By Gilbert Soler

Page Introduction. By Gilbert Soler.........................657 Deoxidation of Basic Open-hearth Steel. By T. S. Washburn.............658 Slag-metal-oxygen Relationships in the Basic Open-hearth and Electric Processes. By J. S. Marsh. (With discussion)...........................672 The Total Oxygen Content of Plain Carbon Open-hearth Steel during Deoxidation and Teeming. By Michael Tenenbaum and C. C. Brown. (With discussion)......685 The Occurrence of Oxygen in Liquid Open-hearth Steel—Sampling Methods. By T. E. Brower and B. b. Larsen..........................712 Effect of Deoxidation on the Strain-sensitivity of Low-carbon Steels. By H. K. Work and G. H. Enzian. (With discussion)........................723 The Relation among Aluminum, Sulphur, and Grain Size. By C. E. Sims.......734 Some of the papers and discussions that appear on the following pages were presented at the meeting of the Iron and Steel Division in Cleveland, Ohio, on Wednesday, October 18, 1944. with L. F. Reinartz and H. K. Work as Chairmen; the remainder were scheduled for the New York Meeting of the Institute in February 1945, which was canceled.

Jan 1, 1945

By C. A. Siebert, D. J. Girardi

PRACTICALLY every metallurgical process in-volves, at some stage or another, the contact of a metal with a gas. Because of this, gas-metal re-actions are of great practical importance and have been subjected to numerous investigations. It has long been recognized that the presence of cuprous oxide in liquid copper has an important effect on its casting characteristics and .physical properties. This has led to the desirability of determining the quantitative relationships between cuprous oxide in the liquid copper and the usual gases present during processing. Such data are not only of practical importance but also of a theoretical interest in that they provide a means of applying the principles of physical chemistry to problems in applied metallurgy. The object of this investigation was to determine the quantitative relationship at equilibrium between the gases carbon monoxide and carbon dioxide and the cuprous oxide content of liquid copper. The reaction and its equilibrium constant may be expressed as follows: 2 Cu (liq) + CO2 (g) = Cu2O + CO (g) acu2o X aco/a2 cu X aco2 Here the underlined symbol Cu2O designates cuprous oxide dissolved in liquid copper and (a), the activity of the various constituents. The activities of carbon monoxide and carbon dioxide are assumed to be directly proportional to their re- spective partial pressures and the activities of cuprous oxide and copper are taken to be proportional to their respective mol fractions. The equilibrium constant may then be expressed as follows: K2 = Ncu2o X Pco [Ncu]2 X Pco2 where N = mol fraction The solubility of carbon monoxide and carbon dioxide in liquid copper is a rather controversial subject.'-' A review of the literature is given by 0. W. Ellis.' It appears that carbon monoxide and carbon dioxide are both only very slightly, if at all, soluble in liquid copper. Volskii and Slobodskoi5 determined the equilibrium between carbon monoxide, carbon dioxide, and liquid copper at 1100°C. Their results show a higher cuprous oxide content for a given CO/CO2 ratio than found in the present work. The system hydrogen, water vapor, and liquid copper was investigated by Allen and Hewitt8 over the temperature range of 1090" to 1350°C. Equilibrium values for the system carbon monoxide, carbon dioxide, and liquid copper calculated from these data agree reasonably well with the present work. Materials and Procedure The copper used was oxygen free, designated as OF and analyzed as 99.98 pct copper with no appreciable amount of any one impurity based upon spectrographic determinations. The carbon dioxide was cylinder gas averaging about 99.95 pct CO2 with air as the major impurity. The carbon monoxide was produced by passing carbon dioxide over heated charcoal. Alundum combustion boats were used as containers for the liquid copper. No appreciable reaction took place between the copper and the alumina. This was evident from the fact that the copper sample after a run did not ordinarily adhere to the bottom of the boat and that the

Jan 1, 1951

By B. Fitch

This paper deals with the behavior of sedimenting suspensions. More particularly, it treats, in as organized a manner as possible, the body of knowledge, theoretical or empirical, by which one predicts the behavior of miscellaneous swarms of particles in suspension. Such knowledge is necessary for precise and economical design of equipment. While the behavior of a single spherical particle settling through an infinite sea of quiescent fluid is well understood, practical sedimentation processes are almost always concerned with particles of assorted sizes, densities, and shapes, in such concentration that there is profound particle interaction. Such swarms of particles are observed to settle in any of four markedly different manners. Which one they follow is governed by particle interaction. It is determined largely by the dilution of the suspension, and the relative tendency of the particles to cohere. TYPES OF SEDIMENTATION The relationship between the different modes of sedimentation is shown paragenetically in Fig. 1. The left side of the diagram represents particles having little tendency to cohere; the right side represents particles for which interparticle cohesion is large compared to the settling force. The vertical axis represents dilution. As seen in the diagram, sedimentation is divided into three broad fields or regimes. At high dilutions there exists a regime here named 'clarification.' Particles in clarification may settle either individually, or by collecting into separated floccules. Thus there are two different possible modes of settling in the clarification regime. It is characteristic c~f this regime that there will be no clear line of demarcation between settling suspension and a supernatant. Faster particles settle out ahead of slower ones. In batch tests there develops a gradation of both particle sizes and pulp density due to progressive depletion of the largest particles from any given pulp level.

Jan 1, 1962

By R. J. Wygal

A method is presented by which homogeneous, isotropic, and reproducible aggregates of particles such as glass beads, sand, ground glass, etc., may be prepared simply and quickly by using a "particle distributor". Several applications of the packing method to the construction of model reservoirs are described. The flow characteristics of these packings me given. Some factors which limit the usefulness of unconsolidated packs for simulating reservoir rock are overcome through artificial cementation of the aggregates. INTRODUCTION Many laboratory studies of porous media are based on experiments using test packs of sand, glass beads and other granular materials. More confidence can be had in the results of such studies if the test packs are known to have uniform properties throughout, to be mechanically stable and to be accurately reproducible. This paper presents a method by which such packs of a variety of shapes and sizes may be constructed using a particle distributor. Some factors which limit the usefulness of unconsolidated packs as a means for simulating reservoir rock are described. A method of overcoming these limitations, which involves artificial cementation of the packs, is presented. DEVELOPMENT Particles packed by the tamping or vibrating techniques are usually either non-uniform or mechanically unstable. An invention by Currie and Gregoryl overcomes these difficulties to some extent. The invention is based on the use of a stream of falling particles impinging on and passing through a distributor matrix of several layers of closely spaced spheres. The particles are well dispersed by numerous collisions with the spheres. They become homogeneously distributed at some distance below the distributor matrix and at that position are collected in the sample container. This apparatus, however, was found to be ineffective when small particles were used since small particles accumulate on the top surfaces of the spheres. An improved distributor matrix was made, first in the form of a stack of five sieves, and then in the more adaptable form of spaced layers of wire screen. Fig. 1 shows a longitudinal view through a five-layered distributor of eight-mesh wire screen. This device gives excellent results.* Fine particles pass through the distributor with very little hold up. The fine structure of the wire matrix with its many deflecting surfaces ensures good particle distribution. There are no dead areas immediately below the screen as were sometimes observed to occur below a matrix of spheres. Using such a device, 20-30 mesh sands were packed to a porosity of 32.1 per cent at rates varying from 0.17 to 6 lb/rnin. The lowest porosity achieved by tamping small increments of similar sands into a container was 33 per cent. Motion pictures at 3,000 frarnes/sec of the surface of a growing pack of 2-3/4 mm glass beads have helped to show the mechanism by which packs of low porosity are obtained. The beads, although packed at the rate of 5 lb/min, were observed to hit the pack surface singly, for the most part, and at well spaced points of impact. Part of their energy is transferred to surface beads which are thereby

By Donald C. Myntti

INTRODUCTION A major segment in a successful heavy equipment maintenance and repair program is the provision of well-laid out and well-equipped shop and service facilities The facilities described here will be those required for a large, high tonnage hard rock open pit mine utilizing rotary drills, shovels, haulage trucks, support equipment, and service trucks. The term support equipment covers the equipment required to support the drill, shovel, and truck operations, these are crawler tractors, road graders, front-end loaders, water trucks, rollers, rubber-tired tractors, etc. Service trucks are the automotive type consisting of rubber-tired over-the- road equipment. The primary structures generally involved in the total maintenance effort are as follows. (1) the main shop with an attached warehouse (the structure could also house the tire and lube shops plus the equipment cleaning stalls), (2) a service station with bulk petroleum product storage tanks, (3) a heating plant, (4) a security station (lf this is a corporate requirement), (5) operating department and employee assembly buildings, and (6) an electrical substation. Under certain conditions, many of these facilities with the exception of the substation could be combined In one or several structures. This arrangement could have a great advantage especially in areas where the heating of the structures is extremely critical.

Jan 1, 1979

By Woolf, W. G.

Filtration of hot (60°C) supersaturated zinc sulphate solution (sp gr 1.540) from slimy leach residues at the electrolytic zinc plant of Sullivan Mining Co., Kellogg, Idaho, is de- scribed. Separation of liquids and solids in the finished leach is by Burt filters modified to meet conditions of high-acid, high-density process for electrolytic zinc. Operating characteristics of the Burt filter on this pulp are presented.

Jan 1, 1950

L. C. UREn,* BerkelEy, Cal. (written discussion).—I heartily concur with Rlr. .Fobs concerning the need for advanced courses on various phases of Petroleum Engineering. I think that his criticism is probably true of most of the engineering schools that are specializing at all in Petroleum Engineering, that is, that most of their so-called graduate courses are not of graduate caliber but are merely more specialized aspects of undergraduate subjects. It would undoubtedly be to the advantage of the petroleum profession if more advanced work could be offered in a few of the leading engineering institutions so that there would be something substantial to offer graduate students wishing to return after a period of undergraduate work, for additional training. There is no doubt but that a better trained engineer, more useful to the oil industry, could be secured from schools offering such advanced training. The problem of adpting our instruction to fit the needs of engineers trained along other lines who wish, after completion of their undergraduate work, to enter thc petroleum engineering field, is a more difficult one. It has been my experience that such men are usually sadly deficient along certain lines and that they are really not prepared for the more advanced work in Petroleum Production Engineering until they have gone back over the work which they have missed in their undergraduate training. I note that Mr. Fohs suggests that other eastern and western colleges not now stressing Petrolelim Engineering, should be encouraged to take up advanced work of this character. With this, however, I cannot agree unless the institutions arc also prepared to offer a full sequence of undergraduate work on which the more advanced courses may be superimposed. Whether or not there is a need for additional engi-ncering colleges entering the petroleum engineering field is an open qucstion. I believe that we arc turning out enough petroleum engineers at the present time and that none of the six institutions now specializing in this field arc overcrowded. Morc-ovcr, they are fairly well distributed over the country, though there may be room for an additional school in the field in the eastcrn section of the United States. F. W. Padgett, Norman, Okla. (written tliscussion).—Assuming that the stnclcnt has the proper fundamentals, that is, general science and a knowledge of the technology of the industry, then the problem is: What courses should be offered from the graduate standpoint? (a) Course Work.—His knowledge of the technology of the industry can be extended advantagcously by means of one and two-hour courses, which consist in a more detailed survey of the various branches of the industry. (b) Lilerdure.—This work may, or may not, be connected directly with his research problem. The student should become familiar with methods of locating articles in the 1iterature; should also become familiar with all the important original

Jan 1, 1928

By Henry Schaefer

Solution by electric analogy of performance problems of reservoirs containing oil and gas has heretofore depended upon a process of successive approximations based on material-balance calculations, because of variation in fluid compressibility. By the addition or subtraction of electric condenser capacity, the analogy network can be adjusted automatically for changing compressibility due to evolution of gas in the reservoir. The addition of a condenser is accomplished by an electronic circuit, which is described; subtracting a condenser is done by merely opening the electrical circuit by means of a relay. Introduction V. Paschkis and H. D. Baker1 first developed in this country a method of applying the analogy of flow of electric current in noninductive circuits to solution of heat-flow problems and suggested its application for certain other problems, such as flow of fluids or mass transfer and chemical diffusion. Necessary details for applying the analogy to flow of fluids in porous media were developed by IV. A. Bruce;= he classified3 the types of analysis and predictions that can be made by the analogy in class I, when the reservoir contains oil but no gas for the period under consideration; in Class 2, when both oil and gas exist in the free state in the reservoir sometime during the period under consideration. Duplication of bottom-hole pressure history and predictions for class I reservoirs can be obtained directly by electric analogy. Until now, the solution of problems pertaining to reservoirs in class 2 was obtained by successive approximations along with material-balance calculations. The object of this paper is to present a method for simplifying the application of electric analogy to class 2 reservoirs, resulting in a solution of these problems as direct as is possible for class I reservoirs. This is accomplished by an electronic control circuit, which adjusts the analogy network for changing compressibilities of fluids contained in the reservoirs. Analogy Network In electrical phenomena the analogy to two-dimensional fluid flow in a porous media is that of current flow through an ideal conducting sheet. This sheet, perfectly insulated on both sides, has resistance and capacitance uniformly distributed throughout its area but is of negligible inductance. The need for having the surface boundaries perfectly insulated is that good correspondence may be had with a permeable fluid-conducting stratum bounded above and below by impermeable media. 111 actual application the ideal conducting sheet, which has distributed parameters, is replaced by a network having lumped values of resistance and capacitance—the resistances are series elements and the capacitances are shunt elements. The larger the number of lumped

Jan 1, 1947

By Henry Schaefer

Solution by electric analogy of performance problems of reservoirs containing oil and gas has heretofore depended upon a process of successive approximations based on material-balance calculations, because of variation in fluid compressibility. By the addition or subtraction of electric condenser capacity, the analogy network can be adjusted automatically for changing compressibility due to evolution of gas in the reservoir. The addition of a condenser is accomplished by an electronic circuit, which is described; subtracting a condenser is done by merely opening the electrical circuit by means of a relay. Introduction V. Paschkis and H. D. Baker1 first developed in this country a method of applying the analogy of flow of electric current in noninductive circuits to solution of heat-flow problems and suggested its application for certain other problems, such as flow of fluids or mass transfer and chemical diffusion. Necessary details for applying the analogy to flow of fluids in porous media were developed by IV. A. Bruce;= he classified3 the types of analysis and predictions that can be made by the analogy in class I, when the reservoir contains oil but no gas for the period under consideration; in Class 2, when both oil and gas exist in the free state in the reservoir sometime during the period under consideration. Duplication of bottom-hole pressure history and predictions for class I reservoirs can be obtained directly by electric analogy. Until now, the solution of problems pertaining to reservoirs in class 2 was obtained by successive approximations along with material-balance calculations. The object of this paper is to present a method for simplifying the application of electric analogy to class 2 reservoirs, resulting in a solution of these problems as direct as is possible for class I reservoirs. This is accomplished by an electronic control circuit, which adjusts the analogy network for changing compressibilities of fluids contained in the reservoirs. Analogy Network In electrical phenomena the analogy to two-dimensional fluid flow in a porous media is that of current flow through an ideal conducting sheet. This sheet, perfectly insulated on both sides, has resistance and capacitance uniformly distributed throughout its area but is of negligible inductance. The need for having the surface boundaries perfectly insulated is that good correspondence may be had with a permeable fluid-conducting stratum bounded above and below by impermeable media. 111 actual application the ideal conducting sheet, which has distributed parameters, is replaced by a network having lumped values of resistance and capacitance—the resistances are series elements and the capacitances are shunt elements. The larger the number of lumped

Jan 1, 1947

By F. A. Champion

The work described in this paper was carried out in the Research Laboratories of the British Aluminium Company Ltd., under the general direction of A. G. C. Gwyer, Scientific Manager of the Company. In considering the effect of stress?corrosion conditions on metals, or the failure of metal through stress corrosion, it is evidently advisable to adopt a clear definition of the meaning of those phrases. There appears to be general agreement that stress-corrosion conditions may be defined as the continuous application of static stress to a metal while it is exposed to corrosive conditions, but recognition of the occurrence of true stress-corrosion in a metal is often a difficult matter giving rise to some confusion. For the purpose of this paper stress corrosion in a metal is defined as the acceleration of corrosion by the application of static stress. On this view it is necessary to test a metal not merely under stress-corrosion conditions, but also under the same corrosion conditions without the simultaneous application of stress, if the liability of the metal to stress corrosion is to be assessed. Failure of a metal under stress-corrosion conditions is sometimes quoted as evidence of stress corrosion (for example, by Althof(1)2), but this evidence is totally inadequate if the above definition is

Jan 1, 1945

Z. W. Bartlett, J. C. Carrington, H. C. Petersen and K. T. Price were elected vice-presidents of the Freeport Sulphur Co. Blandford C. Burgess was transferred on January 1 to the new Defense Materials Procurement Agency as strategic materials specialist. In May the Region III headquarters of this organization was moved to London. L. C. Campbell was elected president of National Coal Assn. Mr. Campbell, who has been a member of the National's Board of Directors and Executive Committee for many years, is vice-president of the Coal Div. of the Eastern Gas & Fuel Associates and in charge of their extensive mining operations in West Virginia, Pennsylvania and Kentucky. Vern H. Christoph has been transferred to Panama Canal Co., Marine Bureau, Navigation Division, Port Captains Office, as an admeasurer at Cristobal, Canal Zone. Eugene Cline, recently graduated from the University of Kentucky, has been employed by Pond Creek Pocahontas Coal Co., at Evanston, Ky. Sanford S. Cole, assistant manager of research at the Titanium div. of National Lead Co., received the Alumni Citation from his alma mater, Alfred University, Alfred, N. Y. This was in recognition of outstanding achievements and services in the field of ceramics which have brought honor to the institution. U. K. Custred, recently graduated from University of Kentucky, and may be reached now at Box 87, Monterey, Tenn. Robert E. Dwyer, executive vice-president of Anaconda since 1940, was recently elected president of this company and its subsidiaries, Chile Copper Co., Chile Exploration Co., and Andes Copper Mining Co. As president, Mr. Dwyer succeeds the late William H. Hoover who died in Butte, Mont.

Jan 1, 1952

By Nicholas J. Grant, Ulf Kalling, John Chipman

THE operation of a blast furnace is dependent to an important extent upon the sulphur content of materials charged and the desired limit of sulphur in the product. It has long been known that the blast furnace is the most efficient tool for desulphurization in common use and that this efficiency is associated with the strongly reducing conditions of the hearth and is enhanced by increased basicity and fluidity of the slag. The chemical reactions of desulphurization may be studied from the viewpoint of the ratio of the process or of the final equilibrium conditions. Both kinds of studies contribute to an understanding of the process and both are included here. A simple measure of the desulphurization power of a slag is given by the ratio: Pct sulphur in slag (Pet S) Pct sulphur in metal [Pct S] This ratio was used by Holbrook and Joseph',' to measure relative desulphurizing powers under controlled laboratory conditions. It was also used by Hatch and Chipman3 as a measure of the equilibrium distribution. For the latter purpose it would be preferable to employ thermodynamic activities rather than percentages, but until very recently this has been impossible for lack of data. Now, thanks to the work of Morris and Williams and Morris and Buehl," the effects of carbon and silicon upon the activity of sulphur in the metal are known. The confirmation of this work and its extension to include the effects of other elements by Sherman and Chipman and by Rosenqvist and Cox' make it possible to calculate the activity of sulphur in pig iron of any composition. Hence it is now possible to use data on the equilibrium distribution of sulphur to find its activity in the liquid slag and to approach an ultimate solution of the thermodynamic aspects of the problem. The rate of transfer of sulphur from metal to slag is the problem of major industrial importance and indeed the principal need for equilibrium data has been as a necessary adjunct to the kinetic studies. The rate of approach to equilibrium under laboratory conditions seems slow compared to the requirements of industrial practice, and it is clear that further laboratory studies of rates are needed. In the research reported below, the items which were investigated were the following: I—The role of mechanical stirring on the approach to equilibrium. 2—The role of MgO in desulphurization as compared to CaO. 3—The role of MnO in desulphurization. 4— The limiting reactions which constitute the slow steps in desulphurization. Experimental Procedure The experimental set-up and procedure previously described by Hatch and Chipman" were essentially followed with several small modifications. The graphite crucible containing the slag and metal charge was altered to provide considerably more active stirring and mixing of the slag and metal in the carbon monoxide atmosphere. For this purpose the crucible was machined to provide two deep cylindrical wells which were interconnected at top and bottom as shown in Fig. 1. A graphite screw with a flat thread and of shallow pitch (4 threads per in.) spinning at 600 to 800 rpm was used to lift the slag and metal over the partition between the two wells and throw them over into the second well, where the metal settled through the slag into the reservoir at the bottom. It was possible to see actual particles of slag and metal being thrown over the partition. In this respect, the stirring was more vigorous than used in the work of Hatch and Chipman. A charge of 400 g of wash metal was first melted, and 20 g of FeS was then added to yield a bath containing 1.65 pct S. Immediately 400 g of slag (as pure mixed oxides) was added and fused. The slag was generally fused in 1 hr * 10 min. Within 30 to 45 min after melting, the temperature was adjusted to 1525"C, and the first slag and metal samples were taken. The slag was picked up on the end of a cold Armco iron rod, whereas the metal was sucked into a silica tube. The wash metal composition was (in percent): 4.29 C; 0.022 S; 0.021 P; 0.38 Si. The slags used were of four fixed starting compositions covering a wide range of acid-base ratios shown in Table I. Deliberate variations in MgO were made in these slags to check the role of MgO in blast-furnace desulphurization. Changes due to additions and reactions were followed by analysis of samples. Additions of Mn and MnO were made to most of the heats to note the role of Mn and MnO on desulphurization. Three heats (62 through 64) were made in an open pot induction crucible (graphite) using a

Jan 1, 1952

By Holt, Grover J.

PRIOR to :1937 any discussion of mining and transportation in the iron mines of Minnesota would have been limited largely to conventional methods which have been used for years in the iron ore industry. Today, however, an inspection trip to the crest of almost any open pit on the ranges will re- veal great progress underground mining and the transportation of underground ore have also developed rapidly and if and when underground mining of iron ore again becomes generally economically feasible; these mining methods will probably witness a transformation equal to that which has taken place in the open pits.

Jan 1, 1941

By H. E. Elliott, R. S. Busk, A. T. Peters

ONE of the problems of the fabricator of metals and alloys is the propensity of some composition ranges toward abnormal grain growth during certain stages of fabrication. In this respect magnesium alloys are no exception among alloys. Fortunately, convenient foundry control methods have been developed by which the abnormal grain growth possible in certain magnesium-alloy castings can be suppressed. An unusual characteristic of magnesium alloys, however, is that castings of some composition ranges are subject to local grain growth during heat-treatment without the necessity of intentional mechanical stressing of the part prior to heat-treatment. This effect occurs only under certain critical casting conditions, and only in certain alloys of greater than about 8.5 per cent aluminum content, such as C alloy (Mg, o per cent Al, 2 per cent Zn, 0.2 per cent Mn) and G alloy (Mg, i0 per cent Al, 0.2 per cent Mn). The first observation of this phenomenon in cast magnesium alloys occasioned much surprise, since it is not observed in other metals. Jeffries and Archer' have stated that "the grain size of cast metals, provided they have not been plastically deformed, cannot be changed by heating below the melting point." The study of the conditions leading to abnormal grain growth in cast magnesium alloys, and of the mechanism of this phenomenon, has led to some very interesting observations. Perhaps the most significant of these was the observation that stresses originating from cooling contraction in magnesium-alloy castings are the only stresses necessary, under certain conditions, to cause local recrystallization and subsequent grain growth in the casting during heat-treatment. of abnormal local grain growth was a definite problem in the production foundry on C alloy sand castings. Illustrated (Fig. r) is a picture of a casting scrapped because of this defect. A mottled effect is produced in coarse-grained areas by suitable etching solutions. The properties of metal in the affected area are much impaired by such grain coarsening. Ultimate tensile strengths of half the normal value have been measured in metal of this nature. In this paper are described the techniques that have been developed by The Dow Chemical Co. for studying, and in large measure solving, this production problem. Also discussed are studies of the mechanism by which excessive grain coarsening occurs, and the fundamental conditions that produce this effect. The abnormal grain growth discussed in this paper will be referred to as "germination," since this term has been defined' as any process leading to an abnormally coarse grain size. This paper deals only with abnormal local grain growth that may occur during the solution heat-treatment of certain magnesium-alloy castings, as dis-

Jan 1, 1945

By E. C. Wright

THIS paper describes some properties of steels in the composition range 0.10 to 0.30 per cent carbon and 1 to 7 per cent chromium. It is well known that some steels of this type develop high tensile strengths upon receiving comparatively simple heat treatments, such as ordinary air cooling from appropriate temperatures, with "or without subsequent tempering treatments. These high strengths are frequently associated with unusual toughness as measured by the Izod or Charpy impact test. The chromium content, in addition to imparting the above properties, enhances the resistance to corrosion and improves the strength and oxida-tion resistance at elevated temperatures. Moreover, these steels have good forging and fabricating properties, as evidenced by the fact that several thousand tons of seamless tubing have been made during the past five years from steels containing 0.10 to 0.25 per cent carbon and 5 per cent chromium.

Jan 1, 1933

By H. M. Chance

The Taviche district is about 12 miles from the town of Ocotlan in the State of Oaxaca, and about 250 miles south of the City of Mexico. Its altitude rises to something more than 5,000 ft.; and although within the tropics (latitude about 17° N.) the climate is mild and salubrious, neither excessively hot in summer nor cold in winter. The phrase, "perpetual spring," which has been applied to it, aptly describes the weather during my stay. Sugar-plantations, bananas and other tropical and semitropical fruits flourish in the valleys, while the hills

Jan 1, 1905

By Alan Stanley

R. T. Hukki (Finland Institute of Technology, Helsinki, Finland)—In the analysis of mill products containing minerals of appreciable difference in specific gravity the well-known principle of the method described by Stanley is applied in a number of ways for a variety of problems. The use of Le Chatelier bottle as explained in the paper may be a dependable and sufficiently accurate way, although no information is given as to the reproducibility of the specific gravity determinations. In the case of MacIntyre ore the method is applied for three separate products produced apparently without reagents and relatively free of fine slimes. Should it be applied for flotation products carrying a substantial amount of slimes, difficulties should be anticipated in the process of eliminating air inclusions from the sample. The difficulties mentioned above may be overcome by the use of a volumeter, an instrument designed for specific gravity determinations of finely divided solids in dry state. This instrument, see Fig. 4, is manufactured by F. Süffert-Bürner A. G. in Basel, Switzerland. Its operation is based on the law of Boyle and Mariotte. With the use of the volumeter, the specific gravities of test samples having a total volume of about 30 cm are easily reproducible within ±2 units in the second decimal of the specific gravity figure, and even better than that with utmost care. This accuracy is sufficient for ordinary operational control. How closely the specific gravity determinations follow the respective chemical assays depends primarily on the nature of the sample itself. In this respect no specific gravity instrument can give better results than those justified by the consistency of mineral distribution in samples analyzed.

Jan 1, 1954

By Burt A. Waite

The new OSM regulations for ground water monitoring of underground coal mines have been the source of many concerns for the mining industry. Because the regulations were initially written at the federal level, but are being administered at the state level, considerable confusion still exists within the industry as to what is really required. Based on submission and/or approval of more than 30 monitoring plans for existing mines in Pennsylvania, West Virginia, and Ohio, three basic sections are necessary. They are: 1. background data on the hydrogeologic setting of the mine, 2. the monitoring plan itself, and 3. mining procedures to minimize adverse effects on ground water. Like all of the OSM requirements, ground water monitoring will be a new burden the coal industry must bear, but with proper planning and communication with the regulatory authorities it need not be as bad as originally feared.

Jan 1, 1983

By R. G. Davies

Above 500°C, where dislocation climb is rate controlling, it is observed that the activation energy for creep is independent of the apblied stress, although it varies from 62 kcal per mol at 15 pct A1 to 73 kcals per mol at 20 pctA1 due to the change in short-range ovdw with composition. Below 500°C, when the nonconservative motion of jogs upon dislocations is thought to be rate controlling, the activation energy is stress dependent. A sudden increase in the creep rate, for which no explanation is availab2e, occurs at the highest stress at all temperatures. CREEP has been the subject of numerous research publications during the past decade with most of the attention focused upon high temperature steady state creep, i.e., above 0.5 TM, where TM is the absolute melting temperature, as it is the most amenable to theory. Many of the proposed theories involve the climb of dislocations out of their slip plane, which allows them to circumvent obstacles or to annihilate dislocations of opposite sign on other slip planes.' For pure metals it is observed that the activation energy for this creep is equal to the activation energy for self diffusion.' The position is much more complicated in alloys as there are many possible microcreep mehanisms, as well as dislocation climb, which could be rate controlling. There has been little systematic investi- gation of alloys, but Weertman (lead and indium base alloys)3 and Lawley, Coll, and Cahn (Fe-A1 alloys)4 suggest a microcreep process as the controlling factor. A Cottrell-Jaswon atmosphere mechanism is proposed for the lead and indium alloys, and a mechanism involving crystallographic order for the Fe-A1 alloys. Lawley et al. showed that the formation of a super-lattice, either of the FeAl or Fe3A1 type. decreased the rate and increased the activation energy for creep. From the measurements of lattice parameters,= resistivity,' magnetic properties,7'8 internal friction: and dilatometry10 the ordered region is thought to commence at -19 at. pct Al. However, a recent investigation by the author indicates a value

Jan 1, 1963

By Frederic Benard

PRIoR to 1936, the Ontario Refining Co. received all incoming blister copper from The International Nickel Company's smelter in the usual form of 460-lb. cakes, or slabs. These were received in open cars in lots of 250 pieces. At the refinery the cakes were unloaded onto narrow- • gauge cars, for convenient handling and pickup by charging cranes. In March 1936, an investigation was started on the feasibility of transferring converter copper in the molten state from the smelter to the refinery anode furnaces, a distance of 1 1/4 miles. Although common in steel practice, the transportation of blister copper in this form had not previoisly been attempted and a preliminary study of the various factors involved was therefore necessary. For this purpose, a series of experiments was made in which molten copper, removed at different stages during the furnace cycle, was held in a small portable holding furnace. This vessel was essentially a refractory-lined steel cylinder provided with ports for filling and emptying, heated by an oil burner. Dimensions of the steel shell were 3 ft. 10 in. diameter by 7 ft. 3 in. long, and thickness of refractories depended on the design and combination used for the particular experiment. The vessel was filled with approximately 2 1/2 tons of copper at a predetermined temperature, the lining having been preheated to a definite point by means of an oil burner. All openings were well luted and temperature readings were made every 15 min. by means of an immersion-type thermocouple. In this manner the rate of heat loss resulting with different refractory design could be developed. The ratio of exterior surface to weight of metal was taken into consideration in comparing the experimental results with what might be expected for a full-sized unit, and observations were also made on type and degree of slag accretion. It was not possible to get as much information on this latter point as desirable, but all evidence showed that the problem would be control of slag build-up rather than attack on refractories. From the information derived, and in consultation with the engineering staff of the supplying company, an order was placed for the first

Jan 1, 1944