By R. E. Somers

I. Introduction...........................604 1. Location, Topography, and Climate...............604 2. Scope of Work and Acknowledgments...............606 3. History and Mining......................606 11. General Geology.........................609 1. Introduction...........................609 2. Granite. :..........................610 3. Quartz Porphyry......................... 612 4. Monzonite........................... 614 5. Volcanic Breccia........,................ 618 6. Gravels............................. 619 111. Economic Geology......................... 619 1. Introduction........................... 619 2. Mineralogy........................... 619 3. Occurrence of the Ores...................... 622 4. Oxidation and Downward Enrichment............... 630 5. Rock Alteration........................639 6. Genesis of the Ores........................ 643 I. Introduction 1. Location, Topography, and Climate The Burro Mountains are located in the southwestern part of New Mexico, in Grant county. The group is made up of two distinct mountain masses, known as the Little Burros and the Big Burros, the former lying about 6 miles southwest of Silver City, and the latter about 9 miles farther in the same direction. They are separated by the valley of the Mangas River, a tributary of the Gila, and a stream only in name, except after a heavy downpour of rain. The Little Burros attain an elevation of 6,625 ft. above sea level, and the Big Burros 8,054 ft., with the surrounding country averaging about 6,000 ft. To the south of these mountains stretches the desert plain, while to the north are the more frequent elevations of the mountainous country.

Jan 1, 1916

By F. A. Crossley

The additions: o, Sn, Zr, Cb, Mo, and V were studied for their effects on the a/a + Ti3A1 boundary of Ti-A1 base ternary alloys. These additions were chosen because of their importance to commercial titanium alloy practice—oxygen as the major impurity (in terms of influence on mechanical properties) and the others as major alloying additions. The composition and temperature ranges of investigation varied according to the system as shown in Table I. The principal means of investigation was light-microscopy. The basis of the ternary studies was the recently determined titanium-rich end of the Ti-A1 system.' MATERIALS, METHODS, AND PROCEDURES Ingots were prepared in 15 g size for all alloys except those of the Ti-Al-Mo and Ti-A1-V systems which were prepared in 20 g size. These alloys were prepared from high-purity, electrolytically refined titanium obtained from the Bureau of Mines, Boulder City Metallurgical Laboratory, Boulder City, Col., and Chicago Development Corp., Riverdale, Md., for the 15 g and 20 g ingots, respectively. The alloying additions were obtained from commercial sources, and were at least of 99.9 pct purity, except the V-15 wt pct A1 master alloy for vanadium additions. This alloy was of 98.2 pct purity; the major impurities were 0.37 wt pct Fe and 0.38 wt pct Si. The ingots were prepared by multiple melting in a nonconsum-able-electrode arc furnace. The ingots were covered with Markal coating "CR-T22" (Markal Co., Chicago) to protect them from scaling. Markal coating is applied as a slurry of solids in a volatile carrier liquid. The coated article is air dried. Upon heating to the hot working temperature the coating fuses to form a glassy, protective film. The ingots were heated to 1000°C and rolled to 0.16 in. thickness, reheating after each pass. The glassy film was removed by sand blasting. Ten mils were removed from all surfaces by grinding and/or pickling (3 pct HF, 30 pct HN03, balance water). Grinding was always followed by pickling to remove traces of the grindmg medium. Hydrogen removal was accomplished by vacuum annealing at 1000°C for 2 hr to a final pressure of about 0.02 µ Hg. This was followed by annealing in evacuated Vycor bulbs (800°C, 2 hr, ice brine quenched (IBQ)) in order to maximize ductility. The materials were then lightly pickled and cold rolled to 0.12 in. thickness or cracking, whichever occurred first. After rolling, 1/2 by 1/4 in. specimens were cut for the equilibration anneals given in Table 11 and carried out as previously described.1 Final polishing of the specimens for metallographic examination was done by electrolytic means. Specimens were first examined without etching under bright field and polarized light illumination, for this is the only means of detecting the "two-phase" phenomenon.1,2 The term "two-phase syndrome" refers to Ti-A1 al-loys which appear on the bases of their chemical, phys-ical, and mechanical properties, to be two-phase, but are actually single phase and inhomogeneous in composition. Since processing and heat treatment of the alloys of the first group were completed before the two-phase syndrome was discovered, a number of the specimens were found to exhibit this phenomenon—80 pct of those of the Ti-Al-Zr system, 5 pct of those of the Ti-Al-Sn system, 30 pct of those of the Ti-Al-Zr system. The affected specimens were homogenized by heating above the ß transus temperature and quenching. The heat treatment and working schedules to accomplish this are given in Table 111. After rolling, specimens were pickled (3 pctHF, 30 pct HNO3 in water) to remove 1 to 2 mils from the

Jan 1, 1970

By George Krauss, Seth R. Thomas

One complete cycle, allstenite to martensite to aus-tenite, of Martensitic transformation was induced in a commercial 18 Cr-8 Ni stainless steel. Transmission electron microscopy showed that the reverse transfarmation, martensite to austenite, perpetuated the dense defect substructure of the martensite produced by the direct transformation, austenite to 'martensite, and reproduced the retained austenite matrix orientation. A general precipitation of lathlike M,,C, particles was noted to be present in, and is suggested as cause for, regions of martensite that Izad formed after a complete cycle of transformation. The habit plane of the precipitate particles was found to be within 5 a plane previously established as the habit of nitride precipitates of similar morphology in bcc iron. The direct transformation of austenite (y) to martensite (a) in metastable 300 series stainless steels has received considerable attention in the past,'-8 and the martensite product given special emphasis in recent years,9"*u but little information has been published about the reverse martensitic transformation during which bcc a martensite is converted to fcc y austenite."-" The reversal mechanism and the resulting crystallographic relationship between parent and product austenite are of fundamental concern. The reversal product, fully austenitic, and hereafter referred to as reversed austenite, exhibits a defect structure far different from its virgin counterpart. Some studies have been reported in which the structure of reversed austenite in iron nickel alloys is compared to annealed austenite with respect to austenite strengtheningM and Stabilization.' The martensite in these Fe-Ni alloys, however, shows a basic difference from that produced in stainless steels. Structurally, the Fe-Ni martensite is profusely twinned," while the (low-carbon) Fe-Cr-Ni martensite contains a high density of tangled dislocations and is apparently twin-free.I0 reediis" has recently shown in an Fe-16 Cr-12 Ni stainless alloy that this typical martensitic defect structure and the reverse transformation directly influence the structure of the reversal product. He found that much of the reversed austenite had returned to the orientation of the virgin austenite and that fine twins were formed in the austenite after the reverse transformation. This investigation was undertaken in order to describe as completely as possible the structural changes produced by a cycle of transformation in a typical 18-8 stainless steel. EXPERIMENTAL PROCEDURE The 301 stainless steel under investigation (17.44 Cr, 7.75 Ni, 0.80 Mn, 0.60 Si, 0.40 Mo, 0.40 Cu, 0.08 C, 0.03 N, bal Fe)was received as 0.060-in.-thick

Jan 1, 1968

By Frederick C. Hull

THE grain size of a metal or alloy is one of the most important factors determining its properties. In steels, for example, grain size affects hardenability, toughness and machinability; in brasses, grain size is related to hardness and deep-drawing quality. In the field of heat-resistant alloys, grain size has a marked effect on ductility, creep and endurance strength. In order to determine these effects, as well as to control the properties of materials, many accurate and rapid measurements of grain size must be made. This paper presents a new and improved method for the estimation of grain size. USUAL METHODS of EVALUATING GRAIN SIZE A frequently used method of estimating grain size is that of comparing the image of a polished and etched specimen on the ground-glass screen of a metallographic microscope with standard grain-size charts. Several types of standards are available for use with different classes of microstructures. Geometric Grids.-The Metals Handbook1 has a series of hexagonal grids ranging in size from ASTM No. I to 8. Idealized Grain Networks.-Idealized grain-boundary networks for ASTM grain sizes I to 8 are included in the American Society for Testing Materials Tentative Standard E19-39T. Standard Micrographs.- The Metals Handbook and ASTM Tentative Standard EI9-39T contain micrographs of hypoeutectoid and hypereutectoid steels ranging in grain size from No. I to 8. The grain size of annealed brass (diam¬eter of the average grain in millimeters) is obtained by comparison with 10 micrographs of varying grain size in ASTM Tentative Standard Es-39T. A handicap to accurate evaluation of grain size by this method is the fact that it is difficult to compare photographs in a dimly lighted room with the image on the ground-glass screen, or, if the general illumination is increased so that the printed standards may be clearly seen, the contrast of the image of the unknown is decreased. It is easier to estimate grain size by comparing a micrograph of the unknown with the grain-size standards. However, photographing every specimen on which the grain size is desired is too costly in time and materials to be practicable. For hardened steels, the Shepherd or Jernkontoret fracture grain-size standards are very accurate and useful, but this method obviously cannot be applied to ductile alloys such as brass, stainless steels and austenitic heat-resistant alloys. Jeffries' method for grain-size measurements consists of counting the number

Jan 1, 1947

By William J. Harris, Morris Cohen

INTRODUCTION THE recent application of lineal analysis1,2 to the austenite-martensite reaction has made possible a quantitative study of the kinetics of this transformation during rapid cooling. Martensite range curves can thus be constructed to portray the onset of the reaction at [M.] and its subsequent progress as a function of temperature down to and below the ambient. It now seems in order to investigate other aspects of the martensite transformation, using this quantitative method of approach. One of the least understood characteristics of the austenite-martensite reaction is that of stabilization which has been defined by Troiano and Greninger3 as "a lowering of [M.], resulting from aging, without change in chemical composition of the parent solid solution." In other words, if the hardening quench is arrested at a predetermined subcritical temperature (Th) for a sufficient period of time, more austenite may be retained at a given lower or reference temperature (Tr) than if the steel had been cooled directly and rapidly to Tr in the first place. For the purposes of the work at hand, the extent of stabilization produced by the isothermal treatment at Th, is measured explicitly in terms of the excess austenite [(S)] that exists in the steel at Tr, over and above the amount that is normally present after direct quenching to Tr. Tr is conveniently taken to be room temperature, but this choice is not essential and is sometimes undesirable. The holding temperature (Th) may be above or below [M], and still cause stabilization depending upon the chemistry of the austenite. Stabilization has been found to occur in the presence of bainite4 and of martensite5,6,7,8 as well as in the absence of either.9 The phenomenon of stabilization is not concerned with (and may even be obscured by) ferrite formation or any other type of phase change occurring at Th that alters the chemistry of the remaining austenite. Such a structural change would obviously influence the martensite transformation during subsequent cooling. Stabilization, however, is more subtle; it appears to manifest itself without detectable variation of the austenite composition, whether in the presence or absence of transformation products. There are relatively few direct references to stabilization in the literature. The stabilizing effect of room temperature aging and tempering on the subzero transformation of retained austenite has been clearly shown in plain carbon,6.8 low alloy 6.7.8 and high alloy tool steels.10,5 Starting with the as-hardened steel, the degree of stabilization increases with tempering time and temperature through

Jan 1, 1948

By P. W. Bridgman

DURING the war, the Navy undertook the construction, under my direction, of an experimental gun embodying features designed to lessen the cost and time of production. These experiments were initiated after representations as to their, desirability had been offered by myself, by the Naval Consulting Board, and by the National Research Council. The first drawings were made in June, 1917, and the experiment was completed in November, 1918. For the sake of clearness it will pay to recapitulate briefly the fundamental idea of gun construction. It is well known that if a hollow cylinder is subjected to internal fluid pressure, the maximum stress occurs in the inside layers, the outer parts carrying much less than their due share of the stress. This inequality of stress is more pronounced the thicker the walls of the cylinder. If such a cylinder is pushed to the elastic limit, failure in elasticity will take place long before the outer layers have reached the limit of their capacity. Economical use of the material would demand, however, that all parts of the cylinder reach the limits of their capacity simultaneously. This may be brought about, at least in cylinders of not too great thickness, by producing in. the inner layers an initial compression, and in the outer layers an initial tension. The effect of internal pressure is at, first to relieve the compression of the inside layers, while increasing the tension of the outside layers. If the initial stresses are properly distributed, all parts of the cylinder will reach their elastic limits simultaneously, thus giving a cylinder of maximum strength for its weight. In gun construction as hitherto practiced, this initial distribution of stress is produced either by winding the inner tube with wire, a common English practice, or by shrinking hoops over the inner tube, which has been the standard American practice. Either process is long and expensive, particularly with the larger guns, 12- or 14-in., which require

Jan 2, 1920

By D. Turnbull, J. H. Hollomon, J. C. Fisher

UNDERSTANDING of the diffusion problem has recently been furthered by the analysis of Birchenall and Mehl.1 They pursued the problem of the variation of the diffusion coefficient with composition for non-ideal solid solutions. Their analysis follows the tradition of Wagner,2 Jost,3 Dehlinger,4 and Darken,' who assumed the net flux of dif¬fusing material to be proportional to the gradient of a quantity related to free energy. The basic assumption in Birchenall and Mehl's formulation of the problem is that the net flux of diffusing material is proportional to a thermodynamic activity gradient. To estimate the applicability of the derived relations, they corrected the diffusion coefficients of carbon in austenite by utilizing Smith's' activity data for carbon, and the diffusion coefficients for zinc in copper with activity data computed from the vapor pressure measurements of Hargreaves.7 The corrected coefficients for carbon were virtually independent of carbon concentration. For the diffusion of zinc in copper a moderate variation of diffusion coefficient with concentration remained after the correction. The problem of diffusion can be formulated in another way than that used by Birchenall and Mehl. The method is that of chemical rate theory and has been used by Eyring and his coworkers8,9 as well as by Eyring and Zwolinski10 in a discussion to Birchenall and Mehl's paper. As yet the method has not been applied to substitutional solid solutions. On the basis of their assumptions, Eyring and Zwolinski derived a relation between the diffusion coefficient and activity that is identical with that of Dehlinger and Darken but which does not correct for the variation of the diffusion coefficient with concentration as well as does the relation derived by Birchenall and Mehl. It was thought that the theory of diffusion would be more complete if the inconsistency between the two analyses could be rationalized and if diffusion in substitutional alloys were analyzed on the basis of the concepts of the chemical rate theory. CHEMICAL RATE THEORY According to the theory of absolute reaction rates8 the reaction [A,+A2+ ... +.A;->X,+X2 +...+X; EqI] is viewed as taking place in two steps. First the reactants A1, A2, . . . A[i] combine to form an activated complex M with which they are in equilibrium; [A, + A2 + .. . + Ai = M. Eq 2] Second the activated complex decomposes to give the products X1, X2. . .. X[j]; [M->X1+X2+ ... +.X;. Eq3] It has been shown8 that the number of activated complexes decomposing per unit volume per unit time is given by the expression† [kT]

Jan 1, 1948

As described in the section on the Palabora twin crushers, the Palabora ore consists of two types: a carbonatite containing a low titanium magnetite, and a foskorite containing high titanium magnetite. As the Palabora pit was widened and deepened, more and more of the foskorite had to be mined. The 25,000 mt expansion of the Palabora plant which went into operation in early 1977 therefore takes its feed from the foskorite section of the orebody. For the expansion, a third 54 in. by 74 in. gyratory crusher was installed to crush feed for two 32 ft by 15 ft (9.75 by 4.6 m), 9000 hp (6710 kw) autogenous single -stage grinding mills. These units are located near the two existing primary crushers, and the ground ore is pumped 5277 ft (1640 m) to the expanded flotation plant by five stages of centrifugal pumps. The new gyratory is installed in a unique Figure-8 shaped enclosure with the crusher in the smaller 27 ft 11 in. (8. 5 m) diameter cylinder and the maintenance area in the 36 ft 1 in. (11 m) diameter cylinder. Cylinder walls are only 23.6 in. (600 mm) thick because their circular design permits all the concrete to be in compression. A rectangular dump pocket which sits on the smaller cylinder contains two manganese steel faced splitters to protect the crusher spider and countersunk water spray headers under the dumping positions for dust suppression. The dump pocket holds 330 st or 300 mt and is also lined with manganese steel. The crusher is mounted on a reinforced concrete diaphragm over the 363 st (400 mt) crushed ore pocket. In the back of the pocket is plastic pipe. Radioactive level control sources are lowered into this pipe from the crusher support floor. The pipe is protected by concrete covered with steel castings. Level control detectors are mounted on the front wall of the pocket. Liner plates on the crushed ore pocket walls are removed and in- stalled by the use of a circular monorail and trolley mounted on the pocket ceiling. The door in the front of the crushed ore pocket is hinged at the top rather than at the sides and is raised by an electric winch. For removal of the eccentric, rails are installed in the pocket and a unique hydraulically operated cart is moved under the eccentric. A platform is raised to receive the eccentric and lowered so that it may be removed. Crushed ore is removed from the pocket by a hydraulically powered, 8 ft

Jan 1, 1978

By W. L. Kerlie, J. H. Richards

The variation in hydrogen content of basic open-hearth steels during refining and the effect of changing from steam to air atomization were studied. The water content of the furnace atmosphere, the slag basicity, and the degree of oxidation of the slag-metal system largely control the hydrogen in the steel. SMALL amounts of hydrogen have an adverse effect on the ductility of steel and a wide range of hydrogen contents has an adverse effect on the internal soundness of both ferrous and nonferrous castings. This has been of major concern to the metal industry, both manufacturers and fabricators, for many years. As one of the results of continuing investigations of the hydrogen problem, much has been learned about methods of reducing the hydrogen content of liquid metals below the relatively high levels that are normally associated with such phenomena as rising ingots and excessive porosity in sand casting. However, it was not until a reliable and simple method for sampling and analyzing liquid metal was developed that much progress was possible in quantitatively evaluating the effect of steelmaking practice on hydrogen contents at levels below 6 to 8 ppm. Throughout all the work described in the following presentation the Geffner pintube technique was used to obtain samples of liquid metal1 * and the tin-fusion method, developed at Massachusetts Institute of Technology,2 was used to analyze the samples. Before attempting a systematic experimental program for minimizing the hydrogen content of open-hearth steels, it was necessary to determine the variation in hydrogen in the open-hearth bath during the normal processing of a heat. The logs of ten heats are illustrated in Figs. 1 through 7. The number at each point on the graphs refers to the number of pintube samples analyzed for hydrogen. An increase in the hydrogen content of the liquid metal during the early period of refining is apparent in all heats. There is evidence of a decrease in hydrogen later in the refining period, see Fig. 2, for example. Therefore, the existence of a maximum hydrogen content at some intermediate time during the refining period is anticipated. To test for the existence of a maximum, the data illustrated in Figs. 1 to 5 were grouped together so that they could be examined on a collectively comparable basis. The grouping was effected, as illustrated in Fig. 8, by superimposing Figs. 1 to 5 so that the apparent hydrogen maxima coincided at a fixed position, indicated by the zero on the time axis. Also, by vertical adjustment until the graphs appeared to the eye to be superimposed, the hydrogen scale was made to show the change in hydrogen content. That is, a standard amount was subtracted from the hydrogen values for each heat. Therefore, Fig. 8 represents a generalized presentation of the data and, for this reason, cannot be used to predict the actual hydrogen content of the bath during refining, but rather to show the probable rate of change in hydrogen during refining. Statistical examination of the grouped data in Fi.g. 8 shows that the apparent. increase and suhsequent decrease in hydrogen are real and confirms the existence of a maximum in general. The average increase In hydrogen during the early period of refining is between 0.8 and 1.3 ppm per hr, and the

Jan 1, 1958

By Ottey M. Bishop, William G. Peryam, Fred E. Johnson

THE Lepanto Consolidated Mining Company is the largest copper producer in the Philippines, and the only one that makes a concentrate valuable principally for its copper; also, it has the only productive copper mine situated at considerable distance from the sea, and is the only one in the islands operating its own smelter. The Lepanto mine is in the Municipal District of Mankayan, sub-province of Benguet, near the heart of the Mountain Province of Northern Luzon. It is 165 km. from its shipping point at San Fernando, Province of La Union, on the shore of the China Sea. Elevations at the property range from 3200 to 4500 ft. The climate is very mild; temperatures are seldom below 50° or above 80°F. Annual rainfall approaches 170 in. and is mainly confined to a rainy season lasting from May to October. The months from December to April, inclusive, are usually extremely dry. This climatic pecularity entails the problems of landslides on the roads during the rainy season and water shortage during the dry season. The Mountain Trail, an improved rocksurfaced toll road maintained by the Commonwealth Government, gives access to the property. The 105 km. over this road may be traveled in about 4 ½ hr. during the dry season. Very few sections of the road are straight for more than 100 meters, and about one third of it is a one-way road controlled by gates. All freight for the property is delivered by the Manila Railroad Company to Bauang, La Union, 45 km. west of Baguio and at sea level, where it is picked up by freight trucks and hauled via Baguio to Lepanto. Granulated matte is hauled in bulk from Lepanto in four-ton lots on freight trucks to the storage bins at San Fernando. Freight rates from Bauang to the property amount to [P]8.oo per ton, and from the property to San Fernando the rate is [P]16.00 per ton. The company pays the road toll, [P] 1.00 per truck, each way. THE CAMP The company maintains a modern camp, well separated from the mine and reduction plant. Comfortable and sanitary living quarters, water, and light, as well as free medical service are provided all employees. A hospital staffed by a doctor and two nurses takes care of all medical treatment. Considering recreational facilities of great importance, the company has provided two tennis courts, two basketball courts, and badminton courts for employees. Bowling alleys and a motion picture theater are operated by the company, the profits being expended for other recreational purposes. A moderate sized recreation hall serves for barrio dances, meetings,

Jan 1, 1942

By H. S. Bell

IT SEEMS unnecessary to dwell upon the advantages of the modern pipe still as compared with the older type of distillation equipment used by oil refiners. The relatively low installation cost, coupled with remarkable operating efficiencies of pipe stills, precludes the consideration of other types except in rare instances where some peculiarity of product or plant may have an influence. The question of the actual heat required to distil petroleum is quite involved. We have extensive data on the latent heats of the various hydrocarbons under different conditions of pressure. We also have information regarding the specific heats of various oils and the effect of temperature thereon. Because of the complexity of petroleum and of each fraction, it seems impossible to theoretically analyze the partial-pressure effect of the great number of hydrocarbons upon one another during distillation. If a distillation curve and percentage analysis of any crude or product are available, it is possible to construct a curve with ordinates representing per cent. distilled and B. t. u. per pound or per gallon, or other desired unit. To do so the crude is split into fractions, of 5 or 10 per cent. The boiling point and gravity of each fraction being determined, it is possible to evaluate the heat required. As each fraction is removed, the residue must be raised to a higher temperature and latent heat supplied for the successive fraction. As the calculations progress, the latent heats decrease while the specific heats increase. Such a curve is illustrated by Fig. 1 for a typical 39.9 B° North Texas crude.

Jan 1, 1928

By W. G. Sinclair

THE North Texas district presented in this paper includes the counties of Archer, Baylor, Clay, Cooke, Foard, Hardeman, Jack, Knox, Montague, Wichita, Wilbarger and Young. It corresponds with the Texas Railroad Commission's district No. 9. Table I conforms with the nomenclature of pools as designated by the Commission. Most of the oil and gas produced in this region, generally referred to as the Red River uplift, comes from the Pennsylvanian strata. In recent years, however, increasing amounts are being developed in both the Mississippian and Ordovician.

Jan 1, 1946

By R. S. Dean

THE first attempt to establish an equilibrium diagram of the lead-antimony series was made by Roland-Gosselin1 in 1896. This investigation classified the system as a purely eutectiferous one, with the eutectic at 12.5 per cent. antimony and 228° C. In the next year, Stead2 placed the eutectic temperature at 247° C. The error in temperature made by Roland-Gosselin, however, has been perpetuated in the literature with a remarkable degree of persistency; this value was accepted by Campbell (1902), and Ewen (1910),3 and will be found in the last edition of Desch's3 Metallography (1922). Gonterman's investigation, made in 1907, was the most complete one available at the time the present investigation was started. He concluded' that the system was a simple eutectiferous one and placed the eutectic at 13 per cent. antimony and 247°C. Other investigations by Tammann (1907),5 Garbow (1909),6 Rudolfi (1910),7 Loebe (1911),8 and Leroux (1913)9 added little, if any-thing, to Gonterman's diagram. A number of investigations have been made of physical properties of the alloys. The electrical conductivity of the series was studied by Matthiessen (1860)10 and by A. W. Smith (1921);" the thermoforce by Rudolfi (1910),12 and Pelabon (1923);13 the specific heat by Durrer

Jan 2, 1926

By Charles T. Holland

IN connection with the problems of bumps in coal mines, much has been written concerning the manner in which roof action and methods of mining enter [ ] into the pressure effects observed but little has been written upon the relationship between the physical properties of coal and associated rocks and the cause of bumps. The question of the strength of bituminous coal, of its elasticity, and the energy it can absorb and store has been neglected to a considerable extent in connection with this problem. STRENGTH OF COAL It is generally agreed that one of the necessary conditions for bumps is a strong [ ] coal.1 Therefore, since the strength of coal is an important factor, a study of this property should be made. Several investigators have conducted laboratory experiments upon the strength of coal, using small cubical or rectangular test pieces. An attempt will not be made to go into all of these investigations, but they are briefly summarized in Table I. Experiments of the U. S. Bureau of Mines8 and of Lawall and Holland (pp. 27 and 34 of ref. 9), however, indicate that regardless of whether the coal is a soft and weak semibituminous (Pocahontas No. 3) or a hard and strong bituminous (Stockton) coal, the maximum ultimate unit stress developed in laboratory tests is higher in small cubes than in larger cubes of the same coal.

Jan 1, 1942

By Murray F. Hawkins

Horner1 and van Everdingen8 ave shown that the pressure drop within the wellbore, as a result of having produced the well at a constant rate q for time t, where t is sufficiently large, is: van Everdingen observed that better agreement between theory and well performance can be obtained if, instead of assuming the permeability is kc everywhere about the well, it is assumed the permeability near the well-bore is substantially reduced as a result of drilling, completion and/or production practices. In order to account for the additional pressure drop he introduced the dimensionless quantity S, the skin effect factor, so that Eq. 1 becomes: Eq. 2 might have also been obtained as follows. Assume a zone of altered permeability k, exists about the well out to a radius r and beyond that the unaltered, external permeability k. The additional pressure drop required to overcome this skin of reduced permeability may be calculated with sufficient accuracy using the incompressible flow equation; for Browns-combe and Collins1 have shown almost no difference between compressible and incompressible steady-state flow, in the vicinity of the wellbore, and the small volume of fluid in the vicinity of the wellbore makes unsteady-state mechanics unnecessary. Then. The sign of this skin pressure drop will be positive or negative depending upon whether the altered permeability k, is smaller or larger, respectively, than the external permeability k... Adding the pressure drop of Eq. 3 to Eq. 1 to find the total pressure drop: Comparing Eq. 4 with Eq. 3 it is seen that the skin effect may be defined by: be determined from pressure build-up tests1,3,4,5,6,7,8 The average permeability kavg including the altered and external permeabilities, can be determined from PI tests, and may be defined approximately on the basis of steady-state flow, as was done by Thomas' in defining the damage factor, by: The productivity ratio is the ratio of the average to the external permeability, kavg/ke or This equation shows that the productivity ratio and the skin effect are not uniquely related, because of the uncertainty in the drainage radius, and also, in many instances, the wellbore radius. Fortunately, they enter in the logarithm. The curves of Fig. I are plots of Eq. 8 for values from 100 to 50,000. The points represent the skin effects and corresponding productivity ratios from a large number of well tests, taken from Fig. 15 of Ref. 5 or Fig. 13 of Ref. 9. While some of the data

Jan 1, 1957

By F. Lynwood Garrison

Except in the old Catalan forge, or its modifications, attempts to make iron and steel directly from ore in a practical and economical manner have failed so frequently and completely that such schemes are looked upon with justifiable distrust. Without exception, all have failed from one cause or another, although in some instances every indication of a practical success was manifest in the beginning. It is, therefore, necessary to carefully examine and consider every detail affecting the process, or more properly, furnace, under consideration. This I have done to the best of my ability during a long visit to Russia last summer, and after satisfactorily observing the practical success of the furnace in the iron works of Count Stroganoff at Dobriansky in the Government of Perm, I decided to investigate as completely as possible the history of similar furnaces in Finland and Russia. These data, sifted and verified with the greatest possible care, form the substance of the present paper.* An illustration on page 321 of Percy's Iron and Steel shows the old type of Osmundssmide or harkugnar, which has been in use in Northern Europe since pagan times. Fig. 1 shows a furnace of this kind. It should, perhaps, more properly be called a high-bloomary furnace or forge, the Swedish word hark meaning bloom or loupe. It was with this type of furnace that Mr. Husgafvel began his experiments at Porsaskoski in 1875. Attempts to obtain better results with larger furnaces of this type were failures, as every bloom or loupe obtained necessitated blowing out the furnace with a consequent large waste of fuel. A larger furnace of course increased this waste with no corresponding advantage. A movable hearth of threeeighth inch iron, lined with a mixture of clay, quartz and lime, was next tried, but in consequence of the frequent repairs of this lining,

Jan 1, 1888

By J. D. Hanawalt, W. H. Gross

Magnesium has long been known as the lightest of our engineering metals. This metal, silvery white in color, has a specific gravity of only 1.74. Aluminum, the next lightest structural metal, is 1 ½ times heavier; zinc is 4 times heavier; iron and steel are 4 ½ times heavier; and copper and nickel are 5 times heavier. Magnesium does not occur in the free state but is very abundant in nature, constituting 2.5 pct of the earth's crust in the form of various ores. It is the third most abundant structural metal, being exceeded only by iron and aluminum. Magnesium is unique, however, in that in the form of magnesium chloride it also exists in the oceans. Sea water is the source most widely used for production in the United States but magnesium is also commercially produced from magnesite, dolomite, and other ores as well as from certain inland brines. The vast quantity of magnesium existing in the waters of the oceans can be visualized when it is realized that the removal of one hundred million tons per year (the approximate annual steel production in the United States) for a million years would reduce the magnesium content of sea water only from 0.13 to 0.12 pct, providing no more magnesium had washed into the sea in the meantime. Not only is magnesium potentially very abundant but it is in addition a very versatile metal and can be shaped and worked by practically all methods known to the art of metal working. It can be cast by sand, die, and the various permanent-mold methods;

Jan 1, 1953

By J. L. Gillson

The big mass of anorthosite in the Lake Sanford district and the bodies of titaniferous magnetite that occur in a small area near the south margin of the mass have been described repeatedly, and the puzzling problems of the genesis of the rocks and ores have stimulated the deductive reasoning of geologists for a hundred years. Some of these men have taken a leading part in describing the anorthosite rock and forming hypotheses concerning its origin; some have contributed most to the study of the ore deposits; and some have made classical Studies introducing a basic approach to the problems of the anorthosite rock and genesis of the titaniferous magnetites. Much of the writing on the problems of rock and ore genesis has been based on physical-chemical reasoning rather than on field and microscope observations of the rocks and ores. Most of these geologists conclude that the anorthosite was formed by true magmatic crystallization, involving previous settling or squeezing out of ferromagnesian minerals from the parent magma. The associated gabbro is a separate segregation or later intrusion, and the lighter colored and finer grained facies of the anorthosite is either a chilled border zone of the anorthosite or the result of granulation by crushing of the coarse, dark blue rock of the main mass. This blue rock, called the Marcy type, is named after the highest peak in the range. The finer grained and lighter colored rock is called the Whiteface, after another mountain appropriately named for a cliff colored by this facies of the anorthosite.

Mar 1, 1956

Jan 1, 1925

By D. K. Crampton

The object of this work was to obtain and correlate information on effect of internal stress in variously drawn tubes on several properties. Also, a simple approximate method of comparing types of stress distribution in such variously drawn tubes was sought. There is also included some work on comparison of single and polycrystalline materials and effect of different types of operation and preferred orientation. Preparation of Material A series of tubes was drawn to study the effect of the type and degree of final reduction on various physical properties and the approximate distribution of stress intensity across the tube wall. The material used all came from a single heat of 70-30 brass melted in a regular production Ajax-Wyatt induction furnace. The analysis of the metal as cast was: copper, 70.36 per cent; lead, 0.04; iron, 0.02; zinc, balance. The material was cast in "shells" with 4 in. outside diameter and in. wall thickness. It was drawn part way down according to the usual standard mill schedule and then by suitable individual schedules to finish by a variety of types and degrees of drawing to the same final cases in every instance; namely, 0.750 in. outside diameter by 0.080 in. wall thickness. The exact final draws, together with the percentage area reductions, diameter reductions and gage reductions are given in Table 1. In fabricating these tubes, rather unusual precautions were observed to insure the elimination of ail variables not under immediate study. All intermediate anneals were carried out at about 1200" F. down to the so-called "cut-in size"; namely, 17/16 by 3/16 in. From this point on, all anneals were made at from 1050' to 1100" F. The greatest care was used all through to have the tubes as free from minor surface defects as possible. When such defects were visible on intermediate sizes they were carefully filed out. On the final draw to 3/4-in diameter the die was aligned with the greatest possible precision in order to insure as straight a tube as possible

Jan 1, 1933