By Shenghui Guo, Ying Lei, Wei Li, Jinhui Peng, Libo Zhang, Yu Li

"Abstract: In this work, low temperature carbothermic reduction of Panzhihua low grade ilmenite after ball milling were investigated. The ball milling of ilmenite and graphite were processed in a ball mill. The milling process can attenuate the particle of ilmenite, and the ilmenite characteristic peak were broadened and weakened. The reduction temperature and behaviors are studied on the thermo gravimetric apparatus; lower temperature and higher reaction rate were obtained for the reduction of ilmenite with graphite after milled. The reduction temperature and times of ilmenite decreased to 1000-1025°C and 40-60min via milled for 4 or 8h; Low down the reduction temperature can eliminate the solution of Mg2+ and FeTi03 in a certain degree; the reduced ilmenite has an obvious loose structure, can favored the subsequent procedure such as leaching.1 IntroductionThere is about 9.66 billion tons of Vanadic Titan-magnetite deposited in Panzhihua, China. In this reserve, there is about 8.73x108 t ofTi02, Accounting for 90.54% of the Chinese reserves, and 35.17% of the international reserves and ranking first in the world. [JJ Titanium mineral deposits major classified into Rock type and Placer type. Rock type is the igneous mineral, which have great content of FeO (Relative to Fe20 3) and gangue. The rock textures are compact and almost are complex ore. Rock type Titanium mineral major are ilmenite and titan magnetite ore, difficult to separate the metal ore and gangue. l.21 Thus, the Ti02 grade of Rock type ilmenite much lower than the Placer type (Table land 11). Panzhihua ilmenite are the typical Rock-type, due to the higher contents of MgO, CaO and Si02 and the complex mineralogy in ilmenite in Panzhihua region, making its direct reduction progressively more difficult. Mechanical activation, usually carried out by energetic milling or ball milling, was reported to significantly decreased the reduction temperature and accelerate the reaction rate of reduction of ilmenite with carbon, silicon and Magnesium. f3·(>J It reported that the process temperature were decreased to 600-1000°C and the annealing time were reduced to 30-120min after milled for 50-400 h. Shorter milling time involved was imported for else procedure such as direct leaching. 171 Hardly any research had referred to the carbothermic reduction reactivity of ilmeite milled for a short time as 1-1 Oh. In the present work, the aim is to investigate the reactivity and reaction temperature of carbothermic reduction of Panzhihua ilmenite. The Phase composition and micro morphology of samples are characterized."

Jan 1, 2011

By Zemin Ma

A novel chromate [Cr(VI)] reducing bacterium was isolated from chromite ore processing residue disposal site of China and identified as a Leucobacter sp. by 16S rRNA gene sequence homology. The minimum inhibitory concentration of strain CRB1 was 820 mg l-1 of Cr(VI). The reduction of Cr(VI) occurred only under aerobic conditions. With an initial concentration of 2.5×108 cells ml-1, 1800 mg l-1 of Cr(VI) was reduced entirely within 38 h under the optimum conditions, at 30 °C and pH 9.0. Increasing Cr(VI) concentrations prolonged reduction process and higher cell densities meant quicker reduction. A blue precipitate was produced during chromate reduction of strain CRB1, which was binding to the surface of bacterial cells and determined as trivalent chromium with electron paramagnetic resonance (EPR) spectrometry. The conspicuous chromate reduction ability of Leucobacter sp. CRB1 suggested a potential for bioremediation of Cr(VI) containing wastes.

Jan 1, 2008

Heap leaching with thiosulfate is only used in one location for the treatment of a refractory preg-robbing gold ore initially pre-treated with bio-oxidation. The chemistry of thiosulfate leaching is complex. Further work is required to develop a better control of the system. A mild refractory gold ore containing pyrite and chalcopyrite was used in this study to investigate the use of thiosulfate as an alternative heap leaching technology. Preliminary bottle rolls tests indicated that similar gold extraction was obtained with cyanide and thiosulfate. In the column leach test, effects of thiosulfate, copper and ammonia concentrations, and their ratio on both gold extraction and reagent consumption, were assessed. The range of reagent concentration were: 0.1 - 1.0M (NH4)2S2O3, 0.03 - 0.10M CuSO4*5H2O, 1.0 - 6.0M NH4OH. The solid-liquid ratio was in the range of 0.83:1 to 5: 1. Best results showed that 72% of gold was extracted in 50 days with 0.3M (NH4)2S2O3, 0.05M CuSO4*5H2O and 6M NH4OH or a combination of 1.0M (NH4)2S2O3, 0.03M CuSO4*5H2O and 3M NH4OH. The reagent consumption at solid/liquid ratio of 3:1 was 37 - 48.6 kg/t (NH4)2S2O3 and 0 - 0.62 kg/t CuSO4*5H2O. The results of thiosulfate leaching were also compared with cyanide leaching.

Jan 1, 1999

By T. DebRoy

In recent years rapid technological advances have been achieved in the application of high energy density heat sources such as lasers and electron beams in diverse metals processing operations such as metal refining, fabrication, coating, surface modification and alloying. However, our phenomenological understanding of these new and emerging processes has not kept pace with the technological achievements. Inadequate understanding of plasma-metal interactions, the complexity of the component physical processes, and the scarcity of thermophysical data at temperatures much higher than the melting points of metals are the main difficulties in the comprehensive analysis of these processes. Several unique contemporary issues related to metals processing with high energy density beams such as rapid evaporation of alloying elements during processing and the role of plasma in influencing vaporization rate interfacial tension and species solubility in metals are discussed in this paper.

Jan 1, 1993

By Vinod K. Sikka, René Cooper

"Cohoes, New York 12047 Intermetallics are an attractive class of advanced materials. The aluminide intermetallics offer advantages including: (1) lower density, (2) oxidation resistance, (3) carburization resistance, and (4) interesting mechanical properties because of their ordered crystal structure. Even though the attractive properties of the aluminides and other intermetallics have been known for nearly four decades, their practical applications have not been developed for two reasons: (1) the poor ductility (in some cases, both ambient and high temperatures) and (2) the lack of processability into meaningful components. Recent advances such as ductilization of Ni3Al by small additions of boron and the knowledge that environmental effects are the major cause of poor ductility in Fe3Al and FeAl systems have brought the intelmetallics into the forefront of research and their commercial applications. This paper has described a method for melting Ni3AI-based alloys that successfully utilize the exotherrn for the formation of NiAl from the elemental materials. The reaction-synthesis method has also been utilized for the production of NiAI and NiAI-based alloy powders from the elemental powders. The reaction-synthesized powders of NiAI and NiAI-based alloys were consolidated by hot extrusion and evaluated for tensile properties over a temperature range from room temperature to 1050ºC. The powder-processing conditions have been found to have more influence on the ductile-to-brittle transition temperature of NiAI than the powder-production method.IntroductionIntermetallics are an attractive class of advanced materials [1-11]. The alum in ide interrnetallics offer advantages including: (1) lower density, (2) oxidation resistance, (3) carburization resistance, and (4) interesting mechanical properties because of their ordered crystal structure. Even though the attractive properties of the aluminides and other interrnetallics have been known for nearly four decades, their practical applications have not been developed for two reasons: (I) the poor ductility (in some cases, both ambient and high temperatures) and (2) the lack of processability into meaningful components. Recent advances such as ductilization of Ni3Al by small additions of boron and the knowledge that environmental effects are the major cause of poor ductility in Fe3Al and FeAl systems have brought the intermetallics into the forefront of research and their commercial applications. The paper will briefly review the processing techniques being pursued for the commercial applications of Ni3Al-based intermetallics. The major emphasis of the paper will deal with synthesis of Ni3Al and NiAI intelmetallics."

Jan 1, 1994

By Isabella Lancellotti, Fabrizio Passarini, Luisa Barbieri, Fernanda Andreola, Ivano Vassura, Luciano Morselli

"The techniques able to incorporate wastes by means of a heat treatment present the advantage to fix the residue with chemical bonds. Among these techniques there are vitrification and sintering which are characterised by different operating temperatures in the range of 950-1500°C and the involved raw materials develop silicatic crystalline phases and glassy matrices capable to immobilize heavy metal contents in the waste matrix. In this work incinerator bottom ash, polishing and glazing ceramic sludges have undergone to thermal treatments in order to valorise the waste as secondary raw material for the obtainment of re-products. The chemical efficiency of the process adopted has been evaluated by comparing the results of release tests applied to the as-received wastes and to the thermally treated materials in order to verify the effectiveness of the different matrices to fix the waste components.IntroductionVitrification is one of the most promising technological options for the treatment of some kinds of waste. The high temperature involved in the process (1200-1500°C) leads to the complete destruction of organic pollutants, such as dioxins, and glassy network formed can incorporate heavy metals. Some vitrification processes naturally occur: glasses produced by volcanic eruptions, such as obsidians (Na2O-K2O-Al2O3-SiO2) and basaltic (CaO-MgO-Al2O3-SiO2) rocks, are basically inert materials even when they contain toxic elements, because these are embedded in an extremely stable glassy matrix. The disadvantage of vitrification is that it is an energy-intensive process involving relatively high costs, therefore its use is better justified if a high-quality product with optimised properties can be fabricated. The most effective way to improve the properties of the vitrified material is the transformation into glass ceramic. This is a fine-grained polycrystalline material (typically from 50% to 98% of the volume may be crystalline) formed when a glass of suitable composition is heat treated and hence undergone to controlled crystallisation (phenomenon named devitrification). The three key variables in the design of a glass-ceramic are: glass composition which controls glass viscosity related to the effectiveness of nucleation and rapidity of crystallisation; glass-ceramic phase assemblage (that is, the types of crystals and the proportion of crystals to glass) which is responsible for many of the physical and chemical properties; nature of the crystalline microstructure (crystal size and morphology and the textural relationship among the crystals and glass) which is the key to many mechanical and optical properties. In particular, a partly crystalline material can be obtained by powder sintering."

Jan 1, 2008

By Yasuyuki Murayama

MF is the semi-blast furnace which has been developed at Mitsui Miike Smelter in the 1960's to treat vertical retort residue. The MF has also been tested for treatment of various recycling materials and wastes. Now various secondaries and wastes (steel dust, zinc leaching residue, Cu-Ag sludge, spent catalyst and spent rubber, etc.) are mainly treated. Powder materials are briquetted with reductant before being fed to the furnace. Products are crude zinc oxide, matte, non-hazardous slag and steam. Zinc and lead are recovered in oxide dust, and copper and silver are recovered in the matte. The MF furnace can be widely applied to many kinds of materials which contain such non-ferrous metal-valuables. In addition, the improvement in operation and technology has effectively made the unit capacity much larger. The MF furnace now has many advantages for these treatment processes.

Jan 1, 1992

By Ken-ichi Machida

"Surface modification of R-Fe-N intermetallic compounds was made to improve their magnetic property and nitrogenabsorbing ability, arid high-performance resin-bonded magnets and nitrogen storage materials were developed: Surface coating for Sm2Fe11Nx by the zinc metal produced via photodecomposition of Zn(C2Hs)2 was effective to avoid the further oxidation in the molding process of the fine powders for bonded magnets and the resulting (BH)max values were improved to -186 kJm-3. Meanwhile, R2Fe17 as the mother compounds for RzFe11Nx was highly active for decomposition of NH3 molecule and subsequent nitrogen absorption as metal nitrides. Furthermore, even inert Nz molecule was dissociated on them by impregnating Ru metal and the resulting nitrogen atoms were absorbed in the crystal lattice of R2Fe17. These results demonstrated that the nitrogen storage system was established by cycling the nitrogenation and hydrogenation of RzFe11/R2Fe11Nx materials.IntroductionProcessing for rare earth metals and intermetallic compounds requires well-controlled conditions in order to avoid the oxygen contamination involved in it due to their high reactivity, as causes the serious damage for materials such as magnets, metal hydride for hydrogen storage, and so on. Rare earth-iron intermetallic compounds, R2Fe17, provide the corresponding metal nitrides (R2Fe11Nx) by heating in N2 or a mixed gas stream ofNH3-H2 [l] and, among them, Sm2Fe11N3 has been particularly noted as one of the promising materials for high-performance permanent magnets such as bonded ones [2- 6]. Usually, the nitrogenation for Sm2Fe17 is made in Nz, but it needs the much more hard conditions of reaction pressure (-10 MPa), temperature (-550°C) and time (-72 h) than the nitrogenation in the NH3-H2 mixture [l]. In the latter case, a significant amount of nitrogen can be interstitial introduced in· the R2Fe17 crystal lattice (x=-7) under the more moderate conditions than in N2 (at 0.1 MPa and -450°C for -3 h) [3-6] and then, in a similar manner as metal hydride systems [7], the excess nitrogen in RzFe1 7Nx (x>3) is reversibly desorbed by heating at a temperature around 500°C in Ar to form the RzFe11N3 compounds. This behavior of nitrogen absorption and desorption has a close relation to the sites for nitrogen in the crystal lattices."

Jan 1, 2000

By J. A. Bakken

Thermal plasmas are interesting for a wide range of metallurgical and chemical processing applications. The 300 kW experimental reactor PRESS, which has been in use since 1987, is operated in the transferred arc mode with three or one plasma torches . Tests include remelting of silicon fines and production of ultrafine silica. Work on a novel three stage process for production of silicon metal is under way. A 1:1 model of the plasma reactor is used to measure the wall heat flux distribution calorimetrically. The cold walls of this model are divided into several water-cooled sections. The same plasma torches as in the real hot-wall reactor are used. In parallel to the experiments and calorimetric measurements theoretical work is done on numerical modelling of one and three transferred arcs. A modified version of the flow simulation program FLUENT from Creare Ltd. is used.

Jan 1, 1991

By Baozhong Zhao

Experimental results have shown that fluxing with soda ash (Na:zC03) can remove As and Sb from molten copper at the rate of As>Sb, but is relatively ineffective in removing Hi. The rate of impurity removal is controlled by impurity mass transfer in the metal phase. In this paper, a mathematical model was developed to describe the impurity removal phenomena. The model incorporates the effects of molten bath mixing intensity, soda ash feeding rate, oxygen content in the molten copper and soda ash fluxing by surface addition and injection. The model predictions are in good agreement with experimental results and may be used in designing large scale tests.

Jan 1, 1996

By J. Fraser Forbes

"The meaning of the term ""process control"" has evolved significantly since its widespread use began in the manufacturing industries in the 1940s. Further, the scope of process control applications has drastically increased both in terms of the breadth of industries using process automation technologies and the vertical integration of these technologies within a single industry. This evolution and integration of process control technologies within the manufacturing industries has proceeded to such an extent that process automation is an integral part of modern business practices.This paper will examine the current status of process control technology from simple process regulation through process performance optimization to business planning. Each layer of the operations automation hierarchy will be discussed both in. terms of the current state-of-the-art and the directions in which these technologies are evolving. The key tools and tasks necessary for success at every level of the automation hierarchy will be introduced. Finally, the critical challenges that must be faced in accomplishing the goal of complete Computer Integrated Manufacturing (CIM) will be described.Finally, although this paper addresses issues of practical importance to any manufacturing company, the discussions will be framed in terms of the particular challenges facing and the opportunities available within the materials manufacturing industries."

Jan 1, 2000

By Donghai Li, Cheng Pan, Pan Chen, Xuewei Lv, Mei Liu

"Chromite concentrate after beneficiation can not be directly used in the electric furnace. Therefore sintering is one of the effective way to agglomeration, by which the chromite concentrate can be utilized and the power cost of ferrochrome smelting can be reduced. The properties of raw materials and the sintering process of chromite concentrate were studied in this work. The results showed that chromite concentrate used can hardly granulated alone, while chlorite addition can improve the effect of granulation. Moisture plays an important role in sintering process. The granulation effect is optimal when the amount of water addition is 12%. Strength and abrasion index are the evaluation indexes of sinter quality. It was found that the strength of sinter increased with coke dosage increasing to 12%, and then decreased when it continuously increased. Opposite regularities were found for the abrasion index of the sinter.1 IntroductionChromium is a very important metal element which is mostly used in the production of stainless steel. In the earth, it is always formed compound with iron as ferrochromium spinel (FeO.Cr203), and its mineralogical name is chromite.[1] Currently, the global production of chrome ore is about 20 million tonnage every year , in which fine ore (less than 8 mm) accounted for about 80% [2] Although the price of the fine ore is cheaper than the lump one, too much fines will lead to the poor permeability and causes increased electricity consumption while producing ferrochrome. Therefore, the agglomeration process of chrome ore is one of the effective measures to increase the usage ratio of fine ore."

Jan 1, 2013

By Harovel G. Wheat

It has been shown that the incorporation of fly ash into concrete as a replacement for part of the cement can be beneficial. In some cases, the strength of the concrete can be increased and the permeability can be decreased. This latter property can lead to a reduction in the migration and/or penetration of aggressive species into reinforced concrete. Some of these species, such as chlorides from deicing salts or marine environments, can subsequently result in accelerated corrosion of the steel reinforcement, a loss of the protection provided by the passive film on steel, and a loss of structural integrity of the concrete. Care has to be taken so that the appropriate compositions of the components of the fly ash are utilized in order to ensure maximum benefit to the concrete structures. This will be discussed as it relates to fly ash generation and treatment.

Jan 1, 2002

By D. A. Robbins

The Resource Conservation and Recovery Act. of 1976 (RCRA) requires testing of waste materials as part of the determination of whether these materials are classified and managed as hazardous wastes. The adoption of one standard testing procedure and its application to all types of waste materials has stirred much controversy. In the center of this controversy is the appropriateness of this testing procedure in characterizing non-ferrous metal intermediates and slags. The authors have evaluated the relative availability of metals in several types of copper and lead slags as defined by various testing protocols. Also discussed is the relationship between the chemical character of the slag and the availability of metals to leaching and certain metallurgical practices that can influence metals availability.

Jan 1, 1983

By Baozhong Ma, Yonggang Wei, Shiwei Zhou, Bo Li, Chengyan Wang, Hua Wang

The effects of additives with Na2S, Na2SO4 and CaSO4 on phase transformation of nickel laterite ore in low-temperature reduction roasting process using carbon monoxide were investigated. The results showed that diffraction peaks of forsterite increased with increasing reduction temperature for 30min with the addition of 10wt% Na2SO4 and 50vol% CO, and diffraction peaks of forsterite increased with increasing the content of Na2SO4 at 900°C for 30min. Comparing the above three additives, phase transformation of nickel laterite ore were strongly influenced with the addition of 10 wt% Na2SO4 and 10 wt% Na2S. Calcium sulphide from the thermal decomposition of CaSO4 was carried out in the reaction product. SEM-EDS analysis result deduced that increasing the dosage of Na2SO4 from 10wt% to 15wt% could promote the polymerization of ferronickel and improve the grade of nickel in ferronickel.

Jan 1, 2015

By Satu Jyrkönen

A single-particle laminar-flow technique was used to study reactions of sulfidic nickel particles. The studied materials were three natural nickel concentrates and four synthesised nickel mattes. The variables of the experiments were the gas preheating temperature (500 - 1300°C), the composition of the reaction gas (N2 + 0 - 75 vol-% 02) and the ,particle size of the feed. Chemical analysis of the particles was used to determine the oxidation degree of the materials, and optical and scanning electron microscopy were used to detect alteration in their morphology, internal composition and structure. General reactivity of the materials was monitored by the extent of sulfur removal. The reaction mechanism of the studied materials was found to depend primarily on the materials composition as well as oxygen content of the reaction gas.

Jan 1, 1998

By Timothy W. Ellis

This paper presents the basic theory of operation, physical chemistry and phase equilibria which allow the development of liquid-liquid extraction circuits based on metallic solvents. The incorporation of reduction and reduction/diffusion processes into the process 'scheme is discussed and a detailed description of ,several liquid-liquid extraction schemes are developed. A synopsis of experimental results obtained using this: method to separate rare earth and other metal based materials will be given.

Jan 1, 1996

By Saad Elias Kaskah

"The Box-Behnken Design (BBD) is used to model the sacrificial Cathodic Protection System (SCPS) to find the factors effectiveness behaviour. For protection potential assessment the BBD receives (resistivity of environment, sacrificial anode alloy, distance between anode and cathode and surface area for the structure to be protected) as input and gives the protection potential as output. By applying BBD with their analysis tools we get many results. The important results which are the factors individual effectiveness on the sacrificial cathodic protection (SCP) process are the resistivity which has the greatest effect on the potential protection (rank=l) followed by sacrificial anode alloy type (rank=2), surface area for structure protected required (rank=3) and distance between anode and cathode (rank=4). The interaction of sacrificial anode alloy and cathode area {X2X4 ) has significant effect on CP process with the limits which are used in this work while the other factors interaction (X1X2, X1X3, X1X4,X2X3, X3X4 ) has insignificant effect on the limits which used in this work.IntroductionFor carbon steel in seawater the normal corrosion potential E '°""_is in the range -550 to -600 mV vs. Ag/AgCI [1]. The most effective method to overcome the corrosion is cathodic protection {CP) which represents a control method in the steel wall corrosion. Cathodic protection has been used in several areas including marine and underground structures, storage tanks, and pipelines [2]. Sacrificial anodes system generates protective current which depends upon the inherent potential difference between the anodes and the structure to be protected. If the structure is made of iron or steel, any metal that is more active in the electromotive force series can theoretically be used as anode material [3]. There are many factors influencing on cathodic protection like resistivity (NaCl content), chemical composition of sacrificial anode alloy, distance between anode and cathode, surface area of cathode, temperature, humidity, velocity of solution, dust, impurities, bacteria and etc .. The present work studied four factors: NaCl content, resistivity), chemical composition of sacrificial anode alloy, distance between anode and cathode, surface area of cathode) with different three levels of values for each one. Then this work will find the optimum value from the factors levels that tacked to investigated there influencing on sacrificial cathodic protection system."

Jan 1, 2013

By Gerardo Fuentes

The stoichiometry and kinetics of the hydrothermal reaction of enargite in copper sulphate solutions was investigated in the range 140–300 °C, and particle size under 15 and 50 μm. The stoichiometric experiment was performed at 300 °C, using one gram of sample (96% enargite, 4% tennantite) and 100 mL of copper sulphate solution (10 gpl) at 1.2 pH. Enargite reacted completely after 80 min. A solid product was obtained and characterized by XRD. The main product was chalcocite (M) and some traces of djurleite and chalcocite (Q). Tennantite did not react under these conditions. The kinetic experiments were conducted at 140 °C, 190 °C, 250 °C and 300 °C. From fitted data and Arrhenius equation the calculated activation energy (Ea) was 51 kJ/mol. According to the hydrothermal transformations studied, the reactivity of different phases found in the copper concentrates was bornite > chalcopyrite > covellite > sphalerite > pyrite > enargite > tennantite.

By V. J. Ramirez, A. M. E. Noguez, M. J. Navarrete, B. G. Salas, N. T. Robert

"The close die forging stress in truncated conical cavities is evaluated with dimensional analysis. Five dimensionless groups are proposed from the process variables in order to simplify the forging stress determination. These groups are experimentally related and graphically expressed. This methodology can be used to predict the actual forging stress in industrial close die forgingThe use of the dimensionless groups allow to comprise more cases than the presented here, provided similar geometries and operational conditions.Introduction.Closed die forging is essentially a plastic deformation inside a two piece mold (forging die) with the inverted shape of the actual forging geometry. This plastic deformation will always be the result of a compressive stress. There are theoretical models which include complex calculations for the analytical determination of stresses (1, 2, 3, 4). Results of these calculations are approximate, requiring generally ulterior tests to obtain the true operational conditions(5).In this paper, it is presented a simplified approach to the actual compression stress needed in the forging. A well known tool in engineering: the Buckingham's Pi theorem in conjunction with dimensionless groups and a working piece scale model is used. Dimensional analysis will give the dimensionless terms needed to experiment with a selected scale model geometry to make the stress determination. The results presented demonstrate the reliability of this methodology."

Jan 1, 1997