By Xuewei Lv, Maojun Zhou, Xiaobo Huang, Rende Zhang

"The characterization of the surface roughness of the mineral particles is of vital importance for the studies of the mineral processing. In this study, an evaluation of the roughness of the iron ore particles, with the measurements of size distribution and the measurements of specific surface area with the liquid nitrogen absorption, was developed. The main theory of this method is the fact that the roughness of the particle influences the specific surface area apparently. The specific surface area of the particles can be measured with the laser diffraction method and the liquid nitrogen absorption method. The influence of the surface roughness of the particle can be measured with the nitrogen absorption and cannot be measured with the laser diffraction. Therefore, the roughness can be got by comparing the specific surface area with two measurement methods.IntroductionThe characterization of the surface roughness of the mineral particles is of vital importance for the studies of the mineral processing. There are three main methods for measuring the size distribution of mineral particles: sieving, laser diffraction, and sedimentationl). Many techniques involve sedimentation such as the Horiba2, 3) and the Cyclo-sizer1). In the mineral industry, size distribution is usually determined by sieving because it can be carried out accurately for all particle sizes larger than 45 . The preferred method to obtain the size distribution of finer particles is laser diffractometry. The technique has several advantages: it produces measurements in a few minutes with considerably less labor compared with the cyclo-sizer and for a range of sizes considerably wider in comparison with the sedigraph4). The equivalent-sphere size distribution reported by laser diffractometry is valid for metallurgical calculations and can be routinely used in mineral processing plants. The surface area of the particles can be measured by the BET method of nitrogen adsorption, or it can be calculated from the size distribution. However, the latter calculation requires the size distribution to be accurately known across the whole size range, and assumptions have to be made about the shapes and surface roughness of the particles and presence or absence of pores (see below). The BET method is based on the physical adsorption of gas over the whole exposed surface area and measures the surface area stemming from the roughness and open pores on the surface of the particle5). The calculation of the surface area from the size distribution is usually based on the assumption that all the particles are smooth spheres, without considering the shape and/or roughness of the particles. Determining the surface roughness of the particle with these methods, is the objective of this study."

Jan 1, 2012

By Erich Hovestädt, Hans-Jürgen Odenthal, Christian Wuppermann, Herbert Pfeifer, Antje Rückert

"During the argon oxygen decarburization (AOD) process high-chromium steel melts are decarburized by oxygen and inert gas injection through sidewall nozzles and a top-lance. Due to the large amount of the injected processing gas, low frequency oscillations of the vessel can be observed. It is suspected that these oscillations can influence the converter's structure. The exchange of forces between fluid and the surrounding vessel is the focus of this study. An oscillation model was developed and tested, one objective being to limit the computational effort which is necessary for fully coupled and time resolved CFD and FEM simulations. Experimental results obtained from water-model studies as well as from on-sight measurements are available and were used in order to validate the numerical results. The authors' intention is a contribution towards a more in depth understanding of the factors influencing vessel vibration during the AOD process.IntroductionDuring the last four decades the AOD process has been established as a reliable and efficient refining process in stainless steel making. The injection of process gases (O2, N2, Ar) through sidewall nozzles shows advantages in mixing effectiveness compared to other injection geometries e.g. bottom blowing [1]. Stainless steel grades contain usually more than 10% chromium. With decreasing carbon content during the decarburization periods the tendency of chromium oxidation increases according to the varying chemical equilibrium which depends on the partial pressure of carbon-monoxide (CO) in the gas phase. That's why oxygen is gradually replaced by inert gases, usually argon or nitrogen, in order to lower the CO partial pressure and thus to minimize chromium oxidation. Despite the high injection velocity of approximately Ma = 1, the kinetic energy of the gas jets is consumed within a short distance from the nozzle exits due to the large density ratio between gas and melt of approximately 1:8000. With increasing distance to the nozzle exit, the initial horizontal velocity of the gas jet decreases and due to buoyancy force motion of the detached bubbles turns into a vertical direction. Subsequently a gas plume develops with its typical conical shape described by various authors [1-4]. Due to the drag force between gas bubbles and melt also the liquid phase is forced into a vertical motion. Near the free surface and the wall regions the melt flow is deflected in different directions. Subsequently, the typical flow pattern in the AOD vessel arises, as sketched in Figure 1 and described in literature [5-9]."

Jan 1, 2012

By Christian Bernhard, Mario Hartl, Susanne K. Michelic

"One aspect of an efficient process and product optimization of the liquid steelmaking process is the understanding of reactions and interactions between the components steel, slag and nonmetallic inclusions. The present paper focuses on a fundamental study of this topic by combining the powerful methods of thermodynamic modeling with systematic experiments on a laboratory scale and subsequent SEM/EDS analyses. The modeling aspect is addressed by the commercial software FactSage 6.1; laboratory experiments are performed for a low-alloyed, Ca-treated carbon steel combined with varying slag compositions. The consequent SEM/EDS analyses provide a detailed insight into the inclusion landscape which offers a strong tool for characterizing the modification of inclusions. In the present study the combination of these methods is mainly applied to oxides, due to their crucial influence on the final product quality, thus giving important indications for further optimizing the secondary metallurgy processes.IntroductionIn recent years, the range of application for steels has been enlarged continuously; also resulting in extreme surrounding conditions combined with considerable stresses for the material. This trend is directly linked with higher demands on the properties of steels. In order to optimize the final product quality, the cleanness of steels is an important criterion. For this reason, the broad topic ""Steel Cleanness"" has become one of the main research points at the Chair of Metallurgy. Next to the continuous optimization of methods for the characterization of cleanness, the primary aim is to combine thermodynamic modeling and laboratory experiments in order to describe the changes in inclusion landscape under different conditions.The steel cleanness can particularly be influenced in the processes of secondary metallurgy. In different processes the reactions and interactions between the components steel, slag and nonmetallic inclusions (NMI) are essential for the final inclusion landscape. Consequently, the understanding of the occurring reactions is a fundamental aspect for further development and process optimization. In secondary metallurgy especially oxide-slag systems consisting of the components Ca0-Ah03-Mg0-Si02, which significantly influence the modification of NMI, are of importance. Several works dealing with the interactions of oxide non-metallic inclusions with different slag systems have been published in the last years [1-4]. In order to observe the dissolution of oxides in different slag compositions a Laser Scanning Electron Microscope is frequently used. A very detailed study on the ternary system Ah03-Ca0-Mg0 and its subsystems was also done by De Aza et al. [5, 6]."

Jan 1, 2011

By Tianyou Huang, Yuan Lu, Haimin Long, Jinwu Kang, Gang Nie

"The distortion of metal parts during heat treatment process is one of the main obstacles in industry to ensure high-quality work and less or no machining allowance, especially for large but thin steel castings such as heavy turbine blades. In the paper, a method is proposed to control the distortion by adjusting heat transfer coefficient of metal parts during heat treatment process. Required heat transfer coefficients can be realized by getting the metal parts into contact with various media such as water spray, insulation felt or materials with different heat conductivity. The control method based on this idea is set up and achieved. By using insulation felt and water spray to change the heat transfer coefficient during the stages of heat treatment process, the results indicate that the proper control time and vary with materials.IntroductionThe distortion of metal parts during heat treatment process is one of the main obstacles in industry to ensure high-quality work and to realize less or no machining allowance [1]. For example, the Three Gorges turbine blade’s distortion is as large as 50mm during heat treatment process. The uneven heating and cooling during heat treatment process is the main reason for distortion [2]. By adjusting heat transfer coefficient of different areas of metal parts, the heat treatment process could be controlled. The temperature variation, direct cause for distortion, could be under control. Loeser Klaus used high pressure gas to achieve uniform heat transfer during gas quenching and proposed the possibility to use ""Dynamic Quenching"" processes where the quenching severity is varied during quenching by stepwise control of either gas velocity or gas pressure [3]. Li Zhichao also suggested minimizing distortion by marking a component into several areas and imposing different heat transfer coefficients on each area [4]. Heat transfer coefficient can be controlled by getting the metal parts into contact with different media such as water spray, insulation felt, air or different heat conduction materials. In addition, the exact time to adjust the heat transfer coefficient is another factor for distortion. A method is presented in this paper by actively adjusting heat transfer coefficient for different areas of metal parts and different stages of heat treatment process to control their distortion. The corresponding experiments have been made by using different metal materials."

Jan 1, 2012

By Toshiro Kuji, Masakazu Fujita, Tetsuji Saito

"The magnetic properties of the magnetic materials were deeply dependent on the microstructures. In this study, the novel technique to produce the desired microstructures in a controlled manner was proposed. The technique consisted of the production of the amorphous alloys and the control of the crystallization process. The technique was applied to improve the magnetic properties of Nd-Fe-B permanent magnets. The microstructural control of the magnets exhibited the excellently high energy-products of higher than 430 kJm-1. The relationship between the magnetic properties and the microstructures of the Nd-Fe-B permanent magnets was discussed.IntroductionThe intrinsic properties of the materials are basically determined by the properties of the constituent elements or the compounds. However, it is often noticed the difference between the observed properties and the theoretical values expected from the intrinsic properties of the materials. This indicates that the observed properties of the materials are determined not only by the properties of the constituent elements. In other words, the observed properties of the materials are also strongly dependent on the morphology of materials. This means that the microstructural control may creates a great improvement of the properties of materials.In Nd-Fe-B permanent magnets, the superiority arises from the uniaxial intermetallic Nd2Fe14B compound which has a large saturation magnetization and a high anisotropy field [1,2]. The magnetic properties of the Nd-Fe-B permanent magnets are dependent on the microstructure, that is, the size, shape and degree of the crystallographic alignment of the Nd2Fe14B phase. Currently, the Nd-Fe-B permanent magnets have been produced by either sintering or melt-spinning [3,4]. In the sintered magnets, alignment of the Nd2Fe14B phase is achieved by the prior green compaction of the crushed ingot powders in an applied magnetic field [3]. In the melt-spinning approach, alignment of the Nd2Fe14B phase is achieved by hot deformation [5]. Amorphous melt-spun ribbons are comminuted and then are consolidated into bulk form by hot pressing before hot deformation. As-hot-pressed magnets have randomly oriented Nd2Fe1~ grains [6]. Subsequent die upsetting of as-hot-pressed magnets gives rise to the crystallographic alignment of the Nd2Fe14B phase."

Jan 1, 1998

By Tuula Mäkinen

In 1959 Outokumpu started up an integrated nickel smelter and refinery at Harjavalta. The flash smelting ? Peirce-Smith converting route was applied, and the high-grade converter matte was further refined to nickel cathodes by leaching and electrowinning. In 1995 the production capacity was increased from 17 000 mtpa to 52 000 mtpa, based on the Direct Outokumpu Nickel Smelting Process. The additional refinery capacity is based on hydrogen pressure reduction, producing nickel powder and briquettes. The smelting operation is currently part of Boliden Group and the nickel refinery part of OM Group. In the DON technology, high-grade nickel matte with low iron content is produced in the flash smelting furnace directly without subsequent converting. The metal values in the smelting slag are recovered in an electric furnace as an iron containing Ni-matte. The mattes produced differ from the conventional nickel mattes in many respects, and therefore focused R&D efforts have been made in order to cope with their melting points, fluidities and settling properties. When developing and operating metallurgical processes it is crucial to manage and control the characteristics of the products as well as by-products generated in different steps of the process chain. The low melting points of the high-grade nickel mattes produced in the DON furnace, particularly those low in copper, have pointed out challenges in the furnace design, in particular in the hearth and its thermal engineering. Also key issues of the DON technology are smelting of high-magnesia concentrates, the recoveries of nickel and copper, as well as those of PGM`s and cobalt. These factors can be affected by a proper selection of the process concept, and the operational conditions in the processing vessels. This paper deals with the experience of the DON technology gained over the first ten years of operation, including the significant environmental impacts. Selected results of the thermo-dynamic modelling of DON and EF mattes and high-magnesia slags are reviewed, with the reference to the mattes produced. Also the design principles of the FSF and EF will be discussed.

Jan 1, 2006

By Tim J. A. Smith

Fundicion Refimet S.A. has operated a custom copper smelter at La Negra, near Antofagasta in northern Chile since 1993. From an initial operation based on Reverb smelting and Peirce-Smith, converting, the plant was expanded from 90 000 t/y to 160 000 t/y copper production in early 1997, by conversion to oxy-fuel smelting and use of concentrate injection on Converters. As part of this expansion a novel reverb gas cooling and cleaning system was developed and designed by Kilborn SNC-Lavalin Europe, the London, UK-based mining and metals; Office of Canada's SNC-Lavalin group. The reverb gas cooler needed to satisfy several very specific requirements including low cost, flexibility, robustness and simplicity of operation. Of particular importance was the requirement to cool and clean the ,oxy-fuel reverb gases and render them suitable for subsequent treatment in a conventional sulphuric acid plant. It was also important to avoid accretion or dust handling problems. This paper describes the key design features and subsequent successful installation, commissioning and operation of the unit.

Jan 1, 1998

By Dai Xi

In the present work, the viscosities of molten FenO-MgO-SiO2 and FenO-MgO-CaO-SiO2 semi-synthetic slags for nickel flash smelting were measured in the temperature range from 1473 to 1723K by a rotational viscometer. The ratio of Fe to Si02 was fixed at 1.2, calcium and magnesium oxide contents varied in the range from 2 to 8 mass% and 9 to 12 mass%, respectively. The results showed that silicate anions became smaller by increasing CaO content, which results in a decrease of the viscosity of the slag. In the case of MgO addition the viscosity behavior was complicated. At MgO content below II mass%, the viscosity increased with the increase of MgO at all temperatures tested. However, when the MgO content was above II mass%, the viscosity decreased slightly for FenO-MgO-CaO-SiO2 system. At higher MgO contents, low-viscosity slags can be obtained by adding CaO. At a given composition, .the viscosity decreased with increasing temperature. The higher the temperature, the more MgO can be added before saturation. The effect of Fe3O4 on the viscosity was quite significant. The viscosity of slag increased by 300mPa-s at 1573K when Fe3O4 content varied from 3 to 9 mass%. The viscosity values are presented as the functions of temperature and composition. A comparison between FenO-MgO-SiO2 and FenO-MgO-CaO-SiO2 systems is given in this study.

Jan 1, 2003

By Kunihiko Takeda, Kimio Imaizumi, Tsuyoshi Arai

"The study on the preparation of mono-dispersed liquid droplet was performed using ultrasonic as one of the steps of producing the perfectly mono-dispersed particle. The ultrasonic system was a 33.6kHz ultrasonic generator, an amplifier, an electric distortion element, and a bolted Langevin type horn installed in .a cell. For the first time, a liquid pillar under a nozzle of the cell ·was stably formed. Then, dense and coarse parts were alternatively constructed by oscillating the wavelength of the ultrasonic.· The diameter of those liquid droplets were found to be· perfectly uniform, therefore, it was measured by ""multiplex photography"" using a synchronized stroboscope with the ultrasonic.- From the results, more than 30,000 of perfectly uniform liquid droplets in 1 second were observed by this method.IntroductionRecently, research on the control of physical form is done in various fields of industry. Some examples are the processing technology of the minute compound material of micro-machines and integrated circuits, and the form control of molecule size like catalysts. There is a need for such material to take on various forms in correspondence to its use. ""Form control"" as used in this study will indicate ""research on physical chemistry factors which determine the size of the material"" and will refer to the contour uniformity of comparatively little particles. A well-known method of preparing particles is to spout a mist of liquid and slurry from a nozzle l) 2). Particles for metals, catalysts and food have been prepared by this method. In this case, although an approximate particle diameter can be decided by controlling the nozzle diameter and the violent outflow velocity, it is not easy to completely control ·the contour and to prepare a particle with uniform diameter. ·However, the preparation of perfectly uniform particles is necessary for solders for the adhesion of electronic wiring 3), ion exchange resins4), catalysts and so on. Large quantities of fine particles and super-fine particles are generated when manufactured in the usual way. Large quantities of these fine· particles and super-fine particles have polluted the internal and external' environments of factories. The products yield' ·decreases, also. From such a background, this study examines the preparation of perfectly uniform particles that could be· collected -100% as products. Recently, NASA has succeeded in the preparation of perfectly uniform particles in zero gravity 5). But the preparation of 'perfectly uniform particles by this method is difficult, and it can not be used in general industry"

Jan 1, 2000

By E. J. Peuraniemi

Recently commissioned Kennecott-Outokumpu flash converting was developed to replace the approved but environmentally outdated Peirce-Smith -converting to satisfy the globally tightening emission regulations. In the present study, dust formation and reaction mechanisms of two copper mattes with different experimental parameters were studied in lean suspension conditions. Both mattes had very high copper content of approximately 75 wt% and low iron content of 4.5 wt% and 1.2 wt% Fe. A laboratory scale, vertical laminar-flow furnace with a low feeding rate was used to simulate the phenomena taking place in the reaction shaft of a flash converter. Experimental conditions included temperature of 1300 °C with reaction gas oxygen contents of 20 vol%, 50 vol%, and 75 vol%. In the experiments, sieved particle fractions were fed to the furnace and sampled after short reaction time intervals by quenching them into a water film. Collected particles were analysed chemically for their main elements to define their removal rates. Also, optical and scanning electron microscopy with EDS-analyser were applied to determine phenomena occurring during reactions. Kinetics of oxidation as well as ignition of particles are discussed. Changes in particle morphology, size, and composition are reviewed to describe dust formation and reaction mechanisms.

Jan 1, 1999

The merging of flash smelting with spray converting in one single furnace is proposed as a continuous copper making process. The proposed process is expected to produce blister copper, clean slag and gas with high sulfur dioxide concentration. Some high grade matte is an intermediate product recycled within the proposed furnace, spray-atomized and converted. The thermodynamic equilibria of the simultaneous oxidations which take place during copper smelting and converting are discussed in order to establish the gradient of oxygen potential along the furnace required for smooth operation. The proposed process is a dynamic system designed to reach equilibrium only close to the slag skimming end of the furnace. The process feasibility is based on the predesigned significant difference between the rates of converting reactions in a finely dispersed system and the rates of deconverting reactions between immiscible liquid phases of restricted interface area. The converting of small stationary droplets of matte, in a silica saturated system, was studied in the laboratory for extremely short oxidation times (10 to 120 seconds). These experiments led to some interesting observations on reaction mechanisms and kinetic trends. The droplet size and the matte grade affected very strongly the oxidation rate and the proportion of the different products obtained.

Jan 1, 1976

By Martin Brueggemann

The Tyrone copper solution extraction and electrowinning plant was the first such facility built by Phelps Dodge Mining Company in 1984. Over the next 20 years, the aqueous flow rate capacity of the plant has been expanded from the original design of 12,000 gallons per minute (gpm) to 34,000 gpm to meet production goals in the face of declining copper grades in the leach solutions. The ability to process higher aqueous flow rates through existing equipment comes at the expense of increased organic loss through entrainment to raffinate. These losses of organic (diluent and extraction reagents) can account for up to 10 percent of the plant?s total operating costs. With the recent dramatic price increase of petroleum-based products, these operating costs due to losses are sure to increase. This paper will discuss recent improvements at the Tyrone SXEW plant that have resulted in a 40 percent reduction of organic losses. These improvements include picket fence modifications, new fence materials, organic recovery systems, and operational practices within the solution extraction process.

Jan 1, 2006

By Susumu Okabe

The Mitsubishi Continuous Copper Smelting/Converting Process employs an electric furnace for settling the slag/matte mixture formed in the smelting furnace. In order to improve the separation of slag and matte and to minimize power consumption, the design and the operating conditions of the electric furnace should be optimized. As the first step, numerical heat and fluid flow analysis of the melts was carried out based on the distribution of current density and Joule?'s heat obtained by the electric field calculation. For these calculations, 3-D body fitted coordinate system and a finite volume method were applied. Using the developed numerical model, the flow pattern analysis by pulse input of a tracer element was simulated. It was found that a strong thermal convection of the molten slag exists around the electrodes due to the concentrated Joule's heat generation in a small area just under the electrodes, and this strongly affects the flow pattern in the furnace. The calculation results were compared with the data obtained from 'a plant test.

Jan 1, 1998

By Björn Hinzel, Joachim Rösler

"The most important characteristic of open-pored metals is porosity, since it enables all of their functional applications as filters or sound absorbers. Due to the notch effect of the pores, mechanical properties of porous metals are better than the ones of comparable structures made of polymers or ceramics. Consequently, only open-pored metals can be used in aircrafts to reduce flow noise or noise resulting from the core engine by acoustic absorption. Absorption properties depend highly on pore size and porosity of the material, which must be characterized as precisely as possible in order to analyze the correlation between morphology and noise reduction performance. Here, a line segmenting method is explained in order to characterize pore size and porosity of absorber materials using image processing based on two dimensional microscopy images, including sample preparation and specification of the set-up. Then, the influence of the pore structure on the measured absorption behavior is discussed. Finally, the correlation of acoustic behavior, pore morphology, and porosity is outlined.IntroductionSignificant noise loads affect everyone causing anxiety, depression, insomnia and other effects which impair health and productivity [1],[2]. Due to the rising number of flights and aircrafts, air traffic noise increases dramatically. To counter this development, various approaches have been developed to reduce the different noise sources resulting from airframe, jet or engine [3],[4],[5],[6]. One approach to reduce this noise is the application of noise reducing liners in the hot gas path [7]. This is especially important, since the engine is becoming the dominant noise source of modern airplanes during take-off [8]. Due to the elevated temperatures and high fatigue loading in this part of the aero-engine, conventional passive absorber materials cannot be used. Polymers would not be able to bear the heat and ceramic fibers would crack under the mechanical loading due to the notch effect. Consequently, this study focuses on metals with open pores, which can resist elevated temperatures and fatigue loading and additionally resemble geometrically conventional passive absorbers. Based on the production processes, e.g. sintering of metal fibers [7], powder processing using a foaming agent [9], coating of polymer foams [10], or using melt infiltration techniques [11], the characteristic dimension of the porosity is usually in the range of 0.01-10mm. In this work, sintered metals and metal sponges are analyzed after the theory of sound absorption is briefly outlined. Then, measurements of the acoustic absorption of metal sponges and sintered metals in an impedance tube are performed. To understand and predict the acoustic properties of metals with open porosity, it is necessary to characterize the materials as precisely as possible. This is explained in detail using a line segmenting technique, followed by a discussion of the connection of pore characteristics and acoustic absorption. Finally, a conclusion is given."

Jan 1, 2012

By John Nauman

Liquid ferrous silicates that are related to cop- per slags have been studied as media for the transfer of heat in pyrometallurgical processes. The effective thermal diffusivities have been measured from 1025Oto 1400°C, and values in the range of 0.004 to 0.007 cm2/ sec have been obtained. The heat-transfer characteristics of these slags have been determined by measuring the rise of temperature of a cold nickel sphere immersed in the liquid slag. The sphere is spun about its vertical axis to obtain a well characterized flow of liquid about the sphere. The principal barrier to the transfer of heat from the bulk slag to the metal sphere is a solid shell of slag that forms around the sphere and subsequently melts. It appears that the detailed nature of this shell is important to theheat- transfer process. A mathematical model is used to predict the rate of heating of the sphere, and to evaluate various aspects of the system that can influence the transfer of heat.

Jan 1, 1976

By X. J. Wu

Effects of various factors such as diaphragm materials, composition of electrolytes and current density on copper electrowinning from cupric chloride solutions was investigated. It is found that the crux of this process is to prevent the dissolution of copper by cupric ion and the formation of suspended CuCl precipitate. A process with high difference of copper concentrations between the feed solution and the spent electrolyte was selected. With this process, in which the feed solution contains 90 g/dm3 [Cu"], 3M NaC1, and 10mg/dm3 bone glue, and the spent electrolytes contains 10 g/dm3 [Cul, a very smooth and dense copper cathode can be produced with current efficiency above 93% and energy requirement less than 1.7 kwh/kg Cu at 25°C with N2 sparging. If a slightly higher energy requirement is permitted, smooth and dense copper cathodes can be produced at the current density up to 800 A/m2 with the identical solutions.

Jan 1, 1991

By María Cristina Ruiz

In the processing of copper concentrates by the conventional smelting-converting technology, complying with the increasingly severity of environmental legislation in some countries has become difficult, mainly due to severe fugitive emissions of gases produced during the batch PS (Peirce-Smith) converting step. In this work, the results of an investigation on the pressure leaching with sulfuric acid and oxygen of white metal (produced in a Teniente Converter reactor) are discussed. The study was carried out at laboratory scale and the main variables studied were temperature, concentration of sulfuric acid and partial pressure of oxygen. The experimental results indicated that most of the sulfur in the white metal was oxidized to sulfate in the whole range of temperature studied (105ºC to 150 ºC). The concentration of sulfuric acid over 0.05 M, and oxygen partial pressure over 6 atm had little effect on the dissolution of copper from the white metal. On the other hand, temperature had the most significant effect on copper dissolution; below 130 ºC copper dissolution was incomplete after 5 hours of leaching while at 150 ºC the dissolution was complete in 90 minutes and 10 atm of partial pressure of oxygen

Jan 1, 2006

By S. -H. Jeon, Y. -S. Choi

"The three dimensional current distribution on the rectangular cathode is predicted using a boundary element method with a linear element of trigonal type. The effect of cell geometry and anode shape on current distribution is simulated. Calculated results compare well with experimental results. The proper combination of anode size and distance between electrodes increase the current uniformity.The importance of electrodeposition as a fabrication technology in the electronics industry is large and growing. The main advantages of this wet processing method, in comparison to other dry processing methods, lie in its high yield, rapid processing and low cost. In nearly every application of electrodeposition the pursuit of deposit uniformity, especially thickness uniformity, has been technically imperative. The thickness uniformity of the deposit depends largely on the current distribution over the cathode. The current distribution is primarily determined by the geometrical characteristics of the electrodes and the cell. Also the polarization at the electrode surface and the mass transfer affect the current distribution.The current distribution is an important consideration for those involved in designing electrochemical systems and electroplating systems in particular. Although it is important, the common practice in industry is to use trial and error method to design the cell that optimize the uniformity of current distributions in electroplating. The purpose of this paper is to illustrate the useof boundary element method to predict three-dimensional current distribution in rectangular cell.The calculation of the current distribution is possible by various numerical techniques, which include the finite difference method (FDM)1, the finite element method (FEM)2, and the boundary element method (BEM)3,4. These methods of the numerical calculation have various problems, respectively, but the BEM is considered to be the most efficient. This is due to the fact that the BEM has the advantage of solving field equations only on the surface of a calculation domain. A good comparison between the BEM and the FEM for the secondary current distribution in a Hull cell was made by Matlosz et al.5The fundamentals on the theory of current distribution in electroplating are well-established in the literature by a number of authors.6, 7, 8 However, a small fraction of these works have been specially addressed to three-dimensional analysis, and, mostly thel·10 have focused on the problem qualitatively rather than quantitatively.Extending the previous work to three-dimension, we developed the program for the quantitative calculation of 3-dimensional current distribution using a boundary element method with a linear element of trigonal type. Integrals with singularity from the fundamental solution have been analytically computed and it is shown in detail in the Iiterature11. This paper deals with the three dimensional current distribution for the electrode position of copper in a cubic type cell and the effect of anode shape, size and the distance between electrodes on current distribution is studied."

Jan 1, 1997

By Shantaliu S. Shevade, Muhammad M. Rahman

"This paper presents a systematic analysis of fluid flow and heat transfer processes during the magnetic heating of the substrate material. Heat is generated in the substrate material when a magnetic field is imposed due to change in orientation of the molecules. As a result, the substrate temperature rises. The i;tudy considered microchannels with rectangular and square cross section with heat generation in the substrate due to imposed magnetic field. The results computed were for Gadolinium substrate and water as the working fluid. The purpose of this study is to explore the transient heat transfer coefficient when the fluid is circulated through the substrate via microchannels. Equations governing the conservation of mass, momentum, and energy were solved in the fluid region. In the solid region, heat conduction was solved. From the simulation results, plots of Nusselt number and heat transfer coefficient were obtained over the length of the channel. A thorough investigation for velocity and temperature distributions was performed by varying channel aspect ratio, Reynolds number, and heat generation rate in the channel. It was found that the peripheral average heat transfer coefficient and Nusselt number is larger near the entrance and decreases downstream because of the development of the thermal boundary layer. With the increase in Reynolds number, the outlet temperature decreased and the average heat transfer coefficient increased.IntroductionMagnetocaloric effect (MCE) is the heating or cooling of the magnetic materials due to varying magnetic field. The effect was originally discovered by Warburg. Magnetocaloric materials store heat energy in the way the atoms vibrate and in the way electrons spin within each atom. More heat energy increases the vibrations and also makes the spins more random. When a strong magnetic field is applied to a magnetic material, the magnetic moments of its atoms become aligned making the system more ordered. The more ordered material has lower entropy and compensates for the loss by heating up. When the magnetic field is removed, the magnetic moments return to their random directions, entropy increases and the material cools. Gadolinium is a magnetic material that exhibits high temperature rise during adiabatic magnetization around its transition temperature of 295 K. It has been experimentally observed that adiabatic temperature rise increases with magnetic field strength and can be as high 20 K when a magnetic field of IO T is applied. Thus magnetic field, when applied to a microchannel heat exchanger, causes temperature change in the magnetic material. The fluid flowing through the channel gets cooled or heated due to this adiabatic temperature change."

Jan 1, 2004

By S. K. Kawatra

"A typical steelmaking facility produced 50,000 tons per year of slag in their hot-metal desulfurization process. This slag had a sufficiently high iron content that it could be beneficiated and recycled in a blast furnace, provided that the slag could be agglomerated into pellets suitable for use as blast furnace feed. In this work, beneficiated slag was agglomerated using both a conventional bentonite binder, and a fly-ash-based binder (FBB) that was formulated by the investigators. The FBB consisted of a combination of highcarbon fly ash with calcium hydroxide activator, allowing the FBB to exhibit binding properties when moistened. It was determined that beneficiated slag agglomerated with FBB had superior compressive strengths compared to slag agglomerated with conventional bentonite binder. The FBB is therefore a satisfactory method of binding the agglomerated slag. Since the fly-ash component of the FBB is commonly discarded as waste, this approach also provides a means for utilizing high-carbon fly-ashes that currently have very little commercial value.IntroductionIn 2006 approximately 72.4 million short tons of fly-ash were produce in the United States [1]. The majority of fly-ash which was used that year was consumed concrete, structural fills, and cement. It is also used in road base, aggregate, and other applications. However, 55.2% of the fly-ash produced in 2006 was not utilized and ended up being sent to a landfill. Essentially all of the land filled fly-ash could be a suitable binder for pelletizing desulfurization slag and other steel plant waste oxide materials. Fly-ash based binders (FBB) have been shown in laboratory studies to be suitable for producing iron ore concentrate pellets of equivalent strengths as those bonded with bentonite [2,3,4]. The utilization of highcarbon fly-ash within the market is important for reducing the volume of currently unmarketable and land filled fly-ashes. FBB would be a much cheaper alternative to the current bentonite binder or organic binders used for iron ore concentrate and would help to reduce pellet costs. Currently, transportation more than doubles the final cost of bentonite since it is produced hundreds of miles from the pelletizing plants, while fly-ash is produced from power plants located nearby pellet plants and steel mills. FBB’s also show promise for use in other high volume applications such as foundry sand mold binders."

Jan 1, 2008