By M. Hashimoto

The equilibrium distribution ratios of sulfur between molten copper and CaO-fluxes containing caF2 and caC12 were determined in the range of 1300° to 1400° C under carbon monoxide. The rate of approach to equilibrium is rapid and increases with increasing CaCll concentration. In CaO-CaFl-CaCl2 fluxes, the distribution ratio varies in a complex way with temperature and CaFl concentration. The results are compared with those obtained with the binary fluxes of CaO with BaFZ and MgFl ?

Jan 1, 1983

By Jing Zhan

The fibrous precursor can be obtained by coordination precipitation process, using oxalate, cobalt chloride and ammonia. The composition and morphology of fibrous precursor were characterized by XRD, IR, DTA/TGA and SEM analysis. The results show that XRD pattern and composition of the precursor with fibrous morphology precipitated at pH=9.0 were different from that of ß-CoC2O4?2H2O precipitated at pH=1.0. The mechanism on the thermal decomposition of fibrous precursor was addressed. The influences of various conditions in pyrolysis, including the temperature, time, atmosphere, and the morphology of the precursor, on the morphology, average size and specific surface area of the Co powders were investigated in detailed. At last, the final product, fibrous cobalt powders with diameter about 0.3~0.5µm in size and 40~60 in aspect ratio, were produced by thermal decomposition at 400~500? in the weak reducing atmosphere. The structure of pores in cobalt powders was capillary tube with open ports and the majority was mesoporous.

Jan 1, 2009

By Fumitaka Tsukihashi

Increasing amounts of steel scrap are being used as resources for steelmaking. Therefore, there has been a growing interest in the removal of harmful tramp elements such as antimony, zinc, tin, arsenic, bismuth, lead and copper from the molten steel. The problem that should be solved is the economic removal treatment of residual tramp elements in the steelmaking processes and the production of high quality steel by reducing the effect of the contaminated tramp elements and satisfying the environmental regulations. In this paper, the available thermodynamic data of the residual tramp elements in the molten steel arc summarized and the possibility of the removal of residual tramp elements from the molten steel is thermodynamically estimated.

Jan 1, 2003

By Guohui Zheng

The ever increasing quantities of solid wastes generated by various industries are at the source of the growing need for proper waste disposal methods. Thermal treatment of combustible wastes is a proven technology which permits the reduction of hazardous material having to be landfilled. However, this method is not universally applicable to waste disposal. For example, the transferal of heavy toxic metals into the thermal remediation products is a major issue of public concern. This paper focuses on the analysis of morphology changes from solid sludge to ash which is a product of the sludge combustion. The morphological parameters analyzed were particle size and external surface. They were determined using Jeol 840 Super Probe. The experiments were conducted in a computer-controlled high-temperature combustion system consisting of the thermogravimetric furnace coupled with Fourier transform infrared spectrometer (TGA-FTIR). Sludge particles were made of complex fibers trapped in the aluminosilicate matrix. At low temperatures, up to 680 K, the solid residue looked similar to the initial sludge. Between 680 K and 1180 K the sludge underwent intensive burning and steadily changed into powdered ash. At the temperature of 1050 K the ash was composed of separate, flat flakes with sizes ranging from 5 to 20 um. At 1470 K the flakes aggregated into large particles. The surface observed at 1670 K was a mixture of mullite crystals. Such structure could result from the solidification of the ash material after its melting. Morphological changes influenced the distribution of metals in the solid residue. For example, Cr was concentrated in small aggregates. Such distribution should allow for recovery of valuable metals from the solid waste residue.

Jan 1, 1996

By A. C. Wadhawan

In the present context of rapid industrialization, production of Lead-Zinc metals from low grade materials, residues and wastes can make substantial contribution to the supply of these metals in India. Recovery from secondary sources also plays an important role in conservation of mineral resources and lower power consumption. Conscious effort is therefore, required to increase the secondary metals which, besides saving in energy cost will also help in waste material management and keeping environment clean. The major thrust is, therefore, needed in this direction. During all these years, the Indian Lead- Zinc industry has made sustained efforts for recovery of metals from low grade ores and from metallurgical wastes and residues. The paper identifies the treatment of low grade ores by various technologies and techniques and the treatment of metallurgical residues and wastes generated during primary Lead and Zinc smelting in India. Some of the major achievements in past decade have also been elaborated in the paper. The strategies to be followed for continuing treatment of low grade ores and waste materials by adopting newer, environmental friendly technologies, in consonance with the rigid standards being adopted by most of the countries including India. have also been dealt with in the paper.

Jan 1, 1994

By Y. Ikeda

Typical electric appliances were dismantled into component pieces to study the recyclability of these discarded goods. Types and weight ratios of these component materials were investigated and characterized. The results showed that if they are dismantled properly, these goods could be classified into several groups of similar materials and/or structures, namely those consisting of single materials, metal-plastic combinations, metal-metal combinations and complex combinations of many different materials. By separating each combination into recyclable materials and isolating hazardous materials, it was found that the final waste for disposal could be reduced and the recycling efficiency could be improved markedly as compared to the conventional shredding method. The metal-metal combinations account for 60% by weight of the total metal contents in electric appliances, and therefore, it becomes important to segregate these metals. For the complex combinations, a process consisting of pyrolytic decomposition of plastic contaminants followed by smelting of the residue is proposed. It is anticipated that nearly zero-emission recycling of electric appliances will be achieved by applying this treatment process.

Jan 1, 1995

By Chuanfu Zhang, Liwei Liang, Yanxin Wu, Jinliang Wang

"According to the reaction shaft operation characteristics during the flash smelting process, 15 groups of slag samples containing high Fe3O4 were prepared by some chemical reagents, and then the slag viscosities were measured using a RTW-10 type synthetic test instrument for melt physical property by the rotating cylinder method. The effects of Fe/SiO2 ratio (mFe/mSiO2), Fe3O4 content (wFe3O4), Cu2o), MgO content (WMgO) and Cao content (wCaO) on the slag viscosity were also studied. Results show that slag viscosity is decreased with the increase of temperature, mFe/mSiO2, wCu2o, wMgO and wCao, and with the decrease of wFe3O4, under the range of slag contents: mFe/mSiO2 1.36~1.78, wFe3O4 17.83%~21.18%, wCu2o 3.51%~8.34%m wNgI 2.21%~6.57%m w/caI 6.22%~9.387% and temperature range if 1250 o/c~1450 oC. Only wFe3O4m and w/caO have great influence on the slag viscosity when temperatures as high as 1400 oC. Only wFe3O4 and wCaO have great influence on the slag viscosity when temperatures as high as 1400 oC or so. To form a freeze slag with higher viscosity inside the reaction shaft, wFe3O4 should be more than 20% and wCaO should be less then 6%.IntroductionSince its appearance in 1949, Outokumpu flash smelting technology has making continuous innovation and has become the most competitive intensified smelting technology [1], widely considered to be the standard clean smelting process [2]. At present, flash smelting technology is adopted to newly build or reconstruct most of the world's copper or nickel smelting enterprise [3]. Reaction shaft is the most important part of the flash smelting furnace. During the flash smelting process, reaction shaft must be able to withstand the following harsh conditions at the same time: 1) high temperature varying from 1400 °C to 1500 °C. 2) strong oxidative atmosphere containing 50% - 80% oxygen. 3) solid particles and melt with speed up to l00 m/s. 4) high acidic or basic slag with strong chemical corrosiveness. 5) smelting gas containing 50% - 80% SO2. 6) matte with strong dissolution."

Jan 1, 2012

By S. Ozbilen, B. Erdogan, M. Erdogan

To study by thermal analyses the response of precipitation hardenable alloys of Al-Cu-Mg and Al-Li-Cu-Mg system to natural and artificial ageing, a series of ternary and quaternary Al-alloys with nominal compositions of Al-l.13wt%Cu-0:65wt%Mg (alloy-I), Al-1.15wt%Cu-0.57wt%Mg-0.07wt%Li (alloy-2), Al-l.19wt%Cu-0.56wt%Mg-0.75wt%Li (alloy-3), Al-2.0lwt%Cu-0.89wt%Mg (alloy-4), Al-2.14wt%Cu"0.56wt%Mg-0.07wt%Li (alloy-5) were used in the present investigation. Samples in the form of rolled sheets are subjected to water quenching at 25EC after solution treatment at 530EC for 20 min. Alloys were aged naturally at room temperature (25EC) up to 2 months and artificially at 190EC up to 2 days. By using differential scanning calorimetry (DSC) in the temperature range of25-300EC, differential thermal analysis (DTA) in the temperature range of25-600EC together with Vicker's hardness measurements, the response to natural and artificial ageing of the alloys used in the present study were investigated. It was observed that in these alloys, GPB(Cu, Mg) zones [Guinier-Preston zones with Cu and Mg] do form during water quenching at 20EC following solutionizing heat treatment. Natural ageing of the same alloys causes formation of more GPB(Cu, Mg) zones, which results in hardening in the alloys. Artificial ageing at 190EC up to l day results in GPB zone dissolution causing preliminary decrease in hardness values while two days of artificial ageing in the alloys cause S' (Al2CuMg) precipitation confirmed by DSC/DTA analyses resulting in an increase in hardness values. Li addition up to 0.75wt% helps T1 (Al2CuLi) and T 2 (Al6CuLi3) phase formation together with S' precipitation as DSC/DTA analyses show after the same heat treatment.

Jan 1, 1998

By Chen-Ming Kuo, Esher Hsu

"The importers and manufacturers who import or produce products with packaging containers are charged a recycling fee in Taiwan. The amount of waste packaging containers used for calculating the recycling charge is based upon the amount declared by importers and manufacturers which might be underestimated. This study aims to estimate the amount of waste packaging containers generated by households in Taiwan and also explores its distribution. The sampling survey and ratio estimation are conducted for estimating the recycled amount; while the refuse sampling method for municipal solid waste composition is employed to estimate the un-recycled waste packaging containers. The estimated total amount of waste packaging containers in 2011 generated by households in Taiwan is 696,511 m.t., of which, 79.49% of the waste packaging containers were recycled and 20.51 % were landfilled or incinerated. This study shows that the amount of waste packaging containers declared by importers and producers is underestimated around 20%.IntroductionWaste packaging containers including iron cans, aluminum cans, glass bottles, plastic containers, paper containers, aluminum foiled paper packs are officially announced to be recycled in Taiwan. In order to create the economic incentive for raising recycling performance, associated manufacturers and importers are charged a recycling fee to subsidize recyclers. The amount of packaging containers declared by importers and manufacturers is used for calculating the recycling charge and recycling rate. The importers and manufacturers might underreport their producing (importing) amount to pay less recycling fees. Therefore, the estimated waste packaging containers based upon the amount declared by importers and manufacturers is usually underestimated. Related previous studies about waste packaging containers recycling in Taiwan are done by Hsu and co-workers [1-4]. Hsu and Kuo [1] estimated total production values of recycling and evaluated the performance of recycling performance based upon the estimated production values. Hsu and Liu [5] provided a cost analysis of recycling for waste packaging containers in Taiwan. Bor, Chien, and Hsu [2] presented a market-incentive recycling system for waste packaging containers in Taiwan. Hsu and Kuo [4] provided an amending mechanism for product charge and recycling subsidy in response to the social economic changes for waste packaging containers recycling. Lee and Hsu [ 6, 7] explored the distribution, fee rates, and collection rate of waste containers. This study aims to estimate the amount of waste packaging containers generated by households in Taiwan and also explore its distribution."

Jan 1, 2014

By Yuanbo Zhang, Ruijun Wang, Qian Li, Zhao Jing, Guanghui Li, Zhengwei Yu, Chen Liu

The high content of sodium and potassium in sinter is harmful for blast furnace ironmaking. Reductive sintering technology can remove more alkali metals than conventional sintering process. In order to improve the removal ratios of Na and K, reductive sintering with both CO-containing flue gas circulation and carbon-bearing pellet was conducted in this study. Experimental results show that all indexes except the VSV and P were improved in reductive sintering with CO circulation. Flue gas circulation technique combined with carbon-bearing pellets were beneficial to reductive sintering, because it could maintain good sintering indexes and enhance the removal of Na, K. The best removal ratios of Na, K and reduction degree of iron oxides were 20.37%, 63.73% and 23.76%. In reductive finished sinter, silicate mineral becomes the important binder phase, and main iron mineral phases are wustite (FexO) and magnetite (Fe3O4).

Jan 1, 2016

By Saynbaatar, Gangping Ma, Jianhua Fu, Qiqige, Jinghua Wang

The influence on the performance of foam concrete made by replacing cement with some industrial waste residues was researched in this paper. The result shows that the 7d and 28d compressive strength of foam concrete increases firstly and then decreases with the increasing amount of industrial waste residue. The proper added range is 10%-20% for steel slag, blast furnace slag and coal ash, but, 8% for desulfurized fly ash. With the proper adding ratio, the compressive strength of foam concrete always increased comparing with the pure cement foam concrete. When adding 48% of the compound industrial waste residues, the 28d compressive strength of the foam concrete reached the 2.9MPa which could match the pure cement foam concrete. The results indicates that there is a synergistic effect among the compound industrial waste residue, and this effect is benefit to improving the compressive strength of foam concrete.

Jan 1, 2015

By V. Jiricny

There is a growing need to process galvanized steel scrap from automobiles, etc., in order to remove the zinc coating that otherwise causes problems in remelting of the scrap in electric arc furnaces. One approach that has moved to the pilot plant stage is that of Metal Recovery Technologies, Inc., of East Chicago (MRI). That company leaches the zinc fiom the scrap with a sodium hydroxide solution. The leached and washed scrap can then be returned to the steel industry. What is left is a sodium hydroxidelzincate solution which must be processed to recover the zinc and the NaOH. Presently, this is done by MRI using electrodeposition on planar electrodes at moderate current density and the resulting zinc is in the form of fine powder which is hard to process into, say, zinc for galvanizing. MRI has supported an investigation of a novel electrode, the spouted bed electrode (SBE), for zinc electrodeposition. In laboratory cells, zinc particles with low porosity have been grown up to 3mm in size. Microanalysis of the deposited zinc showed low level of impurities. DC energy consumption values were usually in the range of 2-2.5 kWg which is well below the energy consumption of the existing cells (and of present-day cells for electrowinning from acid sulfate electrolytes). These results were achieved at current densities (few thousand A/m2) that are much higher than possible with conventional electrodes. Discussion is provided of the scale-up of the cell to a commercial scale.

Jan 1, 1998

By QIE Jun-mao, DONG Fang, DENG Hao-hua

The DIL402C thermal dilatometer and STA449C thermal analyzer were employed to test the linear expansion and contraction coefficient，CP and DSC curve of 304 stainless steel. The result showed that the linear expansion coefficient range was 20.9700×10-6～21.5712×10-6 and the linear contraction coefficient range was 21.2528×10-6～21.9471×10-6.The linear expansion and contraction coefficient were higher than other steel grade，so the 304 stainless steel belonged to the crack sensitive steel. Because of the crystal phase transformation occurred during the 1000~1400 ℃,the curve of CP fluctuated obviously and the defects of casting blank occurred easily. Chosen 1414℃ as the liquidus temperature of 304 stainless steel based on the analysis results of DSC. The curve of DSC was unsmooth during 1450～1100℃，the crystal phase transformation occurs and thermal stability of slab was inferior.When the initial solidified shell formed in this temperature range,the thickness of the shell would be nonuniform and the surface defects occurred more easily.

Jan 1, 2015

By I. J. Moon

The reduction behavior of hematite by H2 and H2-CO gas mixtures was investigated to elucidate the reduction mechanism at 800-950 °C. The hematite compacts were made by Cold Isostatic Pressing to produce compacts of uniform shape and size. The compacts were sintered at 1000° C for 30min, and showed a contraction of 29%. Mercury pressure porosimeter was used for measuring the total porosity, pore size distribution and pore surface area of the compacts. Reduction was measured by means of weight-loss technique using Cahn Balance (Model : TG-171, capacity log, accuracy f 10pg). Microscopic examination and X-ray analysis were used to correlate the structure of reduced compacts with the mechanisms of reduction. Neither chemical reaction control nor diffusion control is adequate in describing the complete course of reduction of the hematite compact. The reduction of hematite compacts was initially controlled by the chemical reaction at oxidelmetal interface. The reaction goes through a transition phase .where it is undergoing a mixed control, followed by the diffusion control towards the end of the reduction. The values of apparent activation energies for chemical reaction control were 3.48-8.43 kcal/mol depending on the gas compositions.

Jan 1, 1997

By A. S. Block-Bolten

Two innovations in nickel-arsenic separation have been studied on a laboratory scale. The first requires only a nitric acid atmospheric leach without preliminary roasting and leads to favorable final conditions for precipitation of arsenic as highly stable FeAsO4, The second is an NaOH-H2O2 pressure leach which is an alternative to the known NaOH-O2 pressure leach. Either method offers the possibility of rapid and efficient separation of nickel from arsenic and is applicable, for example to the high grade niccolite deposits in the Great Slave Lake area of northern Canada.

Jan 1, 1982

By A. Kontopoulos

The extraction of nickel and cobalt from low-grade greek laterites by sulfuric acid leaching has been studied. Batch and continuous mini-plant atmospheric leaching as well as pressure leaching techniques were employed. Atmospheric leaching at temperatures as high as 95 OC generally resulted in low Ni extractions (up to 82%), high acid consumption (650-850 kg/t ore or 80-100 kg/kg Ni) and high Fe co-dissolution (30%). Pressure leaching at 260 OC increased Ni extraction to over 98%, with minimal Fe co-dissolution (2.5%); acid consumption was 300 kg/t ore (31 kg/kg Ni). Detailed experimental results and conceptual flow sheets for atmospheric and pressure leaching are presented.

Jan 1, 1991

By N. Menad

. Electronic wastes are heterogeneous mixture, with mainly copper, aluminium and steel attached to or mixed with various types of plastics and ceramics. In general, small amounts of precious metals are incorporated in this mixture. Today, these components constitute an environmentally problematic fraction in disposal. Their physico-chemical characteristics have been investigated through chemical, x-ray diffraction, infrared spectroscopy, scanning electron microscopy and thermal analysis.

Jan 1, 2000

By Hu Meilong, Liu Lu, Bai Chenguang

Extracting perovskite from high titanium-bearing blast furnace (BF) slag is a green and potential method to recover the second titanium resource. The non-isothermal crystallization process of perovskite in synthesized high titanium-bearing slag was studied in situ by confocal scanning laser microscope (CSLM) with cooling rate of 20 K/min. The results showed that perovskite was the primary phase formed during cooling process in the titanium-bearing synthesized slag (TiO2=23%). Perovskite started to precipitate at 1719 K and finally presented an orthogonal straight lines morphology.

Jan 1, 2014

By Run-bo Wang, Zhe Wang, Fan-yi Meng, Jian-Liang Zhang

The influence of semicharcoal substitution for coke breeze on sintering performance was investigated by pot-grate sintering test. At a fixed fuel ratio, sinter productivity and strength decreased with the substitution increasing from 0 to 100% due to better combustibility. To enhance the utilization efficiency of 100% semicharcoal, sintering parameters (moisture and suction pressure) was adjusted. With the moisture increasing, sinter performance of 100% semicharcoal increased because of the suppression of semicharcoal incomplete combustion. As the moisture further increasing to 9.0%, sinter quality gave rise to a decrease trend. The results also showed that the increase of suction pressure was benefit for the increase of heat transfer rate, leading to the improvement of heat utilization energy. Measures to enhance magnetite oxidation during sintering are discussed based on current understanding of the fundamentals that control the sintering process.

Jan 1, 2015

By L. J. Davies

Refractories usage in furnaces for the extraction of nickel from both sulphides and lateritic ores is reviewed. Recent changes in raw materials and basic brick qualities developed to meet the increasing demands of existing and new processes are outlined. Examples of used brick examinations to establish mechanisms of wear are given. The importance of physical and chemical properties are discussed. The use of simulative laboratory testing to aid in refractories development and selection is described.

Jan 1, 1988