Search Documents

By G. Gao

Flyash from municipal solid waste (MSW) incinerators is frequently classified as a characteristic hazardous waste due to its lead and cadmium content. Extensive investigation has therefore been carried out to detoxity the flyash by leaching and to recover lead, cadmium and zinc. Detoxification can be accomplished by leaching in HCI/NaCI solutions. Optimization of leaching conditions for effective detoxification and subsequent metal recovery can be achieved by controlling the acidity of the lixiviant and flyash to lixivaint ratio. Lead and cadmium In the leaching solution is recovered by cementation with zinc dust. Leaching and cementation experiments have shown that zinc concentrations suitable for electrowinning, > 15 g/liter, can be achieved. Experiments have also been performed to determine the effects of pH, particle size of the zinc dust used, quantity of zinc added and dissolved impurities on the cementation kinetics. After recovery of lead and cadmium, electrowinning or electrowinning coupled with solvent extraction can be used to recover zinc. A process flowsheet is presented.

Jan 1, 1991

By David Dreisinger

The cyanidation of copper containing gold ores results in the co-dissolution of copper along with gold. Copper dissolution results in elevated cyanide consumption that may make the treatment of the gold ore uneconomic. Copper-cyanide species in gold mill effluents may increase the environmental toxicity of the gold mill solutions. The objective of this study was to examine the use of solvent extraction to recover the copper cyanide species from gold mill effluents. Solvent extraction with Cognis (formerly Henkel) reagents LIX 79 and LIX 7950 was studied. Excellent extraction of copper and cyanide was achieved using pH control in extraction. Copper and cyanide may be stripped from the reagents using basic eluants. Various routes for copper and cyanide recovery from the strip solution were studied. Excellent results were obtained using electrowinning in both divided (Nation membrane) and undivided cells. Cyanide recovery was obtained by AVR treatment of a bleed stream from electrowinning. Full results of solvent extraction, copper and cyanide recovery are reported.

Jan 1, 1998

By N. Panagiotopoulos

A low-grade (1.06% Ni, 0.06% Co) hematitic type lateritic ore from Triada, Euboea Island, Greece, has been leached with sulfuric acid at atmospheric pressure for the extraction of the contained Ni and Co values. The effect of various parameters, including reaction time and leaching temperature, acid strength, pulp density, etc., on Ni, Co extraction and Fe dissolution was determined. By leaching at 95°C for 4h with a 3N sulfuric acid solution at 25% pulp density, Ni and Co extractions were 82 and 75% respectively, and Fe co-dissolution 28%, yielding a pregnant solution containing 2.7 g/l Ni, 0.16 g/l Co, and 33 g/l Fe. Overall acid consumption was 850 kg/t ore (or 100 kg/kg Nil. Preheating of the laterites at 600°C before leaching resulted in much faster leaching kinetics for Ni, but the final extraction and acid consumption remained unaffected; Fe extraction was not influenced. Three-stage counter-current leaching at 9S°C, using 2N acid strength at each stage and 35% pulp density, reduced acid consumption to 350 kg/t ore (41 kg/kg Nil, and yielded 81% Ni recovery. Percolation leaching of -10 mm laterite at ambient temperature with 3N acid for 7 days resulted in 58% Ni extraction.

Jan 1, 1988

By P. Peczak

A Monte Carlo simulation technique has been used to study dynamic recrystallization in polycrystals. A continuum microstructure of the polycrystal is modeled employing a discrete lattice. The response of the material to hot deformation is simulated by adding stored energy and recrystallization nuclei continuously with time. The experimentally observed nonuniform character of deformation substructures is modeled by employing a phenomenological expression for inhomogeneous distribution of the stored energy. All simulations were performed on HP-Apollo 9000 Series 700 workstations. A program written in FORTRAN with use of PHIGS graphics library calls was used to interactively monitor the current state of the matrix and all relevant parameters: deformation stress, average grain size and effective nucleation rate. Visual analysis of the simulated microstructure allows a better understanding of the data developed by averaging over a number of very long Monte Carlo runs. Since the essential features of dynamic recrystallization are accurately reproduced by the model, it is used to discuss the role of the controlling mechanisms of the dynamic recrystallization in real polycrystal.

Jan 1, 1993

By László I. Kiss, Verena Mackowiak, Alexandre Perron, Dominic Toulouse, Alicia Liedtke, Sándor Poncsák

"Bubbles play a very important role in different metallurgical applications like for example in electrowinning. During heterogeneous nucleation, the maximal size of the bubbles growing at the nucleation sites as well as the nucleation frequency is determined by the so-called detachment condition. Detachment occurs when the external forces acting on the bubble exceed the retaining forces along the solid-gas-liquid triple interface line. The phenomenon depends strongly on the shape and orientation of the solid surface and on the nature and strength of the external buoyancy and drag forces. In the present study the detachment conditions of bubbles from downward facing horizontal and inclined plates were studied experimentally under the effect of gravitational and hydrodynamic forces. The results show the deformation of the bubbles under the effect of the external forces and the detachment conditions as function of the bubble volume.IntroductionIn heterogeneous nucleation bubbles are generated at the so-called nucleation sites along the solid-liquid interfaces. They continue to grow there and after they reached a certain size they detach from the solid surface and leave the nucleation site. This scenario is well known both in boiling and electrolysis. During the growth period a stable equilibrium exists between the forces that retain the bubble at the nucleation site and the forces that try to remove it. This equilibrium evolves with the increasing volume of the bubble to the point when the detachment forces overcome the retaining forces.The life of a single bubble generated by heterogeneous nucleation can be divided into two periods separated by the detachment - or in other words by the departure - of the bubble: first the growth at the nucleation site and then the movement away. The knowledge of the detachment conditions makes possible the determination of the maximal volume of the bubble at the nucleation site that, in tum, makes possible the determination of the nucleation frequency. This is why so many researches have been directed toward the clarification of the details of the bubble detachment in the past decades. The equilibrium between the attaching and separating forces depend on the presence of body, surface and flow induced forces in the liquid, on the geometry and orientation of solid surface, on the properties of the solid-liquidgas system etc."

Jan 1, 2004

By Matthew John M. Krane, Christopher J. Vreeman, J. David Schloz

"A continuum mixture model of the direct chill casting process is used to model the transport phenomena and solidification behavior in the Direct Chill casting of an Al - 6 wt% Cu billet using Wagstaffs AirslipTM process. The model, which includes the transport of free-floating solid particles, can simulate the effect of a grain refiner on macrosegregation and fluid flow. Numerical predictions of sump profiles and composition and temperature fields are presented. Two 45 cm diameter billets were cast under production conditions with and without grain refiner. Temperature and composition measurements and sump profiles are compared to the numerical results. The comparison shows excellent agreement for the grain refined case. It is believed that an incorrect model assumption prevents good agreement in the non-grain refined billet. IntroductionDirect chill casting is a semi-continuous process in which molten aluminum enters the top of a water-cooled mold, is cooled, and forms a solid ingot drawn out below (Figure l(b)). The molten aluminum begins to solidify due to the cooling effect of the mold wall. As the ingot is withdrawn from the bottom of the mold, water jets impinge on the surface, directly cooling the billet and forming a solid layer around a liquid melt, commonly referred to as the sump.A particular defect that occurs in a wide range of casting processes, including the direct chill (DC) casting of aluminum alloys, is macrosegregation, the uncontrolled redistribution of alloying elements on the scale of the ingot during solidification. Macrosegregation in DC cast ingots can produce non-uniform mechanical properties [l], which affects the behavior of the metal during downstream forming and heat treat operations."

Jan 1, 2001

By Kuniaki Murase, Tetsuji Hirato, Yasuhiro Awakura

"Electrodeposition of CdTe was studied using aqueous ammonia-alkaline electrolytic baths in which Cd11-and Te1V-ions are dissolving as Cd11(NH3)/+ and Te1vol-ions, respectively. Ca-thodic polarization curves of the baths suggest the presence of strong interaction between the Cd11-and Te1V-ions; electrodeposition of tellurium is inhibited by the presence of Cd(NH3)/+ ions. The interaction makes it possible to electrodeposit CdTe films with stoichiometric composition. Polycrystalline CdTe thin film of about 1 µm thickness was electrodeposited at 343 K from ammonia-alkaline solutions (pH= 10.7) containing TeO32-(<20 mmol dm-3) and Cd(NH3)/+ ( < 60 mmol dm-3) ions. Increasing Cd(NH3)/42+/TeO32- mole ratio or decreasing total concentration of ammonia/ammonium-ion gave flat and smooth crystalline CdTe deposits at constant cathode potential-0.70 to -0.30 V vs SHE at 343 K.IntroductionCadmium telluride (CdTe) is well-known as a compound semiconductor whose band gap, i.e. 1.44 eV, is suitable for solar energy conversion with a photovoltaic cell. Various methods, such as CVD (chemical vapor deposition) and electrodeposition, of preparing CdTe thin films for solar cells have been investigated.Acidic sulfate solutions with a pH of 1-2 are usually employed for CdTe processing by electrodeposition.1-3) The electrodeposition of compound semiconductors is usually achieved (i) at a higher cathode potential than the redox potential of less-noble species, can in this case, and (ii) under the condition of diffusion-limiting current of a more noble species, Te1Y.4) There-fore, a suitable CdII/TeIV concentration ratio in the acidic electrolytic baths, resulting in the deposition of stoichiometric CdTe, is determined by the diffusion-limiting current density of TeIV- reduction, i.e. the concentration of HTeIVO2+ · Since the solubility ofTe1v species HTeIVO2+ in the acidic solutions is quite low, the rate at which CdTe is deposited from the acidic solutions is extremely slow."

Jan 1, 1998

By E G. Prado

We have confirmed on bench scale the removal of chlorides and alkalies (+95%) and over 2/3 of the zinc, lead and cadmium from EAF dusts. This has been achieved with arrononium acetate solutions alone, or with combinations of water wash, amonia-ammonium carbonate and ammonium acetate solutions. Also confirmed are the process routes for the recovery of the aforementioned elements into marketable products. The technology involves the complete recycling of the reagents. The FAF residue is returned to the electric furnace without risk of impurities buildup. Commercial scale testing with the recycled dust was satisfactory, including quality of the slag and its behavior during the melting stage. A cursory feasibility evaluation is presented.

Jan 1, 1994

By E. A. van Dijk

Dusts from steel-making processes contain substantial amounts of zinc. Such dusts are also a hazardous waste and dumping them becomes unacceptable from environmental point of view. Therefore processes that can recover zinc and possibly other metals from steel-making dusts are being investigated. The aim of this paper is a contribution to the more fundamental kinetic aspects of zinc reduction from silica free calcium ferrite slags. The effects of alumina, lime and magnesium oxide contents of the slag, the COICO, ratio and the effect of initial Fe2O3/CaO ratio were studied experimentally at 1400°C The results indicated that the reduction of zinc from molten slag was possibly a first order reaction. As expected higher COICO, ratios increased both the extent and the rate of reduction. It was also observed that a higher iron content of slag improved the reduction of zinc from calcium ferrite slags. This fact seems to support the proposed mechanism that zinc is partly reduced by ferrous iron to zinc vapour and that ferric iron is reduced by carbon monoxide. The reduction rate of zinc in these slags was decreased by increasing alumina content of the slag. Alumina decreased the calculated optical basicity of the slag showing the fact that reduction of zinc oxide was more favorable in more basic slags. Probably the formation of complex ions by alumina and zinc oxide such as ZnAl2O32+ lowers the activity of Zn2+ ions in the slag and hence render them more difficult to reduce.

Jan 1, 1999

By Nural Kuyucak

Acid mine drainage (AMD) occurs at operating and abandoned mine sites as a result of oxidation of sulphide minerals, and is characterized by low pH and heavy metal contamination (e.g. Fe, Zn, Cu, Cd, Al, Mn). It usually requires treatment before release in order to meet regulatory requirements. Chemical methods, such as lime neutralization and sulphide precipitation, are commonly used to treat AMD. However, the conventional processes require high capital and operating costs, and constant attention for many years into the future. In addition, the amount of sludge produced by conventional lime treatment processes poses an increasingly significant disposal problems at decommissioned mining operations. There is, therefore, an urgent need to develop passive, cost-effective processes for mitigating AMD and seepages originating from tailings and waste rock areas. Noranda Technology Centre (NTC) has been evaluating various methods being developed by other institutions, and exploring new ideas, to achieve passive in situ processes for treating AMD. These methods include anoxic limestone (ALS), lime-organic mixture (LOM), biosorbents (BIOS) and biotrench (BT). Current investigations at NTC involve preliminary bench-scale testing. Based on the outcome of the bench tests, a field test will be performed at a selected site. Details of the bench tests are discussed in the paper. Key Words: Acid mine drainage, treatment, metals removal, passive treatment, anoxic lime, limestone, biological treatment, sulphate reducing bacteria, biosorption, biosorbent

Jan 1, 1993

By I. H. Gundiler

Sandia National Laboratories (SNL) is tasked to support The Department of Energy in the dismantlement and disposal of SNL designed weapon components. These components are sealed in a potting compound, and contain heavy metals, explosive, radioactive, and toxic materials. SNL developed a process to identify and remove the hazardous sub-components utilizing real-time radiography and abrasive water-jet cutting. The components were then crushed, granulated, screened, and separated into an aluminum and a precious-and-base-metals fraction using air-tables. Plastics were further cleaned for disposal as non-hazardous waste. New Mexico Bureau of Mines & Mineral Resources assisted SNL in investigation of size- reduction and separation technologies.

Jan 1, 1995

By Tseng. B. H.

Samples of unchlorinated and chlorinated carbonaceous concentrate from a carbonaceous gold ore were analyzed by transmission electron microscopy (TEM) for organically bonded sulfur and chlorine. The concentrate assayed 1.53 oz/t gold and 6.01% organic carbon. Much of the organic carbon occurred as sizable coarse particles up to several hundred microns in size, which showed no visible evidence of reaction with chlorine after chlorination treatment. Both the untreated and chlorinated fractions of the carbonaceous concentrate were analyzed by the TEM method, which detected organically bonded sulfur in all of the carbon particles examined in the untreated sample, ranging from about 1 to 5% organic sulfur, and averaging near 3.1%. TEM analysis of 40 carbon particles in the chlorinated sample indicated that organic sulfur was reduced significantly in the carbon and replaced in part by the chlorine, as the result of chlorination.

Jan 1, 1987

By Dilip Banerjee

"This paper discusses the Advanced Technology Program (ATP)'s support over the last decade to the development and use of process modeling as a tool to address some of the challenges faced by the U.S. metal casting industries. A particular focus will be given to highlight how process modeling can be used to improve the manufacturability of components needed for high performance and critical applications. The challenges associated with the design and production of thin-walled, cast parts with intricate and complex internal geometries will be discussed. Modeling issues associated with the control of the final grain structure in the solidified parts will also be addressed. This paper will describe the advantages of using appropriate mathematical models for designing new alloys for use in various applications.Finally, the role that ATP has played in uplifting the U.S. technological base through partnerships with industry and academia in high-risk research in order to bring to market new and improved products for the broader benefit of the nation will be discussed.ATP's BackgroundIn the 1980s, U.S. industries were losing market share to low-cost, high-quality manufacturers from Asian countries. Corporate leaders and policy makers determined that in order to sustain and grow market share, U.S. industries needed to improve their competitiveness and productivity through product and process innovation. There was evidence that companies were systematically under-investing in leading-edgetechnologies and failing to complete the development of new technologies [l]. There were also arguments in academic circles that pointed to a potential market failure in the area of early-stage technological developments. These concerns provided impetus for creation of the Advanced Technology Program (ATP) within the National Institute of Standards and Technology through the Omnibus Trade and Competitiveness Act of 1988. Through a rigorously competitive, cost-shared partnership with industry, ATP fosters the development and broad dissemination of high-risk technologies that offer the potential for significant broad-based economic benefits to the United States."

Jan 1, 2004

By George Owusu

A study has been carried out on the use of solvent extraction, instead of the traditional zinc dust cementation process, to remove copper from concentrated zinc sulphate leach solutions. In a series of experiments using plant solution containing 1.9 g/L Cu, 2 g/L Fe, 173 g/L Zn, 7.9 g/L H,SO,, 0.25 g/L Cd, 15 mg/L Co etc. and LIX 622 in SX-1, up to about 97-98 % of copper present in the zinc sulphate leach solution was extracted with negligible co-extractions of zinc, iron, cadmium, cobalt, etc. pH modification was not required for this reagent. The copper loaded organic was almost completely stripped using 150 g/L sulphuric acid. Investigations into the effect of any possible organiclextractant contamination on zinc electrowinning showed (if any) little effect on current efficiency if the organic contamination is less than 45 ppm; current efficiencies of 95-97 % were obtained. At organic contaminations higher than 45 ppm, the current efficiency dropped to about 92- 94 %. Visually, the organic-contaminated cathode sheets had rough surface morphology, becoming more intense with increasing organic concentration, compared to the non-contaminated cathode sheets.

Jan 1, 1998

By Larry G. Twidwell

The removal of dissolved arsenic from mine waste waters utilizing a lime/phosphate precipitation technique has been studied on a laboratory scale at Montana Tech of The University of Montana and on a pilot scale at MSE Technology Applications as a wastewater treatment process potentially capable of removing dissolved arsenic to <50 µg/L. Arsenic bearing lime and lime/phosphate slurries were subjected to laboratory extended-time air-sparged aging for over four years. The lime slurries released their arsenic back into solution in a relatively short period of time, whereas the lime/phosphate slurries showed limited release of arsenic. The developed process has been pilot scale tested by MSE-TA for the EPA Mine Waste Technology Program on three waters, ASARCO smelter blowdown water, ASARCO thickener overflow water, and Mineral Hill Mine groundwater. The laboratory study results will be presented and discussed in this presentation. The pilot scale results will be presented and discussed in a companion presentation. Stability, Aging, Apatite, Johnbaumite

Jan 1, 2005

By R. Padilla

The reaction of chalcopyrite with gaseous sulfur has been investigated in the range 350-450 °C in order to transform this mineral into a more acid soluble copper sulfide and insoluble iron sulfide. The results of thermodynamic analysis of this system as well as the X-ray diffraction analysis of the reaction products showed that in the temperature range 350 400°C the sulfidation reaction proceeded without formation of intermediate copper-iron sulfides according to: The effects of temperature and time on the conversion of chalcopyrite were studied. Conversion of chalcopyrite reached about 80% very rapidly with increase in temperature up to about 400°C. The recovery of copper from the sulfidized samples was determined by leaching in oxygenated 1.2M H2S04, 2M NaCI solution. Copper recoveries over 90 % were obtained from samples sulfidized for 30 min at temperatures lower than 400°C.

Jan 1, 2001

By Guolin Zheng, Jian Pan, Deqing Zhu, Xianlin Zhou

"In ferronickel production, nickel oxide and part of the iron oxide are reduced to metal by agglomeration and smelting in blast furnace. Due to the physical and chemical properties of the laterite ores, a large fraction of fines is generated during the pre-treatment stages and the strength of agglomeration is weakened, which results in low productivity and bad quality. In this paper, the process of pelletization of nickel laterite was developed, and some parameters to strengthen the pelletization of nickel laterite have been optimized. The results show that the compressive strength of fired nickel laterite pellet can reach over 2000 Newton per pellet while firing at the temperature of 1220 °C~1250 °C in 12 min. The product pellet can be used as high-quality burden for blast furnace to manufacture ferronickel.IntroductionIn recent years, the global stainless steel market was developed exuberantly, which greatly promoted the needs of the basic raw material of stainless steel smelting - metal nickel. Currently nickel sulfide ores are only 40% of global nickel reserves, but offer 60% of all the nickel production. However, with the deficit of resources, the nickel sulfide ore (high grade ore) is depleting, so there is an increasing focus on the utilization of low-grade nickel laterite. Recent research has focused on the wet treatment process to utilize nickel laterite, and less on the use of other technologies [1-8]. The economical and efficient technology relies on the reduction of nickel oxide and part of the iron oxide metal by agglomeration and smelting in blast furnace in China. Some domestic steel companies have adopted this process [9, 10]. Unfortunately a large fraction of fines is generated during the pre-treatment stages and the strength of agglomeration is weakened, which results in low productivity and bad quality of fired pellets. In this study, the process of pelletization of nickel laterite was developed firstly, and some parameters to strengthen the pelletization of nickel laterite have been optimized, and the product pellet can be used to produce stainless steel and ferronickel alloy by blast furnace."

Jan 1, 2011

By M. Misra, J. Nanor

The precipitation and removal of arsenic from process waters can be accomplished with addition of lanthanum chloride alone or in conjunction with ferric sulfate. The long term stability of these corresponding precipitated compounds is critical from the disposal stand-point. In this paper the characterization of ferric, lanthanum and lanthanum-ferric arsenate compounds formed at room temperature in acidic and alkaline pH is presented. The characterization techniques used included zeta potential, XRD and SEM. Zeta potential measurements of ferric and lanthanum hydroxides in the presence of arsenate indicate that oxyanions of arsenate are chemically adsorbed onto the positively charged surfaces of these hydroxides. In alkaline pH there is desorption of arsenate species from the ferric hydroxide surface, hence the product is thought to be unstable. On the contrary, lanthanum arsenate is stable in alkaline pH. XRD patterns show that the ferric arsenate formed in acidic and alkaline pH is amorphous, whereas lanthanum arsenate and lanthanum-ferric arsenate formed in acidic and alkaline pH are crystalline.

Jan 1, 1999

By Linfeng Zhou, Rong Sun, Guanghui Li, Zhiwei Peng, Tao Jiang

The effects of microwave roasting on separation of rhenium (Re) and molybdenum (Mo) from a molybdenite concentrate have been investigated based on evaluation of the heating characteristics of the concentrate in the microwave field. The results show that a variety of operating variables, namely microwave power, sample weight, sample geometry, roasting temperature, roasting time and atmosphere significantly impact on the volatilization rates of Re and Mo. The optimum conditions for Re-Mo separation are microwave power 1300 W, sample weight 20 g, sample geometry pellets, temperature 600 oC, time 1.5 h, and atmosphere 20%O2. Under these experimental conditions, the volatilization rate of Re reaches 88.12%, while that of Mo is just 5.15%. Microwave-assisted roasting provides an alternative route to separating Re and Mo from molybdenite concentrate.

Jan 1, 2016

By Animesh Jha, Catherine Davey

"Carbothermic reduction and nitridation reactions using synthetic kaolinite mineral were investigated for the formation of silicon based nitrogen ceramics. The temperature dependence of the reaction rate and its effect on phases formed are reported. The effect of the reactivity of carbon on the kinetics of formation of AIN and ShN4 is discussed. Using the standard Gibbs free energy values for the formation of nitrides and oxides of aluminium and silicon, a log po2 verses I/T diagram is constructed. The experimental data results are discussed and compared with the predicted phase equilibria. We also report the influence of sub-oxide gaseous species on the microstructure of the ceramic phases produced.IntroductionSynthetic kaolinite is a clay containing alumina, silica and water of crystallisation, and has a chemical formula 3(Al2O 3.2SiO2.2H2O). This mineral is relatively inexpensive and, is therefore an ideal candidate for use in the production of ceramic powder mixtures for example silicon nitride and aluminium nitride for composite material formation, When the mineral is heated, the water of crystallisation from the crystal lattice is lost via the 3(Al2O 3.2SiO2.2H2O) = 3(Al2O3.2SiO2) + 6H2O reaction. It has been shown [1·2j that on further heating to 1673K, the anhydrous kaolinite decomposes to a mixture of mulllte and silica, 3(Al2O3.2SiO2) = 3Al2O 3.2SiO2 + 4SiO2 which is consistent with the alumina-silica phase diagram, shown in figure 1.The binary alumina-silica phase diagram has a well-defined sub-eutectic immiscibility dome and this characteristic dernixing behaviour is reflected in the thermal decomposition of anhydrous kaolinite consequently the microstructural features resemble the spinodal decomposition process. It is well established that the spinodal decomposition process raises the nucleation frequency due to their low free energy barrier, (?G). The small magnitude of this barrier consequently promotes the evolution of a very fine microstructure. The process of spinodal decomposition is therefore expected to be influential during the reduction-nitridation of kaolinite minerals."

Jan 1, 1996