By Hugo Cabrera-Real

This work investigated the chemical and mineralogical properties of CaO-SiO2-CrOx-CaF2- MgO slags. Synthetic slags were prepared and the effect of the slag basicity (CaO/SiO2) and MgO contents on the stability of the mineralogical species formed was analyzed. The morphology and composition of the slags were analyzed by XRD and SEM-EDS, whilst their chemical stability was evaluated by leaching with an aqueous acetic acid solution. It was found that in slags with CaO/SiO2 = 1, the main Cr-compound was MgCr2O4 spinel, which forms octahedron crystals. Small amounts of CaCr2O4 and CaCrO4 were also observed. It was found that increasing the slag basicity from 1 to 2 the compounds MgCr2O4 and CaCr2O4 were formed together with the Cr(V)-containing compound complex Ca5(CrO4)3F which forms hexagonal crystals. The results showed that the highest chromium concentration levels in the leaching liquors corresponded to slags with CaO/SiO2 = 2, probably owing to the formation of Ca5(CrO4)3F.

Jan 1, 2010

By WU Jian-hui

Keywords: metallic material, precursor synthesis, precipitation, nickel, fibrillar powder The composition and morphology of the precursor of fibrillar nanocrystalline nickel powder prepared by oxalate precipitation are characterized by XRD,IR and SEM analysis, and the effects of temperature, nickel concentration, pH, surfactant and drying process on the morphology and the dispersion of the precursor are investigated. By the experiment results, the fibrillar precursor is a complicated nickel salt. The precursor prepared in the of 60~70°C,0.6~0.8 mol/L nickel ion, pH=8.4~8.6 and with addition of PVP surfactant is well dispersive and in fiber form. The powder dried by azeotropic distillation is dispersive.

Jan 1, 2005

By Chen Song

Keywords: Mixed extractant, Copper, Cobalt, Nickel, Synergistic effect During separation process of copper and cobalt from nickel sulphate solution, the effects of constitutions and compositions of mixed extractant D2EHPA and PC88-A or Cyanex 272, has been studied. In one step extraction cycle, the following results are obtained:[Ni]/[Co]>4000 and [Ni]/[Cu]>40000 in nickel sulphate solution, [Co]/[Ni]>1000 and [Co]/[Cu]>30000 in cobalt chlorinate solution, [Cu]/[Ni]>10000 and [Cu]/[Co]>200 in copper sulphate solution. It was elucidated that the above-mentioned synergistic mixtures can effectively separate cobalt and copper from nickel sulphate acid solution and achieve a greater synergistic effect.

Jan 1, 2005

By G. L. Liu

"Deformation Banding ( DB ) in cold rolled mild steel has been experimentally established by microstructure investigation. Deformation banding model includes such deformation mode when it is applied to rolling texture simulation. The cause for the occurrence of deformation banding is the reduction of the total work for plastic deformation through a relaxation of the deformation constraints. In the first DB model, all grains are assumed to band from the first deformation step. Such an unrealistic assumption has been eliminated in the new model by the introduction of a banding criterion based on an energy minimizing approach. The prediction is closer to the measured texture by applying banding criterion and setting critical resolved shear stresses (CRSS) ratio for { 110 } and { 112 } slip modes to 0.85.IntroductionBased on the continuum theory of plastic flow and deformation mechanism of crystallographic dislocation slip, Taylor's FC ( Full Constrain ) theory [1] has been widely used in texture modeling. As the process of cold rolling of sheet materials produces a microstructure consisting of elongated or equiaxed flat grain or cell, the ""lath"" and ""pancake"" relaxed constraints ( RC ) models [2, 3] were introduced as the successful improvements over the classical FC model. It has been also recognized that crystals may split into different orientations during deformation and the term deformation banding is used to describe such deformation processes [4, 5]. Lee et al. [6, 7] pointed out that the success of the RC theory in predicting textures depends on the physical processes of deformation banding. They developed so called Deformation Banding ( DB ) model by considering DB in the longitudinal plane to be accounted for by the RC method and allowing DB in the rolling plane. DB model was applied to simulate the texture development in bee case [8], the predicted bee rolling textures are in reasonable agreement with the measured textures. In the first DB model, however, all grains are assumed to band right upon the first deformation step. A banding criterion was formulated [7] which states that DB will occur if the work used in DB model is less than that in RC model. Such criterion has been incorporated into the original DB model for texture simulation and is referred to as DBC ( Deformation Banding Criterion ) model."

Jan 1, 1998

By Fang Wu

The paper designs an extraction flow for the total recovery of nickel and cobalt and removing magnesium simultaneously from the cadthodic materials of the spent hydrogen-nickel and cadmium-nickel batteries. The separation of Co, Ni and Mg though P507 extraction .The extraction equilibrium pH is 4.5~5.0, ßNi/Co is 140~180, and ß Ni/Mg is 20~25; nickel and magnesium are scrubbed in two steps, in which the equilibrium pH of nickel and magnesium scrubbing is controlled at 5.0±0.1 and 4.4±0.1 respectively. The stepwise scrubbing technique is adopted to remove 94.5% of magnesium and to recover 99.45% of nickel and 95.35% of cobalt. During the integrated extraction and precipitation process the total recovery fraction of nickel and cobalt are 99.99% and 99.95%, and the recovery fraction of magnesium is 94.02%.The recovered NiSO4 and CoSO4 solution are enriched and crystallized.

Jan 1, 2009

The effect of rare earth element Y (0-2.0at.%) on the microstructure of TiAl alloys at the as cast and rapidly solidified conditions has been investigated. The results show that the addition of Y greatly refined the microstructure of TiAl alloys at both conditions. The refinement is more significantly with higher Y content. The refinement of Y in the cast alloys is attributed to that the strip-shaped Y-rich phase locating on the grain boundaries impedes the grain growth during solidification. In the rapidly solidified alloys, Y-rich phase dispersing uniformly as spherical particles in the matrix acts as heterogeneous nucleation sites which increases the nucleation rate of ??phase during the ????phase transformation, and produces a refined initial microstructure during solidification. Higher cooling rate restricts the grain growth during subsequent cooling.

Jan 1, 2010

By Xuan Li

Aluminum slag is generated when aluminum metals are recycled through a smelting process in the presence of salt. There are small amounts of aluminum metals trapped in the aluminum slag. This research aims at evaluating the use of aluminum slag as an expansion agent for the production of lightweight concrete by taking advantage of the residual aluminum metals in the slag. The research identified key elements of producing lightweight concrete products through utilizing various mixture components including sodium hydroxide (NaOH), lime (CaO), cement, and gypsum. The volumetric expansion rate was investigated and the density and strength of the products were determined. The results show that aluminum slag can be utilized for the production of lightweight concrete products.

Jan 1, 2010

By Zhouhua Jinag

The attempt has been made to manufacture high nitrogen austenitic stainless steels by pressurized electro-slag remelting furnace with maximum nitrogen pressure of 7MPa. To obtain high nitrogen content in steels, the compound electrodes with different nitrogen sources (FeCrN, Si3N4) were prepared. Using the Si3N4 as the nitrogen alloying source, the silicon contents in ingots were prone to be out of the specification range, and the electric current fluctuated greatly and the surface qualities of the ingots were poor. The surface qualities of the ingots were improved using FeCrN as nitrogen alloying source. The sound and compact macrostructure ingot with the maximum nitrogen above 1.0wt% could be obtained. A series of high nitrogen austenitic stainless steels have been successfully developed by this method. The mechanical and pitting corrosion resistance properties of high nitrogen austenitic stainless steels were investigated. The results show that the steels exhibit excellent mechanical and pitting corrosion resistance properties.

Jan 1, 2009

By Hector Carreon

Due to elevated temperatures, excessive stresses and severed corrosion conditions, turbine engine components are subject to creep processes that limit the components life such as a turbine bucket. The failure mechanism of a turbine bucket is related primarily to creep and corrosion and secondarily to thermal fatigue. As a result, it is desirable to assess the current condition of such turbine component. By using eddy current images, it was shown that the eddy current technique could be used to monitor creep damage in a nickel base super-alloy. The eddy current results also show a significative variation in the electrical conductivity on the creep damage zone with respect to the background zone in nickel-base super-alloy samples. In addition, the absolute thermoelectric power coefficient show also a strong dependence associated with creep damage in nickel base super-alloy samples using a copper hot tip reference. The eddy current and thermoelectric power techniques seems to show promise as nondestructive evaluation tools for monitoring the level of creep damage in metallic alloys.

Jan 1, 2010

By H. Doostmohammadi

During the tapping of liquid steel from Electric Arc Furnace (EAF), some slag is carried over into the ladle. High levels of FeO and MnO in slag carryover increase the oxygen activity in steel melt leading to oxide inclusion formation during the ladle treatment. The demand on cleaner steels requires minimization of carryover slag. In this work, the effect of EAF slag carryover on ladle slag-steel equilibrium calculations for a hot working tool steel was studied. Steel and slag sampling were done in Uddeholm Tooling AB in Sweden. XRF and OES techniques were used to determine chemical composition of samples. The quantity of slag carryover was calculated based on a mass balance followed by thermodynamic calculations on metal-slag equilibrium using Thermo-Calc software. The agreement between predictions and experimentally determined compositions was good. This leads to the development of a prediction method for optimizing the production of other tool steel grades.

Jan 1, 2009

By Zhigang Liang

A carbon free precast block was prepared by using high-alumina fused corundum as aggregate and fused magnesia, and ultra-fine Al2O3 and ultra-fine SiO2 powders as matrix materials. A small linear expansion for the precast block was achieved through spinel formation from the reaction of MgO with Al2O3. The precast block showed a lower apparent porosity, higher hot modulus of rupture and better slag corrosion resistance compared to the traditional Al2O3-MgO-C brick. Moreover, the practical application of the precast block to the ladle lining proved it to possess a better thermal insulation which could effectively prevent the temperature drop of molten steel during the refining process. It can be predicted that the carbon free precast block could possibly be accepted as a new type of ladle lining material for the production of low-carbon and ultra-low-carbon steel.

Jan 1, 2009

By Daniel Bennett

There are few methods currently applied towards on-line bulk mineralogical analysis. Yet on-line knowledge of process mineralogy could potentially provide large benefits, such as increased extraction efficiency or resource optimization. The work described in this paper involves the development of radio frequency methods for bulk mineralogical analysis. Some resonances that occur in the radio frequency spectrum are mineral specific, and potentially allow quantitative estimation of mineralogy in an ore stream. Results will be presented on the specific detection of chalcopyrite. Initial quantitative measurements investigating matrix effects have indicated the feasibility of on-line mineralogical estimation using radio frequency techniques.

Jan 1, 2006

By P. A. Olubambi1

Representative samples of the hydrothermal vein deposits of the bulk complex sulphide ore deposit, 10 km south of Ishiagu, in Ebonyin State, South Eastern part of Nigeria were collected from two small scale mining companies. The samples were mixed and successively crushed in a jaw crusher and cone crusher, and ground in a rod mill. Characterization was carried out with SEM, EDX, XRD, XRF and ICP-OES. Mineralogical analysis revealed the presence of sphalerite, galena, siderite, pyrite, quartz and chalcopyrite. X-ray Diffractometry showed that sphalerite mineral in the ore occurs as sphalerite ferrous with varied percentage of Zn and Fe within the various sizes while chalcopyrite occurs as a chalcopyrite group mineral with chemical formula Cu2MnSnS4. Results of the elemental analysis showed variations in elemental composition within the different sizes.

Jan 1, 2006

By Tsunehisa Nishimura

Stable operation of the blast furnace needs adequate control of the lower part. To clarify the behavior of the lower part of the blast furnace with accurate consideration of the property of slag and its flow characteristic, a new mathematical model has been developed. Using this model, the effects of the change of operational conditions on the behavior of the lower part of the blast furnace were studied. Further, means to control of the lower part of the blast furnace, especially effective means to maintain adequate temperature, were discussed. And desirable slag property and composition, especially the method to control FeO concentration dripping from the bottom of the cohesive zone to avoid a decrease in temperature of the lower part of the blast furnace was estimated.

Jan 1, 2006

By Wen-Ming Chien

Keywords: AN-KN Phase Transition, Lattice Parameters of AN-KN, X-ray Diffraction The lattice parameters of the low and high temperature phase of KNO3-rich (in NH4NO3) solid solutions have been determined by the X-ray diffraction method. The low temperature single KNO3 phase (KN II) are from 92%-100% KNO3 in NH4NO3 composition range and from room temperature to 393 K showing in X-ray diffraction patterns. The high temperature KNO3 phase (KN I) showed very broad composition range between 20% to 100% KNO3. The lattice parameters of KNO3-rich (KN II and KN I) solid solutions have been calculated at different temperature range. The volumes of orthorhombic KN II phase decrease from 0.3208(3) to 0.3195(3) nm³ at the room temperature as the compositions increase from 95% to 100% KNO3. The lattice constants of the hexagonal KN I phase show that there is no significant change in a-direction when the temperature increases. Details X-ray results and lattice expansion equations during heating will be presented.

Jan 1, 2005

Sm-Co alloy is a kind of magnetic material with high power and has been applied in modern industry widely. In this study, the wet chemical co-precipitation was developed for synthesis of the Sm-Co alloy oxide precursor. The thermodynamic analysis of the studied system was done to clarify the solution behavior theoretically based on the thermodynamic equilibrium and simultaneous equilibrium. Then, the experiments were done to address the various effects on the wet chemical process, including solution pH, reactant concentration, dispersant, reaction temperature and time, etc. It is found that by precise control of the process, the Sm-Co alloy oxide precursor was synthesized with fine crystallization and special size & size distribution.

Jan 1, 2005

By Yongzhong Xiao, Tiejun Chun, Jian Pan, Zhen He, Deqing Zhu

"In this paper, the reduction kinetics of low grade hematite ore was calculated. Mineralogy shows that the ROM (run of mine) ore is of low grade hematite ore type, assaying 27.2 wt% Fetotal and with main valuable minerals of hematite. The reduction kinetics shows that the reduction reaction rates of pellets with additive and without additive are all controlled by diffusion through the product layer. The calculated apparent activation energy of pellets with 12 wt% complex additive is 8.55 KJ/mol, dropping 62.23% compared to that of pellets without additive.IntroductionWith the rapid development of iron and steel industry in China, there has been a soaring demand for iron ores in the past decade. The imports of iron ores have increased from 148 million ton in 2003 to 620 million ton in 2010[1]. Therefore, large quantities of low grade iron resources are necessary to utilize in China at the moment. During the past years, extensive research has been carried out on the low grade hematite ores [2-6], such as reverse floatation, gravity separation, high-gradient magnetic separation and direct reduction-magnetic separation. Direct reduction-magnetic separation is an innovation way to treat the low grade hematite [7]. However, the research of reduction kinetics of low grade hematite is few. Some research about the reduction kinetics of reducing iron oxides by CO was studied [8]. The results indicated that the apparent activation energy is 8.0-28 KJ/mol when the reducing reaction is controlled by internal diffusion. The apparent activation energy is 50-75 KJ/mol when the reducing reaction is controlled by chemical reaction. In this paper, the reduction kinetics of pellets was also been studied."

Jan 1, 2012

By Hong Yong Sohn

Keywords: Barium sulfate, Barium sulfide, Environment, Kinetics, Pollutants, Sulfur dioxide conversion, Thermodynamics Nonferrous smelters and coal gasification processes generate sulfur dioxide streams, most of which are treated to produce sulfuric acid with the accompanying problems of market shortage and transportation difficulties. While the conversion of sulfur dioxide to elemental sulfur has many environmental advantages, no processes exist that are environmentally acceptable and economically viable. A method for converting sulfur dioxide to elemental sulfur by a cyclic process involving calcium or barium sulfide and calcium or barium sulfate without generating solid wastes has been developed. In this process, the sulfate, as the starting raw material, is reduced by a suitable reducing agent such as hydrogen to produce the sulfide, which is used to reduce sulfur dioxide producing elemental sulfur vapor and regenerating the sulfate. The latter is then reduced to reproduce the sulfide. This paper describes work on the BaS/BaSO4 system. Thermodynamic analysis and experimental results indicated that the BaS-SO2 reaction produces mainly sulfur vapor and solid barium sulfate and that the gaseous product from the BaSO4-H2 reaction is mainly water vapor. The rates of the two reactions are reasonably rapid in the temperature range 700-1050°C.

Jan 1, 2005

By Thomas Weyand, Thomas Claridge, Dale Nickels

"This paper addresses the initial results of a project to evaluate the suitability of copper mining tailings as raw material for the production of structural products using PMET’s patented technology. Preliminary testing indicated that high performance structural products were possible using these materials. A demonstration scale project produced approximately 1,500 bricks in various colors. These products fall under under ASTM C- 73 and were found to present properties suitable for severe weather applications. Although the products in this project were of typical brick dimensions, other products are possible, for example concrete block substitutes or pavers. These products from the PMET process are commercially known as Brixx. This paper will provide operational details of the production process, mineralogy and mechanical properties of the products.INTRODUCTIONPMET has developed process technology that can convert various siliceous waste materials into competent structural products. This technology is the subject of US patent # 6,068,803. In general, the process consists of mixing lime, water and the major feed stock, pressing to form a “green” shape, and curing the product in an autoclave for 6 hours with saturated steam at ~200oC. The curing process forms Tobermorite, which acts as a crystalline binder. Freeport-McMoRan approached PMET to see whether mine tailings from the Sierrita mine, containing significant amounts of clay, might be a suitable feed material for the production of structural products. “Brixx” is the commercial term used to describe the resultant structural product formed in the test work. This paper is a preliminary evaluation of a technology that is being considered by Freeport-McMoRan. This report is not an endorsement by Freeport-McMoRan of the process or products, nor is it a commitment to use this technology."

Jan 1, 2008

By Jiann-Yang Hwang

Microwave heating has been proved an effective method to rapidly heat iron oxide. This offers an opportunity to apply microwave heating in the steelmaking process. The reduction reaction of iron oxide is traditionally achieved at high temperature with reducing gases such as H2 and CO generated from various sources, including coke, coal, and natural gas. This study investigates the differences in iron oxide reduction using conventional and microwave heating under H2 and CO atmospheres. A special microwave thermal gravimetric device was designed and built to facilitate the investigation. With this device, iron oxides can be heated by electric resistance heating, microwave heating, or a combination of methods. The incoming CO and/or H2 also can be preheated to simulate a potential utilization of recovered heat. The iron oxide weight and temperature can be monitored during an entire reduction period. A series of reduction experiments have been conducted. The results are presented and discussed.

Jan 1, 2006