By T. Szaplonczay, D. E. Light

The auto-oxidation of sulfur dioxide to form sulfuric acid in commercially produced barren and recycle liquors, containing 1.66 and 4.56 gpl Fe respectively, from Elliot Lake was studied. A gas mixture, containing 3.5% SO2 and air was introduced into these liquors through a frit at a rate of 6.0g SO2 per hour per liter of solution. The barren and recycle were heated to 60°C. At the end of the first 24 hours of the process the concentrations of acid produced were 158 and 220 gpl H2SO4 for the barren and recycle respectively. Corresponding conversion efficiencies were 70 and 83%. In the period from 24 to 36 hours the rate of acid production decreased so that the H2SO4 concentrations at the end of 36 hours were 180 gpl for the barren and 260 gpl for the recycle; average conversions for the initial 36 hours were 55 and 68% respectively. Many investigators1'2'3 have considered the oxidation of sulfur dioxide to form sulfuric acid in aqueous solutions containing metallic ions. A summary of the work performed on this subject prior to 1946 has been presented by Keyes4 who described the auto-oxidation process as follows. Keyes also suggested that in this second reaction ferric ion serves as a catalyst for the conversion of sulfur dioxide to sulfuric acid. Neytzell-de Wilde and Taverner5 have reported on the use of auto-oxidation to produce a 4 to 5% sulfuric acid solution for use in a cyclic leach process at South African uranium plants. This paper describes investigations carried out to determine the feasibility of using the auto-oxidation process to produce sulfuric acid solutions of as high concentration as possible using commercially produced uranium plant barren and recycle liquors from the Elliot Lake region of Ontario. These liquors contained 1.66 and 4.56 gpl respectively of iron, chiefly in the ferrous state. This investigation is of particular interest to the uranium producers in Elliot Lake where the ores contain 3 to 4% sulfur, as sulfides. Flotation of these sulfides and roasting of same to produce SO, bearing gases have been successfully demonstrated using conventional methods.6'7 Barren and recycle solutions, as described previously, are also produced in large tonnages by these uranium producers. The experimental method and apparatus used to examine the auto-oxidation process will be described first. Then the tests carried out on laboratory prepared aqueous solutions containing ferric sulfate to determine optimum conditions will be presented. The next section will describe the tests using the commercial barren and recycle liquors. A final section will summarize the conclusions of the work. EXPERIMENTAL APPARATUS AND PROCEDURES Two types of solutions were used in the tests, a laboratory prepared aqueous solution containing definite amounts of ferric sulfate, and commercially produced iron bearing solution obtained from a uranium leaching plant in the Elliot Lake area. Two liters of a solution to be examined were placed in a 3 in. diam by 30 in. long glass cylinder with a cross-sectional area of 7 sq in. A mixture of air, and SO2 supplied from a lecture bottle for convenience, was introduced into the bottom of the vessel through a standard 30 mm glass frit, 700 sq mm in area. The temperature of the apparatus was controlled by a heating tape and variable transformer. Exhaust gases were vented to atmosphere. At the end of the test period the gas flow was shut off and the solution was analysed for H2SO4, Fe ++, and Fe +++, by conventional means. Four variables were examined using the laboratory prepared aqueous solution of ferric sulfate. First, the effect of SO2 concentration, from 1 to 1076, in the feed gas mixture was considered. Second, the temper-

Jan 1, 1964

By J. A. Roberson, A. M. Adair

A plate of an 18 pct Ni (250 grade) maraging steel was homogenized, cold rolled, and re crystallized to produce a fine grained, homogeneous structure. The strength properties were then measured as a function of cold rollinq prior to aging. Material in the solution heat treated condition exhibited substantial strengthening from cold rolling. The strength increase and the rate of strengthening were proportional to the amount of cold work. This benefit, of up to 50 ksi, was retained during aging for 3 hr at 900°F. The structures produced by cold rolling and aging have been systematically investigated by transmission electron microscopy. The dislocation debris produced by cold work influences the morphology and distribution of precipitate particles as well as the rate of precipitation. An essential feature of the high nickel maraging steels is a martensitic transformation from y to a with the resultant production of a supersaturated bcc solid solution. This solution decomposes to form precipitates during a subsequent aging treatment.' The martensitic transformation in low carbon Fe-Ni alloys and the mechanical properties of these alloys have been studied extensively.2"4 The carbon content of maraging steel is kept very low to avoid the embrittling Fe3C phase and to minimize the acicular, or twinned martensite common to high carbon steels. Maraging steels are usually strengthened only by heat treatment, but cold working is also quite effective in this respect as was shown by Decker, Eash, and Goldman,' Kula and Hickey,5 and the present work. There is, however, some disagreement between the present results and those of Kula and Hickey. Because of their unusual combination of strength and toughness, the maraging steels are suitable for applications where reliability at high stress levels is required. The strength level is achieved through a combination of solid solution hardening,' substructure hardening,3 and precipitation hardening,6 of which the last is the most important. The toughness of these steels has been reported to be a result of the absence of brittle grain boundary precipitates,7 and the fact that the matrix is a massive martensite rather than a twinned martensite.' One of the problems in the manufacture and use of maraging steel has been its tendency to develop laminations in sheets parallel to the rolling plane.9,10 The present investigation was intended to determine whether or not an improvement in the microstructure of this steel by thermomechani-cal processing would improve mechanical properties. I) EXPERIMENTAL PROCEDURES A plate ($ in. thick) of an 18 pct Ni-250 grade maraging steel* was obtained and examined metallo- "Analysis, wt pct: 18.1 Ni, 8.6 Co, 5.3 Mo, 0.4 Ti, 0.07 Mn, 0.05 Cr, 0.05 Si, 0.002B. 0.1 Cu. 0.05 Al. 0.002 Zr, 0.016 C, balance Fe. graphically. It was found to contain laminations as described by previous investigators. This plate was then annealed at 2100°F for 24 hr to promote homogeneity. Pilot studies on small coupons had shown that this was the minimum temperature required to accomplish homogenization in 24 hr. Since this treatment caused excessive grain growth, the steel was subsequently cold rolled and recrystallized. Cold rolling was accomplished at about 5 pct per pass to a total reduction of 66 pct. The standard solution annealing treatment (1 hr at 1500°F) was adequate to cause recrystallization of the cold worked steel. The recrystallized steel was then cold rolled and ground by various amounts to produce specimens with uniform thickness and selected amounts of cold rolling. All tensile specimens with less than 90 pct cold reduction were ground to a thickness of 0.050 in. Specimens with 90 pct cold reduction were 0.025 in. thick. All

Jan 1, 1970

By N. J. Grant, B. C. Giessen, U. Wolff

With the aid of the splat-cooling technique of rapid quenching, metastable alloy phases based on antimony ad bismuth have been prepared. At room temperature, simple cubic phases were found in the Sb + Au, 56 + Yd, and Sb + Ni systems. Another phase was retained in the Au-Bi system at -190°C; in this systent, a microcrystalline phase and a rhombohedrally distorted phase were also observed. The crystal chemistry of these phases is discussed in terms of their valence electron concentration range. A remarkable five-step Phase sequence was found upon heating and equilibration of certain metastable Au-Bi alloys. USING the splat- cooling technique of rapid quenching from the liquid,' a large number of metastable intermediate alloy phases have been prepared in recent years. Thus, Hume-Rothery phases of the hexagonal type based on the valence electron concentration have been produced in systems where they are missing in equilibrium, e.g., Ag-Ge 1 or AU-Sb. 3 In a comprehensive study of metastable alloys based on tin, simple hexagonal metastable y phases were found, raising the total of stable and metastable y phases from 3 to 13. 4 In the In-Bi system, five new metastable intermediate phases were retained.' In most cases, the new metastable phases have some crystal chemical characteristics in common: a) They have rather simple, elementlike structures with few atoms per unit cell, e.g., y phase,4'5 or the metastable primitive cubic phases in the Ag-Te and and Au-Te systems.= b) Their structures are often related to those of the terminal phases, or to elements that are straddled in their position in the periodic table by the constituent elements; this is the case for metastable ß (In-Bi) with the structure of white ß Sn,' or metastable a (Cd-sn). 4 c) They seem to represent the crystal structures appropriate to certain average group number (AGN) ranges in which no or few single-phase structures exist in equilibrium. These average group number ranges can probably be equated in the case of many elements of the Ba(Zn)-Bs(As) groups with the averaged valence electron concentration. In the present work, the splat-cooling technique has been applied to the alloys of antimony and bismuth. In equilibrium, neither element forms intermediate alloy phases with other B elements from groups Bl(Cu) to B4(Si) that contain more than 66.7 at. pct of Sb or Bi, respectively, e.g., AUSb 2. 7 Thus, antimony- or bismuth-rich phases, which might be closely related to antimony or bismuth, and which would reflect struc- tural changes occurring on alloying with small amounts of addition elements, do not exist. Also, the terminal solubility of antimony and bismuth for all B metals is very small. It was therefore of interest to investigate the influence of enforced, nonequilibrium solid solution of addition elements in antimony and bismuth on their crystal structures. It was found that additions of group B 2-B4 metals act distinctly differently than additions of group T 10 and B1 metals. The latter set of additives will be treated here. EXPERIMENTAL TECHNIQUES Alloy preparation and splat-quenching followed closely the procedures described in Refs. 1, 4, and 5; they consisted of the preparation of master alloys from high-purity starting materials (99.99+ pct) and blast-atomizing of 20-mg quantities onto copper sheets. The resulting approximately 1 to 5 u thick foils were investigated by X-ray diffraction. The cooling rates obtained are of the order of 107 to 10 8 C per set,'" causing solidification to proceed at a rat; of approximately 100 cm per sec.' Powder patterns of the resulting fine-crystalline materials were taken with filtered CuK, radiation. For antimony alloys the substrates were held at room temperature and for bismuth alloys at -190°C both during splat foil deposition and X-ray investigation. Annealing treatments at several

Jan 1, 1969

By U. Andres

U. Andres (The Technion, Haifa, Israel)-The authors are to be congratulated on their research, new and interesting, in a field which, however, the present writer and his assistants have been trying since 1962 to bring to the attention of the scientific and technical world, by means of publications covering several different aspects of this many-sided problem. We announced, in these publications, the results of magneto-hydrostatic (MHD) separation of magnetic and nonmagnetic minerals which we made in magnetic fluids (in paramagnetic solutions and suspensions of magnetic particles) which interact with permanent" and impermanent" inhomogeneous magnetic fields. There is no doubt that the authors have succeeded in creating ferrimagnetic colloids made by dispergation of 10-30 wt % of magnetite in kerosene in the presence of 7-10 vl % oleic acid. It may be judged by [Figs. 3 and 4] that the suspensions represent great stability systems and also "hysteresisless" fluids [(Fig. 5)] which bear witness to the existence of superparamagnetic suspensions. If the viscosity of these colloids is not so high, and the cost of preparing them can be covered, the fluids which have here been received can possibly be of interest to the technology of mineral separation. The potential possibility and technological perspective of similar media is demonstrated in our joint work with G. Bunin18 in 1965. The research carried out on the pushing out of cylinders and spheres from magnetic fluid is impressive; it would, however, have been interesting if the authors had compared their results with those on the pushing out of bodies from magnetic fluids adduced from our work." In my books" there happens to be described an experiment on the pushing out of a sphere in magnetic wedge field, in which the pushing out force of suspension with 5 vl % of magnetite reached 125 g per cc. This testifies to interesting possibilities of these media. Our works' shows also, on the basis of Laplace's equation the receiving of an interesting distribution of pushing out forces by selection of corresponding configurations of magnetic poles. Objection must be made to the authors' introduction of the term "antigravity force." The direction of this force does not depend on the direction of the gravity force and their opposition, i.e., antigravity is only one particular case. I am in full agreement with the authors' statement that magnetic pushing out forces "can be utilized to separate nonmagnetic objects according to variations in their densities." It is, however, necessary to make only one important addition, which can be found in our research on MHS at the Technion in Haifa, namely, that magnetic fluids in magnetic fields can be utilized in the separation of minerals according to variations in their magnetic susceptibility. The authors' conclusion is especially important considering the fact that in our publications" (including one in English") some designs of MHS separators and some technological results received on MHS-separators have already been described. S. E. Khalafalla and G. W. Reimers (Authors' Reply)We were aware (mostly through Chemical Abstracts of the American Chemical Society) of the use of solutions of paramagnetic salts such as manganous sulfate in agnetohydrodynamic separations by the Russian school headed by G. Bunin."n Professor Andres' contributions to this school are also evident in his application of the ponderomotive forces in an electrolyte placed in electric and magnetic cross-fields to separate coal and other useful minerals." It must be realized, however, that the foregoing research by Bunin et al." involved the use of magnetic fields and field gradients of very large magnitudes, i.e., such that H • grad H - 101 Oe2 per cm. The magnetization of paramagnetic salt solutions range from 0.1 to 0.5 gauss (at fields of a few thousand Oersteds) and never reach saturation. The magnetization of our superparamagnetic ferrofluids ranges from 100 to 500 gauss and reach saturation at fields of a few hundred Oersteds. Hence, to effect the same separation, the quantity "H

Jan 1, 1974

By Donald L. Johnson

REVIEWS on the applications of optical ellipsometry to the study of polycrystalline metal surfaces and oxidation-corrosion processes have been presented by Kruger and Hayfield, and white.' In view of the ability of this method to measure differences in film thicknesses to below 10A, ellipsometry was used to study nitrogen chromium surface reactions during the early stages of growth. Chromium specimens in the form of a vapor-deposited film on glass substrate were exposed to purified nitrogen for selected time increments at 700°F. This temperature was selected because it gave the best combination of exposure time and thickness change. Ellipsometer readings were taken immediately after exposure to determine polarizer and analyzer angles using monochromatic light at 5000A.2 After each set of readings was obtained, the specimens were exposed for an additional increment of time in nitrogen and a new set of readings taken. Film thickness was computed from LUCy's3 equation for nonabsorbing thin films. In Lucy's derivation, two equations for computing thickness were obtained. Peterson and Bashara4 have discussed the validity for using one of these equations when an independent value of the refractive index is used. The film was assumed to be Cr2N (Ref. 5) and was determined to be optically isotropic. Optical isotropy was determined by rotating the films about the surface normal and noting that the azimuth and phase difference did not change. Since Cr2N is reported to be hexagonal, it is assumed that optical isotropy results from randomly oriented grains of very small size. The thickness was computed using refractive indexes varying from 1.6 to 2.0. The maximum variation in computed thickness over this range for a given exposure was 20 pct. The data reported are based on a refractive index of 1.8. Reference readings on the metal surface were taken just prior to nitrogen exposure. No attempt was made to deoxidize or denitride the metal surface after vapor deposition, although specimens were observed to gain approximately 2A per day in air at room temperature. Twelve experimental exposures were made on a single sample over a total accumulative time of 132 min. Additional experiments over longer time intervals were made to determine the effect of heat up and cool down during and after exposure. As a result of these experiments, the thickness computed for each exposure was increased by 4A. Time profiles based on the linear law are similar to the oxidation profiles for many metals.' The rate of accumulation of the nitride film is rapid at first and slows down as the film thickness increases. The parabolic law x2 =k1t +k2 [11 gives a straight line in Fig. 1; therefore, it is concluded that the kinetic behavior is parabolic. Sey-bolt and Haman5 reported similar results for CrlN on chromium at 1000°C although the order of the thickness was much greater (10-3 cm). Analysis of thickness data based on other values of refractive index shows that the curves are shifted vertically but retain the same shape. According to Mott,7 it is expected that for thin films k2 is zero in Eq. [I]. Since the plot in Fig. 1 is linear through the origin, k2 is zero and the parabolic nature of the film growth is further indicated. The parabolic rate constant, calculated from the slope in Fig. 1, is 4.4 x 10-16 sq cm per sec. The corresponding work (+) required to bring an electron from the metal into the oxide is estimated to be 1.5 ev.7 The author thanks professor N. M. Bashara and D. W. Peterson, Electrical Materials Laboratory, University of Nebraska, for making the ellipsometer available and providing technical assistance. The Electrical Materials Laboratory is supported by the office of Naval Research, NONR 3718 (01). This work was partially supported by the Engineering Experiment Station and the Mechanical Engineering Department, University of Nebraska.

Jan 1, 1967

By H. Biloni, B. Chalmers

Metallographic studies of the segregation of solute in and near the surfaces of chill-cast alloys have shown that, under sufficiently severe conditions, nucleation on the cold mold surface is followed by the formation of a disc of solid of the same composition as the liquid. This disc is surrounded by two concentric rings in which the concentration first decreases and then increases. The discs and rings are surrounded by a region in which arms of low solute concentration separate regions of high concentration. These arms start at the periphery of the outer ring and are initially radial; they make a gradual curved transition from the radial direction to a crystallographic direction. A normal dendritic substrcture is established beyond the position at which the arms have become crystallographically aligned. When the cooling is less severe, the disc becomes less irregular in shape and has a concentration minimum at the center. The term "Predendritic" is proposed for these transitions. A qualitative explanation is outlined for the phenomena observed at the surface and in the equiaxed region of the ingots. It is well-established1-' that the normal mode of solidification for alloys under most conditions is dendritic. A characteristic of dendritic solidification is the growth of rods or plates in specific crys-tallographic directions. The remaining liquid solidifies later, usually with a higher concentration of solute than the original liquid. Very little is known, however, about the transition from a crystal nucleus until the dendritic pattern is established. It is clear that there must be a transition because the nucleus is much smaller than the characteristic spacings found in the "steady-state" structure. And it also seems clear that the initial conditions must be important since the undercooling existing during the nucleation of the grains has a remarkable influence upon the grain size4 and the segregation pattern. The present paper reports a study of the micro-segregation in regions where crystals have nucleated, and the conclusions that can be drawn regarding the early stages of growth, in connection with the details of the solidification process. Aluminum of 99.993 purity, A1-Cu alloys containing 0.5 to 20 wt pct Cu, and Pb-Sn alloys with 5 wt pct Sn were cast and examined metallographically at the as-cast surface, close to the surface, and in the interior after casting. The alloys were cast from controlled temperatures against surfaces at different temperatures ranging from room temperature to approximately the liquidus temperature of the alloy. The surfaces were, in various experiments, graphite, stainless steel, copper, and aluminum. The methods used for metallographic examination were as follows. 1) The Nomarski phase contrast interferometer6 was used to obtain information on the topography of the as-cast surface. 2) The distribution of any solute present in A1 99.993 pct and copper in the A1-Cu alloys was studied by the anodic film technique originated by Lacombe and Mouflard7 and previously applied in the study of the solidification of aluminum by Biloni.8 The electropolished surface of the specimen is anodized under controlled conditions so that the thickness of the oxide film and therefore the interference colors under white light are sensitive to the local composition. This technique was applied to the as-cast surfaces and to metallographically prepared surfaces from the interior. 3) If in Al-Cu alloys, the surface is anodically oxidized for several minutes, instead of seconds as in the color-film technique, the copper segregation is outlined by a different level with respect to the matrix. This method is less sensitive but complementary to that for the color films. 4) The distribution of copper revealed and mapped by the metallographic techniques was confirmed by electron probe. 5) In samples with high concentration of copper, evidence for the copper distribution could be seen optically after electropolishing.

Jan 1, 1965

By J. H. Hamilton, J. R. Lewis, J. H. Dismant, W. M. Fassell

RECENTLY this laboratory undertook the task of preparing some low carbon metallic cobalt by the carbon reduction of precipitated cobalt oxides. The oxides came in two lots and had the compositions given in Table I. Industrially, cobalt rondels' are made by the carbon reduction of cobalt oxide in small reverberatory furnaces at temperatures near but not above 1050 °C. This is a slow and tedious small batch process but does give cobalt metal which is low in carbon (1 pct C). Inasmuch as these cobalt oxides were relatively low in copper and iron it was decided to reduce them with petroleum carbon in a small three-phase electric arc furnace of about 3 to 5 Ib of metal capacity. It was hoped such a procedure would save considerable time and perhaps also indicate an improved commercially feasible process. The furnace was preheated by using small pieces of carbon electrodes to maintain the arc until a temperature of 1500°C was reached. The broken pieces of electrodes were then removed and 500 g of the cobalt oxides and 60 to 100 g of petroleum coke added. At the end of the reduction reaction, a high lime flux was added to the furnace to facilitate the removal of sulphur. Due to the fineness of the cobalt oxide powder used and also to the presence of chlorides there was considerable dust lost in charging the furnace. This was overcome by preparing briquettes composed of the cobalt oxides, charcoal, and a little bentonite to serve as a binder. The results obtained are summarized in Table 11, which shows that the cobalt metal produced in the arc furnace was high in carbon varying from 2.5 to 3.5 pct. This, of course, is much too high. For certain uses, such as in the preparation of permanent magnets, the carbon content of cobalt must be low. It was necessary therefore to find an effective method of reducing the carbon content of the cobalt that had been prepared in the arc furnace. Van Arkel3 recommends the use of Co2O3 as a means of removing carbon from cobalt. Experiments by the authors indicate that carbon is removed with difficulty by this method. Other methods used, including lancing of the molten high carbon cobalt with a jet of oxygen, proved to be ineffective. The method finally used makes use of the fact that cobalt metal is decarburized by carbon dioxide at the temperature of the molten metal. Two methods were used: 1—carbon dioxide was bubbled up through the molten cobalt, and 2— molten cobalt was maintained in a carbon dioxide atmosphere. In the first method the gas was introduced below the surface of the molten metal by means of a quartz tube. A high frequency induction furnace was used to keep the cobalt molten in both of these experiments. This kept the metal somewhat agitated and no doubt was an important factor in hastening the decarburization 'process by the second method. Both methods gave satisfactory results as shown in Table 111. An interesting observation in connection with this 'work was that a small sample of carburized cobalt metal could be decarburized by heating it with an acetylene torch adjusted to give an oxidizing flame. This may have been due to the presence of carbon dioxide in the products of combustion. Samples of molten high carbon steel were decarburized by the same method and it is suggested that nickel and perhaps manganese can be decarburized in a similar manner. Additional work, including rate studies and other theoretical aspects of this problem, is in progress in this laboratory.

Jan 1, 1953

By S. E. Haszko

Fused alumina or silica crucibles were used as the containing vessel. X-ray powder photographs were taken with CrKa radiation and the use of Straumanis type Norelco cameras of 114.6 mm diam. Crystallographic data for these compounds are shown in Table I. These results are in agreement with others of this series reported previousiy by Wernick and Geller.l The abnormally large atomic volume of Eu and Yb metal3 is manifested in EuA12 and YbAl2, when one compares them with the compounds reported in Ref. 1. However, the behavior of Yb in the Ni compound is the same as that observed in Ni5Yb having the Cu5Ca structure.4 Thus, it appears that Yb has a valence closer to 3 only in the Ni compounds; i.e.. the 2s and Id electrons are lost to the conduction band. 1,4 Europium in EuAl2, appears to have a valence closer to 2. In previous work.' X-ray patterns of ingots of NdCo2 indicated a multiphase material with faint indication of the presence of a phase having the MgCu2 structure. It was thought that NdCo2 formed peri-tectically from the melt, resulting in a multiphase system when cooled under nonequilibrium conditions. An X-ray pattern of a sample from a melt cooled more slowly than in past work showed that the major phase was NdCo2. The lattice constant, Table 1, is in excellent agreement with the value one can predict from the data of Ref 1. One of the other phases was identified as Co,Nd. The author wishes to thank J. H. Wernick for his guidance in this work, and D. Dorsi for the preparation of these compounds. 'J. H. Wernick and S. Geller: AIME Trans., in press. 'J. H. Wernick and S. E. Haszko: to be published. 'F. H. Spedding and A. II. Daane: Progress in Nuclear Energy, Series 5, Eds.: H. M. Finniston and J. P. Howe, McGraw-Hill Book Co., 1956. 'S. E. Haszko: to be published. 'J. H. Wernick and S. Geller: unpublished work. 6J. 11. Wernick and S. Geller: Acla Cryst., 1959, vol. 12, p. '162. The Influence of Hydrogen on the Lattice Parameters of Ti-Sn Alloys A. Coucoulas and H. Margolin A reinvestigation of the lattice parameters of Ti-Sn alloys by the present authors has revealed consistently higher c and a values than those obtained by Worrier. The difference is most pronounced in the c-parameters which are, therefore, used as a basis of comparison. This discrepancy was not due to air contamination, since precautions were taken to exclude this possibility. Specimens for Debye-Scherrer photograms were prepared by arc-melting 15-g buttons of Bureau of Mines titanium and 99.99 pct Sn, with compositions of 6, 8, 10, and 12 at. pct Sn. These buttons were forged under an oxygen-acetylene torch to 1/8-in. sq rods to produce relatively fine grained material. Scale and some surface were ground off, and the rods, after wrapping in molybdenum and titanium sheet, were vacuum annealed 15 min at 800 °C to remove hydrogen. Heat treatment of one of the samples at 875°C to produce ß and reveal a at the surface showed no surface contamination. Following the vacuum treatment, the specimens were wrapped in molybdenum and annealed for 1week at 800°C under two atmospheres of argon. After water-quenching, the rods were ground so that the thickness tapered to 0.1 mm at the tips. The ground specimens were then recapsuled as previously and reannealed 1 hr at 800°C to remove cold work. The

Jan 1, 1961

By J. S. Brown, A. G. Guy

With the exception of the work of Tammann and Hartmann,1 no published information has been found on the structural changes produced in eutectic structures as the result of heating following plastic deformation. In part this lack of information may be due to the fact that many eutectic structures contain an intermetallic compound as a prominent phase, and as a consequence have been considered to be unworkable. For example, Tammann and Hartmann were able to obtain useful data only on those alloys that they could greatly reduce in thickness by cold rolling. This restriction placed on the investigation of alloys containing intermetallic compounds has been largely removed by the work of Savitskii2 which showed that large deformations of such alloys can be produced by relatively slow compression at temperatures near the melting range. It was possible, therefore, to carry out the present work on a range of binary eutectics including one composed of two intermetallic compounds. The essential results obtained on the alloy systems studied are illustrated by the Pb-Mg eutectic containing 33.2 pct Mg, Fig 1. The cast structure, Fig la, was obtained by melting together magnesium of 99.8 pct purity and chemically pure test lead, casting into a heated, small steel mold, and furnace cooling in the mold from about the eutectic temperature. The fairly coarse eutectic structure thus obtained was too brittle to work at room temperature without cracking. Fig 16 shows the worked structure obtained by compressing a 1/2-in. cube 70 pct in about 15 sec at 550°F and then water quenching. The pronounced changes in the distribution of the two phases produced by heating the worked alloy at 850°F for 1 hr are shown in Fig lc. Recrystallization of both phases appears to have taken place, and the mechanical properties of the cast alloy must have been significantly changed by the working and heat treatment. Similar results were obtained with the Mg-59.5 pet Bi, Mg-36.4 pet Sn, Mg-65.4 pet Cu, and Bi-40 pet Cd eutectics, only the last of which could be worked at room temperature. Tammann and Hartmann reported a thickening and shortening of the needles of the eutectics which they heated about 10°C below the melting range for 1 hr after drastic cold rolling. They found the following eutectics, given the indicated amounts of reduc- tion, to have a granular structure after heat treatment: Sn-9 pet Zn (98 pet); Cd-82.5 pet Pb (60 pet); and Bi-43.5 pet Pb (90 pet). On the other hand the alloy Al-11.7 pet Si (60 pet) showed no change after heating. Tammann and Hartmann observed a distinct shrinking of the needles in unworked eutectics subjected to heat-treatment. In the present work inappreciable change in the eutectic structure was found on heating undeformed alloys. In summary, it appears that eutectic structures can be recrystallized into a "spheroidized" condition by heating near the eutectic temperature after severe deformation. If the eutectic contains one or more brittle phases the necessary deformation can be accomplished by pressing at high temperatures. It is reasonable to expect that this tendency towards equiaxed grains from the plate- or needle-like eutectic structure should be general since the energy relations and mode of growth in recrystallization are so different from those that hold for eutectic crystallization. References 1. G. Tammann and H. Hartmann: Ztsch. Melallkunde (1937) 29, 141-144. 2. E. M. Savitskii: Doklady Akad. Nauk S.S.S.R. (1940) 62, 349-351. Abstr. in Melal Prog. (July, 1949) 56, 126, 128.

Jan 1, 1950

By W. J. Rogers, L. J. Dwiggins, R. O. Williams

THERE has been comparatively little work on the importance of strain rate and temperature as variables in the formation of deformation textures. For this reason the present work was started, the choice of compression being in part that of convenience and in part because of the absence of quantitative data in this area. These do not turn out to be important variables within the range studied which permits the results to be condensed into this note. Samples 1/4 in. in diam and 1/2 in. long were machined from 99.9 pct pure commercial aluminum and recrystallized to a fine grain size. A set of five samples were deformed between a spring-driven weight and an anvil resulting in roughly 20 pct strain each time. The strain rate varied because of decle-ration and shortening of the sample but would average about 10&apos; per min. Deformation at temperatures over the range of -76" to 150°C were obtained by heating or cooling the samples. Complete lubrication could be obtained by oil since the short time of contact did not permit its escape. The samples were compressed to a total true strain of 1.4 to 1.6. A larger sample was prepared similarly with spiral grooves in the ends to hold paraffin which provided essentially complete lubrication. This sam ple was compressed slowly at room temperature at a rate of about 2 per min to a total strain of 1.0. Cylindrical samples were carefully machined from these discs with a radial direction as an axis. They came from the center half of the samples and were roughly 1/16 in. in diam. The samples were etched down 15 pct to remove any surface effects. Diffraction data were then obtained for six different kinds of planes by the use of the Norton technique as applied to a fiber texture. Direct comparison between the raw data failed to reveal any significant difference between any of the samples and consequently the data from only one sample was completely reduced. The particular sample had been deformed at O°C The background was subtracted from the intensity data which were averaged over the four quadrants and then normalized to random. These data were then used to obtain fiber-axis distribution charts as previously described.2 For this sample the (422) plane was also run to assist in this inversion. The final result, Fig. 1, provided a comparable fit to that previously obtained from fiber data. About 85 pct of the material forms an elliptical texture around the <110> direction. The radius (at half height) is 5.5 deg along the (111) boundary and 8 deg along the (100) boundary. The remaining 15 pct forms a ridge running from this texture to near the <311> direction. The regions around the (100) and (111) planes are devoid of material. The earlier qualitative results of ~arrett~ are in complete agreement with the present results. The possibility has been dis-cused that the material around the <311> results from friction between the sample and compression plates.4 The present results are considered proof that such is not the case because of the uniformity of sample deformation and the requirement of axial symmetry before fiber-axis distribution charts can be accurately obtained. Recently results have been obtained to show that strain rate and temperature are important variables in the extrusion of aluminum.5 Perhaps the most important observation was that the partial recrystal-lization occurred even at room temperature. Strain rate was considered to be a factor only in that it produced a temperature change. There are many differences between the two experiments, the most important possibly being that their material was roughly ten times the purity of the present material. The present experiment, however, may not be as definitive as desired in this respect since it has been shown that compressed aluminum recrystallizes without a texture change6 although supplementary

Jan 1, 1961

By Richards R. Vandervoot

T HE creep behavior of many polycrystalline metals at moderate stresses can be described by the empirical relationship: where Em is the minimum creep rate, A is a constant, a is the applied stress, E is the average elastic modulus at the test temperature, and D is the self-diffusion coefficient.&apos; This equation is generally applicable for strain rates of less than around 10-5 per sec and temperatures greater than about one-half the melting point in absolute units. Under these conditions atomic mobility plays an important role in the deformation process, and steady-state creep occurs when a dynamic equilibrium is reached between the generation and recovery of dislocation substructure. Although several theoretical mechanisms have been proposed to explain the creep of polycrystalline solids,2"4 the dislocation climb model2 is in accord with most experimental observations. The majority of creep data used to develop Eq. [1] came from metals with either the fcc or hcp crystal structures. However, on the basis of results for a and 7 iron as well as those for a and a thallium, Sherby concluded that the high-temperature deformation behavior of close-packed metals and bcc metals is probably the same.&apos; The greater creep resistance of fcc and hcp metals and alloys on a relative temperature scale was attributed to lower diffusivities in the close-packed structures. To further compare the creep properties of fcc, hcp, and bcc metals, creep data for all six bcc refractory metals were analyzed according to Eq. [I]. The results are shown in Fig. 1. The sources of information for the quantities used to prepare this figure are listed in Table I, except for high-temperature elastic moduli. The latter data were obtained from Refs. 28 and 29. The dashed lines in the figure represent the range and breadth of data analyzed by Sherby for fcc and hcp metals. In general, the deformation behavior of all of the refractory metals, ex- cept possibly that of tungsten, can be represented by Eq. [1]. This correlation is strong evidence of the similarity that exists between creep of pure close-packed metals and creep of pure bcc metals. At (Em/D) < 108, the results of Flagella and Tarr on tungsten (W-1 in Fig. 1) agree with the five-power stress law, while those of Green (W-5 in Fig. 1) show a seven-power stress dependence. Where (Em/D) > 108, the stress exponents for other data on tungsten were in the range 10 to 15. It is possible that the creep rate dependence on stress in this region is not a power law but exponential (i.e., Em - eßo). However, it was not feasible to differentiate between these two cases because of the steep slope and scatter in the data. Note the inflection point in the curve for the data of Flagella and Tarr (W-1 in Fig. 1). The slope of the line changes from 5 to around 10 at Em/D = 108. The breakdown of the fifty-power stress law at high stresses is not uncommon in other metals, and this phenomenon may result from nonequilibrium conditions in the material such as excess lattice vacancies produced by rapid straining.30 The mechanical strength of a polycrystalline metal is related to its microstructure. Attempts to establish the influence of grain size on the creep rate of metals and alloys have led to a wide variety of results. For example, the following effects have been observed: creep rate decreases as grain size increases;31&apos;32 creep rate decreases as grain size decreases;&apos;,33 creep rate is a minimum at some critical grain size and increases with either an increase or decrease in

Jan 1, 1969

By Kehsin Kuo

DIE steel with 1.47 pct C, 0.42 pct Mn, and 8.22 pct W contains Fe,C and WC in the annealed state and WC embedded in a martensitic matrix in the hardened state (quenched from 800°C). The presence of a large amount of undissolved angular WC carbide particles makes this steel extremely wear-resistant. However, the WC carbide begins to dissolve in the austenite when the heating temperature is raised above 1000°C, but this solution process is still not complete at 1250°C although partial melting has already taken place at the austenite grain boundaries. At 1325 C, this steel contains austenite and liquid metal but no WC carbide, Fig. 1. On quenching into brine, the liquid metal solidifies into a constituent which etches differently from the austenite-martensite matrix. This constituent appears lighter than the matrix at the 1250°C stage when etched with 2 pct nital but darker in Fig. 1 when etched with Murakami&apos;s reagent. Such a constituent has also been found in burnt tungsten high speed steels. This constituent has been isolated from the matrix by anodic dissolution in a 5 pct HC1 electrolyte and was found by the X-ray powder method to be iso-morphous with &manganese, Table I. The agreement in line intensity between these two phases indicates that there is no ordering in this new phase. The calculated cube edge of this phase is 6.395A, somewhat larger than that of ß-manganese (6.30A). Besides this phase, the anodic residue also contains free carbon from the matrix and amorphous WO,, although the X-ray powder pattern of the residue shows the presence of only this phase. This makes it impossible to determine directly the composition of this phase from the residue. Attempts to prepare an alloy containing only this phase have hitherto been fruitless. The following experiments serve to show that this phase can only be obtained by drastic quenching from the liquid state and that its tungsten and carbon contents must be lower than those in the Fe,W,C carbide. On air cooling from 1325oC, the liquid metal solidifies into a eutectic consisting of austenite and the Fe3W3C carbide. The nature of this dark-etching Fe3W3C has also been ascertained by X-rays. This eutectic becomes coarser on furnace cooling. The solidification of a specimen cooled for 5 min from 1325" to 1200°C and water quenched is still not complete and the fine eutectic is formed during the quenching. Since this new phase can be replaced by a eutectic of austenite and the Fe,W,C carbide, its composition must lie somewhere between the latter two phases. The special features of this phase are: 1—it can only form directly from the liquid state by drastic quenching and 2—it is a ternary phase of iron, tungsten, and carbon. The ß-manganese structure of this phase is also interesting. In the Periodic Table, iron and tungsten lie on opposite sides of manganese; a certain combination of these two elements, in the presence of carbon, may have average properties similar to those of manganese. It has already been established that the x phase, a ternary one of iron, chromium, and molybdenum, has the a-manganese structure."&apos; A similar phase has also been found in the ternary system Fe-Cr-W and in the following binary systems: Re-Cb, Re-Ta, Re-Mo, and Re-W.6 References 1 G. D. Preston: Philosovhical Magazine 11928) 5. 7th Series, p. 1207. - K. W. Andres: Nature (1949) 164, p. 1015. 35. G. McMullin, S. F. Reiter, and D. G. Eberling: Trans. ASM 11954) 46, p. 799. &apos; J. S. Kasuer: Acta Metallurgica (19541 2, p. 456. • H. J. Goldschmidt: Trans. ASM (19541 46, p. 807. P. Greenfield and P. A. Beck: Private communication.

Jan 1, 1957

By A. S. Yue

Small-angle tilt boundaries have been observed in a lamellar eutectic structure. These boundaries are morphologically similar to a theoretical till boundary originally proposed by Burgers. The production of a small-angle tilt boundary in the lamellar eutectic structure is attributed to the formation of an indentation on a planar solid-liquid interface during growth. Constitutional supercooling due to the accumulation of impurity atoms ahead of the interface is primarily responsible for the generation of an indentation. The distance between two faults of like sign, designated as lamellar fault distance, is calculated by the Burgers equation for small-angle boundaries. It was found that the lamellar fault distance decreases exponentially and the tilt angle increases exponentially with freezing rate. SMALL-ANGLE tilt boundaries have been observed in many crystals in the as-grown states by etching techniques. However, a detailed substantial proof for revealing the presence of dislocations in the form of etch-pits was recently accomplished by Vogel. These boundaries are described as an array of dislocations of like sign. The angle of tilt associated with a boundary is treated theoretically by Burgers3 and is given by 0 = b/D for small tilt-angle where b is the Burgers vector of the dislocations and D is their average spacing. During the course of experimentation on the solidi fication of the lamellar Mg-32 wt pct Al eutectic a microstructure which was strikingly similar to a dislocation tilt boundary was observed. An example of the type of microstructure is given in Fig. 1, which shows a combination of transverse and top sections of the lamellar eutectic structure. The lamellae of the top section on one side of the apparent tilt angle are not parallel with those on the other side. Consequently, some lamellae must be terminated somewhere. Fig. 1 shows that the termination of lamellae is analogous to a dislocation tilt boundary in a crystal lattice originally proposed by Burgers. This work represents a closer look at such structures. The factors governing the production of the small-angle tilt boundary are discussed in terms of the freezing condition and impurity distribution in the melt. The effect of freezing rate on the distance between two faults, designated as lamellar fault distance, and the tilt angle is also described. In addition, the lamellar fault distance is determined by means of the Burgers equation for small-angle tilt boundary. EXPERIMENTAL PROCEDURE The slightly impure Mg-32 wt pct Al eutectic rods, 5/8 in. in diam and 12 in. long, were made from 99.99 wt pct Al and 99.98 wt pct Mg and were cast in a high-purity graphite mold. Some of these rods were purified by zone-refining the eutectic using direct-radiation helical-coil furnaces5 A molten zone about 2 in. long was passed through the cast rods at a speed of 5.3 x 104 cm per sec for ten passes of the molten zone. Before the freezing experiment was begun, 2-1/2 in. of the material from the head and tail ends of the zone-refined eutectic were removed from the rod to eliminate any impurity. The freezing experiments were carried out under controlled conditions,8 using a protective atmosphere of purified argon. At the end of each run, observation of the tilt boundary was made throughout the entire length of the rod with a light microscope on the top, longitudinal, and transverse sections (three mutually perpendicular sections) of the lamellar eutectic solid. The experimental data used for the determination of interlamellar spacing and tilt angle were taken from the middle portion of

Jan 1, 1964

By S. Weinig, E. S. Machlin

IN a previous study of the grain boundary stress relaxation phenomenon,&apos; the authors had arrived at the conclusion that two successive steps were involved in the complete relaxation of stress at a grain boundary. These two steps were grain boundary migration and grain boundary slip. It was further suggested that the slower of these two processes is rate controlling. In an attempt to ascertain the validity of the above, a study of grain growth kinetics on the same alloys used for the previous study was undertaken. Separate wire specimens, 0.030 in. diam, in the same as-deformed state (99 pct reduction in area) as in the previous investigation were heated to the various temperatures for a sequence of times. The compositions used and the temperatures of testing are summarized in Table I. A statistical determination of grain size was then made on each specimen, using the average length of traverse between boundaries as a measure of the grain size. Examples of typical results obtained are shown in Figs. &apos;1 and 2. The grain growth law D = ktn was found to fit most of the data. Using this relation, values of the grain growth exponent n were calculated and the inter -esting dependence of n on solute content shown in Figs. 3 and 4 was then obtained. Also, it was found that the constant K which was obtained from extrapolation is roughly independent of solute content. (K is uncertain to within ±25 pct.) An estimate of the activation energy for grain growth was made using the technique of Burke? This method utilizes the plot of the reciprocal of time necessary for the grain size to increase from a definite starting size Do, to a final size D, for each isothermal heat treatment. The slope of this curve corresponds to the heat of activation for the process. In Fig. 5 the rate of grain growth is plotted against the reciprocal of absolute temperature. The activation energies were obtained from these curves and are summarized in Fig. 6. Discussion It is interesting to note that the same saturation in the variability with concentration has been found for the grain growth exponent n in this research as was found in the previous researches on both grain boundary stress relaxationa and internal friction of dislocation origin." The significant feature is that saturation in the variation of these properties has been found to occur at about the same level of solute concentration, namely, between 0.1 and 0.5 atomic pct. The only characteristic common to these different quantities is that solute adsorption at grain boundaries and dislocation can take place and affect these values in a similar fashion. Thus, it is concluded that the grain growth exponent n depends upon solute adsorption at the grain boundaries. It appears, therefore, that theoretical considerations leading to the contrary conclusions5,6 have not treated the real process by which solute atoms exert their effect on grain growth. Prior to the analysis of the observed activation energies, certain of the aspects of the aforementioned grain boundary stress relaxation investigation will be briefly reviewed. It was found that with the addition of solute atoms the grain boundary stress relaxation peak (internal friction vs temperature) decreased in intensity. Simultaneously a second peak was observed which increased with increasing solute atoms. Both of these peaks were shown to be the result of grain boundary stress relaxation. They have been termed, respectively, poire peak and solute peak. It was suggested that the solute peak was dependent upon grain boundary migration, whereas the pure peak was a manifestation of grain boundry slip. Activation energies for both peaks were obtained as a function of Solute content. The value of the activation energy in the temperature range corresponding to the solute peak was

Jan 1, 1958

By John Wulff, David A. Stevenson

The solubility of iron and cobalt in liquid lead, the solubility of chromium in liquid tin, and nickel in liquid silver were determined up to 1300°C in an atmosphere of hydrogen. Liquid samples were taken at different temperatures and analyzed. The data obtained were plotted to show the relationship between log mole fraction of solute and the inverse of the absolute temperature. Resulting values for the differential heat of solution (AH) and the excesspartial molar entropy (S)are: for the iron-lead system = _24,200 cal per mole and AT = 5.0 e.u. for the a phase, and AH = 18,300 and S = -0.1 e.u. for the y phase; for the cobalt-lead system AH = 16,500 cal per mole and AS =0.7 e.u.; for the chromium-tin system AH = 15,600 cal per mole and AS = 8.5 e.u.; for the nickel-silver system AH =18,000 cal per mole and AS = 4.0 e.u. RECENT developments in coating, brazing, and heat transfer have focused attention on specific cases of solid-liquid interaction in metal systems, particularly those involving dilute liquid solutions. One fundamental quantity of interest in such systems is the equilibrium phase distribution between solid and liquid phases. In any effort to fully understand such interactions, one must be able to describe the equilibrium state precisely. Furthermore, in order to develop genera! relations for such systems, one must know the equilibrium state in a number of different cases. This investigation was devoted to a study of the equilibrium phase distribution in four binary systems: solid iron-liquid lead; solid cobalt-liquid lead; solid chromium-liquid tin; solid nickel-liquid silver. The iron-lead system was previously studied by Shepard and parkman&apos; and later by Fleischer and Elliott2 with differing results. Both investigations were carried out by sampling the saturated liquid, and analyzing it chemically. The cobalt-lead system was previously reported by Pelzel,3 who noticed no discontinuity near the transformation. A limited investigation of the chromium-tin system was made by Wlodek and wulff4 using a weight loss method. This work was done in conjunction with the development of a process for coating molybdenum with chromium from tin solutions. To more fully under- stand the kinetics of the process, a more accurate determination of a solubility was desirable. No significant data were found in the literature on the nickel-silver system. Data on the latter system were, however, relevant to the investigation of the corrosion kinetics of copper-nickel alloys in liquid silver as carried out by Harrison and wagner,5 EXPERIMENTAL APPARATUS AND PROCEDURE Of the techniques available for the study of such systems the most effective appears to be that of liquid sampling,2,6,7 which is the method used in the present investigation. A schematic diagram of the sampling furnace is given in Fig. 1. Large pieces of solute metal, in excess of saturation solubility, were added to 200 g of the solvent metal, and the entire charge placed in an alundum crucible. Analytical reagent or materials of chemically pure grade were used in all investigations. The crucible was contained in a zircon muffle tube positioned vertically in the uniform hot zone of a Globar resistance furnace. The tube was provided with a number of ports which permitted sampling at temperature and in controlled atmospheres or vacuum; the ports were also useful for evacuation and introduction of gases as well as for thermocouple measurements. A chromel-alumel thermocouple Sheated in a porcelain tube was used for temperature measurements. A purified hydrogen atmosphere was employed in all experiments reported in this paper. The hydrogen was purified by passing it first over hot copper gauze to remove oxygen and then through a molecular sieve immersed in

Jan 1, 1962

By R. F. Mehl, J. T. Ransom

For many years the Metals Research Laboratory of Carnegie Institute of Technology has been concerned with the statistical nature of the engineering properties of steel from an experimental viewpoint, particularly those properties representing ductility.&apos; In the past three years new work has been directed toward evaluating the statistical nature of the endurance properties. It has been shown that both the fracture curve and the endurance limit in fatigue are markedly statistical in nature. The S-N curve (and the endurance limit) of ferrous materials is often determined with specimens which number as few as ten. The common procedure is to test the first specimen at a stress well above the expected endurance hmit. Each succeeding specimen is then tested at a progressively lower stress, until, after five or six tests, a specimen runs ten million or so cycles without failing. Two or three more specimens are then used to find the highest stress at which failure will not occur; the limiting stress determined in this way is called the endurance limit. It has now been found, however, that the variability in the fracture curve and in the endurance limit in heat-treated alloy forging steels is so great that S-N curves must be drawn on the basis of distribution curves which can be appraised only by statistical methods. Two methods have been adopted in this study: (1) straightforward statistical studies of cycles to fracture of a number of specimens at each of a series of stress levels, and (2) a new abbreviated statistical method, known as "staircase testing."2 The latter corisists in testing a series of specimens, one by one, with the test stress for any given specimen automatically

Jan 1, 1950

By William P. Blake

Postscript to the paper read by Prof. William P. Blake at the Lake Superior meeting, September, 1904. POSTSCRIPT.*-Since the publication of my paper upon the blackening of the surface of rocks in desert regions, I have noted that similar views of the origin of superficial discoloration in the case of certain rocks from the Salt Lake basin of Utah have been expressed by Prof. George P. Merrill. In the pamphlet, he described the brown-coated weathered boulders from Tooele county, reaching the conclusion that the discoloration was due to the solution of the manganese and iron compounds &apos;in the interior of the boulder, while they were in the water, and the gradual bringing of this material to the surface through capillarity and its oxidation when exposed.

Mar 1, 1905

Jan 1, 1967

Jan 1, 1967

By AIME AIME

M ALBERTSON is research engineer for the Shell Petroleum COT. He joined the Roxana Petroleum Corp. (later the Shell) in 1920, at Hanger, Texas, became district geologist at Shreveport, and after two years was transferred to the production department, where he has been for the past fifteen years. His jobs have ranged from a modest field engineer up to assistant production manager. During this time hc has successively resided in Texas, Louisiana, Missouri, Louisiana, Oklahoma, Missouri, Texas, The Hague (Holland), and Texas. II? the Yates Pool, Texas, in 1929, "Al" initiated&apos; the tubing of wells under pressure to control gas-oil ratios, particularly at restricted rates of flow. This led to the compulsory tubing of all oil wells drilled in the State

Jan 1, 1937