By F. T. Principe

In order for solvent extraction technology to be acceptable as an alternative to existing jarosite precipitation circuits, iron must be cleanly separated and concentrated into a feed stream suitable for downstream iron by-product recovery which meets market specifications and economics. Ten years ago, significant progress was made in a joint McCill University/CANMET project that involved iron extraction with mono(2-ethylhexyl) phosphoric acid and stripping with HCI. Our iron solvent extraction research was reactivated recently by looking into this and other members of the organophosphorus extractant family. Our research focuses on the mechanisms and control of anion (SO42/CI) transport across the various phases (Rafinate/Organic/Strip), iron build-up in the strip liquor, and extractant stability/selectivity. In this paper, these issues along with some other performance parameters are discussed using data derived from an extensive search of the two commercially available and best known members of the organophosphorus family, di-2-ethylhexyl (D2EHPA) and mono-2-ethylhexyl (M2EHPA) phosphoric acid. Further in this discussion, the challenges lying ahead in the development of sx systems that overcome the deficiencies of D2EHPA and M2EHPA are outlined. In particular, the necessity of considering secondary separation technologies that can further concentrate iron values in the chloride strip liquor to levels economically attractive for the production of saleable iron oxide by pyrohydrolysis is addressed.

Jan 1, 1998

By Zhitong Sui

Based on several case studies on the precipitating behavior of valuable nonferrous metal compounds (VNMC) in molten slags a green technology for the recovery of VNMC from molten slags was proposed. This technology involves three steps: (I) The selective enrichment of the dispersed VNMC into the designed mineral phase in the molten slag; (2) The selective coarsening of the designed mineral phase to a critical grain size in the molten slag; (3) The selective separation from tailing of the grown mineral phase in the solidified slag by dressing or hydrometallurgy processes. This is a clean and low cost technique and has a great capacity to deal with a large quantity of slags. The utilization of the recovered VNMC such as Titanium, Boron, Vanadium compounds was summarized as examples of application. It was confirmed by experiments that the precipitating behavior of the designed mineral phases like Perovskite(CaTiO3), Suanite(2MgO*B2O3) and Sincosite(CaOoV2O5*P2O5) in molten slags is obviously affected by operation factors such as temperature, chemical composition, heat-treatment, additives and so on. The precipitating kinetics and mechanism of the VNMC from molten slags during solidification processes were also investigated.

Jan 1, 2003

By Patrick R. Taylor

Coatings of TiCIFe have been produced by Reactive Plasma Spraying using ilmenite ore concentrate as the feedstock powder and methane as the reactive gas. A free energy minimization analysis of the ilmenite-methane system is presented. The coatings have been characterized by x-ray diffraction and SEM. The microstructure of the coatings indicates good interparticle cohesion. The composition of the coating is deficient in iron compared to the initial Fe to Ti ratio found in ilmenite.

Jan 1, 1998

By X. Jay Gao

A fast high-temperature carburizing process integrated with materials design and optimization via a systems design approach was developed to significantly reduce process cycle time. Process experiments were focused on boost cycles to obtain a robust boost process and investigate surface reaction kinetics, primary carbide formation and dissolution. Weight gain and microhardness were measured, all showing evidence of non-monotonic time evolution for longer boost times at higher temperatures. Optical and electron microscopy and other techniques have been used to identify possible carbides, their location and types. These results assist the picking of first boost time with least variation rate in terms of content of case carbon and carbides, dissolvable in subsequent diffuse if any. The results also provide critical information to properly formulate surface reaction kinetics and diffusion and formation kinetics of carbides modeled using DICTRA. Keywords: high temperature vacuum carburizing, partial pressure carburizing, heat treatment, process development, carbide, case hardening, microstructural analysis, over carburizing

Jan 1, 2003

By Gerardo Fuentes

The stoichiometry and kinetics of the hydrothermal reaction of enargite in copper sulphate solutions was investigated in the range 140–300 °C, and particle size under 15 and 50 μm. The stoichiometric experiment was performed at 300 °C, using one gram of sample (96% enargite, 4% tennantite) and 100 mL of copper sulphate solution (10 gpl) at 1.2 pH. Enargite reacted completely after 80 min. A solid product was obtained and characterized by XRD. The main product was chalcocite (M) and some traces of djurleite and chalcocite (Q). Tennantite did not react under these conditions. The kinetic experiments were conducted at 140 °C, 190 °C, 250 °C and 300 °C. From fitted data and Arrhenius equation the calculated activation energy (Ea) was 51 kJ/mol. According to the hydrothermal transformations studied, the reactivity of different phases found in the copper concentrates was bornite > chalcopyrite > covellite > sphalerite > pyrite > enargite > tennantite.

By M. Y. Mohassab-Ahmed

In an effort to develop a novel flash ironmaking process, the chemistry of selected slags was investigated. In different ironmaking processes, the molten bath (iron-slag bath) is expected to be in contact with gas atmospheres of H2/H2O, CO/CO2/H2/H2O, and CO/CO2. The latter was investigated to allow comparison with the blast-furnace conditions. The slag composition was selected to resemble that of the blast furnace with CaO/SiO2 in the range 0.8 to 1.4. The temperature range was 1550 to 1650°C. The oxygen partial pressure was maintained in the range 10-10 to10-9 atm. The effect of water vapor on the chemistry of the slag as well as the equilibrium reactions involving the slag has been studied for the first time. H2O dramatically affects the chemistry of the slag and strongly affect the phase equilibria in the slag as well as the equilibrium distribution of elements between slag and molten metal.

Jan 1, 2014

By Scott A. Howard

MgO is routinely used as the basis for refractory materials, however, its susceptibility to hydration may result in dimensional instability and subsequent failure. The addition of boron has been shown to reduce th,e hydration susceptibility of MgO yet its dissolution into certain grades of steel may degrade their performance. In order to predict the efficacy of reducing hydration susceptibility by the incorporation of mono-, di-and tri-and quadravalent cations, the lattices of various cation-substituted systems were modeled. To more accurately simulate the substituted lattices, either cation or anion vacancies were incorporated to maintain electrical neutrality and all possible arrangements of defects in a 2x2x2 MgO supercell were investigated. Correlations were then made between the lattice energies of these systems and their susceptibility to hydration as reported in the literature. The results indicate the presence of higher charged cations tended to increase lattice stability while the cations with lower valency tended to have lower lattice energies. The relatively small body of experimental results available in the literature are consistent' with this study's results.

Jan 1, 1989

By Mansoor Barati

The present paper is based on a term project for final year undergraduate students, requiring them to evaluate a process for producing silicon from rice husk. The traditional method for production of silicon involves carbothermal reduction of quartz in electric arc furnaces at temperatures exceeding 2000 °C. The technology consumes a considerable amount of electrical energy as well as fossil fuels, resulting in significant CO2 emissions. A flowsheet for production of silicon metal from rice husk is laid out in this paper. The technology will consist of combustors, which will generate steam using the rice husk biomass, power generator, and electric furnace for reduction of the rice husk. Materials and energy balance calculations presented here indicate that such process can be operated independent of external electricity.

Jan 1, 2014

By Baozhong Ma, Yonggang Wei, Shiwei Zhou, Bo Li, Chengyan Wang, Hua Wang

The effects of additives with Na2S, Na2SO4 and CaSO4 on phase transformation of nickel laterite ore in low-temperature reduction roasting process using carbon monoxide were investigated. The results showed that diffraction peaks of forsterite increased with increasing reduction temperature for 30min with the addition of 10wt% Na2SO4 and 50vol% CO, and diffraction peaks of forsterite increased with increasing the content of Na2SO4 at 900°C for 30min. Comparing the above three additives, phase transformation of nickel laterite ore were strongly influenced with the addition of 10 wt% Na2SO4 and 10 wt% Na2S. Calcium sulphide from the thermal decomposition of CaSO4 was carried out in the reaction product. SEM-EDS analysis result deduced that increasing the dosage of Na2SO4 from 10wt% to 15wt% could promote the polymerization of ferronickel and improve the grade of nickel in ferronickel.

Jan 1, 2015

By Jose Carlos D’Abreu, Edelink Efrain Tinoco Falero, Mauricio Marcos Otaviano, Helio Marques Kohler

Nowadays the most important Direct Reduction - DR processes in shaft furnaces has to deal with carbon fines precipitation and DRI carburization issues. Based in a cooperative research program joining Catholic University (PUC-Rio) and SAMARCO Mining Co, a project dealing with pellets reduction and those two phenomena was established. This work analyzes kinetically the three reactions mentioned before, considering typical values for the operational variables temperature, flowrate, pressure and gas composition, parameters commonly used to control the DRI formation in the Reduction Zone - RZ of the shaft furnaces. From laboratories experimental results, the kinetic equations for those reactions were established and, using the superposition principle, generated a specific global kinetic model for the iron oxide reduction and the soot formation. Finally, using those experimental results and applying a planned statistical factorial analysis for the experiments, the numerical coefficients for each equation were calculated and the correlation factor determined for the proposed global kinetic equation.

Jan 1, 2015

By Rak-lun Choi

Plasma-induced damage of InGaN/GaN multiple quantum well (MQW) light-emitting diodes (LEDs) has been studied in terms of forward turn-on and reverse breakdown voltages, together with etch rate and surface morphology. The physical degradation of sidewall along with rough surface morphology of n-GaN caused by increased ion scattering induced the deterioration of the forward and reverse voltages. It was found that the turn-on voltage is sensitive to the surface roughness of the etched n-GaN and the breakdown voltage is strongly affected by the sidewall contamination. Annealing under nitrogen after the mesa etching improved the electrical properties of the InGaN/GaN MQW LEDs. Efficient blue light-emitting diodes (LEDs) were fabricated using InGaN/GaN triangular MQWs. The LEDs with triangular QWs showed a lower operation voltage and 2.4 times higher light output power than those with the rectangular MQW LEDs at 20 mA and 20 °C. The intensity of electroluminescence (EL) at 20 mA was almost independent of ambient temperature in the triangular QW LED, but decreased substantially in the rectangular one.

Jan 1, 2003

By Michael Zinigrad

The quality of metallic materials depends on their composition and structure and these are determined by various physico-chemical and technological factors. To effectively prepare materials with required composition, structure and properties it is necessary to carry out a research in two parallel directions: Comprehensive analysis of thermodynamics, kinetics and mechanisms of the processes taking place at the solid-liquid-gaseous phase interface during welding processes and development of mathematical models of the specific welding technologies. We have developed unique method of mathematical modeling of phase interaction at high temperatures. This method allows us to build models taking into account the thermodynamic characteristics of the processes, the influence of the initial composition and temperature on the equilibrium state of the reactions, the kinetics of heterogeneous processes, the influence of the temperature, composition, hydrodynamic and thermal factors on the velocity of the chemical and diffusion processes. The model can be implemented in the optimization of various technological processes in welding, surfacing, casting as well as in manufacturing of steels and non-ferrous alloys, materials refining, alloying with special additives, removing of non-metallic inclusions.

Jan 1, 2003

By Takashi Fujii

In the OG (Osaka Gas) process which includes a fusion process of sewage disposal sludge in coke bed knowledge of molten and fluid properties of the sludge are most important to controll the process in good condition. Thus, the softening and melting temperatures and viscosity were measured by the sessile drop technique and a rotating viscometer. Obtained results are summarized as follows: Melting character of sludge slag is varied according to their composition, but closely related to CaO/SiO2 ratio in ordinary sludge and to CaO/(Cr2O3,+Al2O3+P2O5) ratio in Cr2O3 containing sludge. Fluid property of sludge slag has a correlation with optical basicity or Riboud parameter, However, the correlation is poorer than that of metallurgical slags. Especially, chromium oxide containing sludge shows high viscosity and behaves somewhat different manner from ordinary sludge.

Jan 1, 1992

By Xie Hao

According to its raw materials orthogonal test scheme is designed and a large number of systemic experiments were carried out in order to study the sintering characteristics of three types of fine ores in Kunming Iron&Steel Co.Ltd(KISC). The effects of carbon mixture ratio and basicity on sintering time, agglomeration ratio, physical properties and utilize coefficient were researched via single factor analysis and range analysis. The experimental results show the best mixture ratio of each fine ore. Analysis found that the influence of the carbon mixture ratio is more significant than which of the basicity on the sintering process except agglomeration ratio of foreign ore.

Jan 1, 2009

By Courtney A. Young

All cyanide species are considered toxic and can be found predominantly in industrial effluents generated by metallurgical operations. For example, cyanide's strong affinity for metals makes it favorable as an agent for metal finishing and treatment and as a lixivant for metal leaching, particularly gold. These technologies are environmentally sound but require safeguards to prevent water contamination. Various methods of cyanide remediation by separation and destruction are available, but certain methods are more effective than others depending on the cyanide species being remediated. Photolytic destruction is regarded as the one technique that is independent of the cyanide species involved. The destruction of various cyanide species by several photolytic techniques has been investigated for the past few years. A literature survey suggests heterogeneous photocatalysis with anatase (TiO,) should behave similarly to homogeneous photolysis with hydrogen peroxide (H,O,) since proposed reaction mechanisms for both processes involve hydroxyl radicals. However, experimental evidence on a suite of cyanide species suggests otherwise. A new mechanism for the photocatalytic destruction of cyanides, especially SAD species, is therefore proposed.

Jan 1, 1998

By Zhang Yongzhu

Developments on bioleaching of low grade ores and refractory gold ores by T. Ferrooxidans in China are summarized. Effect of the ions on bacterial growth, bioelectrochemical reaction mechanism of sulfide minerals and bacterial reaction mechanism are also discussed.

Jan 1, 1992

By Toshiaki Akahoshi

Keywords: Wasted catalyst, Hydrodesulfurization, Ammonium vanadate, Ammonium molyb-date, Hydrometallurgical process. The fundamental reactions have been investigated in order to develop a hydrometallurgical process for recovery of molybdenum and vanadium from wasted catalysts generated in the hy-drotreating desulfurization of heavy oil. The principal steps of the process are a mild oxidation roasting of the waste catalysts at temperature around 500°C, leaching of the target metal components with dilute ammoniacal aqueous leachates, selective precipitation of vanadic acid, and ammonium molybdate precipitation. The selective recovery of vanadium as vanadic acid is successfully performed using ammonium sulfate as a salting-out agent. Recovery of ammonium molybdate is based on large dependence of solubility of ammonium molybdate in ammoniacal solutions upon temperature and ammonium salt concentration. In this process, the solution after recovery of vanadium and molybdenum is recycled to the leaching stage of the roasted materials, and the ammonium salts in the process liquor is in the repeated use. Employment of am-moniacal system makes it possible to operate the roasting at much lower temperature than that for the currently operating process.

Jan 1, 2005

By G. Van Weert

The pellet reactor was developed approximately 20 years ago in the Netherlands for softening drinking water. Since then, some 35 plants have been built, ranging in capacity up to 8500 m3/h. Applications now also include removal of phosphates and fluorides and the production of metal carbonates and sulphides from waste streams. The pellet reactor consists of a fluidized bed, wherein the process solution is thoroughly mixed with the precipitation reagent at special inlet nozzles to give over-saturation of the compound to be precipitated. In water softening applications, the compound is CaCO,. In the case of nickel or other metal waste streams, Na2CO3 solution is added in sufficient amounts to precipitate metal (hydroxy) carbonate on the fluid bed particles. These grow typically to dense spheroids, which are removed when they reach 0.8 to 1.0 mm diameter. These spheroids are easily dewatered, free flowing and low dusting. The latter property is becoming an attractive advantage in connection with new plant hygiene regulations. The operation of a 60 cm diameter pellet reactor on nickel containing plating waste is described and the properties of the produced nickel carbonate spheroids are discussed.

Jan 1, 1993

By W. Petruk

A study was performed to determine whether mineral textures affect are breakage during grinding, and to establish a correlation between are breakage and mineral liberation. A base metal are from the Brunswick No. 12 deposit in New Brunswick, Canada was ground for different periods of time in a laboratory ball mill, and both the unbroken are and the ground products were studied by image analysis. Similar size distributions were obtained for material from the 15-minute grind in a laboratory ball mill (K. 0 67 pm), for the grinding circuit discharge from a commercial mill (K. 0 = 59-72 pm), and for pyrite grains in unbroken are (K,. = 74 pm). This similarity indicates that the 1S-minute grind separated weakly adhering pyrite grains along grain boundaries, and represents the limit of easy breakage for the are. At this grind (15 minutes) large discrete are mineral grains and weakly adhering interstitial fillings aIrong pyrite were liberated. On the other hand, the 15-minute grind neither separated rooderately bonded pyrite grains nor released rooderate1y bonded interstitial minerals from pyritei a 45-minute grind (K.. 31 pm) in a laboratory ball mill was required. For Brunswick No. 12 are, a 45-minute grind in a laboratory ball mill (Keo = 31 pm) is equivalent to regrinding in a commercial mill (K ?? Fl:$ 30 pm). Grinding beyond 45 minutes in the laboratory ball mill broke the are by fracturing pyrite across grain boundaries and by Chipping grain edges. Such intense grinding (longer than 45 minutes) did not markedly increase sphalerite liberation. In contrast, the intense grinding increased galena liberation because a significant proportion of the galena occurs as minute inclusions in pyrite. These findings show that ore breakage and coincident liberation depend upon size distributions, intergrowths, and mode of occurrence of the minerals in an ore.

Jan 1, 1988

By Frederico Muylaert Margem, Giulio Rodrigues Altoé, Glenio Daniel, Pedro Amoy Netto, Sergio Neves Monteiro, Maria Carolina Andrade Teles

The environmental concern is creating pressure for the substitution of high energy consumption materials for natural and sustainable ones. Compared to synthetic fibers, natural fibers have shown advantages in technical aspects such as flexibility and toughness. So there is a growing worldwide interest in the use of these fibers. Fique fiber extracted from fique plant, presents some significant characteristic, but until now only few studies on fique fiber were performed. This work aims to make the analysis of the tensile strength of polyester composites reinforced with fique fibers. The fibers were incorporated into the polyester matrix with volume fraction from 0 to 30%. After fracture the specimens were analyzed by a SEM (scanning electron microscope).