By J. F. Myers, F. M. Lewis

This second progress report of grinding presents comments regarding ball consumption and data pertaining to the hydroscillator, which is closed circuited with the tricone mill. A study and postulate of how balls function is presented. The paper summarizes cost reduction obtained by the method of "grinding for the tail race" rather than for "mesh tons."

Jan 11, 1950

Stripping of the Exotica open-pit mine, which is proceeding at about 120,000 tpd, is dwarfed by its proximity to the 500-million-ton Chuquicamata tailing pile. The excavating work is being carried on smoothly and efficiently and, as of the end of October, accounts for the removal of 77 million tons of total material of which some 200,000 tons is stockpiled ore. Diamond drilling has outlined an orebody 5900 ft long and 3400 ft wide containing an estimated 153 million tons of ore at 1.35% recoverable copper based on 80 % extraction.

Jan 11, 1969

By A. A. Archer

Marine mining is here defined as the commercial recovery of minerals other than oil and natural gas from the surface of, or below, the seabed by operations connected only indirectly with the land. The number of operations falling within this definition and the number of countries involved are remarkably limited in view of the widespread interest shown in marine mining prospects during the last few years. Marine mining is still restricted to continental shelves, where the only superficial minerals currently being mined are sand and gravel, calcium carbonate in different forms, and tin and iron sands.

Jan 12, 1973

By J. C. Kerkering, J. C. Franklin, T. O. Meyer, R. W. McKibbin

Abstract-A continuous survey of radon gas was made in two interconnecting stopes in a southwestern U. S. uranium mine to determine how the various phases of the mining cycle affected the radon concentration. The radon was monitored continuously with five detectors. One detector monitored the intake air, one the exhaust air, and three the stope air. The radon concentrations present during slushing, blasting, and exhaust fan shutoff were compared with concentrations on a nonwork day as a base level. Inside the stope, the radon concentration increased about 40% during slushing and 425% after blasting. Intake air radon increased 1600% and the stope air increased 550% while the surface exhaust fan was off.

Jan 6, 1978

By John M. Hartman

The high temperature of the blast of modern furnaces renders it desirable that the pipe conveying the blast into the furnace crucible shall transmit and radiate as little heat as possible. To accomplish this, the pipe shown in the accompanying sketch was devised and patented. It consists of a slide-valve, leg-pipe, and belly-pipe, which are held together and to the tuyere by a system of levers and links. The slide-valve is superior to the old throttle-valve. The legpipe is formed of two thicknesses of wrought-iron pipe, with a space of half an inch filled in with clay and brick. The belly-pipe is made in the same way as the leg-pipe, and terminates in a globe face to suit the tuyere. The quarter turn is made extra thick, of cast iron, and the cap on the end is lined with clay also. The catches, A, B, C, are merely for convenience in putting the pipe together. The joints D and E are globe faces, and allow the pipe to adjust itself to any angle. The eye-piece is made of violet glass, which cuts off the glare from the bright coals in the furnace and allows a close examination of the interior, so that any water dropping or vapor can be detected. The glass does not become coated with dirt, like mica. Since good running of furnaces is shown by a bright tuyere, it is necessary to have a good eye-piece to examine them. To detach the pipe, a man lifts the weights, the side rods are then slipped off the bell crank under the quarter turn, the link under the belly-pipe is unhooked, and the pipe carried away. The same process is reversed to put the pipe together. The nozzle is changed by taking off the cap, G, drawing the nozzle through the belly-pipe, and inserting another. In this way the change can be made quickly, without taking down the pipe. On the old tuyere pipe bolts with brass nuts were used, which burned up and gave trouble. In other cases key-bolts were used, making it difficult to adjust the pipe. Bolts make too rigid a joint, and there is no provision for movement from contraction or expansion. As the temperature of the blast increases there is more expansion, and where rigid joints are

Jan 1, 1879

By John M. Hartman

THE high temperature of the blast of modern furnaces renders it desirable that the pipe conveying the blast into the furnace crucible shall transmit and radiate as little heat as possible. To accomplish this, the pipe shown in the accompanying sketch was devised and patented. It consists of a slide-valve, leg-pipe, and belly-pipe, which are held together and to the tuyere by a system of levers and links. The slide-valve is superior to the old throttle-valve. The leg-pipe is formed of two thicknesses of wrought-iron pipe, with a space of half an inch filled in with clay and brick. The belly-pipe is made in the same way as the leg-pipe, and terminates in a globe face to suit the tuyere. The quarter turn is made extra thick, of cast iron, and the cap on the end is lined with clay also. The catches, A, B, C, are merely for convenience in putting the pipe together. The joints D and E are globe faces, and allow the pipe to adjust itself to any angle. The eye-piece is made of violet glass, which cuts off the glare from the bright coals in the furnace and allows a close examination of the interior, so that any water dropping or vapor can be detected. The glass does not become coated with dirt, like mica. Since good running of furnaces is shown by a bright tuyere, it is necessary to have a good eve-piece to examine then. To detach the pipe, a man lifts the weights, the side rods are then slipped off the bell crank under the quarter turn, the link under the belly-pipe is unhooked, and the pipe carried away. The same process is reversed to put the pipe together. The nozzle is changed by taking off the cap, G, drawing the nozzle through the belly-pipe, and inserting another. In this way the change can be made quickly, without taking down the pipe. On the old tuyere pipe bolts with brass nuts were used, which burned up and gave trouble. In other cases key-bolts were used, making it difficult to adjust the pipe. Bolts make too rigid a joint, and there is no provision for movement from contraction or expansion. As the temperature of the blast increases there is more expansion, and where rigid joints are

Jan 1, 1879

By S. Shapiro, J. A. Ford

The crystallo graphy of several grains of the lamellar Ni-Ni3 B eutectic solidified under conditions appvoachirt equilibriun has been examined.. A preferred interlace relationship has been observed in this system which may be described as: A detailed study of this interface by means of an atomistic model reveals the interface Plane to be puckered and more accurately describable as: Analysis of the atomic configuration on these planes reveals that this interface conforms to the orientation criteria proposed for directionally solidified lanzellar eutectics. In addition, a model is proposed to help explain the growth of a "puckered" interface. DURING the past several years an increasing number of unidirectional solidification experiments on eutectic alloys have been reported in the literature. The primary emphasis, in most cases, has been the effect of growth variables on microstructure. Some authors have, however, studied the crystallographic orientations and interfacial relationships resulting from these experiments. Four crystallographic studies have been published;'-4 in each of these there is a factor which tends to prohibit the extension of the observations beyond the particular system. In the Al-CuA12 system, the approximately equal volume fractions of the phases have resulted in sorrie controversy as to which phase constitutes the matrix. In the Mg-Mg,Sn eutectic the presence of several interconnecting lamellar systems2 complicates the analysis. The two remaining eutectics. 1nSb-b and Al-Ali, are both rodlike (the latter exhibits a plate morphology at low solidification rates): the matrix in each of these alloys is the simpler (fcc) phase. Studies of nucleation in eutectic alloys indicate that the more complex constituent is the nucleating -.phase.' For the purpose of an analysis of interface crystallography it was deemed desirable to study a lamellar system in which the matrix was the more complex and, presumably. the nucleating phase. Recently it has been shown that there is a eutectic in the Ni-B system between Ni3B and i; preliminary investigation by the authors indicated that the matrix in this eutectic is the boride phase. The structure of Ni,B is reported to be orthorhombic, the compound being isostructural with cementite. This eutectic is therefore analogous to that between austenite and cementite. Furthermore, the Ni-B system is not susceptible to a competing eutectic reaction as occurs in the Fe-C alloys; nor does it exhibit a eutectoid decomposition. For these reasons the study of the interfacial relationship in the Ni-Ni3B eutectic was undertaken. PROCEDURE Ingots of nominal composition 3.5 and 3.6 wt pct B were induction-melted in boron nitride crucibles within a graphite susceptor under a boric oxide slag; a dynamic argon atmosphere was maintained over the melt to prevent rapid oxidation of the susceptor. The raw materials used were 99.97 pct Ni from Huntington Metals Division of International Nickel Co. and 99.8+ pct B chips supplied by the United Mineral and Chemical Co. The analyses of the starting materials are listed in Table I. The melt was held at 1500cC for 2 hr to insure complete reaction and allowed to cool to room temperature. The castings were chemically analyzed for boron and were metallographically examined for uniformity. The metallographic samples were mechanically polished through 0.1 p A1,0, and etched with Carapella's reagent. Each master casting was cut up to make several specimen blanks which were remelted, in boron nitride crucibles, to form ingots of 1/2 to 3/4 in. in diarn by 7 in. long. These ingots were unidirectionally solidified using a modified vertical Bridgman technique. The rate of solidification was assumed to be equal to the uniform rate at which the crucible-susceptor assembly was withdrawn from the induction coil. This rate was varied from 1.18 to 2.21 cm per hr. In order to perform these experiments it was found necessary to redetermine the eutectic composition. This was accomplished by the zone-melting technique described by Yue and lark.' An ingot of 4.5 wt pct B was zone-melted in a horizontal boron nitride boat 7-1/2 in. long with a 112-in.-square cross section. A

Jan 1, 1967

Jan 1, 1931

By Iichiro Omori

THE Mabuki process, a Japanese hearth process for the treatment of matte, uses the same princi-ple as the Bessemer steel process. The only difference between the two is that in the Mabuki proc-ess a hearth furnace, not a converter, is used. Though the hearth is not as good as the converter, the first cost is very low and the capacity is compara-tively small; so the process is most suitable for smelters FIG. 1.-PLAN AND SECTION OF HEARTH. having a small production. To construct the hearth, an excavation, 6 ft. in each dimension, is made in the ground and a drainage channel is dug at the bottom. Then all side walls are faced with stone or slag brick and the cavity is filled with fireclay or brasque, except the hearth at the top.

Jan 9, 1922

By E. S. Machlin

The wzodel of Blandin and Diplunt;, generalized to include a phase factor, is applied to the carbon-carbon interaction in iron. Darken&apos;s "energetic" model is generalized to include not only first neighbor interactions but further neighbor interactions as well. On the bases of these generalized models relations are derived for the activity of carbon in both austenite and ferrite in terms of the carbon-carbon Pair interaction energies. A single function then yields the pair interaction energies consistent with the experimental activities of carbon in both ferrite and austenite. Thus, a simple explanation is given for the observation that the nearest-neighbor interaction between carbon is repulsive in austenite and attractive in ferrite. Certain consequences of this approach are explored. OnE object of the present paper is to attempt to take into account the consequences of electrostatic contributions to the carbon-carbon pair interaction energy for carbon as a solute in iron. Friedel&apos; has shown that oscillations in electrostatic potential are to be expected about a solute atom in a metallic solution. Blandin and 6lant6&apos; have shown that such oscillations yield an interaction energy between pairs of solute atoms that obeys the relation: W{ = A cos(2ftFri + 4>)/(kFri)3 [l] where kF = Fermi wave vector, ri = distance between solute atoms comprising the pair7 <p = phase factor dependent only on electronic nature of solute and solvent, A = coefficient dependent only on electronic nature of solute and solvent. Machlin3 found that Eq. [I] accurately described the pair interaction energy derived from short-range order measurements based on field ion microscope observations of dilute alloys of platinum. He also found that the value of the phase factor $ derived from residual resistivity measurements agreed well with that obtained from the analysis of the short-range order data. Harrison and paskin4 were able to predict the long-range ordering energy of 0 brass using Relation [I] and residual resistivity values to predict the value of the phase factor $. Machlin5 has repeated their analysis and applied it to the prediction of the long-range ordering energy in AgZn and AgCd with excellent agreement between prediction and experiment. Both A and $ are independent of the crystal structure. The Fermi wave vector depends uniquely upon the conduction electron concentration per unit volume in the spherical approximation of the Fermi surface. Thus, Eq. [I] is expected to apply to both fer- rite and austenite with only one set of values of A and $. Mossbauer studies6 yield the result that iron has one 4s electron. We shall make an assumption found to hold previously for platinum3&apos;7 and nikel, which is that only the s electrons are involved in shielding the perturbing potential of carbon. With this assumption, kF = 1.35 A-l. Although A and $ may be obtained from certain mdels&apos;&apos;&apos; we shall take A and $ to be empirical constants in the spirit of Kohn and osko.&apos; Thus, Eq. [I] involves two adjustible parameters. Consequently, two independent relations in A and $I are required in order to evaluate them for carbon as a solute in iron. We may use a recent analysis of Aaronson, Domain, and poundg who showed that Darken&apos;s energetic model,1° as well as others, can be used to describe the activity-temperature data for carbon in iron in both the aus-tenitic and ferritic phases. Darken&apos;s model takes into account only first neighbor pair interactions. For our needs, all neighbor pairs need to be taken into account. It is convenient to generalize Darken&apos;s model. The result for the partition function for austenite is: over the temperature range 800" to 1200°C and where the uncertainty corresponds to one standard deviation. Eq. [4] effectively yields only one relation. Another relation is required to obtain unique values for A and $. One property of Eq. [4] is that it is independent of crystal structure. Hence, data for a iron can be used to obtain another relation. To arrive at this relation we must generalize Eqs. [2] and [3] so that they may be applied to the bcc a iron. The result is that:

Jan 1, 1969

By Ralph Arnold

Since 1915, when Elk Basin field was brought in, eight oil fields have been developed in Montana and the production has arisen from 50,000 bbl. in 1916 to 8,000,000 bbl. in 1926. The production for 1927 was 5,121,600 bbl. and the total up to the end of 1927 was 27,138,239 barrels. The eight fields, with their year of discovery are: Elk Basin, Carbon County (1915); Devil&apos;s Basin, Petroleum County (1919); Cat Creek, Petroleum County (1920); Soap Creek, Big Horn County (1921); Kevin-Sunburst, Toole County (1922); Lake Basin, Stillwater County (1924); Pondera, Pondera and Teton counties (1927); and Bannatyne, Pondera and Teton counties (1927). About 170 wildcat wells have been drilled in the state of which 8 were successful and 162 gas wells or dry. Hence, only one out of 21, or 5 per cent. of the wildcats have been successful. The average depth of the wells has been 1600 ft. and the average cost $32,000 apiece. • Up to Jan. 1, 1927, a total of 1376 wells have been drilled in the producing oil and gas fields of the state, of which 904, or 66 per cent., were successful oil wells; 82, or 6 per cent. were gas; and 390, or 28 per cent, were dry. The percentage of dry wells is excessive as compared to the wells in other states, due to the uncertainties of limestone reservoir rocks. The total production of oil to Jan. 1, 1927, has been 22,016,639 bbl. and of gas 7,265,330,000 cu. ft. The average price at the well for the oil has been $1.47 per bbl. and for gas about 4 c. per 1000 cu. ft. The value at the point of consumption has been about 23 c. per 1000 cu. ft. The total revenue derived from crude oil has been $32,277,119, and from gas 8350,613, or a total income to the producer of $32,727,832. Each well drilled in the state has already (to Jan. 1, 1927) averaged a return of over $21,000. The total number of domestic (Montana) oil and gas companies organized, since the first in 1885, has been 844, of which 702 are still alive and 142 dead. Oil and gas companies registered for operation within the state to Jan. 1, 1927, but with outside charters, are 143, of which 66 are alive and 77 are dead. Outside the few distributing companies, which are included in these figures, the grand total of 997 companies which have

Jan 1, 1928

By R. Littlewood

The concepts of "redox potential" and "oxide-ion activity" are suggested as measures of the fundamental slag properties of interest to the extraction metallurgist. Thermodynamic data for single oxides are presented graphically in these terms and a method of expressing desulfurization of steel in electrochemical terms is indicated. The application of the theovy to mixtures of oxides (slags) is discussed and the redox potential is shown to provide a link between all the redox equilibria in a slag-metal system. In particular, the redox potential of the slag, its basicity, and the oxygen partial It is now generally recognized that slags are mixtures of polymeric anions of silicates, aluminates, phosphates, and so forth, neutralized by cations. However, conventional thermodynamic treatments of slags have almost always been in terms of activities of the pure component oxides (e.g., SiO,, CaO, A1203, and so forth), which are known not to exist as such in slags. While this type of empirical treatment is perfectly acceptable and provides a rigorous and self-consistent way of considering thermodynamic properties, it can give little guide to the structure of slags, since its very nature ig- pressure are closely connected. Direct deternzination of these by electrode-potential measurements is possible. Literature calculations of ion activities in the system Ca0 -Fe0-SiO,/molten iron are used to evaluate redox potentials, which are shown to correlate with data on sulfur partition in the system. In addition to its application to equilibrium conditions, an electrochenzical approach to slag-metal reactions might provide a basis for new methods of studying the kinetics of these reactions and for plant-control instruments in the pyrometallurgical industries. nores such complications. Recently, the thermodynamic properties of some slags have been successfully interpreted in terms of activities of anions of varying degrees of complexity. (While these have been successful curve-fitting exercises, there is no direct implication that the anions used in the models are necessarily the ones which actually exist in slags.) The success of these ionic thermodynamic treatments is encouraging but a complete picture of slag structure is still a long way off. What is needed is a complete knowledge of the values of stability constants for all reactions in slags of the type:

Jan 1, 1965

By Enid C. Plante

To extend our knowledge of the flotation behavior of sulphide minerals, the response of the following minerals to ethyl xanthate as collector was studied by captive bubble and cylinder flotation tests: antimonite (Sb2S3), arsenopyrite (FeAsS), covellite (CuS), rnarcasite (FeS2), orpiment (As&.), pyrrhotite (FeS) and tetrahedrite (4CU2S, Sb2S3). Lollingite (FeAs2) was also exarnined to determine if its behavior could be correlated with that of pyrite or rnarcasite (FeS2. Experimental Method Mineral for Flolation and Contact Tests Mineral was prepared in the manner a1ready described1 and its behavior both freshly ground and "oxidized" was studied. Tests in which the mineral was allowed to oxidize for various periods showed that a uniform response to xanthate was reached in two days or less. Oxidation Products The soluble oxidation products from most of the above minerals were measured and their effect on the flotation of the mineral studied. The mineral samples were wet ground to minus-52 mesh and deslimed, and 20 g of this material placed in 200 ml of distilled water of a measured pH value, and CO2-free air bubbled through each suspension at a constant rate (about I bubble/sec) for 5 days. It has been shown1 that the size of the mineral is unimportant in the rate of formation , oxidation products and that probably the supply of oxygen to the mineral is the rate-determining step. At the end of 5 days the pH value of the &apos;supernatant liquid was measured again, the mineral filtered off and the soluble products determined. Methods for estimation of sulphur acids, ferrous and ferric iron and copper have already been described.l No satisfactory method was found for antimony. Arsenic was estimated as the arsenate.2 Flotation of "Unoxidized" Minerals with Ethyl Xanthate as Collector Fig I to 3, 4. 6, show the effect of alkali and cyanide as depressants for the minerals with 25 mg potassium ethyl xanthate per liter as collector at 35°C. Wark and Cox8 have shown that with ethyl xanthate as collector, galena, pyrite and chalcopyrite show a greater tolerance to cyanide and hydroxyl ions at room temperature than at 35°C Covellite (Fig I), marcasite (Fig 2) and pyrrhotite (Fig 3) behave similarly. The independence of the curves for pyrrhotite at 35°C with respect to cyanide

Jan 1, 1949

By T. E. Leontis

Data are presented in this paper to show that addition of zirconium to sand-cast Mg-Th alloys effects a marked decrease in the grain size of these alloys which is accompanied by a significant increase in the mechanical properties over the entire range of thorium content investigated. The beneficial effect of zirconium on the strength properties is maintained at elevated temperatures up to 700°F. In addition the alloys exhibit exceptionally high creep resistance at temperatures up to 600°F. Zirconium does not greatly improve the strength or creep characteristics of extruded Mg-&apos;Th alloys. Cerium is not a desirable addition to Mg-Th-Zr alloys. IN a previous paper,&apos; it was shown that addition of thorium to magnesium imparts exceptionally high resistance to creep at elevated temperatures both in the sand-cast and in the extruded states. The large grain size of the sand-cast alloys, however, renders them of questionable value as engineering materials. Sauerwald² showed that the grain size can be reduced effectively by the addition of zirconium. Results of a detailed study of the properties of Mg-Th-Zr alloys over a wide range of thorium content are presented in this paper. In accordance with the preliminary findings of Sauerwald,² it is shown here that Mg-Th-Zr alloys possess the unusual combination of fine grain size and a high level of strength and creep resistance at elevated temperatures. Some information on the effect of cerium on the properties of Mg-Th-Zr alloys is presented also. Effect of Th on Solubility of Zr in Molten Mg Sand-cast test bars and 3 in. diam extrusion billets of Mg-Th-Zr and Mg-Th-Ce-Zr alloys* were pre- pared according to the procedures described in the previous paper.&apos; The zirconium was added in the form of sponge metal as supplied by the Bureau of Mines.&apos; The maximum amount of zirconium that usually can be introduced into magnesium at the customary alloying temperature of 1350° F is about 0.7 pct. The analyses in Table I clearly show that thorium in- creases the solubility of zirconium in liquid magnesium. The tabulated zirconium contents are designated as "acid soluble;" this serves to distinguish these values from the small amount of zirconium that is not dissolved when the alloy is subjected to the action of a dilute acid solution. The "acid-insoluble" zirconium is believed to be ineffective as an alloying ingredient. The acid-insoluble zirconium contents ranged between 0.03 and 0.16 pct in the present alloys, the tendency was toward higher values in alloys with higher thorium content. In contrast to the effect of thorium, cerium decreases the solubility of zirconium in magnesium. This is shown by the three Mg-Th-Ce-Zr alloyst in- cluded in Table I and stands in agreement with the observations of Nelson and Stricter".&apos; on Mg-misch-metal-Zr alloys. Effect of Zr on Grain Size of Mg-Th Alloys The potent effect of zirconium as a grain refiner has been demonstrated for many types of magnesium alloys.3-8 Of greatest importance to date are Mg-Zn-Zr alloys5,6,8 and Mg-mischmetal-Zr alloys.3,4,7 Zirconium has also been found to exert a marked grain-refining action on Mg-Th alloys. All the Mg-Th-Zr alloys cast in the form of ½ in. diam test bars have an exceedingly fine grain size (Table I). Reference to the previous paper&apos; will show that binary Mg-Th alloys containing up to 6 pct Th are almost completely columnar even in the M in. diam reduced section of a test bar, and that 10 to 50 pct Th alloys have an equiaxed grain structure of 0.03 to 0.08 in. The data in Table I also show that addition of cerium to Mg-Th-Zr alloys has no effect on the grain size. In addition to increasing the strength properties, the fine grain size of Mg-Th-Zr alloys

Jan 1, 1953

The following correspondence relating to a paper bearing the above title, presented by J. F. Wolff, at the New York meeting in February, 1917, and published in the Transactions, Volume LVI, page 142, has passed between the author of the paper, and Mr. Anson G. Betts, and is interesting, although it was received much too late for incorporation in its proper place in Volume LVI. ANSON CT. BETTS, Asheville, N. C.-1. I should like to ask Mr. Wolff if he finds-from analysis of the iron formation and of the iron ore, and from the relative amounts of each in each unit area of the formation, unleached and after leaching, that the iron remains entirely insoluble and the total quantity still remains present; or whether he finds that some of the iron is removed, or possibly even added by deposition from the water passing through the formation. 2. The water that passed into the iron formation had to go somewhere; was it absorbed by underlying formations through hydration, or, after passing through the ore formation, did it come to the surface in springs at a lower elevation, or how did it escape from the ground? 3. I should like to ask Mr. Wolff whether he finds that the iron formation in the sedimentary series does not, come next to the quartzites and generally between the quartzites and slates. J. F. WOLFF, Duluth, Minn.-1. In common with others, you appear to have some hesitancy in accepting the fact of the removal, by solution, of the enormous quantity of silica which has been leached out of portions of the Biwabik iron formation, thus forming orebodies of merchantable iron ore. I believe that even Dr. Waldemar Lindgren once hesitated to accept this fact. However, the evidence is so simple and absolutely conclusive that the fact is established beyond all question. At the contact of orebodies with their rock walls, the bands of iron ore in the orebody can be seen in contact with the corresponding bands of original iron oxide in the rock wall, and the chert layers in the rock wall can be seen to give place to fine granular material (fine silica and iron oxide) and pore space. This is especially noticeable where slumping at the rock walls his not been so great as to displace the layers in the orebody from their contact with their corresponding layers in the rock wall.

Jan 9, 1918

Discussion of the paper of DORSEY HAGER, to be presented at the Colorado meeting, September, 1918, and printed in Bulletin No. 138, June, 191S, pp. 1109 to 1118. WALLACE E. PRATT, Wichita Falls, Tex. (written discussion*).¬Mr. Hager has touched upon interesting problems related to the broad subject with which he has entitled his paper. As to the existence of the important structural feature in the buried Bend series, which Mr. Hager constructs from well-logs, and designates as the "Bend Arch," there seems to be general agreement among a number of observers. Indeed, M. G. Cheney1 and Robt. T. Hill2 have each published structural maps of the Bend Arch that do not differ essentially from the map shown in Mr. Hager&apos;s Fig. 1. The reflection, in the overlying, unconformable Cretaceous, of certain folds in the Pennsylvanian, with which the petroleum accumulations has to do, is an important observation on the part of Mr. Hager, since, as he says, much critical territory is covered by Cretaceous, and it is highly desirable that the underlying Pennsylvanian structure be mapped, if possible. If the folds in the Pennsylvanian are of post-Cretaceous age, then it should be possible, in spite of the intervening unconformity, to determine approximately the position of buried folds beneath the Cretaceous overlap. The idea of post-Cretaceous folding would not be out of accord with the suggestion by Carroll H. Wegemann that the folding of the Permian beds in southern Oklahoma was still in progress as late as the Tertiary.3 But most observers have related the folds in the Pennsylvanian and Permian beds at the surface, both in North Texas and southern Oklahoma, to the process of. emergence of the land area at the end of the Permian. It seems more probable that the reflection of Pennsylvanian folds in the unconformable Cretaceous which Mr. Hager observed is due to long continued persistence of stresses which were largely relieved at the close of the Permian, than that the principal period of folding was post-Cre-taceous; this being the case, it seems likely that only folds of greatest intensity in the Pennsylvanian will, be decipherable in the Cretaceous overburden, and that many promising structural features are so concealed by the Cretaceous as to escape detection except by drilling.

Jan 8, 1918

By W. W. Tyler, A. C. Wilson, L. B. Nesbitt

INVESTIGATIONS of thermal conductivity and impact strength of the titanium alloy RC-130-B and 316 stainless steel were undertaken because of interest in strong, nonmagnetic, commercially available alloys of low thermal conductivity for use in low temperature experiments. Measurements of electrical resistivity and thermoelectric power were also made for some of the samples studied. The titanium alloy designated as RC-130-B is manufactured by Rem Cru Titanium Inc. It contains 0.14 pct C, 3.99 pct Al, and 4.7 pct Mn. A general discussion of properties of the two phase Ti-4Mn- 4A1 alloys is given by Finlay and Vordahl.&apos; The alloy is machinable and has a yield strength greater than 130,000 lb per sq in. at 0.2 pct offset. The 316 stainless steel sample used for both conductivity and impact strength measurements was obtained from the Allegheny-Ludlum Steel Corp. and is designated as Allegheny metal 18-8M, Type 316, Grade 316. The sample had received 25 pct minimum final cold reduction and had a Brine11 hardness rating of 255. Several impact tests were made on a sample of 316 stainless which had not received the 25 pct cold reduction. Also several data points are reported giving thermal conductivity and electrical resistivity for a sample of 304 stainless steel taken from stock. Figs. 1 and 2 give thermal conductivity and electrical resistivity data for the titanium alloy and for

Jan 1, 1954

By Lester Guttman

THE connection between short-range order and thermodynamic activities in binary solid solutions has been pointed out by Birchenall1 who calculated approximate values of the energy of interaction of Zn and Cu and of the degree of short-range order in alpha-brass at one composition and two temperatures. The purpose of this note is to call attention to a somewhat more accurate theory than that used by Birchenall and to extend the calculations to a wider range of temperatures and compositions as a means of testing its applicability. This is an example of the well-known general method of comparing measured thermo-dynamic functions of a system with those calculated from a microscopic model by means of statistical mechanics. In this case, mathematical approximations must be used which make difficult any decision about the validity of the model. Birchenall&apos;s statistical method resembles closely that called by Fowler and Guggenheim2 the "quasi-chemical" method which has been shown to lead in certain cases to results identical with those obtained by the method of Bethe.3 The quasi-chemical method has been extended by Takagi4 to give general formulae for the free energy of binary solid solutions based on several lattices at all compositions and temperatures. Specifically, he treats the four systems typified by: I. ß-brass; 2. a- brass; 3. AuCu3; 4. AuCu. When the temperature is so high that no long-range order exists, these formulae reduce to the same form for all lattice types, namely: [ ] Here the symbols have the following meanings: [F-Helmholtz free energy E-energy S-entropy k-the gas constant per molecule z-coordination number, (e.g. 12 in. a-brass). N-total number of atoms c-atomic fraction of A] VAA, VBB, VAB-energy per bond of the corresponding bonds log means log, throughout The superscript 0 denotes the thermo- dynamic function in the standard state, which has been chosen to be pure A or B with the same crystal structure as the solid solution. The quantity x is the ratio of the number of A-A bonds to the total number and for minimum F satisfies the equilibrium condition [ ] The free energy may also be written in terms of µA and µB, the chemical potentials or partial free energies per atom:

Jan 1, 1948

By D. J. Carney, J. Chipman, N. J. Grant

G. Derge—With the development of this last weapon, there is not much of a chance for hydrogen. It is certainly a very interesting paper, and it gives us more confidence in sampling liquid steel for hydrogen than we have ever had before. This satisfactory work gives considerable confidence to all of the chilled methods of sampling which should be more or less successful depending upon the degree of chilling obtained. J. T. MacKenzie—How do you handle a nonmagnetic specimen in that device? D. J. Carney (authors&apos; reply)—I left that out in going over the analytical procedure. For the 18-8 steel, what was done was to get some iron wire which was degassed. One turn of wire was made around the sample; it was inserted into the analytical apparatus, and that was enough to allow the magnet to pull the sample and drop it in the furnace. Other methods could be devised for this apparatus to do the same thing. This was just a quick method. C. E. Sims—This method of sampling and analysis is very ingenious, and the results obtained attest to a satisfactory degree of accuracy. It was noted in the paper that the samples are satisfactory only when there is a complete absence of pipe. This should be empha- sized, particularly in view of the fact that they are cut off under water. Some reservations are held in regard to the adequacy of the method of sample storage prior to analysis. Cooling on dry ice undoubtedly slows down the rate of diffusion to a marked degree, and it obviously suffices when the analysis is made within a few hours. All of the samples, except some of high-nickel steels, were analyzed within 12 hr. It is still unknown how long this method would be safe. In the work at Battelle Institute, it was impracticable always to start analysis within 12 hr for various reasons. Some samples did not reach the laboratory for several days, and some were held as long as a month before analysis. During this period, they were held over mercury, and the gas evolved at room temperature was collected and analyzed. It should be mentioned that both the mercury and the container must be kept very clean.

Jan 1, 1951

By Charles C. Peterson, Ronald E. Enstrom

Significant improvements have been made in the ursine systern for epitaxial vapor gvowtlz of Gds. The electron concentration has been reduced to below 1015 cm-3 with electron-mobility values as high as 7200 sq on per v-sec at 30PK and 60,000 sq cw7 per v-sec at 77°K. These high-purity layers have been successfully gvown on n&apos; layers with thicknesses as snzall as 1 p and as large as 125 p. Furthermore, high-purity layers have been incorporated into an structure without degradation of electrical properties. Different impurity gradients at the n&apos; to n interface were achieved. Using these structures, Gunn oscillators have been operated at frequencies as low as 0.4 GHz and as high as 40 GHz, which equals the highest valzle yet reported. The frequencies nleasured are in reasonable apeenlent with those calculated fron7 the n-layer widths and the transit times. CW operatiolz has been achieved from 3 to 20 GHz. In Gunn devices for >40 GHz operation (i.e., witk an n-layer tkickness below 2.5p), the n layer has been generally too pure to permit oscillations to occuv. ThE mechanism of the Gunn oscillator&apos; is now generally understood.2-5 Electron transfer from the (000) minimum to the ( 100) minima leads to a voltage-controlled negative resistance, which results in the formation of domains of high and low electric fields which travel through the crystal with a characteristic velocity of about 107 cm per sec. When a constant voltage is applied to the sample, this domain motion generaliy leads to oscillations at the transit time frequency, fT = 107/L, where L is the thickness of the active n layer.&apos; In this case, a single high-field domain is nucleated at the cathode and grows until it reaches the anode, where it is absorbed; a new domain then forms at the cathode.5 There are related modes of oscillation of the same device in which a tuned circuit causes a periodic variation of the voltage across the device. The frequency then may be either above or below fT. It has been shown that oscillations will occur when n • L 2 1012 cm"2, where n is the carrier concentration in the active region. At lower doping densities, 10" 5 n . L 5 lo&apos;&apos;, the doping is said to be subcritical for oscillation and the description of the device operation changes since the domains become comparable in thickness to the device thickness, L. Nevertheless, such devices have been found to be "active" and, in fact, are useful as amplifiers.778 For CW operation, one wishes to minimize the power dissipation, which is related to the electric field, E, and the low-field resistivity, p. Below threshold, the power dissipation density is approximately Typically, at threshold where E -- 3 x 103 v per cm, the dissipation density is 107/p watts per cu cm, p in ohm-cm. Furthermore, it is desirable to provide good conduction of the heat generated in the active region. The temperature rise, AT, across the active layer of a sandwich structure, with a heat sink on one side, is given by AT = (E&apos;/P)(L~/~~) where it is assumed that the thermal conductivity, u, and resistivity, p, of GaAs do not vary appreciably over the range of temperature and electric fields existing in the layer. This expression shows that, subject to maintaining an appropriate (n . L) product, CW operation is favored by a higher resistivity, a lower threshold field, and a thinner device. The above device requirements place some severe restrictions on the materials to be used, especially for high-frequency (>10 GHz) operation. Here, it is necessary to prepare very thin (<10 µ) layers of GaAs, in a state of high purity (-1 ohm-cm), complete with very low-resistance ohmic contacts. Problems of handling such thin and fragile samples become inereasingly severe as the frequency is raised. Furthermore, while good low-resistance ohmic contacts are easily applied to low-resistivity GaAs, contacting difficulties are encountered for these higher-resistivity materials.

Jan 1, 1968