By Yan Fu, Chuanlin Fan, Xiujing Zhai, Yongfeng Chang, Binchuan Li

"The mechanism of the selective chlorination of nickel and cobalt in reduced limonitic laterite was investigated. Reduced ores were obtained from the reduction roasting of a limonitic nickel laterite. The thermal decomposition of related chlorides and the selective chlorination of the reduced ore were carefully studied using Differential Thermal analysis - Thermogravimetry (DTA-TG), X-Ray Diffraction and chemical leaching methods. In the temperature range of 300 - 500 °C, aluminum chloride hexahydrate was chosen as chloride agent. During the selective chlorination, reduced ore was partly chlorinated by hydrogen chloride generated from the thermal decomposition of chloride agent. Then the oxydrolysis of ferrous chloride re-generated hydrogen chloride was used to further the chlorination. Finally, iron was mostly rejected as hematite, while nickel and cobalt were selectively chlorinated. More than 91 %Ni , 90%Co and about 4%Fe in the chlorinated ore was extracted using a water leaching method.IntroductionLimonitic nickel laterite is an important nickel reserve, which is rich in iron in the form of goethite and has low contents of magnesium, aluminum, silicon, and other elements. Goethite is the main nickel-bearing mineral in the laterite [1]. Nickel is generally present in goethite in three modes: (a) associated with amorphous or poorly crystalline goethite, (b) weakly adsorbed to the crystalline goethite surface, and ( c) as lattice substituents [2]. In addition, cobalt in limonite was found to be associated with a manganese phase rich also in nickel [3]. These results indicate that the extractions of nickel and cobalt are highly dependent upon the degree of the decomposition of the nickel, cobalt-bearing minerals.For the selective extraction of nickel and cobalt from limonitic laterite, the ore is usually processed by hydrometallurgical methods, including high pressure acid leaching (HPAL) [4] or reductive roasting - ammonia leaching (Caron process). However, there are still some disadvantages in these processes, such as the expense of autoclaves and scaling problems in HP AL [ 4, 5], and relatively low overall metal recovery, large energy and reagent requirements for the Caron process."

Jan 1, 2011

By Jian Li, J. Miles, P. Liu, W. Cook, W. Zheng, Alvin Qian

"High temperature corrosion resistance is one of the key challenges in water-cooled nuclear reactor material development. Iron based materials with low Cr content exhibits superior high temperature mechanical properties. However, due to the relatively low Cr content, their corrosion resistances under supercritical water (SCW) conditions are generally poor. High-Cr alloys, despite their much improved corrosion resistance, often suffer from embitterment due to the precipitation of sigma phase in the microstructure. In this study, corrosion resistance of an in-house produced high Cr steel (25%Cr) showed much better corrosion resistance compared to that of low Cr alloy (14%Cr). This high-Cr steel can potentially be used as a corrosion-resistant coating for structural materials in sew applications.INTRODUCTIONThe supercritical water-cooled reactor (SCWR) concept is one of the promising designs for the next generation nuclear reactor, in which the water coolant is designed to be at about 625°C and 25 MPa at the outlet of the reactor core. Under these relatively high-temperature and high-pressure conditions, the cooling water is at supercritical state. High-temperature mechanical properties, corrosion resistance and radiation damage are some of the key challenges. At present, no single commercial material can meet all the requirements of the severe SCWR in-core conditions. Canada supports research in several key areas of SCWR development, including materials selection. A major focus is on materials development, selection and evaluation for both in-core and out-of-core components.Allen et. al. [1] carried out a comprehensive study on the SCW corrosion resistance up to 600 °C on commercially available high temperature materials including Ni-based super alloys, various types of stainless steels and ferritic/matensitic steels. They concluded that ferritic steels develop a relatively thick but mechanically stable oxide layer, while austenitic alloys develop a thinner oxide layer that has been found to spall in some cases. Of the three types of alloys examined, the Ni-based alloys exhibited the lowest oxide thickness, however pitting was observed in the vicinity of intermetallic precipitates."

Jan 1, 2011

By R J. Singh, E. Z. Chacko, Devilal, S. K. Jha, Rina Sahu, Sheshank Shekhar

"Breakouts are one of the biggest problems encountered during continuous casting of steel billets. Billets get cracked locally or break completely in two parts during solidification causing the liquid part of the partially solidified billet to empty inside the cooling chamber. Proper control of important parameters is necessary to avoid break outs during continuous casting. In the present work, the nature of the break outs at a billet caster at Tata Steel was studied. Data analysis was also done for certain casting parameters and the Sulphur tracer test was conducted to understand solidification in the mould. It was found that to reduce the occurrence of break outs, it was necessary to tune the operations based on the grade being cast and the design of the mould tube being used.IntroductionA break out during the continuous casting process is a rupture of the partially solidified shell inside the secondary cooling chamber, causing the contained liquid steel to spill out. In the mid 1970s while continuous casting technology was still in early stage of development, causes of breakouts was not well understood. Today, with technological development much has been understood about breakouts but, most of the understanding has been in the slab casting process wherein due to the higher level of instrumentation, a lot of information has been gained. In billet casting however, due to the geometry of the mould housing with the tube mould, multiplied by the complexity of the multiple strands, instrumentation has not been used and obtaining data for analysis has been difficult.Breakouts at billet casters are still the main hindrances to production. A break out results in a loss in production since the strand which has had a break out is now not available to produce and thus a six strand caster would be reduced to a five strand caster, increasing the time for casting the same tonnage. Additionally extra set up time is required as more often than not a mould change is required in order to have the strand casting again."

Jan 1, 2014

By Mark Samonds

"Manufacturing processes which involve liquid to solid and solid state transformations in metals encompass a wide variety of physical phenomena. The past twenty years have seen a steady evolution in the complexity and scope of numerical models of these processes, beginning with thermal analyses without phase change. Recently, a few software packages have become available which have true multi-physics capabilities. This permits the treatment of thermal, fluids, stress, electromagnetic, chemical reaction and microstructure development aspects altogether in a fully coupled simulation. This paper will consider various aspects of these types of models.Coupled thermal and fluid flow analyses of continuous castings have been around for fifteen years. Coupled thermal and free surface fluid flow simulations of shape castings have been available for ten years, including view factor radiation models for investment castings. Only recently, however, have fully coupled thermal, fluid, and stress analyses become practical. This implies the reverse coupling of the mechanical deformations to the solution of the energy and momentum equations through modification to the interface heat transfer coefficients and the fluid domain geometry. This has been implemented with a combined eulerian-lagrangian finite element method. Appropriate mechanical constitutive models will also be discussed.Many types of defects need to be predicted in casting processes. Those related to stress include hot tearing, hot cracking, part distortion, and thermal fatigue in dies. Macroporosity, microporosity, and microsegregation are determined by the solidification behavior and microstructure development in a casting. In particular, microporosity is influenced by dissolved gases, the morphology of the mushy zone, the liquid to solid density change, and the local pressure conditions. Macrosegregation is caused by the partitioning of solutes during. solidification and subsequent thermo-solutal convection. An additional transport equation is required for each solute that is being tracked. Computational thermodynamics is being incorporated into these types of analyses to determine transformation temperatures, partition coefficients, densities, and enthalpies. In combination, the microstructure and microporosity models can frequently predict a variety of mechanical models, such as yield strength, tensile strength, and elongation."

Jan 1, 2001

By Isabela Leao Amaral da Silva, Alice Barreto Bevitori, Frederico Muylaert Margem, Victor Bastos da Silva, Sergio Neves Monteiro, Artur Camposo Pereira

"The jute fiber is one of the most rigid natural lignocellulosic fibers, which has since the last decade been investigated as possible reinforcement for polymeric composites. In the present work, the tensile properties of DGEBA/TETA epoxy composites reinforced with jute fibers with different diameters were investigated. Composites with volume fractions up to 30% of continuous and aligned jute fibers were tensile tested at room temperature to evaluate the ultimate strength, elastic modulus and total strain. For each volume fraction, separated fibers with smaller larger diameters were tested. The results indicated that the tensile properties tend to improve with increasing volume fraction of the thinnest jute fibers. The role played by the fiber/matrix interaction was analyzed by scanning electron microscopy.IntroductionThe interest of this research is to develop composites with epoxy resin matrix reinforced with continuous and aligned jute fibers, for applications in various industries, including construction and automotive industry. Conflicts related to the use of non-renewable forms of energy are increasing the interest to enter the market to replace natural materials, synthetic materials synthetics have a higher power consumption in its manufacture [ 1-4].Therefore, applications of natural lignocellulosic fibers obtained from cellulose-based plants are receiving increased attention as an alternative to replace more environmentally correct nonrecyclable materials, energy intensive and glass fiber composites in [5-6]. The use of composites reinforced with natural fibers is a reflection of the concerns with environmental issues such as pollution caused by waste that is not biodegradable or cannot be incinerated and climate change due to C02 emissions associated with the processes of intensive energy and also motivates this work to develop self-sustaining, since natural fibers generate a source of income, especially in developing countries, where most originate, encouraging the cultivation of non-food agriculture [7-9]. Additionally, it is worth also remembering that these fibers come from renewable sources, in addition to being abundant, inexpensive and have a relevant set of mechanical properties [10]."

Jan 1, 2013

By Camila Martini Matos, Maria das Graças da Silva Valenzuela, Francisco Rolando Valenzuela Diaz, Lucy Gomes de Sant' Anna, Orley de Oliveira Magalhães, Flavio M. S. Carvalho, Isaac Jamil Sayeg

"Kaolin clays are widely used in various industry segments. Its main properties are fine granulometry, chemical inertness and whiteness. In general, kaolins are not easily organophiilized as a result of its 1: 1 structure. The aim of this paper is to describe the modification of a Brazilian kaolin sample, in order to obtain an organophilic kaolin of high performance. The clay as received was identified by X-ray diffraction and characterized by optical microscopy, cation exchange capacity and swelling tests for observation of their performance in water and organic solvents. Then, the sample was treated with a 10% sodium carbonate solution and with ammonium quaternary, washed several times with distilled water, dried at 60°C, and characterized by XRD and swelling assays. Our results show that the clay was organophiilized and its ability to swell in organic solvents has increased.IntroductionThe kaolin clay, also known as ""china clay"" is chemically a hydrated aluminum silicate characterized as a very fine powder and lamellar structure (1:1), being constituted mainly by kaolinite [l]. Kaolin is a mineral extremely used as raw material. Its properties such as color, softness, small particle size and chemical inertness make it a suitable material for several industrial applications. The desired properties of kaolin varies widely for each application, beginning with its largest use in the paper industry until minor uses in the sectors of cosmetics and pharmaceutics. These two last applications require purified kaolin with defined functionality [2]. To find improvements in the functionality of kaolin for specific applications is important for many industrial uses. Sometimes the way to find these improvements might be modification of the kaolin clay by treatment with a chemical substance as ammonium quaternary, causing surface modifications [3,4]. In this work is described the modification of a Brazilian kaolin sample by treatment with cetyl trimethylammonium chloride (CTAC). The properties of the modified kaolin are being assessed by characterization and essays to understand its functionality and industrial application."

Jan 1, 2013

By Mala Nath, Atjit Mallick, Asheesh Kumar

"The present research work is aimed to focus on the development of chemically stable light weight microporous carbonaceous material, such as activated charcoal incorporated either with titanium n-butoxide, titanium diisopropoxide bis(2,4-pentanedionate), vanadium 2,4-pentane-dionate or zinc 2,4-pentanedionate having varying wt% of the metal (2-8%) using ethanol as solvent at 40--50 oC followed by calcinations at 100, 150 and 200 cC, except the samples with titanium diisopropoxide bis(2,4-pentanedionate) which are calcinated at 80 oC. Atomic absorption studies along with FESEM revealed that the maximum incorporation of metals (Zn, V and Ti) in activated charcoal was observed with 4 wt% of zinc 2,4-pentanedionate calcinated at 150 oC , 4 wt% of vanadium 2,4-pentanedionate at 100 oC, 2 wt% of titanium n-butoxide at 100 oC and 2 wt% of titanium diisopropoxide bis(2,4-pentanedionate) at 80 oC, and equilibration time of 20-24 h was used in each case. Hydrogen sorption behavior in these carbonaceous materials has also been studied at 77.4 K and low pressure up to I bar. The highest hydrogen uptake obtained was 1.45 wt% (164.5 cm3 (STP)/g at P/Po = 1.0) for activated charcoal incorporated with 4 wt% of zinc 2,4-pentanedionate calcinated at 150 oC.IntroductionTwo of the major challenges for humanity in the next twenty years are the shrinking availability of fossil fuels, the global warming and potential climate changes that result from their ever-increasing use. So it is necessary to fmd an energy source that is convenient, flexible and controllable. One possible solution to these problems is to use an energy carrier such as hydrogen, and ways to produce and store hydrogen in electric power plants and vehicles. Hydrogen storage is the bottleneck for the breakthrough of hydrogen as energy carrier in automotive applications [1]."

Jan 1, 2012

By Akram Alfantzai, Farzad Mohammadi, Maysam Mohammadi

"Degradation of lead anodes has always been a major concern among the electrowinning industries. In this study, the effect of agitation of the zinc electrowinning solution on the integrity of lead anodes was investigated. Galvanostatic experiments were performed at 37±0.5°C using 0,600 and l000rpm magnetic stirring rates for 24 hours. The Pb02 layer formed on the anode surface was reduced to PbS04 (discharged). The discharge information was used to calculate the amount of Pb02 present on the surface. Weight loss measurements along with the discharge calculations revealed that the degradation rate of the lead anode increased as the solution was stirred more vigorously. Furthermore, the amount of remaining Pb02 on the surfaces was decreased as a function of solution velocity. Therefore, it may be concluded that, degradation rate oflead anodes is controlled by detachment of the corrosion products from the surface rather than by electrochemical reactions. IntroductionElectrowinning is one of the extraction stages of zinc, in which pure zinc is deposited from acidic solution after froth flotation, roasting and leaching processes. The anode electrode materials play important roles in the electrowinning process. Their electrocatalytical capacities determine the oxygen evolution overpotential, and consequently the cell potential and energy efficiency of the zinc electrodeposition [l]. Purity of the zinc deposited on the cathode is affected by the solubility and corrosion resistance of the anode materials. Using insoluble materials as anode in the electrowinning leads to the higher purity of the deposited metal on the cathode[2]. Lead (Pb) and its alloys have been used as the anode in the zinc electrowinning because of its special properties such as relatively low cost, low melting point, insolubility in solutions containing sulphuric acid and high conductivity in both states of metallic and oxidized [3, 4]. In zinc electrowinnig, zinc reduction occurs on the cathode (reaction 1) and the oxygen evolution reaction (OER) (reaction 2) is the main anodic reaction [5, 6]."

Jan 1, 2013

By Xinli Wang, Matthew Andriese, Jiann-Yang Hwang, Zhiwei Peng, Byoung-Gon Kim

"The microwave dielectric properties of silicon dioxide at frequencies of 915 and 2450 MHz were characterized in the temperature range of 24 to approximately 1000 °C using the cavity perturbation technique. It is shown that the relative dielectric constant of silicon dioxide at both frequencies remains almost unchanged below 500 °C, above which there is a slight increase of 2%. The relative dielectric loss factor of silicon dioxide exhibits a strong temperature dependence above 500 °C and increases by approximately 7 and 5 times at 915 and 2450 MHz, respectively. The substantial increase in the relative dielectric loss factor is mainly attributed to the enhanced dielectric polarization and accelerated electrical transport in silicon dioxide at elevated temperatures.IntroductionSilicon dioxide (Si02) is usually considered a microwave transparent material due to its poor absorption capability at room temperature [1]. This characteristic has led to various applications of silicon dioxide in microwave processing of materials and communication. For instance, Si02 has been used to produce sample holders for microwave heating and substrates for electronic devices [2,3]. These applications generally require the material to withstand high temperatures under microwave irradiation. This indicates that microwave absorption capabilities of silicon dioxide at elevated temperatures are also important for its utilization.The microwave absorption capability of Si02 can be determined based on dielectric characterization (permittivity measurement) of the material at commonly used microwave frequencies, 915 and 2450 MHz, in a broad temperature range. To date, however, no detailed work on the dielectric properties (permittivity) of silicon dioxide at high temperatures has been reported. The present work is aimed to study the dielectric properties of silicon dioxide from room temperature to approximately 1000 °C at 915 and 2450 MHz. The results show that the permittivity of silicon dioxide has a strong temperature dependence above 500 °C, suggesting a substantial increase in its microwave absorption capability."

Jan 1, 2013

By C. A. Nogueira, F. Pedrosa, F. Margarido, R. N. G. Guerra

"A hydrometallurgical process for recycling spent Zn-MnO2 batteries was developed, involving leaching with sulfuric acid, purification by precipitation and metals separation for further recovery. Leaching of zinc oxide was easily attained while for manganese oxide was rather difficult depending on temperature and acid concentration. At 90°C and with the liquid/solid ratio of 20 L/kg, more than 95% of zinc is recovered in 30 minutes with 0.5M H2SO4. To attain similar recovery for manganese, higher levels of acid concentration and time are needed (e.g 0.7 M and 2 hours). After leaching a purification step is necessary to remove iron co-dissolved through Fe(III) precipitation. Separation of zinc from manganese by solvent extraction with 1M DEHPA follows in the process route. The countercurrent multistage separation diagram developed allows the production of a zinc electrolyte with 120 g/L Zn and 0.005 g/L Mn, and a raffinate with 16 g/L Mn and 0.013 g/L Zn.IntroductionThe recycling of spent Zn-MnO2 batteries is carried out by dedicated recyclers using several process alternatives [1]. Most of the running processes use pyrometallurgical technologies [2] based on zinc distillation. Alternative treatments by hydrometallurgy have been reported [3-5] but its application is scarce.In order to contribute to the development of alternative solutions, a process for recycling batteries based on Zn-MnO2 systems has been studied. The process is based on the hydrometallurgical treatment of spent batteries in sulfuric acid media (Figure 1). The process starts with the physical processing by shredding using cutting grinders, where the batteries are opened and size reduced, allowing the liberation of the interior electrode particles or pastes. The fines can be then separated and the coarse material containing the steel scrap can be treated to remove the remaining aggregate electrode. The final scrap also contains some plastics and other non-metal materials and can be further valorized."

Jan 1, 2008

By Gjergj Dodbiba, Toyohisa Fujita, Takahiro Kikuchi, I-Chen Wu

"In order to separate molybdenum (Mo) from the high-level radioactive liquid waste (HLLW), Pb-Fe based adsorbents were synthesized. The adsorbents were precipitated by adding sodium hydroxide in mixture of 1 mol/L lead nitrate and 1 mol/L ferric nitrate aqueous solutions. Each precipitate was then filtered, dried and ground to obtain a fine powder, which has been used as an adsorbent. Two main parameters were considered when synthesizing the adsorbents, i.e. the pH value at precipitation of adsorbent precursor and the calcination temperature of Pb-Fe based adsorbent. Moreover, the structures of the synthesized adsorbents were investigated by means of an X-ray diffractometer.The experimental results indicated that the calcination temperature of the Pb-Fe based adsorbent has a great influence on adsorption capacity of the adsorbent for Mo. It was found that when the Pb-Fe based adsorbent was calcinated at 500 oC, the sorbed concentration of Mo was the highest.1. IntroductionThe high-level radioactive liquid waste (HLLW), arising from the reprocessing of nuclear fuel are generally immobilized in an alkali borosilicate glass matrix. Broadly speaking, alkali borosilicate glasses are the matrix of choice for the immobilization of the HLLW, since they permit vitrification of waste stream of variable composition, [1]. Within this frame, the incorporation of molybdenum (Mo) is of particular interest in the vitrification of HLLW. Molybdenum is know to have a low solubility in borosilicate glass compositions and its presence in excess results in the phase separation of a complex yellow molten salt during vitrification, [1]. The formation of so-called “yellow phase” material during the vitrification process is undesirable since it leads to the accelerated corrosion of the inconel crucible liners. Furthermore, the “yellow phase”, which is reported to contain also other fission products, is soluble in aqueous solution providing a potential route for the leaching of radionuclides from the vitrified waste, should it come into contact with water, [1]."

Jan 1, 2008

By Andrew Shabalin, Vladimir Skorohodov, Svetlana Babaeva, ?lga Makovskaya

"At processing of some kinds of wastes (electronic scrap, secondary materials, spent nuclear fuel) in nitric acid solutions, and also in technology of silver refining, the significant amounts of palladium and platinum passes into a solution. The ion-exchange concentration of palladium and platinum in nitric acid solutions (5-500/dm3) are investigated. More than 30 various classes of ionites are tested. The most chemically resistance resins at the given conditions are identified. It is shown, that the maximum sorptive capacity to studied metals at high acidity the complexing, synthetic and inorganic sorbents possess. To definition of platinum metals sorption optimum conditions the kinetics is studied, isotherms of a sorption at various parameters from nitrate solutions are obtained. The conditions of the platinum and a palladium desorption from the pregnant sorbents and its regeneration with the subsequent reuse of materials were defined. The raw materials containing precious metals have very diverse composition and physical properties. Commonly the materials are processed by hydrometallurgical way. If gold or PGMs there are in raw materials to its opening hydrochloric acid solutions are applied. As an oxidizer nitric acid, hydrogen peroxide, gaseous chlorine, etc are used. Nevertheless, at processing of argentiferous materials and preliminary treatment of a waste including the spent nuclear fuel, nitric acid solutions are often used and the specified metals in some extent pass into solution [1]. Therefore selective extraction of PGMs from nitrate solutions is an actual problem. In the present work the ion-exchange concentrations of palladium and platinum in nitric acid solutions (5-500 g/dm3) are investigated. At the testing more than 30 various classes of ionites the most chemically resistance resins at the given conditions are identified. These resins are synthesized on the base of polyacrylate, styrene-divinylbenzene and vinylpyridine. For a selection of the most effective resin among what are made in Russia and overseas, a number of ionites with various functional groups were studied. Influence of functional groups type on a PGM sorption is shown for extraction of a palladium as an example (table 1). The presented data shows, that palladium concentration in a phase of ionites depends on sorbent type. If the increasing of solution acidity essentially reduces palladium sorption by sulfonic cation-exchange resins (KU-2×8) than its sorption by strongly basic anionites is approximately equal. Intermediate position is occupied by complexing sorbents. The latter (AN-31, SN-3, ANKB-35, Lewatit TP 207, Purolite S 930) are the most effective for extraction of PGMs from nitrate solutions from the point of view of capacity value. According to [2], solution behavior of Pt (II) and Pd (II) are similar. As is known from coordination chemistry, ligand environment of the metal ions substantially impacts to character of electronic spectra. The figure 1 shows the results of measurements of optical density of platinum bearing solutions with various concentration of nitric acid at ?=400 nanometers"

Jan 1, 2008

By Rajesh K. Mishra

In secondary precious metals refining, the feed to the plant itself is a waste generated in manufacturing processes. Constant changes in manufacturing processes produce ever changing feed materials to the secondary PGM (platinum Group Metals) refineries. After extracting the precious metals, secondary wastes are generated. The discharge of effluent is dictated by both the PGM losses in wastes and the regulatory mandates. This paper will discuss some. of the conventional as well as some newer approaches to face both the challenges.

Jan 1, 1995

By Linping Yu

A simplified ED process was developed for organic acids recovery from cyclohexanone waste in this paper. In this regard, the one-stage ED was investigated directly without pretreatment, such as ion-exchange or nanofiltration to removal of foulants. The current efficiency and the energy consumption in the ED process for the recovery of carboxylic acids from cyclohexanone waste is theoretically analyzed and experimentally tested. The concentration of recovered carboxylic acid is related to many parameters and still needs more work to be determined.

Jan 1, 2009

By Kurt Westerlund

Cooling of hot sticky gases with solids in a circulating fluidized bed called FLUXFLOW is described. Fluxflow is used for gas streams from metallurgical reactors, e.g., Isasmelt copper in Australia and TBRC for lead in Sweden. The features and potential of this technology in metallurgy and waste treatment ie described. The FluxfLow la a new, cost efficient high availability solution to treat hot sticky gases that has made new gas handling and heat recovery flow sheets available to the process industry.

Jan 1, 1994

By Natasa Mitevska

The distribution coefficients of Ag, As, Au, Bi, Co, Cu, Ni, Pb, Sb, Se, Te, and Zn between copper matte and slag from the reverb furnace No.2 at the Copper Smelter and Refinery, RTB BOR (Yugoslavia), are presented in this paper. The influence of the matte grade on the minor elements distribution coefficients between copper matte and slag is analyzed. The minor elements distribution in the slag phase along the slag melt depth and the furnace length is also determined.

Jan 1, 2002

By H. P. Wang, E. M. Perry

"Analytical solutions for investigating the solidification of casting problems with initial superheat and natural boundary conditions have been derived using an integral method. There are two moving interfaces in the solution field, one for the phase change line and the other for the superheat line. Two coupled nonlinear differential equations, representing two moving layers, were calculated by the Runge-Kutta numerical integration scheme. The solutions are in terms of six dimensionless parameters: phase change number, two Biot numbers for interfaces, diffusivity ratio, and dimensionless superheat temperature and time. Parametric studies on these parameters have been conducted to provide generic information about this phase change problem. This analytical information is extremely useful for validating numerical solutions. A simplified I-D finite element model was constructed for the purpose of comparison. The excellent agreement between the analytical and finite element solutions has proven that they are mutually validated.This validated finite element modeling tool was then used for modeling an investment casting process of a super-alloy with a simple geometry: a two-step plate. The nonlinear latent heat release, a common property of alloy materials, was approximated by several piecewise linear segments. The transient temperature response of this 2-D finite element solution, including a metal/mold gap resistance, shows excellent agreement with experimental data.This fundamental work provides a solid basis for further work on the development of a process modeling tool for the complex investment casting process.IntroductionAt present, the investment casting process is used in a variety of industries. In the aircraft engine industry, in particular, investment casting is used to produce parts ranging from turbine blades to engine frames. Because a large single casting can replace many component parts that require machining, fabrication, and assembly, this one-piece casting approach becomes a very cost-effective manufacturing process.The main constraint in using this process for mass production is the long design-to-production lead time. The standard rigging design is still an art, based on the experience of casting experts, rather than on scientific methods. Many trials are often required before making a sound final casting. In order to .reduce the number of expensive casting trials, the development of computer-aided tooling technology is needed.The fundamental physics describing this manufacturing process can be simply described. They reduce to a solid/liquid phase change problem, with two parts - first, the thermal balance of the initial superheat temperature of the molten metal and the preheat temperature of the ceramic shell through heat conduction, and second, the energy release from the mold surface to the ambient by radiation."

Jan 1, 1986

By Philip Thompson

"Carefully planned laboratory test programs provide valuable data regarding the amenability of low grade gold ores to heap leaching. The most common laboratory test is the column leach test. The overwhelming problem associated with this type of test is the limit on the test column height. Most laboratories use a three (3) meter (10 foot) high column as a standard test due to building ceiling limitations, sample size limitations, etc. This paper presents a case study in which an ore sample was tested in a 1.5 meter, a three meter, and a six meter high column to determine the effect of column height on the test results. Other important factors such as sample preparation protocol, preliminary bottle roll testing to determine appropriate crush size, column diameter requirements, and leach solution analyses, are also discussed.IntroductionColumn leach testing has been used for years by many laboratories to determine the amenability of low grade precious metals bearing ores to heap leaching. However, the test work can be compromised by poor planning, misinterpretation of results, and extrapolation of data beyond the reasonable boundaries of the experiment. Preliminary test work should be performed prior to column testing. This preliminary work provides valuable information regarding the response of the ore to cyanidation and aids in the design of the column tests.The sample should be screened into various size fractions prior to testing. The fractions are assayed to determine the gold content of each size fraction and of the overall sample. The most valuable preliminary test is the bottle roll cyanidation test which is usually performed on five kilograms of coarse sample in a large rolling bottle which can accept material up to 50 millimeters top size. The residue from this test is screened at different sizes to determine the distribution of unleached gold in the residue. Comparison of the gold distribution in the leach residue with the distribution of gold in the feed at the same size intervals provides an indication of the appropriate crush size for the sample. The overall gold extraction from the sample at the crush size tested is also determined from these data. Lime and cyanide requirements can also be estimated from this test. The viscosity of the bottle roll pulp and the size distribution of the feed and leach residue can also suggest whether agglomeration of the ore will be required prior to column testing. Ores which contain significant amounts of clays (greater than 5 percent) will generally require agglomeration to prevent plugging of the test column."

Jan 1, 1997

By Thomas F. Hagelien, Stein Tore Johansen, Svend Graadahl

"The dross appearing at the surface of an aluminium melt consists, in addition to aluminium, of mainly oxide films but also other non metallic inclusions. The inclusion particles are often poorly wetted by the metal and accumulate at the metal surface. However, in impeller stirred reactors for melt refining stirring may be exceedingly strong and inclusions accumulated at the metal surface may be entrained into the bulk metal. Concerning inclusion removal, such effects may deteriorate the effectiveness of melt refining.In this paper we investigate the surface entrainment of buoyant particles in a water model of an impeller stirred refining reactor. Under varying operating conditions the particle concentration in the bulk liquid is measured by laser light attenuation. The observed entrainment of particles is explained theoretically and metallurgical consequences of the findings are discussed.IntroductionIn the modern cast house continuos metal refining and casting is well established. One of the most distinct advances in metal refining has been the introduction of degassers which introduce bubbles into the metal. The bubbles act to remove dissolved elements together with nonmetallic inclusions. In the most efficient degassers stirring by different kind of rotors is applied to increase mass transfer and inclusion removal. However, it has been known from experience in the cast house that for violent stirring the concentration of some types of inclusions may increase from inlet to outlet of the reactor. This phenomenon has so far been attributed to production of dross in the reactor due to oxidation of metal. Due to removal of inclusions by bubbles the dross layer inside the reactor must be expected to increase in thickness by time. The removed inclusions and produced oxides due to strong stirring is removed at regular interval by the operators of the degasser. However, a fundamental understanding of the phenomena which take place in and below the dross layer is lacking. In the present work we add buoyant particles to the surface of a refining reactor and investigate how these particles may be entrained and dispersed into the liquid depending on the flow conditions. Similar investigations for gas stirred ladles have been performed by Taniguchi et al [1] who found that below a critical gas flow rate all particles are trapped at the surface. Above the critical gas flowrate the surface velocity are sufficiently high to entrain the particles. In this situation it looks like all particles are ready for the melt and a balance between terminal velocity and turbulent dispersion determine the concentration in the liquid."

Jan 1, 1999

By Kunihiko Takeda, Kimio Imaizumi, Tsuyoshi Arai

"The study on the preparation of mono-dispersed liquid droplet was performed using ultrasonic as one of the steps of producing the perfectly mono-dispersed particle. The ultrasonic system was a 33.6kHz ultrasonic generator, an amplifier, an electric distortion element, and a bolted Langevin type horn installed in .a cell. For the first time, a liquid pillar under a nozzle of the cell ·was stably formed. Then, dense and coarse parts were alternatively constructed by oscillating the wavelength of the ultrasonic.· The diameter of those liquid droplets were found to be· perfectly uniform, therefore, it was measured by ""multiplex photography"" using a synchronized stroboscope with the ultrasonic.- From the results, more than 30,000 of perfectly uniform liquid droplets in 1 second were observed by this method.IntroductionRecently, research on the control of physical form is done in various fields of industry. Some examples are the processing technology of the minute compound material of micro-machines and integrated circuits, and the form control of molecule size like catalysts. There is a need for such material to take on various forms in correspondence to its use. ""Form control"" as used in this study will indicate ""research on physical chemistry factors which determine the size of the material"" and will refer to the contour uniformity of comparatively little particles. A well-known method of preparing particles is to spout a mist of liquid and slurry from a nozzle l) 2). Particles for metals, catalysts and food have been prepared by this method. In this case, although an approximate particle diameter can be decided by controlling the nozzle diameter and the violent outflow velocity, it is not easy to completely control ·the contour and to prepare a particle with uniform diameter. ·However, the preparation of perfectly uniform particles is necessary for solders for the adhesion of electronic wiring 3), ion exchange resins4), catalysts and so on. Large quantities of fine particles and super-fine particles are generated when manufactured in the usual way. Large quantities of these fine· particles and super-fine particles have polluted the internal and external' environments of factories. The products yield' ·decreases, also. From such a background, this study examines the preparation of perfectly uniform particles that could be· collected -100% as products. Recently, NASA has succeeded in the preparation of perfectly uniform particles in zero gravity 5). But the preparation of 'perfectly uniform particles by this method is difficult, and it can not be used in general industry"

Jan 1, 2000