By Chao Lian, Hongxu Li, Hao Bai, Wei Wei

"Application of high-emissivity coating on inner walls in industrial furnaces increases the furnace thermal efficiency. The coating with high emissivity strengthens radiation heat transfer in the furnace, however, according to Wien's displacement law and Planck's radiation law, under heating temperature, the wavelengths of the radiation transfer are mostly between 1-5 µm, implying that increasing emissivity of the coating in near infrared band is more effective for higher thermal efficiency. In this paper, a new CuO-ZnO-based coating material sintered at 1600K was developed. The emissivity of the samples were measured and the result shows that, in near-infrared band, the emissivity of the sample reaches 0.98 at 773K with 13at.% of CuO doped in ZnO. In addition, the effects of CuO doping and use temperature on emissivity were also discussed. Furthermore, crystallization behaviors of ZnO-CuO sintering were investigated by DTA,XRD and SEM-EDS etc., which offered information for possible optimal design of the material.1. IntroductionIndustrial furnaces are widely used in various industrial heating. For example, the metal smelting furnace, ore sintering furnace in metallurgical industry; the distillation furnace, cracking furnace in petroleum industry etc,. The research on efficient energy saving technology has important significance. High emissivity coatings are widely used in many high temperature applications to effectively transfer the heat by radiation [ 1]. The theoretical calculation and experimental studies have shown that, coated high emissivity coating in the heating surface is an effective method to enlarge the infrared radiation power [2].At present, the infrared high emissivity coating has been widely used in China, and have been achieved remarkable energy saving effect. According to Wien' s displacement law and Planck' slaw, most energy of the black body at high temperature is radiated in the wavelength range of l-5µm; however it happens that many materials have the low emissivity within this range. Thus, it is important to improve the near-infrared band emissivity of materials [3]."

Jan 1, 2013

By Peter Olubambi, Babatunde Obadele, Oluwagbenga Johnson

"The microstructure and corrosion behaviour of titanium carbide (TiC) reinforced duplex stainless steel matrix surface composites synthesized by laser melt injection technique was investigated. The surface melting operation was conducted using a 4.4 kW CW Nd:YAG laser with laser power of 1.5 kW, scanning speed of 0.4 to 1.0 m/min, beam size of 3 mm and argon shield gas flow rate of 4 L/min. The morphologies and microstructures of the coatings examined using field emission gun scanning electron microscope (FEGSEM) revealed homogeneous distribution of fine precipitates of TiC in the matrix, while X-ray diffraction (XRD) analysis confirm no phase change. TiC addition to the steels significantly increased hardness value to about 547 Hv0.1 but slightly decreased the corrosion resistance of the steels in 3.5% NaCl possibly due to the intergranular carbide coating that prevented chromium from forming continuous passive oxide layers.IntroductionComposite materials evolve from the idea of combining two basically dissimilar materials with different physical and mechanical properties to arrive at a product whose final properties are superior to those of the individual components [1]. Metal matrix composites (MMCs) are receiving much attention and are the focus of intense research and development worldwide for aerospace, automotive and other applications because of their excellent combination of ductility and toughness of the metallic matrix with high hardness and strength of carbides reinforced in the matrix [2]. Surface modification techniques such as laser, thermal spray, plasma spray, chemical vapour deposition have been use to fabricate MMCs. Laser melt injection (LMI) is a surface modification technique known since the 1980s [3] has been used to improve surface properties of metallic alloys such as aluminium, titanium and steels [4-6]. It involves the lateral injection of carbides, ceramics and cermets blown by a gas stream into a liquid metallic pool, created by laser irradiation of the top surface of the base material."

Jan 1, 2012

By Jenq-Gong Duh, Jyh-Wei Lee

"Hard chromizing process is a method for developing a surface modified coating providing wear, corrosion resistance and high temperature surface protection. Two carbon steels with 0.45 wt% and 0.95 wt% carbon contents, respectively, were chromized with pack cementation process at 950'C for 4 and 9 hours, respectively. The phase transformation and microstructure phenomena of chromized coating layer and matrix of two steels were studied with X-ray diffractometer and electron probe microanalyzer. (Cr,Fe)23C6 and (Cr,Fe)7C3 carbides and (Cr,Fe)2N1-x nitride phases were observed on the chromized surfaces. The thickness of chromized layers obeyed the parabolic rate law. The mechanism and diffusional kinetics of the chromizing process were proposed. The diffusivity of chromium in the (Cr,Fe)7C3 carbide phase was calculated using the moving boundary method.IntroductionChromizing process is one of the surface treatment technologies that can produce a chromium contained surface layer with sufficient corrosion and wear resistance on the steel matrix [1-7]. The relatively low cost and no ""line-of-sight"" restrictions are main advantages of chromizing. Adequate bonding strength of these coatings to the substrate was reported [7]. Chromizing process can be classified into soft chromizing and hard chromizing [2]. Soft chromizing is applied to steels containing less than 0.1wt% carbon through which chromium will be diffused. High temperature oxidation resistance improvement is the main purpose of soft chromizing process. On the contrary, the hard chromizing can be applied to steel containing more than 0.3wt% carbon, and very hard chromium nitride and carbide layers will be formed on the surface, which are very resistant to wear, corrosion and temperature [5-7]. In the previous studies on the Fe-Mn-Al-Cr alloy [5,7] and carbon steels [6], the thickness (X) of chromizing layers was analyzed and found the parabolic rate Jaw prevailed:"

Jan 1, 2004

By A. Slotwinski, R. E. Barry, M. M. Menon, P. T. Spampinato

"A coherent FM laser radar based sensor for remote metrology of plasma facing material surfaces in a fusion reactor is described. The sensor is capable of 3-D mapping of surfaces, based on a series of precise range measurements from large distances (up to 20 m). Other features include the ability to operate under adverse environmental conditions involving very high gamma radiation (3xI04 Gy/hr), ultra-high-vacuum (<I0-5 Pa), and high temperature (200°C). The paper describes the basic principles of the sensor, together with experimental results obtained with the sensor. The ability of the sensor for remote rendering of ""visual quality"" images without the need for any external illumination is also illustrated.IntroductionMeasurement of the features of large area surfaces (-1500 m2) to sub-millimeter accuracy, from relatively large distances (20 m), is necessary in the case of the International Thermonuclear Experimental Reactor (ITER -a 1500 MW fusion reactor that is currently in the design phase). Furthermore, the measurements may have to be performed after the reactor is temporarily shut down. During such shut-downs, the ITER in-vessel environment will be highly radioactive due to neutron activation of the reactor wall (gamma radiation field of 3xl04 Gy/hr), the vessel will be maintained under ultra-clean vacuum conditions (<10-5 Pa), and the plasma facing surfaces will be maintained at elevated temperature (200°C). Therefore, the precision measurements must be conducted remotely, and because of the large dimensions of the fusion reactor and the limited number of access ports, the measurements must be done from large distances. The reactor vessel is a large toroid. Fig. 1 shows the cross section of the toroidal vacuum vessel, and the location of the metrology probe. Because of the very large surface area involved, fast scanning capability is also needed to reduce the reactor down-time."

Jan 1, 1997

By Sang-Joon Kim, Hae-Geon Lee, Hyun-Jin Cho

"Decarburization phenomena on the surface of liquid iron have been simulated by numerical method and the results were compared to the experimental data. During the DeC process in a converter, a large amount of splashed droplets are generated from the top surface of the bath and consequently the reaction surface area is increasing tremendously. Since the decarburization mainly occurs at the interface, it is important to understand the reactions on the liquid iron droplets. The flow and species concentration fields around liquid droplets taking into account the reaction of carbon with oxygen at the interface were calculated by a commercial CFD code FLUENT which solving multiphase Navier-Stokes equation with Volume Of Fluid method, species transport equations and energy transport equation. The initial carbon concentration was fixed to 4 wt% and the concentrations of oxygen in the atmosphere were varied from 5 to 50 wt%. As comparing the numerical calculation with experimental data written in the reference, the results have a good agreement for decarburization rate.IntroductionIn a primary steelmaking process, one of the main functions is to decarburize from hot metal and the 4% of carbon is decreased to about 0.5% of carbon. Even though there are some possible reactions leading to the removal of carbon from hot metal, the main reaction occurs on the free surface by direct oxidation of carbon at the gas-liquid interface with producing the carbon monoxide gas. In many metallurgical processes involving a jet impinging onto a steel bath surface, especially in a Basic Oxygen Furnace (BOF) converter, it is important to understand the behavior of molten iron droplets splashing out of the steel. The iron droplets are generated by an oxygen or air jet blowing and it increases the total surface area of liquid iron tremendously. Since the decarburization reaction is mainly affected by the surface area, it is necessary to verify the decarburization phenomena around the splashed droplets from liquid iron in order to allow an analysis ofBOF process possible."

Jan 1, 2011

By Na Wang, Chao Du, Hongmin Zhu, Kai Huang, Shuqiang Jiao

"Niobium aluminides were directly synthesized by a sodiothermic reduction process of NbC15 - AlCb which was dispersed into LiCl - KCl - NaCl - CaCb melts. The melt supplied a homogenous reaction medium which was substantially beneficial to the co-reduction of Nb and Al to form niobium aluminides in situ. The reduction was performed at 500°C for 4 hours. The products were analyzed by X-ray diffraction (XRD) and scanning electron microscope (SEM). The corresponding results indicated that niobium aluminides powders were successfully synthesized.1. IntroductionNiobium aluminides have received considerable attention as high-temperature structural materials, due to their high melting points, relatively low density, high strength, excellent oxidation and creep resistance [1-4]. Figure 1 shows that there are three intermetallic compounds in the Nb - Al binary [5], which includes Nb3Al (A15 structure, Cr3Si type), Nb2Al (D8b structure, cr-CrFe type) and NbAb (D022 structure, TiAb type). These niobium aluminides have been used in turbine blades or in stationary gas turbines [6-8]. However, despite their attractive features, the ir applications are still limited by the long and costly fabrication process [9, 10].Niobium aluminides were industrially fabricated by the mechanically alloyed process [11-13]. Traditionally, niobium is extracted from Nb2O 5 or K2NbF7 by a metallothermic reduction process while aluminum is produced by the Hall-Heroult process of Ah03 electrolysis. Based on the extraction of Nb and Al, respectively, niobium aluminides is synthesized by a mechanical powder alloying process. The present process for making niobium aluminides requires a set of complicated equipment, has high production cost and time consuming [14, 15].The purpose of this work is to present the simple, economic and direct synthesis of niobium aluminides powders utilizing a sodiothermic reduction from NbC15 - Al Cb dispersed into molten salts."

Jan 1, 2011

By Selvin Yesilay, Guray Kaya, Bekir Karasu, Asli Cakir

"In this investigation, the wastes of Eti Maden Kirka Boron Company of Turkiye were evaluated in the production of diopside and anorthite-based glass-ceramic glazes suitable for porcelain tiles fast and single-fired under industrial conditions. First of all, high wear resistant frits were produced with the use of concentrator and derivative borax wastes. Second of all, pre-engobed porcelain tile bodies were coated with the standard and newly produced frit-based glazes and industrial fast single-firing was employed. Final products were undergone to the certain standard tests to determine their Vickers hardness, wear resistance, thermal expansion coefficient values, gloss and coloring parameters. The micro-structures and phase formations of the fired glazes were also studied. Consequently, it was confirmed that the utilization of borax solid wastes in fast single-fired porcelain tile glass-ceramic glazes is possible. Introduction Porcelain tiles were introduced at the end of 1980s by Friandre, one of the leading Italian porcelain manufacturers. The American National Standard Specifications for Ceramic Tile defines porcelain tiles as: dense, smooth, impervious (with water absorption value less than 0.5 %) and stain resistant [1]. The excellent technical performances for ceramic tiles, such as mechanical, wear, frost and chemical resistance that make their use possible in indoor and outdoor building applications [2-3]. In the last decade, the growth rate of the global production of porcelain tiles increased more than those of other ceramic products; in fact, the technical properties of porcelain tile, coupled with even more improved aesthetic appearance, gave it a prominent role on the tile market [2]. Glass-ceramics are composed materials of one or more crystalline phases immersed in a residual glassy phase [4-5]. Glass-ceramic technology is based on controlled nucleation and crystallization of bulk glass [6]. The concepts of controlled crystallization of glass designate the separation of a crystalline phase from the parent glass in the form of tiny crystals. Their growth rate and final size are controlled by a suitable heat treatment [7]."

Jan 1, 2008

By Toshiyuki Hiranami, Keizou Uematsu

"AbstractionSpray freeze drying method was proposed to fabricate ·ceramic: powder granules for high performance ceramics. Obtained granules and their green compact were characterized by SEM and immersion liquid technique. Granules have a spherical shape of about l 00 µ m in diameter, ·and no binder segregation was found with the immersion liquid technique. The granule had sufficient strength for usual handling, while the strength was much lower than that of granules prepared by conventional spray-drying. Unlike the conventional green compacts, granule interfaces were not observed in the green body made with the spray-freeze dried granules.IntroductionIt was well kn9wn that spray-dried granules have binder segregation layer on their surfaces. The trace of this segregation layer survives in the later processes i.e. compaction and firing, and behaves as fracture origins in the sintered bodies. The origin of this problem is solvent drying process from slurry droplet surface in spray drying system. As alternative method we propose a freeze drying process for granule preparation, in which solvent is remove by sublimation though the process, binder segregation can be prevent.In this study, we applied spray freeze drying method to fabricate alumina powder granule, and characterized the obtained granules, and their green compacts and sintered bodies.Experimental procedure.Alumina powders and additives aqueous solution were mixed for 24 hours using a ball mill to· prepare the slurry for spray freeze drying. .The solid loading of the slurry was 30vo1%. Deflocculant (PAA-NH4 type) was added 0.5mass%, and the binder (PVA). 1.0, 2.0 or 3.0mass% of alumina. Obtained slurries were sprayed into liquid nitrogen to make frozen granules. The granules were freeze dried.For the characterization of the granules, immersion, liquid technique observation and single granule strength test were carried out. Strength of individual granule wa5 measured using micro compression testing machine (MCTM, SHIMADZU). Granule strength was calculated from following equation."

Jan 1, 2000

By Zhang Libo, Wang Xin, Peng Jin-hui, Ju Shaohua, Guo Sheng-hui, Xu Lei, Huang Meng-yang

"China is lacking high grade titanium ores. This work intends to leach impurities such as Fe, Ca and Mg from a low grade titanium ore, to increase the grade. The original material contained 65% TiO2 , 16.12% Fe, 9.4% CaO + MgO, 4.2% SiO2, 1.25% A12O3, and the particle size is between 0.053-0.045mm. Microwave energy was used to enhance the leaching effect. The results showed that when normal heating was used to leach the mineral, the extraction of impurities Fe, Ca and Mg was very low. However, when microwave energy is introduced, the extraction of Fe, Ca and Mg increased dramatically. The optimized conditions are: relative power 5W/g, the ratio of concentrate to HC1 isl5%, leaching at 160°C for 20 min with a ratio of liquid to solid 12:1 mL/g. The material obtained under these conditions contains 92.73% TiO2, 0.207% Ca + Mg, 0.8% Fe, with 94.6% Ti recovery. The poduct meets with the quality for boiling chlorine.IntroductionThe resources of titanium are very abundant, and are distributed all over the world. There are almost 140 minerals containing TiO2 with a content of more than 1%. However, there are only several minerals which can be used for producing sponge titanium. They are mainly rutile and ilmenite. The grade of nature rutile concentrates is higher than 95% TiO2, and it is a high quality raw material. But the resources of nature rutile are relatively low; after mining for many years, its resources are exhausting gradually. Although ilmenite reserves are great, ilmenite cannot be used as a raw material because of its low content of TiO2, only 45-70%; also it has a high impurity content of Ca, Mg and Fe. In these years, there is a tendency for titanium industry to use high grade concentrate."

Jan 1, 2012

By Akram Alfantzai, Farzad Mohammadi, Maysam Mohammadi

"Degradation of lead anodes has always been a major concern among the electrowinning industries. In this study, the effect of agitation of the zinc electrowinning solution on the integrity of lead anodes was investigated. Galvanostatic experiments were performed at 37±0.5°C using 0,600 and l000rpm magnetic stirring rates for 24 hours. The Pb02 layer formed on the anode surface was reduced to PbS04 (discharged). The discharge information was used to calculate the amount of Pb02 present on the surface. Weight loss measurements along with the discharge calculations revealed that the degradation rate of the lead anode increased as the solution was stirred more vigorously. Furthermore, the amount of remaining Pb02 on the surfaces was decreased as a function of solution velocity. Therefore, it may be concluded that, degradation rate oflead anodes is controlled by detachment of the corrosion products from the surface rather than by electrochemical reactions. IntroductionElectrowinning is one of the extraction stages of zinc, in which pure zinc is deposited from acidic solution after froth flotation, roasting and leaching processes. The anode electrode materials play important roles in the electrowinning process. Their electrocatalytical capacities determine the oxygen evolution overpotential, and consequently the cell potential and energy efficiency of the zinc electrodeposition [l]. Purity of the zinc deposited on the cathode is affected by the solubility and corrosion resistance of the anode materials. Using insoluble materials as anode in the electrowinning leads to the higher purity of the deposited metal on the cathode[2]. Lead (Pb) and its alloys have been used as the anode in the zinc electrowinning because of its special properties such as relatively low cost, low melting point, insolubility in solutions containing sulphuric acid and high conductivity in both states of metallic and oxidized [3, 4]. In zinc electrowinnig, zinc reduction occurs on the cathode (reaction 1) and the oxygen evolution reaction (OER) (reaction 2) is the main anodic reaction [5, 6]."

Jan 1, 2013

By C. A. Nogueira, F. Pedrosa, F. Margarido, R. N. G. Guerra

"A hydrometallurgical process for recycling spent Zn-MnO2 batteries was developed, involving leaching with sulfuric acid, purification by precipitation and metals separation for further recovery. Leaching of zinc oxide was easily attained while for manganese oxide was rather difficult depending on temperature and acid concentration. At 90°C and with the liquid/solid ratio of 20 L/kg, more than 95% of zinc is recovered in 30 minutes with 0.5M H2SO4. To attain similar recovery for manganese, higher levels of acid concentration and time are needed (e.g 0.7 M and 2 hours). After leaching a purification step is necessary to remove iron co-dissolved through Fe(III) precipitation. Separation of zinc from manganese by solvent extraction with 1M DEHPA follows in the process route. The countercurrent multistage separation diagram developed allows the production of a zinc electrolyte with 120 g/L Zn and 0.005 g/L Mn, and a raffinate with 16 g/L Mn and 0.013 g/L Zn.IntroductionThe recycling of spent Zn-MnO2 batteries is carried out by dedicated recyclers using several process alternatives [1]. Most of the running processes use pyrometallurgical technologies [2] based on zinc distillation. Alternative treatments by hydrometallurgy have been reported [3-5] but its application is scarce.In order to contribute to the development of alternative solutions, a process for recycling batteries based on Zn-MnO2 systems has been studied. The process is based on the hydrometallurgical treatment of spent batteries in sulfuric acid media (Figure 1). The process starts with the physical processing by shredding using cutting grinders, where the batteries are opened and size reduced, allowing the liberation of the interior electrode particles or pastes. The fines can be then separated and the coarse material containing the steel scrap can be treated to remove the remaining aggregate electrode. The final scrap also contains some plastics and other non-metal materials and can be further valorized."

Jan 1, 2008

By Somayeh Dashti, Ehsan Vahidi, Fereshteh Rashchi

"The main goals in zinc electrowinning process are decreasing of power consumption and increasing of current efficiency. In this study, the electrowinning of zinc in the presence of different additives in electrolyte were established and Arabic Gum, Gelatine, sodium lauryl sulphate and l-hexyl-3-methylimidazolium hydrogen sulfate in the five levels using Taguchi method was examined. In our previous researches, using orthogonal array, effect of zinc electrowinning parameters such as anode type, current density, sulphuric acid concentration, temperature and zinc ion concentration was studied and the optimized conditions for zinc electrowinning was obtained. Anode composition: Pb-Ag 0.5%-Sn2%-Sb1%, current density (A/m2):500, acid concentration (g/1):165, temperature: 60°C, zinc ion concentration (g/1):70. The main goals in zinc electrowinning process are decreasing of power consumption and increasing of current efficiency. ln this research, the effect of four additives: Gum Arabic, Gelatine, sodium lauryl sulphate and an organic material in the four levels with Taguchi method was examined. ln fact the effect of electrolyte environment and determining the best electrolyte under the optimized conditions is the main aim of this study.IntroductionDue to its low cost and abundance, zinc is widely used in the production of brass, galvanized steel, sacrificed anodes and primary and secondary batteries [I]. Some 80% of world primary zinc production is derived via roast-leach-electrowinning processes [2-4]. In the electrowinning process to both improve final product quality and current efficiency the leachate should be purified [5].To produce zinc a current method is to extractit from acidic zinc sulphate solutions by electrolysis with aluminum cathodes and insoluble lead-based anodes [6]. Though the electrolytic processing of zinc has been performed for many years, there are still current efficiency problems in the cathodic process. These low efficiencies (88- 93%) have a serious impact on the costs associated with the energy consumption. On the other hand, these low efficiencies increase energy consumption and decrease the quality of the surface morphology [7- 8]."

Jan 1, 2012

By Heinz Boeni, Daniel Ott, Uca Silva

"Latin America is facing a rapid increase in internet use. Penetration with electronic equipment is in some countries approaching the level of industrialized countries. There is an evident need to resolve the management of “end-of-life” computers and other electronic equipment. Several studies in Latin America assessed the increasing e-waste quantities and confirmed the importance of a sustainable e-waste management. This paper gives an overview on the status on e-waste management in Latin America, explains the challenges for establishing an e-waste management system in a developing country setting and highlights the social and economic potential and the possibilities of a regional approach.IntroductionGlobal ICT-Trade and generation of e-waste from ICTThe global production of electronic devices and particularly of Information and Communication Technologies (ICT) faces the biggest industrial expansion of the history: OECD figures show that global trade of ICT technologies has reached 7.7% of the gross world product by 2004, the major proportion accruing from China [1]. In 2006 an estimated 230 million computers and 1 billion cell phones have been sold worldwide which corresponds to a volume of 5’848’000 t [2]. As a consequence, Waste from Electrical and Electronic Equipment (WEEE), or e-waste, is by far the fastest growing waste component. It reaches more than 5% referred to Municipal Solid Waste and e-waste generation in developing countries according to UNEP is expected to triple by 2010 [2].According to the OECD e-waste is “any appliance using an electric power supply that has reached its end-of-life” [3]. The European WEEE directive [4] distinguishes 10 categories of ewaste: Big household appliances, Small Household Appliances, IT and Telecommunications Equipment, Consumer Equipment, Lighting Equipment, Electrical and Electronic Tools, Toys, Leisure and Sports Equipment, Medical devices, Monitoring and Control Instruments, and Automatic dispensers. In this paper e-waste and WEEE are used as synonyms. Focus will be laid on e-waste from IT equipment (IT-waste), corresponding to category 3 of the European WEEEDirective."

Jan 1, 2008

By Alejandro R. Alonso, Lizet Alvarado, Gretchen T. Lapidus

"Cobalt and lithium recovery from spent Li-ion secondary batteries has been increasingly studied in recent years due to the high value of both metals and the low proven reserves for lithium. The standard method employed until now has been the deactivation and crushing of the batteries, followed by leaching of the L1C0O2 spinel from the battery cathode using acid solutions, such as 1.5 to 2.0 M HC1 or H2SO4, in a temperature range from 120°C to 250°C. Once leached, the cobalt is separated by electrodeposition and the lithium by precipitation, using large amounts of carbonate to bring the solution to alkaline pH values. In the present work, citric-thiosulfate solutions are used for the spinel leach at room temperature, favoring a reductive environment at room temperature, which stabilizes the cobalt(II) as cobalt citrate and lithium(I) at pH 5, and recovers approximately 99% of both metals.IntroductionThe Li-ion batteries industry has become an important economic sector in recent years. This type of battery is the most promising system for energy storage, because of its high efficiency in charge-discharge cycles, and its adaptability to many configurations. The demand will probably increase because of the need for mobile energy sources in many types of devices ranging from cell phones, tablets, and laptops to medical, navigation and sophisticated communication equipment and even in automobiles.One major problem related to the use of these batteries is the method employed for recycling the components, mostly cobalt and lithium. Currently, there are two processes employed on an industrial scale: the Sony/Sumimoto process, used since 1990 [1] and the Toxco Process [2]. In the first case, incineration is used to open the batteries and at same time volatilize the organic solvents. After that, the metals (copper, iron and aluminum) are physically separated. The cobalt and lithium are recovered as oxides and then thermally treated in order to recycle them for new batteries manufacture."

Jan 1, 2012

By C. Beckennann, C. Y. Wang

"Computer simulations of structural and compositional development in equiaxed dendritic alloy solidification are performed using a recently developed multi phase model. The model not only accounts for the transport phenomena occurring on the macroscopic (system) scale, but includes also the grain nucleation and growth mechanisms taking place at various microscopic length scales. In this paper, a numerical technique consisting of a fully implicit control-volume based finite difference method and a multiple time step scheme is developed for accurate and efficient simulations of both micro- and macro-phenomena. Sample numerical results are presented to reveal the effects of liquid now and crystal sedimentation on segregation and the final grain size distribution. In particular, the importance of the interplay between the dendrite microstructure and multiphase now patterns is shown.IntroductionIn recent years, modeling of equiaxed dendritic solidification without convection has experienced considerable progress (1,2]. Nucleation and growth kinetic laws have been coupled with transient heat conduction calculations to determine the solidification microstructure. However, modeling of equiaxed dendritic solidification with melt convection and solid movement has not been attempted so far, largely because of the complications associated with the transport of free equiaxed crystals in the melt. The gravity-induced transport of free crystals is fundamental to the development and extent of the equiaxed zone and also greatly affects the columnar to equiaxed transition. Another possible effect of crystal sedimentation or floatation is to cause severe macrosegregation as well as structural inhomogeneities. The only study available in the literature that accounts for both liquid convection and solid transport is by Ni and Beckermann (3], but deals with globulitic structures (as opposed to dendritic)"

Jan 1, 1994

By R. S. Celmer

The distributions of cobalt, molybdenum, copper, and selenium between nickel matte and silica-saturated iron silicate slag have been determined in the region of the metallic saturation boundary, at 1523 K. Results are given as a function of the composition of the coexisting Fe-Ni alloy and the activity of iron in the system. Under strongly reducing conditions, these minor elements display a marked preferential accumulation in the sulphide phase. It is shown that the dissolution of cobalt and molybdenum in slag follows an oxidative mechanism, and distribution equilibria are correlated with the oxygen potential. From these data, the thermodynamic properties of cobalt in nickel matte are computed. Further, comparisons of minor element partitions are made between the nickel and copper matte smelting cases under metal saturation conditions.

Jan 1, 1988

By G. Haesebroek

In L969 Metallurgie Hoboken-Overpelt started an industrial plant for the separation of iron and zinc from a concentrated CoCL2 solution. Iron and zinc are extracted in column contactors by a solvent containing 12 vol % of tertiary amines in xylene. The extracted metals are stripped from the pregnant organic phase by precipitation with a NaOH solution at pH LL. In this paper an overview is given of the industrial process. In order to overcome some drawbacks of this process (low flash point of the diluent, reagent consumption, batchwise stripping) an alternative solvent extraction process has been examined. In this alternative process, iron and zinc are extracted with an or¬ganic phase containing 50 vol % of TBP in Escaid 110. The pregnant solvent is stripped with water in conventional mixer settlers. Despite the ability of this process to overcome most of the inconveniences due to the use of tertiary amines, it suffers from the poor stability of TBP in concentrated chloride solutions, resulting in unavoidable and inacceptable precipitation phenomena in the stripping section.

Jan 1, 1988

By L. J. Lutz

The U.S. Bureau of Mines has developed an electrorefining process to recover Ni, Co, Cr, and other metals from mixed and contaminated superalloy scrap. The superalloy scrap is cleaned then directly electrodeposited as a Ni -Co deposit. The process recovers approximately 90 pct of the Ni-Co available from the scrap as a 99t pct pure Ni-Co alloy. During electrorefining the electrolyte undergoes a purification process which results in Cr and other refractory metals reporting to the purification residue. Operating data is given for a 3-L compartmented electrolytic cell. Techniques for the removal of Fe, Cr, and trace impurities from the recycled electrolyte are outlined. The economics of a facility producing 15 mt/d of a Ni-Co alloy are also discussed.

Jan 1, 1993

By M. F. El-Demerdash

The activity distribution diagrams for different species in aqueous systems are developed. Computational method may be considered as an extension of the Activity-Term method introduced by the authors to construct EH-pH diagrams. In the Activity-Term method, all activities of different species are evaluated before deciding the most stable one. In the present study, a factor is assumed to allow for the conservation of the element. At any point, the total concentration of all species should contain only the input m moles of the element (elements) considered. This approach is applied to Zn-, 5-, and Zn-S-H2O and activity distribution diagrams are plotted as a function of pH, at different potential levels and at different temperatures.

Jan 1, 1990

By William A. Hockings

Methods for the measurement of liberation of finely ground iron ores are described. The general method consists of separating a sample of the ground ore into a number of size fractions, followed by measuring the liberation of each fraction. The size separation has been done using electro-formed screens of 20-, 10-and 5-micrometer apertures, and also by air elutriation. Liberation (i.e., the distribution of compositions of individual particles) has been measured by optical microscopy. A computer pro-gram was used to adjust the raw count data so that it agrees with the chemical analyses of the size fractions. Various ways of presenting the results are given, and Some applications of the results to flotation processing are discussed.

Jan 1, 1981