Search Documents

By A. P. Pavia

Investigation on profitable ways to recover significant quantities of silver remaining dissolved in highly concentrated chloride solutions frequently pass through the development of solvent extraction (SX) routes. In this work, the general pathways involving Ag(I) extraction by dibutylthiourea (DBT) or tetraethylthiuram disulfide (disulfiram, DSF), from concentrated acidic chloride solutions, are investigated. With this purpose, the dependence of Ag(I) distribution coefficient on ligand and chloride concentrations has been analysed. Furthermore, in order to check whether there is some protonation at any site of DBT or DSF after contact with adequate chloride phases, lH NMR has also been used. The collected spectroscopic data suggest that anionic Ag(I) extraction reactions are not likely to occur. Based on the overall results achieved, proposals for the most probable Ag(I) extraction reactions are made.

Jan 1, 2001

By Rodney J. Ishak

The reduction of Mn3O4 to MnO has been investigated in a thermobalance apparatus. The charge was composed of manganese ore (decomposed by heating/calcination or pre-reduction to mainly Mn304) and coke. The material was charged to a crucible, which was suspended in the balance. CO-gas was distributed through a grid in the bottom of the crucible. Two sizes of ores were used; 2.4-4.8 mm and 6.7-9.5 mm. Coke particles were in the size range 4.8-6.7 mm. Experiments were conducted in the 900-1100°C temperature range. The composition of the product gas was monitored continuously. External mass transport between bulk gas and particle surface does not seem to limit the rate of reduction. Assuming that both diffusion through product layer and chemical reaction at the interface between MnO and Mn304 are rate controlling, the data was tried both in a shrinking core model and in a grain model using regression. The grain model gives the best physical description of the process, because the reactant is in fact a porous medium. With this model the effective diffusivity was calculated to be in the 1.5-6.10-5 m2/s range. The pore size was mainly between 0.1 and 10 um.

Jan 1, 2003

By Flávia Paulucci Cianga Silvas, Otávio da Fonseca Martins Gomes, Viviane Tavares de Moraes, Denise Crocce Romano Espinosa, Jorge Alberto Soares Tenorio, Guilherme Apostólico Bortolini, Stoyan Gaydardzhiev

"Printed circuit boards (PCB) are particularly problematic to recycle because of the heterogeneous mix of organic materials, metals, and glass fiber. PCBs are found in almost every electroelectronic equipment and their recycling process involves a pre-treatment to separate the products which contain targeted metals. In this work, a physical processing involving sequential shredding and hanuner milling were used to obtain a comminuted sample from scrap printers PCBs. The thus prepared sample was analyzed for particle size distribution and by optical microscopy as well was subjected to pyrolysis, leachabilty and chemical composition determination by XRF. The metals concentration was determined by ICP and AAS. The PCBs have been also analyzed by SEM-EDS (micro-analysis and X-ray mapping). The results show that the studied PCBs are lead free, multilayer with 4 copper layers, have 45% of metals and the copper is present in significantly higher concentration than the rest of the metals.IntroductionThe global generation of e-waste (electrical and electronic equipment waste - WEEEs) grows at a rate of about 40 millions of tons per year [ l].Among this e-waste there are PCBs that are present in almost all electronic equipment. Their composition is heterogeneous and varies according to several factors, including: kind of EEE, when and where it was produced, fabrication technology [2], etc. In printers, the PCBs represent about 6.6- 8 wt.% [3].The PCBs treatment may include physical, pyrometallurgical, hydrometallurgical, ectrometallurgical and more recently bio-hydrometallurgical process. Normally there is a combination between these processes [2, 4, 5, 6, 7, 8, 9, 10].The diversity between the different PCBs composition complicates the recycling process since the composition of metal and others materials can vary according to the models. So characterization is an indispensable step before any processing of PCB to begin. Owing to the above said, the main goal of this work has been set to characterize representative samples of PCBs from printers through physical, chemical and microstructural analyses."

Jan 1, 2014

By B. L. Chulu

In the carbothermic reduction of lead sulfate to produce lead, the inclusion of soda ash (Na,CO,) in the charge provides for the control of sulfur dioxide in the effluent gas. An important mechanism in the process appears to be the carbothermic reduction of the sodium carbonate whereby sodium gas and carbon monoxide are produced. These intermediates then participate in the reduction of the lead sulfate to produce lead metal and stable sulfur species in the molten slag phase. In addition, there is some evidence that the presence of lead metal in the charge may also serve to increase the lead recovery in the process. These aspects were investigated by conducting laboratory-scale smelting tests with small charges (;3g), at 1173°K(9000C). Recovery did not exceed 74w% and the role of incipient lead metal in the charge could not be clearly assessed.

Jan 1, 1993

By G. A. Bala

As part of ongoing research to define mechanisms of microbial enhanced oil recovery (MEOR), this work describes the activity of Bacillus l1chen1formis JF-2 (ATCC 39307) Mosurfactant against crude oils with varying compositions. Surfactant based MEOR improves oil recovery by lowering the oil/brine interfactal tension (IFT) therefore permitting oil to be displaced or solub1lized into the aqueous phase.? MEOR is an Enhanced Oil Recovery (EOR) process which allows for the introduction of chemical and miscible fluids, in the form of microbial metabolic end-products, through the injection of microorganisms into the reservoir or stimulation of indigenous reservoir microbial populations. These microorganisms represent a replenishable in situ source of acid, gas, biopolymer, solvent, or surfactant products which can be. supported and manipulated by the addition of simple and inexpensive nutrients to enhance the recovery of oil. Microbially mediated surfactant production represents one mechanism of MEOR. Bacillus licheniformis JF-2. has been used in a mode 1 MEOR system based on Berea sandstone cores (permeabilly .85 to 400 md) to examine surfactant based MEOR of medium to heavy crude oils (API gravity 38.1° to 17.5°). Enhanced oil recovery was achieved with all oils tested using either cell free culture supernatants or microbial suspensions as injectants with no detrimental effect to the oil. Spatial distribution of cells following mf?crobtal flooding was analyzed with scanning electron microscopy. Data indkate complete distribution of cells with a predominance of organisms located distal to the point of injection. There appears to be no sign:if1cant recovery trend with respect to oil composition.. The biosurfactant produced by Bacillus lichen1form1s JF-2 lowers the interfacial tension of all oils tested equally well.

Jan 1, 1991

By Xia Hong-ying, Peng Jin-hui, Zheng Zhao-qiang, Zhang Li-bo

"Preparation of activated carbon from the walnut shell by microwave assisted steam activation was studied. Influences of the three parameters, activation temperature, activation duration and steam flow rate on the adsorption capacity and yield of walnut shell activated carbon(WSAC) were investigated,optimization process was obtained by the Response Surface Methodology (RSM). The optimum preparation conditions were as follows: activation temperature of 980°C, activation duration of 41 min and steam flow rate of 1.66 ml/min. The optimum conditions resulted in an activation carbon with an iodine number of 1025 mg/g and a yield of 52.17%, while the BET surface area, total pore volume and average pore diameter of WSAC were 1328m2/g, 0.72ml/g and 2.2nm respectively. The study supported the potentiality of comprehensive utilization ofWalnut shell and the benefits of the microwave heating.IntroductionActivated carbons are one of the most important adsorbent materials in modern society because of its abundantly developed pore structure, strong adsorption ability, high surface area and thermo stability. They have extensive application in many industries fields which include gas purification [1], catalyst supports [2] and other pollutants [3]. However, in recent years, the industrial production of activated carbon is facing the problem of raw material scarcity and high cost, which limit to be widely used. Therefore, the selection of an appropriate precursor plays an important role and it has become hot sport to seek cheap raw material to lower preparation cost. As a kind of reproducible resource, the waste from agriculture and forestry is a high-grade raw material for preparing activated carbon due to is high carbon content, such as palm shell [4], rice hull [5], and coconut shell [6]. At present Walnut shell is widely accepted to be a renewable source of biomass. According to statistics, there is more than 1000,000 tonnes of walnut shells are produced in China annually [7]. As a good precursor for activated carbon production, Walnut shell is a major agricultural waste, to make better use of the cheap and abundant agricultural waste, it is proposed for activated carbon production."

Jan 1, 2014

By A. V. Tarasov

The proposed process is based on creating a controlled frothed layer of molten slag, in which fine particles of carbonaceous reductant and raw material to be processed are mixed with emulsified iron. Frothing of the slag layer without external blowing occurs as a result of intensive evolution of gaseous reduction products. The froth reaction process is maintained due to the heat of an electric arc in the slag layer. When the metal bath is heated by the arc to 1400- 1 500°C, the low temperature of the slag surface of about 1200-1 300°C is maintained due to low thermal conductivity of slag froth preventing heat loss. In order to maintain the required slag froth level and control the process temperature, air tuyeres are installed above the slag bath; blowing air serves also for oxidation of zinc in fumes and for its transportation. High adsorption and thermal insulating properties of slag froth ensure virtually complete elimination of dust and mist entrainment along with low heat losses. The main macrokinetic regularities of the carbon thermal reduction of zinc-containing slag melts have been studied under frothing conditions. The mechanism of formation of gas-slag emulsion has been identified under the conditions of reaction [C]+[O]=CO occurring locally at the slag-metal interface. It has been demonstrated that under the froth reduction conditions the zinc removal rate from the melt increases on the average by 3 to 5 times. Based on the physical and chemical data obtained, basic principles of the dezincing technology have been developed for different intermediate oxide iron-containing products produced in the process of ferrous and non-ferrous metals production.

Jan 1, 2002

By I. Gaballah

Jarosite contains up to 15 % of heavy metal compounds 'HMC'. The current waste disposal methods will not be allowed in the near future due to new environmental regulations and pollution risks. For these reasons, thermal treatments of raw or decomposed jarosite, in controlled atmospheres, were investigated. The aim of these treatments is to decontaminate the jarosite and/ or to recover the HMC for recycling. According to physico-chemical characteristics of the samples, the thermal treatments in controlled atmospheres N2, CO+N2 and C12+air lead to the extraction rate that vary from 93 to 98 %. Heavy metal compounds were separated by cooling the gaseous phase. The treatments' residue was almost free from HMC. Between 700 "C and 800 "C, the chlorinating treatment was successful of eliminating more than 97 % of HMC contained in four different samples.

Jan 1, 1999

A novel pressure leaching process for platinum group metal (PGM) feedstocks is described. The process is particularly well suited for treatment of ores or concentrates that are too low grade for economic processing by the conventional smelting/leaching process. Operating conditions have been identified under which gold, the PGM's and the base metals dissolve simultaneously in a pressure leaching autoclave. The product of this leaching process can then be treated by one of several flowsheets, of which the preferred will likely involve solid/liquid separation, followed by precipitation (or adsorption on activated carbon) of gold and the PGM's, followed by copper solvent extraction/electrowinning. Depending on the concentrations of nickel and cobalt, the copper raffinate would either be partially recycled to the autoclave to allow NilCo concentrations to build up, or it would proceed directly to a Ni/Co refinery. This paper deals with the pressure leaching process and the recovery of gold and the PGM's from the pressure leach product.

Jan 1, 2000

By John L. Watson

The dewatering of steel industry waste sludges prior to discard or recycling often presents significant problems due to the fineness of the sludge particles, which may blind the filter medium and/or produce a cake with limited porosity, Several steel plant wastes, such as sludges from BOF and EAF gas cleaning operations exhibit not only a very fine particle size, but also some degree of magnetic character, A novel process has been developed to utilize the magnetic character of such sludges to enhance dewatering through a multi-force operation involving magnetic, chemical and vacuum forces, The process consists essentially of undertaking vacuum filtration of a flocculated sludge in a magnetic field, This is achieved by installing a permanent magnetic in a fixed position on the axis of a vacuum drum filter, thus effecting filtration of magnetic and non- magnetic particles, bound together in flocs, in a magnetic field, Previous tests using a modified laboratory vacuum drum filter treating artificial (magnetite) and industry waste (BF sludge) feeds have demonstrated that filtration capacity may be enhanced significantly with increases of up to 3000/0, An explanation of the mechanisms associated with the enhanced filtration was not obvious, and this research was undertaken to permit the cake formation in the magnetic field to be monitored to provide an insight into the manner in which particles agglomerate to form the cake. These tests revealed that the magnetic field caused magnetic particles to be aligned perpendicular to the filter surface and to form channels through which filtrate could freely pass thus increasing capacity, The effects of various magnetic fields and field strengths on the filtration process were also investigated. A simple computer model was constructed to demonstrate the proposed theory of multi-force dewatering, The model output graphically illustrated the suggested mechanism and confirmed the enhanced capacity of the novel dewatering process,

Jan 1, 1996

By R. A. Roberti

Most copper refineries use conventional wheel systems to cast anodes. over a period of time the copper moulds that are used become warped and cracks develop. To control mould warpage, the mould's are either rejected after a certain warpage is reached, or the shape is restored by mechanical means. The cracks, unless they are very severe, are repaired by a peening process. Even with regular maintenance to control warpage and cracks, the moulds have a limited useful life. If warpage and cracks are not controlled, anode quality deteriorates and tankhouse operations are seriously affected. -An intensive study was initiated to develop means of controlling mould warpage which culminated in the d?evelopment of technology to control mould warpage to within ±1. 5 mm, and at the same time effectively contr0l: cracking and significantly increase the mould life-. The warpage control has been achieved by using a unique mould design. Mould cavities are present on both sides of the mould and periodic inverting controls the wa-rpage in the cavities. The mould casting procedure has been developed and all production wheels have been converted to the new mould design. The performance characteristics of these moulds will be detailed. 21

Jan 1, 1987

By Don Ibana

Supported by the Minerals Council of Australia (MCA) through the Minerals Tertiary Education Council (MTEC), three Australian universities–Curtin University, Murdoch University and the University of Queensland–have formed the Metallurgical Education Partnership (MEP) to jointly develop and deliver an engineering design capstone unit–Metallurgical Process and Plant Design–in their respective undergraduate programs in extractive metallurgy, in order to enhance the students’ educational experience. A unique feature of the program is the close interaction of the students in all three universities and a significant involvement of industry professionals. Now in its sixth year, it is clear that this unit is achieving its objectives

Jan 1, 2014

By Hong Yong Sohn, Miguel Olivas-Martinez

"Different approaches are used for calculating the ‘energy requirement’ of a process. The determination of energy requirement becomes confusing for a process in which a fuel is also a reactant. The key issue is which heat of chemical reaction should be included in the ‘energy requirement’ value. We will use the example of ironmaking processes to illustrate the problem. The different approaches essentially boil down to the question: does one include the combustion heat of the reductant used in the reduction reaction or just the heat of the reduction reaction? Depending on the viewpoint, either approach can be accepted; it is a matter of convention. There is a need, however, to select a standard approach because the absolute value of ‘energy requirement’ of a process depends on the choice. The energy requirement of a novel flash ironmaking process will be compared with that of an average blast furnace operation.IntroductionDifferent approaches are used for performing energy balance calculations and perhaps more significantly in presenting the ‘energy requirement’ of a process. The question becomes more involved for a process in which one or more reactants are also used to generate the process heat by combustion. Often the key issue is which heat of chemical reaction to include in presenting the ‘energy requirement’ of the process.It is worthwhile to note at the outset that the difference in energy requirements between different processes for converting similar raw materials to the same desired product is largely unaffected by the choice of chemical reactions to be included. However, the absolute value presented as the ‘energy requirement’ of a process can be different by a large amount depending on the approach. We use the example of ironmaking processes to illustrate the problem. In these processes, as currently practiced or under development, carbon and/or hydrocarbons (including hydrogen) are used as the fuel as well as the reactant for reducing the iron oxide mineral.The different approaches in this case essentially boil down to the following question: does one include the combustion heat of the reductant used in the reduction reaction or treat the reductant portion as just a reactant? Depending on the viewpoint, either approach can be considered acceptable. It is a matter of convention. There is a need, however, to select a standard approach because the absolute value of ‘energy requirement’ of an ironmaking process (e.g., the currently dominant blast furnace process) depends on such a choice. It is particularly important to clearly state the specific approach used when the energy requirement of ironmaking is compared with those of other industrial processes such as petrochemicals production."

Jan 1, 2014

By E. Fregeau-Wu

The mineralogy and grain size distribution of phases in a steelmaking slag and experimental products from the heating of the slag under various conditions were determined to explore the possibility of recycling of the iron and manganese to the blast furnace. The steelmaking slags consisted of three major phases: dicalcium silicate, dicalcium ferrite, and Mg-Mn-wustite. Most of the phosphorus was contained in the dicalcium silicate and to lesser extent in the dicalcium ferrite. Due to the fine grain size of the dicalcium silicate, grinding and magnetic separation required pretreatment to increase the grain size and hence the liberation. Experiments on a steelmaking slag were conducted by heating the slag to 1633-1748°K( and slow-cooling in an inert atmosphere at various rates with or without the addition of fluorspar (CaF2) as a flux. Grain size distribution analyses of the starting material and the slow-cooled products were performed using the SEM-IPP area scan method and the QEM*SEM linear scan method. Comparable and reproducible results were obtained on the same sample using both methods. A size versus volume percent plot showed the increased grain growth most effectively. Examples of the grain size distributions obtained were used to show that a higher soaking temperature prior to slow-cooling, a slower cooling rate, and the addition of fluorspar to the slag promoted grain growth.

Jan 1, 1989

By Giuseppe Bonifazi

Minerographic and petrochemical research was carried out on crude ore samples from the complex polymetallic Zn-Cu-Pb sulfide ores of , Sotiel in Huelva province west of Seville, Spain. A computerized image analysis system was used to define the structural and textural characteristics of the ore to obtain information on the degree of liberation of the different minerals (i.e. pyrite, sphalerite, galena, chalcopyrite). Techniques of digital multispectral image processing of reflected light microscopy images were used. Particular structures were identified by means of mineral associations and numerically quantified to obtain useful information for designing beneficiation processes.

Jan 1, 1991

By A. M. T. S. Bandara

The solubility of rare earth (RE) salts in aqueous solutions depends on many factors including the type of cations and anions in solution, their concentrations, temperature and the type of solid precipitated. Experiments were conducted using anhydrous La2(SO4)3 and Ce2(SO4)3⋅8H2O as solids and lanthanum(III) perchlorate prepared by dissolving La2O3 in HClO4 solutions as RE-sources. Solutions of H2SO4, H3PO4 and their mixtures in the presence or absence of Na+, Ca2+, Fe(III) or Al(III) as perchlorates served as test solutions. Saturated solutions and precipitated solids were assayed and characterized using standard techniques to show that the La(III) and Ce(III) ions precipitate as hydrated sulphates, phosphates or double salts with sodium, depending upon the solution composition. The change in solubility of RE-salts with solution composition and temperature is the result of the composite effect of changes in solubility products (pKSP) of salts, pKa of acids and other equilibrium constants for ion-association.

By Georgios N. Anastassakis, Nickolaos Georgiou

"Soil contamination by oil as well as by other organic pollutants poses a major problem to the environment. Various methods have been used to remove organic contaminants from soil, such as: biological, thermal, chemical and physical. Methods based on Mineral Processing principles have also been used (cyclone separation, gravimetric separation, attritioning and washing). This paper studies the possibility to remove a rich-in-contaminant soil fraction by applying flotation. The contaminated soil was artificially prepared by mixing soil with diesel fuel. Sodium dodecylsulfate (SDS) and a tertiary amine (TA) were used as collectors. The effect of collector quantity added and conditioning time was studied. The results showed that the removal of a rich-in-contaminant soil is feasible while a clean fraction is also obtained. In several cases, the removal of oil-contaminated soil approaches or reaches 100%. Introduction Human activities are intimately associated with environmental pollution to the air, water and soil, as well. Soil pollution from inorganic and organic compounds is of equal importance with that of air and water, as it results in soil degradation and its concomitant problems with respect to meeting the human needs (house building, agriculture etc). Heavy metals along with their compounds are encountered among the most usual soil inorganic pollutants. The corresponding organic soil-pollutants are oil, oil-derivatives, pesticides, various aromatic (benzene, phenols, cresols, toluene etc) and poly-aromatic (naphthalene, anthracene etc) hydrocarbons, as well as various other organic compounds (pyridine, cyclo-hexane etc). Oil remains the basic energy source sharing 38% of the global needs, being followed by coal and gas with a share of 26 and 21% correspondingly [1]. The entire activities related with oil production, transport and consumption promote pollution in the air, water and soil. Consequently, soil pollution from oil is favoured at refineries, storage sites (due to possible pipe and tank leakage, tank cleaning works, loading and transportation) and, finally, at the oil-selling sites. Oil (or diesel-oil) fuel is a mixture of hydrocarbons, with 10-20 carbon atoms in the chain of each. It is mainly composed of paraffins, naphthenes and various aromatic compounds. In general, oil is composed of 20-30% in aromatic compounds, 5-6% in naphthenes and the rest is paraffins [1]."

Jan 1, 2008

By R. Elliott, H. Bayati

"Effect of time and temperature on microstructure and mechanical properties of an austempered ductile iron, ADI, of composition 3.6%C, 2.6%Si, 0.4%Cu, 0.2%Mn are reported. Xray analysis and. microstructural observations indicate that lowering the working temperature, aging temperature, increases the lifetime of ADI significantly. Results show· that lowering the aging temperature increases the strength and reduces the ductility of ADI. DSC traces for ADI austempered at 340°C are presented. Comparison of the DSC analysis and kinetic measurements demonstrates that the DSC traces can be· used to predict the life time of ADI successfully.IntroductionAustempered ductile iron, ADI, is one of the most significant developments in cast iron technology over the past two decades. Outstanding properties of high yield, ultimate strength, ductility, fatigue and wear· resistance make ADI suitable for a range of applications including gears, connecting rods, crankshafts and agriculture machine components. The austempering reaction in cast iron occurs in two stages, Fig. I, in contrast to the single stage reaction in steel. In stage I the relatively low carbon austenite produced during austenitising transforms into ferritic plates and high carbon austenite, a metastable structure called·ausferrite. The high carbon ailstenite and supersaturated ferrite produced in stage I decompose into ferrite and carbide in stage II: to form a structure similar to the bainitic structure in steel. This behaviour exposes a well-defined processing window, t1 - t2, over which the maximum amount of ausferrite is produced, Figure 1. Whereas the bainitic structure determines the properties of austempered steel, ADI properties are mainly affected by volume fraction of retained austenite (VRA), austenite carbon content (ACC), unreacted or martensite volume fraction (UA V), compositiori and amount of carbides, and morphology of ferritic plates[l,2]. Due to the detrimental .effect of martensite and carbides on properties of ADI, an ideal structure of ADI consists only of ausferrite [l,2]. Thus, it is common to determine the processing window for each austempering treatment in order to identify the optimized austempering time. Decomposition of austenite (stage II) signals the end of the life time for an ADI component, therefore, the aging behaviour of ADI at different working conditions can be studied by determining the t2."

Jan 1, 2000

By Jonkion M. Font

An expression for the distribution ratio of arsenic between slag and copper matte or liquid copper was developed by both, an extension of the Reddy-Blander moderl for deriving a priori the arsenic capacity, and by a relationship between the arsenic capacity and the arsenic distribution ratio. In this study, the a priori arsenic capacities in the FeO-SiO2, CaO-SiO2,MgO-SiO2, FeO-CaO-SiO2, FeO1.5-CuO0.5-MgO-SiO2, FeO-FeO1.5-CuO0.5-CaO-Mgo and FeO-FeO1.5-CuO0.5-CaO-Mgo-SiO2, slags were calculated at 1573 K. The a priori arsenic distribution ratio between the FeO-FeO1.5-CuO0.5-CaO-MgO-SiO2 slag and copper matte mn (Lx, )' and between the FeO-FeO1.5-SiO2 or FeO-FeO1.5-CuO0.5*-CaO-Mgo slag and liquid copper (Ls/cua) were calculated. The model calculated data are found to be in good agreement with the reported experimental data. The availability of reliable thermodynamic data for slag components and impurities in the slag-matte- metal system is essential for the accurate prediction of impurity capacities and distribution ratio data. The arsenic distribution ratio model developed here, can be extended for predication in multi-componet slags and mattes or liquid metal, and thereby may lead to the development of new slag systems for the efficient removal of arsenic in the copper smelting, converting and refining processes,

Jan 1, 2003

By S. A. Platias

Large amounts of dunile tailings can be recycled for olivine produdion from the existing beneficiation adivity of chromite ore in northern Greece. This olivine production aims at the preparation of a material suitable for the substitution of the environmental hazardous quartz sand in the foundries of Europe In smelting of chromite ore the losses that occur ore usually of the order of 6-8% Cr that report in the slag. Most of this is in the form of oxides that cannot be recovered, but usually 30-35% is in the form of FeCr alloy that can be recovered by gravity methods. About 90% of the produced slag is sold for road construdion after crushing to a desired grain size. Finally, recycling of chromites sludges from the ferrochrome produdion plant, through the preparation of pellets, improved the total chromite yield by 2%.

Jan 1, 1996