By Stavros A. Argyropoulos

Exothermic mass transfer takes place in various areas involving metallic systems, ranging from liquid metal processing operations to the growth of thin films in microelectronics. The formation of intermetallic compounds plays an important role in the exothermic mass transfer of metallic systems. Two types of exothermicity are identified , namely , Microexothermicity and Macroexothermicity. The former is encountered when small amounts of metals are mixed, while the latter is exhibited when a solid metal in a lump form is added into liquid metal. In this paper two types of exothermic mass transfer in metallic systems will be presented and reviewed. Mathematical modelling work for these types of exothermic mass transfer will be analyzed.

Jan 1, 1993

By Zhao-feng Xie

A new process of recycling valuable metals containing in the slag of jamesonite smelting in the blast furnace was studied. In this process, the valuable metals such as Pb, Sb, Zn and In etc. were fumed and volatilized and enriched in the dust firstly and then the dust was leached by sulfuric acid. In the leaching procedure, Zn and In in the dust entered into the leaching solution and were separated from Pb and Sb which remained in the residue.The optimal operation conditions of the fuming procedure are as follows: the mass ratio of the blast furnace slag, coal powder and lime are 100:22:10 respectively and the fuming time are 1.5~2.5 h, the fuming temperature is not below 1200C and the volatilization rates of Pb, Sb, Zn and In are 95%, 92%, 86% and 75% respectively. The optimal conditions for the leaching procedure are also presented: the consumption of sulfuric acid is 1.15 times of the theoretical consumption, the ratio of liquid to solid is 4:1 and the leaching temperature, leaching -1time and stirring speed are 90, 1.5h and 300 r?min separately. The leaching rates of Zn and In are 98.5% and 95.2% respectively. The experimental results shows that the valuable metals in the dust can be recovered and separated effectively by this process and the?ir recovery efficiencies are as follows: Pb94%,Sb91%, Zn84% and In69%.

Jan 1, 2009

By R. Fragoudakis

AISI 4130 steel is a medium carbon Cr-Mo steel used in automotive, aeronautic and other general-purpose industries. In this study, 4130 steel fatigue specimens were carburized at 927oC to enhance the carbon content in the steel, raising it from approximately 0.30% (non-carburized) to 0.90% (carburized, oil quenched and tempered). Rotating bending fatigue tests were performed on the R. R. Moore Rotating Beam Fatigue Testing System, in order to determine the high cycle fatigue (HCF) life of 4130 steel and plot the corresponding S-N diagrams. A comparison of the results of carburized and non-carburized specimens shows that carburizing of steel: a) increases the surface hardness and b) improves the fatigue strength of the steel by at least two orders of magnitude.

Jan 1, 2010

By Qingsheng Liu

A new method of recycling aluminum dross for preparation Al-Si-Ti alloy was studied in this paper. This was carried out in two processes. first the aluminum doss was pretreated by leaching and calcining process, the fine purity and phase of the intermediate oxide powder up to electrolysis demands, then, could be obtained when aluminum dross after washing have been leached for 2h at 100? in 20% hydrochloric acid and calcined for 2h at 1200?, which was treated by cryoite-based molten salt electrolysis. Finally, the Al-Si-Ti alloy was successfully obtained through electrochemical co-deposition in the cathode shows a typical as-cast microstructure. This new recycling method can produce high quality alloy and may bring remarkable economic and social benefits.

Jan 1, 2010

By Jilai Xue

Experiments with various industrial cathodes ranging from 35 wt.% to 100 wt.% graphitic and fully graphitized carbons were carried out in a laboratory aluminum electrolysis cell. Sodium and cryolite bath penetration into the cathode samples was measured by XRD and SEM-EDS analysis. For a higher cryolite ratio in the bath, the cathodes with lower graphitic carbons exhibited more sodium penetration than the fully graphitized. The increased graphitization in the cathode materials can reduce Na, NaF and Na3AlF6 penetration. SEM-EDS inspection reveals that the sodium and fluorides penetration within the cathode samples has different patterns for varying graphitization of the carbon materials. XRD quantitative analysis indicates that there is a large percentage of Na3AlF6 in the penetrated bath. The results can provide useful information for quality evaluation of the industrial cathode products.

Jan 1, 2010

By Jinhui Li

Silver is a very important metal used in a wide range of applications. It is necessary to recovery of Ag from electronic wastes for increasing of Ag price and circumstance protection. For separating and recycling Ag from Ag-Cu composite materials, thermodynamic data of reaction is calculated and some experiments have been proceeded with Ag-Cu composite material scraps, time, temperature, nitric-sulfuric mixed acid volume ratio and the volume ration of mixed acid vs. water have been discussed. The results show that the optimization conditions is that nitric-sulfuric mixed acid volume ratio 5:95, volume ratio of mixed acid vs. water 10:1, temperature 55?, time 25min. In the conditions, Ag can be selectively leached from Cu-based composite material, Cu base is not eroded nearly.

Jan 1, 2009

By Xiaowen Liu

The DSC/TG, IR and XRD analysis were used to characterize the heating phase transformation of illite, which came from Ouhai deposit, China. It was discovered that the dehydration and de-hydroxylation of illite carried out stage by stage during heating. The adsorptive water and layer-inter water were dehydrated from room temperature to 500°C; and dehydroxylated in the range 500°C~800°C. In these stages of process, illite?s layer structure kept almost unchanged. After 800°Cillite began to change into disorder structure. At about 1100°C, the layer structure of illite had been destroyed, and amorphous SiO2 and mullite crystallite appeared. At about 1200°C the structure of illite completely destroyed and mullite crystal phase had become perfect..

Jan 1, 2006

By Yufeng Guo

Mineralogy and physico-chemical characteristics of a nickel hydrometallurgical residue and recovery of iron-bearing minerals by flocculation-magnetic separation were studied. The results show that the nickel residue is super-fine and fraction less than 0.045mm reaches 85.4%. Ferrous minerals are chiefly magnetite and ferruginous glass. Magnetite accounts for 31.7% and exists as free magnetite. Ferruginous glass is of multicomponent amorphous substances with low-iron grade but strong magnetism, and accounts for 39.9% of total iron minerals. Addition of flocculants increases granularity and magnetic force of fine iron-bearing particles and improves iron grade and recovery. The tests with flocculation separation show that a concentrate assaying 56.68% Fe with 81.72% recovery was obtained in a magnetic tube. A concentrate with 56.92% iron grade and 67.96% recovery was obtained by flocculation-magnetic separation with a magnetic cylinder.

Jan 1, 2006

By Junfeng Shen

Geosynthetic clay liner (GCL) is a kind of waterproofing material used widely in engineering. The waterproof mechanism is understood in terms of bentonite particles becoming a water-obstructcolloid layer after they absorb water and swell. The swell stress, however, has not been determined directly till now. In our experiment, the swell stresses of the GCL under saturated and water absorbing conditions are measured directly using a custom-made instrument. The results show that (1) the instrument designed by the authors performed satisfactorily and the test results are reproducible; and, (2) The trend line of swell stress variation with time can be divided into three segments. The first segment is characterized by a quick increase of the swell force in the first 0?50 hours. The swell stress increases by 7.00×10-4?1.00×10-3 Mpa / hour. The second segment shows a slow increase of the swell stress during the 50?1730 hours. The swell force increases by 7.54×10-6?2.02×10-5Mpa / hour. The third segment is characterized by little variation in the swell stress after 1730 hours. In this segment, the average value of the swell stress measurements is 0.0719Mpa and the maximum value is 0.0729Mpa. It is suggested that the swell stress is mainly raised by water entering the pores among montmorillonite particles and the interstitial layers in individual montmorillonite crystals, leading to an increase in volume and manifested as a stress on the surrounding materials.

Jan 1, 2006

By J. Daniel Bryant

Deformation processing of rapidly solidified powder alloys presents a technical challenge different in several ways from the processing of ingot based alloys. The metastable phases formed during planar flow casting of aluminum alloy 8009 (FVS0812) must be safe-guarded from high temperature excursions during processing to avoid decomposition; this restriction prohibits liquid phase sintering of particles during consolidation. The development of strong particle-particle adhesion, therefore, relies on the imposition of very large strains during forming operations to insure sufficient mechanical meshing of the aluminum particles and break-up of prior particle oxide boundaries. These strains are generally much greater than those required for metallurgical transformations in ingot based alloys. In an attempt to quantify the deformation required to improve interparticle bonding, the finite element method (FEM) was employed. Preliminary results which predict the metal flow and strain distribution in several workpiece configurations are discussed. These predictions are then correlated to measurements made on experimental subscale forgings. Lastly, experimentally measured quantities which reflect the degree of interparticle bondingg are related back to FEM model predictions.

Jan 1, 1992

By Taegong Ryu

Nanosized tungsten powder was synthesized by the hydrogen reduction of ammonium paratungstate (APT) in thermal plasma. The effects of operating conditions on the product composition and particle size were investigated. The particle size of synthesized W powder was less than 30 nm in all cases tested. The sintering behavior of the synthesized powder (25 nm average size) was then investigated and compared with those of commercial W powder of 500 nm average size and W powder of 23 nm average size produced by milling the commercial powder. The sintering was done at 1400oC with various holding times. The hardness of the resulting compact from the synthesized W powder (315 VHN) was similar to that from the milled W powder (309 VHN), but the plasma-synthesized powder had a much lower tendency to form cracks. The compacts of both nanopowders were significantly harder than that of the commercial powder (192 VHN).

Jan 1, 2009

By Xiaodong Wang

A liquid metal flow generated by a magnetic field whose traveling direction is periodically reversed, the Reversed Traveling Magnetic Field (R-TMF) is studied. The modulation frequency ranges from 0 to 6 Hz. Ultrasonic Doppler velocimetry probes the generated fluid flow. Depending on the modulation frequency, a number of characteristic flow features are exhibited. A transition frequency (approximately 4 Hz) exists, above which the flow is no longer sensitive to the force modulation. Below this transition point, the amplitude of the velocity oscillation increases, and then below fm = 0.05 Hz, it saturates around a value close to that observed without any modulation. A theoretical model to obtain an analytical solution of electromagnetic force and to predict flow motion is developed, which is fairly in agreement with the experiments.

Jan 1, 2009

By R. E. Fanning

"IntroductionThe Aluminum industry is one of many materials industries which strive to make their material the preferred choice for large volume products. In some applications one material has a natural advantage over others, but more frequently several materials compete with one another, each providing one or more advantages and some trade-offs. Customers may design their product with several objectives such as minimum system cost, maximum customer appeal or maximum manufacturing flexibility, choosing materials which best combine cost and performance. In such markets it may become necessary for a material supplier to enhance the attractive features of the particular material to outweigh its disadvantages.It is difficult, if not impossible, to predict how various materials will evolve. Technological breakthrough, government regulations, material availability or sociological issues may redefine the balance between competing materials. In spite of some uncertainty regarding the competitive position of competing materials, there is little doubt that unrelenting pursuit of product quality improvement and cost reduction are essential to future viability of the aluminum industry. It is the intent of this paper to identify some areas where technological improvement would be beneficial. Thus this paper is a collection of briefly described problems that will hopefully stimulate the thoughts and research required for knowledge based solutions. Rolling ProcessA particular example is the beverage can industry where aluminum, steel, glass and plastics vie for a share of the m.arket. The high cost of aluminum relative to steel or glass requires minimizing the amount of metal per can. The high intrinsic value of aluminum has led to extensive recycling of cans although net metal cost is still higher than that of the competing materials. Intensive engineering of the beverage can led to improved design and better understanding of material requirements. These improvements permitted substantial reduction in sheet thickness over the past decade. The downward trend in metal thickness for beverage can sheet is shown in Figure 1."

Jan 1, 1988

By Guangqing Zhang

The paper presents results of a systematic study of synthesis of titanium oxycarbide and its chlorination. Titanium oxycarbide was produced by carbothermal reduction of titania in hydrogen, argon and helium. Formation of titanium oxycarbide started at 1200°C in all gases. The reduction was the fastest in hydrogen. Formation of titanium oxycarbide in hydrogen was close to completion in 120 min at 1300°C, 60 min at 1400°C and less than 30 min at 1500°C. Reduction in argon and helium progressed at a similar rate and reached 90-95% after 300 min at 1400-1500°C. The chlorination of titanium oxycarbide was ignited at 150-200°C. Chlorine partial pressure and gas flow rate strongly affected the chlorination rate. Chlorination of titanium oxycarbide produced with carbon to titania molar ratio 2.5 at 235-400°C was close to 100% in 30 min.

Jan 1, 2009

By Orhan Gokce Goksu

It has been shown that metallic tungsten powder can be obtained by electrochemical reduction of solid CaWO4 in molten CaCl2-NaCl eutectic mixture at 600oC. In this study, constant and pulse voltage electrolysis experiments were performed to optimize reduction kinetics and obtain information about the mechanism of above process. It was found that pulse voltage applications yield faster reduction rates when average voltage of pulse voltage application was the same as constant voltage application. In addition, analysis of the current vs. time graphs of constant and pulse voltage electrolysis studies showed that reduction occurs at potential differences higher than about 2.2 V between CaWO4 cathode and graphite rod anode.

Jan 1, 2010

By Jilai Xue

Oxygen gas bubbles generate on anode during Pb electro-deposition process in PbSiF6-H2SiF6 aqueous solutions at room temperature. Cell voltage varies as the bubbles formed on the anodes surface. The bubble layer on the anode makes a voltage drop that consumes energy in the Pb process, which can be reduced by applying ultrasound on the anode. The effects of ultrasound frequency and anodic current density were investigated with ultrasound on and off, alternatively during the Pb electrode-position process. The removing of the gas bubbles were recorded in association with a drop in the cell voltage. The cell voltage can be lowered by 4% - 6% with ultrasound, which has potential for energy saving in Pb production.

Jan 1, 2010

By Linli Wu

During the measurement of contact angle, a misty band was observed near the substrate. Hsien-Nan Ho and Shinn-Tyan Wu thought this was because the oxygen atoms on the interface migrate to the droplet surface to form an oxide band near the substrate. But from our experiments misty band appeared before the drop reach to the substrate. Theoretically speaking, the oxygen partial was the same everywhere in the vacuum furnace. So there was no condition to provide enough oxygen forming oxide. This appearance would be explained more reasonably with the optics principle. Most reflected light would be absorbed by the substrate and the light cannot reach the observation area, so the misty band formed.

Jan 1, 2006

By Joël P. T. Kapusta

Although Peirce-Smith converting remains the workhorse in matte converting, the copper and nickel industries are still confronted with production hindrances such as tuyere blockage, excessive refractory wear and limits in the oxygen enrichment levels of the blast air. The knowledge acquired on high-pressure gas injection technology as well as the invention of the concentric tuyere for steelmaking led to the development of the Air Liquide Shrouded Injector (ALSI) technology for copper and nickel converting. Following a technology demonstration in 1997-98 with four shrouded injectors installed in a Peirce-Smith converter, Falconbridge Limited implemented ALSI Technology on a commercial scale in May 1999 as an integral part of its new Slag Make Converter at Sudbury, Ontario, Canada. The paper presents the various aspects of commissioning ALSI Technology, as well as the operating changes and injector design modifications over the five years the shrouded injectors have been in operation.

Jan 1, 2005

By J. Samir

The objective of this study is to simulate the isothermal filling up of moulds by a RTM process when adopting CV/FEM and VOF method and when also taking into account the presence of obstacles coupled to the effect of the thickness and reinforcement layers variation. The codes developed intended to ensure an optimal positioning of the injection points and of the vents and also to determine optimal injection pressures, in order to minimize the cycle times. These codes use a mesh generator proper to the team, allowing a discretization of the domain in triangular unstructured elements, with the possibility of a local refinement and inserts inclusion.

Jan 1, 2009

By Tiebao Yang

In high pressure die casting processes, a die plays a critical role in removing heat from the molten metal during the cavity filling and solidification stages. Proper control of die temperature is essential for producing superior quality components and yielding high production rates. This paper proposes a local temperature control scheme for die thermal management based on a computerized intelligent real-time monitoring and control system (IRMCS). In this scheme, cooling water lines are controlled by a pump and solenoid valves. A controller is designed according to the law of die temperature fluctuations. The results obtained from the experiments carried out on a laboratory die casting process simulator indicate that the controller can limit the local die insert temperatures in a given band. Hence, the desired thermal pattern of the die insert becomes achievable.

Jan 1, 2006