By A. J. Ardell, O. D. Sherby

The elevated-temperature steady-state creep behavior of polycrystalline a Zr was studied in vacuo under constant tensile stress. The experiments were conducted from 660° to 845°C over the stress range 870 to 5400 psi. The steady-state creep rate, is, of a Zr was found to be related to the applied stress, a, and temperature, T, by the equation where C is a constant. Two interpretations of the data are considered, each requiring different values of the parameters ß, Q, and . It is shown that this formula can be derived using Gilman's phenomeno logical equation relating dislocation velocity to the shear stress for the case where dislocation mobility is limited by the nucleation of kink motion. From the fundamental dependence of strain rate on dislocation velocity and the density of mobile dislocations, the factor exp(ßo) can be related to the stress dependence of the dislocation density, and Q to the energy of kink formation. The two interpretations considered are as follows: Case I—the parameters are adjusted so that the equation above describes the data over the entire range of stress and temperature, implying that creep is controlled exclusively by dislocation glide; Case IIthe parameters are adjusted to allow for the possibility that creep is diffusion-controlled at high stresses but glide-controlled at low stresses. For both cases the values of the parameters are within the spread permitted by the data. Factors favorable to the observation of the unusual stress -dependence of i, for a Zr are discussed and it is shown that the anomalously rapid rates of self-diffusion and the low modulus on the principal glide system are primarily responsible for the anomalous creep behavior. Metal-lograflhic observations are presented and discussed with reference to the overall creep behavior. PREVIOUS investigations of the creep behavior of a Zr have been conducted from room temperature to about 500C The results of these investigations are primarily of engineering significance because of the variety of conditions under which they were carried out, and the low testing temperatures employed. Little information is available concerning the fundamental nature of the elevated-temperature creep behavior of a Zr. This investigation of the creep behavior of a Zr above half the melting temperature (the melting temperature, T,, of a Zr is estimated to be about 1860"K was initiated because there are two significant anomalies of the physical properties of a Zr: a) the rate of self-diffusion in polycrystalline a Zr is anomalously rapid: b) both Young's modulus for polycrystalline a Zr and the shear modylus as-sociated with the prismatic slip system { 1010)( 1120) (the principal slip system in a Zr 7) have anomalously large temperature variations The importance of these quantities to the understanding of creep behavior has been demonstrated, and it was hoped that this investigation would provide a critical test of the predictions based upon the analysis of creep data for other pure metals. However, as the investigation progressed it became increasingly clear that the unusual creep behavior of a Zr could not be analyzed in a conventional manner. 1) EXPERIMENTAL EQUIPMENT AND PROCEDURES Two grades of zirconium, designated A and B, were used in this investigation. The analyses, as supplied by the vendors, are presented in Table I. Material A, with a nominal purity of 99.84 pct, was supplied by the Wah Chang Corp. in the form of cold-rolled sheet from which specimens were machined without further fabrication. Material B, with a nominal purity of 99.95 pct, was purchased from the Nuclear Materials and Equipment Corp. in the form of iodide crystal bar.

Jan 1, 1968

By Clarence Seyler

THE technical difficulties of cutting thin sections of coal for examination by transmitted light have hitherto restricted the investigation of the important subject of the microstructure of coal to the few possessed of the requisite skill and time. Apart from this, the method fails with anthracites and other coals rich in carbon, owing to the opacity of the material. Occasional use of the method of polishing a surface, with or without etching, has been made, but it was not until Winter1 published an account of his results that attention was seriously directed to the method. In May, 1923, a specimen of dull anthracite came into my hands; I tried Winter's method on it and the presence of megaspores and other vegetable structures became clearly visible. A preliminary notice was published by me;2 but I soon abandoned the use of Schulze's solution having found that a mixture of chromic and sulfuric acids gave far better results. In the meantime Turner and Randall, in America, had independently developed the method of flame etching, as applied to anthracite, with great success. I have spent a year studying the method of chromic etching, which gives excellent results with bituminous coals and cannels, as well as with anthracite. For anthracites, I have used the chromic method and Turner's method of flame etching, whichever was the more convenient or as a check one on the other. The polishing is done, according to metallurgical practice, by the use of a polishing machine and successively finer emery paper, followed by polishing on cloth moistened with a suspension of levigated green oxide of chromium, and a final rubbing on "selvyt" (a cotton velvet polishing cloth) moistened' with alcohol. The polished sample is examined by reflected light with a 2/3 and 1/6 in. objective. Bituminous coals usually show considerable structure, and even anthracites show it faintly in places. The sample is then etched by immersion in a boiling solution made by adding 10 c.c. of concentrated sulfuric acid to 30 c.c of a saturated solution of chromic acid; enough water is then added to dissolve

Jan 3, 1925

Jan 1, 1924

By Daniel Hanson

FoR most of their practical applications metals are required to withstand stresses of appreciable magnitude: indeed, it id because they possess the quality of resisting stress without becoming permanently deformed that they find such extensive use in the service of man. Metals and alloys must, in service, usually behave as elastic substances—or nearly so. It is not difficult to satisfy this condition at ordinary temperatures. Iron and its alloys, especially the steels, are at normal temperatures excellent elastic bodies, capable of satisfying most of the mechanical requirements of the engineer: where electrical, chemical or other properties are impor-tant, which cannot be met by steels, it is usually possible to find a non-ferrous alloy such as nickel, copper or aluminum, which will prove satisfactory. When the metals or alloys are not inherently sufficiently elastic, cold-working or heat-treatment may develop elastic properties to a sufficient extent for practical needs. By means of relatively simple, rapid tests we can measure such properties as elastic modulus, limit of proportionality and proof stress, upon which design can be based with confidence. The case of the soft metals, such as lead and tin, is well known to be exceptional. They possess no definite limit of elasticity, and the value of proof stress or tensile strength depends to a great extent on the speed with which the test is carried out. Design here must be based on other considerations than a well-established theory of the proportionality of stress and strain. It is now generally recognized that steels and non-ferrous alloys possess at temperatures not greatly exceeding that of the atmosphere, characteristics quite different from those existing at ordinary temperatures, and that they assume qualities similar to those of the soft metals. Not only have they no limit of elasticity, but the proof stress and the ultimate stress depend on the time of application of the load. Flow under load may persist for long periods of time, possibly indefinitely, and the determination of a true maximum stress becomes a matter of great difficulty.

Jan 1, 1939

THE developments in construction and operation of the basic open-hearth furnace that have taken place in recent years have placed new emphasis on the vital influence played by regulation and control of the combustion system in both furnace production and furnace life. The several factors influencing flame development, such as regulation of fuel supply, air supply, air preheat, furnace draft, and furnace reversal, must be controlled closely if successful furnace performance is to be accomplished. Rugged instrumentation of distinctive design is required to sup- ply dependable information concerning operating conditions, which is requisite to proper regulation of combustion. This chapter attempts to give a practical discussion of the various features of open-hearth practice and instrumentation related to the efficient heating of the furnace, control of temperature, and protection of the furnace structure from accidental overheating. The appended references will be helpful to readers wanting a more detailed treatment of individual topics. OPEN-HEARTH FUELS The most important open-hearth fuels are listed in Table 4-1 together with their compositions and other data useful for combustion calculations. A detailed discussion of open-hearth fuels is not attempted here, but certain factors peculiar to their application to this type of process are briefly indicated on the following pages. Very often an open-hearth shop is forced by economic factors to use a fuel to which its furnaces are not very well adapted, because the general fuel-allocation scheme for the works as a whole seems to demand it. Often a variable marginal supply of coke-oven gas or tar must be consumed by the open hearth, together with another fuel such as producer gas, natural gas, or oil, to fill out total requirements. Most furnaces employ more than one kind of fuel during their useful life; however, the partial redesign

Jan 1, 1964

By G. Willard Quick, John R. Freeman

Jan 1, 1930

By R. J. Wagner, F. F. Craig, H. G. Riley, J. D. Griffith

Peripheral water injection has been underway in the Sholem Alechem Fault Block "A" Unit, Stephens County, Okla., since 1955. In the engineering planning of the flood, it was recognized that maintenance of pressure in the large, dry gas caps was vitally necessary to prevent the loss of an estimated 27 million bbl of oil through saturation of the gas caps by the oil banks moving updip on the peripheral flood pattern. The development of an abundant, low-cost water supply and the rising cost of makeup-gas purchases indicated that gas-cap control by water injection was desirable from an economic standpoint, provided an eflective water barrier could be placed without premature water breakthrough into downdip oil producers. A laboratory model scaled to the existing reservoir conditions was comtructed to evaluate the feasibility of gas-cap water injection. Model studies indicated that (I) water injected at the edge of the gar-oil contact would form a continuous barrier between the oil and gas zones, and (2) water would advance uniformly downdip without segregation due to gravity effects provided a specified, minimum water-injection rate was maintained. The model test results also indicated that it was not necessary to fill the gas cap completely with water. Water injection at the edge of one of the gas caps was initiated in March, 1958, to field test gas-cap water injection. Water breakthrough occurred at a downstruc-ture producing well in April, 1959, after approximately 2.5 million bbl of water had been injected into the gas cap. This was the volume calculated to be required to form the barrier between the oil zone and gas cap. This performance indicates that prevention of oil encroachment into dry gas caps in a peripheral water flood by water injection at the gas-oil contact appears practical and that the model studies provided a valid prediction of field performance. INTRODUCTION The Sholem Alechem Fault Block "A" Sims Sand Unit was one of the fist major waterflood projects in Oklahoma to utilize a peripheral injection pattern. Design of control measures to minimize oil encroachment into the large crestal gas caps was one of the greatest single problems during engineering planning of this flood. Engineering studies indicated that saturation of the gas caps with oil displaced by the peripheral water flood could result in a loss of about 27 million bbl of oil, or over one-half the estimated waterflood recovery. This estimate was based on a residual oil saturation after water flooding of 35 per cent pore volume, compared to the negligible oil saturation initially in the gas caps. The Sholem Alechem Springer field, located in Stephens County, Okla., is an elongated anticline with structural dips varying from 400 to 1,000 ft/mile. The structure contains numerous faults, some of which are sealing. The portion of the field considered in this paper is Fault Block "A", which is the largest of the five major fault segments in the field. A map of the unit is shown on Fig. 1. The unit is bounded on the east and west by major sealing faults, on the north by a water-oil contact and to the south by a deterioration of sand development. Two domes, each having gas caps, exist in the unit and are separated by a north-south fault as shown in Fig. 1. The sands being flooded are the Sims sand members of the Springer series of early Pennsylvanian age. The Sims sands average over 100 ft in thickness in Fault Block "A" and have a porosity of approximately 19 per cent. Core permeabilities average 160 md, with interstitial water saturation of about 23 per cent pore volume. Three different zones can be correlated over most of the area. However, they are commingled in most of the producing wells. The two upper zones, designated as First and Second Sims, are the most important. Both the First and Second Sims have gas caps in the east dome, while only the First Sims has a gas cap in the west dome. These gas caps, whose limits are also shown on Fig. 1, initially occupied nearly 11 per cent of the total reservoir volume. The major concern of this paper is the control of the two gas caps in the First Sims sand. Fig. 2 is a cross section, to scale, across the east dome of this formation. Notable features are the relatively shallow dip, the deterioration of the First Sims sand on the south side of the gas cap and the water-oil contact on the northern edge. The formation dip at the gas-oil contact in this cross section is approximately 5".

By E. S. Bumps, W. F. Craig, M. Baeyertz

Metallurgists have looked at fractures macroscopically for many years and have evolved a vocabulary in which such words as "cleavage," "brittle," "shear," "ductile," "granular," "fibrous," and "silky" are used to describe the appearance of the fractured surface; but the meaning of these words in terms of metal structure is not well established. Observations of the structural meaning of "brittle" and "ductile" fractures in plate steels have been made, notably, by Kramer and coworkers1 and by Tipper.2 Grossman3 has studied the fracture of tempered martensite and combinations of ferrite and martensite. Notwithstanding these and other less concerted attacks on the problem, present understanding of fracture rests more on assumptions and logic than on experiment. It is the purpose of this paper to add a little to the growing fund of experimental observations of the nature of fractures in steel. The particular fractures to be described were obtained in conventional impact testing of an ordinary structural steel shape. In impact tests of the Charpy type, the specimens fail in a characteristic manner that depends on the steel and the temperature of testing. With ordinary structural and many other steel products, an appropriate range of testing temperature will cause a considerable change in the energy absorbed before fracture. This change is known as the energy transition and is accompanied, more or less closely, by alteration in the appearance of the fracture. At testing temperatures below the transition, the terms "brittle," "cleavage," or "granular" are used to describe the fracture; above it, "ductile" or "shear" are often used. Within the transition, the fracture changes from "brittle" to "ductile" by a progression in appearance, wherein the "brittle" portion of the fracture becomes restricted to a smaller and smaller central area of the fracture, as the testing temperature is raised and the "ductile" type of fracture is approached. All this is well known to metallurgists. The specimens under consideration are of the conventional V-notch Charpy type. They were taken from a structural steel shape of the following analysis: C Mn P S Si 0.17 0.46 0.009 0.029 0.03 Both longitudinal and transverse specimens were tested and examined. Fig 1 shows the energy values plotted against testing temperatures in the usual way. The curves for both longitudinal and transverse specimens show an energy transition, although the maximum energy absorbed at testing temperatures above the transition is greater in the case of the longitudinal specimens. Fig 2 illustrates the changes in the macroscopic appearance of the fractures that are associated with the energy transitions shown in Fig 1. Macrographs of the fractured surfaces of the specimens have been identified with the fracture ratings at intervals on each fracture curve. The numerical fracture rating on the ordinate of Fig 2 indicates the percentage of the area of each fracture that was considered to be "brittle" on macroscopic observation. Such rating of the fracture type in impact tests is now customary in many laboratories. Hereafter the specimens will be identified by reference to Fig 2 as 90 pct "brittle," 80 pct "brittle," and so on, in accordance with this macroscopic evaluation of the appearance of the fractured surface. The discussion of the fractures is divided into three parts. The first two are concerned with the mode of fracture and its relation to general structural features. As the same metal-lographic features occur in both longi-

Jan 1, 1950

By N. Brown, R. Kossowsky

Plain carbon steels with 0.48 and 0.95 pct C were quenched and tempered at 705°C to produce carbide dispersions with spacings on the order of 1 p. The morphology of the structure consisted of a carbide-dislocation network. The strengthening due to the dispersion was found to vary linearly with M-½ where M is the mean free-ferrite path determined by the entire network. No preyield microstrain preceded the upper yield point. After prestraining, the lowest stress at which dislocation movement could be detected was 104 psi; this frictional stress was independent of the dispersion and prestrains up to 6.5 pct. The Cottrell-Petch equation for grain-size strengthening was used to discuss the dispersion strengthening in this investigation. The results support an impurity mechanism for the upper yield point rather than one based on the Johns ton- Gilman theory. IT was pointed out by Gensamerl that the mean free path in the matrix is the important variable which controls the degree of dispersion strengthening. Gensamer's data on steels showed a linear relationship between the yield point and the logarithm of the mean free-ferrite path. The first theory was by Orowan,2 who suggested the mechanism of dislocations bowing between particles, with the resulting relationship that where a is the yield point, P is the distance between particles, and G is the shear modulus. The Orowan equation applies to that range of dispersion where P is large compared to the particle size and the particles are not coherent, so that the matrix is essentially free of internal stresses. As was pointed out by Orowan, there are different degrees of dispersion which, in turn, will influence the strength-controlling mechanism. However, in this investigation, we wish to confine ourselves to the region of coarse dispersion, where the Orowan mechanism should, intuitively, be applicable. It was soon evident that the data, which existed at about the time that the Orowan theory was proposed, did not agree with the Orowan equation in that the actual strengthening was always greater than the theoretical predictions. Thus, Fisher, Hart, and pry3 modified the Orowan theory by suggesting that the Orowan process took place in the microstrain region preceding macroscopic yielding and the subsequent, rapid work hardening in the form of residual dislocation loops around the particles largely determined the observed macroscopic yield point. The F-H-P theory stated that the increment of strengthening due to the work-hardening mechanism was proportional to f3/2 where f is the volume fraction of the precipitate. F-H-P used data by Shaw, Shepard, Starr, and Dorn4 on A1 3-5 pct Cu to support their theory. Roberts, Carruthers, and Averbach5 were the first to make a microstrain study of dispersion strengthening, and they found that for steel the Gensamer relationship was obeyed. Hayman and Nutting6 suggested that in the case of tempered steel 1) the ferrite grain boundary was the primary obstacle and 2) the carbide particles simply formed part of the grain boundary obstacles. They found that the strength varied as G"" where G is the ferrite grain size. Turkalo and LOW' determined the structure of quenched and tempered plain carbon steel using a replica technique; they concluded that the carbide particles did not necessarily lie in the ferrite grain boundaries. When they defined the mean free-ferrite path as being determined by both particles and the ferrite path boundaries, their data obeyed the Gensamer relationship. Meiklejohn and skoda8 showed that the strengthening from iron particles in mercury was a function of the particle size and the distance between particles. Dew-Hughes9 explained the Meiklejohn and Skoda results by the following theory: 1) grown-in dislocations which surrounded the particles were produced by the thermal stresses during the time the material was cooled to the testing temperature, and 2) the observed strengthening was associated with the cutting of the grown-in dislocations by the glide dislocations. Ansell and Lenel10 proposed a theory in which the glide dislocations pile-up or surround the particle until the number of dislocations in the pile-up is sufficient to yield or fracture the particle. The resulting theory says that the yield point varies as p-1/2, where P is the distance between particles. The Ansell-Lenel theory is almost identical to the

Jan 1, 1965

By Gerald F. G. Sherman

The ore deposits of the Warren district, in which the mines of the Copper Queen Consolidated Mining Co. are situated, have been described in a number of technical publications, and will not be discussed here in detail. Certain of their characteristics, however, control methods of underground transportation and hoisting of ore. In the Copper Queen mine, the majority of the ore has occurred in a zone encircling the west boundary of the porphyry intrusion of Sacramento Hill. It has a width varying from 800 to 1,200 ft., and a thickness of about 400 ft. It reaches the surface in the older part of the mine to the northwest, but dips to the southeast, where it is reached at 1,400 ft. below the Czar collar, in its farthest extension at present developed on Copper Queen ground. There is one major extension from the northwest end of the zone toward the west along the Czar fault, and others of minor importance. Individual orebodies are scattercd through the zone in an eccentric manner, only matched by their own irregularities of form and size. Their most gencral characteristics are the softness of the ore and their grcat horizontal rather than vertical extent. It has been estimated that the average vertical thickness of ore in the Czar and Lowell divisions is between 30 and 35 ft. It is calculated by assuming it to be uniformly distributed over its horizontally projected area. In this zone, and for some distance above it, the ground has been subjected to intense alteration and intense but irregular oxidation. It has resulted in an enormous quantity of earthy or clayey material, which may be either ore or waste, which when wet is both heavy and tenacious. Below alteration, the ground is fairly hard, and the limestones contain primary ores differing from those heretofore considered typical of the camp, and which have not yet been thoroughly exploited. The mine production has been drawn from many orebodies spread over a great area.l A diagram map (Fig. I), of haulage drifts and loading stations, illustrates the situation in 1914.

Jan 1, 1916

By Wilbur T. Stuart

TO assist the mining industry in attacking problems of water control, the U. S. Geological Survey has begun a program of research in mining hydrology. In certain fundamental respects water control is similar to development of water supplies from wells or to the drainage of agricultural lands, as many of the tools developed in recent years for quantitative ground-water problems are applicable, with modification, to mine-water problems. In 1952 a 30-day pumping test conducted jointly by the Eureka Corp. Ltd. and the Defense Minerals Exploration Agency provided an opportunity to gain knowledge concerning water movements around a flooded mine shaft. The methods of analyzing the data may be used as a guide for the evaluation of similar problems elsewhere. The Fad shaft of the Eureka Corp. is on Ruby Hill, 1 1/2 miles west of Eureka, Nev. The shaft was completed at a depth of 2465 ft in November 1947 at a site adjacent to the downfaulted block in which the ore was found. As the drift on the 2250 level progressed toward the ore zone, a large flow of water was encountered after the Martin fault was intersected. This flow exceeded the installed pump capacity, and an unsuccessful attempt to recover the shaft and the 2250 level was made in 1948.1, 2 Geology and Hydrology: The complex structure of Ruby Hill is that of an anticline broken first by thrust faulting and later by normal faults. The present orebody comprises several mineralized zones within a block of the Eldorado limestone of middle Cambrian age which was downfaulted 1400 to 1600 ft, and it may be related to a similar body mined at a higher level south of the Ruby Hill fault. At the depth of the largest zone of ore the block is roughly rectangular in shape, about 1000 ft wide and 1500 ft long, and dips about 30" NE, see Fig. 1. It is apparently bounded on the south by the Ruby Hill fault, on the east by the Jackson fault, on the north by the Martin fault, and the west by the Bowman fault. Within the block, but between the Ruby Hill and the Martin faults, are the Office and Adams Hills faults; west of the block and the Bowman fault are the Albion and Spring Valley faults. There are many conflicting reports concerning the water-yielding characteristics of the Eldorado limestone and the condition of the fault zones, that is, whether they are open or tight. However, the diamond-drill records indicate that open spaces as much as 2 or 3 ft across were encountered, and considerable cementing and lining of holes was necessary to maintain circulation of drilling fluid. There is also evidence that the Eldorado limestone was cavernous where it was mined in the early days south of the Ruby Hill fault. At the site of the Fad shaft the formations encountered from the surface down included the Pogonip limestone, Dunderberg shale, Hamburg limestone, and Secret Canyon shale. These formations did not yield large quantities of water to the shaft. The Pogonip limestone, which appears to be permeable and might yield water elsewhere, is above the water table in the vicinity of the shaft. The Secret Canyon shale, immediately overlying the Eldorado in some places but in most places separated from it by the Geddes limestone,3 is apparently tight and does not transmit water. During the 30-day test period the shale briefly confined the water in the underlying formations so that artesian conditions were observed in drillholes E and F, which are cased into the Eldorado limestone, whereas unconfined conditions were observed in drillholes B, C, and D, which were open to the shale. The Geddes limestone, which normally lies between the Secret Canyon shale and the Eldorado limestone, was not encountered in the Fad shaft. The Geddes, a flaggy, fractured limestone, is reported capable of yielding large volumes of water. Water stored in the interstices of this thin-bedded limestone within the Ruby Hill fault zone on the 1200 level of the Locan shaft drowned the pumps in 1923 when the Richmond-Eureka Mining Co. attempted to explore the area along the fault. Eldorado limestone was not encountered in the Fad shaft. In the ore-block area the Eldorado limestone was not entirely offset from other water-yielding formations by movement along the Bowman fault; therefore it may be hydraulically connected with the other formations. Adjacent to the Ruby Hill, Jackson, and Martin faults, the Eldorado lies in contact with other possible water-yielding formations. One of these, the Prospect Mountain quartzite, is separated from the Eldorado by thin, sheared, and broken beds of the Geddes within the Ruby Hill fault zone. A limited examination by the author of the Prospect Mountain quartzite in the Richmond mine at a higher level and south of the Ruby Hill fault indicates that the quartzite is poorly permeable. The monzonite mass south of the quartzite would be a further barrier to the flow of water. The poor permeability of this area is substantiated by records of levels at which water was encountered south of the Ruby Hill fault. In view of the normally low rate of ground-water recharge, if this desert area had been permeable, water levels could not have been maintained at altitudes of many hundred feet above the present water table west and north of Ruby Hill. Thus the ore-bearing block of Eldorado limestone is in contact with possible water-yielding rocks on at least two sides, and if the fault zones are possible conduits for water circulation the geologic and hydrologic conditions are suitable for the infinite-aquifer type of analysis as used and modified here. History of Pumping: During sinking of the Fad shaft a maximum pumping rate of 1500 gpm kept the shaft dewatered sufficiently, but in March 1948, after the 2250 level drift passed through the Martin fault into the Eldorado limestone, the pumps and shaft were flooded. Subsequently additional pump-

Jan 1, 1956

By E. H. Dix

All commercial aluminum contains small percentages of copper, iron, and silicon as unavoidable impurities. The purest metal obtainable commercially, special grade high purity ingot, contains a maximum of 0.50 per cent. impurities of which the usual minimum amount of copper is 0.01 per cent.; silicon, 0.12 per cent.; and iron, 0.20 per cent. This grade is too costly for most purposes. The two standard grades, Nos. 1 and 2, containing a minimum of 99.0 and 98.0 per cent. aluminum, respectively, are more generally used. Other grades of secondary aluminum often contain as high as 3 or 4 per cent. of impurities, which include 1 per cent., or more, of zinc. Specifications for high-grade aluminum-casting alloys generally allow a maximum of 1.7 per cent. for total impurities. The S. A. E. Specification No. 33, which is intended to cover alloys made from secondary aluminum ingot, gives the iron maximum as 1.5 per cent. and the maximum for silicon (including manganese and tin) as 0.75 per cent. The effect of even relatively small amounts of impurities on the physical properties of ingot aluminum is shown by the following cornparison of two lots of aluminum, which may be taken as representative of special grade and grade No. 2 ingot, respectively. AnalysEs Special Grade, Gbade No. 2, Per Cent. PeR CBnt. Copper................................. 0.01 0.32 Silicon................................. 0.12 0.32 Iron................................... 0.42 0.82 Aluminum.............................. 99.45 98.54

Jan 1, 1923

By S. Brunauer

The hydration of portland cement is treated as a chemical reaction and the changes in matter, in energy and the rate of change of the process are discussed, Portland cement is a mixture of four major and at least as many important minor constituents. In the hydration process, the four major compounds (trical-cium silicate, dicalcium silicate, tricalcium alumi-nate and tetracalcium aluminoferrite), plus gypsum and water form five or six new compounds. In spite o the great complexity of the reaction, considerable progress has been made in its understanding, primarily with the help of such research tools as X-ray diffraction and electron microscopy. The rate of the reaction can be followed by direct and indirect methods of measurements. The effects o composition, particle size (or specific surface), temperature and water-cement ratio on the rates of hydration are discussed. The hydration of portland cement is a chemical reaction accompanied by such highly important physical phenomena as heat evolution, setting and hardening. It is a vast and complex subject, on which hundreds of papers have been published. At the time of the writing of this paper, in October 1962, a two-volume book, which alone contains dozens of papers pertaining to cement hydration appeared in print.' The present paper deals with a few aspects of this vast subject, and the selection was not easy. The work reported here deals with some of the most recent investigations in the field. In any chemical reaction, the physical chemist is primarily interested in three things: changes in matter, changes in energy and the rate of change of the process or the speed of the reaction. This is true also of the chemical reaction between portland cement and water, and all three aspects of the reaction will be discussed. These three aspects are of vital interest to the engineer as well. Portland cement is not a cementing material — the hydration products, the new materials which form in the reaction, have the cementing action. The energy changes manifest themselves in a considerable evolution of heat, which may be useful or harmful. It is useful, for example, in winter concreting, but in very large concrete structures like dams, a large evolution of heat, which cannot be easily dissipated, may produce distress in the structure. Primarily for such a purpose was the Type IV or low heat portland cement developed. The speed of the chemical reaction is important because it determines the time of setting and hardening. The initial reaction must be slow enough to permit placing of the concrete before setting occurs. On the other hand, after the placing of concrete it is often highly desirable to obtain as rapid chemical reaction as possible. For this purpose the Type 111 or high early strength portland cement was developed. CHANGES IN MATTER Portland Cement: In a basic investigation, before one begins to study a reaction, one either knows the quantities and compositions of the starting materials, the reactants, or one determines them. This is obvious; the chemist expresses the changes in matter that occur in a reaction by a chemical equation, which has the quantities and compositions of the reactants on the left side of the equation and the quantities and compositions of the reaction products on the right side. The first question is then what to put on the left side of the equation in the reaction between portland cement and water? It is not very easy to answer this question. Portland cement is not a single chemical compound but a mixture of many compounds. Four of these are considered the major compounds, and at least four of the minor compounds also play important roles in the hydration reaction. In order to avoid complicating matters, the present discussion will be restricted primarily to the four major compounds, which constitute usually more than 90% of a portland cement. The relative amounts of these compounds vary from cement to cement. Actually not only the amounts but the compositions of these constituents also vary to some extent, but the variation in composition of the individual components will be neglected for simplicity.

Jan 1, 1963

By Charles L. Mantell, Kurt Straler

The hydrogen reduction of Cr2O3 to chromium metal was found to be feasible at very low water-vapor concentrations, corresponding to dew points of -38° to -24°C, over a temperature range of 1130" to 1490°C. Hydrogen reduction under these conditions was predicted by the calculated equilibrium curves which also indicated that CrzOs is reduced directly to chromium without forming the intermediate oxide, CrO. This reduction path was confirmed by X-ray diffraction analysis. The percent reduction of Cr2O3 at each reaction temperature was constant with time, suggesting an inhibiting effect of water vapor. A small increase in the residual water-vapor concentration of a single temperature, 1490°C, strongly retarded the rate of reduction This effect was expressed by an empim'cal equation which indicated a direct relationship between "distance from equilibrium" and the rate of reduction. me effect of temperature over the range of 1130" to 1490°C was expressed in an Arvhenius plot of log rate vs reciprocal absolute temperature. From this curve the apparent enthalpy of activation was found to be 29,600 cal. Based on the hypothesis that the rate of reductiun is contvolled at the oxide-metal interface, an over-all rate equation consistent with the experimental data and the thery of absolute reaction rates was formulated. A simplification of this expression to an Arrhenius equation was justified by the overriding effect of temperature on the rate of reaction for the minimum water-vapor concentration range. MOST of the metals in Subgroup V1 of the periodic table can be prepared commercially by direct reduction of their oxides by hydrogen or carbon monoxide, at temperatures considerably below the melting points of both the metals and their oxides. Chromium is an exception, being generally reduced from its ore, Cr2O3 . FeO, by silicon in an electric arc furnace which operates above the melting point of the Fe-Cr alloy or above the melting point of chro- mium if a chromium oxide be the starting material. In reduction of chromium oxide by hydrogen, either reduction does not occur at all or the rate of reduction is extremely slow. Theoretical considerations based on the high, exothermic, free energy of formation of Cr2O3 compared to the oxides of the other Subgroup VI metals, molybdenum, tungsten, and uranium, would also suggest a slow rate of reaction and a high activation energy. Interest in the direct gaseous reduction of fine-powdered ores in fluidized beds was considered justification for examination of this reaction. In order to develop a basis for a continuing study of the commercial feasibility of the direct gaseous reduction of chromite, a study of the kinetics of the reduction of Cr2O3 with hydrogen was undertaken. To the authors' knowledge no accurate kinetic data for this reaction have been obtained. Neither has an activation energy been determined nor has an attempt been made to establish a mechanism of reaction. LITERATURE Maier10 compared the data of I. Y. Granaat,6 H. von Wartenburg and S. Aoyama, and G. Grube and M. Flad7 with that derived from calorimetric and ther-modynamic properties for the equilibria for the reduction of Cr2O3 with hydrogen. These results, plotted as the log of the equilibrium constant vs absolute temperature for the reduction of Cr2O3 and the intermediate oxide, CrO, to chromium, show agreement between the differently derived data. In both cases the equilibrium constants were extremely low. Maier showed that, over a temperature range of 1000° to 2000°K, Cr2O3 is more readily reducible than CrO. Granat assumed that CrO was preferentially formed from Cr2o3 above 1100°C. Grube and Flad's analysis of their reaction products in the 895" to 1000°C range indicated the coexistence of only Cr2O3 and chromium. The hydrogen reduction of the other Subgroup VI metals, molybdenum, tungsten, and uranium, shows that reduction of the higher oxide proceeds through all of the intermediate oxides before being reduced to the metal. Since evidence pointed to an anomaly in the reduction behavior of Cr2O3, the authors investigated the reduction path of Cr2Os.to chromium. This was done theoretically with more recently available free-energy data and experimentally by X-ray diffraction analysis. This work reinforces Maier's conclusion.

Jan 1, 1964

By Milton E. Wadsworth, R. Ted Wimber

Cobalt sulfate solutions containing ammonium acetate and chloroplatinic acid were reduced by hydrogen in a pyrex-glass lined autoclave in the temperature range of 170o to 232°C and hydrogen partial pressure range of 115 to 830 psia. The reduction rate was directly proportional to the hydrogen partial pressure and surface area of the pyrex glass and was independent of the quantity of chloroplatinic acid added initially. Experiments involving the variation of the relative concentration of ammonium acetate indicated that the reducible cobalt complex was probably the diacetate complex of cobalt, Co(AC)4H20, or a new mononcetate complex Co Ac, which was in solubility equilibrium with a pink precipitate of CO(AC)-4HzO. THE reaction in which a metal is dissolved by an acid to produce gaseous hydrogen and a salt solution was discovered early in the history of chemistry. In 1859 Beketoff found experimentally that this reaction could be reversed; i.e., a salt solution could be reduced by gaseous hydrogen to produce a metal and an acid. A review of work done on this phenomenon since that time may be found elsewhere., The hydrogen reduction of a cobalt salt solution is facilitated by complexing the cobalt ion. An ammonia complex of cobalt has been reduced commercially in the recovery of cobalt metal. A new reducible complex of cobalt was discovered5 when it was found that a co-baltous sulfate solution containing ammonium acetate could be reduced by hydrogen at temperatures in the region of 200°C. When a cobalt sulfate-ammonium acetate solution was heated to a temperature below its normal boiling point, a violet color became apparent, indicating complex formation. The nature of this complex was investigated5 by the addition of NH4Ac to a CoSO4 solution maintained at 85o. During the first additions of NH, Ac, the pH of the solution remained fairly constant at about 5.85. However, as the ratio of NH,Ac to CoSO, approached two, the pH rose and then leveled off at about 6.05. The absorption spectra of a Co(Ac), solution and a CoSO,, NH Ac solution were obtained at 85°C and were compared and found to be the same. These findings suggested that the diacetate complex of cobalt, Co(Ac),.4H20, was formed at 85°C. When a cobalt sulfate-ammonium acetate solution was heated to a temperature above about 165o, a finely divided pink precipitate appeared. The X-ray diffraction pattern of this precipitate indicated that it was Co(Ac), - 4H,O. In addition, it was discovered that when chloroplatinic acid, H,PtCl;, was added initially to the cobalt sulfate-ammonium acetate solution, a faster reduction was obtained. The roles of the solution complex, pink precipitate and chloroplatinic acid in the reduction process were then investigated. APPARATUS The experimental work was carried out in a two-liter stainless-steel autoclave. Adetailed description of the autoclave and the auxiliary equipment used in maintaining constant temperature and pressure may be found elsewhere.= Because the stainless steel was corroded, and also because it acted as a hydrogena-tion catalyst, an all-glass liner was fabricated such that the solution came only into contact with flame-polished pyrex glass. EXPERIMENTAL PROCEDURE The solutions used in the experimental work were prepared by dissolving reagent grade chemicals in distilled water. Although variation of the brand of ammonium acetate appeared to have no effect on the experimental results, CoSO, 7H O from the J. T. Baker Chemical Co. of Phillipsburg, N. J.,was found to give faster reductions than that prepared by Allied Chemical and Dye Corp., N. Y. The former was used throughout the course of the experimental work and was weighed up at the outset of each experiment. The ammonium acetate was dissolved to form a 6M stock solution, which was stored under refrigeration. A 10 pct solution of chloroplatinic acid (J. T. Baker Chemical Co.) was diluted to a 1.15 x 1Q2 M stock solution, which was standardized by precipitation of K,PtCl, as outlined by Scott. The appropriate volume of the chloroplatinic acid, H,PtCl,, solution was pipetted into the clean, dry glass liner. The cobalt sulfate-ammonium acetate solution, which had previously been saturated with

Jan 1, 1962

By R. E. Zimmerman, Michael Sokaski, E. R. Palowitch, M. R. Geer, H. F. Yancey, W. Deurbrouck, S. C. Sun

PART 1: DENSE MEDIUM SEPARATION by M. SOKASKI, M. R. GEER and H. F. YANCEY INTRODUCTION In the early days of coarse-coal treatment by the dense-medium process in Europe, loess was one of the materials used for medium solids. Newly developed cyclones were used to reclaim and thicken :he loess suspension. On occasion, when the cyclone thickener at the Maurits mine in the Netherlands plugged, the overflow was found to be filled with clean coal free of impurity. From this observation stemmed the concept of the cyclone as a cleaning device. Development took place during World War 11 in the laboratory of the Dutch State Mines under the direction of M. G. Driessen. A 15-ton-per-hour pilot plant was in operation in the laboratory by 1945, when, in September, Driessen made the first public disclosure of the process in a paper presented to the Institute of Fuel in London. In April 1945,2 operation of this pilot plant was observed by one of the authors, who was so impressed with the potential of the cyclone process that, on his return to the United States, a research program on the cyclone was started by the Bureau of Mines immediately. This work led to an AIME paper in 1946 in which the first details of cyclone operation on American coals was made available. Commercial adoption of the cyclone proceeded in Europe, initially in the Netherlands, Germany, and France. In the United States, where coal is less costly and most of the coals are so easy to clean they respond well to simpler cleaning systems, the first cyclone plant was not built until 1961.3 As of the spring of 1967, a total of 31 commercial cy- clone plants had been installed or were under construction in the United States; this does not include eight Dynawhirlpool plants. The capacity of the cyclone plants ranges from 50 to 1300 tons per hour and totals 6600. THEORY Before discussing the theory of a dense medium cyclone, a brief description may be helpful to some readers who are not familiar with its basic operation. In a typical dense-medium cyclone, illustrated in figure 10-1, the mixture of medium and raw coal enters tangentially near the top of the cylindrical section, thus forming a strong vertical flow. The refuse moves along the wall of the cyclone and is discharged through the under- flow orifice. The washed coal moves toward the longitudinal axis of the cyclone and passes through the vortex finder to the overflow chamber.

Jan 1, 1968

By W. E. D. Jr. Stokes

THE application of aviation to mining and petroleum operations, on the basis of economy and attainment, has become a demonstrated fact. According to Dominion Government records, 30. Canadian companies engaged in air transportation with northland mining camps, carried 13,000 tons of freight in 1935, and in 1936 carried 16,000 tons. In addition, many mining companies used planes to transport prospectors with canoes, outboard motors, gasoline drums and supplies to remote locations, and one company maintained a plane to take radium-bearing ore from its mine on Great Bear Lake nearly 1000 miles south to the rail-way at Waterways, Alberta. Heavy pieces of mining machinery weighing 2 tons are being carried by Ford trimotor planes over the Andes, at an altitude of not less than 15,000 feet. At Bulolo, New Guinea, 17,500 tons of disassembled gold-dredging equipment has been flown over inaccessible terrain, while supplies and building materials for a, community of 1000 whites have been transported by airplane. A 3 1/2-ton shaft was carried on one notable trip, while at another time an automobile, 2 tons of rice and a large safe went over the mountains in one plane. Fig. 1 shows an electric generator that was carried by plane to Bulolo.

Jan 1, 1937

By R. D. Carnahan, J. E. White

A study of dispersion strengthening in TD-Nickel (nickel plus 2 vol pct Tho2) was conducted employing microstrain techniques at ambient room temperature. It was found that optimum strength was due primarily to the incorporation of stored energy developed by a variety of thermal-mechanical treatments. The relatively low strength of the recrys-tallized condition implies that the dispersed particles themselves offer only token resistance to deformation. The development of resistance to large-scale recovery or recrystallization at temperatures near the melting point requires a more extensive sequence of strain-anneal cycles than does the development of optimum strength. A micro-Bauschinger effect was observed which appears to be related to the lattice resistance to the movement of free dislocations. The effect was nearly identical to that in pure nickel indicating that the presence of the dispersed phase and considerably increased dislocation density (stored energy) only alters the number or effectiveness of barriers. THE early stages of deformation of engineering materials can be conveniently studied by utilizing strain-gage techniques which permit resolution of strains less than 5 X 10-7 in. per in. for testing in four-point bending (Carnahan and white1). The present investigation, part of a continuing study on the very early stages of deformation, was designed to reveal the true role of a dispersed phase in promoting high strength in a commercially available dispersion-strengthened alloy. Although this technique has been used for some time to study microdeformation in pure metals and alloys, it has just recently received attention as a means of investigating dispersion strengthening. Studying the very early stages of deformation in alloys which depend upon a finely dispersed inert phase for strength may prove to be a very important method for a better understanding of these materials. It is essential to obtain considerable clarification of actual dislocation movement and the kinds of deformation barriers which exist before optimum properties can be designed into this type of material with any degree of confidence. Considerable research on a variety of dispersion-strengthened materials has resulted in two different schools of thought regarding the strengthening mechanism. One faction2-4 favors the idea that the particles themselves resist the motion of dislocations. The criterion for yielding is the fracture of the dispersed second-phase particles due to an array of piled-up dislocations. Other invesfigators5-a have shown that particles are effective primarily by allowing a greater buildup of stored energy or dislocation density through thermal-mechanical treatments in the composite than the pure matrix material. The particles themselves, then, are not exclusive obstacles, but the complex network of particles, dislocation tangles, subboundaries, and grain boundaries are strength determining. The development of such a complex dislocation network in SAP has been studied recently in some detail by Goodrich and Ansell. The ability of dispersion-strengthened alloys to resist softening or recrystallization is also of considerable importance; however, the criteria for maximum stability may not necessarily be those for maximum strength. In this study, in addition to the evaluation of the microstrain properties of TD-Nickel, it is felt that considerable clarification of the true dependence of strength and stability on the dispersed phase is shown. I) MATERIAL AND PROCEDURE TD-Nickel is a dispersion-strengthened alloy developed by the E. I. DuPont de Nemours Co., which contains 2 vol pct thoria (Tho2) in a pure-nickel matrix. The average ThO2 particle size is approximately 0.1 p and the interparticle spacing is less than 1 u. The material was supplied by DuPont in two conditions: hot-extruded bar stock, and stress-relieved cold-rolled sheet 0.025 in. in thickness. The bar was extruded at 2200°F from a cold-pressed and sintered billet. The sheet stock was prepared from the extruded material by a process involving ten or more 50-pct cold reductions by rolling with intermediate anneals at 1800° to 2000°F. Test specimens used in this study were prepared in the form of rectangular parallelepipeds measuring 0.375 by 1.375 in. in thicknesses ranging from 0.025 to 0.040 in. Samples prepared from sheet and extruded stock were mechanically polished before heat treatment and were handled with extreme

Jan 1, 1964

By T. E. Eagan, W. R. McCrackin

IN dealing with segregation in babbitt, and its effect on the final cast structure, which is a bearing, it is obviously impossible to cover all of the compositions manufactured. Each composition, of course, will exhibit certain specific types of segregation. However, as examples,, two compositions of babbitt are presented: one a tin-base of well-known analysis and the other a lead-base, which in the past few years has found wide usage. Bearings usually are cast either statically or centrifugally; therefore the effect of these two methods on segregation is presented. EXPERIMENTAL PROCEDURE A slab of babbitt 1/2 in. thick by 5 in. wide and 17 in. long was cast, using a book mold with the long edge vertical. An A.S.T.M. grade 2 babbitt was used (3.5 per cent copper, 7.5 per cent antimony, remainder tin), to which 0.10 per cent tellurium had been added. Unfortunately, no metal without tellurium was available. The mold to hold the babbitt was heated to approximately 300°F., the temperature being judged by the babbitter. The pouring temperature of the babbitt was 875°F. (470°C.). One slab was made by allowing the babbitt to cool without stirring. The other slab was stirred during the entire cooling cycle. This stirring consisted of a vigorous churning or puddling into the mold until complete solidification had taken place. Three samples were removed from these slabs. One was taken at the extreme bottom, another half way to the top, and another at the extreme top, all at the center of the width. Chemical, macroscopic and microscopic examination was made of all samples. Table I shows the chemical analyses obtained at the described positions [ ] in the slab. The analyses show no serious amount of gravity segregation. Microscopic examination from edge to edge of the slab showed little change in structure. From top to bottom there was a progressive coarsening of the grain size in the stirred slab but little change in the slab that was not stirred (Fig. I). No definite exhibit of segregation could be detected. In line with our experimental study on the tin-base babbitts, we cast an almost duplicate slab using A.S.T.M. Alloy No. 15, containing 0.9 to 1.25 per cent tin, 14.75 to 15.5. per cent antimony, 0.80 to 1.25 per cent arsenic and 0.4 per cent copper. The slab was 16 in. long and 3/8 in. thick, cast with the long side vertical. One slab was allowed to cool normally and the other was stirred continually during cooling. The pouring temperature of the babbitt was

Jan 1, 1944

By R. T. Southin

Cast ingots of 99.99 pct purity A1 and aluminum/copper alloys containing up to 2 pct Cu have been found to contain four zones rather than the three previously accepted, i.e., chill, colummar, and equiaxed zones. The fourth zone consists of a coarse dendritic layer across the top surface of the ingot which is open to the atmosphere. It is also found that the grains in the equiaxed region have a "cornet" shape, with a head which is coarsely dendritic and a tail which grew with the same structure as the columnar grains. Experiments using mechanical barriers, and others involving the elimination of the surface dendrile layer, have indicated that nucleation of the equiaxed zone is caused by the showering of dendritic particles from this surface dendrite layer. These particles are the dendritic heads found in the comet grains. A mechanism of nucleation and growth of these comet grains is put forward. Experiments with a number of other metals and alloys suggests that these conclusions may apply generally to ingots cast without the addition of nucleating agents, and solidified under normal conditions. THE macrostructure of cast ingots may contain the following three zones: i) a peripheral zone of fine equiaxed grains, commonly called the chill zone; ii) a zone of columnar grains extending inwards from the chill zone; iii) a central zone of equiaxed grains; these are normally larger than the chill grains. All three zones are not necessarily present in any particular ingot since their existence and magnitude depend upon the casting conditions and composition of the cast material. The mode of formation of zones i and ii is fairly well understood. However, the cause of the central equiaxed zone remains a matter of conjecture. Previous theories put forward to explain the mechanism of nucleation in the equiaxed zone have been examined by Chalmers1 and Winegard.2 At the time when the present work was carried out the most re -cent hypothesis was that due to Chalmers,1 who recognized more fully than previous workers that conditions in this zone during solidification were not conducive to nucleation. In his hypothesis, he suggested that nuclei were formed near the mould wall during the very early stages of solidification, and that they can drift into the central zone by convective motion. This was supported by evidence from experiments using mechanical barriers to stop the drift of nuclei. A similar hypothesis had previously been put forward by Genders.3 More recently, Jackson et al. 4 have observed that dendrite arms in organic compounds can melt off during solidification. They have postulated that this occurs in metals and alloys, and that the dendrite arms which have been freed from the main dendrite act as nuclei for the equiaxed zone. In the present work, critical metallographic examination has shown that there is a fourth zone in the macrostructure of cast ingots which is a dendritic layer over the top surface of the ingot. It is also shown that there is a relationship between this zone and nucleation of the equiaxed zone. EXPERIMENTAL DETAILS The alloys examined were prepared from super -purity aluminum of 99.99 pct min purity (spectro-graphically detected impurities of Cu, Fe, Si, and Mg) and copper of 99.98 pct min purity (spectrographically detected impurities of Si, Zn, As, Fe, Pb, Bi, Ni, Sn, Mn, Ag, Cr, and Al). Three compositions of ingots were examined, containing 0.0, 0.1, and 2 pct Cu, respectively. The alloys were melted in an alumina-lined salamander crucible using a medium-frequency electric induction furnace; when the appropriate casting temperature was reached, the alloys were cast without degassing or fluxing treatment. The mould used was made of electrode graphite and had the following dimensions: external diameter 6 in., height 9 in., with a mould cavity 8 in. deep and a diameter tapering from 5 in. at the top to 4 in. at the bottom. Casting temperatures used were generally in the order of 70" to 90°C above the liquidus and the mould was at room temperature before casting. Inserts kere placed in the mould cavity in some experiments. These consisted of either an 18-g stainless-steel tube of 2 in. diam held axially in the mould i in. off the bottom and extending 1 in. out of the top of the mould or a "trap-door" barrier of stainless-steel gauze of 24-mesh held horizontally in the mould 31/2 in. down from the top. The construction of this insert is shown in Fig. 1. All inserts were preheated prior to casting to prevent chilling. RESULTS The macrostructures of ingots of the three compositions are described, in terms of the three generally recognized zones, in Table I, and illustrated in Figs. 2(a) to (c). The most interesting observation in this table is that relating to the shape of the equiaxed grains, which were not in fact equiaxed but of almost tear-drop shape. Closer examination of these grains showed that each consisted of a head which had a coarse dendritic structure and a tail which always grew in the opposite direction to heat flow, and which had the same structure as that of the columnar material of the ingot concerned; i.e., in the pure aluminum and 0.1 pct Cu alloy it was cellular and in the 2 pct Cu alloy it was cellular-dendritic. Identification of original cast grains was greatly hampered in the super-purity aluminum ingots, and to a lesser degree in the 0.1 pct Cu alloy,

Jan 1, 1968