By R. J. Evans

The Combined Metals Reduction Co.'s plant is at Bauer, Utah. It was built primarily to treat ore from the Combined Metals mine at Pioche, Nevada. Shortly after its completion, the company acquired the old Honerine mine, and ores from this mine, as well as custom ores from widely scattered districts, are now being treated at the Bauer plant. Pioche Ore The Pioche ore, which comprises about 50 per cent. of the mill feed, occurs as a replacement of an impure thin-bedded limestone. The lime beddings are separated by thin layers of micaceous shale containing appreciable quantities of sericitc and graphite. The ore is an exeeptionally fine-grained, dense mixture of minerals and gangue, assaying approximately 0.03 oz. gold, 7.2 oz. silver, 7 per cent. lead, 15 per cent. zinc, 16 per cent. iron, 29 per cent. insoluble and 1.5 per cent,. lime. Of the total lead 7 per cent. is in the form of sulfate and carbonate. Approximately 10 per cent,. of the ore consists of chert nodules impregnated with barren pyrite; the nodules average 0.8 mm. in size, and ire extrcmely hard, compared with the other constituents of the ore. Microscopic examination of Pioche ore ground to 80 per cent . minus 150 nicsh shows pyrite, sphalerite and galena still attached. Early Attempts at Ore Dressing Metallurgists, both professional and those working for private companies, have been more or less familiar with the Pioche ore sinee. 1913; in fact, a total of 35 commercial and plant laboratories expenmented with the ore between 1913 and 1921. The work during this period was decidedly negative, it being seemingly impossible to effeet a satisfactory separation of the valuable minerals into marketable products. In 1913, it was recognized that fine grinding-—that is, about minus. : 200 mesh—-was required to liberate the minerals from one another, and from the gangue, but such fine grinding was not considertd practicable at this time.

Jan 1, 1928

By Stuart Croasdale

Not long ago I was called upon to conduct some experiments on the treatment of ores from the New Cornelia copper mine, Ajo mountains, Arizona, for the Calumet & Arizona Copper Co. The problem was a very interesting one and contained some unusual features. Incidental with this problem was the utilization of a large amount of low-grade pyrite in the Bisbee mines of the company, provided this could be accomplished by any feasible method. The New Cornelia mine is situated 45 miles south of Gila Bend, the nearest railroad point, on the Southern Pacific Railroad. It is about 160 miles, almost due west, from Tucson. This section is one of the most arid in the United States. The normal annual precipitation, as given by the United States Weather Bureau covering a period from 1870 to 1901, is 3 to 5 in. During June and July, 1913, the records kept by the company gave the following results. These are all I have available, but they show the enormous evaporation that can be expected, which may be a factor in leaching operations on a large scale. Temperature, Degrees F. High Low Average June...................... 112 62 84.0 ' July...................... 115 71 87.8 Evaporation June July Concrete tank, inches............ 11.7 10.72 Iron tank, inches.............. 14.8 13.07 Rainfall, inches................ None 0.77 Cloudy days................... None 10.00 Aside from several springs about 10 miles from the property, the nearest known water in quantity at the time these experiments were made was the Gila river at Gila Bend, 45 miles distant. Part of the developinent of the property of course included drilling for water in the valley, which was in progress at the conclusion of my experiments. The ore deposit itself is unusual. It consists of of intrusive plug of monzonite or granite porphyry. Chalcopyrite, bornite, and magnetite are finely disseminated throughout the magma in sufficient quantities to make the greater part of the mass commercial ore to a certain depth.

Jan 1, 1915

By H. S. Rawdon

One of the most vital problems in the manufacture of steel at present is the occurrence of the defects that have been popularly termed "snow flakes," "flakes," or "scabs." Particularly is this the problem of many manufacturers who, during the past 2 yr., have undertaken large-scale production for the first time. A study of the microstructure of such defective material throws considerable light upon the nature of these defects and is essential before measurcs may be taken for the elimination of the defects. Flakes do not appear to be found in the plain carbon steels; they have been found. however, in abundance in some of the simple alloy steels that are being used in such vast quantities; vie., nickel steel of the approximate composition, 0.40 carbon and 3.5 per cent. nickel, and in the chrome-nickel type. The present article summarizes the characteristic features of defective steel of the flaky type as they have been found by laboratory study of numerous specimens, and it aims to show the conditions within the metal that are favorable to the occurrence of this type of defect without entering into the details of mill practice (size of ingot, design of molds, rate of cooling, distribution of cooling stresses, etc.), all of which conditions appear to play a role in the production of these defects. MacrostrUctURe To one familar with flaky steel, the appearance of "snow-flakes" is unmistakable and is not to be confused with other types of defects. Figs. 1 to 6 show the appearance of fractures of steel showing this type of defect; the white silvery area, which always has the appearance of being of a very coarsely crystalline structure, in the specimen stands out in bold contrast to the darker background and readily justifies the use of the term "snow-flakes." Fig. 1 shows the appearance of the faces of the two halves of a nickel-steel forging that has been split to show the interior flakes. Fig. 2 is a nickel-steel bar (carbon 0.40 per cent.,

Jan 1, 1920

By R. G. Treuting, R. M. Brick

Despite the basic importance of slip in the plastic deformation of metals, and the considerable experimental investigation, thought, and speculation that have been devoted to the fundamental nature of these processes, surprisingly few data have been reported regarding the microscopic appear- ance and distribution of slip lines,‡ the external manifestation of the slip process. Photographs hitherto reproduced in the literature are in general at low or unspecified magnifications with no correlation to the prior shear. A single-crystal cylindrical tensile specimen of alpha brass about 1/2 in. in diameter, one of many previously prepared by H. L. Burghoff,1 was available for study. A plane about 3/16 in. wide, parallel to the specimen axis and normal to the plane containing the slip direction and the specimen axis, was ground and metallographically polished along the entire 5-in. gauge length. Heavy etching produced a surface free of both scratches and flow. The specimen was strained in tension until slip markings first became visible on the polished surface (Figs. 1 and 2). Re-stressing the crystal caused additional markings to appear at an initially lower stress than previously was required. Stretching the specimen to produce a dense concentration of slip lines caused such variations in level in the polished surface (normal to the slip direction) that microscopic study at higher magnifications became impossible. After annealing 15 hr. at 850°C, the specimen recrystallized to form two grains with a boundary approximately normal to the specimen axis and about midway along its length. Each was X-rayed, and two planes were again polished along the length of the specimen, in this case each parallel to the slip direction in one of the two crystals. A light longitudinal scratch parallel to the specimen axis was drawn down the center of each plane. A Huggen-berger extensometer was attached to the crystal A, whose slip plane would have the higher resolved shear stress of the two, and the specimen was again strained in tension.

Jan 1, 1942

By R. M. Brick, R. G. Treuting

Despite the basic importance of slip in the plastic deformation of metals, and the considerable experimental investigation, thought, and speculation that have been devoted to the fundamental nature of these processes, surprisingly few data have been reported regarding the microscopic appear- ance and distribution of slip lines,‡ the external manifestation of the slip process. Photographs hitherto reproduced in the literature are in general at low or unspecified magnifications with no correlation to the prior shear. A single-crystal cylindrical tensile specimen of alpha brass about 1/2 in. in diameter, one of many previously prepared by H. L. Burghoff,1 was available for study. A plane about 3/16 in. wide, parallel to the specimen axis and normal to the plane containing the slip direction and the specimen axis, was ground and metallographically polished along the entire 5-in. gauge length. Heavy etching produced a surface free of both scratches and flow. The specimen was strained in tension until slip markings first became visible on the polished surface (Figs. 1 and 2). Re-stressing the crystal caused additional markings to appear at an initially lower stress than previously was required. Stretching the specimen to produce a dense concentration of slip lines caused such variations in level in the polished surface (normal to the slip direction) that microscopic study at higher magnifications became impossible. After annealing 15 hr. at 850°C, the specimen recrystallized to form two grains with a boundary approximately normal to the specimen axis and about midway along its length. Each was X-rayed, and two planes were again polished along the length of the specimen, in this case each parallel to the slip direction in one of the two crystals. A light longitudinal scratch parallel to the specimen axis was drawn down the center of each plane. A Huggen-berger extensometer was attached to the crystal A, whose slip plane would have the higher resolved shear stress of the two, and the specimen was again strained in tension.

Jan 1, 1942

By M. Gensamer

ALTHOUGH a large number of X-ray photograms of cold-rolled steel have been published, two circumstances have led to the experimental work reported in this paper. The first is that no complete study, making use of the pole-figure method of Wever1, has been made of cold-rolled low-carbon steel. Wever has published pole figures of mild steel sub-jected to plane parallel deformation1,2 and undoubtedly he has applied the method to cold-rolled mild steel, but the authors have not found these data published. Kurdjumow and Sachs3 have applied the method to the study of rolling and recrystallization textures in electrolytic iron; their results will be referred to later. The reason for this dearth of papers using the pole-figure method is obvious; a greater number of photograms and more analytical work (although this work is quite simple and straight-forward) are required to construct a pole figure than most investigators have felt worth while, despite the fact that no other method of which the authors are aware will satisfactorily depict the orientations of the crystal-lites in a polycrystalline aggregate. The second circumstance that led to the work reported in this paper was the appearance of a paper by Wayne A. Sisson4 on the same subject. In his valuable study of the factors influencing the development of pre-ferred orientations in cold-rolled mild steel, Sisson made one observation that required confirmation; that is, that at some stage of the rolling proc-ess the type of preferred orientation changed from the type that gives a photogram characterized as a "six-point" X-ray pattern to that known as a "four-point" pattern. A similar observation had been made by Tam-mann and Heinzel5, who studied the orientations developed in the rolling of steel by the specular reflection of light from the etched surface of rolled samples. These workers also found that the type of preferred orientation

Jan 1, 1936

By Hans Conrad, W. D. Robertson

FORMAL theories of yielding and flow have been developed to describe thermally activated plastic flow in metal crystals.'-" hey are all based on Becker's' original idea that thermal fluctuations aid the applied stress in overcoming internal barriers to flow and lead to the following relation. where j is the strain rate; C is a constant which includes a frequency factor, the entropy, the number of flow units, and the amount of strain associated with each successful fluctuation; E(T) is the activation energy associated with flow, and is a decreasing function of the applied stress, 7; k is Boltzmann's constant; and T is the temperature in OK. The various theories differ mainly in the model chosen and in the nature of the relationship between the applied stress and the activation energy. Beckerl and Orowan' suggest a relationship of the form E a(Ti — t)2, where .ri represents the stress required for flow without the aid of thermal fluctuations; Kauzmann,3 Cottrel1,5 and Seeger6,7 suggest E a(t — t) ; Fisher8 suggests E while Cottrell and Bilby4 suggest a more complex relationship between E and 7. Additional data are needed to test these various theories., esweciallv- in view of Dorn's9 ork. which indicates that the activation energy for creep is independent of the stress and strain. The present paper presents the stress-strain data derived from incremental loading of magnesium single crystals in tension and direct shear, in the temperature range of 78" to 364°K. Incremental loading was employed in order that the creep component of the strain could be determined. Stress-strain curves of aluminum10-13 and copper" single crvstals. derived from incremental loading tests, have been found to be in agreement with those obtained by the more conventional constant strain rate or loading rate tests. Two types of tests were conducted in the present investigation: 1) tests in which the temperature was maintained constant throughout the entire

Jan 1, 1958

By Jay R. Burns

Two magnesium sand-casting alloys are commonly favored in the United States. These are referred to as H and C alloys (Dow Chemical Co.) or AM265 and AM260 alloys (American Magnesium Corporation). Both are of an aluminum-zinc-manganese type. H alloy contains 6 per cent aluminum and 3 per cent zinc and is characterized by relatively good toughness. C alloy contains g per cent aluminum and 2 per cent zinc and is employed where high yield strength and pressure tightness are required. Examination of magnesium castings poured in Europe and England,1,2 however, demonstrates that H and C alloys are replaced by A8 and AZ91, respectively. That is, A8 represents a magnesium alloy having superior toughness while AZ91 is suitable for high yield strength and pressure-tight applications. The basic difference between the American and European alloys is that the foreign alloys employ a somewhat higher aluminum content and less zinc than is found in H and C alloys. The mechanical properties of the alloys, when divided into high and low-aluminum groups, are quite similar, as determined from separately cast foundry-control type test bars.3 In this paper the decrease of mechanical properties caused by any given amount of microporosity is measured for H, C, A8, and AZ91 alloys. The relative susceptibility of each of the four alloys to microporosity is also determined. Typical mechanical properties and nominal chemical analyses are reported in Table I. [ ] The apparent similarities between the two alloys in each group have led to considerable discussion as to the relative merits of each of the compositions.2 Popular points for comparison between the alloys have been the relative susceptibility of each of the four alloys to microporosity5 and the effect of this microporosity on their mechanical properties. It is primarily intended, in this paper, to show the

Jan 1, 1946

By R. V. Norris

It was stated in a former paper1 that an intensive study of anthracite costs was being made by the engineers of the United States Fuel Administration. The results of this study are now available and are offered as a supplement to the former paper. Anthracite costs as reported for the 6-months period, December, 1917, to May, 1918, inclusive, as compiled by the Federal Trade Commission, were used as a base, and charts similar to those described in the former paper were made for the standard white ash anthracite and for red ash and Lykens valley coals. Adjustments The adjustments of cost from a reported to a price-fixing basis, as described for the bituminous methods, were applied but showed only minor adjustments as necessary. The great spread in anthracite prices on the varyingsizes, which for the 6-mo. period under review ranged in average from $5.244 for nut to $2.074 for barley coal, makes the question of the percentage of sizes produced at the different collieries a vital one. The realization with the same prices for each size must be within very wide limits, when it is considered that the percentage of prepared coal reported from different collieries varied from over 80 per cent. to below 30 per cent. for fresh-mined coal. Hence, as the spread in prices for the various sizes must be predicated on some percentage, it is essential to find some method of adjustment to allow for this variation. The logical method of adjustment is to calculate actual costs to costs as of the standard percentage of sizes, so that the margin between the adjusted costs and the average realization shall be the actual margin for each colliery between its actual costs and actual realization due to its particular percentage of sizes. As a base for realization the actual percentage of sizes for fresh-mined coal for the 6-mo. period was adopted. This percentage is given in Table 1.

Jan 1, 1920

By Walter R. Hibbard

THE term lineage was first introduced by Buerger1 to denote dendritic branches, grown from a crystal nucleus during solidification from the liquid, with imperfections in alignment of the order of 10-1 [ ] to 10-4 cm. These imperfections are associated with distortions of the dendrites caused by the subsequent solidification of the inter-dendritic filling and are illustrated in Fig 11. Buerger etched zinc single crystals made by the Bridgman2 method to develop this dendritic pattern and show lineage microscopically. Since maximum crystal growth in face-centered cubic metals occurs along the [100] directions,2 lineage would appear in copper as small deviations of dendritic branches from these directions. Elam4 and others5-8 reported etching effects resulting from coring along the cube face traces of various copper alloy crystals. These traces were used by Samans8 to orient single crystals. Williamson9 noted a "lined structure (in alpha brass single crystals) consisting of an ordered arrangement of etch pits" which were probably traces of {100} planes but somewhat uncertain because they were never straight (i.e., apparently lineage). Greninger10 described the distortion and multiplicity of Laue spots in back reflection X ray photograms of copper single crystals showing lineage. The present investigation includes metallographic, X ray and property studies of lineage in large grain and single crystal specimens of copper. PREPARATION OF SPECIMENS Specimens 10 in. long and ½ in. diam of oxygen-free copper (O.F.H.C.) (99.985 pct) were melted vertically in graphite crucibles under an atmosphere of commercial nitrogen purified through a gas train including sulfuric acid, potassium chloride, magnesium chlorate, hot copper chips and phosphorus pentoxide. After a temperature of 1200°C had been maintained for ½ hr, the furnace was turned off and the specimens cooled at a rate of about 150°C an hour. This method of direct solidification was used by Greninger10 to produce single crystals with marked lineage and in this investigation produced a fair yield of single crystal specimens in

Jan 1, 1947

By H. A. Baumann, A. J. Rostosky

EVER since the first installation of wet-washing methods of coal preparation, the removal of the water added by the washing process has created serious technical and operating problems. The rapid development and widespread adoption of wet washing has necessitated a corresponding development of dewatering methods and equipment. The amount of water retained by coal varies with the size of the coal. The moisture that is largely on the surface of the particles is easily shaken off coarse coal; thus coarse coal can be dried comparatively easily and quickly. Fine coal presents a larger surface area than does coarse coal, so its capacity for retaining moisture is greater. In fine coal, moisture below about 5 per cent is held between the coal particles and its removal is difficult. Draining and drying of the finer sizes is a major problem at many washeries. Two common problems of coal-washing practice that are intimately connected with dewatering and drying are the clarification of washery water and the prevention of stream pollution. The first field has been studied from many angles, including the use of coagulating and settling agents followed by vacuum filters to remove the solids, and the use of sludge tanks with dewatering screens incorporated therein. In many districts, the disposal of sludges into streams has been stopped by law. The lack of space for impounding sludges has created problems of disposal in other districts. Reduction in moisture means a saving in freight costs as well as the elimination of difficulties in unloading and storing. Excess moisture in coal causes it to freeze in localities where severe climatic conditions prevail. Excess water in coals to be used in the production of coke and manufactured gas has a chilling effect on the walls of the oven or retort. Dryness of coal is important in producing good briquettes. CLASSIFICATION OF MOISTURE Moisture in coal can be classified as inherent and surface moisture. Inherent moisture is regarded as a part of the true coal substance, having been present in the original vegetal matter from which coal was

Jan 1, 1943

By C. S. Barrett, C. T. Haller

Twinning in magnesium is known to occur profusely under certain conditions, and when it occurs in polycrystalline materials it brings about a partial or even a complete change in the preferred orientation. The amount of research on this subject, however, has not been in proportion to its importance as a mechanism of deformation and reorientation. Much of the research has been limited to twinning in single crystals. The present study1 concerns polycrystalline sheet, and is an investigation of the twinning produced by plastic deformation as a function of the following variables: 1. Direction and type of deformation. 2. Amount of deformation. 3. Speed of deformation. 4. Temperature of deformation 5. Composition and temper of the sheet. 6. Twins previously produced. 7. Twins previously produced, then annealed. By proper control of these variables it is shown that, on a laboratory scale, samples can be produced that are free from preferred orientations. The materials used were samples of commercial magnesium-alloy sheets with nominal compositions given in Table I. X-ray diffraction was used in most of this work to detect the twins and to estimate the amount of twinning. Since twinning on (102) planes causes a re-orientation of the crystal lattice by 86", it is very easy to study with X-ray diffraction patterns, particularly if one notices the diffraction ring from the basal plane— the 002 reflection. By properly directing the X-ray beam, it is possible to produce 002 reflections from twinned material at, say, the 6 and 12 o'clock positions on the 002 ring, with the untwinned material reflecting to 3 and 9 o'clock positions; and by judging the relative intensity of the arcs on the diffraction ring at these positions, it is possible to judge the amount of twinned material relative to the untwinned. This X-ray method of estimating the amount of twinning is generally superior to metallo-graphic observation, for it was found

Jan 1, 1947

By C. S. Barrett, C. T. Haller

Twinning in magnesium is known to occur profusely under certain conditions, and when it occurs in polycrystalline materials it brings about a partial or even a complete change in the preferred orientation. The amount of research on this subject, however, has not been in proportion to its importance as a mechanism of deformation and reorientation. Much of the research has been limited to twinning in single crystals. The present study1 concerns polycrystalline sheet, and is an investigation of the twinning produced by plastic deformation as a function of the following variables: 1. Direction and type of deformation. 2. Amount of deformation. 3. Speed of deformation. 4. Temperature of deformation 5. Composition and temper of the sheet. 6. Twins previously produced. 7. Twins previously produced, then annealed. By proper control of these variables it is shown that, on a laboratory scale, samples can be produced that are free from preferred orientations. The materials used were samples of commercial magnesium-alloy sheets with nominal compositions given in Table I. X-ray diffraction was used in most of this work to detect the twins and to estimate the amount of twinning. Since twinning on (102) planes causes a re-orientation of the crystal lattice by 86", it is very easy to study with X-ray diffraction patterns, particularly if one notices the diffraction ring from the basal plane— the 002 reflection. By properly directing the X-ray beam, it is possible to produce 002 reflections from twinned material at, say, the 6 and 12 o'clock positions on the 002 ring, with the untwinned material reflecting to 3 and 9 o'clock positions; and by judging the relative intensity of the arcs on the diffraction ring at these positions, it is possible to judge the amount of twinned material relative to the untwinned. This X-ray method of estimating the amount of twinning is generally superior to metallo-graphic observation, for it was found

Jan 1, 1947

By J. W. Halley

RIMMING steels derive their name from their action during solidifica-tion in the molds. As a result of incomplete deoxidation, gas is evolved during freezing, and the metal has a characteristic rolling action. The metal rises along the mold walls and descends in the center of the ingot. This action keeps the top of the ingot open and the advancing rim of solid metal can be seen. The rim grows until the rolling action is insufficient to prevent the top of the ingot from freezing or until the action is stopped by capping the ingot with a heavy plate. The violence of the reaction and its characteristics, such as growth or drop ill the molds, are deter-mined by the Composition, the furnace practice, and the deoxidation in the ladle and in the molds. Though rimming steels represent a large proportion of the amount of plain carbon steel made, they have received comparatively little attention in the technical literature. The manufacture of rimming steels has been described by Hibbard,1,2 Fleming,3 Pierce4 and Jackson.5 The reactions occurring during rimming have been considered from the theoretical point of view by Chipman and Samarin.7 The structure of rimmed-steel ingots has been discussed by Nead and one of the present authors.6 Meyer,8 in studying segregation, investigated the distribution of carbon, sulphur and phosphorus in rimmed-steel ingots by analyzing the rim and core of blooms. In their studies of segregation, the Joint Committee of the Iron and Steel Institute and the British Iron and Steel Federations studied distribution in one billet and one ingot of rimmed steel. A detailed study of the distribution throughout the ingot has not been published. The present investigation was undertaken to determine accu-rately the distribution of carbon, manganese and sulphur in normal rimmed ingots and the general distribution of other common elements present. The study included some work on the effect of pouring condi-tions and furnace practice on the distribution, though there is still much to be done in this direction.

Jan 1, 1938

By D. Turnbull, J. E. May

THE (110) [001] texture in silicon iron is of considerable interest both from the technological and scientific points of view. Its occurrence was reported more than 20 years ago.1-4 The texture develops by means of secondary re crystallizatjon5 and can be very strong, that is, greater than 90 pct alignment even thouh the primary re crystallization texture is weak or complex. This behavior is in contradistinction to the face-centered metals which develop their strong secondary recrystalliza-tion texture from a strong primary recrystalliza-tion texture.', The microstructural changes accompanying the (110) [001] texture formation in silicon iron are as follows: When properly prepared cold-rolled sheet (i.e., 0.015 in. thick) is annealed at about 800°C, primary recrystallization occurs and a fairly stable fine-grained primary recrystallized matrix of about 0.02-mm-diam grain size is produced. The material at this stage does not have the strong (110) [110] texture. As the temperature is raised to about 900°C, relatively large grains appear in the finegrained matrix and they grow at the expense of the smaller grains to many times the sheet thickness. In time the complete sample is consumed by these large grains. This process of the growth of relatively few grains (about one in 105 primary grains) at the expense of many grains is called secondary recrystallization. Since all the secondary grains are of essentially (110) [001.] orientation, the strong texture is developed by this secondary recrystallization process. Theories of the (110) [001] texture in polycrystal-line silicon iron have been proposed by Decker and Harker and by Dunn.Decker and Harker have shown that grains initially in the (110) [001] orientation will upon annealing after cold-rolling, re-crystallize back to the initial orientation. To account for the sharp texture in silicon iron they propose that (110) [001] grains become more highly strained than grains in other orientations and therefore recrystallize first. They are then the lowest energy grains and can consume their higher energy neighbors. Grains in orientations other than (110)

Jan 1, 1959

By Aug. J. Jr. Bowie

(Read at the Wilkes-Barre Meeting, May, 1877.) Brief Outline of the General Topography of the Gold Regions of California. THE topographical features of California, as demonstrated by the explorations of the State Geological Survey, are found to be exceedingly simple. Three equidistant parallel lines can be used in conveying a general idea of the physical geography of Central California. A straight or " main axial line," whose course would be north 31° west, passing through the culminating peaks of the Sierra for a distance of five hundred miles, can be assumed as the eastern boundary of the State. A second parallel drawn fifty-five miles west of the " main axial line" will skirt the western base of the Sierra Nevada, along the edge of the foot-hills. A third parallel run equidistant from the second will represent "as nearly as possible the western base of the Coast Ranges." These parallel lines divide the State into three belts, namely, the Sierra, the Great Valley of California, and the Coast Ranges. " This arrangement of the physical features holds good for a length of four hundred miles in the direction of the main axial line, comprising almost the whole of the agricultural and the greater part of the mining districts."* The section of the country which is of immediate interest to the miner is the western slope of the Sierras. These mountains, rising in a short distance from the Sacramento plains to elevations of over seven thousand feet, with occasional peaks ten and twelve thousand feet high, are cut by numerous deep and precipitous gorges or capons, through which drains the immense watershed of the Sierra, supplying the main rivers of the State and ultimately emptying into the Pacific Ocean. Between these capons, ridges or divides are formed, on top of * See vol. i, p. 5, Geological Survey of California. J. D. Whitney, State Geologist.

Jan 1, 1878

By M. J. Sinnott, W. R. Kiessel

The creep characteristics of commercially pure titanium sheet in the annealed state, cold-worked state, and cold-worked and recovered state in the temperature range from 75' to 750°F have been determined. Titanium has been found to exhibit strain aging characteristics. The effect of strain aging on creep has been determined. A possible explanation for the poor creep properties of titanium is proposed. THE metal titanium exhibits many desirable properties but results on its creep properties have been somewhat disappointing. The creep strength is low even though the material has a very high melting point.' The present work was undertaken to determine the creep strength of titanium in various conditions; annealed, cold-worked, and cold-worked and recovered and to determine why titanium shows such relatively poor creep properties. The general procedure followed in this research consisted in obtaining the usual mechanical prop- erties such as creep strength, short time tensile strengths, and hardness on materials treated to a controlled degree of internal strain, as determined by X-ray diffraction measurements, and their subsequent interpretation in terms of this internal strain. The material used in this work was sheet stock taken from one heat of commercially pure titanium. As-received, this sheet was 0.060 in. thick. The analysis was given as 0.037 pet C, 0.023 pet Si, 0.50 pct W, 0.063 pct Ni, 0.08 pct Fe, and the remainder titanium. The oxygen and nitrogen were unreported but generally are about 0.2 pct in commercial heats. In order to put the material in a state of minimum internal strain all the sheet was given an anneal in a static argon atmosphere for 1 hr at 1600°F prior to processing and testing. The microstructure of the material after this treatment was essentially a single-phase solid solution of uniform equiaxed grains. For the studies on the cold-worked sheet, the material was reduced by rolling in a two high, 5 in. mill. Rolling was done at room temperature in passes

Jan 1, 1954

By G. R. M. Del Giudice

The term "slime-coating" is not new in the art of flotation; the phenomenon has been observed and described by Taggart;(l)† Taggart, Taylor, and Ince;(2) and by Ince.(3) Notwithstanding that flotation was introduced for the treatment of finely crushed ore, the adverse effects of slimes have been recognized since the earliest days of the process, and the Elmore, Delprat, Potter, and other processes actually specified desliming of the ore prior to treatment. The cause of this trouble has been studied and described by Taggart;(1) Taggart, Taylor, and Ince;(2) Ince;(3) Morrow and Griswold;(4) and by Gaudin and Malozemoff.(5) Old Theory of Slime-coatings At present, so far as published work shows, there seems to be but one theory for the mechanism of slime-coatings. Ince(3) states that they are due to attraction between electrostatic charges of opposite sign on the sulfide and on the slime particles, supporting this theory by migration experiments in the Burton tube. He also used the microscope in conjunction with a glass cell employed by Beans and Eastlack(6) in studying migration, but met with interference from endosmosis. Several attempts have been made in the Department of Mineral Dressing at Columbia University to duplicate Ince's experiments with the Burton tube, but the results have never been convincing. Formation of precipitates which settled through the pulp levels, and evolution of gas at the electrodes, which disturbed the interface between the pulp and the distilled water above it, seriously interfered with observations. However, by use of the migration cell shown in Fig. 1, endosmosis effects and the disturbances due to precipitation and gas evolution were avoided, and distinct and reproducible migrations or absence of migration were observed. The cell was made of bakelite and had platinum electrodes. Objectives were employed which had a working distance of at least three millimeters,1 and the parts of the mounting which came in contact with

Jan 1, 1935

By Zay Jeffries

THIS paper will include a brief discussion of Prof. Howe's paper on The Supposed Reversal of Inheritance of Ferrite Grain Size from that of Austenite.1 The general subject of grain refining in steel and iron will also be treated. The conclusions reached are stated in the following hypotheses which are discussed more in detail below. 1. The ferrite grain size in pure iron, the ferrite and pearlite grain size in hypoeutectoid steel, the pearlite grain size in eutectoid steel and the cementite and pearlite grain size of hypereutectoid steel are not inherited from the grain size of the mother austenite. 2. The only structural feature that is generally inherited from the austenite of hypo- and hypereutectoid steels on cooling through their transformation ranges is the position of the excess ferrite or cementite at the austenite grain boundaries, sometimes causing complete and sometimes incomplete networks which outline the old austenite grain boundaries. Rapid cooling through the transformation range will cause the non-inheritance of this structural (network) feature. 3. The austenite grain boundaries themselves are nearly always effaced in all steels and also in pure iron during the Ar transformations. 4. The grain-size refining of steel and iron is brought about by the combined. effect of non-inheritance of the transformation products on either heating or cooling, i.e., the austenite transformation .products do not inherit their grain size from the austenite on cooling through the transformation range for does austenite inherit its grain size from the products which form austenite on heating. 5. In general, in both iron and carbon steel the larger the austenite ,grain size, the larger will be the grain size of the transformation products on cooling. This, of course, assumes all other conditions constant except the austenite grain size. An exception is found to this general rule in very pure iron such as electrolytic iron. 1n this instance small austenite grains may form very large ferrite grains on cooling through Ar3.

Jan 11, 1917

By E. A. Trager, A. W. McCoy, H. R. Shidel

Sampling of the fluid from oil wells for percentages of oil, emulsified oil, and water during the last two years has brought out some interesting facts concerning oil-water emulsion. This result led to a laboratory investigation of emulsion, which substantiated the conclusions made from the field observations. The purpose of this paper is to present the information collected, the laboratory experiments, and our interpretation of the same. In order to define emulsified .oil exactly, give its synthesis and origin, and to show how and when it is formed in the wells, the work was necessarily divided into two separate lines—laboratory work and field observations. It is hoped that this study may lead to a discussion of such points so that the petroleum engineer, geologist, or technologist may be benefited by its practical bearing on oil-field management. Special credit is due Mr. Everett Carpenter, chief geologist of the Empire Gas & Fuel Co., for his assistance and cooperation in this work. Labobatory Investigations on Emulsified Oil Laboratory investigations were conducted in an attempt to learn the composition and some of the properties of emulsified oil, or B. S., as it is more commonly called, also to demonstrate, by laboratory methods, how B. 5. may be formed under conditions similar to those existing at the time a well is being pumped, and how it may be broken down. Literature bearing on this subject is widely scattered and very limited in scope. Bacon and Hamor define B. S., or bottom settlings, as "earthy matter, inert organic matter, or, in the case of Pennsylvanian petroleum, an emulsion of paraffin wax and water, which accompanies crude oil." In this discussion we will limit the term B. S. to that heavy, dark-brown emulsion, composed of a physical mixture of water, oil, and air with some included inert matter, either organic or inorganic. Possibly the first step in a description of this product should be a description of its physical properties, but since most operators are quite

Jan 1, 1921