By A. Onozaki

The Iijima Refinery was put into operation in 1972 and today has an annual production capacity of 156,000 tons of SHG electrolytic zinc. At the Iijima Refinery, the recoveries of gold and silver are 98.0% and 98.2%, respectively. Gold contained originally in the zinc concentrates reports in the Cu-Pb-Ag residue produced in the residue treatment process. Silver contained in the concentrates is distributed between the Cu-Pb~Ag residue and the copper cake produced in the purification process. The Cu-Pb-Ag residue, which contains gold and silver, is sent to the Oyachi flotatfon plant of the Kosaka Smelter; about 82% of the gold and about 85% of the silver are recovered in the copper flotation concentrate.. In this paper, the distribution of gold and silver in the Iijima. Refinery is discussed and operational results of the Oyachi flotation plant are presented.

Jan 1, 1990

By Kazuyoshi Shimakage, Shinji Hirai, Kenji Wada

"An amorphous zirconium oxide coating was prepared by the sol-gel process using zirconium tetra-n-butoxide on the surface of aluminum to improve the corrosion resistance to salt, acid and alkaline attacks. The coating films formed on the smooth aluminum substrates under UV-irradiation indicated an excellent corrosion resistance for salt, acid and alkaline attack tests. For example, the corroded area of coating film in salt attack test for 3600ks in the order of sol-gel coating· film< chromate film <boehmite film, and the sol-gel coating film had the best corrosion resistance. The coating film prepared on the coarse aluminum substrate by a boiling treatment after heat treatment at 573K also had greater corrosion resistance, and a water-avid surface appeared a contact angle of approximately 3°.IntroductionAs given in a previous paper1; a composite film consisting of a porous layer of anodically grown aluminum oxide filled with amorphous zirconium oxide and an amorphous zirconium oxide coating layer deposited thereon via the sol-gel process utilizing the dip-coating technique, was prepared to improve the alkaline corrosion resistance of aluminum. The alkaline corrosion resistance of these composite films was increased in the range of 24 to 50 times those of conventional anodic oxide films anodized in sulfuric acid. As a result, it was proved that heat treatment at 573K after dip-coating was an important process to .remove organic component from gel film and to accelerate the densification of coating layer. Furthermore, the effect of ultraviolet (UV) irradiation at ambient temperature on the densification of coating layer was also examined to lower the heat-treatment temperature2.Then, a sol-gel film prepared by UV irradiation at ambient temperature indicated that alkaline corrosion resistance of aluminum was superior in the range of 2.4 times to 2. 6 times that of the conventional composite film heated at 573K."

Jan 1, 2000

By Lev Levin, Sergei Lesokhin

"The formation of titanium carbide during hot filament assisted carburizing of NiTi alloy was investigated. Phase content and morphology of the diffusion zone were examined by X-ray diffraction, X-ray microanalysis, SEM, and Auger electron spectroscopy. The growth of stable and adherent TiC film was observed. A non-planarity of interphase boundary was noticed. The applicability of the chemical diffusion approach to the analysis of the experimentally observed interface instability is discussed. A criterion, taking into account the influence of growth stresses on the stability of the flat interface, is developed by means of linear perturbation analysis.Introduction.Equiatomic intermetallic NiTi belongs to a class of materials exhibiting the shape-memory effect. The unusual property of this compound promotes its application in many fields, from aerospace technologies to medicine. The relatively high ductility ofNiTi also permits its use as a matrix material in metal-ceramic composites. The objective of this work was to investigate the possible incorporation of a ceramic material (titanium carbide) into NiTi by gas carburizing.Free energy calculations indicate the potential to obtain TiC by carburizing Ni-Ti binary phases. The main obstacle to such a process is the high affinity of titanium to oxygen. At moderate temperatures the formation of TiC is preferable to titanium oxidation only if the partial pressure of oxygen is extremely low [1]. This problem was overcome in this work by the use of hot filament assisted gas carburizing. Due to chemical reactions occurring near the hot filament, the gas mixture, initially consisting of methane and molecular hydrogen, was enriched by atomic hydrogen [2], drastically decreasing the content of free oxygen in the carburizing atmosphere.The second part of this article concerns the theoretical analysis of reasons that lead to the development of the experimentally observed morphology of the diffusion zone. In particular, the influence of the growth stresses on the morphology of an interphase boundary is investigated."

Jan 1, 1996

By B. Abedian, L. M. Racz, S. R. Berry, R. W. Hyers

"The presented work represents an effort to improve understanding and prediction of turbulent flow inside electromagnetically-levitated droplets. We show that the flow field in a test case, a nickel droplet levitated under microgravity conditions, is a low Reynolds number turbulent flow, i.e. in the transitional regime between laminar and turbulent. Past research efforts have used laminar, enhanced viscosity, and k - E turbulence models to describe these flows. In our study, we compare the RNG algorithm to laminar and k - E turbulence model results. We show that accurate description of the turbulent eddy viscosity µr is critical in order to obtain realistic velocity fields, and that µr cannot be uniform in levitated droplets. In the RNG method there are no characteristic length or time scales associated with the flow, thus allowing such anisotropic features to be captured. We perform calculations and analyses for two cases (1) a small, non-deforming, spherical nickel droplet and (2) a deforming, oscillating droplet. In addition to flow field calculations, we compare numerically-obtained surface tension and viscosity values to those obtained experimentally by the oscillating drop technique.IntroductionElectromagnetic levitation (EML) is a containerless processing technique for conductive materials. Its advantages are the avoidance of contamination or chemical reaction at container walls and the ability to perform long-term experiments in a metastable state. Because of its current limitation to small sample sizes, its primary use is in the laboratory. One application of interest is the measurement of thermophysical properties of undercooled liquid metals [1, 2, 3, 4]. In EML, a sample weighing approximately 1 gram is positioned inside an electromagnetic field generated by alternating currents flowing through an axisymmetric water-cooled copper coil. The coil must be designed appropriately so that thesample levitates in a stable manner.Traditionally, mathematical modeling has been performed in tandem with both earth-and spacebound electromagnetic levitation experiments, in order to determine the effect of the magnetic field on material and flow characteristics [5, 6, 7, 8]. These calculations are important because they allow design, planning, and correct interpretation of experiments. In addition, the calculations are of fundamental scientific interest, as they can be applied to other electromagnetic materials processing applications [9]."

Jan 1, 1999

By Jean-Pierre Birat, Ana-Maria Iosif, Denis Ablitzer, Olivier Mirgaux

"Integrating environmental considerations into the product traditional process design is now the major challenge for steel industry. Life Cycle Assessment (LCA) is nowadays considered as an appropriate method for assessing environmental impact and selecting new technologies to reduce CO2 emissions for steel industry.In this paper we propose a new methodological concept which combines LCA thinking with process simulation software in order to carry out the life cycle inventory of classical steelmaking process.Using Aspen PlusTM software, a physicochemical model has been developed for the integrated steelmaking route. This model gives the possibility to carry out life cycle inventories for different operational practices in order to optimise the use of energy, to calculate CO2 and other emissions and to control the mass and the heat balances of processes.It is also shown that such approach can be used to design and assess new technologies for steelmaking without large industrial application.IntroductionDuring recent years, it was recognised that CO2 emissions are the major factor of the global warming effect. In order to meet Kyoto requirements, the steel industry is embracing the challenge of sustainable development by improving its competitiveness and economic success while reducing its environmental impacts. Integrating environmental considerations into the traditional product design process, for powerful eco-efficiency, is now one of the major priorities for steelmakers.The European Steel Industry has measured up to this challenge by creating ULCOS (Ultra Low CO2 Steelmaking) consortium that has taken up the mission to develop breakthrough steelmaking process with the potential to reduce CO2 emissions (Eurofer, 2005). In order to develop technologies to reduce emissions, it is necessary to assess the environmental impact of the classical steelmaking route (coke plant, sinter plant, blast furnace, basic oxygen furnace, continuous casting and hot rolling)."

Jan 1, 2009

By S. P. Vanka, B. G. Thomas, S. Sivaramakrishnan

"During the continuous casting of steel, transient 'flow events can be very important to the generation of quality problems, such as shear entrainment, surface level fluctuations and bubble entrainment. These phenomena can be better predicted using Large Eddy Simulation (LES) models than the K-E models, which have been extensively studied. In this work the turbulent transient flow in a water model of a continuous caster has been both simulated using LES models and measured using Particle Image Velocimetry (PIV). The results of PIV and LES have been compared to validate the LES model and also to enhance the understanding of the prominent transient features of the flow field. The flow near the top surface in PIV was found to contain periods of 5-1 Os when the velocities were three to four times their mean values, which is of importance to the shear entrainment of the liquid flux. In both simulation and PIV the upper roll structure is found to change chaotically from a single large recirculation structure to a set of distinct vortices. The inlet swirl in PIV is seen to persist more than halfway across the mold, causing a characteristic staircase velocity vector pattern when viewed in a plane parallel to the wide faces. The lower rolls in PIV are significantly asymmetric for very long periods of time (- I-hour) and go through a repeating sequence of features. One of these features involving a short circuit between the upward and downward flow in the lower roll is also seen in the simulation and is of significance to bubble entrapment.IntroductionThe turbulent flow through the nozzle and in the mold of the continuous caster has been studied extensively using computational Reynolds Averaged Navier Stokes (RANS) models of turbulent flow [1,2]. Defects, such as internal inclusion of liquid fl4x through surface shear, pencil pipe defects due to bubble entrapment, surface defects due to level fluctuations are caused by transient flow phenomena oc'curring in the mold. These phenomena can be better predicted using transient Large Eddy Simulation [3] or ""LES"" models."

Jan 1, 2000

By Markus Aspiala, Fiseha Tesfaye, Pekka Taskinen

In this paper, the standard thermodynamic properties of Ag3Sb and Ag6Sb intermetallic compounds have been studied by the solid state EMF-method, using Ag+ ion conducting β- alumina and AgI. The intermetallic compounds were synthesized from pure substances in evacuated silica ampoules and their formation were confirmed by the SEM-EDS analyses. The EMF measurements were made on electrochemical cells of the type [Ag | β-alumina | Ag-Sb] and [Ag | AgI | Ag-Sb]. The usage of β-alumina electrolyte, in this study, enabled thermodynamic measurements of the Ag-Sb-intermetallic compounds above 710 K, hitherto unreported. Based on the new experimental data, thermodynamic properties of the Ag-Sb-intermetallic compounds have been determined. The obtained experimental values have been compared with the available literature data.

Jan 1, 2015

By Takashi Fujii

In the OG (Osaka Gas) process which includes a fusion process of sewage disposal sludge in coke bed knowledge of molten and fluid properties of the sludge are most important to controll the process in good condition. Thus, the softening and melting temperatures and viscosity were measured by the sessile drop technique and a rotating viscometer. Obtained results are summarized as follows: Melting character of sludge slag is varied according to their composition, but closely related to CaO/SiO2 ratio in ordinary sludge and to CaO/(Cr2O3,+Al2O3+P2O5) ratio in Cr2O3 containing sludge. Fluid property of sludge slag has a correlation with optical basicity or Riboud parameter, However, the correlation is poorer than that of metallurgical slags. Especially, chromium oxide containing sludge shows high viscosity and behaves somewhat different manner from ordinary sludge.

Jan 1, 1992

By Kuniaki Murase, Tetsuji Hirato, Yasuhiro Awakura

"Electrodeposition of CdTe was studied using aqueous ammonia-alkaline electrolytic baths in which Cd11-and Te1V-ions are dissolving as Cd11(NH3)/+ and Te1vol-ions, respectively. Ca-thodic polarization curves of the baths suggest the presence of strong interaction between the Cd11-and Te1V-ions; electrodeposition of tellurium is inhibited by the presence of Cd(NH3)/+ ions. The interaction makes it possible to electrodeposit CdTe films with stoichiometric composition. Polycrystalline CdTe thin film of about 1 µm thickness was electrodeposited at 343 K from ammonia-alkaline solutions (pH= 10.7) containing TeO32-(<20 mmol dm-3) and Cd(NH3)/+ ( < 60 mmol dm-3) ions. Increasing Cd(NH3)/42+/TeO32- mole ratio or decreasing total concentration of ammonia/ammonium-ion gave flat and smooth crystalline CdTe deposits at constant cathode potential-0.70 to -0.30 V vs SHE at 343 K.IntroductionCadmium telluride (CdTe) is well-known as a compound semiconductor whose band gap, i.e. 1.44 eV, is suitable for solar energy conversion with a photovoltaic cell. Various methods, such as CVD (chemical vapor deposition) and electrodeposition, of preparing CdTe thin films for solar cells have been investigated.Acidic sulfate solutions with a pH of 1-2 are usually employed for CdTe processing by electrodeposition.1-3) The electrodeposition of compound semiconductors is usually achieved (i) at a higher cathode potential than the redox potential of less-noble species, can in this case, and (ii) under the condition of diffusion-limiting current of a more noble species, Te1Y.4) There-fore, a suitable CdII/TeIV concentration ratio in the acidic electrolytic baths, resulting in the deposition of stoichiometric CdTe, is determined by the diffusion-limiting current density of TeIV- reduction, i.e. the concentration of HTeIVO2+ · Since the solubility ofTe1v species HTeIVO2+ in the acidic solutions is quite low, the rate at which CdTe is deposited from the acidic solutions is extremely slow."

Jan 1, 1998

By D. Morin

A general study of gold refractory arsenopyrite-pyrite concentrate bioleaching has been carried out including two continuous bioleach testworks at different sizes, namely one at a laboratory scale with a 100 I unit at a 2 kg/d dry solid flowrate and the other at a pilot scale at a 100 kg/d dry solid flowrate. Both tests show a 80% bioleaching of arsenopyrite in about four days of treatment and with the same kinetic. Pyrrhotite is attacked at the earlier stage of the bioleaching but pyrite remains unaffected. The weak potential of oxidation associated with the decomposition of arsenopyrite and the abundance of arsenite leads to a high grade of elemental sulfur in the bioresidue which consumes the major part of the cyanide during the gold recovery. Furthermore. the arsenite and ferrous produced in solution have to be oxidized to obtain a stable precipitate in the waste products and as outlined in previous works of other authors on this subject the addition of iron to obtain a Fe/As molar ratio at least above 3 is necessary. The agitation equipment used in the pilot unit allowed an optimization study calculation for scaling-up the design and power requirements of an industrial installation. For the pretreatment of a gold refractory As high-graded concentrate the reagent cost has the greatest part in the operating cost of the biooxidation step due to the necessary retreatment of the biosolution. In that conditions the power cost is quite marginal. actually it is significant for the treatment of pure pyrite.

Jan 1, 1991

By Roberto Parra

The classic criteria of the preparation of the charge for the smelting of copper concentrates in a flash furnace considers the mass and energy balance from the chemical and mineralogy composition of the concentrates. The operation parameters fixed with this method don&apos;t assure the stability of the operation and the critical problems of the slag quality and dust formation occurs very often. This paper presents the results of a laboratory test that allows the predicition of the behavior of concentrates blends in the view of the minimization of the dust formation and the magnetite control in the slag. The combustion of different copper concentrates and blends were done in a drop tube furnace. The results show that the magnetite and dust formation don&apos;t have a linear behavior with the weight proportion of the blend and some optimal blends of 2 or 3 types of concentrates can be identified. From the reasonable hypothesis that the qualitative behavior of blends in the drop tube represents the real behavior in the burner, the preparation of the charge with this approach could help to solve those operational problems.

Jan 1, 2003

By Katsuyoshi Tatenuma

"In order to mitigate the effect of global warming by preventing the accumulation of atmospheric CO2, a permanent fixation method of surplus CO2 as an insoluble mineral onto the sea bottom is proposed. As the proposed reduction method of atmospheric CO2, the concrete concept of this method is to form an insoluble carbonate mineral (CaCO3) by direct electrolysis of the seawater; Ca2++2HCO3 -+OH- ? ?CaCO3(insoluble)+CO3 2- (soluble)+H++H2O <not as coral reef reaction>, are directly disposed of itself onto the sea bottom. By this treatment, a concentration of carbonate is reduced in the section of superficial seawater, and therefore the absorption capacity of atmospheric CO2 increases depending upon the shift of chemical carbon equilibrium between the mass of superficial seawater and the atmosphere. As no additives are required, or no secondary waste are produced, the proposed method assuming as green-orientated, has possibility to resolve fundamentally the problem of global warming in a green orientate manner.IntroductionRecently, the amount of atmospheric CO2 has been exponentially increasing and it is a main greenhouse effect gas causing the global warming [1, 2]. The concentration of atmospheric CO2 has increased more than 30% (370ppm in 2001) during only last two centuries, therefore approximately 750 Gton-C of CO2 currently exist in the atmosphere, in which 180 Gton-C of CO2 are accounted for the increment during two centuries [1, 3, 4]. In order to avoid the progressive increase of CO2 global abundance, 3 Gton-C of the incrementing amount per year [4], have to be removed annually from the atmosphere."

Jan 1, 2008

By R. Hurman Eric

The dew-point technique of activity measurements take advantage of the volatility of a component in solution. The pressure of the volatile component over a sample is determined from observations of the temperature at which condensation of the vapor occurs. The method is applicable best when the vapor pressure of the components would differ by about two to three orders of magnitude. Experimentally, this is a closed system involving the use of evacuated and sealed transparent quartz sample probes. Furthermore reliable vapor pressure data of the volatile component is essential along with a specialized high temperature furnace capable of giving reproducible results. In this context, the vertical Dew-Point Furnace (DPF) was designed and built after elaborate trails until enough proficiency was gained for reprodueible results. Over the years the DPF was modified and improved. The DPF developed was versatile and could easily be used for activity measurements in the isopiestic mode (another method of measuring activities of a volatile component in a solution). The necessary ancillary systems; namely evacuation-flushing-evacuation followed by sealing of quartz sample probes under vacuum were also perfected over the years. As and when necessary the dew-point technique was supplemented by classical equilibration-quenching method employed on the sealed quartz sample probes to reveal necessary phase equilibrium information. The following were studied utilizing the above technique: (i) Activities in CuzS-PbS and FeS-PbS binaries and CU2S-FeS- PbS ternary at 1200°C; (ii) Activities in CuzS-SnS and FeS-SnS binaries and Cu2S-FeS-SnS ternary at 1200°C; (iii) Phase equilibria and thennodynamic in Cu-Pb-S, Fe-Pb-S, Fe-Sn-S, Cu-Sn-S and Ag-Sn-S systems. Most recently the following systems have been tackled: (i) Phase equilibria and thennodynamics in the Ag-Pb-S and Sn-Pb-S systems; and (ii) Activities in Ag2S-FeS-CuzS-PbS quaternary at 1200°C.

Jan 1, 2003

By Hiroshi Hashimoto

For the application of sodium carbonate slag treatment to product high purity copper on an industrial scale, the counter-flow batch process that reduces the amount of utilized slag is proposed from the viewpoint of the post-treatment of slag. Based on the distribution ratios of several impurities between the slag and molten copper determined previously, the effectiveness of this process is discussed using a mathematical model and confirmed experimentally. According to the model, the slag consumption to remove Sb to a required level in case of the counter-flow batch process with 3 reactors is calculated to be around 30 % of that in the case of an ordinary batch process, where pure sodium carbonate is used as a slag at every stage.

Jan 1, 2003

By Hiroshi Hashimoto

For the application of sodium carbonate slag treatment to product high purity copper on an industrial scale, the counter-flow batch process that reduces the amount of utilized slag is proposed from the viewpoint of the post-treatment of slag. Based on the distribution ratios of several impurities between the slag and molten copper determined previously, the effectiveness of this process is discussed using a mathematical model and confirmed experimentally. According to the model, the slag consumption to remove Sb to a required level in case of the counter-flow batch process with 3 reactors is calculated to be around 30 % of that in the case of an ordinary batch process, where pure sodium carbonate is used as a slag at every stage.

Jan 1, 2003

By R. Hurman Eric

The dew-point technique of activity measurements take advantage of the volatility of a component in solution. The pressure of the volatile component over a sample is determined from observations of the temperature at which condensation of the vapor occurs. The method is applicable best when the vapor pressure of the components would differ by about two to three orders of magnitude. Experimentally, this is a closed system involving the use of evacuated and sealed transparent quartz sample probes. Furthermore reliable vapor pressure data of the volatile component is essential along with a specialized high temperature furnace capable of giving reproducible results. In this context, the vertical Dew-Point Furnace (DPF) was designed and built after elaborate trails until enough proficiency was gained for reproducible results. Over the years the DPF was modified and improved. The DPF developed was versatile and could easily be used for activity measurements in the isopiestic mode (another method of measuring activities of a volatile component in a solution). The necessary ancillary systems; namely evacuation-flushing-evacuation followed by sealing of quartz sample probes under vacuum were also perfected over the years. As and when necessary the dew-point technique was supplemented by classical equilibration-quenching method employed on the sealed quartz sample probes to reveal necessary phase equilibrium information. The following were studied utilizing the above technique: (i) Activities in CU2S-PbS and FeS-PbS binaries and CU2S-FeS- PbS ternary at 1200°C; (ii) Activities in Cu2S-SnS and FeS-SnS binaries and Cu2S-FeS-SnS ternary at I200°C; (iii) Phase equilibria and thermodynamic in Cu-Pb-S, Fe-Pb-S, Fe-Sn-S, Cu-Sn-S and Ag-Sn-S systems. Most recently the following systems have been tackled: (i) Phase equilibria and thermodynamics in the Ag-Pb-S and Sn-Pb-S systems; and (ii) Activities in Ag2S-FeS-CuzS-PbS quaternary at 1200°C.

Jan 1, 2003

An EAF dust generated in a Swedish steel mill has been leached in hydrochloric acid at The solution obtained has been subjected to purification by cementation followed by precipitation of zinc with sodium carbonate. The thermal decomposition of the precipitate was studied using thermal analysis and X-ray diffraction. The results show that during the calcination of the precipitate three different reactions occur. The decomposition of the solid phases Zn5(CO3) (OH)6, CaZn(CO3)2 and CaCO3 occur completely at 370°C, 560°C and 940°C respectively, yielding a final product containing 61.9% ZnO and 38.1% CaO. Methods to minimize calcium and manganese in the final product are discussed.

Jan 1, 2003

By S. Viswanathan, A. S. Sabau

"Dimensional changes between a pattern die and its corresponding investment casting part occur as a result of complex phenomena such as thermal expansion/contraction and hot deformation (elastic, plastic, and creep) during the processing of the pattern material (wax), mold material (shell) and solidifying alloy. Determining the pattern tooling dimensions is crucial to the dimensional control of the investment casting process. To date, computational methodologies have not been applied to the prediction of dimensional changes in investment castings.This paper deals with the evaluation of wax pattern dimensions, which is one important factor in determining pattern tooling dimensions in investment casting. Cerita 29-51, an industrial wax, is considered in this study. The wax pattern dimensions are determined by considering its thermo physical and thermomechanical properties, restraint of geometrical features by the metal die, and process parameters such as dwell time, platen temperature, injection pressure, and injection temperature.IntroductionThe investment casting process involves making a disposable wax pattern by injecting wax into a metal mold, building a ceramic shell mold around the wax pattern by the application of a series of ceramic coatings to the wax pattern, dewaxing the ceramic shell mold, and casting the alloy into the shell mold. Dimensional changes between the pattern tooling and its corresponding cast part occur as a result of thermal expansion, shrinkage, hot deformation, and creep of the pattern .material (wax), mold material (shell), and solidifying alloy during the processing [1]."

Jan 1, 2001

By Dietmar Eifler, Marcus Klein, Hendrik Kramer

Conventional methods to characterize the fatigue behavior of metallic materials are very time and cost consuming. That is why the new short-time procedure PHYBALCHT was developed at the Institute of Materials Science and Engineering at the University of Kaiserslautern. This innovative method requires only a planar material surface to perform cyclic force-controlled hardness indentation tests. To characterize the cyclic elastic-plastic behavior of the test material the change of the force-indentation-depth-hysteresis is plotted versus the number of indentation cycles. In accordance to the plastic strain amplitude the indentation-depth width of the hysteresis loop is measured at half minimum force and is called plastic indentation-depth amplitude. Its change as a function of the number of cycles of indentation can be described by power-laws. One of these power-laws contains the hardening-exponentCHT eII, which correlates very well with the amount of cyclic hardening in conventional constant amplitude fatigue tests. To identify heat-treatment-parameters and SAE 52100 TRIP-alloys with high hardening rates as well as their damage tolerance the PHYBALCHT- and PHYBALLIT-method were used. One modified SAE 52100 TRIP-alloy was investigated in detail. The fatigue behavior and the cyclic hardening of the selected SAE 52100 TRIP-alloy was investigated and compared with conventional SAE 52100. Conventional stress-controlled fatigue tests were performed on a servo-hydraulic test system with a frequency of 5 Hz and a load ratio of R = -1. Different rates of cyclic hardening were identified. The size of the nonmetallic inclusions leading to crack initiation and the number of cycles to failure were used to evaluate differences in the damage tolerance capability.

Jan 1, 2015

By Varuzan Kevorkijan

A new method for faster production of functionally graded metal-ceramic laminates is based on reactive pressureless counterflow infiltration/penetration of a ceramic substrate with two different metallic infiltrants. The porous or dense ceramic preform is pressurelessly infiltrated or penetrated from one side by the first metallic infiltrant to the desired cross section of the preform, producing the top layer made up of the solidified infiltrant and the underlayer consisting of reactive infiltrated preform. The partly infiltrated perform is then completely infiltrated starting from the other side by the second metallic infiltrant, in this way fabricating the internal layer, consisting of the ceramic perform infiltrated with the second infiltrant and the bottom layer formed by the solidified second infiltrant. Systems already investigated include carbide, nitride and boride ceramic performs infiltrated with aluminum and magnesium alloys.

Jan 1, 2003