Si hard phase in Al matrix. The strength and hardness of the foams also increase with increasing contents of the scraps.IntroductionRecently, open-cell metallic foams have been brought to considerable attention of many industries due to their superior properties; such as large surface area, high specific strength, thermal conductivity, high service temperature and excellent anti-microbial activity, that cannot be found in conventional materials [1, 2]. Typically, open-cell foams are used in functional applications for which a requirement of high strength materials is not demanded. Good examples of such applications include heat exchangers, bone-replacement implants, interconnects, catalyst supports, and sound insulators.Among all types of open-cell metallic foams, aluminium (Al) is the most widely used base metal, due to low material cost, low density, low melting temperature and good corrosion resistance. To improve mechanical properties of Al foam, modification of foam microstructure with addition of alloy elements or ceramic particles is commonly carried out [3, 4]. ADC12 alloy is a typical die-casting Al alloy with high content of silicon (Si) close to the eutectic point in Al-Si binary phase diagram. The alloy is extensively used in the casting industry, due to high wear and corrosion resistance, low coefficient of thermal expansion and excellent castability [5]. The mechanical properties of Al-Si alloy are strongly dependent of Si content."

Jan 1, 2012