By Yousef Mohassab, Hong Yong Sohn, Mohamed Elzohiery

As part of the development of a novel flash ironmaking process at the University of Utah, a labscale flash reactor was used to produce iron directly from iron oxide concentrate. This work tested the feasibility of the novel flash ironmaking process using the partial combustion of hydrogen as fuel and reductant. In this flash reactor, the energy required to reduce concentrate particles was obtained from the internal combustion of hydrogen and oxygen with complementary energy from electrical resistance heating to compensate for the heat loss. After the reaction shaft was electrically pre-heated, hydrogen and oxygen streams produced a non-premixed flame inside the reaction shaft. Various conditions such as flame configuration, flame power, positions of concentrate feeding ports, excess hydrogen amount and residence time were tested. More than 90% reduction of magnetite or hematite was achieved at temperatures as low as 1175 oC with < 100% excess hydrogen in <10 s of residence time.

Jan 1, 2016

By Jian-hua Ren, Guang-liang Wu

A lot of dust is produced in iron and steel enterprises, giving rise to serious environment pollution, with which all countries are trying to find methods to deal. The influence of relevant technological factors on dephosphorization was investigated in laboratory, and the effect laws of that were analyzed. The results demonstrate that, in the given conditions of the best slag-metal proportion for hot metal dephosphorization is 1:10, and the optimum temperature is 1350 , The phosphorus distribution ratio of dephosphorization agent containing converter dust of 30% has the maximal value, with dephosphorization rate reaching 85%. Under the optimal conditions, premelting dephosphorization agent can significantly improve the ability of dephosphorization, dephosphorization efficiency increasing to 92%. Therefore, the dust can substitute the oxidant and fixative of dephosphorization agent, be used in hot metal dephosphorization, to enhance the efficiency of utilization.

Jan 1, 2016

By Lifeng Zhang, Zineb Benouahmane, Yaqiong Li

Experimental oxidation tests at high temperature (1000-1200 °C) on SiC samples have been respectively performed under wet and dry air atmosphere for different holding times. The thickness of thermally grown oxide was experimentally measured by DEKTAK Stylus Profilometry. The results showed that the oxidation rate was increased with temperature and holding time, corresponding to a passive oxidation regime which led to the formation of SiO2 layer. The sessile drop method was employed in order to measure the contact angles between Si and SiC at high temperature. Contact angle can be varied from 39.6° to 75.6° by controlling the atmosphere. The deoxidation of the oxide layer and infiltration of liquid silicon caused a decrease in the contact angle.

Jan 1, 2016

By Shenghui Guo, Jianbo Lan, Hongying Xia, Jinhui Peng, Lihua Zhang, Libo Zhang

Spent Hawaii nut shell was converted into a high-quality activated carbon via steam physical activation. Analysis of the experiment including activation temperature, activation duration, steam flow rate on the adsorption capability and yield of activated carbon were identified. Response surface methodology showed that the activation temperature was identified as 866 , an activation duration of 36 min and a steam flow rate of 2.5mL/min with the methylene blue adsorption number of 195 mg/g and yield of 77.75%. The key parameters that characterize quality of the activated carbon such as the BET surface area, total pore volume and average pore diameter were estimated to be 1125m2 /g, 0.94mL/g and 5.21 nm, respectively. Additionally, by the SEM analyses of char and activated carbon, the surface of activated carbon has large number of pores of irregular and heterogeneous morphology.

Jan 1, 2016

By Peng ZANG, Qihang Liu

Experimental work was conducted to determine the relationships of coal char conversion with temperature and heat absorption. The results show that at an earlier stage of the coke forming process, lump coal would absorb large amounts of heat but the increase of high temperature strength of lump coal was not significant. Contrarily, the lump coal’s high temperature strength was greatly improved at later stage of coke forming process. A number of residual coal was found in most tuyere coke samples illustrating that the lump coals added in the melter gasifier were not completely transformed into coke when they arrived at the tuyere region. The results indicate that the improvement of lump coal’s high temperature performance is limited in the melting gasifier by the low coke forming rate which could become the core factor of fines generation of lump coal in the melting gasifier.

Jan 1, 2016

By Yang Wang, Xiancong Zhao, Hao Bai, Qi Shi, Zhancheng Guo

Linz-Donawitz converter gas (LDG) or basic oxygen steelmaking gas (BOSG) is one of the most important secondary energy sources in iron and steel industry, whose effective use plays a vital role in energy saving and emission reduction. However, the generation of LDG suffers from great fluctuation with respect to the production status of steel making. Therefore, a long term prediction model of LDG generation would be essential in gas system balancing and optimization. In this paper, a long term prediction model for the generation volume of LDG was proposed based on the steelmaking production estimation from Gantt chart and k-means clustering algorithm. Compared with the previous model, this model considered the influence of different steel type on LDG generation. The experimental results of a steel plant demonstrate that the proposed model exhibits high accuracy and can provide an effective guidance for balancing and scheduling of byproduct gases.

Jan 1, 2016

By QinGuo, Shenghui Guo, Jinhui Peng, Linqing Dai, Libo Zhang

This paper adopts a simple and novel preparation. Taking cellulose as a template, a tubular morphology structure of micro/nano ZnO crystals was obtained by microwave roasting at high temperature. The higher the microwave roasting temperature, the larger the degree of crystallization. The experiments indicate that the best photo catalytic effect can be obtained at 850 : At this temperature, the oxidation of cellulose is complete. Large quantities of hexagonal shaped ZnO crystal can be observed, specifically the (0001) crystal face. Under ultraviolet-visible irradiation, taking long arc mercury lamp as light source, the material had good photocatalytic activity. The decomposing efficiency of methylene blue reaches 97% in 60min, which is superior to that of preparations without templates at the same temperature.

Jan 1, 2016

By Junwei Han, Wenqing Qin, Dawei Wang, Fen Jiao, Wei Liu

The removal of iron impurity from zinc calcine was studied by magnetization roasting and magnetic separation. The effects of roasting temperature, magnetic intensity, ore grinding, and leaching pretreatment on iron grade and recovery were investigated. The results indicated that iron recovery increased with the increase of roasting temperature or magnetic intensity, while iron grade was always less than 22%, depending on the fact that the magnetite were not liberated completely. The good liberation was difficult to be achieved by ore grinding but was easier by acid leaching, since the magnetite grains were very fine. After the leaching pretreatment, the recovery of 76.31% with iron grade of 53.24% was obtained by one roughing and cleaning. The SEM/EDS analysis showed that a part of sphalerite, zinc ferrite and other gangues were mixed into the iron concentrate, while some of fine magnetite was reported to the tailing.

Jan 1, 2016

By Manju Gurung, Birendra Babu Adhikari, Keisuke Ohto, Hidetaka Kawakita, Katsutoshi Inoue, Shafiq Alam

Novel bio-adsorbent gel was prepared by immobilizing functional groups of glycidyltrimethyl ammonium chloride, a kind of quaternary ammonium chloride, onto polymer matrices of persimmon extract for the recovery of precious metals such as palladium(II) and platinum(IV) from chloride media. It was found that this adsorption gel exhibits high selectivity to gold(III), palladium(II) and platinum(IV) over base metals such as copper(II) and iron(III) while crude persimmon extract, the feed material, exhibits high selectivity only for gold(III). From the adsorption isotherms study, the maximum adsorption capacities for gold(III), palladium(II) and platinum(IV) were evaluated as 3.30, 1.67 and 1.00 mol/kg, respectively. Those for palladium(II) and platinum(IV) are higher than those of simple quaternary ammonium chloride type of chemically modified persimmon tannin gel and commercially available anion exchange resin.

Jan 1, 2016

By Itavahn Alves da Silva, Izabela Diniz Duarte, Carlos Antonio da Silva, Varadarajan Seshadri

Mathematical modeling using computational fluid dynamics has been employed to assess the thermal losses in a steelmaking ladle. Thermal losses lead to thermal stratification and convective flow inside the ladle. The effects of preheating, mineralogical and physical characteristics of the lining as well as thickness of slag cover have been studied and the results obtained from application of the model have been discussed.

Jan 1, 2016

By Shaohua Ju, Feng Jiang, Chuanhua Li, Jinhui Peng, Libo Zhang

A T-junction microchannel is proposed to overcome the existing problems in conventional solvent extraction of indium from zinc hydrometallurgical process. Experiments were performed to separate In3+, Fe3+ and Zn2+ from sulfate solutions using Di-(2-ethylhexyl)phosphoric acid (D2EHPA) as the extractant. The effect of parameters such as pH, microchannel size and contact time on the extraction behavior of In3+, Fe3+ and Zn2+ was investigated. At contact time of 2.52 s and initial solution pH of 0.48, the extraction efficiency of In3+, Fe3+ and Zn2+ was 99.13%, 8.31% and 2.45%, respectively and separation factor of In3+/Fe3+ and In3+/Zn2+ were almost 1229.54 and 4864.98, respectively. Then, the loaded organic phase was stripped in T-junction microchannel. At contact time of 33.6 s, 99.64% of stripping efficiency of In3+ and stripping equilibrium were reached, while concentration of Fe3+ and Zn2+ was lower than 0.01 g/L with good separation of In3+ from Fe3+ and Zn2+.

Jan 1, 2016

By Zhucheng Huang, Ronghai ZHONG, Liangming Wen, Tao Jiang

The reduction roasting-magnetic separation and its strengthening of high silicon coal-containing mini-pellets by sodium additives were researched. The results show that the carbon gasification reaction and reduction of fine hematite in high silicon coal-containing mini-pellets with 3% sodium additives were enhanced. Comparing with no sodium additives, the gasification rate of carbon with 3% sodium additives reacting with CO2 for 40 minutes at 950 and the metallization rate of reduced pellets with 3% sodium additives after roasting for 35 minutes at 960 increased from 35.15% and 58.72% to 86.98% and 86.15%, respectively. The analysis of SEM equipped with EDS demonstrates that the inner pore of reduced pellets with 3% sodium additives was more developed and the iron grains size significantly enlarged, meanwhile, the iron grade of concentrate increased from 60.45% to 80.23% and the iron recovery rate decreased from 84.67% to 80.78% after grinding-magnetic separation.

Jan 1, 2016

By Huimin Lu, Zegao Sun, Zhijiang Gao

The traditional Ti6Al4V alloys were obtained by the smelting reduction of V-Ti bearing beach placer by rotary hearth furnace and aluminothermic reaction in laboratory. First, it gets he lp from combined rotary hearth furnace and grinding magnetic separation process to prepare titanium slag containing vanadium. In this study, a neural network model was used. The comparisons between experiment results and neural network simulation results show that genetic algorithm (GA)-based on back propagation (BP) method can predict the degree of reduction and separation of iron and slag with higher prediction accuracy. Then by aluminothermic reaction process, the optimized process parameters for Ti-V-Al alloys were searched. Al can deoxidize metal V and Ti from the metal oxides of artificial rutile containing vanadium. Finally, traditional Ti6Al4V alloy can be obtained by remelt and adjust the constituents.

Jan 1, 2016

By Pan Gu, Zhen Zhang, Jiang Diao, Bing Xie, Hongyi Li

Furnace refractories are in most cases chemically incompatible with smelter slag, which leads to a steady erosion in their thickness over time. Once too thin, refractory walls become mechanically unstable and catastrophic failure can result. Historically, external shell cooling was applied to generate a freeze lining of slag and thus prevent refractory erosion. Many modern high intensity smelting furnaces instead maintain their physical integrity by the use of internally cooled wall panels, plates or finger coolers. An initial refractory lining is often installed inside of the coolers, such that the furnace originally operates with a temperature (insulated) rather than a heat flux (freeze lined) boundary condition. This paper examines the change in slag-wall heat transfer coefficient and slag superheat as a function of process intensity. The implications of the changes in heat transfer on residual brick thickness are explored using analytical modelling.

Jan 1, 2016

By Tianzu Yang, Weifeng Liu, Lin Chen, Wei Chen, DUCHAO ZHANG, HUI XIAO

Oxygen-rich side blow bath smelting (OSBS) technology was developed in 2000 based on Vanyukov process. This technology exceeds the traditional pyrometallurgical methods by its great processing capability, high metal recovery and environmental-friendly property. In the past 15 years, OSBS technology extended its application area from lead industry to bismuth, antimony and waste recycling industries, etc. This paper introduces the history and new developments of OSBS technology. The typical industrial applications examples of the OSBS technology in China, including high lead slag reduction, low grade bismuth-lead concentrate smelting and metallurgical waste recycling, are reviewed. Especially, the unique furnace properties and technical parameters are compared. Finally, the potential research directions of OSBS technology are summarized.

Jan 1, 2016

By Minting Li, Hailong Yang, ChangWei, Cunxiong Li, Gang Fan, Xingbin Li, ZhiganDeng

The filtration problems on acid leaching sludge of high silicon zinc ore have been paid extensive attention in zinc hydrometallurgy. It was found that soluble silica can be effectively converted into silica precipitate with good settling, filtration and washing properties, and the filtration rate can be in excess of 800 L/m2 · h under certain leaching conditions. According to investigating on the filtration rate, viscosity and concentration of silica of leaching sludge or liquor, the filtering temperature can tremendously improve the filtration property of pulp. At the same time, the experimental data indicated that the viscosity of leaching liquor was the key factor influencing filtration property of leaching sludge.

Jan 1, 2016

By Shengli Wu, Mingyin Kou, Laixin Wang, Zhe Wang, Xinliang Liu

The sticking behavior of iron ores in the shaft furnace is one of the most important problems in the COREX melting progress, which directly influence the smooth operation and productivity of shaft furnace. Therefore, it is of great importance to study the sticking behavior of pellets in COREX shaft furnace. The results showed that porous metallic iron produced at the interface of pellets samples was the main reason for the sticking of pellets in the COREX shaft furnace. The SI (sticking index) and metallization rate increased with the reduction temperature and gas flow, and decreased with melting rate. However, the SI of pellets in the COREX shaft furnace could be decreased by the proper match of melting rate and reduction temperature, reduction temperature and gas flow, while the metallization rate of pellets were kept at a certain level. Furthermore, the matching of melting rate and reduction temperature was more effective than the matching of reduction temperature and gas flow.

Jan 1, 2016

By Z. W. Zhang, Songsong Xu, Jinhui Li, Yun Zou, Yu Zhao

High strength low alloy (HSLA) steels with high strength, high toughness, good corrosion resistance and weldability, can be widely used in shipbuilding, automobile, construction, bridging industry, etc. The microstructure evolution and mechanical properties can be influenced by thermomechanical processing. In this study, themomechanical processing is optimized to control the matrix microstructure and nano-scale precipitates in the matrix simultaneously. It is found that the low-temperature toughness and ductility of the steels are significantly the matrix microstructure during enhancing the strength by introducing the nano-scale precipitates. The effects of alloying elements on the microstructure evolution and nano-scale precipitation are also discussed.

Jan 1, 2016

By Bo Liang, Hongmin Zhu, Kai Huang, Shafiq Alam

A new approach of recovering platinum and palladium from electronic wastes by hydrochloric acid leaching followed by selective adsorption on low-cost and environmentally benign biomass sorbent prepared from easily available agriculture waste is suggested. The obtained adsorbents were prepared by a combination of chemical modification and hydrothermal carbonization process with (NH4)2C2O4. It was found that the maximum adsorption capacity of hydrothermal carbonized garlic peel for Pt( ) and Pd( ) was 1.64 and 0.42 mol/kg respectively. The Langmuir adsorption isotherm was applied to describe the adsorption process. Kinetics of the Pt( ) and Pd( ) ions adsorption was found to follow pseudo-second-order rate equation. The adsorbents were examined by scanning electron microscope (SEM), and Fourier transform infrared spectroscopy (FT-IR). Based on the characterization results, a possible mechanism of Pt( ) and Pd( ) ions adsorption with the hydrothermal carbonized garlic peel was proposed. This study provides a promising adsorbent with efficient adsorption property for platinum and palladium recovery from the leach solution of electronic wastes.

Jan 1, 2016

By Edmundo Manilla, Merete Tangstad, Daniel Davila, Eli Ringdalen

FeMn alloys are typically produced with lumpy ore or sinters. Minara Autlan, the Mexican FeMn producer, is however making Mn-nodules as a raw material for Mn-alloy production. The Mn nodules have been characterized by XRF, XRD, by wet chemical methods and by EPMA. The Mn/Fe ratio is somewhat lower compared to commercial Mn ore on the marked. The basicity of the ore is however close to 1, and additional fluxes may not be used. The Mn-nodules will be in a state of manganosite (MnO), tephroite ((Mn, Ca)2SiO4) and galaxite ((Mn,Mg)Al2O4). This leads to a low melting temperature area. A low porosity and low amount of higher Mn-oxides gives a high thermal strength to the nodules.

Jan 1, 2016